WO2012014456A1 - 共役ジエン化合物と非共役オレフィンとの共重合体、ゴム組成物、架橋ゴム組成物、及びタイヤ - Google Patents
共役ジエン化合物と非共役オレフィンとの共重合体、ゴム組成物、架橋ゴム組成物、及びタイヤ Download PDFInfo
- Publication number
- WO2012014456A1 WO2012014456A1 PCT/JP2011/004226 JP2011004226W WO2012014456A1 WO 2012014456 A1 WO2012014456 A1 WO 2012014456A1 JP 2011004226 W JP2011004226 W JP 2011004226W WO 2012014456 A1 WO2012014456 A1 WO 2012014456A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- copolymer
- conjugated
- diene compound
- conjugated diene
- Prior art date
Abstract
Description
また、実際に、三元共重合体の記載例はあるものの、エチレンーブタジエン共重合体のような二元共重合体の例はない。
さらに、該ランダム共重合体を含む不飽和性エラストマー組成物の耐亀裂成長性については言及されておらず、定かではない。
即ち、特開平11-228743号公報(特許文献4)には、共役ジエン化合物及び非共役オレフィンの単量体単位が不規則に配列してなるランダム共重合体とすることで、耐熱性及び耐亀裂成長性に優れたゴムを製造することについての記載がない。
以下に、本発明を詳細に説明する。本発明の共役ジエン化合物と非共役オレフィンとの共重合体は、共役ジエン化合物及び非共役オレフィンの単量体単位が不規則に配列してなるランダム共重合体であることを特徴としており、該共重合体を示差走査熱量測定した場合、非共役オレフィンの単量体単位からなるブロック部分に由来する結晶化温度が観測されない。即ち、本発明の共重合体は、非共役オレフィンの単量体単位からなるブロック部分が無く、非共役オレフィンの単量体単位の配列が不規則であるため、共役ジエン化合物及び非共役オレフィンの単量体単位が不規則に配列してなるランダム部分(ランダム構造ともいう)を有している。このように非共役オレフィンの単量体単位の配列が不規則であれば、該共重合体の相分離を起こすことなく、耐熱性等の性質を持つ非共役オレフィンを共重合体の主鎖中に導入することが可能となる。なお、示差走査熱量測定(DSC)とは、JIS K 7121-1987に準拠して行われる測定方法である。また、本発明の共重合体は、示差走査熱量測定において非共役オレフィンの単量体単位からなるブロック部分に由来する結晶化温度が観測されないため、結晶性を有さない共重合体と称することもできる。なお、ブロック部分には、マルチブロック部分も含まれる。なお、(X-Y)又は(Y-X)の構造を複数備えるブロック共重合体をマルチブロック部分と称する(ここで、Xは、非共役オレフィンの単量体単位からなるブロック部分であり、Yは、共役ジエン化合物の単量体単位からなるブロック部分である)。
前記シス-1,4結合量は、前記共役ジエン化合物由来部分中の量であって、共重合体全体に対する割合ではない。
上述した共役ジエン化合物の具体例のいずれを用いても、同様のメカニズムで本発明の共重合体を調製することができる。
前記共役ジエン化合物部分の1,2付加体(3,4付加体を含む)含量(共役ジエン化合物由来部分における共役ジエン化合物の1,2付加体部分(3,4付加体部分を含む)含量)が5%以下であると、本発明の共重合体は、耐亀裂成長性や耐オゾン性を向上することができる。さらには、前記共役ジエン化合物部分の1,2付加体(3,4付加体を含む)含量が2.5%以下であると、本発明の共重合体は、耐オゾン性や耐疲労性をさらに向上させることができる。
前記1,2付加体部分(3,4付加体部分を含む)含量は、前記共役ジエン化合物由来部分中の量であって、共重合体全体に対する割合ではない。
なお、前記共役ジエン化合物部分の1,2付加体部分(3,4付加体部分を含む)含量(共役ジエン化合物由来部分の共役ジエン化合物の1,2付加体部分(3,4付加体部分を含む)含量)は、共役ジエン化合物がブタジエンの場合、1,2-ビニル結合量と同じ意味である。
本発明の共役ジエン化合物と非共役オレフィンとの共重合体の第一の製造方法は、下記式(A):
RaMXbQYb ・・・ (A)
[式中、Rはそれぞれ独立して無置換もしくは置換インデニルを示し、該RはMに配位しており、Mはランタノイド元素、スカンジウム又はイットリウムを示し、Xはそれぞれ独立して炭素数1~20の炭化水素基を示し、該XはM及びQにμ配位しており、Qは周期律表第13族元素を示し、Yはそれぞれ独立して炭素数1~20の炭化水素基又は水素原子を示し、該YはQに配位しており、a及びbは2である]で表されるメタロセン系複合触媒、好ましくは下記式(I):
[式中、M1は、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、RA及びRBは、それぞれ独立して炭素数1~20の炭化水素基を示し、該RA及びRBは、M1及びAlにμ配位しており、RC及びRDは、それぞれ独立して炭素数1~20の炭化水素基又は水素原子を示す]で表されるメタロセン系複合触媒、又は該メタロセン系複合触媒とホウ素アニオンとを含む重合触媒組成物の存在下、共役ジエン化合物と非共役オレフィンとを重合させることを特徴とする。
(式中、M2は、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、RE~RJは、それぞれ独立して炭素数1~3のアルキル基又は水素原子を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体を、AlRKRLRMで表される有機アルミニウム化合物と反応させることで得られる。なお、反応温度は室温程度にすればよいので、温和な条件で製造することができる。また、反応時間は任意であるが、数時間~数十時間程度である。反応溶媒は特に限定されないが、原料及び生成物を溶解する溶媒であることが好ましく、例えばトルエンやヘキサンを用いればよい。なお、上記メタロセン系複合触媒の構造は、1H-NMRにより決定することが好ましい。
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.0
の関係を満たすことが好ましく、更に好ましくは下記式:
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.3
の関係を満たし、一層好ましくは下記式:
非共役オレフィンの濃度/共役ジエン化合物の濃度 ≧ 1.7
の関係を満たす。非共役オレフィンの濃度/共役ジエン化合物の濃度の値を1以上とすることで、反応混合物中に非共役オレフィンを効率的に導入することができる。
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、Ra~Rfは、それぞれ独立して炭素数1~3のアルキル基又は水素原子を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体、及び下記一般式(IV):
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpRは、それぞれ独立して無置換もしくは置換インデニルを示し、X´は、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基又は炭素数1~20の炭化水素基を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示す)で表されるメタロセン錯体、並びに下記一般式(V):
(式中、Mは、ランタノイド元素、スカンジウム又はイットリウムを示し、CpR´は、無置換もしくは置換シクロペンタジエニル、インデニル又はフルオレニルを示し、Xは、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基又は炭素数1~20の炭化水素基を示し、Lは、中性ルイス塩基を示し、wは、0~3の整数を示し、[B]-は、非配位性アニオンを示す)で表されるハーフメタロセンカチオン錯体からなる群より選択される少なくとも1種類の錯体を含む重合触媒組成物(以下、第二重合触媒組成物ともいう)が好適に挙げられ、該重合触媒組成物は、更に、通常のメタロセン錯体を含む重合触媒組成物に含有される他の成分、例えば助触媒等を含んでいてもよい。
ここで、メタロセン錯体は、一つ又は二つ以上のシクロペンタジエニル又はその誘導体が中心金属に結合した錯体化合物であり、特に、中心金属に結合したシクロペンタジエニル又はその誘導体が一つであるメタロセン錯体を、ハーフメタロセン錯体と称することがある。なお、重合反応系において、第二重合触媒組成物に含まれる錯体の濃度は0.1~0.0001mol/lの範囲であることが好ましい。
(式中、Rは水素原子、メチル基又はエチル基を示す。)
(式中、X´´はハライドを示す。)
(式中、X´´はハライドを示す。)
(A)成分:希土類元素化合物又は該希土類元素化合物とルイス塩基との反応物であって、希土類元素と炭素との結合を有さない該希土類元素化合物又は反応物と、
(B)成分:非配位性アニオンとカチオンとからなるイオン性化合物(B-1)、アルミノキサン(B-2)、並びにルイス酸、金属ハロゲン化物とルイス塩基との錯化合物及び活性ハロゲンを含む有機化合物のうち少なくとも一種のハロゲン化合物(B-3)よりなる群から選択される少なくとも一種と
を含む重合触媒組成物(以下、第三重合触媒組成物ともいう)を好適に挙げることもでき、該重合触媒組成物が、イオン性化合物(B-1)及びハロゲン化合物(B-3)の少なくとも一種を含む場合、該重合触媒組成物は、更に、
(C)成分:下記一般式(i):
YR1 aR2 bR3 c ・・・ (i)
[式中、Yは、周期律表第1族、第2族、第12族及び第13族から選択される金属であり、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよく、また、Yが周期律表第1族から選択される金属である場合には、aは1で且つb及びcは0であり、Yが周期律表第2族及び第12族から選択される金属である場合には、a及びbは1で且つcは0であり、Yが周期律表第13族から選択される金属である場合には、a、b及びcは1である]で表される有機金属化合物を含むことを特徴とする。上記イオン性化合物(B-1)及び上記ハロゲン化合物(B-3)は、(A)成分へ供給するための炭素原子が存在しないため、該(A)成分への炭素供給源として、上記(C)成分が必要となる。なお、上記重合触媒組成物が上記アルミノキサン(B-2)を含む場合であっても、該重合触媒組成物は、上記(C)成分を含むことができる。また、上記重合触媒組成物は、通常の希土類元素化合物系の重合触媒組成物に含有される他の成分、例えば助触媒等を含んでいてもよい。なお、重合反応系において、第三重合触媒組成物に含まれる(A)成分の濃度は0.1~0.0001mol/lの範囲であることが好ましい。
なお、ランタノイド元素の具体例としては、ランタニウム、セリウム、プラセオジム、ネオジウム、プロメチウム、サマリウム、ユウロピウム、ガドリニウム、テルビウム、ジスプロシウム、ホルミニウム、エルビウム、ツリウム、イッテルビウム、ルテチウムを挙げることができる。なお、上記(A)成分は、一種単独で用いてもよいし、二種以上を組み合わせて用いてもよい。
M11X11 2・L11w ・・・ (XI)
M11X11 3・L11w ・・・ (XII)
[式中、M11は、ランタノイド元素、スカンジウム又はイットリウムを示し、X11は、それぞれ独立して、水素原子、ハロゲン原子、アルコキシド基、チオラート基、アミド基、シリル基、アルデヒド残基、ケトン残基、カルボン酸残基、チオカルボン酸残基又はリン化合物残基を示し、L11は、ルイス塩基を示し、wは、0~3を示す]で表されることができる。
YR1 aR2 bR3 c ・・・ (i)
[式中、Yは、周期律表第1族、第2族、第12族及び第13族から選択される金属であり、R1及びR2は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R3は炭素数1~10の炭化水素基であり、但し、R3は上記R1又はR2と同一又は異なっていてもよく、また、Yが周期律表第1族から選択される金属である場合には、aは1で且つb及びcは0であり、Yが周期律表第2族及び第12族から選択される金属である場合には、a及びbは1で且つcは0であり、Yが周期律表第13族から選択される金属である場合には、a、b及びcは1である]で表される有機金属化合物であり、下記一般式(X):
AlR11R12R13 ・・・ (X)
[式中、R11及びR12は、同一又は異なり、炭素数1~10の炭化水素基又は水素原子で、R13は炭素数1~10の炭化水素基であり、但し、R13は上記R11又はR12と同一又は異なっていてもよい]で表される有機アルミニウム化合物であることが好ましい。式(X)の有機アルミニウム化合物としては、トリメチルアルミニウム、トリエチルアルミニウム、トリ-n-プロピルアルミニウム、トリイソプロピルアルミニウム、トリ-n-ブチルアルミニウム、トリイソブチルアルミニウム、トリ-t-ブチルアルミニウム、トリペンチルアルミニウム、トリヘキシルアルミニウム、トリシクロヘキシルアルミニウム、トリオクチルアルミニウム;水素化ジエチルアルミニウム、水素化ジ-n-プロピルアルミニウム、水素化ジ-n-ブチルアルミニウム、水素化ジイソブチルアルミニウム、水素化ジヘキシルアルミニウム、水素化ジイソヘキシルアルミニウム、水素化ジオクチルアルミニウム、水素化ジイソオクチルアルミニウム;エチルアルミニウムジハイドライド、n-プロピルアルミニウムジハイドライド、イソブチルアルミニウムジハイドライド等が挙げられ、これらの中でも、トリエチルアルミニウム、トリイソブチルアルミニウム、水素化ジエチルアルミニウム、水素化ジイソブチルアルミニウムが好ましい。以上に述べた(C)成分としての有機金属化合物は、1種単独で使用することも、2種以上を混合して用いることもできる。なお、上記第三重合触媒組成物における有機アルミニウム化合物の含有量は、(A)成分に対して1~50倍モルであることが好ましく、約10倍モルであることが更に好ましい。
本発明のゴム組成物としては、本発明の共重合体を含む限り、特に制限はなく、目的に応じて適宜選択することができるが、本発明の共重合体以外のゴム成分、無機充填剤、カーボンブラック、架橋剤、などを含むことが好ましい。
本発明の共重合体のゴム成分中の含有量としては、特に制限はなく、目的に応じて適宜選択することができるが、3質量%以上が好ましい。
本発明の共重合体のゴム成分中の含有量が、3質量%未満であると、本発明の特徴が小さかったり、またはその特徴を発揮しなかったりすることがある。
前記ゴム成分としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、本発明の共重合体、天然ゴム、各種ブタジエンゴム、各種スチレン-ブタジエン共重合体ゴム、イソプレンゴム、ブチルゴム、イソブチレンとp-メチルスチレンの共重合体の臭化物、ハロゲン化ブチルゴム、アクリロニトリロブタジエンゴム、クロロプレンゴム、エチレン-プロピレン共重合体ゴム、エチレン-プロピレン-ジエン共重合体ゴム、スチレン-イソプレン共重合体ゴム、スチレン-イソプレン-ブタジエン共重合体ゴム、イソプレン-ブタジエン共重合体ゴム、クロロスルホン化ポリエチレン、アクリルゴム、エピクロルヒドリンゴム、多硫化ゴム、シリコーンゴム、フッ素ゴム、ウレタンゴム、などが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。
<無機充填剤>
前記無機充填剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば、シリカ、水酸化アルミニウム、クレー、アルミナ、タルク、マイカ、カオリン、ガラスバルーン、ガラスビーズ、炭酸カルシウム、炭酸マグネシウム、水酸化マグネシウム、炭酸カルシウム、酸化マグネシウム、酸化チタン、チタン酸カリウム、硫酸バリウムなどが挙げられる。これらは、1種単独で使用してもよいし、2種以上を併用してもよい。なお、無機充填剤を用いる時は適宜シランカップリング剤を使用してもよい。
前記補強性充填剤の含有量が、5質量部未満であると、補強性充填剤を入れる効果があまりみられないことがあり、200質量部を超えると前記ゴム成分に補強性充填剤が混ざり込まなくなる傾向があり、ゴム組成物としての性能を低下させることがある。
前記架橋剤としては、特に制限はなく、目的に応じて適宜選択することができ、例えば硫黄系架橋剤、有機過酸化物系架橋剤、無機架橋剤、ポリアミン架橋剤、樹脂架橋剤、硫黄化合物系架橋剤、オキシム-ニトロソアミン系架橋剤硫黄などが挙げられるが、中でもタイヤ用ゴム組成物としては硫黄系架橋剤がより好ましい。
前記架橋剤の含有量が0.1質量部未満では、架橋がほとんど進行しなかったり、20質量部を超えると一部の架橋剤により混練り中に架橋が進んでしまう傾向があったり、加硫物の物性が損なわれたりすることがある。
その他に加硫促進剤を併用することも可能であり、加硫促進剤としては、グアジニン系、アルデヒド-アミン系、アルデヒド-アンモニア系、チアゾール系、スルフェンアミド系、チオ尿素系、チウラム系、ジチオカルバメート系、ザンテート系等の化合物が使用できる。
また必要に応じて、補強剤、軟化剤、充填剤、加硫助剤、着色剤、難燃剤、滑剤、発泡剤、可塑剤、加工助剤、酸化防止剤、老化防止剤、スコーチ防止剤、紫外線防止剤、帯電防止剤、着色防止剤、その他の配合剤など公知のものをその使用目的に応じて使用することができる。
本発明の架橋ゴム組成物は、本発明のゴム組成物を架橋して得られたものである限り、特に制限はなく、目的に応じて適宜選択することができる。
前記架橋の条件としては、特に制限はなく、目的に応じて適宜選択することができるが、温度120℃~200℃、加温時間1分間~900分間が好ましい。
本発明のタイヤは、本発明のゴム組成物、又は、本発明の架橋ゴム組成物を用いたものである限り、特に制限はなく、目的に応じて適宜選択することができる。
本発明のゴム組成物、又は、本発明の架橋ゴム組成物のタイヤにおける適用部位としては、例えば、トレッド、ベーストレッド、サイドウォール、サイド補強ゴム及びビードフィラーなどが挙げられるが、これに限定されない。
前記タイヤを製造する方法としては、慣用の方法を用いることができる。例えば、タイヤ成形用ドラム上に未加硫ゴムからなるカーカス層、ベルト層、トレッド層等の通常タイヤ製造に用いられる部材を順次貼り重ね、ドラムを抜き去ってグリーンタイヤとする。次いで、このグリーンタイヤを常法に従って加熱加硫することにより、所望のタイヤを製造することができる。
タイヤ用途以外にも、防振ゴム、免震ゴム、ベルト(コンベアベルト)、ゴムクローラ、各種ホース、モランなどに本発明のゴム組成物、又は、本発明の架橋ゴム組成物を使用することができる。
窒素雰囲気下のもと、(2-PhC9H6)2Nd[N(SiHMe2)2](2.00g,3.03mmol)のトルエン溶液50mLに、AlMe3(9.0mmol)を含むトルエン溶液(アルドリッチ社製)4.5mlをゆっくり滴下し、室温で16時間攪拌した。その後、トルエンを減圧留去し、残留物をヘキサンで数回洗浄したところ緑色粉末である(2-PhC9H6)2Nd(μ-Me)2AlMe2(1.60g,86%)を得た。得られたメタロセン系複合触媒の構造確認は、1H-NMRによって行われた。なお、1H-NMRは、トルエン-d8を溶媒とし、20℃で測定を行った。
十分に乾燥した400ml耐圧ガラス反応器に、1,3-ブタジエン3.95g(0.073mol)を含むトルエン溶液320mlを添加した後、エチレンを0.6MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にジメチルアルミニウム(μ-ジメチル)ビス(2-フェニルインデニル)ネオジム[(2-PhC9H6)2Nd(μ-Me)2AlMe2]204.0μmol、及びトリフェニルカルボニウムテトラキス(ペンタフルオロフェニル)ボレート[Ph3CB(C6F5)4]195.0μmolを仕込み、トルエン20mlに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、モノマー溶液へ添加し、室温で90分間重合を行った。重合後、2,2´-メチレン-ビス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mlを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Aを得た。得られた共重合体Aの収量は3.60gであった。なお、図1は共重合体Aの1H-NMRスペクトルチャートを示し、図2は共重合体Aの13C-NMRスペクトルチャートを示し、図3は共重合体AのDSC曲線を示す。
十分に乾燥した400ml耐圧ガラス反応器に、トルエン溶液160mlを添加した後、エチレンを0.8MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にビス(2-フェニルインデニル)ガドリニウムビス(ジメチルシリルアミド)[(2-PhC9H6)2GdN(SiHMe2)2]28.5μmol、ジメチルアニリニウムテトラキス(ペンタフルオロフェニル)ボレート[Me2NHPhB(C6F5)4]34.2μmol、及びジイソブチルアルミニウムハイドライド1.43mmolを仕込み、トルエン8mlに溶解させて触媒溶液とした。次に、グローブボックスから触媒溶液を取り出し、ガドリニウム換算で28.2μmolとなる量をモノマー溶液へ添加すると同時に、1,3-ブタジエンを含むトルエン溶液を1,3-ブタジエン換算で0.3g/minの速度にて60分間連続的に添加した後、さらに30分間重合を行った。重合後、2,2´-メチレン-ビス(4-エチル-6-t-ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mlを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Bを得た。得られた共重合体Bの収量は15.50gであった。なお、図4は共重合体Bの13C-NMRスペクトルチャートを示し、図5は共重合体BのDSC曲線を示す。
十分に乾燥した2Lステンレス反応器に、1,3-ブタジエン28.0g(0.52mol)を含むトルエン溶液700mlを添加した後、エチレンを0.8MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にジメチルアルミニウム(μ-ジメチル)ビス(2-フェニルインデニル)ネオジウム[(2-PhC9H6)2Nd(μ-Me)2AlMe2]400.0μmol、トリフェニルカルボニウムテトラキス(ペンタフルオロフェニル)ボレート(Ph3CB(C6F5)4)200.0μmolを仕込み、トルエン80mlに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、ネオジウム換算で390.0μmolとなる量をモノマー溶液へ添加し、室温で120分間重合を行った。重合後、2,2´-メチレンービス(4‐エチル-6‐t‐ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mlを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し共重合体Cを得た。得られた共重合体Cの収量は18.00gであった。
十分に乾燥した400ml耐圧ガラス反応器に、1,3-ブタジエン2.83g(0.052mol)を含むトルエン溶液120mlを添加した後、エチレンを0.8MPaで導入した。一方、窒素雰囲気下のグローブボックス中で、ガラス製容器にビス(2-メチルインデニル)プラセオジウムビス(ジメチルシリルアミド)(2-MeC9H6)2Pr{N(SiHMe2)2} 27.0μmol、トリフェニルカルボニウムテトラキス(ペンタフルオロフェニル)ボレート(Ph3CB(C6F5)4)27.0μmol、及びトリイソブチルアルミニウム1.35mmolを仕込み、トルエン5mlに溶解させて触媒溶液とした。その後、グローブボックスから触媒溶液を取り出し、モノマー溶液へ添加し、50℃で60分間重合を行った。重合後、2,2´‐メチレンービス(4‐エチル-6‐t‐ブチルフェノール)(NS-5)5質量%のイソプロパノール溶液1mlを加えて反応を停止させ、さらに大量のメタノールで共重合体を分離し、70℃で真空乾燥し重合体Dを得た。得られた共重合体Dの収量は1.50gであった。
比較例サンプルとして、ブタジエンゴム(BR01、JSR製)を準備した。
共重合体中のブタジエン部分のミクロ構造(1,2-ビニル結合量)を、1H-NMRスペクトル(100℃、d-テトラクロロエタン標準:6ppm)により1,2-ビニル結合成分(5.0-5.1ppm)と全体のブタジエン結合成分(5-5.6ppm)の積分比より求め、共重合体中のブタジエン部分のミクロ構造(シス-1,4結合量)を、13C-NMRスペクトル(100℃、d-テトラクロロエタン標準:73.8ppm)によりシス-1,4結合成分(26.5-27.5ppm)と全体のブタジエン結合成分(26.5-27.5ppm+31.5-32.5ppm)の積分比より求めた。1,2-ビニル結合量(%)、シス-1,4結合量(%)の計算値を表1に示す。
(2)エチレンの含有率
共重合体中のエチレン部分の含有率(mol%)を 13C-NMRスペクトル(100℃、d-テトラクロロエタン標準:73.8ppm)により全体のエチレン結合成分(28.5-30.0ppm)と全体のブタジエン結合成分(26.5-27.5ppm+31.5-32.5ppm)の積分比より求めた。エチレン部分の含有率(mol%)を表1に示す。
(3)重量平均分子量(Mw)及び分子量分布(Mw/Mn)
ゲルパーミエーションクロマトグラフィー[GPC:東ソー製HLC-8121GPC/HT、カラム:東ソー製GMHHR-H(S)HT×2本、検出器:示差屈折率計(RI)]で単分散ポリスチレンを基準として、重合体のポリスチレン換算の重量平均分子量(Mw)及び分子量分布(Mw/Mn)を求めた。なお、測定温度は140℃である。
(4)DSC曲線
JIS K7121-1987に準拠して示差走査熱量測定(DSC)を行い、DSC曲線を描き、ブロックポリエチレン融点(DSCピーク温度)を測定した。なお、測定は、単体ポリマーや触媒残渣等の不純物の影響を避けるため、共重合体を大量のテトラヒドロフランに48h浸漬し、テトラヒドロフランに溶解する成分を全て取り除いた後、乾燥したゴム成分をサンプルとして使用した。
図1の共重合体Aの1H-NMRスペクトルチャートでは、1.3ppm~1.6ppmにエチレンの由来するピークが見られる。また図2の共重合体Aの13C-NMRスペクトルスペクトルでは、27.5ppm~33ppmにエチレンに由来するピークが見られ、さらに詳細にみると、エチレンが4連鎖以上であることを示す29.4ppmのピーク以外のピークが多く観測され、エチレンが3連鎖以下で不規則にブタジエン中に配列していることが示された。なお、文献に記載された環状構造もほとんど有していないことも確認された。
また、図3の共重合体AのDSC曲線では、エチレンの単量体単位からなるブロック部分に由来する120℃付近の結晶化温度が観測されない。
以上より、共重合体Aは、環状構造をほとんど含まず、1,4結合と1,2結合(3.4結合含む)とエチレン結合から構成され、エチレンの単量体単位からなるブロック部分がなく、1,3-ブタジエン及びエチレンの単量体単位が不規則に配列してなるランダム共重合体であることが分かる。
以上より、共重合体Bも、1,3-ブタジエン及びエチレンの単量体単位が不規則に配列してなるランダム共重合体であることが分かる。
また、共重合体C,Dについても、同様に、1,3-ブタジエン及びエチレンの単量体が不規則に配列してなるランダム共重合体であることを確認した。
加硫サンプルを100℃のオーブン中で48時間熱劣化させた後、サンプル取り出しJIS K6251に従って、室温にて引っ張り試験による破断点伸びを測定した。熱劣化を行わないサンプルの引っ張り試験による破断点伸びを100として、表3に伸び保持率(%)として表示した。
保持率(%)が大きい程、耐熱性が良好であることを示す。
JIS3号試験片中心部に0.5mmの亀裂を入れ、室温で0%~100%の一定歪で繰り返し疲労を与え、サンプルが切断するまでの回数を測定した。指数値が大きい程、耐亀裂成長性が良好であることを示す。
Claims (17)
- 共役ジエン化合物及び非共役オレフィンの単量体単位が不規則に配列してなるランダム共重合体であることを特徴とする共役ジエン化合物と非共役オレフィンとの共重合体。
- 共役ジエン化合物部分のシス-1,4結合量が25%以上であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記共役ジエン化合物部分のシス-1,4結合量が50%超であることを特徴とする請求項2に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンの含有量が、0mol%を超え且つ50mol%以下であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンの含有量が、0mol%を超え且つ20mol%以下であることを特徴とする請求項4に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記共役ジエン化合物部分の1,2付加体(3,4付加体を含む)含量が5%以下であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- ポリスチレン換算重量平均分子量が10,000~10,000,000であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 分子量分布(Mw/Mn)が10以下であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、非環状オレフィンであることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンは、炭素数が2~10であることを特徴とする請求項1又は9に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、エチレン、プロピレン及び1-ブテンよりなる群から選択される少なくとも一種であることを特徴とする請求項9又は10に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記非共役オレフィンが、エチレンであることを特徴とする請求項11に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 前記共役ジエン化合物が、1,3-ブタジエン及びイソプレンよりなる群から選択される少なくとも一種であることを特徴とする請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体。
- 請求項1に記載の共役ジエン化合物と非共役オレフィンとの共重合体を含むことを特徴とするゴム組成物。
- ゴム成分100質量部に対し、補強性充填剤5質量部~200質量部と、架橋剤0.1質量部~20質量部とを含むことを特徴とする請求項14に記載のゴム組成物。
- 請求項14に記載のゴム組成物を架橋して得られたことを特徴とする架橋ゴム組成物。
- 請求項14に記載のゴム組成物、又は、請求項16に記載の架橋ゴム組成物を用いたことを特徴とするタイヤ。