WO2012120775A1 - 結晶性評価方法、結晶性評価装置、及びそのコンピュータソフト - Google Patents
結晶性評価方法、結晶性評価装置、及びそのコンピュータソフト Download PDFInfo
- Publication number
- WO2012120775A1 WO2012120775A1 PCT/JP2012/000752 JP2012000752W WO2012120775A1 WO 2012120775 A1 WO2012120775 A1 WO 2012120775A1 JP 2012000752 W JP2012000752 W JP 2012000752W WO 2012120775 A1 WO2012120775 A1 WO 2012120775A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- raman
- waveform
- crystallinity
- thin film
- peak
- Prior art date
Abstract
本発明の結晶性評価方法等は、半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、ガウス関数を用いて、測定したラマンバンドのピーク波形をフィッティングすることで、ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、第1フィッティング波形のピーク値を抽出する第3工程と、抽出したピーク値を用いて、ローレンツ関数によりラマンバンドのピーク波形をフィッティングすることで、ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、第2フィッティング波形の半値幅等を出力する第5工程と、第5工程で出力された半値幅等に基づき、半導体膜の結晶性を評価する第6工程と、を含む。
Description
本発明は、結晶性半導体膜の結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトに関する。
例えば、有機エレクトロルミネッセンス(EL:Electro-Luminescence、以下有機ELと記載)表示装置及び液晶表示装置を用いたテレビジョン受信機等の電子機器がある。この電子機器においては、有機表示装置及び液晶表示装置を構成すべくマトリックス状に配置された発光素子が、複数の薄膜トランジスタ装置(TFT:Thin Film Transistor)により駆動される。
TFTは、例えば基板上に、ソース電極及びドレイン電極と、半導体層(チャネル層)と、ゲート電極とが順次積層されることにより構成される。TFTに用いられるチャネル層は、薄膜状のシリコン半導体を用いるのが一般的である(例えば、特許文献1)。
シリコン半導体膜としては、非晶質シリコン膜(アモルファスシリコン:a-Si)と、結晶性を有するシリコン膜(結晶シリコン膜)とに大別される。結晶シリコン膜は、さらに、多結晶シリコン膜、微結晶シリコン膜、単結晶シリコン膜等に分類できる。
このうち、非晶質シリコン膜は化学気相成長法(CVD法)などによって、比較的低温で、大面積の基板上に均一に作製可能であることから、現在、大画面の液晶表示素子用チャネル層として、最も一般的に用いられている。しかし、非晶質シリコン膜は、結晶シリコン膜に比べて、キャリアの移動度等の特性が劣る。そのため、より高速駆動且つ高精細なディスプレイを実現するために、結晶シリコン膜からなるTFTの実現が熱望されている。
一方、結晶シリコン膜を形成する方法としては、成膜時に結晶シリコン膜を直接成膜する方法(例えば、特許文献2)、または非晶質シリコン膜を成膜後に熱や光エネルギーを印加することで結晶化する方法(例えば、特許文献3)がある。
しかしながら、これらの方法によって作製された結晶シリコン膜は、各々全く異なる膜質を有する。また、同一の方法で作製したとしても、結晶化条件によっては、異なる膜質の結晶シリコン膜を有してしまう場合もある。
一般的に、結晶性半導体膜を能動層として用いた半導体デバイスでは、その能動層の膜質(例えば、結晶性、欠陥密度など)がデバイス特性に大きな影響を及ぼすことが知られている。つまり、結晶シリコン膜をチャネル層に用いたトランジスタ素子では、例えば、キャリア移動度、閾値電圧、信頼性などの素子特性に結晶シリコン膜の膜質が及ぼす影響が大きい。
以上から、結晶性半導体膜を半導体デバイスの能動層として用いるためには、その膜質を評価し、管理することが必要である。膜質管理においては、特に結晶性を管理することが望ましい。
結晶性半導体の結晶性を評価する手法としては、例えば透過型電子顕微鏡(TEM:Transmission Electron Microscope)、X線回折(XRD:X-ray Diffraction Technique)、フォトルミネッセンス(PL:Photo Luminescence)法等による方法が一般的に用いられている。しかしながら、これらの手法は、非破壊、短時間、微小領域をインラインで評価することが困難である。
そこで、上記の要求(非破壊、短時間、微小領域をインラインで評価)を満たす手法として、ラマン分光法がある。
以下、ラマン分光法について、図面を用いて説明する。
図25は、入射光と分子のエネルギー交換によるラマン散乱を模式的に示す図である。
ラマン散乱とは、物質中の原子が振動しているときに光と相互作用して引き起こされる現象である。具体的には、原子核が振動数νで振動している物質に振動数ν0の光を照射すると、振動数の異なる二つの波が干渉し、振動数がν0+νとν0-νの光がν0の光と同時に照射される現象である。
ここで、図25の(b)に示すように、入射光と同じ振動数を与える光散乱をレイリー散乱と呼び、ν0±νを与える光散乱をラマン散乱と呼ぶ。ラマン散乱のうちν0-νの振動数を持つ成分をストークス散乱(図25の(a))、ν0+νの振動数を持つ成分をアンチストークス散乱(図25の(c))と呼んで区別する。
また、入射光とラマン散乱光との振動数差±νをラマンシフトという。このラマンシフトは物質に固有であることから、物質のキャラクタリゼーションの有力な手がかりとなる。
このように、ラマン分光法は、試料にレーザ光を照射し、発生するラマン散乱光を測定することによって、簡便、非破壊・非接触測定、微小領域の評価ができ、微視的な物性を知ることができる手法である。
例えば特許文献4には、ラマン分光法により結晶シリコン膜の結晶性を管理して半導体装置を作製する方法が提案されている。特許文献4では、a-Siをレーザ結晶化して作製する際に、その結晶化状態をラマンピークの波形や半値幅を観察しながら結晶化する方法が開示されている。また、例えば特許文献5には、ラマン分光法により計測したラマンスペクトルから結晶シリコン膜の結晶性管理方法が提案されている。特許文献5では、基板上に結晶シリコン膜を形成し、結晶シリコン膜に固有のフォノンに対応したラマンバンドのピーク波形をラマン分光法により測定し、このピーク波形の非対称性の程度から結晶性を管理する方法が開示されている。
しかしながら、上記特許文献4及び上記特許文献5に開示されている方法では、結晶シリコン膜の結晶性を正確に評価(解析)することはできない。
具体的には、上記特許文献4に開示されている技術では、結晶シリコン膜のラマンスペクトル波形から結晶性に関する情報として、波形を数学的に解析したピーク強度やピーク強度の半値幅を用いている。しかし、これらのパラメータは、測定条件やサンプルの状態などの影響を受け、必ずしも結晶性のみを反映した値とはならないため、これらのパラメータを用いて結晶性を正確に評価・解析することはできない。
また、上記特許文献5に開示されている技術では、結晶シリコン膜のラマンスペクトル波形から結晶性に関する情報として、ピークの非対称性を数学的に解析した情報を用いて、結晶性を管理している。しかし、この解析方法は物理的な根拠が薄弱で、ラマンスペクトルを正確に解析することは困難である。つまり、この解析方法を用いて結晶性を正確に評価(解析)することはできない。
さらに、従来よく用いられている複数のフォノンモードによるピークをガウシアン関数などで仮定した解析方法が用いられている。しかしながら、この解析方法においても、実験結果の再現性が良くないという問題がある。つまり、この解析方法を用いて結晶性を正確に評価(解析)することはできない。以下、この解析方法について具体例を挙げて詳しく説明する。
図26は、結晶シリコン膜のラマンスペクトル500と従来の解析方法による解析結果501とを示す図である。図26において、縦軸は規格化されたラマンピーク強度、横軸はラマンシフト(入射光からの差)を示す。
ここで、実測値である結晶シリコン膜のラマンスペクトル500は、図26に示すように、結晶シリコン成分502(ピーク位置:520cm-1)と、微結晶シリコン成分503(ピーク位置:~500cm-1)と、a-Si成分504(ピーク位置:~480cm-1)との3つの成分により構成されており、各成分のフォノンの分散はガウシアン関数に従うと仮定している。そして、解析結果501は、上記仮定を用いてラマンスペクトル500を解析して描いたフィッティング結果を示している。
解析結果501は、図26中の矢印A~Cで示した400~500cm-1付近において、実測値との不一致が観測される。さらに、各フォノンに対応したピークを見ると、結晶シリコン成分502において、物理的に想定される半値幅(測定系に依存するが4cm-1程度)よりも大きな半値幅によって解析されていることがわかる。つまり、実験結果の再現性が良くない。したがって、上記数学的に実験結果を再現する従来の方法では、正確にラマンスペクトルを解析し、結晶性を管理することは難しい。
以上のように、従来の方法では、多結晶状態や非単結晶状態の結晶シリコン膜の結晶性をラマン分光法によって正確に評価及び解析していくことは難しいという課題がある。
本発明は、上記従来の課題を解決すべくなされたものであり、移動度のばらつきもなく高移動度の特性を有する結晶性半導体膜の結晶性を正確に評価できる結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトを提供することを目的とする。
上記目的を達成するために、本発明に係る結晶性評価方法の一態様は、基板上に形成された半導体膜の結晶性を評価する結晶性評価方法であって、前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、前記第1フィッティング波形のピーク値を抽出する第3工程と、抽出した前記ピーク値を用いて、ローレンツ関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、前記第4工程の前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、前記第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する第6工程と、を含む。
本発明によれば、移動度のばらつきもなく高移動度の特性を有する結晶性半導体膜の結晶性を正確に評価できる結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトを実現することができる。
本発明に係る結晶性評価方法の第一態様は、基板上に形成された半導体膜の結晶性を評価する結晶性評価方法であって、前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、前記第1フィッティング波形のピーク値を抽出する第3工程と、抽出した前記ピーク値を用いて、ローレンツ関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、前記第4工程の前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、前記第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する第6工程と、を含む。
この構成によれば、移動度のばらつきもなく高移動度の特性を有する結晶性半導体膜の結晶性を正確に評価できる結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトを実現することができる。
ここで、前記第6工程では、前記第5工程で出力された前記ピーク値、半値幅、または前記ピーク値を示す波長と、ルックアップテーブルに予め保存されている参照ピーク値、参照半値幅、または参照ピーク値を示す波長と比較することにより、前記半導体膜の結晶性を評価し、前記ルックアップテーブルには、前記参照ピーク値、前記参照半値幅、または前記参照ピーク値を示す波長として、前記第1工程より前に、結晶性半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形を、ローレンツ関数を用いてフィッティングして得られた第3フィッティング波形のピーク値、半値幅または前記ピーク値を示す波長が予め保存されており、前記ルックアップテーブルには、結晶粒径、結晶粒の存在比率及び移動度を含む当該結晶性半導体膜の結晶性の評価が、前記参照ピーク値、前記参照半値幅、または前記参照ピーク値を示す波長と紐付けられて保存されているとしてもよい。
また、本発明に係る結晶性評価方法の一態様は、基板上に形成された半導体膜の結晶性を評価する結晶性評価方法であって、前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、前記第1フィッティング波形のピーク値を抽出する第3工程と、抽出した前記ピーク値を用いて、ローレンツ関数を用いて記述されるラマンスペクトル関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ラマンスペクトル関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、前記第4工程の前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、前記第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する第6工程と、を含み、前記第4工程では、Ic(ω)を結晶性シリコン成分のラマンバンド、Iμc(ω)を微結晶シリコン成分のラマンバンド、Ia(ω)をアモルファスシリコン成分のラマンバンド、σcを結晶性シリコン成分の体積分率、σmcを微結晶シリコン成分の体積分率、σaをアモルファスシリコン成分の体積分率とし、(式A)で表現されるラマンピーク波形解析モデルを作成する工程と、前記結晶性シリコン成分のラマンバンド、微結晶性シリコン成分のラマンバンド、及びアモルファスシリコン成分のラマンバンドを、Lcをフォノンコヒーレンス長、aを格子定数、Γ0を単結晶半導体のラマンピークの半値幅、Cを規格化定数として、(式B)及び(式C)に示すラマンスペクトル関数を記述する工程とを含む。
また、前記第6工程では、前記半値幅が5.0cm-1~6.0cm-1であるか否かを判定することにより、前記半導体膜の結晶性を評価するとしてもよい。
また、記半導体膜はシリコンで構成されており、前記第6工程では、前記半値幅と単結晶シリコンのラマンバンドの半値幅の比が、1.5~1.8であるか否かを判定することにより、前記半導体膜の結晶性を評価するとしてもよい。
また、前記半導体膜はシリコンで構成されており、前記第6工程では、前記半値幅と前記単結晶シリコンのラマンバンドの半値幅の差が1.8cm-1~2.4cm-1であるか否かを判定することにより、前記半導体膜の結晶性を評価するとしてもよい。
また、前記第6工程では、前記ピーク値と結晶シリコンのラマンバンド半値幅との比が0.1~0.2であるか否かを判定することにより、前記半導体膜の結晶性を評価するとしてもよい。
また、上記の結晶性評価方法を用いて、前記結晶性半導体膜の結晶性を評価することにより、所定の結晶性半導体膜の結晶性を示す前記結晶性半導体膜を選別する。
また、本発明に係る測定装置の一態様は、基板上に形成された半導体膜の結晶性を評価する結晶性評価装置であって、前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する測定部と、ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第1生成部と、前記第1フィッティング波形のピーク値を抽出する抽出部と、抽出した前記ピーク値を用いて、ローレンツ関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第2生成部と、前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する出力部と、前記出力部で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する評価部とを備える。
また、本発明に係るコンピュータソフトの一態様は、コンピュータ読み取り可能記録媒体に記録された結晶性半導体膜の結晶性を評価するコンピュータソフトであって、上記態様の結晶性評価方法をコンピュータに実行させることにより、前記半導体膜の結晶性の評価を出力するプログラムが組み込まれている。
(実施の形態1)
以下、本発明に係る薄膜トランジスタ装置及びその製造方法について、実施の形態に基づいて説明するが、本発明は、請求の範囲の記載に基づいて特定される。よって、以下の実施の形態における構成要素のうち、請求項に記載されていない構成要素は、本発明の課題を達成するのに必ずしも必要ではないが、より好ましい形態を構成するものとして説明する。なお、各図は模式図であり、必ずしも厳密に図示したものではない。
以下、本発明に係る薄膜トランジスタ装置及びその製造方法について、実施の形態に基づいて説明するが、本発明は、請求の範囲の記載に基づいて特定される。よって、以下の実施の形態における構成要素のうち、請求項に記載されていない構成要素は、本発明の課題を達成するのに必ずしも必要ではないが、より好ましい形態を構成するものとして説明する。なお、各図は模式図であり、必ずしも厳密に図示したものではない。
まず、本発明の実施の形態に係る薄膜トランジスタ装置100の構成について、図1を用いて説明する。図1は、本発明の実施の形態1に係る薄膜トランジスタ装置の構成を模式的に示す断面図である。
図1に示す薄膜トランジスタ装置100は、チャネル保護型でボトムゲート型の薄膜トランジスタであって、基板101と、基板101上に形成されたゲート電極102と、ゲート電極102上に形成されたゲート絶縁膜103と、ゲート絶縁膜103上に形成された結晶シリコン薄膜104と、結晶シリコン薄膜104上に形成された非晶質シリコン薄膜105と、非晶質シリコン薄膜105上に形成された絶縁層107と、非晶質シリコン薄膜105上に絶縁層107を挟んで形成されたソース電極108S及びドレイン電極108Dとを具備する。さらに、本実施の形態における薄膜トランジスタ装置100は、結晶シリコン薄膜104の上方において、非晶質シリコン薄膜105とソース電極108S又はドレイン電極108Dとの間に形成された一対のコンタクト層106を備える。以下、本実施の形態に係る薄膜トランジスタ装置100の各構成要素について詳述する。
基板101は、例えば、石英ガラス、無アルカリガラス又は高耐熱性ガラス等のガラス材料からなるガラス基板である。なお、ガラス基板の中に含まれるナトリウムやリン等の不純物が結晶シリコン薄膜104に侵入することを防止するために、基板101上にシリコン窒化膜(SiNx)、酸化シリコン(SiOy)又はシリコン酸窒化膜(SiOyNx)等からなるアンダーコート層を形成してもよい。また、アンダーコート層は、レーザアニールなどの高温熱処理プロセスにおいて、基板101への熱の影響を緩和させる役割を担うこともある。アンダーコート層の膜厚は、例えば、100nm~2000nm程度である。
ゲート電極102は、基板101上に所定形状でパターン形成される。ゲート電極102は、導電性材料及びその合金等の単層構造又は多層構造とすることができる。ゲート電極102は、例えば、モリブデン(Mo)、アルミニウム(Al)、銅(Cu)、タングステン(W)、チタン(Ti)、クロム(Cr)、及びモリブデンタングステン(MoW)等によって構成される。ゲート電極102の膜厚は、例えば20nm~500nm程度である。なお、レーザアニールなどの高温プロセスを用いる場合、ゲート電極材料としては、モリブデンやタングステンなどの高融点金属からなる材料を用いることが好ましい。
ゲート絶縁膜103は、ゲート電極102上に形成される。ゲート絶縁膜103は、本実施の形態では、ゲート電極102を覆うように基板101上の全面に形成される。ゲート絶縁膜103は、例えば、酸化シリコン(SiOy)、窒化シリコン(SiNx)、シリコン酸窒化膜(SiOyNx)、酸化アルミニウム(AlOz)又は酸化タンタル(TaOw)の単層膜又はこれらの積層膜によって構成される。ゲート絶縁膜103の膜厚は、例えば50nm~300nmである。
なお、本実施の形態では、チャネル層として結晶シリコン薄膜104が含まれているので、チャネル層との界面部分のゲート絶縁膜103としては酸化シリコンを用いることが好ましい。これは、薄膜トランジスタ装置100における良好な閾値電圧特性を維持、及び、高い移動度を実現するためには結晶シリコン薄膜104とゲート絶縁膜103との界面状態を良好なものにすることが好ましく、これには酸化シリコンが適しているからである。
結晶シリコン薄膜104は、本発明の半導体膜に相当し、ゲート絶縁膜103上に形成される半導体膜からなる第1チャネル層であって、ゲート電極102の電圧によってキャリアの移動が制御される領域である所定のチャネル領域を有する。チャネル領域は、ゲート電極102の上方の領域であり、チャネル領域の電荷移動方向の長さはゲート長に対応する。結晶シリコン薄膜104は、例えば、非結晶性の非晶質シリコン(アモルファスシリコン)を結晶化することによって形成することができる。
ここで、結晶シリコン薄膜104における結晶シリコンの平均結晶粒径は、50nm~300nm程度である。結晶シリコン薄膜104の膜厚は、例えば20nm~100nm程度である。また、結晶シリコン薄膜104が示す結晶性を次のように表すことができる。すなわち、結晶シリコン薄膜104の固有のフォノンモードに対応するラマンバンド半値幅(以下ラマン半値幅とも表現)は、5.0cm-1~6.0cm-1である。ここで、結晶シリコン薄膜104の固有のフォノンモードとは、TO(Transverse Optical)フォノンモードである。
また、結晶シリコン薄膜104が示す結晶性について別の表現を用いてもよい。例えば、結晶シリコン薄膜104のラマン半値幅と単結晶シリコンのラマン半値幅との比は、1.5~1.8であるとしてもよい。または、結晶シリコン薄膜104のラマン半値幅と単結晶シリコン基板のラマン半値幅の差は、1.8cm-1~2.4cm-1であるとしてもよい。さらに、結晶シリコン薄膜104のラマンバンドのピーク値と、多結晶シリコン薄膜のラマン半値幅との比(ピーク値/ラマン半値幅)は、0.1~0.2であるとしてもよい。ここで、結晶シリコン薄膜104のラマンバンドのピーク位置は、516cm-1~518cm-1であり、単結晶シリコン(c-Si)のラマン半値幅の値は、3.4cm-1である。
結晶シリコン薄膜104の電界効果移動度は、結晶シリコン薄膜104が上記のように構成されることで、20cm2/VS~50cm2/VSとなっている。
非晶質シリコン薄膜105は、チャネル領域を含む結晶シリコン薄膜104上に形成される第2チャネル層である。本実施の形態における非晶質シリコン薄膜105は、真性アモルファスシリコン膜によって構成される。なお、本実施の形態における非晶質シリコン薄膜105の膜厚は、例えば10nm以上40nm以下である。この非晶質シリコン薄膜105の役割は、トランジスタ動作時におけるドレイン端での電界集中を緩和させることである。つまりこの非晶質シリコン薄膜105は、電界緩和層として機能する。
絶縁層107は、チャネル層(結晶シリコン薄膜104及び非晶質シリコン薄膜105)を保護する。絶縁層107は、一対のコンタクト層106を形成するときのエッチング処理時において、非晶質シリコン薄膜105がエッチングされてしまうことを防止するためのチャネルエッチングストッパ(CES)層として機能する。絶縁層107は、チャネル領域を含む結晶シリコン薄膜104の上方であって非晶質シリコン薄膜105の上に形成される。
また、絶縁層107は、シリコン、酸素及びカーボンを含む有機材料を主として含有する有機材料からなる有機材料層、あるいは、酸化シリコン(SiOx)又は窒化シリコン(SiNy)等の無機材料からなる無機材料層である。なお、絶縁層107は、絶縁性を有し、一対のコンタクト層106同士は電気的に接続されていない。
一対のコンタクト層106は、不純物を高濃度に含む非晶質半導体膜からなり、結晶シリコン薄膜104及び非晶質シリコン薄膜105の上方に絶縁層107を介して形成される。一対のコンタクト層106は、例えば、アモルファスシリコンに不純物としてリン(P)をドーピングしたn型半導体層であって、1×1019[atm/cm3]以上の高濃度の不純物を含むn+層である。なお、P型のTFTを作製する場合、コンタクト層106は、ボロン(B)などの不純物をドープしたP型コンタクト層を形成すればよい。
一対のコンタクト層106は、絶縁層107上において所定の間隔をあけて対向配置されている。一対のコンタクト層106のそれぞれは、絶縁層107の上面から非晶質シリコン薄膜105までを跨るようにして形成されている。本実施の形態において、一対のコンタクト層106のうちの一方は、絶縁層107の一方の端部及び非晶質シリコン薄膜105に跨るようにして形成されており、絶縁層107の一方の端部における上部と側面、及び、絶縁層107の一方の側面側領域における非晶質シリコン薄膜105の上面を覆うように形成される。また、一対のコンタクト層106のうちの他方は、絶縁層107の他方の端部及び非晶質シリコン薄膜105に跨るようにして形成されており、絶縁層107の他方の端部における上部と側面、及び、絶縁層107の他方の側面側領域における非晶質シリコン薄膜105の上面を覆うように形成される。なお、コンタクト層106の膜厚は、例えば5nm~100nmとすることができる。
本実施の形態における一対のコンタクト層106は、非晶質シリコン薄膜105とソース電極108S及びドレイン電極108Dとの間に形成されているが、非晶質シリコン薄膜105の側面及び結晶シリコン薄膜104の側面には形成されていない。一対のコンタクト層106は、非晶質シリコン薄膜105及び結晶シリコン薄膜104と面一に形成されている。
なお、一対のコンタクト層106は、下層の低濃度の電界緩和層(n-層)と上層の高濃度のコンタクト層(n+層)との2層から構成されてもよい。低濃度の電界緩和層には1×1017[atm/cm3]程度のリンがドーピングされている。上記2層はCVD(Chemical Vapor Deposition)装置において連続的に形成することができる。
一対のソース電極108S及びドレイン電極108Dは、結晶シリコン薄膜104及び非晶質シリコン薄膜105の上方において、所定の間隔をあけて対向配置されるとともに一対のコンタクト層106上に当該一対のコンタクト層106と面一に形成されている。
ソース電極108Sは、一方のコンタクト層106を介して、絶縁層107の一方の端部(一端部)及び非晶質シリコン薄膜105に跨るようにして形成されている。また、ドレイン電極108Dは、他方のコンタクト層106を介して、絶縁層107の他方の端部(他端部)及び非晶質シリコン薄膜105に跨るようにして形成されている。
本実施の形態において、ソース電極108S及びドレイン電極108Dは、それぞれ導電性材料又はこれらの合金等からなる単層構造又は多層構造とすることができ、例えば、アルミニウム(Al)、モリブデン(Mo)、タングステン(W)、銅(Cu)、チタン(Ti)又はクロム(Cr)等の材料により構成される。本実施の形態では、ソース電極108S及びドレイン電極108Dは、MoW/Al/MoWの三層構造によって形成されている。なお、ソース電極108S及びドレイン電極108Dの膜厚は、例えば、100nm~500nm程度とすることができる。
以上のように、薄膜トランジスタ装置100は構成される。
この薄膜トランジスタ装置100では、チャネル層として構成される結晶シリコン薄膜104は、固有のフォノンモードに対応するラマンバンドの半値幅が、5.0cm-1~6.0cm-1を満たし、かつ、平均結晶粒径が約50nm~300nmを満たしている。
それにより、この薄膜トランジスタ装置100は、移動度のばらつきもなく高移動度の特性を有する結晶シリコン薄膜をチャネル層として有することができる。
なお、薄膜トランジスタ装置100は、後述する製造工程において、本発明の結晶性評価方法、結晶性評価装置またはそのコンピュータソフトによって、選別された結晶シリコン薄膜104を用いて形成される。結晶性評価方法等は後述するため、ここでは説明を省略する。後述する製造工程において、本発明の結晶性評価方法等を用いて、少なくとも固有のフォノンモードに対応するラマンバンドの半値幅が、5.0cm-1~6.0cm-1を満たす結晶シリコン薄膜104が選別される。
次に、本発明の実施の形態1に係る薄膜トランジスタ装置100の製造方法について、図2A~図2Kを用いて説明する。図2A~図2Kは、本発明の実施の形態1に係る薄膜トランジスタ装置の製造方法における各工程の構成を模式的に示す断面図である。
まず、図2Aに示すように、基板101を準備する。基板101としては、例えば、ガラス基板を用いる。なお、ゲート電極102を形成する前に、プラズマCVD等によって基板101上にシリコン窒化膜、シリコン酸化膜、及びシリコン酸窒化膜などからなるアンダーコート層を形成するとしてもよい。
次に、図2Bに示すように、基板101の上方に所定形状のゲート電極102をパターン形成する。例えば、基板101上に全面にモリブデンタングステン(MoW)等からなるゲート金属膜をスパッタによって成膜する。そして、フォトリソグラフィ及びウェットエッチングを施すことにより、ゲート金属膜をパターニングして所定形状のゲート電極102を形成する。MoWのウェットエッチングは、例えば、リン酸(HPO4)、硝酸(HNO3)、酢酸(CH3COOH)及び水を所定の配合で混合した薬液を用いて行う。
次に、図2Cに示すように、基板101の上方にゲート絶縁膜103を形成する。例えば、ゲート電極102を覆うようにして、基板101の上方の全面に、酸化シリコンからなるゲート絶縁膜103をプラズマCVD等によって成膜する。ここで、酸化シリコンは、例えば、シランガス(SiH4)と亜酸化窒素ガス(N2O)とを所定の濃度比で導入することで成膜することができる。
次に、図2Dに示すように、ゲート絶縁膜103の上に、結晶性シリコンからなる結晶シリコン薄膜104を形成する。具体的には、まず、ゲート絶縁膜103上に、例えばアモルファスシリコン(非晶質シリコン)からなる非晶質シリコン薄膜をプラズマCVD等によって成膜し、脱水素アニール処理を行った後に、非晶質シリコン薄膜をレーザアニールして結晶化させることにより結晶シリコン薄膜104を形成する。なお、非晶質シリコン薄膜は、例えば、シランガス(SiH4)と水素ガス(H2)とを所定の濃度比で導入することで成膜することができる。また、脱水素アニール処理は、例えば、450℃~550℃で、5分~1時間程度行えばよい。
なお、本実施の形態では、グリーンレーザを用いたレーザアニールによって非晶質シリコン薄膜を結晶化させたが、結晶化の方法としては、波長が370nm~900nm程度のパルスレーザを用いたレーザアニール法、波長が370nm~900nm程度の連続発振レーザを用いたレーザアニール法を用いるとしてもよい。
その後、結晶シリコン薄膜104に対して水素プラズマ処理を行うことにより、結晶シリコン薄膜104のシリコン原子に対して水素化処理を行う。水素プラズマ処理は、例えばH2、H2/アルゴン(Ar)等の水素ガスを含むガスを原料として高周波(RF)電力により水素プラズマを発生させて、当該水素プラズマを結晶シリコン薄膜104に照射することにより行われる。この水素プラズマ処理によって、シリコン原子のダングリングボンド(欠陥)が水素終端され、結晶シリコン薄膜104の結晶欠陥密度が低減して結晶性が向上する。
ここで、本実施の形態では、本発明の結晶性評価方法等により、所望の特性を有する結晶シリコン薄膜104を選別する。具体的には、まず、本発明の結晶性評価方法等により、結晶シリコン薄膜104の結晶性を示す値(ピーク強度、半値幅、ラマンシフト量など)を評価する。続いて、取得した結晶シリコン薄膜104の結晶性を示す値(ピーク強度、半値幅、ラマンシフト量など)に基づき、所望の特性を有する結晶シリコン薄膜104を選別する。例えば、好ましい膜質条件すなわち結晶シリコン薄膜104の好ましい結晶性を示す値として、結晶シリコン薄膜の固有のフォノンモードに対応するラマンバンドの半値幅が5.0cm-1~6.0cm-1を満たすかを検査する。そして、検査の際、上記条件をクリアした結晶シリコン薄膜104のみを選別する。このようにして、所望の特性として移動度のばらつきもなく高移動度の特性を有する結晶シリコン薄膜104のみを選別して後の工程に送ることができる。なお、このように選別された結晶シリコン薄膜104の平均結晶粒径は、50nm~300nm程度である。
また、移動度のばらつきもなく高移動度の特性を有する結晶シリコン薄膜104のみを選別する方法としては、上記に限られない。すなわち、結晶シリコン薄膜104の結晶性を示す値として、結晶シリコン薄膜104のラマン半値幅と単結晶シリコンのラマン半値幅との比が1.5~1.8を満たすものを選別するとしてもよいし、結晶シリコン薄膜104のラマン半値幅と単結晶シリコン基板のラマン半値幅の差が、1.8cm-1~2.4cm-1を満たすものを選別するとしてもよい。また、結晶シリコン薄膜104のラマンバンドのピーク値と、多結晶シリコン薄膜のラマン半値幅との比(ピーク値/ラマン半値幅)が、0.1~0.2を満たすものを選別するとしてもよい。ここで、結晶シリコン薄膜104のラマンバンドのピーク位置は、516cm-1~518cm-1であり、単結晶シリコン(c-Si)のラマン半値幅の値は、3.4cm-1である。
次に、図2Eに示すように、結晶シリコン薄膜104上に、非晶質シリコン薄膜105を形成する。具体的には、結晶シリコン薄膜104を形成した後に、プラズマCVD等を用いて、所定の成膜条件(形成条件)によってアモルファスシリコン膜からなる非晶質シリコン薄膜105を成膜する。
次に、図2Fに示すように、非晶質シリコン薄膜105上に、絶縁層107を形成するための絶縁層形成用膜107aを形成する。絶縁層形成用膜107aは、無機材料を用いて形成される。
例えば、絶縁層形成用膜107aが酸化シリコン等の無機材料によって形成される場合、絶縁層形成用膜107aの上に、所定形状の絶縁層107を規定するフォトマスクとして、所定幅のレジスト(不図示)を形成する。
次に、レジストをマスクとしてドライエッチングを施すことによって、図2Gに示すように、絶縁層形成用膜107aをパターニングして所定形状の絶縁層107を形成する。次いで、絶縁層107上に形成されているレジストを除去する。これにより、絶縁層107の上面が露出する。
次に、図2Hに示すように、絶縁層107を覆うようにして非晶質シリコン薄膜105上に、コンタクト層106となるコンタクト層用膜106aを形成する。具体的に、絶縁層107の上面から非晶質シリコン薄膜105の平坦部までを跨るようにして、例えばプラズマCVDによって、リン等の5価元素の不純物をドープしたアモルファスシリコンからなるコンタクト層用膜106aを成膜する。
なお、コンタクト層用膜106aは低濃度の電界緩和層と高濃度のコンタクト層との2層から構成されてもよい。低濃度の電界緩和層は1×1017[atm/cm3]程度のリンをドーピングすることによって形成することができる。上記2層はCVD装置において連続的に形成することができる。
次に、図2Iに示すように、コンタクト層用膜106aを覆うようにして、ソース電極108S及びドレイン電極108Dとなるソースドレイン金属膜108を形成する。例えば、スパッタによって、MoW/Al/MoWの三層構造のソースドレイン金属膜108を成膜する。
その後、図示しないが、所定形状のソース電極108S及びドレイン電極108Dを形成するために、ソースドレイン金属膜108上にレジスト材料を塗布し、露光及び現像を行って、所定形状にパターニングされたレジストを形成する。
次に、このレジストをマスクとしてウェットエッチングを施してソースドレイン金属膜108をパターニングすることにより、図2Jに示すように、所定形状のソース電極108S及びドレイン電極108Dを形成する。なお、このとき、コンタクト層用膜106aがエッチングストッパとして機能する。その後、ソース電極108S及びドレイン電極108D上のレジストを除去する。また、ソース電極108S及びドレイン電極108Dをマスクとしてドライエッチングを施すことにより、コンタクト層用膜106aをパターニングして所定形状の一対のコンタクト層106を形成する。なお、ドライエッチングの条件としては、塩素系ガスを用いることができる。
このようにして、本発明の実施の形態に係る薄膜トランジスタ装置100を製造することができる。
なお、その後、図2Kに示すように、ソース電極108S及びドレイン電極108Dの上から全体を覆うようにして、SiN等の無機材料からなるパッシベーション膜109を形成してもよい。
また、上記では、説明を簡便にするため、一つの薄膜トランジスタ装置の製造方法について説明したが、それに限らない。一つの薄膜トランジスタ装置ではなく、複数の薄膜トランジスタ装置をアレイ状に製造するとしてもよい。その場合には、図2Dに示す工程では、アレイ状に形成された複数の結晶シリコン薄膜104うちの一つの結晶シリコン薄膜104を代表して検査すればよい。そして、検査後、上記条件をクリアした結晶シリコン薄膜104を含むアレイのみを選別するとすればよい。それにより、複数の薄膜トランジスタ装置を、ばらつきのない高移動度の特性を有する結晶シリコン薄膜で構成することができるので、この薄膜トランジスタ装置を大画面に用いられる有機ELパネル等に用いることができるという効果を奏する。
続いて、図2Dにおいて、本発明の結晶性評価方法等を用いて、所望の特性を有する結晶シリコン薄膜104を選別する方法について説明する。具体的には、本発明の結晶性評価方法、結晶性評価装置、またはそのコンピュータソフトを用いて、結晶シリコン薄膜104の結晶性を示す値(ピーク強度、半値幅、ラマンシフト量など)を評価する。そして、所望の特性として移動度のばらつきもなく高移動度の特性を有する結晶シリコン薄膜104のみを選別する方法について説明する。
図3は、本発明の実施の形態1における結晶シリコン薄膜の結晶性評価に用いるラマン分光装置200の概略図である。つまり、例えば結晶シリコン薄膜104における固有のフォノンモードに対応するラマン半値幅などの結晶シリコン薄膜104の評価(検査)は、例えば図3に示すラマン分光装置を用いて行われる。以下、図3に示すラマン分光装置200について説明する。
図3に示すラマン分光装置200は、光源201と、アッテネーター202と、フィルター203と、ミラー204と、ビームスプリッター205と、対物レンズ206と、ステージ208と、スリット209と、分光器210と、検出器211とを備え、試料207に対してラマン分光測定を行う。ここで、試料207は、上述の製造方法にてゲート電極上に結晶シリコン薄膜が形成されたものまたはそれに相当するものである。
光源201には、波長470nm~700nm程度レーザ光が用いられる。例えば、光源201は、波長514.5nmのアルゴンイオンレーザ、波長532nmのYAGレーザなどが用いられる。
アッテネーター202は、光源201から出射されたレーザ光を、試料207に影響が生じない程度に減光する。
フィルター203は、アッテネーター202で減光された光を、所望の波長以外の光を徐光して通過させる。
なお、本実施の形態では、レーザパワーは、光源201及びアッテネーター202に構成される各対物レンズの倍率によって、試料207のスペクトルの変化がないように調整している。例えば、各対物レンズの倍率を50倍とする場合、試料207上におけるレーザパワーを1mW~20mWに調整する。
ミラー204は、フィルター203を通過した光の進行方向を制御する。
ビームスプリッター205は、ミラー204により進行方向が制御された光を、顕微鏡システムの対物レンズ206まで導く。また、ビームスプリッター205は、試料207の試料面で散乱した散乱光であって対物レンズ206で集光された散乱光を、スリット209を介して分光器210に導く。
対物レンズ206は、ビームスプリッター205を介して導かれた光を集光し、ステージ208上の試料207に照射する。ここで、対物レンズ206は、その倍率を変化させることで、試料207面に照射されるレーザ光の照射スポット(空間分解能)を変化させることができる。例えば、この対物レンズ206の倍率を100倍とした場合、試料207の試料面でのレーザ光の照射スポット径を、約0.6μmとする。
また、対物レンズ206は、試料207の試料面で散乱した散乱光を集光して、ビームスプリッター205に導く。
スリット209は、その幅(スリット幅)により通過する光のスペクトル分解能を向上させる。ここで、スリット幅は、狭い場合にはスペクトル分解能を向上させるものの、散乱光の強度が減少する。このため、分解能とS/Nの兼ね合いで、装置毎に適切に設定する必要がある。本実施の形態では、例えば、20μm~200μm程度に設定される。
分光器210は、光を波長の違いに従って分解し、スペクトル(分散された光)を得るための装置である。分光器210は、スリット209を介して導かれた光を分散する。分光器210は、一般的に、シングルモノクロメーターが用いられる。分光器210に構成されるグレーティングの数を増加させると、分解能は向上するものの、スペクトルの取得領域が減少し、散乱光強度が減少する。そのため、測定対象によってグレーティングの数(溝数)を適切に選択する必要がある。本実施の形態では、例えば1800G/mm~3000G/mm程度の溝数のものを用いる。
検出器211は、分光器210で分散された光を、シグナルとして検出することで、ラマンスペクトルを得る。検出器211は、例えば光電子倍増管やCCD(Charge Coupled Device)を用いて構成される。ここで、分光器210と検出器211との距離は、焦点距離と呼ばれる。焦点距離が長いと、スペクトルの波数分解能は向上するものの、散乱光強度が減衰する。そのため、本実施の形態では、焦点距離250mm~500mm程度としている。
以上のように、ラマン分光装置200は構成される。
次に、上記ラマン分光装置200を用いて得られたラマンスペクトルを解析する方法について説明する。
図4は、本発明の実施の形態1におけるラマンスペクトルの解析方法を説明するためのフローチャートである。図5は、本発明の実施の形態1における結晶シリコン膜のラマンスペクトルとその解析結果を示す図である。
まず、ラマン分光装置200を用いて、ラマンスペクトルを測定する(S201)。具体的には、半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する。より具体的には、結晶シリコン薄膜の固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する。ここで、ラマン分光法は、ラマンシフトが物質に固有であることを利用する測定方法であり、試料にレーザ光を照射し、発生するラマン散乱光を測定することによって、非破壊・非接触測定で微視的な物性を知ることができる。測定条件としては、測定位置をゲート電極上の結晶シリコン薄膜とし、励起波長を532nmとする。また、測定スポット径は1.3μmΦであり、波数分解能は1.5cm-1である。
結晶シリコン薄膜の固有のフォノンモードに対応するラマンバンドのピークは、516cm-1~518cm-1に観測される。なお、結晶シリコン膜は、450cm-1~550cm-1の領域にシリコンの固有のフォノンに対応するラマンバンドのピークが観測され、微結晶シリコン膜の固有のフォノンに対応するラマンバンドのピークは500cm-1~510cm-1付近、a-Si膜の固有のフォノンに対応するラマンバンドのピークは480cm-1付近に観測される。本実施の形態では、測定したスペクトル(ラマンスペクトル)のうち、結晶シリコン薄膜の固有のフォノンモードに対応するラマンバンドのピーク波形に対して解析を行っている。
次に、測定したラマンスペクトルのベースラインを補正する(S202)。具体的には、結晶シリコン薄膜の固有のフォノンモードに対応するラマンバンドのピーク波形を測定後、測定したピーク波形のベースラインを補正する。例えば、ラマンスペクトルを解析した領域に対して直線近似を行なう方法によりベースラインの補正を行う。ラマンスペクトルは、サンプル(ここでは試料207)や測定環境の影響を受けて、ベースラインが傾斜してしまうからである。なお、ベースラインが傾斜していない場合もあり、その場合には、ベースラインの補正を行う必要はない。
次に、ガウス関数を用いて測定したラマンスペクトルのフィッティングを行う(S203)。具体的には、ガウス関数を用いて、測定したラマンバンドのピーク波形をフィッティングすることで、ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する。そして、第1フィッティング波形のピーク値を抽出する。より具体的には、ガウス関数(ガウス分布)を用いてラマンピーク波形解析モデルを生成し、生成したラマンピーク波形解析モデルを高さ方向についてフィッティング(ラマンスペクトルの再現)を行う。そして、フィッティングされたラマンピーク波形解析モデル(第1フィッティング波形)の強度(ピーク値)を抽出する。本実施の形態では、ガウス関数(ガウス分布)を用いて結晶シリコン薄膜のラマンバンドのラマンピーク波形解析モデルを生成する。そして、ベースラインを補正したラマンスペクトルのうち、結晶シリコン薄膜の成分すなわち516cm-1~518cm-1に観察されるラマンバンドのピークに対してフィッティングを行い、強度(ピーク値)を抽出する。
次に、抽出したピーク値を用いて、ローレンツ関数によりラマンスペクトルのフィッティングを行う(S204)。
具体的には、抽出したピーク値を用いて、ローレンツ関数によりラマンバンドのピーク波形をフィッティングすることで、ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する。より具体的には、ローレンツ関数を用いて、別途ラマンピーク波形解析モデルを生成し、生成したラマンピーク波形解析モデルを用いて、結晶シリコン薄膜のラマンバンドの幅方向についてフィッティングを行う。
つまり、本実施の形態では、ベースラインを補正した結晶シリコン薄膜のラマンバンドに対して、まず、ガウス関数から生成したラマンピーク波形解析モデルを用いてピーク値をフィッティングした後に、ローレンツ関数から生成したラマンピーク波形解析モデルを用いて、さらに幅方向に対してフィッティングを行う。その解析結果を示したものが図5である。
次に、S204でのラマンスペクトルのフィッティング結果から、パラメータを抽出して出力する。具体的には、第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する。より具体的には、スペクトル解析すなわちS204でフィティングして得られたラマンピーク波形解析モデルから、パラメータとして各成分におけるピーク位置、半値幅(ラマン半値幅)、ピーク値(ピーク強度)または体積分率(結晶化率)などを抽出して、出力する(S205)。
次に、例えば予めルックアップテーブルに保存されているパラメータとS205で出力されたパラメータとを比較し、結晶シリコン薄膜の結晶性を示す値を取得する(S206)。具体的には、出力されたピーク値、半値幅、またはピーク値を示す波長(ラマンシフト量)に基づき、結晶性半導体膜の結晶性を評価する。
より具体的には、S205で出力されたピーク値、半値幅、またはピーク値を示す波長(ラマンシフト量)と、ルックアップテーブルに予め保存されている参照ピーク値、参照半値幅、または参照ピーク値を示す波長(ラマンシフト量)と比較することにより、前記結晶性半導体膜の結晶性を評価する。
ここで、結晶シリコン薄膜の結晶性を示す値とは、例えば、結晶シリコン薄膜104のラマンバンドの半値幅(ラマン半値幅)である。また、結晶シリコン薄膜104のラマン半値幅と単結晶シリコンのラマン半値幅との比の値であってもよく、結晶シリコン薄膜104の半値幅と単結晶シリコン基板のラマン半値幅の差の値でもよい。また、例えば、結晶シリコン薄膜104のラマンバンドのピーク値と、多結晶シリコン薄膜のラマン半値幅との比(ピーク値/ラマン半値幅)の値であってもよい。
また、ルックアップテーブルには、参照ピーク値、参照半値幅、または参照ピーク値を示す波長として、S201より前に、結晶性半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形を、ローレンツ関数を用いてフィッティングして得られた第3フィッティング波形のピーク値、半値幅またはピーク値が予め保存されている。また、ルックアップテーブルには、結晶粒径、結晶粒の存在比率及び移動度を含む当該結晶性半導体膜の結晶性の評価が、参照ピーク値、参照半値幅、または参照ピーク値を示す波長と紐付けられて保存されている。
以上のようにして、ラマン分光装置200で得られたラマンスペクトルを解析して、結晶シリコン薄膜の結晶性を示す値を取得する。
なお、このラマン分光装置200を用いて得られたラマンスペクトルは、上記の評価方法を実行する評価装置により実行されるとしてもよい。その場合、評価装置は、測定部と、第1生成部と、抽出部と、第2生成部と、出力部と、評価部とを備えるとすればよい。ここで、測定部は、半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する。第1生成部は、ガウス関数を用いて、測定したラマンバンドのピーク波形をフィッティングすることで、ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する。抽出部は、第1フィッティング波形のピーク値を抽出する。第2生成部は、抽出したピーク値を用いて、ローレンツ関数によりラマンバンドのピーク波形をフィッティングすることで、ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する。評価部は、第2フィッティング波形のピーク値、半値幅、またはピーク値を示す波長を出力する出力部と、出力されたピーク値、半値幅、またはピーク値を示す波長に基づき、半導体膜の結晶性を評価する。
また、評価装置を構成する処理手段をステップとしてコンピュータに実行させるコンピータソフトとして実現したりしてもよい。つまり、上述した結晶性評価方法を行うプログラムが記録されたコンピュータソフトが組み込まれているコンピュータを実行することで、結晶性を評価してもよい。
次に、本発明の結晶性半導体膜の結晶性評価方法を用いることにより、結晶性半導体膜の結晶性を正確に評価できることについて説明する。
図6は、結晶性半導体膜の結晶性評価方法と半値幅の値のばらつきとの関係を示す図である。ここで、縦軸は、同程度に結晶化された組織を10点以上測定し、516cm-1~518cm-1に観察されるラマンバンドの半値幅(cm-1)のばらつきすなわちラマン半値幅ばらつきを示している。横軸は、測定したラマンスペクトルのラマン半値幅を評価する方法を示している。具体的には、図6に示す本願は、測定したラマンスペクトルをガウス関数でフィッティングし、ピーク値を得た後、得られたピーク値を初期値として、ローレンツ関数でフィッティングすることでラマン半値幅を得る評価方法を示している。一方、図6に示すGaussは、測定したラマンスペクトルをガウス関数のみでフィッティングしてラマン半値幅を得る評価方法を示している。図6に示すLorentsは、測定したラマンスペクトルをローレンツ関数のみでフィッティングしてラマン半値幅を得る評価方法を示している。また、図6に示すMixは、測定したラマンスペクトルをガウス関数とローレンツ関数を複合させた複合関数(Voit関数)でフィッティングしてラマン半値幅を得る評価方法を示している。
図6からわかるように、従来の評価方法(Mix、Gauss、Lorents)に比べると、本願の評価方法を用いると、得られたラマン半値幅のばらつきが小さいことがわかる。つまり、本願の評価方法を用いると、より正確なラマン半値幅(結晶シリコン薄膜の結晶性を示す値)を得ることができるのがわかる。
次に、本発明の実施の形態に係る薄膜トランジスタ装置100の結晶シリコン薄膜104における所望の結晶性を示す値(好ましい膜質条件)について説明する。
図7は、本発明の実施の形態1における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜のラマン半値幅との関係を示す図である。ここで、図7に示す各データ点は、上述の製造方法にてゲート電極上に結晶シリコン薄膜が形成された複数の試料207それぞれに対するものである。また、縦軸は、移動度(cm2/VS)を示しており、横軸は516cm-1~518cm-1に観察されるラマンバンドの半値幅(cm-1)すなわちラマン半値幅を示している。また、図8は、図7の移動度の絶対値のばらつきを示す図である。つまり、図8は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度(図7)の絶対値のばらつきと、その結晶シリコン薄膜のラマン半値幅との関係を示す図である。ここで、縦軸は、結晶シリコン薄膜の移動度のばらつき(%)(3σ/平均値×100)を示しており、横軸は、結晶シリコン薄膜のラマン半値幅(cm-1)を示している。
図8に示すように、移動度のばらつきが少ない範囲は、ラマン半値幅は、5.2cm-1~5.8cm-1を示す範囲F2であるのがわかる。
それにより、図7において、移動度のばらつきが比較的少ない範囲は、移動度が20cm2/VS~50cm2/VSを示す範囲F1であるのがわかる。つまり、ラマン半値幅が5.2cm-1~5.8cm-1を示す範囲F1では、移動度は20cm2/VS~50cm2/VSを示すことがわかる。
したがって、好ましい膜質条件として、結晶シリコン薄膜が、そのラマン半値幅として5.0cm-1~6.0cm-1を満たす場合に、所望の特性(結晶シリコン薄膜は移動度のばらつきもなく高移動度の特性)を有する。
このことからも、好ましい膜質条件として結晶シリコン薄膜のラマン半値幅が5.2cm-1~5.8cm-1を満たす場合に、結晶シリコン薄膜は所望の特性(移動度のばらつきもなく高移動度の特性)を有することがわかる。
これは、ラマン半値幅が5cm-1より小さい場合には、結晶シリコン薄膜の粒径が大きく(大粒径)なり、移動度のバラツキが大きくなると解することができる。一方、ラマン半値幅が6cm-1より大きい場合には、結晶シリコン薄膜の粒径は小さいものの、Explosiveの結晶状態(微結晶組織と部分的に溶融した組織の混晶)が混ざることで、移動度のバラツキが大きくなると解することができる。
以上のように、図2Dに示す薄膜トランジスタ装置100の製造工程では、図4のS206において、結晶シリコン薄膜の固有のフォノンモードに対応するラマン半値幅が、5.0cm-1~6.0cm-1を満たしているか否かを判定することにより、結晶性半導体膜の結晶性を評価する。そして、薄膜トランジスタ装置100では、上記条件を満たす結晶シリコン薄膜104が選別されてチャネル層として構成される。
なお、上記では、所望の特性(移動度のばらつきもなく高移動度の特性)を有する結晶シリコン薄膜の結晶性を示す値を、結晶シリコン薄膜のラマン半値幅を用いて示したが、それに限らない。結晶シリコン薄膜のラマン半値幅の単結晶シリコン(c-Si)のラマン半値幅に対する比で示すとしてもよいし、結晶シリコン薄膜のラマン半値幅の単結晶シリコンのラマン半値幅の差の値で評価するとしてもよい。以下、その例について図9及び図10を用いて説明する。
図9は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜のラマン半値幅の単結晶シリコン(c-Si)のラマン半値幅に対する比との関係を示す図である。ここで、縦軸は、移動度(cm2/VS)を示しており、横軸は、結晶シリコン薄膜のラマン半値幅の単結晶シリコン(c-Si)のラマン半値幅に対する比を示している。また、単結晶シリコン(c-Si)のラマン半値値は、3.4cm-1であり、ラマンシフトが520cm-1付近のラマンバンドの半値値である。
図9において、範囲F3は、移動度が20cm2/VS~50cm2/VSを示す範囲である。この範囲F3では、結晶シリコン薄膜のラマン半値幅の単結晶シリコン(c-Si)のラマン半値幅に対する比は、1.5~1.8を示す。
したがって、S206において、結晶シリコン薄膜のラマン半値幅の単結晶シリコン(c-Si)のラマン半値幅に対する比が、1.5~1.8を満たすか否かを判定することにより、所望の特性を有する結晶性半導体膜の結晶性か否かを評価する。そして、上記好ましい膜質条件を満たす場合に、結晶シリコン薄膜は所望の特性(移動度のばらつきもなく高移動度の特性)を有すると評価される。
図10は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜のラマン半値幅及び単結晶シリコン(c-Si)のラマン半値幅の差との関係を示す図である。ここで、縦軸は、移動度(cm2/VS)を示しており、横軸は結晶シリコン薄膜のラマン半値幅から単結晶シリコン(c-Si)のラマン半値幅を引いた値(cm-1)を示している。ここで、単結晶シリコン(c-Si)ののラマン半値幅の値は、3.4cm-1である。
図10において、範囲F4は、移動度が20cm2/VS~50cm2/VSを示す範囲である。この範囲F4では、結晶シリコン薄膜のラマン半値幅と単結晶シリコン(c-Si)のラマン半値幅との差は、1.8cm-1~2.4cm-1を示す。
したがって、S206において、結晶シリコン薄膜のラマン半値幅と単結晶シリコン(c-Si)のラマン半値幅との差が、1.8cm-1~2.4cm-1を満たすか否かを判定することにより、所望の特性を有する結晶性半導体膜の結晶性か否かを評価する。そして、上記好ましい膜質条件を満たす場合に、結晶シリコン薄膜は所望の特性(移動度のばらつきもなく高移動度の特性)を有すると評価される。
また、上記では、所望の特性(移動度のばらつきもなく高移動度の特性)を有する結晶シリコン薄膜の結晶性を示す値を、結晶シリコン薄膜のラマン半値幅を用いて算出した値を用いて示したが、それに限らない。以下、例示として、結晶シリコン薄膜のラマンバンドのピーク位置またはピーク値(ピーク強度)を用いる場合について説明する。
まず、図11を用いて、516cm-1~518cm-1にラマンバンドのピークが観察される結晶シリコン薄膜の移動度について示す。
図11は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜のピーク位置との関係を示す図である。ここで、縦軸は、ピーク位置(cm-1)を示しており、横軸は結晶シリコン薄膜の移動度(cm2/VS)を示している。
図11に示すように、516cm-1~518cm-1にラマンバンドのピークが観察される結晶シリコン薄膜では、~150cm2/VSの高移動度を有することがわかる。
次に、結晶シリコン薄膜のラマンバンドのピーク位置またはピーク値(ピーク強度)を用いた結晶シリコン薄膜104における好ましい膜質条件について説明する。
図12は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜の規格化されたピーク強度との関係を示す図である。ここで、縦軸は、多結晶シリコン薄膜の移動度(cm2/VS)を示しており、横軸は、移動度40cm2/VSにおける結晶シリコン薄膜のピーク強度で規格化されたピーク強度を示している。
図12に示すように、移動度が20cm2/VS~50cm2/VSを示す範囲では、結晶シリコン薄膜の規格化されたピーク強度は、0.5~1.2を示しているのがわかる。
したがって、S206において、結晶シリコン薄膜の規格化されたピーク強度が、0.5~1.2を満たすか否かを判定することにより、所望の特性を有する結晶性半導体膜の結晶性か否かを評価する。そして、上記好ましい膜質条件を満たす場合に、所望の特性(結晶シリコン薄膜は移動度のばらつきもなく高移動度の特性)を有すると評価される。
図13は、本実施の形態における製造方法によって形成された結晶シリコン薄膜の移動度と、その結晶シリコン薄膜の規格化されたピーク強度のラマン半値幅に対する比との関係を示す図である。ここで、縦軸は、結晶シリコン薄膜の移動度(cm2/VS)を示しており、横軸は、移動度40cm2/VSにおける結晶シリコン薄膜のピーク強度で規格化されたラマン半値幅を示している。
図13に示すように、移動度が20cm2/VS~50cm2/VSを示す範囲では、結晶シリコン薄膜の規格化されたラマン半値幅は、0.1~0.2を示す。
したがって、S206において、結晶シリコン薄膜の規格化されたピーク強度のラマン半値幅に対する比が0.1~0.2を満たすか否かを判定することにより、所望の特性を有する結晶性半導体膜の結晶性か否かを評価する。そして、上記好ましい膜質条件を満たす場合に、結晶シリコン薄膜は所望の特性(移動度のばらつきもなく高移動度の特性)を有すると評価される。
以上のように、本実施の形態によれば、本発明の結晶性評価方法等を用いて、所望の特性を有する結晶シリコン薄膜104を選別し、選別された結晶シリコン薄膜104をチャネル層として薄膜トランジスタ装置を構成する。それにより、所望の特性(移動度のばらつきもなく高移動度の特性)を有する結晶シリコン薄膜をチャネル層に用いる薄膜トランジスタ装置を実現することができる。
なお、本実施の形態の薄膜トランジスタ装置では、チャネル保護層が、非結晶質シリコン薄膜上にされているとして説明したがそれに限られない。結晶質シリコン薄膜上に形成され、チャネル保護層上に非晶質シリコン薄膜が形成されるとしてもよい。以下、それを変形例として説明する。
(変形例)
図14は、本発明の実施の形態1の変形例に係る薄膜トランジスタ装置の構成を模式的に示す断面図である。なお、図1と同様の要素には同一の符号を付しており、詳細な説明は省略する。
図14は、本発明の実施の形態1の変形例に係る薄膜トランジスタ装置の構成を模式的に示す断面図である。なお、図1と同様の要素には同一の符号を付しており、詳細な説明は省略する。
図14に示す薄膜トランジスタ装置150は、実施の形態に係る薄膜トランジスタ装置100に対して、非晶質シリコン薄膜155と絶縁層157との構成が異なる。
絶縁層157は、チャネル層(結晶シリコン薄膜104)を保護する。絶縁層157は、一対の非晶質シリコン薄膜155とコンタクト層156を形成するときのエッチング処理時において、非晶質シリコン薄膜155がエッチングされてしまうことを防止するためのチャネルエッチングストッパ(CES)層として機能する。絶縁層157は、チャネル領域を含む結晶シリコン薄膜104の上に形成される。なお、絶縁層157の材料等は、絶縁層107と同様であるため、説明を省略する。
一対の非晶質シリコン薄膜155は、チャネル領域を含む結晶シリコン薄膜104と絶縁層157との上方に形成される。一対の非晶質シリコン薄膜155は、絶縁層157上において所定の間隔をあけて対向配置されている。一対の非晶質シリコン薄膜155のそれぞれは、絶縁層157の上面から結晶シリコン薄膜104までを跨るようにして形成されている。本変形例において、一対の非晶質シリコン薄膜155のうちの一方は、絶縁層157の一方の端部及び結晶シリコン薄膜104に跨るようにして形成されており、絶縁層157の一方の端部における上部と側面、及び、絶縁層157の一方の側面側領域における結晶シリコン薄膜104の上面を覆うように形成される。また、一対の非晶質シリコン薄膜155のうちの他方は、絶縁層157の他方の端部及び結晶シリコン薄膜104に跨るようにして形成されており、絶縁層157の他方の端部における上部と側面、及び、絶縁層157の他方の側面側領域における結晶シリコン薄膜104の上面を覆うように形成される。なお、一対の非晶質シリコン薄膜155の材料等は、非晶質シリコン薄膜105と同様であるため、説明を省略する。
一対のコンタクト層156は、絶縁層157上において所定の間隔をあけて対向配置されている。一対のコンタクト層156のそれぞれは、非晶質シリコン薄膜155上に形成されている。なお、一対のコンタクト層156の材料等は、コンタクト層106と同様であるため、説明を省略する。
以上のように、薄膜トランジスタ装置150は構成される。
次に、以上のように構成される薄膜トランジスタ装置150の製造方法について説明する。図15A~図15Kは、本発明の実施の形態1の変形例に係る薄膜トランジスタ装置の製造方法における各工程の構成を模式的に示した断面図である。
図15A~図15Dは、図2A~図2Dと同じ工程であるため、説明を省略する。
次に、図15Eに示すように、結晶シリコン薄膜104上に、絶縁層157を形成するための絶縁層形成用膜157aを形成する。絶縁層形成用膜157aは、無機材料を用いて形成される。ここでは、例えば、絶縁層形成用膜157aが酸化シリコン等の無機材料によって形成されるとする。
次に、絶縁層形成用膜157aの上に、所定形状の絶縁層157を規定するフォトマスクとして、所定幅のレジストを形成する。その後、レジストをマスクとしてドライエッチングを施すことによって、絶縁層形成用膜157aをパターニングして所定形状の絶縁層157を形成する。次いで、絶縁層157上に形成されているレジストを除去する。これにより、図15Fに示すように、絶縁層157の上面を露出させる。
次に、図15Gに示すように、絶縁層157及び結晶シリコン薄膜104上に、非晶質シリコン薄膜155を形成する。具体的には、絶縁層157を形成した後に、プラズマCVD等を用いて、所定の成膜条件(形成条件)によってアモルファスシリコン膜からなる非晶質シリコン薄膜155を成膜する。
次に、図15Hに示すように、非晶質シリコン薄膜155上に、コンタクト層156となるコンタクト層用膜156aを形成する。具体的には、非晶質シリコン薄膜155上に、例えばプラズマCVDによって、リン等の5価元素の不純物をドープしたアモルファスシリコンからなるコンタクト層用膜156aを成膜する。
なお、コンタクト層用膜156aは低濃度の電界緩和層と高濃度のコンタクト層との2層から構成されてもよい。低濃度の電界緩和層は1×1017[atm/cm3]程度のリンをドーピングすることによって形成することができる。上記2層はCVD装置において連続的に形成することができる。
次に、図15Iに示すように、コンタクト層用膜156aを覆うようにして、ソース電極108S及びドレイン電極108Dとなるソースドレイン金属膜108を形成する。例えば、スパッタによって、MoW/Al/MoWの三層構造のソースドレイン金属膜108を成膜する。
その後、図示しないが、所定形状のソース電極108S及びドレイン電極108Dを形成するために、ソースドレイン金属膜108上にレジスト材料を塗布し、露光及び現像を行って、所定形状にパターニングされたレジストを形成する。
次に、図15Jに示すように、レジストをマスクとしてウェットエッチングを施してソースドレイン金属膜108をパターニングすることにより、所定形状のソース電極108S及びドレイン電極108Dを形成する。なお、このとき、コンタクト層用膜106aがエッチングストッパとして機能する。その後、ソース電極108S及びドレイン電極108D上のレジストを除去する。続いて、ソース電極108S及びドレイン電極108Dをマスクとしてドライエッチングを施すことにより、コンタクト層用膜156aと非晶質シリコン薄膜155をパターニングして所定形状の一対のコンタクト層156と非晶質シリコン薄膜155を形成する。なお、ドライエッチングの条件としては、塩素系ガスを用いることができる。
このようにして、本発明の実施の形態に係る薄膜トランジスタ装置150を製造することができる。
なお、その後、図15Kに示すように、ソース電極108S及びドレイン電極108Dの上から全体を覆うようにして、SiN等の無機材料からなるパッシベーション膜109を形成してもよい。
以上のように、本発明の結晶性評価方法等を用いて、所望の特性を有する結晶シリコン薄膜104を選別し、選別した結晶シリコン薄膜104をチャネル層として用いて薄膜トランジスタ装置を構成する。それにより、所望の特性(移動度のばらつきもなく高移動度の特性)を有する結晶シリコン薄膜をチャネル層に用いる薄膜トランジスタ装置を実現することができる。
このように、本実施の形態によれば、移動度のばらつきもなく高移動度の特性を有する結晶性半導体膜の結晶性を正確に評価できる結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトを実現することができる。
なお、本実施の形態の薄膜トランジスタ装置は、有機EL素子を用いた有機EL表示装置だけでなく、液晶表示装置等、アクティブマトリクス基板が用いられる他の表示装置にも適用することができる。また、このように構成される表示装置については、フラットパネルディスプレイとして利用することができ、テレビジョンセット、パーソナルコンピュータ、携帯電話などのあらゆる表示パネルを有する電子機器に適用することができる。
以上、本実施の形態に係る結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトについて、実施の形態及び変形例に基づいて説明したが、本発明に係る結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトは、上記の実施の形態及び変形例に限定されるものではない。
例えば、上記の実施の形態では、絶縁層(チャネル保護膜)を用いたチャネル保護型の薄膜トランジスタ装置を構成する結晶性半導体膜の評価について説明したが、本発明は、絶縁層(チャネル保護膜)を用いないチャネルエッチング型の薄膜トランジスタ装置を構成する結晶性半導体膜の評価にも適用することができる。
また、例えば、本実施の形態に係る結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトにおいて、抽出したピーク値を用いて、ローレンツ関数によりラマンスペクトルのフィッティングを行う(S204)としたがそれに限られない。ローレンツ関数そのものでなく、ローレンツ関数から記述される関数(例えば後述するラマンスペクトル関数)によりラマンスペクトルのフィッティングを行うとしてもよい。その場合、ラマンスペクトルに対してより再現性のあるフィッティング波形を得られる効果を奏する。
(実施の形態2)
以下、本発明の実施の形態2における半導体膜の結晶性評価方法(以下、膜質解析方法と記載)、について、図面を参照しながら具体的に説明する。
以下、本発明の実施の形態2における半導体膜の結晶性評価方法(以下、膜質解析方法と記載)、について、図面を参照しながら具体的に説明する。
本実施の形態において、結晶シリコン膜に対するラマン分光測定は、図3に示すラマン分光装置を用いて、試料307(不図示)に対して行う。
ここで、試料307は、ガラス基板上に、ベースコート層及び非結晶シリコン膜(a-Si膜)が形成され、その後に、非晶質シリコン膜を結晶化させることで結晶シリコン膜が形成されたものである。ベースコート膜としては、例えば、膜厚100nm~1μm程度のシリコン酸化膜やシリコン窒化膜などの熱伝導率の小さい膜が用いられている。非結晶シリコン膜(a-Si膜)は、例えば、膜厚20~200nm程度の膜をプラズマCVD法で堆積されている、非晶質シリコン膜を結晶化させる方法としては、レーザや熱を用いる。なお、レーザを用いて結晶化する場合(レーザー結晶化方法)においては、波長200~1000nm、パルス発振及び連続発振の光源で結晶化を行う。なお、レーザを用いて結晶化を行う前に、非晶質シリコン膜(a-Si膜)の突沸を防ぐために、400~600℃の温度で脱水素アニールを行うとしてもよい。
次に、ラマン分光装置200で得られたラマンスペクトルを解析する方法について説明する。
図16は、本実施の形態における結晶性半導体膜の膜質解析方法に用いるラマンスペクトルの解析方法を説明するためのフローチャートである。
まず、ラマン分光装置200を用いて、ラマンスペクトルを測定する(S301)。具体的には、結晶性半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する。例えば、図26に示すように、結晶性半導体膜である結晶シリコン膜においては、450~550cm-1の領域にシリコン膜固有のフォノンに対応するラマンピークが観測される。上述したように結晶シリコン膜固有のラマンピークは520cm-1、微結晶シリコン膜固有のラマンピークは500~510cm-1付近、a-Si膜固有のラマンピークは480cm-1付近に観測される。後述する実施例では、上記の領域に観測されるラマンピークに対して本解析方法を用いて解析を行った。
次に、測定したラマンスペクトルのベースラインを補正する(S302)。具体的には、ピーク波形の測定後、当該ピーク波形のベースラインを補正する。例えば、スペクトルを解析した領域に対して直線近似を行なう方法によりベースラインの補正を行う。なぜなら、ラマンスペクトルは、サンプル(ここでは試料307)や測定環境の影響を受けて、ベースライン傾斜してしまうことがあるからである。これは、例えば、図26にも示されており、入射光(レーリー光)の影響でベースラインが傾斜している。なお、ベースラインが傾斜していない場合もあり、その場合には、ベースラインの補正を行う必要はない。
次に、ラマン強度関数(ラマンスペクトル関数)を用いてラマンスペクトルのフィッティングを行う(S303)。
具体的には、ラマンピーク波形解析モデルを生成し、生成したラマンピーク波形解析モデルを用いて、ピーク波形を再現する。詳細は、後述するが、ベースラインを補正したラマンスペクトルに対して、結晶シリコン成分、微結晶シリコン成分、a-Si成分の3つの成分が存在すると仮定し、ラマンスペクトルの解析を行うことで、ラマンスペクトルのフィッティング(ラマンスペクトルの再現)を行う。
次に、ラマンスペクトルのフィッティング結果から、パラメータを抽出する(S304)。具体的には、スペクトル解析によって得られたラマンピーク波形解析モデルから、パラメータとして各成分におけるピーク位置、半値幅、ピーク強度、体積分率などを抽出する。
以上のようにして、ラマン分光装置200で得られたラマンスペクトルを解析する。
次に、上述のS303におけるラマンスペクトルの解析方法において、詳細に説明する。
従来、各固有フォノンの分散を表す関数を、ガウス関数、ローレンツ関数、及びその複合関数(Voit関数)を用いて表現できると仮定して解析されてきた。一方、本発明では、各固有のフォノン分散を表す関数としてフォノンのコヒーレンス長を考慮したラマンスペクトル関数を用いて解析する。以下の(式1)及び(式2)に、本発明で用いるラマンスペクトル関数を示す。
ここで、Lcはフォノンコヒーレンス長、aは格子定数(結晶シリコン:0.53nm)、Γ0は結晶シリコンのラマンピークの半値幅(測定系に依存)、Cは規格化定数、f(q)は重み付け関数である。
通常、ラマン散乱は光の非弾性散乱であるため、選択則に従えば運動エネルギーが0であるとき、TOフォノンのラマンピーク(520.6cm-1)のみが観測される。ところが、結晶シリコン膜の結晶性が乱れると、上記の選択則が崩れ、他のフォノンモードもラマン活性となりある程度観測されるようになる。
図17A~図17Fは、本発明の実施の形態2におけるフォノンのコヒーレンス長のラマンスペクトル依存性を計算した結果を示す図である。図において、縦軸は規格化されたラマンピーク強度、横軸はラマンシフト(入射光からの差)を示す。図17A~図17Fは、それぞれLcを50、10、5、2、1.5、1.0nmと変化させてラマンスペクトルを計算した結果を示している。
結晶が乱れた系やフォノンが閉じ込められた系ではフォノンのコヒーレンス長が制限されることが知られている。また、図17A~図17Fの結果から、Lcの減少と共に、ラマンピークの半値幅が広がり、低波数側にピーク位置がシフトしていくことがわかる。また、Lcが5nm以下になると、ラマンスペクトルの形状がLcに大きく依存していくことがわかる。
したがって、a-Si成分、微結晶シリコン成分、結晶シリコン成分のラマンスペクトル関数は、フォノンコヒーレンス長によって特徴付けることができる。それ故に、測定した結晶シリコン膜のラマンスペクトルは、以下の(式3)、(式4)によって表すことができる。
ここで、σa、σmc及びσcはそれぞれ、a-Si成分、微結晶シリコン成分及び結晶シリコン成分の体積分率を示し、Ia(ω)、Iμc(ω)及びIc(ω)はそれぞれ、a-Si成分、微結晶シリコン成分及び結晶シリコン成分のラマンスペクトル関数を示す。
以上から、S303では、まず、Ic(ω)を結晶性シリコン成分のラマンバンド、Iμc(ω)を微結晶シリコン成分のラマンバンド、Ia(ω)をアモルファスシリコン成分のラマンバンド、σcを結晶シリコン成分の体積分率、σmcを微結晶シリコン成分の体積分率、σaをアモルファスシリコン成分の体積分率とする。続いて、(式3)で表現されるラマンピーク波形解析モデルを作成する第1工程と、結晶シリコン成分のラマンバンド、微結晶シリコン成分のラマンバンド、及びアモルファスシリコン成分のラマンバンドを、Lcをフォノンコヒーレンス長、aを格子定数、Γ0を単結晶半導体のラマンピークの半値幅、Cを規格化定数として(式2)に示すラマンスペクトル関数を記述する第2工程と、前記ラマンスペクトル関数を用いてラマンピーク波形解析モデルを生成し、生成した前記ラマンピーク波形解析モデルを用いて、前記ピーク波形を再現する第3工程と、を含む。第1工程~第3工程により、ラマンスペクトル関数を用いてラマンスペクトルのフィッティング(ピーク波形の再現)を行う。
つまり、本実施の形態の解析方法では、それぞれの成分のフォノンコヒーレンス長及び体積分率をパラメータとして、実験結果(ラマンスペクトル)に対してフィッティングを行なう。そして、ピーク位置、半値幅、結晶化率などのパラメータの抽出をする。
ここで、結晶化率とは結晶シリコン膜の膜質を表す指標として用いられ、以下の(式5)に示すように定義される。
結晶化率=σmc+σc (式5)
次に、様々な手法によって作製した結晶シリコン膜について、上述した本実施の形態の解析方法を用いて解析した例を実施例として説明する。
(実施例1)
本実施例では、連続発振(CW)レーザを用いてa-Si膜を結晶化した結晶シリコン膜のラマンスペクトルを解析した結果について説明する。
本実施例では、連続発振(CW)レーザを用いてa-Si膜を結晶化した結晶シリコン膜のラマンスペクトルを解析した結果について説明する。
試料(試料307)は、ガラス基板上に、約200nmのシリコン窒化膜(ベースコート層)及び約50nmのa-Si膜を形成し、その後CWレーザを用いて結晶化したものである。a-Siの結晶化は、波長532nm、パワー密度70Kw/cm2のCWレーザを用いて行った。
また、試料307として、結晶組織を変化させるためにレーザのスキャン速度を変化させたサンプルを作製した。具体的には、固相成長、部分溶融成長、及び溶融成長した結晶性シリコン膜を有するサンプルを作製した。なお、固相成長、部分溶融成長、及び溶融成長した結晶性シリコン膜を形成するために、それぞれのサンプルにおいて、440、360、260mm/sのスキャン速度でレーザ照射を行った。
図18A~図18Cは、実施例1における結晶性シリコン膜の平面電子顕微鏡(SEM)像を示す図である。図18A~図18Cは、それぞれ、上記方法により、固相成長、部分溶融成長、及び溶融成長した結晶性シリコン膜のSEM像を示している。固相成長した結晶性シリコンの粒径は、図18Aから約30nmであることが観測される。部分溶融成長した結晶性シリコンの粒径は、図18Bから約40nm~50nmであり、溶融成長した結晶性シリコン膜の粒径は、図18Cから約100-200nmであることが観測される。
図19は、実施例1における固相成長した結晶シリコン膜のラマンスペクトルとその解析結果を示す図である。図20は、実施例1における部分溶融成長した結晶シリコン膜のラマンスペクトルとその解析結果を示す図である。図21、実施例1における溶融成長した結晶シリコン膜のラマンスペクトルとその解析結果を示す図である。
図19~図21から、固相成長、部分溶融成長、及び溶融成長した結晶シリコン膜の結晶化率は、それぞれ、43%、85%、100%と抽出することができた。この結果は、図18A~図18Cで確認した結晶性とも定性的に一致した結果であるといえる。
また、図19~図21に示すように、測定結果と解析結果を比較すると、従来の解析方法に比べて、よく一致していることが確認できる。特に、低波数側のフィッティング精度が著しく向上していることが確認できる。これは、上述した(式3)に示されるように各成分のスペクトルにフォノンコヒーレンス長による重み付けを行っているため、各成分の分散を波数に対して非対称にすることができるためである。また、各成分のスペクトルは物性値であるコヒーレンス長を反映させているため、物理的な意味をもつ。
図22は、本実施の形態の解析方法と従来の解析方法とを用いて導出した結晶シリコン膜の結晶化率を比較した図である。図22では、縦軸は、ラマンスペクトル解析によって導出した結晶化率、横軸は規格化したレーザ出力を示す。また、図22では、同じラマンスペクトルを本実施の形態の解析方法及び従来の解析方法(各成分の分散をガウス関数と仮定)によって抽出した結晶化率をプロットしている。
レーザ結晶化において、レーザ出力の上昇とともに結晶粒径が大きくなることで知られている。また、図22においても、レーザ出力の上昇とともに結晶化率が増加していることがわかる。以上を鑑みると、本実施の形態の解析方法は、従来の解析方法と比べて、結晶化率を低く見積もり、さらに、レーザ出力に対する傾きが急である、すなわち、結晶性に対して敏感であることがわかる。
以上の結果に示されるように、本実施の形態の解析方法は、結晶シリコン膜のラマンスペクトルをより正確に解析することができる。したがって、得られたパラメータは、従来に比べて、物理的に意味のあるものとなる。また、結晶シリコン膜の結晶性を高感度で解析することが可能となる。それ故に、本実施例からわかるように、得られたパラメータを用いることで、より正確に結晶シリコン膜の膜質を管理することが可能となる。
(実施例2)
本実施例では、急速熱アニール(RTA:Rapid Thermal Annealing)を用いてa-Si膜を結晶化した結晶シリコン膜のラマンスペクトルを解析した結果について説明する。
本実施例では、急速熱アニール(RTA:Rapid Thermal Annealing)を用いてa-Si膜を結晶化した結晶シリコン膜のラマンスペクトルを解析した結果について説明する。
試料(試料307)は、石英基板上に、約200nmのシリコン窒化膜(ベースコート層)及び約50nmのa-Si膜を形成し、RTA法を用いて結晶化したものである。a-Siの結晶化は、750℃、5分間の処理により行なった。本実施例では、例示していないが、アニール温度、保持時間、冷却速度などを制御することで、結晶シリコン膜の結晶性を制御することができる。
図23は、実施例2における結晶シリコン膜の平面電子顕微鏡(SEM)像を示す図である。図23は上記のRTA法を用いて結晶化された結晶シリコン膜を示している。図23に示す結晶シリコン膜は、部分溶融成長した結晶であり、その粒径は約40-50nmであることが観測される。
図24は、実施例2におけるRTA法で結晶化した結晶シリコン膜のラマンスペクトルとその解析結果を示す図である。図24に示す解析結果から、結晶シリコン膜の結晶化率は、66%と抽出することができた。図24において、測定結果と解析結果とを比較すると、従来の解析方法に比べて、よく一致していることが確認できる。
結晶シリコン膜は、結晶化の手法によって、結晶組織の状態が異なることで知られている。そこから、本実施例においてRTA法で形成した部分溶融成長した結晶シリコン膜の結晶化率が、実施例1の結晶シリコン膜(結晶組織)の結晶化率と異なるのは、結晶化手法による結晶組織の違いを反映している可能性が高い。
以上の結果に示されるように、本実施の形態の解析方法は、RTA法によって作製した結晶シリコン膜においても、そのラマンスペクトルをより正確に解析することができる。
それ故に、本実施例からわかるように、得られたパラメータを用いることで、より正確に結晶シリコン膜の膜質を管理することが可能となる。
以上、本実施の形態によれば、結晶性半導体膜の膜質を物理実態に基づいたモデルを用いることができるので、結晶性半導体膜の膜質を正確に評価及び解析できる結晶性半導体膜の膜質解析方法を実現できる。
具体的には、結晶シリコン、微結晶シリコン及びa-Siのフォノンモードにおいて、フォノンコヒーレンス長を考慮したラマンスペクトル関数を用いたスペクトル分離方法を用いることで、実測スペクトルの再現性を向上させることができる。さらに、物理実態に基づいたモデルを用いることで、抽出したパラメータの信頼性が向上し、正確な結晶性を評価・解析することが可能となる。
なお、本実施の形態の結晶性半導体膜の膜質解析方法は、この実施の形態に限定されるものではない。本発明の趣旨を逸脱しない限り、当業者が思いつく各種変形を本実施の形態に施したものや、異なる実施の形態における構成要素を組み合わせて構築される形態も、本発明の範囲内に含まれる。
例えば、本実施の形態に係る結晶性半導体膜の膜質解析方法において、生成されるラマンスペクトル関数を、実施の形態1の結晶性評価方法に適用してもよい。例えば、例えば、本実施の形態に係る結晶性評価方法、及び結晶性評価コンピュータソフトにおいて、抽出したピーク値を用いて、ラマンスペクトル関数によりラマンスペクトルのフィッティングを行うとしてもよい。このラマンスペクトル関数は、ローレンツ関数そのものではないが、ローレンツ関数から記述される関数である。したがって、S204において、ローレンツ関数そのものでなく、ラマンスペクトル関数によりラマンスペクトルのフィッティングを行うこともできるので、この形態も、本発明の範囲内に含まれる。
より具体的には、基板上に形成された半導体膜の結晶性を評価する結晶性評価方法として以下の工程を含むとしてよい。すなわち、半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、第1フィッティング波形のピーク値を抽出する第3工程と、抽出したピーク値を用いて、ローレンツ関数を用いて記述されるラマンスペクトル関数によりラマンバンドのピーク波形をフィッティングすることで、前記ラマンスペクトル関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、第4工程の第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、半導体膜の結晶性を評価する第6工程と、を含み、第4工程では、Ic(ω)を結晶性シリコン成分のラマンバンド、Iμc(ω)を微結晶シリコン成分のラマンバンド、Ia(ω)をアモルファスシリコン成分のラマンバンド、σcを結晶性シリコン成分の体積分率、σmcを微結晶シリコン成分の体積分率、σaをアモルファスシリコン成分の体積分率とし、(式3)で表現されるラマンピーク波形解析モデルを作成する工程と、結晶性シリコン成分のラマンバンド、微結晶性シリコン成分のラマンバンド、及びアモルファスシリコン成分のラマンバンドを、Lcをフォノンコヒーレンス長、aを格子定数、Γ0を単結晶半導体のラマンピークの半値幅、Cを規格化定数として、(式1)及び(式4)に示すラマンスペクトル関数を記述する工程とを含むとしてもよい。
また、例えば、本実施の形態において、上述のようなラマンスペクトルの解析方法によって、結晶性半導体膜のラマンバンド波形を解析するが、これらの解析はコンピュータを用いて行うことができる。従って、本発明の基板上に形成された結晶性半導体膜の膜質解析を行うために、ラマン分光法により得られるラマンバンド波形を解析するプログラムが組み込まれたコンピュータソフトが、本発明に関するものとなる。
また、本実施の形態において、上述のようなラマンスペクトルの解析方法によって、結晶性半導体膜のラマンバンド波形を解析するが、これらの解析結果から抽出したパラメータを用いて、結晶性半導体膜の膜質管理を行うことができる。従って、本発明の基板上に形成された結晶性半導体膜の膜質解析を行ない、デバイスプロセスの工程管理を行う方法も本発明に関するものとなる。
それにより、本実施の形態の解析方法を搭載したコンピュータソフト及びこの解析方法を用いてインラインで迅速に膜質管理する方法を実現できる。
以上、本実施の形態によれば、結晶性半導体膜の膜質を物理実態に基づいたモデルを用いることができるので、結晶性半導体膜の膜質を正確に評価及び解析できる結晶性半導体膜の膜質解析方法、結晶性半導体膜の膜質解析コンピュータソフト、及びそれを用いた管理方法を実現できる。
以上、本発明によれば、移動度のばらつきもなく高移動度の特性を有する結晶性半導体膜の結晶性を正確に評価できる結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトを実現することができる。
以上、本発明の結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトについて、実施の形態に基づいて説明したが、本発明は、この実施の形態に限定されるものではない。 その他、各実施の形態に対して当業者が思いつく各種変形を施して得られる形態や、本発明の趣旨を逸脱しない範囲で各実施の形態における構成要素及び機能を任意に組み合わせることで実現される形態も本発明に含まれる。
本発明は、半導体膜の結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトに利用でき、特に液晶ディスプレイ、有機エレクトロルミネッセンステレビなどの表示装置等に用いられる薄膜トランジスタ装置(TFT)を製造する際の結晶シリコン膜の結晶性を正確に評価する結晶性評価方法、結晶性評価装置、及びそのコンピュータソフトに利用することができる。
100、150 薄膜トランジスタ装置
101 基板
102 ゲート電極
103 ゲート絶縁膜
104 結晶シリコン薄膜
105、155 非晶質シリコン薄膜
106、156 コンタクト層
106a、156a コンタクト層用膜
107、157 絶縁層
107a、157a 絶縁層形成用膜
108 ソースドレイン金属膜
108S ソース電極
108D ドレイン電極
109 パッシベーション膜
200 ラマン分光装置
201 光源
202 アッテネーター
203 フィルター
204 ミラー
205 ビームスプリッター
206 対物レンズ
207、307 試料
208 ステージ
209 スリット
210 分光器
211 検出器
500 ラマンスペクトル
501 解析結果
502 結晶シリコン成分
503 微結晶シリコン成分
504 a-Si成分
101 基板
102 ゲート電極
103 ゲート絶縁膜
104 結晶シリコン薄膜
105、155 非晶質シリコン薄膜
106、156 コンタクト層
106a、156a コンタクト層用膜
107、157 絶縁層
107a、157a 絶縁層形成用膜
108 ソースドレイン金属膜
108S ソース電極
108D ドレイン電極
109 パッシベーション膜
200 ラマン分光装置
201 光源
202 アッテネーター
203 フィルター
204 ミラー
205 ビームスプリッター
206 対物レンズ
207、307 試料
208 ステージ
209 スリット
210 分光器
211 検出器
500 ラマンスペクトル
501 解析結果
502 結晶シリコン成分
503 微結晶シリコン成分
504 a-Si成分
Claims (10)
- 基板上に形成された半導体膜の結晶性を評価する結晶性評価方法であって、
前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、
ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、
前記第1フィッティング波形のピーク値を抽出する第3工程と、
抽出した前記ピーク値を用いて、ローレンツ関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、
前記第4工程の前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、
前記第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する第6工程と、を含む、
結晶性評価方法。 - 基板上に形成された半導体膜の結晶性を評価する結晶性評価方法であって、
前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する第1工程と、
ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第2工程と、
前記第1フィッティング波形のピーク値を抽出する第3工程と、
抽出した前記ピーク値を用いて、ローレンツ関数を用いて記述されるラマンスペクトル関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ラマンスペクトル関数によるフィッティングされた波形である第2フィッティング波形を生成する第4工程と、
前記第4工程の前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する第5工程と、
前記第5工程で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する第6工程と、を含み、
前記第4工程では、Ic(ω)を結晶性シリコン成分のラマンバンド、Iμc(ω)を微結晶シリコン成分のラマンバンド、Ia(ω)をアモルファスシリコン成分のラマンバンド、σcを結晶性シリコン成分の体積分率、σmcを微結晶シリコン成分の体積分率、σaをアモルファスシリコン成分の体積分率とし、(式A)で表現されるラマンピーク波形解析モデルを作成する工程と、
前記結晶性シリコン成分のラマンバンド、微結晶性シリコン成分のラマンバンド、及びアモルファスシリコン成分のラマンバンドを、Lcをフォノンコヒーレンス長、aを格子定数、Γ0を単結晶半導体のラマンピークの半値幅、Cを規格化定数として、(式B)及び(式C)に示すラマンスペクトル関数を記述する工程とを含む、
結晶性評価方法。
- 前記第6工程では、前記第5工程で出力された前記ピーク値、半値幅、または前記ピーク値を示す波長と、ルックアップテーブルに予め保存されている参照ピーク値、参照半値幅、または参照ピーク値を示す波長と比較することにより、前記半導体膜の結晶性を評価し、
前記ルックアップテーブルには、前記参照ピーク値、前記参照半値幅、または前記参照ピーク値を示す波長として、前記第1工程より前に、結晶性半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形を、ローレンツ関数を用いてフィッティングして得られた第3フィッティング波形のピーク値、半値幅または前記ピーク値を示す波長が予め保存されており、
前記ルックアップテーブルには、結晶粒径、結晶粒の存在比率及び移動度を含む当該結晶性半導体膜の結晶性の評価が、前記参照ピーク値、前記参照半値幅、または前記参照ピーク値を示す波長と紐付けられて保存されている、
請求項1に記載の結晶性評価方法。 - 前記第6工程では、前記半値幅が5.0cm-1~6.0cm-1であるか否かを判定することにより、前記半導体膜の結晶性を評価する、
請求項1~3のいずれか1項に記載の結晶性評価方法。 - 前記半導体膜はシリコンで構成されており、
前記第6工程では、前記半値幅と単結晶シリコンのラマンバンドの半値幅の比が、1.5~1.8であるか否かを判定することにより、前記半導体膜の結晶性を評価する、
請求項1~3のいずれか1項に記載の結晶性評価方法。 - 前記半導体膜はシリコンで構成されており、
前記第6工程では、前記半値幅と前記単結晶シリコンのラマンバンドの半値幅の差が1.8cm-1~2.4cm-1であるか否かを判定することにより、前記半導体膜の結晶性を評価する、
請求項1~3のいずれか1項に記載の結晶性評価方法。 - 前記第6工程では、前記ピーク値と結晶シリコンのラマンバンド半値幅との比が0.1~0.2であるか否かを判定することにより、前記半導体膜の結晶性を評価する、
請求項1~3のいずれか1項に記載の結晶性評価方法。 - 請求項1~7のいずれか1項に記載の結晶性評価方法を用いて、前記結晶性半導体膜の結晶性を評価することにより、所定の結晶性半導体膜の結晶性を示す前記結晶性半導体膜を選別する、
半導体膜の製造方法。 - 基板上に形成された半導体膜の結晶性を評価する結晶性評価装置であって、
前記半導体膜に固有のフォノンモードに対応するラマンバンドのピーク波形をラマン分光法により測定する測定部と、
ガウス関数を用いて、測定した前記ラマンバンドのピーク波形をフィッティングすることで、前記ガウス関数によりフィッティングされた波形である第1フィッティング波形を生成する第1生成部と、
前記第1フィッティング波形のピーク値を抽出する抽出部と、
抽出した前記ピーク値を用いて、ローレンツ関数により前記ラマンバンドのピーク波形をフィッティングすることで、前記ローレンツ関数によるフィッティングされた波形である第2フィッティング波形を生成する第2生成部と、
前記第2フィッティング波形のピーク値、半値幅、または前記ピーク値を示す波長を出力する出力部と、
前記出力部で出力された前記ピーク値、前記半値幅、または前記ピーク値を示す波長に基づき、前記半導体膜の結晶性を評価する評価部とを備える、
結晶性評価装置。 - コンピュータ読み取り可能記録媒体に記録された結晶性半導体膜の結晶性を評価するコンピュータソフトであって、
請求項1~7のいずれか1項に記載の結晶性評価方法をコンピュータに実行させることにより、前記半導体膜の結晶性の評価を出力するプログラムが組み込まれている、
コンピュータソフト。