WO2011061922A1 - 透明導電膜の製造方法、透明導電膜の製造装置、スパッタリングターゲット及び透明導電膜 - Google Patents
透明導電膜の製造方法、透明導電膜の製造装置、スパッタリングターゲット及び透明導電膜 Download PDFInfo
- Publication number
- WO2011061922A1 WO2011061922A1 PCT/JP2010/006713 JP2010006713W WO2011061922A1 WO 2011061922 A1 WO2011061922 A1 WO 2011061922A1 JP 2010006713 W JP2010006713 W JP 2010006713W WO 2011061922 A1 WO2011061922 A1 WO 2011061922A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- transparent conductive
- conductive film
- component
- film
- sputtering
- Prior art date
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
- C23C14/08—Oxides
- C23C14/086—Oxides of zinc, germanium, cadmium, indium, tin, thallium or bismuth
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K13/00—Etching, surface-brightening or pickling compositions
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
- C23C14/08—Oxides
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/22—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the process of coating
- C23C14/34—Sputtering
- C23C14/3407—Cathode assembly for sputtering apparatus, e.g. Target
- C23C14/3414—Metallurgical or chemical aspects of target preparation, e.g. casting, powder metallurgy
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/22—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the process of coating
- C23C14/34—Sputtering
- C23C14/35—Sputtering by application of a magnetic field, e.g. magnetron sputtering
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/22—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the process of coating
- C23C14/54—Controlling or regulating the coating process
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/58—After-treatment
- C23C14/5806—Thermal treatment
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
- C23C14/58—After-treatment
- C23C14/5873—Removal of material
Definitions
- the present invention relates to a method for producing a transparent conductive film excellent in etching characteristics, conductive characteristics, etc., a transparent conductive film production apparatus, a sputtering target, and a transparent conductive film.
- ITO Indium Tin Oxide
- ITO films mainly composed of indium oxide and tin oxide are widely used as transparent conductive films.
- the ITO film is formed by a vacuum deposition method, a sputtering method, or the like, and a sputtering target made of ITO is often used in the sputtering method.
- the ITO film formed at room temperature is in a state where both crystalline and amorphous are mixed, it is difficult to obtain desired conductive characteristics.
- an ITO film formed at a temperature of 200 ° C. or higher has a high conductive property because it is in a crystalline state.
- the crystallized ITO film has low solubility in a weak acid such as oxalic acid, and it is necessary to use a strong acid such as hydrochloric acid or sulfuric acid as an etching solution. For this reason, it is difficult to ensure a high etching selectivity between the ITO film and its underlying film or other wiring layers.
- an object of the present invention is to provide a method for producing a transparent conductive film, which can form a transparent conductive film having good etching characteristics and conductive characteristics without using water vapor. is there.
- an object of the present invention is to provide a transparent conductive film manufacturing apparatus and a sputtering target capable of forming a transparent conductive film having good etching characteristics and conductive characteristics without using water vapor.
- a method for producing a transparent conductive film includes a first component made of indium oxide, a second component made of tin oxide, lanthanum, neodymium, dysprosium, europium, Placing the substrate in a chamber having a target material comprising a third component comprising at least one element selected from gadolinium, terbium, zirconium, aluminum, silicon, titanium, and boron or an oxide thereof. . By sputtering the target material, an indium tin oxide thin film is formed on the substrate.
- a transparent conductive film manufacturing apparatus includes a chamber, a support portion, and a film formation portion.
- the chamber is configured to be able to maintain a vacuum state.
- the support is for supporting a substrate in the chamber.
- the film forming unit includes a first component made of indium oxide, a second component made of tin oxide, and lanthanum, neodymium, dysprosium, europium, gadolinium, terbium, zirconium, aluminum, silicon, titanium, and boron.
- a target material including at least one selected element or a third component made of an oxide thereof.
- the film forming unit forms the indium tin oxide thin film on the substrate supported by the support unit by sputtering the target material in the chamber.
- a sputtering target is a sputtering target for forming a transparent conductive film on a substrate by a sputtering method, and includes a first component, a second component, And a third component.
- the first component is made of indium oxide.
- the second component is made of tin oxide.
- the third component is composed of at least one element selected from lanthanum, neodymium, dysprosium, europium, gadolinium, terbium, zirconium, aluminum, silicon, titanium, and boron, or an oxide thereof.
- a transparent conductive film is a transparent conductive film formed over a substrate by a sputtering method, and includes a first component, a second component, and a first component. 3 ingredients.
- the first component is made of indium oxide.
- the second component is made of tin oxide.
- the third component is composed of at least one element selected from lanthanum, neodymium, dysprosium, europium, gadolinium, terbium, zirconium, aluminum, silicon, titanium, and boron, or an oxide thereof.
- a method for producing a transparent conductive film according to an embodiment of the present invention includes a first component made of indium oxide, a second component made of tin oxide, lanthanum, neodymium, dysprosium, europium, gadolinium, terbium, zirconium, and aluminum. And disposing a substrate in a chamber having a target material including at least one element selected from silicon, titanium, and boron or a third component made of an oxide thereof. By sputtering the target material, an indium tin oxide thin film is formed on the substrate.
- an amorphous indium tin oxide thin film (hereinafter also referred to as “ITO film”) can be formed as it is. Therefore, when the ITO film is patterned by etching, a weakly acidic etching solution such as oxalic acid can be used. In addition, it becomes easy to ensure a high etching selectivity between the base film and other wiring layers, so that good etching characteristics can be obtained. Furthermore, by crystallization of the ITO film by heat treatment (annealing), good conductive properties can be imparted. Since the heat-treated ITO film has good transmittance characteristics in the visible light region, it can be suitably used as a transparent conductive film for flat panel displays, solar power generation modules and the like.
- the substrate on which the ITO film is formed is typically a glass substrate, but may also be a silicon substrate or a ceramic substrate. Further, an organic substrate can be used as long as it has heat resistance with respect to the heat treatment temperature.
- the third component is an element group capable of forming an ITO film soluble in a weak acid.
- Dy dysprosium
- an oxide thereof as the third component, an ITO film having a specific resistance of 300 ⁇ ⁇ cm or less and excellent conductive properties can be obtained.
- the gas for sputtering the target material can be a mixed gas of argon and oxygen.
- Argon primarily generates ions that sputter the target material.
- Oxygen functions as a reactive gas and adjusts the oxygen concentration of the deposited ITO film. By appropriately adjusting the oxygen partial pressure, an ITO film having desired conductive characteristics and etching characteristics can be formed.
- the heat treatment temperature (annealing temperature) for crystallizing the ITO film can be 200 ° C. or higher. When the heat treatment temperature is lower than 200 ° C., amorphous and crystal may be mixed in the ITO film.
- the upper limit of the heat treatment temperature is not particularly limited, and is appropriately set according to the heat resistance of the substrate on which the ITO film is formed.
- a transparent conductive film manufacturing apparatus includes a chamber, a support part, and a film forming part.
- the chamber is configured to be able to maintain a vacuum state.
- the support is for supporting a substrate in the chamber.
- the film forming unit includes a first component made of indium oxide, a second component made of tin oxide, and La, Nd, Dy, Eu, Gd, Tb, Zr, Al, Si, Ti, and B.
- a target material including at least one selected element or a third component made of an oxide thereof.
- the film forming unit forms the indium tin oxide thin film on the substrate supported by the support unit by sputtering the target material in the chamber.
- a sputtering target is a sputtering target for forming a transparent conductive film on a substrate by a sputtering method, and includes a first component, a second component, and a third component. And ingredients.
- the first component is made of indium oxide.
- the second component is made of tin oxide.
- the third component is composed of at least one element selected from La, Nd, Dy, Eu, Gd, Tb, Zr, Al, Si, Ti, and B or an oxide thereof.
- an amorphous ITO film can be formed on a substrate by sputtering the target material (sputtering target) having the above structure. Therefore, when the ITO film is patterned by etching, a weakly acidic etching solution such as oxalic acid can be used. In addition, it becomes easy to ensure a high etching selectivity between the base film and other wiring layers, so that good etching characteristics can be obtained.
- FIG. 1 is a schematic view showing a transparent conductive film manufacturing apparatus according to an embodiment of the present invention.
- the illustrated apparatus is configured as a sputtering apparatus 100 for forming a transparent conductive film.
- the sputtering apparatus 100 connects a film forming chamber 101 for forming a transparent conductive film (ITO film) F on the surface of the substrate S, a load / unload chamber 102, and the film forming chamber 101 and the load / unload chamber 102. And a gate valve 103.
- ITO film transparent conductive film
- the film forming chamber 101 includes a first chamber 11 having a sealed structure and an evacuation system 30 that can evacuate the inside of the first chamber 11.
- the film forming chamber 101 can be evacuated to a predetermined film forming pressure and can maintain the degree of vacuum.
- the vacuum exhaust system 30 includes a main pump (turbo molecular pump) 31 and an auxiliary pump (rotary pump) 32 that exhausts the back pressure side.
- the film formation chamber 101 has a sputtering cathode 20.
- the sputtering cathode 20 includes a sputtering target (hereinafter simply referred to as “target”) 21, a magnet unit 22 for forming a magnetic field on the surface of the target 21, and the target 21 and the substrate S (and the first chamber 11). And a DC power source (not shown) for applying a DC voltage therebetween.
- the target 21 is made of an indium tin oxide-based material.
- the sputtering cathode 20 is installed on the bottom wall portion of the first chamber 11 as a DC magnetron type sputtering cathode.
- the film forming chamber 101 includes a gas introduction unit 40 for introducing a process gas (sputtering gas) for sputtering into the first chamber 11.
- the gas introduction unit 40 constitutes a gas introduction system together with a gas supply source, a flow rate adjustment valve, and the like (not shown).
- the gas introduction unit 40 introduces a mixed gas of argon (Ar) and oxygen (O 2 ) into the first chamber 11.
- the partial pressure of oxygen in the mixed gas atmosphere is, for example, 2.0E-3 (2.0 ⁇ 10 ⁇ 3 ) Pa or more and 1.0E-2 (1.0 ⁇ 10 ⁇ 2 ) Pa or less.
- the film formation chamber 101 may have a deposition plate for preventing the film formation material from adhering to the inner wall of the first chamber 11 and other structures.
- a deposition plate for preventing the film formation material from adhering to the inner wall of the first chamber 11 and other structures.
- the load / unload chamber 102 includes a second chamber 12 having a sealed structure, and a vacuum pump 33 capable of evacuating the inside of the second chamber 12.
- the load / unload chamber 102 can be evacuated to a degree of vacuum comparable to the pressure in the film forming chamber 101, and can be maintained at that degree of vacuum.
- the load / unload chamber 102 has a door valve (not shown), and the substrate S can be transferred between the inside and the outside of the second chamber 12 via the door valve. When the substrate S is delivered, the load / unload chamber 102 is at atmospheric pressure.
- the sputtering apparatus 100 of this embodiment further includes a carrier 50 that transports the substrate S between the film forming chamber 101 and the load / unload chamber 102 via the gate valve 103.
- the carrier 50 is linearly moved against a guide rail (not shown) spanned between the film forming chamber 101 and the load / unload chamber 102 by a driving source (not shown).
- the carrier 50 transported from the load / unload chamber 102 to the film formation chamber 101 is returned to the load / unload chamber 102 after reciprocating in the film formation chamber 101.
- the substrate S is held on the lower surface of the carrier 50 and is formed in the film forming chamber 101 in the process of passing immediately above the sputtering cathode 20.
- a glass substrate is used as the substrate S.
- the film formation surface of the substrate may be a glass surface that is a base material, or may be the surface of an insulating film already formed on the base material. Further, a metal wiring film such as copper may be present on the surface of the insulating film.
- the carrier 50 constitutes a “support portion” that supports the substrate S in the first chamber 11.
- the sputtering cathode 20 and the gas introduction unit 40 constitute a “film formation unit”.
- the film forming unit forms the indium tin oxide thin film on the substrate S supported by the carrier 50 by sputtering the target 21 in the first chamber 11.
- the magnet unit 22, the DC power source and the like constituting the sputtering cathode 20 constitute a “plasma generating mechanism”.
- the plasma generation mechanism generates ions for sputtering the target 21 by generating plasma of a sputtering gas (mixed gas of Ar and O 2 ) introduced into the first chamber 11 from the gas introduction unit 40. .
- the target 21 is configured as a target material or a sputtering target for forming the transparent conductive film F on the substrate S by sputtering.
- the target 21 is a disc-like or rectangular plate-like sintered body made of an indium tin oxide (hereinafter also referred to as “ITO”) material, and the sintering density thereof is, for example, 98% or more.
- ITO indium tin oxide
- the target 21 includes a first component made of indium oxide (In 2 O 3 ), a second component made of tin oxide (SnO), and a third component as an additive.
- the third component is lanthanum (La), neodymium (Nd), dysprosium (Dy), europium (Eu), gadolinium (Gd), terbium (Tb), zirconium (Zr), aluminum (Al), silicon (Si) , At least one element selected from titanium (Ti) and boron (B) or an oxide thereof.
- the third component is soluble in acid, and enables amorphous ITO to be formed immediately after film formation.
- the target 21 having the above structure is sputtered in the film forming chamber 101 to form the ITO film F containing the first, second, and third components on the substrate S. Therefore, the composition of the target 21 is appropriately adjusted according to the composition of the ITO film F to be formed.
- the oxygen concentration of the ITO film F may be adjusted by the oxygen partial pressure in the film formation chamber 101 during film formation.
- a typical weight ratio of indium oxide (first component) to tin oxide (second component) is 9: 1, but is adjusted in the range of 97.5: 2.5 to 85:15, for example. .
- the addition amount of the additive (third component) is represented by the following formula (1), where ⁇ is the additive element. 0.1 ⁇ ⁇ / (In + Sn + ⁇ ) ⁇ ⁇ 10 [atomic%] (1)
- the additive element is an oxide
- the oxide is ⁇ Ox
- the addition amount is expressed by the following equation (2). 0.06 ⁇ ⁇ Ox / (In 2 O 3 + SnO) + ⁇ Ox ⁇ ⁇ 6 [atomic%] (2)
- the amount of the third component added is less than 0.1 atomic%, it is difficult to stably form an amorphous ITO film. In other words, an ITO film in which crystalline and amorphous are mixed may be formed.
- the added amount of the third component exceeds 10 atomic%, it becomes difficult to obtain desired characteristics with respect to the conductive characteristics and light transmittance of the obtained ITO film.
- the addition amount of the third component varies depending on the type of element used, but is selected within the above range.
- an amorphous indium tin oxide thin film (ITO film) F can be formed on the substrate S. Since the ITO film F immediately after film formation is in an amorphous state, a weak acidic etching solution such as oxalic acid or acetic acid can be used when patterning the ITO film F. In addition, after patterning, the ITO film F is crystallized by annealing (heat treatment), whereby an ITO film F having a low specific resistance and excellent conductive characteristics can be obtained.
- annealing heat treatment
- FIG. 2 shows the process flow.
- the method for producing a transparent conductive film of the present embodiment includes an ITO film F film forming process (step ST1), an ITO film F patterning process (step ST2), and an ITO film F annealing process (step ST3). .
- step ST1 of the ITO film F the sputtering apparatus 100 shown in FIG. 1 is used.
- the substrate S carried into the load / unload chamber 102 is held on the lower surface of the carrier 50.
- the vacuum pump 33 is driven to evacuate the load / unload chamber 102.
- the gate valve 103 is opened and the carrier 50 is transferred into the film formation chamber 101.
- the gate valve 103 is closed.
- the carrier 50 transported to the film forming chamber 101 is moved linearly in the film forming chamber 101.
- the substrate S is formed by the sputtering cathode 20 while being moved together with the carrier 50.
- a sputtering gas Ar + O 2
- the introduced sputtering gas is excited by a DC electric field applied between the target 21 and the carrier 50 and a fixed magnetic field formed on the surface of the target 21 by the magnet unit 22, thereby generating a sputtering gas plasma.
- Ions (particularly Ar ions) in the plasma are attracted to the sputtering cathode 20 under the action of an electric field, and the surface of the target 21 is sputtered.
- oxygen contained in the sputtering gas generates highly active oxygen radicals, and the generated oxygen radicals react with ITO particles knocked out from the surface of the target 21. Therefore, the oxygen concentration of the ITO film F formed on the substrate S is controlled by the amount of oxygen in the sputtering gas.
- a so-called passing film formation method is employed in which film formation is performed while passing the substrate S above the target 21.
- the substrate S is formed on the forward path of the carrier 50 that reciprocates in the film forming chamber 101, but is not limited thereto, and may be formed on the return path of the carrier 50, or the forward path and the return path. Both may be formed into a film.
- the substrate S is transported through the film formation chamber 101 without heating (room temperature).
- a heating source may be incorporated in the sputtering apparatus 100 to heat the substrate to a predetermined temperature during film formation.
- the substrate S on which the ITO film F is formed is transferred to the load / unload chamber 102 through the gate valve 103 together with the carrier 50. Thereafter, the gate valve 103 is closed, the load / unload chamber 102 is opened to the atmosphere, and the film-formed substrate S is taken out through a door valve (not shown). As described above, the amorphous ITO film F is formed on the surface of the substrate S.
- the ITO film F is patterned into a predetermined shape by a wet etching method. Prior to this, a resist mask is formed on the ITO film F. In the etching step, the ITO film F exposed from the opening of the resist mask is dissolved by applying an etching solution on the surface of the substrate S from above the resist mask. Then, the patterning process of the ITO film
- an etching solution containing weakly acidic oxalic acid for example, oxalic acid or The ITO film F can be etched using a chemical solution (ITO-05N, ITO-06N, ITO-07N) (trade name) manufactured by Kanto Chemical.
- a chemical solution ITO-05N, ITO-06N, ITO-07N
- Kanto Chemical a chemical solution manufactured by Kanto Chemical.
- the patterning shape of the ITO film F differs depending on the type of device to be manufactured. For example, when an ITO film is used as a pixel electrode for a liquid crystal display, the ITO film F is patterned on a pixel basis. When the ITO film is used for a solar power generation module, the ITO film F is patterned in units of individual power generation cells.
- the ITO film F is crystallized by annealing (heat treatment) the patterned ITO film F.
- the purpose of crystallization of the ITO film F is to reduce the specific resistance of the ITO film F and improve the conductive characteristics.
- a heat treatment furnace is typically used.
- the annealing conditions can be set as appropriate, and can be set to 200 ° C. or higher in the atmosphere, for example.
- the annealing temperature is less than 200 ° C.
- the ITO film F may be mixed with crystals and amorphous.
- the upper limit of the annealing temperature is not particularly limited, and is appropriately determined depending on the heat resistance of the substrate S, ITO film F, or other functional thin film (insulating film, metal film) other than the ITO film F formed on the substrate S. Is set.
- the annealing atmosphere is not limited to air, and may be a nitrogen atmosphere, for example.
- the annealing time is set according to the annealing temperature. Typically, the annealing time is set shorter as the annealing temperature becomes higher.
- the transparent conductive film (ITO film F) As described above, the transparent conductive film (ITO film F) according to this embodiment is manufactured.
- the transparent conductive film of this embodiment includes a first component made of indium oxide, a second component made of tin oxide, La, Nd, Dy, Eu, Gd, Tb, Zr, Al, Si, Ti, and B. And a third component comprising at least one element selected from the group consisting of oxides thereof.
- the amorphous ITO film F can be formed as it is.
- an amorphous ITO film can be manufactured without adding water vapor to the sputtering gas. Therefore, adverse effects associated with the addition of water vapor to the sputtering gas, for example, generation of particles due to easy peeling of the ITO film attached to the deposition preventing plate, and the stable exhausting action of the film forming chamber 101 are hindered. It is possible to prevent variations in sputtering pressure due to the above.
- the ITO film F is crystallized by heat treatment (annealing), the ITO film F having good conductive characteristics can be manufactured. Since the ITO film F manufactured in this way has good transmittance characteristics in the visible light region, it can be suitably used as a transparent conductive film for flat panel displays, solar power generation modules and the like.
- Example 1 A sputtering target (hereinafter also referred to as “Dy-added ITO target”) in which 1.5 atomic% of dysprosium oxide was added to indium tin oxide was produced.
- Dy-added ITO target an ITO film having a thickness of 1000 mm (hereinafter also referred to as “Dy-added ITO film”) was formed on the substrate by the sputtering apparatus shown in FIG.
- the film forming conditions are as follows: DC power 600 W (1.16 W / cm 2 ), distance between target and substrate (T / S distance) 100 mm, magnetic unit magnetic field size 300 G, film forming rate (dynamic rate) 70 mm. ⁇ M / min.
- a mixed gas of argon and oxygen was used, and a plurality of ITO film samples were formed with different oxygen partial pressures.
- the partial pressure of argon is 0.67 Pa (200 sccm)
- the partial pressure of oxygen is 0 Pa, 1.33 ⁇ 10 ⁇ 3 Pa, 2.66 ⁇ 10 ⁇ 3 Pa, 5.32 ⁇ 10 ⁇ 3 Pa, 7.98. ⁇ 10 ⁇ 3 Pa and 1.06 ⁇ 10 ⁇ 2 Pa were set.
- the X-ray diffraction intensity of the ITO film sample produced at an oxygen partial pressure of 5.32 ⁇ 10 ⁇ 3 Pa was measured.
- “Rinto (trade name)” manufactured by Rigaku Corporation was used.
- the etching rate of each produced ITO film sample was measured.
- As the etching solution a chemical solution containing oxalic acid (“ITO-06N” (trade name) manufactured by Kanto Chemical Co., Inc.) was used. Subsequently, each ITO film sample was annealed in the atmosphere at 230 ° C. for 1 hour.
- the X-ray diffraction intensity, specific resistance, and visible light (wavelength: 400 nm to 800 nm) transmittance of each ITO film sample after annealing were measured.
- specific resistance “Loresta MCP-T350 (trade name)” manufactured by Mitsubishi Chemical Corporation was used.
- visible light transmittance ITO film samples prepared at an oxygen partial pressure of 5.32 ⁇ 10 ⁇ 3 Pa were used.
- visible light transmittance “U-4100” manufactured by Hitachi, Ltd. was used.
- Example 2 A sputtering target obtained by adding 1 atomic% of boron oxide to indium tin oxide (hereinafter also referred to as “B-added ITO target”) was produced. Using this B-added ITO target, an ITO film (hereinafter also referred to as “B-added ITO film”) was formed under the same conditions as in Example 1. With respect to the formed B-added ITO film, the etching rate, specific resistance, light transmittance, and X-ray diffraction intensity before and after annealing were measured under the same conditions as in Example 1.
- Example 1 A sputtering target in which 5 atomic% of cerium oxide was added to indium tin oxide (hereinafter referred to as “Ce-added ITO target”) was produced.
- An ITO film (hereinafter also referred to as “Ce-added ITO film”) was formed under the same conditions as in Example 1 using this Ce-added ITO target.
- the etching rate, specific resistance, light transmittance, and X-ray diffraction intensity before and after annealing were measured under the same conditions as in Example 1.
- Example 2 An ITO target containing indium oxide and tin oxide is sputtered in a sputtering gas containing argon, oxygen and water vapor to form an ITO film (hereinafter also referred to as “H 2 O-added ITO film”) on the substrate. A film was formed.
- the film formation conditions were the same as in Example 1, and the sputtering pressure was formed by changing the oxygen partial pressure to form a plurality of ITO films.
- the argon partial pressure is 0.67 Pa
- the water vapor partial pressure is 2.66 ⁇ 10 ⁇ 3 Pa
- the oxygen partial pressure is 0 Pa, 1.33 ⁇ 10 ⁇ 3 Pa, 2.66 ⁇ 10 ⁇ 3 Pa, 5 .32 ⁇ 10 ⁇ 3 Pa.
- the etching rate, specific resistance, light transmittance, and X-ray diffraction intensity before and after annealing were measured under the same conditions as in Example 1.
- an ITO film sample produced at an oxygen partial pressure of 1.33 ⁇ 10 ⁇ 3 Pa was used.
- the X-ray diffraction intensities before annealing of the Dy-added ITO film, B-added ITO film, Ce-added ITO film and H 2 O-added ITO film are shown in FIG. 3A, and the X-ray diffraction intensities after annealing are shown in FIG. B) respectively.
- FIG. 3A a halo pattern indicating an amorphous state was recognized in the X-ray diffraction pattern of the ITO film before annealing, that is, the ITO film immediately after the film formation.
- an intensity peak was observed at the diffraction angle inherent to the ITO crystal, and this confirmed that the annealed ITO film was in a crystalline state.
- FIGS. 4A and 4B are experimental results showing the specific resistance of each ITO film sample before and after annealing.
- FIG. 4A shows the state before annealing
- FIG. Each after annealing is shown.
- “ ⁇ ” indicates an H 2 O-added ITO film
- “ ⁇ ” indicates a Ce-added ITO film
- “ ⁇ ” indicates a Dy-added ITO film
- “ ⁇ ” indicates a B-added ITO film. (The same applies to FIG. 5).
- the specific resistance after annealing can be lower than that before annealing. This is because the specific resistance is lower in the crystalline state than in the amorphous state.
- the specific resistance after annealing is the minimum for any ITO film sample when the oxygen partial pressure is 5.32 ⁇ 10 ⁇ 3 Pa.
- About Dy-added ITO film and Ce-added ITO film are about 300 ⁇ cm, and B is added. The ITO film was about 400 ⁇ cm.
- the H 2 O-added ITO film it was confirmed that the minimum value of specific resistance (about 300 ⁇ cm) can be obtained by the annealing process when the oxygen partial pressure is 1.33 ⁇ 10 ⁇ 3 Pa. That is, it was confirmed that the specific resistances of the Dy-added ITO film and the Ce-added ITO film have values comparable to the specific resistance of the H 2 O-added ITO film.
- FIG. 5 is an experimental result showing the etching rate of each amorphous ITO film sample. It was confirmed that the Dy-added ITO film has an etching rate equivalent to that of the H 2 O-added ITO film. It was confirmed that the etching rate of the B-added ITO film was higher than the etching rate of the H 2 O-added ITO film. On the other hand, the Ce-added ITO film was confirmed to have a lower etching rate than the H 2 O-added ITO film. This is presumably because Ce oxide is less soluble in weak acids than Dy oxide and B oxide.
- FIG. 6 is an experimental result which shows the visible light transmittance
- an etching rate, specific resistance, and visible light transmittance equivalent to those of the H 2 O-added ITO film can be obtained. Further, by using the Dy-added sputtering target or the B-added sputtering target, an ITO film having excellent patterning characteristics, conductive characteristics, and light transmission characteristics can be stably formed.
- the addition amount of Dy in the Dy-added sputtering target is 1.5 atomic% and the addition amount of B in the B-added sputtering target is 1 atomic%, but is not limited thereto. Since the etching rate, specific resistance, visible light transmittance, etc. of the obtained ITO film change depending on the amount of addition of these third components, the amount of addition can be appropriately adjusted according to the required characteristics. is there.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Physical Vapour Deposition (AREA)
- Manufacturing Of Electric Cables (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Non-Insulated Conductors (AREA)
Priority Applications (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020147013540A KR20140071502A (ko) | 2009-11-19 | 2010-11-16 | 투명 도전막의 제조 방법, 투명 도전막의 제조 장치, 스퍼터링 타겟 및 투명 도전막 |
KR1020187015886A KR20180063386A (ko) | 2009-11-19 | 2010-11-16 | 투명 도전막의 제조 방법, 스퍼터링 장치 및 스퍼터링 타겟 |
CN201080051495.0A CN102666909B (zh) | 2009-11-19 | 2010-11-16 | 透明导电膜的制造方法、透明导电膜的制造装置、溅射靶及透明导电膜 |
KR1020167036789A KR20170005149A (ko) | 2009-11-19 | 2010-11-16 | 투명 도전막의 제조 방법, 스퍼터링 장치 및 스퍼터링 타겟 |
JP2011541809A JP5726752B2 (ja) | 2009-11-19 | 2010-11-16 | 透明導電膜の製造方法、透明導電膜の製造装置、スパッタリングターゲット及び透明導電膜 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2009-263966 | 2009-11-19 | ||
JP2009263966 | 2009-11-19 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2011061922A1 true WO2011061922A1 (ja) | 2011-05-26 |
Family
ID=44059409
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2010/006713 WO2011061922A1 (ja) | 2009-11-19 | 2010-11-16 | 透明導電膜の製造方法、透明導電膜の製造装置、スパッタリングターゲット及び透明導電膜 |
Country Status (5)
Country | Link |
---|---|
JP (2) | JP5726752B2 (zh) |
KR (4) | KR20180063386A (zh) |
CN (2) | CN102666909B (zh) |
TW (2) | TWI500786B (zh) |
WO (1) | WO2011061922A1 (zh) |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102651251A (zh) * | 2012-05-29 | 2012-08-29 | 番禺南沙殷田化工有限公司 | 一种低温结晶ito透明导电薄膜及其制备方法 |
JP2013012409A (ja) * | 2011-06-29 | 2013-01-17 | Toshiro Kuji | 透明導電膜の生成方法及び透明導電膜生成装置 |
JP2014241128A (ja) * | 2013-05-15 | 2014-12-25 | 日本写真印刷株式会社 | タッチセンサおよびタッチセンサモジュール |
US9048452B2 (en) | 2013-02-05 | 2015-06-02 | Samsung Display Co., Ltd. | Method for manufacturing transparent electrode of organic light emitting display device and organic light emitting display device using the transparent electrode |
JP2016225019A (ja) * | 2015-05-27 | 2016-12-28 | 日東電工株式会社 | 透明導電性フィルム |
JP2017518441A (ja) * | 2014-05-30 | 2017-07-06 | ピーピージー インダストリーズ オハイオ,インコーポレイティド | 透明導電性のインジウムドープ酸化スズ |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102945694B (zh) * | 2012-11-08 | 2015-05-20 | 深圳南玻显示器件科技有限公司 | Ito基板及其制备方法 |
CN104746003B (zh) * | 2014-12-24 | 2017-09-26 | 信利(惠州)智能显示有限公司 | 氧化铟锡低温镀膜方法 |
WO2018047977A1 (ja) * | 2016-09-12 | 2018-03-15 | 株式会社アルバック | 透明導電膜付き基板の製造方法、透明導電膜付き基板の製造装置、及び透明導電膜付き基板 |
CN106893132B (zh) * | 2017-03-30 | 2019-11-15 | 维沃移动通信有限公司 | 一种有机曲面壳体加工方法和有机曲面壳体 |
CN110546299B (zh) * | 2017-05-15 | 2022-09-30 | 三井金属矿业株式会社 | 透明导电膜用溅射靶 |
WO2019031105A1 (ja) * | 2017-08-08 | 2019-02-14 | 三井金属鉱業株式会社 | 酸化物焼結体およびスパッタリングターゲット |
CN108149210B (zh) * | 2017-12-26 | 2019-12-31 | 哈尔滨工业大学 | 一种长波红外增透保护膜的制备方法 |
JP7112854B2 (ja) * | 2018-02-19 | 2022-08-04 | 住友化学株式会社 | 酸化錫粉末 |
KR20230015894A (ko) * | 2020-05-25 | 2023-01-31 | 닛토덴코 가부시키가이샤 | 광투과성 도전성 시트의 제조 방법 |
CN117229051B (zh) * | 2023-09-21 | 2024-05-10 | 株洲火炬安泰新材料有限公司 | 一种LaTb共掺杂ITO靶材及其制备方法与应用 |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008114588A1 (ja) * | 2007-03-20 | 2008-09-25 | Idemitsu Kosan Co., Ltd. | スパッタリングターゲット、酸化物半導体膜及び半導体デバイス |
JP2008243928A (ja) * | 2007-03-26 | 2008-10-09 | Idemitsu Kosan Co Ltd | 非晶質酸化物半導体薄膜、その製造方法、薄膜トランジスタの製造方法、電界効果型トランジスタ、発光装置、表示装置及びスパッタリングターゲット |
WO2008139860A1 (ja) * | 2007-05-07 | 2008-11-20 | Idemitsu Kosan Co., Ltd. | 半導体薄膜、半導体薄膜の製造方法、および、半導体素子 |
Family Cites Families (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2989886B2 (ja) * | 1990-11-30 | 1999-12-13 | 日東電工株式会社 | アナログ式タツチパネル |
US5433901A (en) * | 1993-02-11 | 1995-07-18 | Vesuvius Crucible Company | Method of manufacturing an ITO sintered body |
JP3501614B2 (ja) * | 1997-02-26 | 2004-03-02 | 株式会社オプトロン | Ito焼結体およびその製造方法ならびに前記ito焼結体を用いたito膜の成膜方法 |
JP2000054115A (ja) * | 1998-07-31 | 2000-02-22 | Oputoron:Kk | I.t.o焼結体の製造方法及びi.t.o薄膜の形成方法 |
JP3957924B2 (ja) * | 1999-06-28 | 2007-08-15 | 株式会社東芝 | Cmp研磨方法 |
KR100744017B1 (ko) * | 2001-06-26 | 2007-07-30 | 미츠이 긴조쿠 고교 가부시키가이샤 | 고저항 투명 도전막용 스퍼터링 타겟 및 고저항 투명도전막의 제조방법 |
JP4324470B2 (ja) * | 2001-08-02 | 2009-09-02 | 出光興産株式会社 | スパッタリングターゲット、透明導電膜およびそれらの製造法 |
JP4285019B2 (ja) * | 2003-02-07 | 2009-06-24 | 住友金属鉱山株式会社 | 透明導電性薄膜とその製造方法、それを用いた表示パネル用透明導電性基材及びエレクトロルミネッセンス素子 |
JP4285480B2 (ja) * | 2003-05-28 | 2009-06-24 | 日立化成工業株式会社 | 研磨剤及び研磨方法 |
JP2007176706A (ja) * | 2005-12-26 | 2007-07-12 | Mitsui Mining & Smelting Co Ltd | 酸化物焼結体及びその製造方法並びにスパッタリングターゲット及び透明導電膜 |
JP2007238365A (ja) * | 2006-03-07 | 2007-09-20 | Mitsui Mining & Smelting Co Ltd | 酸化物焼結体及びその製造方法並びにスパッタリングターゲット及び透明導電膜 |
JP5298408B2 (ja) * | 2006-05-16 | 2013-09-25 | 株式会社ブリヂストン | 結晶性ito薄膜の成膜方法、結晶性ito薄膜及びフィルム、並びに抵抗膜式タッチパネル |
JP5000230B2 (ja) * | 2006-08-10 | 2012-08-15 | 出光興産株式会社 | 酸化ランタン含有酸化物ターゲット |
JP2008179850A (ja) | 2007-01-24 | 2008-08-07 | Toshiba Matsushita Display Technology Co Ltd | アモルファスito膜の成膜方法およびその装置 |
JP4807331B2 (ja) * | 2007-06-18 | 2011-11-02 | 住友金属鉱山株式会社 | 酸化インジウム系スパッタリングターゲットの製造方法 |
WO2009011232A1 (ja) * | 2007-07-13 | 2009-01-22 | Nippon Mining & Metals Co., Ltd. | 複合酸化物焼結体、アモルファス複合酸化膜の製造方法、アモルファス複合酸化膜、結晶質複合酸化膜の製造方法及び結晶質複合酸化膜 |
JP5237827B2 (ja) * | 2007-10-03 | 2013-07-17 | 三井金属鉱業株式会社 | 酸化インジウム系ターゲット |
JP5362231B2 (ja) * | 2008-02-12 | 2013-12-11 | 株式会社カネカ | 透明導電膜の製造方法 |
-
2010
- 2010-11-16 CN CN201080051495.0A patent/CN102666909B/zh active Active
- 2010-11-16 JP JP2011541809A patent/JP5726752B2/ja active Active
- 2010-11-16 WO PCT/JP2010/006713 patent/WO2011061922A1/ja active Application Filing
- 2010-11-16 KR KR1020187015886A patent/KR20180063386A/ko not_active Application Discontinuation
- 2010-11-16 KR KR1020147013540A patent/KR20140071502A/ko active Application Filing
- 2010-11-16 KR KR1020167036789A patent/KR20170005149A/ko active Application Filing
- 2010-11-16 CN CN201410341203.7A patent/CN104213085A/zh active Pending
- 2010-11-16 KR KR1020127012052A patent/KR20120070597A/ko active Search and Examination
- 2010-11-18 TW TW099139744A patent/TWI500786B/zh active
- 2010-11-18 TW TW104119074A patent/TWI620827B/zh active
-
2015
- 2015-03-31 JP JP2015071220A patent/JP6060202B2/ja active Active
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008114588A1 (ja) * | 2007-03-20 | 2008-09-25 | Idemitsu Kosan Co., Ltd. | スパッタリングターゲット、酸化物半導体膜及び半導体デバイス |
JP2008243928A (ja) * | 2007-03-26 | 2008-10-09 | Idemitsu Kosan Co Ltd | 非晶質酸化物半導体薄膜、その製造方法、薄膜トランジスタの製造方法、電界効果型トランジスタ、発光装置、表示装置及びスパッタリングターゲット |
WO2008139860A1 (ja) * | 2007-05-07 | 2008-11-20 | Idemitsu Kosan Co., Ltd. | 半導体薄膜、半導体薄膜の製造方法、および、半導体素子 |
Cited By (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2013012409A (ja) * | 2011-06-29 | 2013-01-17 | Toshiro Kuji | 透明導電膜の生成方法及び透明導電膜生成装置 |
CN102651251A (zh) * | 2012-05-29 | 2012-08-29 | 番禺南沙殷田化工有限公司 | 一种低温结晶ito透明导电薄膜及其制备方法 |
US9048452B2 (en) | 2013-02-05 | 2015-06-02 | Samsung Display Co., Ltd. | Method for manufacturing transparent electrode of organic light emitting display device and organic light emitting display device using the transparent electrode |
JP2014241128A (ja) * | 2013-05-15 | 2014-12-25 | 日本写真印刷株式会社 | タッチセンサおよびタッチセンサモジュール |
JP2017518441A (ja) * | 2014-05-30 | 2017-07-06 | ピーピージー インダストリーズ オハイオ,インコーポレイティド | 透明導電性のインジウムドープ酸化スズ |
JP2016225019A (ja) * | 2015-05-27 | 2016-12-28 | 日東電工株式会社 | 透明導電性フィルム |
Also Published As
Publication number | Publication date |
---|---|
CN102666909A (zh) | 2012-09-12 |
TW201124546A (en) | 2011-07-16 |
KR20180063386A (ko) | 2018-06-11 |
KR20120070597A (ko) | 2012-06-29 |
JP6060202B2 (ja) | 2017-01-11 |
JPWO2011061922A1 (ja) | 2013-04-04 |
CN104213085A (zh) | 2014-12-17 |
CN102666909B (zh) | 2016-06-22 |
KR20170005149A (ko) | 2017-01-11 |
KR20140071502A (ko) | 2014-06-11 |
TW201538764A (zh) | 2015-10-16 |
JP5726752B2 (ja) | 2015-06-03 |
TWI500786B (zh) | 2015-09-21 |
TWI620827B (zh) | 2018-04-11 |
JP2015158014A (ja) | 2015-09-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6060202B2 (ja) | 透明導電膜の製造方法、スパッタリング装置及びスパッタリングターゲット | |
KR101238926B1 (ko) | 투명 도전막의 성막 방법 및 성막 장치 | |
TWI585227B (zh) | A sputtering target, an oxide semiconductor thin film, and the like | |
US8062777B2 (en) | Semiconductor thin film and process for producing the same | |
US20130341181A1 (en) | Zinc oxide-based sputtering target, method of manufacturing the same, and thin-film transistor having barrier layer deposited using the same | |
TW200902740A (en) | Sputtering target, oxide semiconductor film and semiconductor device | |
CN101514440A (zh) | 一种高电子迁移率氧化铟透明薄膜的制备方法 | |
JP2003520296A (ja) | 透明インジウム錫酸化物の電子ビーム蒸着方法 | |
JP2010222214A (ja) | 金属酸化物薄膜及びその製造方法 | |
KR20140011945A (ko) | 스퍼터링용 타깃, 스퍼터링용 타깃의 사용 방법 및 산화물막의 제작 방법 | |
US20120160663A1 (en) | Sputter Deposition and Annealing of High Conductivity Transparent Oxides | |
CN105970171A (zh) | 一种采用磁控溅射制备柔性稀土氧化物薄膜的方法 | |
WO2017122618A1 (ja) | 非晶質複合金属酸化物の製造方法 | |
KR100862593B1 (ko) | 투명 전도성 박막 및 이의 제조방법 | |
CN103774098B (zh) | 氧化亚锡织构薄膜及其制备方法 | |
WO2011102425A1 (ja) | 酸化物焼結体、酸化物混合体、それらの製造方法およびそれらを用いたターゲット | |
TW201404909A (zh) | 氧化鋅系濺鍍靶、其製造方法、具有使用其沉積之阻絕層之薄膜電晶體、以及製造薄膜電晶體之方法 | |
JP5232787B2 (ja) | カラーフィルタの製造方法 | |
TW201000658A (en) | Method of manufacturing liquid crystal display device | |
EP2796589B1 (en) | Method of manufacturing an organic light-emitting display | |
JP2008053118A (ja) | 酸化亜鉛系透明導電膜の熱処理方法 | |
JP5508889B2 (ja) | 薄膜蛍光体、ディスプレイ、ブラウン管および薄膜蛍光体の製造方法 | |
CN115011939A (zh) | 以石英玻璃为衬底的亚稳态二氧化钒薄膜及其制备方法 | |
Mihara et al. | P‐210: Ta‐Doped SnO2 Thin Films for PDP | |
TW201200616A (en) | Oxide sintered body, oxide mixture, manufacturing methods for same, and targets using same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201080051495.0 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10831321 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2011541809 Country of ref document: JP |
|
ENP | Entry into the national phase |
Ref document number: 20127012052 Country of ref document: KR Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 10831321 Country of ref document: EP Kind code of ref document: A1 |