WO2012067379A2 - 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연/열연 DP강의 제조방법 - Google Patents
인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연/열연 DP강의 제조방법 Download PDFInfo
- Publication number
- WO2012067379A2 WO2012067379A2 PCT/KR2011/008570 KR2011008570W WO2012067379A2 WO 2012067379 A2 WO2012067379 A2 WO 2012067379A2 KR 2011008570 W KR2011008570 W KR 2011008570W WO 2012067379 A2 WO2012067379 A2 WO 2012067379A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- steel
- rolling
- rolled
- strip
- cold
- Prior art date
Abstract
Description
강종 | C | Si | Mn | P | S | Al | N | Cr | B | Sb | Ti | Nb | V | Mo | 비고 |
1 | 0.08 | 0.35 | 1.8 | 0.015 | 0.003 | 0.04 | 0.007 | 0.01 | 0.0006 | 0.02 | - | - | - | 0.03 | 박 슬라브 |
2 | 0.08 | 0.10 | 1.7 | 0.020 | 0.003 | 0.03 | 0.006 | 0.35 | 0.0005 | 0.02 | 0.013 | - | - | - | |
3 | 0.07 | 0.70 | 1.6 | 0.030 | 0.003 | 0.03 | 0.006 | 0.20 | 0.0005 | - | - | 0.01 | - | - | |
4 | 0.06 | 0.50 | 1.7 | 0.020 | 0.003 | 0.04 | 0.007 | 0.20 | - | 0.02 | - | - | 0.03 | - | |
5 | 0.06 | 0.10 | 1.8 | 0.025 | 0.003 | 0.03 | 0.007 | 0.40 | - | 0.02 | 0.015 | 0.01 | - | - | |
6 | 0.06 | 0.20 | 1.8 | 0.015 | 0.003 | 0.03 | 0.007 | 0.40 | - | 0.02 | 0.015 | - | 0.02 | - | |
7 | 0.08 | 0.35 | 1.8 | 0.012 | 0.003 | 0.04 | 0.004 | 0.01 | 0.0060 | 0.02 | - | - | - | 0.03 | 기존밀 |
8 | 0.08 | 0.12 | 1.7 | 0.020 | 0.003 | 0.03 | 0.004 | 0.35 | 0.0050 | 0.02 | 0.013 | - | - | - | |
9 | 0.07 | 0.70 | 1.6 | 0.030 | 0.003 | 0.03 | 0.004 | 0.20 | 0.0005 | - | - | 0.01 | - | - |
구분 | 강종 | 슬라브두께(mm) | 주속(mpm) | 슬라브표면온도(℃) | 압연속도차(%) | 마무리압연온도(℃) | 식1계산값 | 권취온도(℃) | 소둔온도(℃) | 소둔후냉각속도(℃/s) | 인장강도(MPa) | 연신율(%) | 재질편차(△TS,Mpa) | 스트립표면형상 |
발명강1 | 1 | 84 | 6.1 | 1021 | 4 | 780 | 784 | 550 | 790 | 63 | 642 | 31.0 | 15 | 양호 |
발명강2 | 2 | 84 | 6.1 | 1021 | 4 | 780 | 783 | 550 | 790 | 92 | 617 | 31.3 | 14 | 양호 |
발명강3 | 3 | 84 | 6.1 | 1020 | 4 | 800 | 806 | 550 | 790 | 115 | 641 | 30.2 | 15 | 양호 |
발명강4 | 4 | 84 | 6.1 | 1021 | 4 | 800 | 797 | 550 | 790 | 43 | 625 | 32.0 | 15 | 양호 |
발명강5 | 5 | 84 | 6.1 | 1028 | 4 | 780 | 779 | 550 | 790 | 43 | 615 | 30.5 | 16 | 양호 |
발명강6 | 6 | 84 | 6.1 | 1021 | 4 | 780 | 781 | 550 | 790 | 63 | 652 | 30.3 | 19 | 양호 |
발명강7 | 6 | 84 | 6.1 | 1011 | 4 | 780 | 781 | 550 | 790 | 57 | 625 | 30.5 | 15 | 양호 |
비교강1 | 1 | 84 | 4.1 | 1015 | 4 | 780 | 784 | 550 | 790 | 70 | 625 | 29.4 | 33 | 양호 |
비교강2 | 2 | 84 | 6.1 | 1121 | 4 | 780 | 783 | 550 | 790 | 55 | 635 | 30.5 | 21 | 스케일 |
비교강3 | 3 | 84 | 6.1 | 1032 | 21 | 800 | 806 | 550 | 790 | 65 | 630 | 30.1 | 52 | 양호 |
비교강4 | 4 | 84 | 6.1 | 1011 | 4 | 870 | 797 | 550 | 790 | 85 | 628 | 28.1 | 20 | 양호 |
비교강5 | 5 | 84 | 6.1 | 1000 | 4 | 780 | 779 | 420 | 790 | 59 | 690 | 22.3 | 17 | 형상불량 |
비교강6 | 5 | 84 | 6.1 | 995 | 4 | 780 | 779 | 700 | 790 | 73 | 565 | 32.0 | 32 | 스케일 |
비교강7 | 6 | 84 | 6.1 | 996 | 4 | 780 | 781 | 550 | 740 | 92 | 710 | 13.0 | - | 양호 |
비교강8 | 6 | 84 | 6.1 | 1045 | 4 | 780 | 781 | 550 | 850 | 130 | 525 | 29.3 | - | 양호 |
비교강9 | 6 | 84 | 6.1 | 1032 | 4 | 780 | 781 | 550 | 790 | 8 | 542 | 27.1 | - | 양호 |
비교강10 | 6 | 84 | 6.1 | 1033 | 4 | 780 | 781 | 550 | 790 | 160 | 720 | 22.0 | - | 형상불량 |
비교강11 | 7 | 230 | 1.0 | 1084 | 30 | 870 | 784 | 550 | 790 | 68 | 642 | 28.0 | 54 | 양호 |
비교강12 | 8 | 230 | 1.0 | 1080 | 30 | 870 | 783 | 550 | 790 | 72 | 630 | 29.0 | 65 | 양호 |
비교강13 | 9 | 230 | 1.0 | 1069 | 30 | 870 | 806 | 550 | 790 | 86 | 625 | 29.0 | 45 | 양호 |
강종 | C | Si | Mn | P | S | Al | N | Ti | Nb | Cr | Mo | B | Sb | 비고 |
1 | 0.07 | 0.7 | 1.4 | 0.03 | 0.003 | 0.04 | 0.007 | - | - | - | - | - | 0.02 | 박 슬라브 |
2 | 0.05 | 0.6 | 1.7 | 0.01 | 0.003 | 0.04 | 0.007 | - | - | - | - | - | 0.02 | |
3 | 0.07 | 0.1 | 1.7 | 0.03 | 0.003 | 0.03 | 0.006 | - | - | 0.2 | - | - | 0.02 | |
4 | 0.05 | 0.7 | 1.5 | 0.02 | 0.003 | 0.04 | 0.007 | 0.015 | - | - | - | 0.005 | - | |
5 | 0.05 | 0.6 | 1.7 | 0.01 | 0.003 | 0.04 | 0.007 | - | 0.015 | - | - | - | 0.02 | |
6 | 0.06 | 0.5 | 1.8 | 0.01 | 0.003 | 0.03 | 0.008 | - | - | - | 0.1 | - | 0.02 | |
7 | 0.07 | 0.7 | 1.4 | 0.03 | 0.003 | 0.04 | 0.007 | - | - | - | - | - | 0.02 | 기존밀 |
8 | 0.07 | 0.1 | 1.7 | 0.03 | 0.003 | 0.03 | 0.006 | - | - | 0.2 | - | - | 0.02 | |
9 | 0.05 | 0.6 | 1.7 | 0.01 | 0.003 | 0.04 | 0.007 | - | - | - | - | - | 0.02 |
구분 | 강종 | 슬라브두께(mm) | 주속(mpm) | 압연속도차(%) | 마무리압연온도(℃) | 식1계산값 | 권취온도(℃) | 인장강도(MPa) | 연신율(%) | 재질편차(△TS,Mpa) | TS×EI |
발명강1 | 1 | 84 | 6.0 | 5 | 780 | 200 | 200 | 608 | 30 | 20 | 18,240 |
발명강2 | 2 | 84 | 6.0 | 5 | 780 | 195 | 200 | 598 | 31 | 15 | 18,538 |
발명강3 | 3 | 84 | 6.0 | 5 | 780 | 192 | 200 | 625 | 31 | 20 | 19,375 |
발명강4 | 3 | 84 | 6.0 | 5 | 780 | 204 | 200 | 635 | 29 | 20 | 18,415 |
발명강5 | 4 | 84 | 6.0 | 5 | 780 | 195 | 190 | 615 | 28 | 17 | 17,220 |
발명강6 | 5 | 84 | 6.0 | 5 | 780 | 187 | 190 | 628 | 28 | 19 | 17,584 |
비교강1 | 1 | 84 | 4.0 | 5 | 780 | 200 | 200 | 605 | 28 | 35 | 16,940 |
비교강2 | 2 | 84 | 6.0 | 20 | 780 | 195 | 200 | 603 | 29 | 41 | 17,487 |
비교강3 | 3 | 84 | 6.0 | 5 | 890 | 192 | 200 | 602 | 28 | 13 | 16,856 |
비교강4 | 4 | 84 | 6.0 | 5 | 700 | 192 | 200 | 665 | 21 | 28 | 13,965 |
비교강5 | 5 | 84 | 6.0 | 5 | 780 | 204 | 250 | 580 | 24 | 15 | 13,920 |
비교강6 | 6 | 230 | 1.0 | 30 | 850 | 200 | 220 | 610 | 27 | 70 | 16,470 |
비교강7 | 6 | 230 | 1.0 | 30 | 850 | 192 | 220 | 605 | 27 | 64 | 16,355 |
비교강8 | 7 | 230 | 1.0 | 30 | 850 | 195 | 220 | 615 | 26 | 58 | 15,990 |
Claims (16)
- 중량%로 C: 0.05 ~ 0.11%, Si: 0.01 ~ 0.8%, Mn: 1.2 ~ 2.2%, P: 0.001 ~ 0.1%, S:0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Sb: 0.005 ~ 0.1%, Ti: 0.001 ~ 0.1%, Nb: 0.001 ~ 0.1%, V: 0.001 ~ 0.1%, Mo: 0.005 ~ 0.5% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연 및 권취 단계를 통해 열연 스트립을 제조하며, 이 열연 스트립을 산세, 냉간압연, 연속소둔 및 냉각 열처리 단계를 통해 냉연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 하나의 스트립 내에서의 압연 속도차가 15% 이하가 되도록 하고,상기 냉각 열처리 단계는 연속소둔 처리된 스트립을 10 ~ 150℃/s의 냉각속도로 200 ~ 400℃의 온도까지 연속적으로 냉각하여 제조하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 중량%로 C: 0.05 ~ 0.11%, Si: 0.01 ~ 0.8%, Mn: 1.2 ~ 2.2%, P: 0.001 ~ 0.1%, S:0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Sb: 0.005 ~ 0.1%, Ti: 0.001 ~ 0.1%, Nb: 0.001 ~ 0.1%, V: 0.001 ~ 0.1%, Mo: 0.005 ~ 0.5% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연 및 권취 단계를 통해 열연 스트립을 제조하며, 이 열연 스트립을 산세, 냉간압연, 연속소둔 및 냉각 열처리 단계를 통해 냉연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 마지막 압연 스탠드에서의 압연온도가 [910 - 195C - 70Mn + 20Si + 30P - 25N - 15Cr - 40Mo]의 관계식으로 계산된 목표온도의 ±20℃ 범위가 되도록 하며,상기 냉각 열처리 단계는 연속소둔 처리된 스트립을 10 ~ 150℃/s의 냉각속도로 200 ~ 400℃의 온도까지 연속적으로 냉각하여 제조하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 중량%로 C: 0.05 ~ 0.11%, Si: 0.01 ~ 0.8%, Mn: 1.2 ~ 2.2%, P: 0.001 ~ 0.1%, S:0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Sb: 0.005 ~ 0.1%, Ti: 0.001 ~ 0.1%, Nb: 0.001 ~ 0.1%, V: 0.001 ~ 0.1%, Mo: 0.005 ~ 0.5% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연 및 권취 단계를 통해 열연 스트립을 제조하며, 이 열연 스트립을 산세, 냉간압연, 연속소둔 및 냉각 열처리 단계를 통해 냉연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 하나의 스트립 내에서의 압연 속도차가 15% 이하가 되도록 하고,상기 마무리 압연 단계는 마지막 압연 스탠드에서의 압연온도가 [910 - 195C - 70Mn + 20Si + 30P - 25N - 15Cr - 40Mo]의 관계식으로 계산된 목표온도의 ±20℃ 범위가 되도록 하며,상기 냉각 열처리 단계는 연속소둔 처리된 스트립을 10 ~ 150℃/s의 냉각속도로 200 ~ 400℃의 온도까지 연속적으로 냉각하여 제조하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 연속주조 단계는 주조속도가 4.5 mpm 이상으로 하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 조압연 단계는 조압연기 입측에서의 박 슬라브 표면온도가 950 ~ 1100℃가 되도록 하고, 조압연 시의 누적 압하율이 65 ~ 90%가 되도록 하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 가열 단계는 조압연된 스트립을 950 ~ 1100℃로 가열 또는 보열하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 권취 단계는 마무리 압연된 스트립을 450 ~ 680℃에서 권취하는 것을 특징하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 냉간압연 단계는 산세된 스트립을 40 ~ 75%의 압하율로 압연하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 청구항 1 내지 청구항 3 중 어느 한 청구항에 있어서,상기 연속소둔 단계는 상기 냉간압연된 스트립을 750 ~ 840℃로 연속소둔하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 냉연 DP강의 제조방법.
- 중량%로 C: 0.03 ~ 0.1%, Si: 0.01 ~ 1.1%, Mn: 0.8 ~ 2.0%, P: 0.001 ~ 0.1%, S: 0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, Ti: 0.001 ~ 0.1%, Nb: 0.001~0.1%, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Mo: 0.005 ~ 0.5%, Sb: 0.005 ~ 0.1% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연, 냉각 및 권취 단계를 통해 열연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 하나의 스트립 내에서의 압연 속도차가 15% 이하가 되도록 하고,상기 권취 단계는 상기 냉각된 스트립을 [310 - 420C - 50Mn - 15Si - 12Cr - 7.5Mo]의 관계식에서 계산된 목표온도의 ±30℃ 범위 내에서 권취하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 중량%로 C: 0.03 ~ 0.1%, Si: 0.01 ~ 1.1%, Mn: 0.8 ~ 2.0%, P: 0.001 ~ 0.1%, S: 0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, Ti: 0.001 ~ 0.1%, Nb: 0.001~0.1%, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Mo: 0.005 ~ 0.5%, Sb: 0.005 ~ 0.1% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연, 냉각 및 권취 단계를 통해 열연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 마지막 스탠드에서의 압연온도가 Ar1 및 Ar3 변태점 사이가 되도록 하고,상기 권취 단계는 상기 냉각된 스트립을 [310 - 420C - 50Mn - 15Si - 12Cr - 7.5Mo]의 관계식에서 계산된 목표온도의 ±30℃ 범위 내에서 권취하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 중량%로 C: 0.03 ~ 0.1%, Si: 0.01 ~ 1.1%, Mn: 0.8 ~ 2.0%, P: 0.001 ~ 0.1%, S: 0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, Ti: 0.001 ~ 0.1%, Nb: 0.001~0.1%, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Mo: 0.005 ~ 0.5%, Sb: 0.005 ~ 0.1% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연, 냉각 및 권취 단계를 통해 열연 DP강을 제조하는 방법에 있어서,상기 냉각 단계는 런아웃 테이블에서 상기 마무리 압연된 스트립을 50℃/s 이상의 냉각속도로 냉각하고,상기 권취 단계는 상기 냉각된 스트립을 [310 - 420C - 50Mn - 15Si - 12Cr - 7.5Mo]의 관계식에서 계산된 목표온도의 ±30℃ 범위 내에서 권취하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 중량%로 C: 0.03 ~ 0.1%, Si: 0.01 ~ 1.1%, Mn: 0.8 ~ 2.0%, P: 0.001 ~ 0.1%, S: 0.001 ~ 0.02%, Al: 0.01 ~ 1.0%, N: 0.001 ~ 0.02%, 총 트램프원소(Cu+Ni+Sn+Pb): 0.18% 이하 포함되고, Ti: 0.001 ~ 0.1%, Nb: 0.001~0.1%, B: 0.0002 ~ 0.005%, Cr: 0.01 ~ 2.0%, Mo: 0.005 ~ 0.5%, Sb: 0.005 ~ 0.1% 중 하나 이상이 첨가되며, 나머지 Fe 및 기타 불가피한 불순물로 조성된 강을 두께 30 ~ 150mm의 박 슬라브로 연속주조하고, 이 박 슬라브를 조압연, 가열, 마무리 압연, 냉각 및 권취 단계를 통해 열연 DP강을 제조하는 방법에 있어서,상기 마무리 압연 단계는 하나의 스트립 내에서의 압연 속도차가 15% 이하가 되도록 하고,상기 마무리 압연 단계는 마지막 스탠드에서의 압연온도가 Ar1 및 Ar3 변태점 사이가 되도록 하며,상기 냉각 단계는 런아웃 테이블에서 상기 마무리 압연된 스트립을 50℃/s 이상의 냉각속도로 냉각하고,상기 권취 단계는 상기 냉각된 스트립을 [310 - 420C - 50Mn - 15Si - 12Cr - 7.5Mo]의 관계식에서 계산된 목표온도의 ±30℃ 범위 내에서 권취하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 청구항 10 내지 청구항 13 중 어느 한 청구항에 있어서,상기 연속주조 단계는 주조속도가 4.5 mpm 이상으로 하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 청구항 10 내지 청구항 13 중 어느 한 청구항에 있어서,상기 조압연 단계는 조압연기 입측에서의 박 슬라브 표면온도가 950 ~ 1100℃가 되도록 하고, 조압연 시의 누적 압하율이 65 ~ 90%가 되도록 하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.
- 청구항 10 내지 청구항 13 중 어느 한 청구항에 있어서,상기 가열 단계는 조압연된 스트립을 1000 ~ 1150℃로 가열 또는 보열하는 것을 특징으로 하는 인장강도 590MPa급의 가공성 및 재질편차가 우수한 고강도 열연 DP강의 제조방법.