WO2008113507A1 - Diesel particulate filter component - Google Patents

Diesel particulate filter component Download PDF

Info

Publication number
WO2008113507A1
WO2008113507A1 PCT/EP2008/001997 EP2008001997W WO2008113507A1 WO 2008113507 A1 WO2008113507 A1 WO 2008113507A1 EP 2008001997 W EP2008001997 W EP 2008001997W WO 2008113507 A1 WO2008113507 A1 WO 2008113507A1
Authority
WO
WIPO (PCT)
Prior art keywords
section
filter
channel walls
exhaust
diesel particulate
Prior art date
Application number
PCT/EP2008/001997
Other languages
German (de)
French (fr)
Inventor
Timo Walz
Original Assignee
Elringklinger Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Elringklinger Ag filed Critical Elringklinger Ag
Priority to EP08734606A priority Critical patent/EP2122132A1/en
Publication of WO2008113507A1 publication Critical patent/WO2008113507A1/en

Abstract

The invention relates to a diesel particulate filter (10) having a ceramic molded body, in which exhaust gas channels are configured that are limited by channel walls, and which has a filter section (16) and an oxidation catalyst section (14) upstream of the filter section, wherein the oxidation catalyst section has open exhaust gas flow channels (18) at the ends thereof, and the filter section has channel walls (24) comprising defined filter openings, and closures (20a, 22a) closing exhaust gas channels adjacent to each other alternately in the region of one of the channel ends, or in the region of the other channel end. The channel walls of the filter section are equipped at least in sections with a first catalyst substance effecting a reduction of the combustion temperature of the diesel exhaust particles retained by the filter, and the channel walls of the oxidation catalyst section are equipped at least in sections with a second catalyst substance effecting an oxidation of hydrocarbons. In order to improve the efficiency of the oxidation catalyst section, the ceramic body is configured such that the channel wall surface formed by the channel walls of the oxidation catalyst section is larger per unit of length than the channel wall surface formed by the channel walls of the filter section.

Description

Dieselpartikelfilter-Bauteil Diesel particulate filter component
Bei modernen Diesel-Hubkolbenmotoren werden zur Nachbehandlung der Abgase aus dem Verbrennungsprozess sogenannte Dieselpartikelfilter eingesetzt, in denen in Abhängigkeit vom Betriebszustand des Dieselmotors in dessen Abgasen enthaltene Rußpartikel zurückgehalten werden. Durch diese im Filter zurückgehaltenen Rußpartikel steigt der Strömungswiderstand des Dieselpartikelfilters und dadurch der Gasdruck, gegen den die Abgase (Verbrennungsgase) aus dem Motor abströmen, was sich unter anderem negativ auf den Kraftstoffverbrauch auswirkt. Deshalb muss ein solches Dieselpartikelfilter in unregelmäßigen Zeitabständen, deren Länge bei einem Fahrzeug-Dieselmotor vom Fahrverhalten abhängt, regeneriert werden, wobei die im Filter zurückgehaltenen Rußpartikel verbrannt werden, d. h. der Kohlenstoff zu CO2 oxidiert wird. Da bei modernen Dieselmotor-Fahrzeugen diese Regeneration des Die- selpartikelfiiters durch den Anstieg des vom Filter hervorgerufenen Abgasgegendrucks auf einen zugelassenen Maximalwert ausgelöst wird, kann eine Filterregeneration beispielsweise unter Volllast oder im Teillastbereich des Motors erfolgen, d. h. im gesamten sogenannten Kennfeldbereich der Motorsteuerung.In modern diesel reciprocating engines so-called diesel particulate filters are used for the aftertreatment of the exhaust gases from the combustion process, in which depending on the operating condition of the diesel engine in the exhaust gases contained soot particles are retained. By these retained in the filter soot particles increases the flow resistance of the diesel particulate filter and thereby the gas pressure against which the exhaust gases (combustion gases) flow out of the engine, which, inter alia, has a negative effect on fuel consumption. Therefore, such a diesel particulate filter must be regenerated at irregular intervals, the length of which in a vehicle diesel engine depends on driving behavior, whereby the soot particles retained in the filter are burned, ie the carbon is oxidized to CO 2 . Since in modern diesel engine vehicles this regeneration of the diesel particulate filter is triggered by an increase in the exhaust back pressure caused by the filter to an approved maximum value, a filter regeneration can take place, for example, under full load or in the partial load range of the engine, ie in the entire so-called engine control range.
Bei den modernen Dieselmotor-Fahrzeugen werden bei der Regeneration des Dieselpartikelfilters die in diesem zurückgehaltenen Rußpartikel primär dadurch verbrannt, dass die Temperatur der in das Dieselpartikelfilter einströmenden Abgase angehoben wird. Eine effiziente Verbrennung der Rußpartikel ohne dass den Abgasen stromaufwärts des Dieselpartikelfilters Additive, wie Harnsäure, zugesetzt werden, erfordert Abgastemperaturen von mehr als 6000C; diese werden üblicherweise durch Eingriffe in die Motorsteuerung erreicht, nämlich durch Eingriffe wie Drosselung der dem Motor zugeführten Luft, mehrfache Brennstoff-Einspritzung pro Verbrennungszyklus eines Zylinders und/oder zeitliche Verzögerung des Einspritz-Zeitpunkts - alle diese Maßnahmen haben zur Folge, dass ein Teil des in die Zylinder eingespritzten Brennstoffs nur unvollständig verbrannt wird und deshalb unverbrannte Kohlenwasserstoffe in den Abgasstrom des Motors gelangen. Diese unverbrannten Kohlenwasserstoffe werden dann gezielt in einem Oxidationskataly- sator verbrannt, welcher als gesondertes Bauteil im Abgasstrang des Motors stromaufwärts des Dieselpartikelfilters angeordnet ist und durch den infolge der Verbrennung dieser Kohlenwasserstoffe die Abgastemperatur vor dem Dieselpartikelfilter auf eine für einen effizienten Abbrand der Rußpartikel im Dieselpartikelfilter hinreichende Temperatur angehoben wird.In modern diesel engine vehicles, in the regeneration of the diesel particulate filter, the soot particulate retained therein is primarily burned by raising the temperature of the exhaust gases flowing into the diesel particulate filter. Efficient combustion of the soot particles without the addition of the additives, such as uric acid, to the exhaust gases upstream of the diesel particulate filter requires exhaust gas temperatures of more than 600 ° C .; These are usually achieved by interventions in the engine control, namely by interventions such as throttling the air supplied to the engine, multiple fuel injection per combustion cycle of a cylinder and / or time delay of the injection timing - all of these measures have a part of the injected into the cylinders Fuel incomplete is burned and therefore get unburned hydrocarbons in the exhaust stream of the engine. These unburned hydrocarbons are then burnt specifically in an oxidation catalytic converter, which is arranged as a separate component in the exhaust line of the engine upstream of the diesel particulate filter and by the combustion of these hydrocarbons, the exhaust gas temperature before the diesel particulate filter to sufficient for efficient combustion of the soot particles in the diesel particulate filter Temperature is raised.
Aus der EP-B-I 371 826 ist aber auch schon ein Dieselpartikelfilter-Bauteil bekannt geworden, welches stromaufwärts eines Filterabschnitts einen Oxidationskatalysatorabschnitt aufweist, wobei diese beiden Abschnitte einen gemeinsamen, länglichen und einstückigen Keramikkörper aufweisen.From EP-B-1 371 826, however, a diesel particulate filter component has already become known, which has an oxidation catalyst section upstream of a filter section, these two sections having a common, elongated and one-piece ceramic body.
Bei dieser bekannten Vorrichtung handelt es sich also um ein Dieselpartikelfilter-Bauteil mit einem von Dieselmotor-Abgasen zu durchströmenden keramischen Formkörper, in welchem von Kanalwänden begrenzte Abgaskanäle ausgebildet sind und welcher einen Filterabschnitt sowie stromaufwärts des Filterabschnitts einen Oxidationskatalysatorabschnitt aufweist, wobei diese beiden Abschnitte einen länglichen monolithischen Keramikkörper mit einem Abgas-Einlassende und einem Abgas-Auslassende bilden, der Oxidationskatalysatorabschnitt sich in Längsrichtung des Keramikkörpers erstreckende, an ihren Enden offene Abgasdurchströmkanäle und der Filterabschnitt sich in Längsrichtung des Keramikkörpers erstreckende Kanalwände mit definierten Filteröffnungen sowie einander benachbarte Abgaskanäle abwechselnd im Bereich des einen bzw. im Bereich des anderen Kanalendes verschließende Verschlüsse aufweist, die Kanalwände des Filterabschnitts mindestens bereichsweise mit einer eine Reduzierung der Verbrennungstemperatur der vom Filter zurückgehaltenen Dieselrußpartikel bewirkenden ersten Katalysatorsubstanz und die Kanalwände des Oxidationskatalysatorabschnitts mindestens bereichsweise mit einer eine Oxidation von Kohlenwasserstoffen bewirkenden zweiten Katalysatorsubstanz versehen sind. Die vorliegende Erfindung betrifft ein Dieselpartikelfilter-Bauteil dieser Gattung.In this known device is thus a diesel particulate filter component with a flowing through diesel engine exhaust ceramic molded body in which channel walls limited exhaust channels are formed and which has a filter section and upstream of the filter section an oxidation catalyst section, said two sections an elongated monolithic ceramic body having an exhaust inlet end and an exhaust outlet end, the oxidation catalyst in the longitudinal direction of the ceramic body extending, open at their ends Abgasdurchströmkanäle and the filter portion extending in the longitudinal direction of the ceramic body channel walls with defined filter openings and adjacent exhaust ducts alternately in the region of one or in the region of the other channel end occlusive closures, the channel walls of the filter section at least partially with a Reduzie tion of the combustion temperature of the filter particles retained by the filter soot-causing first catalyst substance and the channel walls of the oxidation catalyst section are at least partially provided with a oxidation of hydrocarbons causing second catalyst substance. The present invention relates to a diesel particulate filter component of this type.
Bei dieser bekannten Vorrichtung beträgt die Länge des Oxidationskatalysa- torabschnitts nur einen Bruchteil der Länge des Filterabschnitts (in Durchströmrichtung der Abgase bzw. in Längsrichtung des Keramikkörpers gemessen), die Form und Größe des Querschnitts der untereinander gleichen Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts ist gleich der Form und Größe der gleichfalls untereinander gleichen Abgaskanäle des Filterabschnitts, und die Anzahl der Abgasdurchströmkanäle des Oxidationskataly- satorabschnitts ist wesentlich kleiner als die Anzahl der Abgaskanäle des Filterabschnitts. Am Abgas-Auslassende des Keramikkörpers ist jeder zweite Abgaskanal des Filterabschnitts mittels eines Verschlusses in Form eines separaten Stopfens oder dadurch verschlossen, dass die Kanalwände des betreffenden Abgaskanals in einem Längsschnitt durch den Keramikkörper nach Art eines Giebeldaches schräg aufeinander zu verlaufen und miteinander verbunden sind. Die anderen Abgaskanäle des Filterabschnitts sind am anströmseitigen Ende des Filterabschnitts durch von den Kanalwänden gebildete Giebeldach-artige Verschlüsse verschlossen. Bei der Herstellung dieser bekannten Vorrichtung werden Rohlinge des Oxidationskatalysatorabschnitts und des Filterabschnitts aus einer durch Sintern verfestigbaren keramischen Masse im Extrusionsverfahren erzeugt, wobei diese Rohlinge beidseitig offene Abgaskanäle mit parallel zueinander verlaufenden Kanalwänden aufweisen; sodann werden die Abgaskanäle des Filterabschnitts abwechselnd am anströmseitigen und am abströmseitigen Ende des Filterabschnitts so verformt, dass sich die Giebeldach-artigen Verschlüsse ergeben, worauf die Rohlinge des Oxidationskatalysatorabschnitts und des Filterabschnitts mit ihren Stirnseiten gegeneinander angepresst und so miteinander verbunden werden, dass sich ein einstückiger Formkörper ergibt, welcher schließlich durch Sintern verfestigt wird. Der Erfindung lag nun die Aufgabe zugrunde, ein Dieselpartikelfilter-Bauteil der in Rede stehenden Gattung mit einem Oxidationskatalysatorabschnitt und einem Filterabschnitt hinsichtlich seiner Effizienz bei der Verbrennung der vom Filterabschnitt zurückgehaltenen Rußpartikel zu verbessern.In this known device, the length of the Oxidationskatalysa- torabschnitts is only a fraction of the length of the filter section (measured in the flow direction of the exhaust gases or in the longitudinal direction of the ceramic body), the shape and size of the cross section of the same exhaust gas flow channels of the oxidation catalyst section is the same shape and size the likewise mutually identical exhaust passages of the filter section, and the number of Abgasdurchströmkanäle the Oxidationskataly- satorabschnitts is substantially smaller than the number of exhaust passages of the filter section. At the exhaust outlet end of the ceramic body every second exhaust passage of the filter section is closed by a closure in the form of a separate plug or that the channel walls of the respective exhaust duct in a longitudinal section through the ceramic body in the manner of a gable roof obliquely to each other and are connected. The other exhaust passages of the filter section are closed at the upstream end of the filter section by gable-roof type shutters formed by the channel walls. In the production of this known device blanks of the oxidation catalyst section and the filter section are produced from a solidifiable by sintering ceramic mass in the extrusion process, said blanks have open on both sides exhaust channels with mutually parallel channel walls; Then, the exhaust passages of the filter section are alternately deformed at the upstream and downstream ends of the filter section to give the gable roof-like closures, whereupon the blanks of the Oxidationskatalysatorabschnitts and the filter section are pressed against each other with their end faces and joined together so that a one-piece Form body results, which is finally solidified by sintering. The invention was based on the object, a diesel particulate filter component of the type in question with an oxidation catalyst section and a filter section to improve in terms of its efficiency in the combustion of retained by the filter section soot particles.
Diese Aufgabe lässt sich erfindungsgemäß dadurch lösen, dass pro Längeneinheit (zum Beispiel mm oder cm) des Keramikkörpers die Summe der von den Kanalwänden des Oxidationskatalysatorabschnitts gebildeten Kanalwandflächen größer ist als die Summe der von den Kanalwänden des Filterabschnitts gebildeten Kanalwandflächen. Anders ausgedrückt soll die Summe der von den Kanalwänden des Oxidationskatalysatorabschnitts gebildeten Kanalwandflächen, dividiert durch die Länge des Oxidationskatalysatorabschnitts, größer sein als die Summe der von den Kanalwänden des Filterabschnitts gebildeten Kanalwandflächen dividiert durch die Länge des Filterabschnitts.This object can be achieved according to the invention that per unit of length (for example, mm or cm) of the ceramic body, the sum of the channel wall surfaces formed by the channel walls of the oxidation catalyst section is greater than the sum of the channel wall surfaces formed by the channel walls of the filter section. In other words, the sum of the channel wall surfaces formed by the channel walls of the oxidation catalyst section divided by the length of the oxidation catalyst section should be greater than the sum of the channel wall surfaces formed by the channel walls of the filter section divided by the length of the filter section.
Bei einem erfindungsgemäßen Dieselpartikelfilter-Bauteil steht bei einer Regeneration des Dieselpartikelfilters, das heißt des Filterabschnitts, im Oxidationskatalysatorabschnitt eine wesentlich größere Gesamtkanalwandfläche, das heißt eine wesentlich größere katalytisch wirksame Fläche für die Verbrennung (Oxidation) der bei der Regeneration im Abgasstrom des Motors enthaltenen Kohlenwasserstoffe zur Verfügung als bei der sich aus der EP-I 371 826-B ergebenden Vorrichtung, so dass die Kohlenwasserstoffe nicht nur vollständig verbrannt werden können, sondern die Temperatur der in den Filterabschnitt einströmenden Abgase deutlich höher und deshalb der Abbrand der im Filterabschnitt zurückgehaltenen Rußpartikel effizienter und vollständiger ist als bei der bekannten Vorrichtung, so dass die zeitliche Dauer eines Regenerationsvorgangs verkürzt werden kann.In a diesel particulate filter component according to the invention is in a regeneration of the diesel particulate filter, that is, the filter section, in the oxidation catalyst section a much larger Gesamtkanalwandfläche, that is a much larger catalytically active area for the combustion (oxidation) of the hydrocarbons contained in the exhaust stream of the engine in the regeneration Available as in the resulting from EP-A 371 826-B device, so that the hydrocarbons can not only be completely burned, but the temperature of the inflowing into the filter section exhaust gases much higher and therefore the burning of retained in the filter section soot particles more efficient and is more complete than in the known device, so that the time duration of a regeneration process can be shortened.
Das Grundprinzip der erfindungsgemäßen Lösung kann durch eine entsprechende Wahl der Länge des Oxidationskatalysatorabschnitts und/oder durch eine geeignete andere Gestaltung der Querschnittsform der Abgasdurchströmkanäle im Vergleich zur Querschnittsform der Abgaskanäle des Filterabschnitts verwirklicht werden, alternativ oder zusätzlich aber auch dadurch, dass man die Anzahl der Abgasdurchströmkanäle des Oxidations- katalysatorabschnitts größer wählt als die Anzahl der Abgaskanäle des Filterabschnitts - in diesem Zusammenhang sei auf Folgendes hingewiesen: Bei einem erfindungsgemäßen Dieselpartikelfilter-Bauteil beträgt die typische Wandstärke der Kanalwände des Oxidationskatalysatorabschnitts, gegebenenfalls aber auch des Filterabschnitts, einige Zehntel mm, insbesondere ungefähr 0,3 mm, und bei Abgaskanälen mit quadratischem Querschnitt weist der Filterabschnitt typischerweise 40 bis 50, insbesondere ungefähr 45 Kanäle pro cm2 der Querschnittsfläche des Filterabschnitts auf, während der Oxidationskatalysatorabschnitt weit mehr Kanäle besitzt, nämlich typischerweise ungefähr 200 Kanäle je cm2 der Querschnittsfläche des Oxidationskatalysatorabschnitts. In Folge der geringen Wandstärke der Kanalwände lässt sich infolgedessen bei einem erfindungsgemäßen Dieselpartikel- filter-Bauteil die Anzahl der Abgasdurchströmkanäle des Oxidationskatalysa- torabschnitts gegenüber der Anzahl der Abgaskanäle des Filterabschnitts beträchtlich erhöhen, und zwar bei gleichen Außenabmessungen des Querschnitts des Oxidationskatalysatorabschnitts und des Querschnitts des Filterabschnitts, so dass die Summe der Kanalwandflächen des Oxidations- katalysatorabschnitts auch ohne eine Vergrößerung der Länge des Oxidations- katalysatorabschnitts sehr viel größer ist als die Summe der Kanalwandflächen des Oxidationskatalysatorabschnitts der sich aus der EP-I 371 826-B ergebenden bekannten Vorrichtung.The basic principle of the solution according to the invention can be realized by an appropriate choice of the length of the oxidation catalyst section and / or by a suitable different design of the cross-sectional shape of the Abgasdurchströmkanäle compared to the cross-sectional shape of the exhaust ducts of the filter section, alternatively or additionally in that the number of exhaust gas flow passages of the oxidation catalytic converter section is selected to be greater than the number of exhaust passages of the filter section - in this connection it should be pointed out that with a diesel particle filter component according to the invention the typical wall thickness is the channel walls of the oxidation catalytic converter section, but possibly also of the filter section , a few tenths of mm, in particular about 0.3 mm, and in the case of square-section exhaust ducts, the filter section typically has 40 to 50, in particular approximately 45, channels per cm 2 of the cross-sectional area of the filter section, while the oxidation catalytic converter section has far more ducts, typically approximately 200 channels per cm 2 of the cross-sectional area of the oxidation catalyst section. As a result, in the case of a diesel particle filter component according to the invention, the number of exhaust gas flow passages of the oxidation catalytic converter section can be considerably increased compared with the number of exhaust passages of the filter section, for the same outer dimensions of the cross section of the oxidation catalytic converter section and the cross section of the filter section such that the sum of the channel wall areas of the oxidation catalyst section, even without an increase in the length of the oxidation catalyst section, is much greater than the sum of the channel wall surfaces of the oxidation catalyst section of the known device resulting from EP-I 371 826-B.
Unabhängig von der Größe der Querschnitte des Oxidationskatalysator- abschnitts und des Filterabschnitts zeichnet sich ein erfindungsgemäßes Dieselpartikelfilter-Bauteil insbesondere dadurch aus, dass die Anzahl der Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts dividiert durch die Querschnittsfläche des Oxidationskatalysatorabschnitts größer ist als die Anzahl der Abgaskanäle des Filterabschnitts dividiert durch die Querschnittsfläche des Filterabschnitts. Zur Klarstellung sei noch erwähnt, dass wenn vorstehend von an ihren Enden offenen Abgasdurchströmkanälen des Oxidationskatalysatorabschnitts die Rede ist, hierunter insbesondere zu verstehen ist, dass alle Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts an ihren beiden Enden offen sind.Regardless of the size of the cross sections of the oxidation catalyst section and the filter section, a diesel particulate filter component according to the present invention is characterized in that the number of exhaust gas flow passages of the oxidation catalyst section divided by the cross-sectional area of the oxidation catalyst section is greater than the number of exhaust passages of the filter section divided by the cross-sectional area of the filter section. For the sake of clarification, it should be mentioned that, when the exhaust gas flow passages of the oxidation catalytic converter section open at their ends are mentioned above, it is to be understood in particular that all the exhaust gas flow passages of the oxidation catalytic converter section are open at both ends.
Bei dem Filterabschnitt des erfindungsgemäßen Dieselpartikelfilter-Bauteils wird der Filtereffekt durch definierte Filteröffnungen in den Kanalwänden bzw. durch Poren definierter Größe dieser Kanalwände des keramischen Formkörpers erzielt, und die erste Katalysatorsubstanz kann auf den Kanalwänden und/oder auf den Wänden der Filteröffnungen vorgesehen sein.In the filter section of the diesel particle filter component according to the invention, the filter effect is achieved by defined filter openings in the channel walls or by pores of defined size of these channel walls of the ceramic shaped body, and the first catalyst substance can be provided on the channel walls and / or on the walls of the filter openings.
Die Verschlüsse der Abgaskanäle des Filterabschnitts sind insbesondere einstückig an die Kanalwände des Filterabschnitts angeformt und besitzen vorzugsweise ungefähr dieselbe Wandstärke wie diese Kanalwände.The closures of the exhaust ducts of the filter section are in particular integrally formed on the channel walls of the filter section and preferably have approximately the same wall thickness as these channel walls.
Die Abgaskanäle des monolithischen Keramikkörpers verlaufen vorzugsweise exakt in Längsrichtung des Keramikkörpers, obwohl grundsätzlich auch ein leicht schräger Verlauf möglich wäre.The exhaust ducts of the monolithic ceramic body preferably run exactly in the longitudinal direction of the ceramic body, although in principle a slightly oblique course would be possible.
Bei einem erfindungsgemäßen Dieselpartikelfilter-Bauteil können alle Bereiche des monolithischen Keramikkörpers, gegebenenfalls mit Ausnahme eines Außenmantels, dieselbe Porosität aufweisen, weil dann trotz der Porosität der Kanalwände der Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts in diesem die Abgase im Wesentlichen nur entlang seiner Abgasdurchströmkanäle strömen, weil diese in Folge ihrer offenen Einström- und Ausströmenden keinen nennenswerten Strömungswiderstand des Oxidationskatalysator- abschnitts zur Folge haben. Die Kanalwände der Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts können aber auch gasdicht sein oder eine kleinere Porosität aufweisen als die Kanalwände des Filterabschnitts, ohne dass eine solche kleinere Porosität zur Folge hätte, dass ein nennenswerter Anteil der in den Oxidationskatalysatorabschnitt einströmenden Abgase die Kanalwände des Oxidationskatalysatorabschnitts durchströmt. Ein erfindungsgemäßes Dieselpartikelfilter-Bauteil mit integriertem Oxidations- katalysatorabschnitt weist die folgenden Vorteile auf: Weder müssen zwei separate keramische Formkörper für das eigentliche Dieselpartikelfilter und einen vorgeschalteten Oxidationskatalysator hergestellt werden, noch bedarf es der Handhabung zweier solcher keramischen Formkörper; da bei einem erfindungsgemäßen Dieselpartikelfilter-Bauteil nur ein einziger monolithischer Keramikkörper in ein Gehäuse einer Abgasanlage eingebaut werden muss, ergibt sich eine für die Durchströmung der Abgasanlage optimale Positionierung der Kanäle des eigentlichen Filters und des Oxidationskatalysators relativ zueinander von selbst; die durch das eigentliche Filter und den Oxidationskatalysator hervorgerufenen Druckverluste im Abgasstrang eines Motors werden reduziert, da sich die Erzeugung von für die Funktion unnötigen Turbulenzen in der Abgasströmung vermeiden lässt; wegen der Verwendung eines einzigen monolithischen Keramikkörpers für das eigentliche Filter und den der Erhitzung der Abgase dienenden Oxidationskatalysator treten die in Letzterem erhitzten Abgase ohne nennenswerten Temperaturverlust in das eigentliche Filter ein, wodurch die Effizienz der Verbrennung der im Filter zurückgehaltenen Rußpartikel verbessert wird, und wegen der Vermeidung eines nennenswerten solchen Temperaturverlusts kann die (in Strömungsrichtung der Abgase gemessene) Länge des eigentlichen Filters und/oder die Länge des Oxidationskatalysators verhältnismäßig kurz sein, wodurch sich die erforderlichen Mengen der teuren Katalysatorsubstanzen verringern lassen. Vor allem aber ermöglicht es die vorliegende Erfindung, die Baulänge des Oxidationskatalysatorabschnitts und damit die Baulänge des gesamten Dieselpartikelfilter-Bauteils zu minimieren, da die katalytische Wirkung des Oxidationskatalysatorabschnitts je Längeneinheit des Oxidationskatalysator- abschnitts eine sehr viel bessere ist als bei der bekannten Kombination eines Dieselpartikelfilters mit einem Oxidationskatalysator.In a diesel particulate filter component according to the invention, all regions of the monolithic ceramic body, optionally with the exception of an outer shell, have the same porosity, because then despite the porosity of the channel walls of Abgasdurchströmkanäle the Oxidationskatalysatorabschnitts in the exhaust gases flow substantially only along its Abgasdurchströmkanäle because this in succession their open inflow and outflow do not have any significant flow resistance of the Oxidationskatalysator- section result. The channel walls of the Abgasdurchströmkanäle the oxidation catalyst section may also be gas-tight or have a smaller porosity than the channel walls of the filter section, without such a smaller porosity would result in that a significant proportion of the inflowing into the oxidation catalyst section exhaust gases flows through the channel walls of the oxidation catalyst section. An inventive diesel particulate filter component with integrated oxidation catalyst section has the following advantages: Neither two separate ceramic moldings for the actual diesel particulate filter and an upstream oxidation catalyst must be prepared, nor it requires the handling of two such ceramic moldings; Since in a diesel particulate filter component according to the invention only a single monolithic ceramic body has to be installed in a housing of an exhaust system, an optimum for the flow of the exhaust system positioning of the channels of the actual filter and the oxidation catalyst results by itself; the pressure losses in the exhaust gas line of an engine caused by the actual filter and the oxidation catalytic converter are reduced since the generation of unnecessary turbulence in the exhaust gas flow can be avoided; because of the use of a single monolithic ceramic body for the actual filter and the heating of the exhaust gases serving oxidation catalyst in the latter heated exhaust gases enter without significant loss of temperature in the actual filter, whereby the efficiency of combustion of the retained particulate matter in the filter is improved, and because of To avoid a significant such temperature loss, the length of the actual filter (measured in the flow direction of the exhaust gases) and / or the length of the oxidation catalyst can be relatively short, which can reduce the required amounts of the expensive catalyst substances. Above all, however, the present invention makes it possible to minimize the structural length of the oxidation catalyst portion and thus the overall length of the entire diesel particulate filter component, since the catalytic effect of the oxidation catalyst portion per unit length of the oxidation catalyst portion is a much better than in the known combination of a diesel particulate filter with an oxidation catalyst.
Bei bevorzugten Ausführungsformen des erfindungsgemäßen Dieselpartikelfilter-Bauteils ist am Abgas-Einlassende des Keramikkörpers die Summe der Querschnittsflächen seiner Abgasdurchströmkanäle ungefähr gleich groß wie die Summe der Querschnittsflächen der Abgaskanäle des Filterabschnitts an dessen anströmseitigen Ende, da dann das Bauteil optimal durchströmt wird. Dabei kann das Verhältnis der beiden vorgenannten Querschnittsflächensummen im Bereich zwischen 0,8 und 1,2 liegen, auch wenn ein Verhältnis von ungefähr 1 zu bevorzugen ist.In preferred embodiments of the diesel particulate filter component according to the invention, the sum of the cross-sectional areas of its exhaust gas flow passages is approximately the same as at the exhaust gas inlet end of the ceramic body the sum of the cross-sectional areas of the exhaust ducts of the filter section at its upstream end, since then the component is flowed through optimally. In this case, the ratio of the two aforementioned cross-sectional area sums can be in the range between 0.8 and 1.2, even if a ratio of about 1 is preferable.
Zur Verbesserung der mechanischen Stabilität des monolithischen Keramikkörpers sind bei bevorzugten Ausführungsformen des erfindungsgemäßen Dieselpartikelfilter-Bauteils Kanalwände des Oxidationskatalysatorabschnitts mit Kanalwänden und/oder Verschlüssen der Abgaskanäle des Filterabschnitts verbunden, und zwar insbesondere einstückig durch Anformen der erwähnten Elemente aneinander.In order to improve the mechanical stability of the monolithic ceramic body, in preferred embodiments of the diesel particle filter component according to the invention, channel walls of the oxidation catalytic converter section are connected to channel walls and / or closures of the exhaust ducts of the filter section, in particular in one piece by molding the mentioned elements together.
Obwohl der Oxidationskatalysatorabschnitt primär der Aufheizung der Abgase durch Oxidation unverbrannter Kohlenwasserstoffe dient, kann er auch für die Oxidation von in den unbehandelten Abgasen enthaltenem Kohlenmonoxid zu Kohlendioxid verwendet werden, da es hierzu nur erforderlich ist, die im Oxidationskatalysatorabschnitt eingesetzte zweite Katalysatorsubstanz so zusammenzusetzen, dass sie beide Aufgaben erfüllen kann.Although the oxidation catalyst section primarily serves to heat the exhaust gases by oxidation of unburned hydrocarbons, it may also be used for the oxidation of carbon monoxide contained in the untreated exhaust gases to carbon dioxide, since it is only necessary to compose the second catalyst substance used in the oxidation catalyst section so that it can can fulfill both tasks.
Um das Abgas im Oxidationskatalysatorabschnitt möglichst effizient aufzuheizen, sollte gesichert sein, dass in jedem Betriebszustand des Motors nahezu alle im Abgas enthaltenen Kohlenwasserstoffmoleküle und gegebenenfalls alle im Abgas enthaltenen Schadstoffmoleküle, welche sich aufoxidieren lassen, in Kontakt mit der im Oxidationskatalysatorabschnitt verwendeten zweiten Katalysatorsubstanz kommen; diesem Ziel könnte man zwar grundsätzlich durch längere Abgasdurchströmkanäle näher kommen, dies würde jedoch zur Vergrößerung der Baulänge des Bauteils führen. Dies lässt sich dadurch vermeiden, dass die Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts mit turbulenzerzeugenden Strukturen versehen werden, um in den die Abgasdurchströmkanäle durchströmenden Abgasströmen Verwirbelungen herbeizuführen, aufgrund welcher im Vergleich zu einer laminaren Durchströmung die Häufigkeit des Kontakts der in den Abgasen enthaltenen Moleküle mit der im Oxidationskatalysatorabschnitt verwendeten zweiten Katalysatorsubstanz deutlich erhöht wird. Zu diesem Zweck kann man mindestens einige der Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts an wenigstens einem Teil ihrer Kanalwände mit Turbulenzen in den Abgasströmen erzeugenden Strömungsstörelementen versehen; bei diesen kann es sich grundsätzlich um jede Art von makroskopischen Unebenheiten der Kanalwände handeln, also beispielsweise auch um Vertiefungen in den Kanalwandoberflächen, da die Wandstärken der Kanalwände jedoch klein ist und insbesondere im Bereich zwischen ca. 0,15 bis 0,35 mm liegt, werden Ausführungsformen bevorzugt, bei denen die Kanalwände durch die Strömungsstörelemente nicht geschwächt werden, sondern letztere in die Abgasdurchströmkanäle hinein vorspringen und aus fertigungstechnischen Gründen als insbesondere mit den Kanalwänden einstückige Keramikelemente ausgebildet sind, d. h. schon bei der Herstellung des monolithischen Keramikkörpers zusammen mit den Kanalwänden geformt werden. Ein Verfahren, welches dies kostengünstig ermöglicht, wird nachfolgend beschrieben werden.In order to heat the exhaust gas as efficiently as possible in the oxidation catalytic converter section, it should be ensured that in each operating state of the engine almost all hydrocarbon molecules contained in the exhaust gas and, if appropriate, all pollutant molecules contained in the exhaust gas which can be oxidized come into contact with the second catalytic substance used in the oxidation catalytic converter section; Although this goal could be approached in principle by longer Abgasdurchströmkanäle, but this would lead to increase the length of the component. This can be avoided by providing the exhaust gas flow passages of the oxidation catalytic converter section with turbulence-generating structures in order to induce turbulence in the exhaust gas streams flowing through the exhaust gas flow passages, as a result of which the frequency of contact of the molecules contained in the exhaust gases with that in the exhaust gases is greater than that of laminar flow Oxidation catalyst section used second catalyst substance is significantly increased. For this purpose, at least some of the exhaust gas flow passages of the oxidation catalytic converter section can be provided with turbulence elements in the exhaust gas flow generating flow disturbing elements on at least part of their channel walls; these can in principle be any type of macroscopic unevenness of the channel walls, that is, for example, depressions in the channel wall surfaces, since the wall thicknesses of the channel walls are small, and in particular in the range between about 0.15 to 0.35 mm, embodiments are preferred in which the channel walls are not weakened by the Strömungsstörelemente, but the latter project into the Abgasdurchströmkanäle and manufacturing reasons as in particular with the channel walls integral ceramic elements are formed, ie already formed in the manufacture of the monolithic ceramic body together with the channel walls , A method which enables this cost-effectively will be described below.
Bei bekannten Abgas-Katalysatoren mit einen keramischen Formkörper geradlinig durchquerenden Durchströmkanälen mit überall gleichem Querschnitt und offenen Enden wird der Formkörper üblicherweise aus einer durch Trocknen und Sintern verfestigbaren keramischen Masse im Strangpress- oder Stranggießverfahren hergestellt. Ein solches Herstellverfahren erlaubt jedoch als solches nur die Herstellung von Kanälen, die alle an ihren beiden Enden offen sind und überall den gleichen Querschnitt aufweisen.In the case of known exhaust gas catalysts with a through-flow channel having a ceramic shaped body in a straight line and having the same cross section and open ends, the shaped body is usually produced from a ceramic mass which can be solidified by drying and sintering in an extrusion or continuous casting process. However, such a manufacturing method as such only allows the production of channels, all of which are open at both ends and have the same cross-section everywhere.
Deshalb wird gemäß der vorliegenden Erfindung ein Verfahren zur Herstellung eines erfindungsgemäßen Dieselpartikelfilter-Bauteils vorgeschlagen, bei dem ein zu sinternder Rohling des monolithischen Keramikkörpers schichtweise aufgebaut wird, und zwar durch in zur Längsrichtung der Kanäle quer verlaufende Schichten, welche nicht alle gleich gestaltet sind, da ein Teil dieser Schichten z. B. an der Bildung der Verschlüsse der Filterabschnitt-Abgaskanäle und gegebenenfalls der erwähnten Strömungsstörelemente teilnimmt. Ein solches Verfahren zeichnet sich dadurch aus, dass ein zu sinternder Rohling des monolithischen Keramikkörpers durch in dessen Längsrichtung aufeinanderfolgende Schichten durch wiederholte Abfolge der folgenden Schritte aufgebaut wird:Therefore, according to the present invention, there is proposed a method for manufacturing a diesel particulate filter device according to the present invention, wherein a blank of the monolithic ceramic body to be sintered is built up in layers through layers transverse to the longitudinal direction of the channels, which are not all the same a part of these layers z. B. participates in the formation of the closures of the filter section exhaust channels and optionally the mentioned flow disturbing elements. Such a method is characterized in that a blank to be sintered of monolithic ceramic body is constructed by successive layers in the longitudinal direction by repeated succession of the following steps:
(a) Erzeugung einer einem dem jeweiligen Querschnitt des Keramikkörpers entsprechend gestalteten Schicht aus einer formbaren, verfestig baren keramischen Masse und(A) producing a one of the respective cross section of the ceramic body designed according layer of a moldable, solidified ble ceramic mass and
(b) Verfestigung dieser Schicht,(b) solidification of this layer,
worauf der so erzeugte Rohling gesintert wird.whereupon the blank thus produced is sintered.
Besonders einfach lassen sich solche Schichten, und zwar auch Schichten unterschiedlicher Gestalt, im Siebdruckverfahren erzeugen. Am einfachsten erfolgt die Verfestigung einer zuvor hergestellten Schicht durch Trocknen, wobei diese Schicht nur insoweit verfestigt werden muss, dass sie beim Auftragen der nächsten Schicht ihre Gestalt nicht mehr ändert. Nach der Erzeugung aller Schichten und der Verfestigung der zuletzt aufgetragenen Schicht wird der Rohling dann gesintert.Such layers, and even layers of different shapes, can be produced in a particularly simple manner by screen printing. The easiest way to solidify a previously prepared layer by drying, which layer must be solidified only to the extent that it no longer changes its shape when applying the next layer. After the production of all layers and the solidification of the last applied layer, the blank is then sintered.
Formbare keramische Massen, die beim Verfestigen und beim Sintern des Rohlings ihre Dimensionen zumindest nicht nennenswert ändern, sind auf dem Markt erhältlich.Moldable ceramic masses which at least do not appreciably change their dimensions during solidification and sintering of the blank are available on the market.
Ein solches Herstellverfahren für keramische Formkörper, welche mit kata- lytisch wirksamen Substanzen versehen sind, ergibt sich aus der EP-O 627 983-B1, allerdings betrifft dieses Dokument nur die Herstellung poröser Formkörper für keramische Filter. Ein schichtweiser Aufbau eines monolithischen porösen keramischen Formkörpers für einen Dieselpartikelfilter ergibt sich ferner aus der DE-103 43 046-A, wobei der schichtweise Aufbau im Siebdruckverfahren erfolgt. Weitere Merkmale, Einzelheiten und Vorteile der Erfindung ergeben sich aus der beigefügten schematischen Darstellung einer bevorzugten Ausführungsform des erfindungsgemäßen Dieselpartikelfilter-Bauteils sowie der nachfolgenden Beschreibung dieser Ausführungsform; die Zeichnung zeigt einen Längsschnitt durch den monolithischen Keramikkörper dieser Ausführungsform, und zwar einen Schnitt parallel zur Längsrichtung der in diesem Keramikkörper ausgebildeten Kanäle.Such a production method for ceramic shaped bodies which are provided with catalytically active substances results from EP-O 627 983-B1, although this document relates only to the production of porous shaped bodies for ceramic filters. A layered structure of a monolithic porous ceramic shaped body for a diesel particulate filter is further evident from DE-103 43 046-A, wherein the layered structure is carried out by screen printing. Further features, details and advantages of the invention will become apparent from the accompanying schematic representation of a preferred embodiment of the diesel particulate filter component according to the invention and the following description of this embodiment. the drawing shows a longitudinal section through the monolithic ceramic body of this embodiment, namely a section parallel to the longitudinal direction of the channels formed in this ceramic body.
Der als Ganzes mit 10 bezeichnete monolithische Keramikkörper, der von den zu behandelnden Abgasen in Richtung der in die Zeichnung eingefügten Pfeile durchströmt wird, hat im Schnitt senkrecht zur Durchströmrichtung z. B. eine kreisförmige, rechteckige oder quadratische Gestalt mit einer entsprechend geformten Außenwand 12. Der Keramikkörper 10 hat eingangsseitig einen Oxidationskatalysatorabschnitt 14, an den sich in Durchströmrichtung ein Filterabschnitt 16 anschließt. Im Oxidationskatalysatorabschnitt 14 sind Abgasdurchströmkanäle 18 ausgebildet, welche durch poröse oder gasundurchlässige Kanalwände 18a und die gasundurchlässige Außenwand 12 begrenzt werden und an ihren Oberflächen (ausgenommen die Außenseite der Außenwand 12) mit einer Katalysatorsubstanz beschichtet sind, welche in der Zeichnung nicht dargestellt werden konnte, da derartige Beschichtungen äußerst dünn sind. Die Abgasdurchströmkanäle 18 sind sowohl einlass- als auch auslass- seitig offen und haben insbesondere alle denselben, längs der Abgasdurchströmkanäle konstanten Querschnitt, der grundsätzlich jede beliebige Querschnittsform aufweisen kann, vorzugsweise ist der Querschnitt jedoch quadratisch, rechteckig oder kreisförmig.The designated as a whole with 10 monolithic ceramic body, which is traversed by the exhaust gases to be treated in the direction of the arrows inserted into the drawing, has in section perpendicular to the flow direction z. B. a circular, rectangular or square shape with a correspondingly shaped outer wall 12. The ceramic body 10 has on the input side an oxidation catalyst section 14, to which a filter section 16 connects in the flow direction. In the oxidation catalyst section 14 Abgasdurchströmkanäle 18 are formed, which are bounded by porous or gas-impermeable channel walls 18a and the gas-impermeable outer wall 12 and on their surfaces (except the outside of the outer wall 12) are coated with a catalyst substance, which could not be shown in the drawing Such coatings are extremely thin. The exhaust gas flow channels 18 are open both on the inlet and on the outlet side and in particular have all the same, constant cross-section along the exhaust gas flow channels, which can in principle have any cross-sectional shape, but preferably the cross section is square, rectangular or circular.
Bei der im Oxidationskatalysatorabschnitt 14 verwendeten Katalysatorsubstanz handelt es sich um die zweite Katalysatorsubstanz im Sinne der beigefügten Ansprüche, und sie enthält als katalytisch wirksame Bestandteile typischerweise ein Edelmetall wie Platin oder Palladium, gegebenenfalls aber auch ein Oxid oder Oxide seltener Erden wie Ce. Im Filterabschnitt 16 des monolithischen Keramikkörpers 10 sind Abgaskanäle 20 und 22 ausgebildet, welche jeweils am einen Kanalende durch einen Verschluss 20a bzw. 22a verschlossen sind, und zwar sind die Abgaskanäle 20 alle einströmseitig offen und ausströmseitig verschlossen, die Abgaskanäle 22 sind einströmseitig verschlossen und ausströmseitig offen, und im Keramikkörper 10 liegt (in einem Schnitt senkrecht zur Durchströmrichtung betrachtet) jeder Abgaskanal 20 zwischen Abgaskanälen 22 und jeder Abgaskanal 22 zwischen Abgaskanälen 20. Sieht man von den Verschlüssen 20a und 22a ab, werden die Abgaskanäle 20 und 22 durch Kanalwände 24, welche porös sind und definierte Filteröffnungen aufweisen, und außerdem teilweise durch die gasundurchlässige Außenwand 12 begrenzt. Die Innenseite der Außenwand 12 sowie die Oberflächen der Kanalwände 24 und/oder die Wände ihrer Filteröffnungen sind gleichfalls mit einer Katalysatorsubstanz, nämlich der ersten Katalysatorsubstanz im Sinne der beigefügten Ansprüche, beschichtet, die ebenso wenig zeichnerisch dargestellt werden konnte wie die sehr kleinen Filteröffnungen in den Kanalwänden 24. Auch die erste Katalysatorsubstanz kann als katalytisch wirksame Bestandteile typischerweise ein Edelmetall, wie Platin, enthalten.The catalyst substance used in the oxidation catalyst section 14 is the second catalyst substance as defined in the appended claims and typically contains a noble metal such as platinum or palladium as catalytically active ingredients, but optionally also an oxide or rare earth oxides such as Ce. In the filter section 16 of the monolithic ceramic body 10 exhaust channels 20 and 22 are formed, which are closed at one end of each channel by a closure 20a and 22a, and indeed the exhaust channels 20 are all open upstream and downstream, the exhaust channels 22 are closed upstream and downstream open, and located in the ceramic body 10 (viewed in a section perpendicular to the flow direction) each exhaust passage 20 between the exhaust passages 22 and each exhaust passage 22 between exhaust channels 20. Looking from the closures 20a and 22a, the exhaust passages 20 and 22 through channel walls 24, which are porous and have defined filter openings, and also limited in part by the gas-impermeable outer wall 12. The inside of the outer wall 12 and the surfaces of the channel walls 24 and / or the walls of their filter openings are also coated with a catalyst substance, namely the first catalyst substance in the sense of the appended claims, which could not be represented graphically as the very small filter openings in the Channel walls 24. Also, the first catalyst substance may contain as catalytically active components typically a noble metal, such as platinum.
Wie die Zeichnung erkennen lässt, ist bei der dargestellten Ausführungsform die Anzahl der Abgasdurchströmkanäle 18 wesentlich größer als die Anzahl der Abgaskanäle 20 und 22; ferner sind die Verschlüsse 22a der Kanalwände 24 des Filterabschnitts 16 mit Kanalwänden 18a des Oxidationskatalysator- abschnitts 14 verbunden, und zwar insbesondere einstückig, was sich mit dem geschilderten Herstellungsverfahren ohne Weiteres bewerkstelligen lässt.As the drawing reveals, in the illustrated embodiment, the number of Abgasdurchströmkanäle 18 is substantially greater than the number of exhaust passages 20 and 22; Furthermore, the closures 22a of the channel walls 24 of the filter section 16 are connected to channel walls 18a of the oxidation catalytic converter section 14, in particular in one piece, which can easily be achieved with the described production method.
Nur der Vollständigkeit halber sei noch darauf hingewiesen, dass die Verschlüsse 20a und 22a porös oder gasdicht sein können - vor allem im zuletzt erwähnten Fall ergibt sich im Filterabschnitt 16 der in der Zeichnung durch Pfeile angedeutete Strömungsverlauf der Abgase.For the sake of completeness, it should be pointed out that the closures 20a and 22a can be porous or gas-tight - especially in the last-mentioned case, the flow profile of the exhaust gases indicated in the drawing by the arrows in the filter section 16.
Typischerweise beträgt bei Abgasdurchströmkanälen 18 und Abgaskanälen 20 bzw. 22 mit kreisförmigem Querschnitt der Kanaldurchmesser ca. 1,5 mm oder weniger, und die Wandstärke der Kanalwände 18a und 24, gegebenenfalls auch die Wandstärke der Außenwand 12, liegt vorzugsweise im Bereich zwischen ca. 0,15 mm und ca. 0,35 mm und beträgt insbesondere ca. 0,25 mm.In the case of exhaust gas throughflow channels 18 and exhaust ducts 20 or 22 with a circular cross section, the channel diameter is typically about 1.5 mm or less, and the wall thickness of the channel walls 18a and 24, optionally also the wall thickness of the outer wall 12, is preferably in the range between about 0.15 mm and about 0.35 mm and is in particular about 0.25 mm.
Wenn der zu sinternde Rohling des monolithischen Keramikkörpers 10, wie vorstehend beschrieben wurde, schichtweise erzeugt wird, haben die Schichten typischerweise eine Dicke von ca. 40 μm.When the blank to be sintered of the monolithic ceramic body 10 is formed in layers as described above, the layers typically have a thickness of about 40 μm.
Die in das erfindungsgemäße Dieselpartikelfilter-Bauteil gemäß der Zeichnung von links einströmenden Abgase, welche unverbrannte Kohlenwasserstoffe und gegebenenfalls Kohlenmonoxid und andere aufoxidierbare Bestandteile enthalten, werden im Oxidationskatalysatorabschnitt 14 in vom Motorbetrieb abhängigen zeitlichen Intervallen auf Temperaturen von mehr als 6000C, insbesondere auf Temperaturen zwischen ca. 650 und ca. 8000C, aufgeheizt, und zwar infolge der im Oxidationskatalysatorabschnitt 14 dann stattfindenden Verbrennung der Kohlenwasserstoffe sowie gegebenenfalls der Aufoxidation anderer Abgasbestandteile. Normalerweise strömen die Abgase in die Abgaskanäle 20 des Filterabschnitts 16 ein, durchqueren die porösen Kanalwände 24, wobei Dieselrußpartikel aus den Abgasströmen herausgefiltert und in den Kanalwänden zurückgehalten werden, und verlassen dann den Filterabschnitt 16 über die offenen abströmseitigen Enden der Abgaskanäle 22. Infolge der bei einer Filterregeneration hohen Temperaturen der in den Filterabschnitt 16 einströmenden Abgase sowie der im Filterabschnitt 16 verwendeten Katalysatorsubstanz werden die in den Kanalwänden 24 zurückgehaltenen Rußpartikel in Intervallen immer dann verbrannt, d. h. in CO2 und H2O umgewandelt, wenn die den Motor verlassenden Abgase durch eine der vorstehend beschriebenen Maßnahmen unverbrannte Kohlenwasserstoffe enthalten.In the inventive diesel particulate filter component according to the drawing from the inflowing exhaust gases containing unburned hydrocarbons and optionally carbon monoxide and other aufoxidierbare constituents are in the oxidation catalyst section 14 in engine-dependent time intervals to temperatures of more than 600 0 C, in particular to temperatures between about 650 and about 800 0 C, heated, due to the then taking place in the oxidation catalyst section 14 combustion of the hydrocarbons and optionally the oxidation of other exhaust gas constituents. Normally, the exhaust gases flow into the exhaust passages 20 of the filter section 16, traversing the porous passage walls 24, filtering out particulate matter from the exhaust flows and retaining them in the passage walls, and then leaving the filter section 16 via the open downstream ends of the exhaust passages 22. *** " a filter regeneration high temperatures of the exhaust gases flowing into the filter section 16 and the catalyst substance used in the filter section 16, the soot particles retained in the channel walls 24 are always burned at intervals, ie converted into CO 2 and H 2 O, if the exhaust gases leaving the engine by a the measures described above contain unburned hydrocarbons.
Die Wandstärke der Kanalwände im Filterabschnitt und die Wandstärke der Kanalwände im Oxidationskatalysatorabschnitt können ungefähr gleich, aber auch unterschiedlich sein, und dasselbe gilt für die Querschnittsformen der Abgaskanäle des Oxidationskatalysatorabschnitts und des Filterabschnitts. Damit sich ein wirklich monolithischer Keramikkörper ergibt, wird bei der Herstellung des nachfolgend zu sinternden Rohlings für den den Oxidationskataly- satorabschnitt und den Filterabschnitt umfassenden Keramikkörper ein und dasselbe keramische Grundmaterial verwendet, welches als keramische Substanz insbesondere Siliziumkarbid enthält. Für den Oxidationskatalysator- abschnitt kann jedoch eine keramische Substanz anderer Korngröße verwendet werden als für den Filterabschnitt, um so zu erreichen, dass der gesinterte Keramikkörper im einen Abschnitt eine andere Porosität aufweist als im anderen Abschnitt - während im Filterabschnitt eine hohe offene Porosität und kleine Poren zur effektiven Filtration bei geringem Strömungsgegendruck führen, haben diese Parameter auf die Leistungsfähigkeit des Oxidations- katalysatorabschnitts wenig Einfluss; im Oxidationskatalysatorabschnitt soll die Summe der katalytisch wirksamen Oberflächen möglichst groß sein, was sich auch mit einer geringen Porosität der Kanalwände und einer anderen Korngrößenverteilung als im Filterabschnitt erreichen lässt.The wall thickness of the channel walls in the filter section and the wall thickness of the channel walls in the oxidation catalyst section may be approximately the same, but also different, and the same applies to the cross-sectional shapes of the exhaust channels of the oxidation catalyst section and the filter section. In order to produce a truly monolithic ceramic body, in the production of the blank to be subsequently sintered, one and the same ceramic base material is used for the ceramic body comprising the oxidation catalyst section and the filter section, which contains in particular silicon carbide as the ceramic substance. For the oxidation catalyst section, however, a ceramic substance of a different grain size can be used than for the filter section, so that the sintered ceramic body has a different porosity in one section than in the other section - while in the filter section a high open porosity and small pores result in effective filtration with low back pressure, these parameters have little effect on the performance of the oxidation catalyst section; In the oxidation catalyst section, the sum of the catalytically active surfaces should be as large as possible, which can also be achieved with a low porosity of the channel walls and a different particle size distribution than in the filter section.
Wie die Zeichnung erkennen lässt, benötigt man für die schichtweise Herstellung des zu sinternden Rohlings des monolithischen Keramikkörpers im Siebdruckverfahren nur fünf verschiedene Siebe, da es bei dem dargestellten Keramikkörper insgesamt nur fünf verschiedene Querschnittskonfigurationen gibt. As can be seen from the drawing, only five different sieves are required for the layer-by-layer production of the blank of the monolithic ceramic body to be sintered, since there are only five different cross-sectional configurations in the illustrated ceramic body.

Claims

PATENTANSPRÜCHE
1. Dieselpartikelfilter-Bauteil mit einem von Dieselmotor-Abgasen zu durchströmenden keramischen Formkörper, in welchem von Kanalwänden begrenzte Abgaskanäle ausgebildet sind und welcher einen Filterabschnitt sowie stromaufwärts des Filterabschnitts einen Oxidations- katalysatorabschnitt aufweist, wobei diese beiden Abschnitte einen länglichen monolithischen Keramikkörper mit einem Abgas-Einlassende und einem Abgas-Auslassende bilden, der Oxidationskatalysatorabschnitt sich in Längsrichtung des Keramikkörpers erstreckende, an ihren Enden offene Abgasdurchströmkanäle und der Filterabschnitt sich in Längsrichtung des Keramikkörpers erstreckende Kanalwände mit definierten Filteröffnungen sowie einander benachbarte Abgaskanäle abwechselnd im Bereich des einen bzw. im Bereich des anderen Kanalendes verschließende Verschlüsse aufweist, die Kanalwände des Filterabschnitts mindestens bereichsweise mit einer eine Reduzierung der Verbrennungstemperatur der vom Filter zurückgehaltenen Dieselrußpartikel bewirkenden ersten Katalysatorsubstanz und die Kanalwände des Oxidationskatalysatorabschnitts mindestens bereichsweise mit einer eine Oxidation von Kohlenwasserstoffen bewirkenden zweiten Katalysatorsubstanz versehen sind, dadurch gekennzeichnet, dass pro Längeneinheit des Keramikkörpers die von den Kanalwänden des Oxidationskatalysatorabschnitts gebildete Kanalwandfläche größer ist als die von den Kanalwänden des Filterabschnitts gebildete Kanalwandfläche.A diesel particulate filter component having a ceramic shaped body to be flowed through by diesel engine exhaust gases, in which exhaust ducts are formed by channel walls and which has a filter section and an oxidation catalyst section upstream of the filter section, these two sections comprising an elongated monolithic ceramic body with an exhaust gas The inlet end and an exhaust outlet end form the oxidation catalyst section extending in the longitudinal direction of the ceramic body, open at its ends Abgasdurchströmkanäle and the filter section extending in the longitudinal direction of the ceramic body channel walls with defined filter openings and adjacent exhaust channels alternately in the region of one and in the other Has channeling occlusive closures, the channel walls of the filter section at least partially zurückge with a reduction in the combustion temperature of the filter zurückge characterized in that at least partially provided with an oxidation of hydrocarbons causing second catalyst substance, characterized in that per unit length of the ceramic body, the channel wall formed by the channel walls of the oxidation catalyst section is greater than that formed by the channel walls of the filter section channel wall surface.
2. Dieselpartikelfilter-Bauteil nach Anspruch 1, dadurch gekennzeichnet, dass die Anzahl der Abgasdurchströmkanäle des Oxidationskatalysator- abschnitts größer ist als die Anzahl der Abgaskanäle des Filterabschnitts. 2. diesel particulate filter component according to claim 1, characterized in that the number of Abgasdurchströmkanäle the Oxidationskatalysator- section is greater than the number of exhaust passages of the filter section.
3. Dieselpartikelfilter-Bauteil nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass die Anzahl der Abgasdurchströmkanäle des Oxidationskatalysatorabschnitts dividiert durch die Querschnittsfläche des Oxidationskatalysatorabschnitts größer ist als die Anzahl der Abgaskanäle des Filterabschnitts dividiert durch die Querschnittsfläche des Filterabschnitts.3. The diesel particulate filter component according to claim 1 or 2, characterized in that the number of Abgasdurchströmkanäle the Oxidationskatalysatorabschnitts divided by the cross-sectional area of the Oxidationskatalysatorabschnitts is greater than the number of exhaust passages of the filter section divided by the cross-sectional area of the filter section.
4. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass am Abgas-Einlassende des Keramikkörpers die Summe der Querschnittsflächen seiner Abgasdurchströmkanäle ungefähr gleich groß ist wie die Summe der Querschnittsflächen der Abgaskanäle des Filterabschnitts an dessen anströmseitigen Ende.4. diesel particulate filter component according to one of claims 1 to 3, characterized in that the exhaust inlet end of the ceramic body, the sum of the cross-sectional areas of its Abgasdurchströmkanäle is about the same size as the sum of the cross-sectional areas of the exhaust ducts of the filter section at its upstream end.
5. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, dass die Verschlüsse der Abgaskanäle des Filterabschnitts einstückig und ohne Grenzflächen in die Kanalwände des Filterabschnitts übergehen.5. Diesel particulate filter component according to one of claims 1 to 4, characterized in that the closures of the exhaust ducts of the filter section merge integrally and without interfaces in the channel walls of the filter section.
6. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das keramische Grundmaterial aller Kanalwände des Keramikkörpers dasselbe ist.6. diesel particulate filter component according to one of claims 1 to 5, characterized in that the ceramic base material of all the channel walls of the ceramic body is the same.
7. Dieselpartikelfilter-Bauteil nach Anspruch 6, dadurch gekennzeichnet, dass das keramische Grundmaterial Siliziumkarbid ist.7. diesel particulate filter component according to claim 6, characterized in that the ceramic base material is silicon carbide.
8. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass Kanalwände des Oxidationskatalysatorabschnitts mit Kanalwänden und/oder Verschlüssen des Filterabschnitts verbunden sind. 8. Diesel particle filter component according to one of claims 1 to 7, characterized in that channel walls of the oxidation catalyst section are connected to channel walls and / or closures of the filter section.
9. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 8, dadurch gekennzeichnet, dass die Kanalwände des Oxidationskatalysator- abschnitts eine kleinere Porosität als die Kanalwände des Filterabschnitts aufweisen oder gasdicht sind.9. diesel particulate filter component according to one of claims 1 to 8, characterized in that the channel walls of the Oxidationskatalysator- section have a smaller porosity than the channel walls of the filter section or are gas-tight.
10. Dieselpartikelfilter-Bauteil nach einem der Ansprüche 1 bis 9, dadurch gekennzeichnet, dass die zweite Katalysatorsubstanz eine auch eine Oxi- dation von Kohlenmonoxid bewirkende Katalysatorsubstanz ist.10. Diesel particle filter component according to one of claims 1 to 9, characterized in that the second catalyst substance is also a oxidation of carbon monoxide effecting catalyst substance.
11. Verfahren zur Herstellung eines Dieselpartikelfilter-Bauteils nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass ein Rohling des Keramikkörpers durch in dessen Längsrichtung aufeinanderfolgende Schichten durch wiederholte Abfolge der folgenden Schritte aufgebaut wird:11. A method for producing a diesel particulate filter component according to any one of the preceding claims, characterized in that a blank of the ceramic body is constructed by successive layers in the longitudinal direction by repeated succession of the following steps:
(a) Erzeugung einer einem dem jeweiligen Querschnitt des Keramikkörpers entsprechend gestalteten Schicht aus einer formbaren, verfestigbaren keramischen Masse und(A) producing a one of the respective cross section of the ceramic body designed according layer of a moldable, solidifiable ceramic mass and
(b) Verfestigung dieser Schicht,(b) solidification of this layer,
worauf der so erzeugte Rohling gesintert wird.whereupon the blank thus produced is sintered.
12. Verfahren nach Anspruch 11, dadurch gekennzeichnet, dass die Schichten im Siebdruckverfahren erzeugt werden.12. The method according to claim 11, characterized in that the layers are produced by screen printing.
13. Verfahren nach Anspruch 11 oder 12, dadurch gekennzeichnet, dass die Schichten durch Trocknen verfestigt werden. 13. The method according to claim 11 or 12, characterized in that the layers are solidified by drying.
PCT/EP2008/001997 2007-03-16 2008-03-13 Diesel particulate filter component WO2008113507A1 (en)