WO2009115324A1 - Galvanisches element mit foliendichtung - Google Patents
Galvanisches element mit foliendichtung Download PDFInfo
- Publication number
- WO2009115324A1 WO2009115324A1 PCT/EP2009/002020 EP2009002020W WO2009115324A1 WO 2009115324 A1 WO2009115324 A1 WO 2009115324A1 EP 2009002020 W EP2009002020 W EP 2009002020W WO 2009115324 A1 WO2009115324 A1 WO 2009115324A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- groups
- element according
- galvanic element
- acid
- polymer
- Prior art date
Abstract
Description
Claims