WO2011138290A1 - Procédé de revêtement autophorétique, matériau de revêtement et vernis multicouche - Google Patents
Procédé de revêtement autophorétique, matériau de revêtement et vernis multicouche Download PDFInfo
- Publication number
- WO2011138290A1 WO2011138290A1 PCT/EP2011/056983 EP2011056983W WO2011138290A1 WO 2011138290 A1 WO2011138290 A1 WO 2011138290A1 EP 2011056983 W EP2011056983 W EP 2011056983W WO 2011138290 A1 WO2011138290 A1 WO 2011138290A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- substrate
- coating
- groups
- monomer
- acid
- Prior art date
Abstract
L'invention concerne un procédé pour le revêtement autophorétique d'un substrat métallique à une valeur de pH allant de 1 à 4 et un temps d'immersion du substrat de 1 s à 15 min dans une dispersion polymère aqueuse, qui comporte au moins un copolymère séquencé (méth) acrylique hydrosoluble et/ou dispersible dans l'eau, lequel comprend, intégrés par polymérisation, au moins un monomère oléfiniquement insaturé (a) possédant un groupe de coordination d'ions métalliques, au moins un monomère oléfiniquement insaturé (b) différent du monomère (a) possédant un groupe réticulé B et du diphényléthylène. Selon la présente invention, le substrat métallique n'est pas traité au moyen de substances corrosives avant le revêtement autophorétique. La présente invention concerne en outre un matériau de revêtement correspondant et un vernis multicouche qui comprend une couche correspondante déposée par voie autophorétique.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102010019245.7 | 2010-05-03 | ||
DE102010019245A DE102010019245A1 (de) | 2010-05-03 | 2010-05-03 | Verfahren zur autophoretischen Beschichtung, Beschichtungsmittel und Mehrschichtlackierung |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2011138290A1 true WO2011138290A1 (fr) | 2011-11-10 |
WO2011138290A8 WO2011138290A8 (fr) | 2012-01-26 |
Family
ID=44260793
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2011/056983 WO2011138290A1 (fr) | 2010-05-03 | 2011-05-02 | Procédé de revêtement autophorétique, matériau de revêtement et vernis multicouche |
Country Status (2)
Country | Link |
---|---|
DE (1) | DE102010019245A1 (fr) |
WO (1) | WO2011138290A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015043680A1 (fr) * | 2013-09-30 | 2015-04-02 | Basf Coatings Gmbh | Procédé permettant le revêtement autophorétique de substrats métalliques par traitement postérieur du revêtement au moyen d'une composition aqueuse sol-gel |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3727382A1 (de) | 1987-08-17 | 1989-03-02 | Henkel Kgaa | Addukte von carbonsaeuren und isocyanaten an epoxide, derartige addukte enthaltende waessrige dispersionen, verfahren zu ihrer herstellung und ihre verwendung in der autophoretischen beschichtung metallischer oberflaechen |
WO1996010461A1 (fr) | 1994-09-30 | 1996-04-11 | Henkel Corporation | Traitement destine a l'amelioration de la resistance a la corrosion des revetements autodeposes sur des surfaces metalliques |
DE19858708A1 (de) | 1998-12-18 | 2000-06-21 | Basf Coatings Ag | Verfahren zur Herstellung eines polymeren Umsetzungsprodukts |
DE10126651A1 (de) * | 2001-06-01 | 2002-12-12 | Basf Coatings Ag | Pulverlacksuspensionen (Pulverslurries) und Pulverlacke, Verfahren zu ihrer Herstellung und ihre Verwendung |
DE10206983A1 (de) | 2002-02-20 | 2003-09-04 | Basf Coatings Ag | Verfahren zur Herstellung wässriger Dispersionen von Blockmischpolymerisaten |
DE10256226A1 (de) | 2002-12-02 | 2004-06-17 | Basf Coatings Ag | Verfahren zur Herstellung von Mischpolymerisaten olefinisch ungesättigter Monomere |
DE10330413A1 (de) | 2003-07-04 | 2005-01-20 | Basf Ag | Caprolactam-blockierte Isocyanate sowie deren Verwendung zur Beschichtung von Oberflächen |
DE102006053291A1 (de) | 2006-11-13 | 2008-05-15 | Basf Coatings Ag | Lackschichtbildendes Korrosionsschutzmittel mit guter Haftung und Verfahren zu dessen stromfreier Applikation |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH07501444A (ja) * | 1991-11-12 | 1995-02-16 | プロメガ コーポレイション | 非放射性酵素検定 |
-
2010
- 2010-05-03 DE DE102010019245A patent/DE102010019245A1/de not_active Withdrawn
-
2011
- 2011-05-02 WO PCT/EP2011/056983 patent/WO2011138290A1/fr active Application Filing
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3727382A1 (de) | 1987-08-17 | 1989-03-02 | Henkel Kgaa | Addukte von carbonsaeuren und isocyanaten an epoxide, derartige addukte enthaltende waessrige dispersionen, verfahren zu ihrer herstellung und ihre verwendung in der autophoretischen beschichtung metallischer oberflaechen |
WO1996010461A1 (fr) | 1994-09-30 | 1996-04-11 | Henkel Corporation | Traitement destine a l'amelioration de la resistance a la corrosion des revetements autodeposes sur des surfaces metalliques |
DE19858708A1 (de) | 1998-12-18 | 2000-06-21 | Basf Coatings Ag | Verfahren zur Herstellung eines polymeren Umsetzungsprodukts |
DE10126651A1 (de) * | 2001-06-01 | 2002-12-12 | Basf Coatings Ag | Pulverlacksuspensionen (Pulverslurries) und Pulverlacke, Verfahren zu ihrer Herstellung und ihre Verwendung |
DE10206983A1 (de) | 2002-02-20 | 2003-09-04 | Basf Coatings Ag | Verfahren zur Herstellung wässriger Dispersionen von Blockmischpolymerisaten |
DE10256226A1 (de) | 2002-12-02 | 2004-06-17 | Basf Coatings Ag | Verfahren zur Herstellung von Mischpolymerisaten olefinisch ungesättigter Monomere |
DE10330413A1 (de) | 2003-07-04 | 2005-01-20 | Basf Ag | Caprolactam-blockierte Isocyanate sowie deren Verwendung zur Beschichtung von Oberflächen |
DE102006053291A1 (de) | 2006-11-13 | 2008-05-15 | Basf Coatings Ag | Lackschichtbildendes Korrosionsschutzmittel mit guter Haftung und Verfahren zu dessen stromfreier Applikation |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015043680A1 (fr) * | 2013-09-30 | 2015-04-02 | Basf Coatings Gmbh | Procédé permettant le revêtement autophorétique de substrats métalliques par traitement postérieur du revêtement au moyen d'une composition aqueuse sol-gel |
CN105579614A (zh) * | 2013-09-30 | 2016-05-11 | 巴斯夫涂料有限公司 | 通过用水性溶胶-凝胶组合物后处理涂层而自泳涂覆金属基材的方法 |
US20160244882A1 (en) * | 2013-09-30 | 2016-08-25 | Basf Coatings Gmbh | Method for autophoretic coating of metallic substrates with aftertreatment of the coating with an aqueous sol-gel composition |
Also Published As
Publication number | Publication date |
---|---|
DE102010019245A1 (de) | 2012-01-19 |
WO2011138290A8 (fr) | 2012-01-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2616191B1 (fr) | Procédé de revêtement de surfaces et utilisation des objets revêtus selon ce procédé | |
EP2133371B1 (fr) | Agent anti-corrosion formant une couche avec bonne adhérence et son application sans courant électrique | |
EP2367638B1 (fr) | Procédé de revêtement de surfaces par des particules, et utilisation des revêtements fabriqués par ce procédé | |
AU2013349598B9 (en) | Method for coating metal surfaces of substrates, and objects coated according to said method | |
EP2812130B1 (fr) | Procédé destiné à revêtir des surfaces métalliques de substrats | |
EP3019563B1 (fr) | Procédé de revêtement de surfaces métalliques de substrats et objets revêtus par ledit procédé | |
EP1883679B1 (fr) | Agent anticorrosion formant une couche de vernis et procede pour son application sans courant | |
EP3022330B1 (fr) | Procédé de revêtement de surfaces métalliques de substrats et objets revêtus par ce procédé | |
EP3475464B1 (fr) | Procédé amélioré de prétraitement de protection anticorrosion d'une surface métallique qui contient de l'acier, de l'acier galvanisé, de l'aluminium, du magnésium et/ou un alliage de zinc et de magnésium | |
DE10310972A1 (de) | Stickstoffhaltige Polymere für die Metalloberflächenbehandlung | |
EP2118337A1 (fr) | Procédé d'apprêt anticorrosion pour des substrats métalliques | |
DE102009007633A1 (de) | Korrosionsstabile Mehrschichtlackierung und Verfahren zu deren Herstellung | |
WO2010089017A1 (fr) | Produit de revêtement pour peintures résistantes à la corrosion | |
EP2094793A1 (fr) | Agent anticorrosion formant une couche de vernis à fissuration réduite, et procédé pour son application sans courant | |
EP3142800A1 (fr) | Procédé de revêtement de surfaces métalliques de substrats et objets revêtus selon ce procédé | |
EP1570109B1 (fr) | Procede pour revetir des substrats metalliques avec un agent de revetement polymerisable par polymerisation radicalaire, et substrats ainsi revetus | |
WO2011138290A1 (fr) | Procédé de revêtement autophorétique, matériau de revêtement et vernis multicouche |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 11717275 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 11717275 Country of ref document: EP Kind code of ref document: A1 |