WO2010110389A1 - オルガノポリシロキサンおよびハードコート剤組成物並びにハードコート層を有する樹脂基板 - Google Patents
オルガノポリシロキサンおよびハードコート剤組成物並びにハードコート層を有する樹脂基板 Download PDFInfo
- Publication number
- WO2010110389A1 WO2010110389A1 PCT/JP2010/055276 JP2010055276W WO2010110389A1 WO 2010110389 A1 WO2010110389 A1 WO 2010110389A1 JP 2010055276 W JP2010055276 W JP 2010055276W WO 2010110389 A1 WO2010110389 A1 WO 2010110389A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hard coat
- organopolysiloxane
- resin substrate
- group
- coat layer
- Prior art date
Abstract
Description
T1:R-Si(-OX)2(-O*-)
T2:R-Si(-OX)(-O*-)2
T3:R-Si(-O*-)3
(式中、Rは水素原子または炭素数が1~10の置換もしくは非置換の1価の有機基を表し、Xは水素原子または炭素数1~6のアルキル基を表し、O*は2つのケイ素原子を連結する酸素原子を表す)
T1:R-Si(-OX)2(-O*-)
T2:R-Si(-OX)(-O*-)2
T3:R-Si(-O*-)3
(式中、Rは水素原子または炭素数が1~10の置換もしくは非置換の1価の有機基を表し、Xは水素原子または炭素数1~6のアルキル基を表し、O*は2つのケイ素原子を連結する酸素原子を表す)
本発明のオルガノポリシロキサン(以下、オルガノポリシロキサン(a)という)と、後述ハードコート剤組成物において本発明のオルガノポリシロキサンと併用される他のオルガノポリシロキサンであるオルガノポリシロキサン(b)は、いずれもT単位と呼ばれる含ケイ素結合単位を主として構成された硬化性のオルガノポリシロキサンである。
一般に、オルガノポリシロキサンはM単位、D単位、T単位、Q単位と呼ばれる含ケイ素結合単位から構成される。この内、硬化性のオルガノポリシロキサンは主としてT単位またはQ単位から構成されるオリゴマー状のポリマーであり、T単位のみから構成されるポリマー、Q単位のみから構成されるポリマー、T単位とQ単位から構成されるポリマーがある。またそれらポリマーはさらに少量のM単位やD単位を含むこともある。
本発明におけるオルガノポリシロキサン(a)や同(b)は、上記硬化性オルガノポリシロキサンである。以下、特に言及しない限り、硬化性のオルガノポリシロキサンを単にオルガノポリシロキサンという。
T1:R-Si(-OX)2(-O*-)
T2:R-Si(-OX)(-O*-)2
T3:R-Si(-O*-)3
(式中、Rは水素原子または炭素数が1~10の置換もしくは非置換の1価の有機基を表し、Xは水素原子または炭素数1~6のアルキル基を表し、O*は2つのケイ素原子を連結する酸素原子を表す)
本発明のオルガノポリシロキサンであるオルガノポリシロキサン(a)は、T1~T3の各単位を、T1:T2:T3=0~5:15~40:55~85、かつT3/T2=1.5~4.0の割合で含む。また、オルガノポリシロキサン(a)中のOX基について、それがアルコキシ基である個数(A)とそれが水酸基である個数(B)との割合、(B)/(A)が分子平均で12.0以上である。かつ、オルガノポリシロキサン(a)の質量平均分子量は800~8000である。なお、オルガノポリシロキサン(a)は、TモノマーであるT0を実質的に含まない。
本発明の本発明のハードコート剤組成物は、オルガノポリシロキサン(a)とオルガノポリシロキサン(b)とを含む。オルガノポリシロキサン(b)はオルガノポリシロキサン(a)の質量平均分子量の1/10~1/1.5倍の質量平均分子量を有するオルガノポリシロキサンである。オルガノポリシロキサン(b)は、組み合わされるオルガノポリシロキサン(a)よりも質量平均分子量の小さいオルガノポリシロキサンであり、前記T1~T3単位を有する。T1、T2、T3の数の比、T3/T2の割合、(B)/(A)の比は特に限定されない。
トスガード510(商品名、モメンティブ・パフォーマンス・マテリアルズ社製);分子量:Mn=1370、Mw=1380、Mw/Mn=1.01。T単位の個数:(M単位とD単位とQ単位のそれぞれの個数の総量)=99.9以上:ND。T0:T1:T2:T3=ND:2:36:62。
KP851(商品名、信越化学工業社製);分子量:Mn=1390、Mw=1400、Mw/Mn=1.01、T単位の個数:(M単位とD単位とQ単位のそれぞれの個数の総量)=99.9以上:ND。T0:T1:T2:T3=trace:21:58:21。
本発明のハードコート剤組成物は、オルガノポリシロキサン(a)とオルガノポリシロキサン(b)とを含有する。本発明のハードコート剤組成物における、オルガノポリシロキサン(a)とオルガノポリシロキサン(b)の含有量としては、各成分の質量平均分子量にもよるが、溶媒を除く組成物(以下、必要に応じて「不揮発成分」という)全量に対して、オルガノポリシロキサン(a)の含有量が1~35質量%であり、オルガノポリシロキサン(b)の含有量が40~65質量%であることが好ましく、オルガノポリシロキサン(a)の含有量が5~25質量%であり、オルガノポリシロキサン(b)の含有量が45~65質量%であることがより好ましい。本明細書において、不揮発成分の量とは、150℃で45分間放置した後のハードコート剤組成物の質量変化に基づいて測定したものである。
このような溶媒に用いるアルコールとしては、メタノール、エタノール、1-プロパノール、2-プロパノール、1-ブタノール、2-ブタノール、2-メチル-1-プロパノール、1-メトキシ-2-プロパノール、2-エトキシエタノール、4-メチル-2-ペンタノール、および2-ブトキシエタノール等が好ましく、これらのうちでも、オルガノポリシロキサン(a)およびオルガノポリシロキサン(b)の溶解性が良好な点、樹脂基板への塗工性が良好な点から、沸点が80~160℃のアルコールが好ましい。具体的には、エタノール、1-プロパノール、2-プロパノール、1-ブタノール、2-ブタノール、2-メチル-1-プロパノール、1-メトキシ-2-プロパノール、2-エトキシエタノール、4-メチル-2-ペンタノール、または2-ブトキシエタノールが好ましい。
本発明のハードコート剤組成物においては、通常行われる評価に加えてこれを評価する指標として、得られる硬化被膜が有する以下の方法で求められる引張応力(σ)を用いるものである。
本明細書において、ハードコート剤組成物を評価する指標として用いる上記硬化被膜の引張応力(σ)とは、具体的には、周囲温度25℃で、薄膜ストレス測定装置によって測定された、硬化被膜形成前後のシリコンウエハの曲率半径の値と、硬化被膜(硬化後)の膜厚の値を用いて、下式(1)で表される式によって算出される応力値である。なお、測定手順は実施例に詳述する。
本発明のハードコート層を有する樹脂基板は、上記本発明のハードコート剤組成物を後述の樹脂基板上に塗布して塗膜を形成し、前記塗膜中の硬化性化合物を硬化させてハードコート層とすることにより製造することができる。ハードコート剤組成物を塗布する方法としては、特に限定されないが、スプレーコート法、ディップコート法、フローコート法等の通常の塗工方法が挙げられる。塗工方法によってハードコート剤組成物の粘度、固形分濃度等を適宜調整することが好ましい。
また、本発明のハードコート層を有する樹脂基板によれば、平板状のものをコールドフォーミングといわれる常温での強制曲げ加工により所定の曲率半径となるように曲げてその状態で使用する、いわゆる「曲げ使用」に用いる場合においても、曲げに対する耐性を有し、ハードコート層でのクラックの発生や、樹脂基板における微小クラックの集まり(クレージング)の発生等を十分に抑制することが可能である。
本発明に用いる樹脂基板の材料である樹脂としては、ポリカーボネート樹脂、ポリスチレン樹脂、芳香族ポリエステル樹脂、アクリル樹脂、ポリエステル樹脂、ポリアリレート樹脂、ハロゲン化ビスフェノールAとエチレングリコールとの重縮合物、アクリルウレタン樹脂、ハロゲン化アリール基含有アクリル樹脂等が挙げられる。
本発明のハードコート層を有する樹脂基板においては、樹脂基板と上記ハードコート層の間にプライマー層を有していてもよく、樹脂基板とハードコート層との密着性向上のためには、プライマー層を有していることが好ましい。プライマー層は、特に限定されないが、本発明においては、アクリル系ポリマー、紫外線吸収剤、および溶媒を含むプライマー組成物を樹脂基板上に塗布し乾燥させることによって形成することが好ましい。
溶媒の量は、アクリル系ポリマー等の樹脂成分100質量部に対して、50~10000質量部であることが好ましく、100~10000質量部が特に好ましい。なお、プライマー組成物中の不揮発成分(固形分)の含有量は、組成物全量に対して0.5~75質量%であることが好ましく、1~40質量%であることが特に好ましい。
以下、実施例において用いたオルガノポリシロキサンは、ケイ素原子結合アルコキシ基として、ケイ素原子結合メトキシ基(SiO-CH3)を有するもののみであったため、上記(B)/(A)として、以下の方法により求めたSi-OH/SiO-CH3の比を用いた。
赤外吸光分析装置(FT-IR、サーモフィッシャーサイエンティフィック社製、型式:Avatar/Nicolet FT-IR360)を用い、2860cm-1付近のSiO-CH3に由来する吸収と900cm-1付近のSi-OHに由来する吸収の面積比からSi-OH/SiO-CH3の比を求めた。
オルガノポリシロキサン中のケイ素原子の結合状態、具体的には、M単位、D単位、T単位、Q単位の存在の割合、およびT0~T3の存在比を、核磁気共鳴分析装置(29Si-NMR:日本電子社製、ECP400)を用いて、29Si-NMRのピーク面積比からそれぞれ求めた。測定条件はポリテトラフルオロエチレン(PTFE)製10mmφ試料管使用、プローブ:T10、共鳴周波数79.42MHz、パルス幅10μsec、待ち時間20sec、積算回数1500回、緩和試薬:Cr(acac)3を0.1質量%、外部標準試料:テトラメチルシランである。また、各構造に由来する29Si-NMRの化学シフトは、メチル系オルガノポリシロキサンの場合、以下のとおりである。
M単位:15~5ppm、
D単位:-15~-25ppm、
T単位:-35~-75ppm、
Q単位:-90~-130ppm。
T0:-40~-41ppm、
T1:-49~-50ppm、
T2:-57~-59ppm、
T3:-66~-70ppm。
ゲルパーミエーションクロマトグラフィー(GPC、Waters社製のWaters2695、RI検出、カラム:Styragel ガードカラム+HR1+HR4+HR5E、溶離液:クロロホルム)によって求めた。
(例1)
0.2Lのフラスコに、メチル系シリコーンレジンKR-220L(商品名、信越化学工業社製、Si-OH/SiO-CH3=11.7、各T単位の存在比がT0:T1:T2:T3=ND:ND:28:72、Mn=1200、Mw=4720、Mw/Mn=3.93)(10g)と1-ブタノール(10g)を加えよく撹拌し、酢酸(10g)、イオン交換水(10g)を加え、さらによく撹拌した。この溶液を25℃で1時間撹拌し、オルガノポリシロキサン(a)「MSi-1」を得た。このMSi-1を含有する溶液(MSi-1濃度:25質量%)をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
反応温度を40℃に変更した以外は例1と同様の方法により、オルガノポリシロキサン(a)「MSi-2」を含有する溶液(MSi-2濃度:25質量%)を得た。この溶液をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
得られたMSi-2について、FT-IRにより、原料であるKR-220Lとの比較を行ったところ、SiO-CH3基由来のピークの減少およびSi-OH基由来のピークの増加を確認した。FT-IRのピーク面積比から求めたMSi-2のSi-OH/SiO-CH3の比は58.7であった。MSi-2はT単位からなり、29Si-NMRの化学シフトから求めた各T単位の存在比は、T0:T1:T2:T3=ND:trace:25.1:74.6であった。また、MSi-2のMnは1230、Mwは4160、Mw/Mnは3.38であった。
反応温度を70℃に変更した以外は例1と同様の方法により、オルガノポリシロキサン(a)「MSi-3」を含有する溶液(MSi-3濃度:25質量%)を得た。この溶液をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
得られたMSi-3について、FT-IRにより、原料であるKR-220Lとの比較を行ったところ、SiO-CH3基由来のピークの減少およびSi-OH基由来のピークの増加を確認した。FT-IRのピーク面積比から求めたこのMSi-3のSi-OH/SiO-CH3の比は40.6であった。MSi-3はT単位からなり、29Si-NMRの化学シフトから求めた各T単位の存在比は、T0:T1:T2:T3=ND:trace:22.8:77.0であった。また、MSi-3のMnは1140、Mwは3750、Mw/Mnは3.28であった。
原料であるKR-220Lをメチル系シリコーンレジンKR-500(信越化学工業社製、Si-OH基由来のピークはFT-IRにより確認されず、実質SiO-CH3のみである。各T単位の存在比はT0:T1:T2:T3=ND:15:58:27、Mn=700、Mw=1240、Mw/Mn=1.77)に変更した以外は例2と同様の方法によりオルガノポリシロキサン(a)「MSi-5」を得た。このMSi-5を含有する溶液(MSi-5濃度:25質量%)をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
反応温度を70℃に変更した以外は例4と同様の方法により、オルガノポリシロキサン(a)「MSi-6」を含有する溶液(MSi-6濃度:25質量%)を得た。この溶液をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
得られたMSi-6について、FT-IRにより、原料であるKR-500との比較を行ったところ、SiO-CH3基由来のピークの減少およびSi-OH基由来のピークの出現を確認した。FT-IRのピーク面積比から求めたMSi-6のSi-OH/SiO-CH3の比は39.2であった。MSi-6はT単位からなり、29Si-NMRの化学シフトから求めた各T単位の存在比は、T0:T1:T2:T3=ND:0.8:28.9:70.3であった。MSi-6のMnは490、Mwは1120、Mw/Mnは2.28であった。
原料であるKR-220Lをメチル系シリコーンレジンKR-500(信越化学工業社製、Si-OH基由来のピークはFT-IRにより確認されず、実質SiO-CH3のみである。各T単位の存在比はT0:T1:T2:T3=ND:15:58:27、Mn=700、Mw=1240、Mw/Mn=1.77)に変更した以外は例1と同様の方法によりオルガノポリシロキサン「MSi-4」を得た。このMSi-4を含有する溶液(MSi-4濃度:25質量%)をそのまま後述の[3]ハードコート剤組成物の調製に用いた。
メチル系シリコーンレジンKR-220L(信越化学工業社製、Si-OH/SiO-CH3=11.7、各T単位の存在比がT0:T1:T2:T3=ND:ND:28:72、Mn=1200、Mw=4720、Mw/Mn=3.93)は、Si-OH/SiO-CH3が本発明のオルガノポリシロキサン(a)の範囲外のオルガノポリシロキサンであり、これを例36のオルガノポリシロキサンとして、以下の[3]ハードコート剤組成物の調製に用いた。
メチル系シリコーンレジンKR-500(信越化学工業社製、Si-OH基由来のピークはFT-IRにより確認されず、実質SiO-CH3のみである。各T単位の存在比はT0:T1:T2:T3=ND:15:58:27、Mn=700、Mw=1240、Mw/Mn=1.77)は、Si-OH/SiO-CH3およびT1:T2:T3がともに本発明のオルガノポリシロキサン(a)の範囲外のオルガノポリシロキサンであり、これを例37のオルガノポリシロキサンとして、以下の[3]ハードコート剤組成物の調製に用いた。
このようにして得られた、各例のオルガノポリシロキサンの構造特性を表1にまとめた。
1Lのフラスコに、約15nmの平均粒子径をもつ水分散コロイダルシリカ(pH3.1、シリカ微粒子固形分35質量%)200gと酢酸0.2gを仕込み、メチルトリメトキシシラン138gを添加した。1時間撹拌した後、組成物のpHは4.5で安定化した。この組成物を25℃で4日間熟成してシリカ・メタノール-水分散液中で部分加水分解縮合を確実に形成させた。
(例6~15)ハードコート剤組成物HC-1~HC-6、HC-8~HC-11の調製 上記[1]で得られた例1~5のオルガノポリシロキサン(a):オルガノポリシロキサン(a)MSi-1~Msi-3、Msi-5、MSi-6を含む溶液に、上記[2]で得られたオルガノポリシロキサン(b)PSi-1組成物溶液を、表2に示した量(質量%)で配合し、よく混合することによって、ハードコート剤組成物HC-1~HC-6、HC-8~HC-11(例6~15)を得た。
上記[1]で得られた例35~37のオルガノポリシロキサン:オルガノポリシロキサンMSi-4を含む溶液、メチル系シリコーンレジンKR-220L/1-ブタノール溶液(濃度:25質量%)、メチル系シリコーンレジンKR-500/1-ブタノール溶液(濃度:25質量%)の溶液に、上記[1]で得られたオルガノポリシロキサン(b)PSi-1組成物溶液を表3に示した量(質量%)で配合し、よく混合することによって、ハードコート剤組成物HC-7、HC-13、HC-14(例38、40、41)を得た。また、上記[1]で得られたオルガノポリシロキサン(b)PSi-1組成物溶液をHC-12(例39)とした。
上記例6~15で得られたハードコート剤組成物および例38~41で得られたハードコート剤組成物を用いて得られた硬化被膜について、以下の方法で引張応力(σ)の測定を行った。
外径が4インチ、厚さが525±25μmのシリコンウエハを、オリエンテーションフラットを基準として、薄膜ストレス測定装置FLX-2320(KLA Tencor社製)内の所定位置に収容した後、周囲温度25℃で、このシリコンウエハの曲率半径Rbを計測した。
なお、硬化条件は、ハードコート剤組成物HC-1を樹脂基板の表面に塗布して得られる塗膜について、赤外吸収スペクトル測定装置(Avatar/Nicolet FT-IR360、サーモフィッシャーサイエンティフィック社製)により全反射法を用いて波数910cm-1付近のシラノール基による吸収ピークの消失を確認することにより決定した。
上記で測定されたRa、Rbと、さらに以下に説明する各ファクタを用いて、下記式(1)で表される引張応力(σ)を算出した。
[例16]
厚さ3mmのポリカーボネート樹脂板(カーボグラス(登録商標)ポリッシュ クリヤー(商品名、旭硝子社製))に、アクリル系プライマーSHP470(モメンティブ・パフォーマンス・マテリアルズ社製、固形分10質量%溶液)をディップ方式で、乾燥後の膜厚が4~5μmになるように塗工し、120℃に設定した熱風循環式乾燥器を用いて30分間の加熱乾燥を行いプライマー層を形成させた。つぎに、ハードコート剤組成物HC-1をディップ方式でコーティングし、25℃で20分間放置後、120℃で1時間硬化させてハードコート層を有する樹脂基板のサンプルを作製した。ハードコート層の膜厚は3μmであった。このサンプルは、ポリカーボネート板の両面にアクリル系プライマー層とハードコート層が形成されている。
上記[3]で調製したハードコート剤組成物HC-2~HC-6、HC-8~HC-11を、硬化後のハードコート層の膜厚が表5に示した膜厚となるようにディップ方式でコーティングした以外は、例1と同様の方法でハードコート層を有する樹脂基板のサンプルを作製した。
上記[3]で調製したハードコート剤組成物HC-7、HC-12~HC-14(例38~41)を表6に示した膜厚でコーティングした以外は、例16と同様の方法でハードコート層を有する樹脂基板のサンプルを作製した。
比較のために、市販のシリコーン系ハードコート層を有するポリカーボネート板として、厚さ5mmのポリカーボネート板上にプライマー層とシリコーン系ハードコート層が順に形成されたEC100XX(商品名、筒中プラスチック工業社製)(例50)、および厚さ3mmのポリカーボネート板上にプライマー層とシリコーン系ハードコート層が順に形成されたレキサン(登録商標)マーガードMR10(商品名、SABICイノベーディブプラスチックス社製)(例51)を用いた。
上記[4]の各例で得られたハードコート層を有する樹脂基板サンプルについて、下記項目の評価を行った。具体的には、例16~例49で得られた樹脂基板サンプルを用いて、初期の外観、密着性、耐擦傷性、および耐久性(耐水性、耐湿性、耐熱性)の試験を行った。その評価結果を、例16~34については表5に、例42~例49については表6に示す。また、例16~例25および例42~例46で得られた樹脂基板サンプルを用いて耐候性試験を行った。結果については表7に示す。さらに、例26~例34および例47~例51で得られた樹脂基板サンプルを用いて行った強制曲げ試験については表8にその評価結果を示す。
ハードコート被膜(プライマー層とハードコート層を合わせた被膜全体を「ハードコート被膜」という。)を目視で観察し、異常の有無を判定した。
○:異常なし
×:ハードコート被膜にクラックあり
各サンプルにおけるハードコート層の膜厚を干渉膜厚測定装置(スペクトラ・コープ社製、Solid Lambda Thickness)を用いて測定した。このとき、屈折率はn=1.46の値を用いた。
JIS K5600(5.9)に準拠し、テーバー磨耗試験機(東洋精機製作所社製、型式:ROTARY ABRASION TESTER)に磨耗輪 CALIBRASE(登録商標)CS-10F(TABER社製)を装着し、荷重500g下での500回転後のヘーズ(曇価)を測定し、試験後と試験前の曇価差ΔH500を耐擦傷性とした。ヘーズはJIS K7105(6.4)に準拠し、ヘーズメーター(スガ試験機社製、型式:HGM-2)にて測定した。
JIS K5600(5.6)に準拠し、カミソリ刃を用いて、ハードコート被膜に1mm間隔で縦、横11本ずつ切れ目を入れて100個の碁盤目を作製し、セロテープ(ニチバン社製、CT24)をよく付着させた後、剥離テストを行った。ハードコート被膜が剥離せずに残存したマス目数(X)をX/100で表示した。
サンプルを、40℃の温水に30日間浸漬した後のクラック、剥離の有無、白濁について外観変化および密着性を評価した。
サンプルを、50℃、95%RHの恒温槽中で30日間放置した後のハードコート被膜のクラック、剥離の有無、白濁について外観変化および密着性を評価した。
サンプルを、110℃の熱風循環式オーブン中で30日間加熱した後のハードコート被膜のクラック、剥離の有無について外観変化および密着性を評価した。
光源にメタルハライドランプを用いた促進耐候性試験機(ダイプラ・ウインテス社製;ダイプラ・メタルウェザー KU-R4)を用い、例16~例25および例42~例46で得られた樹脂基板サンプルに対して、光の照射、結露、暗黒の3条件を連続で負荷し、792時間経過後、および996時間経過後のハードコート被膜のクラックの有無および剥離について目視で評価した(耐候クラック性)。792時間以前にハードコート被膜のクラックまたは剥離が観察されたサンプルについてはその時間を記録した。なお、耐候クラック性についての評価は、耐候性試験前にも実施した。また、耐候性試験前/後の黄色度および黄変度ΔYI、ヘーズ(曇価)および曇価差ΔHを測定した。
耐候性試験前(初期)/耐候性試験後のハードコート被膜の外観を目視で観察し、下記基準により、異常の有無を判定した。
○:異常なし、
×:ハードコート被膜にクラックあり
××:ハードコート被膜に剥離あり
JIS K7105(6.3)の透過測定方法に準拠し、分光光度計(島津製作所社製、SolidSpec-3700DUV)にて、耐候性試験前(初期)、792時間経過後、996時間経過後の透過スペクトルを測定した結果から黄色度を計算した。耐候性試験前の黄色度をYI0とし、試験前と792時間経過後の黄色度の差をΔYI792とし、試験前と996時間経過後の黄色度の差をΔYI996とする。判定基準として、ΔYI≦+5であれば合格とした。
JIS K7105(6.4)に準拠し、ヘーズメーター(スガ試験機株式会社製、HGM-2)にて耐候性試験前(初期)、792時間経過後、996時間経過後のヘーズ(曇価)を測定した。試験後と試験前の曇価差ΔHを評価した。耐候性試験前の曇価をH0とし、試験前と792時間経過後の曇価の差をΔH792とし、試験前と996時間経過後の曇価の差をΔH996とする。判定基準として、ΔH≦+5%であれば合格とした。
図1に外観図を示す強制曲げ試験治具を用いて、例26~例34および例47~例51で得られた樹脂基板サンプルについて、以下の方法で強制曲げ試験を行った。
ポリカーボネート板のコールドフォーミング工法における各板厚に対する許容曲率半径Rは常温で、以下の(I)式で表される。
R=180t …(I)
(式中、tは、ポリカーボネート基板の厚さ[mm]である。)
強制曲げ試験治具1にハードコート層を有するポリカーボネート板サンプルを曲げ固定したものを、温度80℃、相対湿度95%の恒温恒湿槽中に入れ、そのまま保持する促進試験を強制曲げ試験として行い、以下の240時間後の強制曲げ外観判定、強制曲げクラック耐性について評価した。
240時間後のハードコート被膜へのクラックおよびポリカーボネート基板への微小クラックの集まり(クレージング)の有無について観察し、下記の基準により目視で異常の有無を判定した。なお、試験に用いた上記[4]の各例で得られたハードコート層を有する樹脂基板サンプルは、樹脂基板3であるポリカーボネート基板の両面にプライマー層とハードコート層からなるハードコート被膜4が形成されたものである。ハードコート被膜のクラックの発生については、少なくとも片面のハードコート被膜で発生すれば「×」と判定された。また、クレージングはハードコート被膜の引張り応力に起因して発生するものである。
○:異常なし
×:ハードコート被膜にクラックあり
××:ポリカーボネート基板にクレージングあり
240時間後の外観判定において問題のないものに関しては、試験を継続してハードコート被膜へのクラック発生時間を調査し、本発明のハードコート層を有する樹脂基板の優位性について判定した。
また、強制曲げ試験に用いた、例26~例34および例47~例51で得られた樹脂基板サンプルについて、上記耐候性試験と同様の試験を負荷時間996時間で行い、耐候クラック性を評価した。996時間以前にハードコート被膜のクラックまたは剥離が観察されたサンプルについてはその時間を記録した。
なお、2009年3月27日に出願された日本特許出願2009-080355号の明細書、特許請求の範囲、図面及び要約書の全内容をここに引用し、本発明の明細書の開示として、取り入れるものである。
L…固定長(mm)
Claims (16)
- 下記T1~T3で表される含ケイ素結合単位を、前記単位の個数の割合で、T1:T2:T3=0~5:15~40:55~85、かつT3/T2=1.5~4.0の割合で含み、分子内のケイ素原子に結合するアルコキシ基の個数(A)に対するケイ素原子に結合する水酸基の個数(B)の割合、(B)/(A)が分子平均で12.0以上であり、質量平均分子量が800~8000であるオルガノポリシロキサン。
T1:R-Si(-OX)2(-O*-)
T2:R-Si(-OX)(-O*-)2
T3:R-Si(-O*-)3
(式中、Rは水素原子または炭素数が1~10の置換もしくは非置換の1価の有機基を表し、Xは水素原子または炭素数1~6のアルキル基を表し、O*は2つのケイ素原子を連結する酸素原子を表す) - 下記T1~T3で表される含ケイ素結合単位を有するオルガノポリシロキサン(a)と同含ケイ素結合単位を有するオルガノポリシロキサン(b)とを含有するハードコート剤組成物であって、前記オルガノポリシロキサン(a)が請求項1に記載のオルガノポリシロキサンであり、前記オルガノポリシロキサン(b)が前記オルガノポリシロキサン(a)の質量平均分子量の1/10~1/1.5倍の質量平均分子量を有するオルガノポリシロキサンである、ハードコート剤組成物。
T1:R-Si(-OX)2(-O*-)
T2:R-Si(-OX)(-O*-)2
T3:R-Si(-O*-)3
(式中、Rは水素原子または炭素数が1~10の置換もしくは非置換の1価の有機基を表し、Xは水素原子または炭素数1~6のアルキル基を表し、O*は2つのケイ素原子を連結する酸素原子を表す)
結する酸素原子を表す) - 前記オルガノポリシロキサン(a)と前記オルガノポリシロキサン(b)とを溶解する溶媒を、組成物全量に対し20質量%以上含有する請求項2に記載のハードコート剤組成物。
- 前記オルガノポリシロキサン(a)に対する前記オルガノポリシロキサン(b)の含有量の割合が質量比で、1.5~30倍である請求項2または3に記載のハードコート剤組成物。
- 溶媒を除く組成物全量に対して、前記オルガノポリシロキサン(a)の含有量が1~35質量%であり、前記オルガノポリシロキサン(b)の含有量が40~65質量%である請求項2または3に記載のハードコート剤組成物。
- さらにシリカ微粒子(c)を含有する請求項2から5のいずれか1項に記載のハードコート剤組成物。
- 前記オルガノポリシロキサン(a)の質量平均分子量が1000~6000である請求項2から6のいずれか1項に記載のハードコート剤組成物。
- 溶媒を除く組成物全量に対して、前記オルガノポリシロキサン(a)の含有量が1~35質量%であり、前記オルガノポリシロキサン(b)の含有量が40~65質量%であり、前記シリカ微粒子(c)の含有量が1~50質量%である請求項6または7に記載のハードコート剤組成物。
- 下記式(1)で表される引張応力(σ)が31MPa以下の硬化被膜が得られる請求項2から8のいずれか1項に記載のハードコート剤組成物。
(式(1)中、Rは、薄膜ストレス測定装置により周囲温度25℃で計測される、シリコンウエハ単体の曲率半径と、前記シリコンウエハを用いて作製される、検体となるハードコート剤組成物を120℃、1時間の条件で硬化させ形成させた硬化被膜を表面に有するシリコンウエハ試料の曲率半径と、の差[m]であり、E/(1-ν)は、シリコンウエハの弾性率E、ポアソン比νから算出される二軸弾性係数(結晶面(100):1.805×1011Pa)であり、hは、シリコンウエハの厚さ[m]であり、tは硬化被膜の厚さ[m]である。) - 樹脂基板の少なくとも一方の面上に、請求項2~9のいずれか1項に記載のハードコート剤組成物の硬化物からなるハードコート層を有する樹脂基板。
- 前記ハードコート層の厚さが0.1~20μmである請求項10に記載のハードコート層を有する樹脂基板。
- 平板状であり、常温において曲げ使用可能な請求項10に記載のハードコート層を有する樹脂基板。
- 前記曲げ使用が、許容曲率半径以上の条件下で行われる請求項12に記載のハードコート層を有する樹脂基板。
- 前記ハードコート層の厚さが0.1~6μmである請求項12または13に記載のハードコート層を有する樹脂基板。
- 前記樹脂基板と前記ハードコート層との間にプライマー層を有する請求項10~14のいずれか1項に記載のハードコート層を有する樹脂基板。
- 前記樹脂基板の材料がポリカーボネート樹脂である請求項10~15のいずれか1項に記載のハードコート層を有する樹脂基板。