WO2011042481A1 - Wool-impregnating agent - Google Patents

Wool-impregnating agent Download PDF

Info

Publication number
WO2011042481A1
WO2011042481A1 PCT/EP2010/064951 EP2010064951W WO2011042481A1 WO 2011042481 A1 WO2011042481 A1 WO 2011042481A1 EP 2010064951 W EP2010064951 W EP 2010064951W WO 2011042481 A1 WO2011042481 A1 WO 2011042481A1
Authority
WO
WIPO (PCT)
Prior art keywords
wool
phosphate
impregnating agent
agent according
weight
Prior art date
Application number
PCT/EP2010/064951
Other languages
German (de)
French (fr)
Inventor
Gerd THÖNE
Original Assignee
Nanosky.Com Aktiengesellschaft
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanosky.Com Aktiengesellschaft filed Critical Nanosky.Com Aktiengesellschaft
Priority to EP10761024A priority Critical patent/EP2486197A1/en
Publication of WO2011042481A1 publication Critical patent/WO2011042481A1/en

Abstract

The invention relates to a wool-impregnating agent. Said agent has silicon dioxide, more than 50 wt.% of water of a phosphate, and a wetting agent.

Description

Titel: Wolle-Imprägniermittel  Title: Wool impregnant
Die vorliegende Erfindung betrifft ein Wolle-Imprägniermittel, insbesondere für Schafwolle. The present invention relates to a wool impregnating agent, in particular for sheep's wool.
Wolle ist als Grundmaterial für eine Vielzahl unterschiedlicher Produkte weit verbreitet. Beispielsweise können Teppiche, Decken und Kleidungsstücke, z. B. Jacken, Mützen oder Handschuhe aus Wolle bestehen. Wesentliche Nachteile von Wolle sind die leichte Entflammbarkeit, die Fähigkeit, Wasser aufzunehmen und die Tatsache, dass Motten gerne Wolle fressen. Auch andere Tiere und Insekten halten sich gerne in Wollmaterialien auf und nisten dort. Wool is widely used as a base material for a variety of different products. For example, carpets, blankets and garments, for. B. jackets, hats or gloves made of wool. Significant drawbacks of wool are the flammability, the ability to absorb water and the fact that moths like to eat wool. Other animals and insects like to stay in wool materials and nest there.
Wollprodukte sollen aber oftmals wasserabweisend oder schwer entflammbar sein. Dies erhöht zum einen den Tragekomfort, zum anderen die Sicherheit für den Benutzer. Erreicht wird dies meist durch die Verwendung einer weiteren Schicht oder Lage aus einem anderen Material. But wool products should often be water repellent or flame retardant. This increases on the one hand the wearing comfort, on the other hand the safety for the user. This is usually achieved by using another layer or layer of another material.
Die Aufgabe der vorliegenden Erfindung besteht darin, ein Imprägniermittel für Wolle, insbesondere Schafwolle bereitzustellen, das die Wolle nutzbar macht. Beispielsweise soll sie durch die Imprägnierung schwer entflammbar und wasserabweisend gemacht werden. Die Herstellung sollte kostengünstig möglich sein . The object of the present invention is to provide an impregnating agent for wool, especially sheep's wool, which makes the wool usable. For example, it should be made by the impregnation flame retardant and water-repellent. The production should be cost-effective.
Die Aufgabe wird durch ein Wolle-Imprägniermittel gelöst, das aufweist: The object is achieved by a wool impregnating agent which comprises:
- Siliziumdioxid,  Silica,
- mindestens 50 Gew.-% Wasser  - At least 50 wt .-% water
- Phosphat,  - phosphate,
- ein Netzmittel.  - a wetting agent.
Vorzugsweise wird ein Siliziumdioxid mit Partikeln im Nano-Größenbereich gewählt. Diese Partikel haben eine Korngröße von etwa 10~ 9 mm. Sie können zwar von Insekten aufgenommen werden, richten dann aber Schaden durch ihre Scharfkantigkeit an. Insekten vermeiden es deshalb, derart imprägnierte Materialien zu fressen. Motten nisten nicht in Wolle, die mit Siliziumdioxid versetzt ist. Es hat sich bei Versuchen gezeigt, dass Fraßverluste an der präparierten Wolle mit 0,2 % äußerst gering ausfallen. Siliziumdioxid in kristalliner Nanoform verdunstet weder, noch löst es sich mechanisch von der Wolle. Siliziumdioxid in Nanoform ist extrem ergiebig, mit nur einem Gramm können etwa 300 m2 Wolle versetzt werden. Preferably, a silica is selected with particles in the nanosize range. These particles have a particle size of about 10 ~ 9 mm. Although they can be picked up by insects, they do damage due to their sharp edges. Insects therefore avoid eating such impregnated materials. Moths do not nest in wool, which is mixed with silicon dioxide. It has been shown in experiments that feeding losses on the prepared wool are extremely small at 0.2%. Silicon dioxide in crystalline nanoform neither evaporates nor dissolves mechanically from the wool. Silicon dioxide in nanoform is extremely economical, with just one gram, about 300 m 2 of wool can be added.
Die Verwendung von Siliziumdioxid als Insektizid ist auch deshalb besonders vorteilhaft, weil es im Gegensatz zu handelsüblichen Pestiziden oder Fungiziden keine schädlichen Nebenwirkungen, für Mensch und Tier aufweist, insbesondere dünstet es nicht aus. The use of silica as an insecticide is also particularly advantageous because, in contrast to commercial pesticides or fungicides, it has no harmful side effects for humans and animals, in particular it does not exude.
Ein besonders vorteilhafter Effekt ergibt sich, wenn der Wolle zusätzlich Laven- delöl oder Chrysantemenauszüge hinzugefügt werden. Diese Stoffe schrecken Motten und andere Insekten zusätzlich ab, in Kombination mit Siliziumdioxid hat sich eine nahezu 100%ige Resistenz gegen Insekten und ähnliche Lebewesen gezeigt. Chrysantemenöle enthalten Pyrethroide, die auch synthetisch herstellbar sind . Diese Pyrethroide oder auch Permethrine sind nicht gesundheitsschädlich und als Zuschlagsstoffe zugelassen. A particularly advantageous effect results when the wool is additionally added to lavender oil or chrysanthemum extracts. These substances additionally deter moths and other insects, and in combination with silicon dioxide have shown almost 100% resistance to insects and similar organisms. Chrysanthemum oils contain pyrethroids, which are also synthetically producible. These pyrethroids or permethrins are not harmful to health and are approved as additives.
Als weiterer positiver Effekt hat sich gezeigt, dass Siliziumdioxid in kristalliner Nanoform hydrophob, also wasserabweisend ist. Die Wolle wird deshalb nicht durchnässt, was zum Einen eine Geruchsbelastung verhindert, sich zum anderen aber auch positiv auf die Wärmedämmeigenschaften auswirkt, die ansonsten durch Feuchtigkeit verschlechtert werden. Another positive effect has shown that silicon dioxide in hydrophobic nanoform is hydrophobic, ie water-repellent. The wool is therefore not soaked, which on the one hand prevents odor, but on the other hand also has a positive effect on the thermal insulation properties, which are otherwise deteriorated by moisture.
Die Erfindung macht sich den Umstand zunutze, dass bekanntlicherweise bei der Synthese von Phosphaten aus Phosphorsäure und einem entsprechendem Reaktionspartner, beispielsweise bei der Synthese von Diammoniumphosphat aus Wasser, Phosphorsäure und Ammoniak erheblich Wärme freigesetzt wird. Demgemäß verläuft die Rückreaktion endotherm, es wird erhebliche Wärme benötigt. Dies kann dazu genutzt werden, brennende Wolle herunter zu kühlen. The invention makes use of the fact that, as is known, in the synthesis of phosphates from phosphoric acid and a corresponding reaction partner, for example in the synthesis of diammonium phosphate from water, phosphoric acid and ammonia, considerable heat is released. Accordingly, the reverse reaction is endothermic, it requires significant heat. This can be used to cool down burning wool.
Nun hat sich aber herausgestellt, dass eine normale, wässrige Lösung von Diammoniumphosphaten nicht die gewünschte Abkühlung beim Zersetzen unter Einwirkung einer feuerbedingten Temperatur, die typisch zwischen 400°C und 1000°C liegt, liefert. Erst der Zusatz eines Netzmittels, insbesondere eines Ten- sids, brachte den gewünschten Erfolg . Es konnte festgestellt werden, dass erheblich Kälte freigesetzt wird, die die brennende Wolle herabkühlt. Die Zugabe eines Netzmittels hat den großen Vorteil, dass die Benetzung der Oberfläche des zu schützenden Materials verbessert wird. Trägt man lediglich eine wässrige Lösung eines Phosphats auf die Wolle auf, stellt man fest, dass die aufgesprühte Salzlösung nach Antrocknen Kristalle bildet. Ein homogener, geschlossener Überzug wird nicht erreicht, vielmehr nur ein partieller Schutz, der nicht zufriedenstellend ist. However, it has now been found that a normal, aqueous solution of diammonium phosphates does not provide the desired cooling upon decomposition under the action of a firing temperature typically between 400 ° C and 1000 ° C. Only the addition of a wetting agent, in particular a surfactant, brought the desired success. It was found that much cold is released, which cools down the burning wool. The addition of a wetting agent has the great advantage that the wetting of the surface of the material to be protected is improved. If you apply only an aqueous solution of a phosphate on the wool, it is found that the sprayed salt solution forms crystals after drying. A homogeneous, closed coating is not achieved, but only a partial protection that is unsatisfactory.
Die Beigabe eines Netzmittels bringt nun aber den Erfolg . Beim Trockenen der aufgebrachten wässrigen Phosphatlösung bilden sich nicht mehr Kristalle, sondern es bleibt eine dünne, deckende Schicht des Phosphatträgers auf der Wolle. Dadurch wird die feuerhemmende Wirkung deutlich verbessert. The addition of a wetting agent brings but now the success. Drying of the applied aqueous phosphate solution no longer forms crystals, but leaves a thin, covering layer of the phosphate carrier on the wool. As a result, the fire-retardant effect is significantly improved.
Das erfindungsgemäße Wolle-Imprägniermittel hat den großen Vorteil, ausgesprochen umweltfreundlich zu sein. Phosphate sind bekanntlich Düngemittel . Wenn sie im Außenbereich verwendet werden und durch Regen teilweise oder gänzlich abgewaschen werden, richten sie keinen Schaden an. The wool impregnating agent according to the invention has the great advantage of being extremely environmentally friendly. Phosphates are known to be fertilizers. If they are used outdoors and are partially or completely washed off by rain, they do no harm.
Weiterhin wird kein spezielles Lösungsmittel benutzt, vielmehr wird Wasser eingesetzt. Auch insoweit ist das erfindungsgemäße Wolle-Imprägniermittel ausgesprochen umweltfreundlich. Furthermore, no special solvent is used, but water is used. Also in this respect, the wool impregnating agent according to the invention is extremely environmentally friendly.
Die Erfindung bezieht sich nicht vorrangig auf solche Phosphate, die unter Zufuhr von Wärme einen Schaum bilden, also intumeszierende Eigenschaften haben. Sie bezieht sich insbesondere auch auf solche Phosphate, bei denen die beschriebene endotherme Zersetzungsreaktion auftritt. The invention does not relate primarily to those phosphates which form a foam with the supply of heat, so have intumescent properties. It also relates in particular to those phosphates in which the described endothermic decomposition reaction occurs.
Ein mit dem erfindungsgemäßen Wolle-Imprägniermittel versetztes Produkt wird im Brandfall durch die endotherme Reaktion heruntergekühlt Wolle- Imprägniermittel verdampft nicht in dem Maße, wie dies bei normalem Wasser beobachtet wird. Die brennenden Produkte lassen sich daher besser benetzen und somit auch besser löschen . A product mixed with the wool impregnating agent according to the invention is cooled down in case of fire by the endothermic reaction. Wool impregnating agent does not evaporate to the extent observed in normal water. The burning products can therefore be better wetted and thus also better extinguished.
Mit dem Wolle-Imprägniermittel imprägnierte Wolle wird beim Anzünden gekühlt und brennt schlechter, sie lässt sich nicht so einfach entzünden. Wool impregnated with the wool impregnating agent is cooled when lit and burns worse, it is not easy to ignite.
Nun sind aber, wie oben beschrieben, Phosphate und deren Salze wasserlöslich. Beispielsweise können diese durch Regenwasser ausgewaschen werden. In Weiterentwicklung der Erfindung schlägt diese deshalb vor, zusätzlich einen Schauminhibitor, insbesondere Silikonentschäumer, hinzuzugeben. Verwendet wird vorzugsweise ein Feststoffanteil an Schauminhibitoren im Bereich von 0,1 bis 5 Gew-%. Die Schauminhibitoren verhindern nicht nur das Schäumen, sondern haben auch eine wasserabweisende Wirkung . Sie behindern das Ablösen oder Auswaschen des Wolle-Imprägniermittels durch Wasser oder Feuchtigkeit. However, as described above, phosphates and their salts are water-soluble. For example, they can be washed out by rainwater. In a further development of the invention, this therefore proposes to additionally add a foam inhibitor, in particular silicone defoamer. A solids content of foam inhibitors in the range from 0.1 to 5 is preferably used % By weight. The foam inhibitors not only prevent foaming, but also have a water-repellent effect. They hinder the detachment or washing out of the wool impregnating agent by water or moisture.
Insgesamt bilden sich auf der Oberfläche der Wolle, die mit dem Wolle- Imprägniermittel ausgerüstet ist, dünne, zähe Filme in Form einer geschlossenen Schicht. Diese Filme sind gegen Wasser beständig, jedenfalls deutlich beständiger als Filme ohne Zugabe eines Netzmittels. Overall, on the surface of the wool, which is provided with the wool impregnating agent, thin, tough films are formed in the form of a closed layer. These films are resistant to water, at least much more stable than films without the addition of a wetting agent.
Für die vorzugsweise als Schauminhibitoren eingesetzten Silikonentschäumer ist zwar bekannt, dass Silikon eine wasserabweisende Wirkung hat, es war aber nicht vorauszusehen und ist überraschend, dass bei dem erfindungsgemäßen Wolle-Imprägniermittel die Zugabe eines Silikonentschäumers oder eines anderen Schauminhibitors eine deutliche verbesserte Wetterfestigkeit bewirkt. Although it is known that silicone has a water-repellent effect for the silicone defoamers, which are preferably used as foam inhibitors, it was not foreseeable and surprising that the addition of a silicone defoamer or another foam inhibitor results in a markedly improved weather resistance in the wool impregnating agent according to the invention.
Neben Silikonentschäumern eignen sich als Schauminhibitoren auch Stearate wie beispielsweise Aluminiumstearat oder Zinkstearat. In addition to silicone defoamers, stearates such as, for example, aluminum stearate or zinc stearate are also suitable foam inhibitors.
Als Phosphat eignet sich für die Erfindung insbesondere das bereits erwähnt Diammoniumphosphat, weiterhin Diammoniumhydrogenphosphat, Particularly suitable as a phosphate for the invention is the diammonium phosphate already mentioned, furthermore diammonium hydrogen phosphate,
Guanidinphosphat, Dimelaminphosphat, Borphosphat, Dinatriumphosphat und Kuperhydroxyphosphat. Guanidine phosphate, dimelamine phosphate, boron phosphate, disodium phosphate and copper hydroxyphosphate.
Einige dieser Phosphate haben die zusätzliche Wirkung, bei Zufuhr von Wärme aufzuschäumen, also eine intumeszierende Wirkung . Dies gilt beispielsweise für Dimelaminphosphat. Diese Wirkung tritt zusätzlich zu den bereits beschriebenen Wirkungen, also insbesondere der endothermen Reaktion unter Anwesenheit des Netzmittels, und der weiteren Vorteile die das Netzmittel bringt, auf. Some of these phosphates have the additional effect of foaming on supply of heat, so an intumescent effect. This applies, for example, to dimelamine phosphate. This effect occurs in addition to the effects already described, that is, in particular the endothermic reaction in the presence of the wetting agent, and the other advantages that brings the wetting agent on.
In einer bevorzugten Ausführung ist das Netzmittel in einem Gewichtsanteil von 0,01 bis 1 Prozent in wässrigen Lösungen enthalten. In a preferred embodiment, the wetting agent is contained in a weight fraction of 0.01 to 1 percent in aqueous solutions.
Der gewichtsmäßige Wasseranteil im erfindungsgemäßen Wolle-Imprägniermittel liegt über 50 %, vorzugsweise zwischen 62 und 95%, insbesondere bei 70 bis 80%. Das Wolle-Imprägniermittel ist ausgesprochen flüssig, es kann wie Wasser aufgetragen werden, insbesondere und vorzugsweise in Form eines feinen Nebels, wie er beispielsweise mit einer Zerstäuberspritze erreicht wird. Nachfolgend werden einige Rezepte, die nur beispielhaft zu verstehen sind, aufgeführt, um die Zusammensetzung des erfindungsgemäßen Wolle- Imprägniermittels zu veranschaulichen : The proportion by weight of water in the wool impregnating agent according to the invention is more than 50%, preferably between 62 and 95%, in particular between 70 and 80%. The wool-impregnating agent is extremely liquid, it can be applied as water, in particular and preferably in the form of a fine mist, as it is achieved for example with a sprayer. In the following some recipes are given by way of example to illustrate the composition of the wool impregnating agent according to the invention:
1. Rezept: 1st recipe:
Vermischt wird ein Feststoffanteil von 38 Gewichts-Prozent mit 62 Gewichts- Prozent Wasser. Der Feststoffanteil hat folgende Zusammensetzung : A solids content of 38 percent by weight is mixed with 62 percent by weight of water. The solids content has the following composition:
97,9 Gewichts-Prozent Diammoniumphosphat 97.9 weight percent diammonium phosphate
2,0 Gewichts- Prozent Silikonentschäumer, wässrig, ca. 38 Gewichts-Prozent Feststoffgehalt und 2.0 weight percent silicone defoamer, aqueous, about 38 weight percent solids content and
0,1 Gewichts-Prozent eines kationischen oder anionischen Tensids. 0.1 weight percent of a cationic or anionic surfactant.
Bewährt haben sich auch Mischungen verschiedener Phosphatsalze, so kann beispielsweise der angegebene Anteil an Diammoniumphosphat ersetzt werden durch 2/3 Diammoniumphosphat und 1/3 Guanidinphosphat oder 1/3 Diammoniumphosphat, 1/3 Guanidinphosphat und 1/3 Dimelaminphosphat. Mixtures of different phosphate salts have also proved useful, for example the stated proportion of diammonium phosphate can be replaced by 2/3 diammonium phosphate and 1/3 guanidine phosphate or 1/3 diammonium phosphate, 1/3 guanidine phosphate and 1/3 dimelamine phosphate.
2. Rezept: 2nd recipe:
18 Gewichts-Prozent Feststoffanteil werden mit 82 Gewichts-Prozent Wasser vermischt. Der Feststoffanteil setzt sich zusammen aus 18 weight percent solids are mixed with 82 weight percent water. The solids content is composed of
98,8 Gewichts-Prozent Guanidinphosphat 98.8 weight percent guanidine phosphate
1,0 Gewichts-Prozent Aluminiumstearat und 1.0 weight percent aluminum stearate and
0,2 Gewichts-Prozent Natriumsulfat. 0.2% by weight sodium sulfate.
3. Rezept: 3rd recipe:
Es wird ein Extrakt hergestellt aus 38 Gewichts-Prozent Feststoffanteil und 62 Gewichts-Prozent Wasser, der Feststoffanteil besteht aus 98,9 Gewichts-Prozent Diammoniumphosphat It is an extract prepared from 38 percent by weight of solids and 62 percent by weight of water, the solids content consists of 98.9 percent by weight of diammonium phosphate
0,9 Gewichts-Prozent Silikonentschäumer und 0,2 Gewichts-Prozent eines Tensids. Eine verstärkte Wasserabweisung der Wolle kann auch dadurch erreicht werden, dass weiterhin Polydimethylsiloxan als Emulsion (20-50%, vorzugsweise 33%) hinzugefügt wird . 0.9 weight percent silicone defoamer and 0.2 weight percent of a surfactant. Increased water repellency of the wool can also be achieved by further adding polydimethylsiloxane as an emulsion (20-50%, preferably 33%).
Die Imprägnierung der Wolle erfolgt vorzugsweise dadurch, dass diese in einer Flotte, bestehend aus den oben genannten Zusatzstoffen getränkt und anschließend getrocknet wird. Die Wolle kann dann je nach Bedarf gekämmt, gesteppt oder abgenäht und in gewünschte Größen zugeschnitten werden . Um die Flotte vor einem Verfaulen zu bewahren, kann ihr ein Konservierungsmittel, beispielsweise Kaliumsorbat, hinzugegeben werden. The impregnation of the wool is preferably carried out by soaking it in a liquor consisting of the abovementioned additives and then drying it. The wool can then be combed, quilted or sewn as needed and cut into desired sizes. To save the liquor from fouling, a preservative, such as potassium sorbate, can be added to it.
Neben dem Tränken der Wolle in der Flotte ist ein Besprühen der Wolle mit einer Mischung der Zusatzstoffe denkbar, diese können aber auch nacheinander in jeweils geeigneten Verfahren aufgebracht werden. Die Wolle kann auch zunächst nur in einigen Zusatzstoffen getränkt und anschließend mit anderen Zusatzstoffen besprüht werden. In addition to impregnating the wool in the fleet, spraying the wool with a mixture of the additives is conceivable, but these can also be applied one after the other in suitable processes. The wool can also first be soaked only in some additives and then sprayed with other additives.
Die Flotte kann beispielsweise die folgende Zusammensetzung aufweisen, wobei die prozentualen Anteile nur als Richtwerte zu verstehen sind : For example, the liquor may have the following composition, the percentages being indicative only:
80-100 % Wasser, vorzugsweise 95,86 % 80-100% water, preferably 95.86%
1-2 % Kaliumsorbat, vorzugsweise 0,5 % 1-2% potassium sorbate, preferably 0.5%
1-5 % Wolle-Imprägniermittel vorzugsweise 2% 1-5% wool impregnating agent preferably 2%
0,2-2% Polydimethylsiloxan, Emulsion 33% vorzugsweise 0,8% 0.2-2% polydimethylsiloxane, emulsion 33%, preferably 0.8%
0,2-2% Nano-Siliciumdioxyd in Wasser, Korndurchmesser weniger 100 nm, vorzugsweise 0,8% 0.2-2% nano-silica in water, grain diameter less than 100 nm, preferably 0.8%
0,01-0,1% Lavendelöl (vorzugsweise 0,04% Lavendelöl) 0.01-0.1% lavender oil (preferably 0.04% lavender oil)
Die Bestandteile müssen anteilig derart gemischt werden, dass sich 100% ergeben. The ingredients must be proportionally mixed so that there are 100%.
Anstelle von Nano-Siliciumdioxyd ist auch die Verwendung von entsprechend fein gemahlenem Glas, Ouarz oder Floatglas (sogenanntes Nanoglas) mit gleicher Partikelgröße möglich. Instead of nano-silica, the use of correspondingly finely ground glass, Ouarz or float glass (so-called nanoglass) with the same particle size is possible.
Die Partikelgröße ist mit weniger als 100 nm angegeben, vorzugsweise hat sich eine Partikelgröße von 30 nm als besonders wirksam erwiesen. Es ist anderer- seits aber auch möglich, Partikelgrößen im Micro-Bereich einzusetzen, da diese zwar schlechtere, aber noch ausreichende Wirkung erzielen. The particle size is specified as less than 100 nm, preferably a particle size of 30 nm has proven to be particularly effective. It is another- On the other hand, it is also possible to use particle sizes in the micro range, since they achieve worse, but still sufficient effect.
Das Wollmaterial kann weiterhin mit Kunststofffasern versehen werden, um ein gewünschtes Volumen zu erreichen und/oder die Wollfasern dauerhaft zu stützen. The wool material may further be provided with plastic fibers to achieve a desired volume and / or to sustain the wool fibers permanently.
Die imprägnierte Wolle kann bevorzugt zur Herstellung von Dämmmaterial oder Dämmstoff, wie er beispielsweise in der Bauindustrie eingesetzt wird, verwendet werden. Dämmmaterial ist ein Material mit geringer Wärmeleitung, das z. B. beim Gebäude- und Anlagenbau oder bei der Herstellung von Kühlschränken, Gefrierschränken und ähnlichem zur Wärmedämmung eingesetzt wird. Außerdem können Dämmmaterialien auch schalldämmende oder andere bauphysikalische Eigenschaften aufweisen. The impregnated wool can preferably be used for the production of insulating material or insulating material, as used for example in the construction industry. Insulating material is a material with low heat conduction, the z. B. is used in building and plant construction or in the production of refrigerators, freezers and the like for thermal insulation. In addition, insulating materials may also have sound insulating or other physical properties.
Es hat sich gezeigt, dass Nutzung von Schafwolle auch für Dämmmaterial besonders vorteilhaft ist, weil diese hervorragende Dämmeigenschaften aufweist, in ausreichenden Mengen zur Verfügung steht und ohnehin bereits schlecht brennt und wasserabweisend ist. It has been shown that the use of sheep's wool is also particularly advantageous for insulating material, because it has excellent insulating properties, is available in sufficient quantities and already burns badly and is water-repellent anyway.
Die Erfindung ist nicht auf die beschriebenen Ausführungsbeispiele beschränkt, diese können vielmehr je nach Anwendungsfall beliebig variiert werden. The invention is not limited to the described embodiments, but they can be varied as desired depending on the application.

Claims

Patentansprüche claims
1. Wolle-Imprägniermittel, insbesondere für Schafwolle, aufweisend : 1. Wool impregnating agent, in particular for sheep wool, comprising:
- Siliziumdioxid,  Silica,
- mindestens 50 Gew.-% Wasser,  at least 50% by weight of water,
- Phosphat,  - phosphate,
- ein Netzmittel.  - a wetting agent.
2. Wolle-Imprägniermittel nach Anspruch 1, dadurch gekennzeichnet, dass das Siliziumdioxid eine Korngröße von weniger als 100 nm aufweist. 2. wool impregnating agent according to claim 1, characterized in that the silicon dioxide has a particle size of less than 100 nm.
3. Wolle-Imprägniermittel nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass weiterhin Polydimethylsiloxan enthalten ist. 3. wool impregnating agent according to claim 1 or 2, characterized in that further polydimethylsiloxane is included.
4. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass weiterhin Lavendelöl enthalten ist. 4. Wool impregnating agent according to one of claims 1 to 3, characterized in that lavender oil is also included.
5. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass Chrysanthemenöl enthalten ist. 5. wool impregnating agent according to one of claims 1 to 4, characterized in that chrysanthemum oil is included.
6. Wolle nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass weiterhin ein Konservierungsmittel enthalten ist. 6. Wool according to one of claims 1 to 5, characterized in that further a preservative is included.
7. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass das Wolle-Imprägniermittel zusätzlich einen Schauminhibitor aufweist, vorzugsweise 0,1 bis 5 Gewichtsprozent bezogen auf den Anteil an Phosphat. 7. wool impregnating agent according to any one of claims 1 to 6, characterized in that the wool impregnating agent additionally comprises a foam inhibitor, preferably 0.1 to 5 weight percent based on the proportion of phosphate.
8. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass das Netzmittel in einem Gewichtsanteil von 0,01 bis 1 Prozent bezogen auf den Anteil an Phosphat in der wässrigen Lösung enthalten ist. 8. wool impregnating agent according to one of claims 1 to 7, characterized in that the wetting agent is contained in a weight fraction of 0.01 to 1 percent, based on the proportion of phosphate in the aqueous solution.
9. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass der Anteil an Phosphat zwischen 5 und 38 Gewichts- Prozent, vorzugsweise zwischen 10 und 22 Gewichtsprozent, insbesondere etwa 16 Gewichtsprozent beträgt. 9. wool impregnating agent according to one of claims 1 to 8, characterized in that the proportion of phosphate between 5 and 38 weight Percent, preferably between 10 and 22 percent by weight, in particular about 16 percent by weight.
10. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass das Phosphat ein Metallphosphat, Ammonium- und/oder Aminphosphat ist. 10. wool impregnating agent according to one of claims 1 to 9, characterized in that the phosphate is a metal phosphate, ammonium and / or amine phosphate.
11. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 10, dadurch gekennzeichnet, dass das Netzmittel ein anionisches oder kationisches Ten- sid und/oder ein Natriumsulfat ist. 11. wool impregnating agent according to any one of claims 1 to 10, characterized in that the wetting agent is an anionic or cationic surfactant and / or a sodium sulfate.
12. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 11, dadurch gekennzeichnet, dass sich das Phosphat von Orthophosphorsäure, Pyrophosphorsäure, Polyphosphorsäure, phosphoriger Säure oder Phosphinsäuren ableitet. 12. Wool impregnating agent according to one of claims 1 to 11, characterized in that the phosphate is derived from orthophosphoric acid, pyrophosphoric acid, polyphosphoric acid, phosphorous acid or phosphinic acids.
13. Wolle-Imprägniermittel nach einem der Ansprüche 1 bis 12, dadurch gekennzeichnet, dass als Phosphat ein Diammoniumphosphat, Diammoniumhydrogenphosphat, Guadeninphosphat, Dimelaminphosphat, Bohrphosphat, Dinatriumphosphat, Kupferhydroxidphosphat oder eine beliebige Kombination dieser Phosphate eingesetzt wird. 13. Wool impregnating agent according to one of claims 1 to 12, characterized in that as phosphate a diammonium phosphate, diammonium hydrogen phosphate, guadenine phosphate, dimelamine phosphate, boric phosphate, disodium phosphate, copper hydroxide or any combination of these phosphates is used.
14. Verfahren zur Imprägnierung von Wolle, insbesondere Schafwolle, nach einem der Ansprüche 1 bis 13, gekennzeichnet durch die Verfahrensschritte: 14. A process for the impregnation of wool, in particular sheep wool, according to one of claims 1 to 13, characterized by the process steps:
Bereitstellen der Wolle, Providing the wool,
Mischen einer Flotte mit den Zuschlagstoffen, Mixing a liquor with the aggregates,
Tränken der Wolle in der Flotte, Watering the wool in the fleet,
Trocknen der Wolle, Drying the wool,
Verarbeiten der Wolle zum Endprodukt. Processing the wool to the final product.
PCT/EP2010/064951 2009-10-07 2010-10-06 Wool-impregnating agent WO2011042481A1 (en)