WO2011082058A1 - Conductive polymer foams, method of manufacture, and uses thereof - Google Patents
Conductive polymer foams, method of manufacture, and uses thereof Download PDFInfo
- Publication number
- WO2011082058A1 WO2011082058A1 PCT/US2010/061774 US2010061774W WO2011082058A1 WO 2011082058 A1 WO2011082058 A1 WO 2011082058A1 US 2010061774 W US2010061774 W US 2010061774W WO 2011082058 A1 WO2011082058 A1 WO 2011082058A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- foam
- electrically conductive
- polymer foam
- conductive particles
- Prior art date
Abstract
Description
Claims