WO2008075639A1 - プレフィルドシリンジ - Google Patents
プレフィルドシリンジ Download PDFInfo
- Publication number
- WO2008075639A1 WO2008075639A1 PCT/JP2007/074215 JP2007074215W WO2008075639A1 WO 2008075639 A1 WO2008075639 A1 WO 2008075639A1 JP 2007074215 W JP2007074215 W JP 2007074215W WO 2008075639 A1 WO2008075639 A1 WO 2008075639A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyester resin
- dicarboxylic acid
- prefilled syringe
- diol
- unit
- Prior art date
Abstract
高耐熱性、低吸着性、低透湿性、低酸素透過性のプレフィルドシリンジを提供する。
少なくともバレル及び接合部のそれぞれを構成する樹脂が、ジオール単位中の1~30モル%が環状アセタール骨格を有するジオール単位であり、ジカルボン酸単位中の70モル%以上がナフタレン骨格を有するジカルボン酸単位であり、下記式(i)~(iii)をいずれも満たすポリエステル樹脂を含むプレフィルドシリンジ。
(i)示差走査熱量計で測定したガラス転移温度が110°C以上
(ii)透湿係数が1g・mm/m2/日以下
(iii)酸素透過係数が10cc・mm/m2/日/atm以下
Description
技術分野
[0001] 本発明は、予め薬液を密封状態で充填した注射容器 (プレフィルドシリンジ)に関す るものである。
背景技術
[0002] 注射容器の素材としては従来ガラスが使用されてきた。し力、しながら、ガラスは落と すと割れてしまうことがあり、ポリカーボネート、ポリエチレン、ポリプロピレン、シクロォ レフインポリマー等、プラスチックへの代替が進んで!/、る。
一方、注射容器の使用方法では空の注射容器に使用時に薬液を吸!/、上げる方法 が従来行われていた。し力、しながら、この方法では操作効率が悪ぐ薬液の充填ミス などヒューマンエラーが発生することが問題となっており、予め所定の薬液を所定量 充填したプレフィルドシリンジへの移行が進んでいる。
プレフィルドシリンジの素材としては前述の理由からプラスチックが好ましいものの、 プラスチック特有の水蒸気透過性 (透湿性)、酸素透過性、吸着性により使用に制限 があり、代替が進んでいないのが現状である。
例えば、ポリカーボネートの注射容器ではその透湿性の為に薬剤の水分が揮発し てしまう問題があり、ポリプロピレンゃシクロォレフィンポリマーの注射容器では、その 酸素透過性の為に薬液が酸化してしまったり、その吸着性の為に特定の薬剤の成分 が薄くなつてしまうという問題がある。
ポリエステル樹脂は酸素透過性、吸着性が小さいことが知られている。ポリエチレン ナフタレートは低透湿性も兼ね備えている力 その結晶性の為に煮沸消毒時に一部 結晶化することで寸法変化が生じシリンジとして機能しな!/、。ポリエステル樹脂で煮 沸消毒に耐える耐熱性と低透湿性を兼ね備えたものは知られて!/、なレ、。
特許文献 1にはガスケットにブチルゴムを用いた低吸着性の合成樹脂製プレフイノレ ドシリンジが開示されている力 十分な高耐熱性、低吸着性、低透湿性、低酸素透過 1·生を有していない。
[0003] 特許文献 1 :特開 2004— 298220号広報
発明の開示
発明が解決しょうとする課題
課題を解決するための手段
[0005] 本発明は、少なくともバレル及び接合部のそれぞれを構成する樹脂が、ジオール 単位中の 1〜30モル%が環状ァセタール骨格を有するジオール単位であり、ジカル ボン酸単位中の 70モル%以上がナフタレン骨格を有するジカルボン酸単位であり、 下記式 (i)〜(iii)を!/、ずれも満たすポリエステル樹脂を含むプレフィルドシリンジに関 するものである。
ω示差走査熱量計で測定したガラス転移温度が 1 io°c以上
(ii)透、湿係数が lg 'mm m /日以下
(iii)酸素透過係数が 1 Occ · mm/m2/日 /atm以下
発明の効果
[0006] 本発明のプレフィルドシリンジは、高耐熱性、低透湿性、低酸素透過性、低吸着性 であり、従来のプラスチック製プレフィルドシリンジに比べ、長期保存性が格段に向上 する。
発明を実施するための最良の形態
[0007] 以下、本発明を詳細に説明する。
本発明のプレフィルドシリンジは、少なくともバレル及び接合部のそれぞれ力 ジォ ール単位中の 1〜30モル%が環状ァセタール骨格を有するジオール単位であり、ジ カルボン酸単位中の 70モル%以上がナフタレン骨格を有するジカルボン酸単位で あるポリエステル樹脂を含む樹脂で構成される。
[0008] [ポリエステル樹脂]
本発明に用いるポリエステル樹脂中の環状ァセタール骨格を有するジオール単位 の割合は 1〜30モル%である。環状ァセタール骨格を有するジオール単位を 1モル
%以上含むことにより、ポリエステル樹脂のガラス転移温度の上昇が達成され、当該 ポリエステル樹脂は耐熱性が向上する。加えて、結晶性が低下し煮沸消毒時の一部 結晶化、それに伴う寸法変化、白化、脆化が起こらない。環状ァセタール骨格を有す るジオール単位の好ましい割合は 3モル%以上であり、より好ましくは 5モル%以上で ある。一方、ポリエステル樹脂中の環状ァセタール骨格を有するジオール単位の割 合が 30モル%を超えるとポリエステル樹脂の透湿性、酸素透過性が増加し、好ましく なレ、ことがある。環状ァセタール骨格を有するジオール単位の好まし!/、割合は 25モ ル%以下であり、より好ましくは 22モル0 /0以下、より好ましくは 20モル0 /0以下、更に 好ましくは 15モル%以下である。従って、環状ァセタール骨格を有するジオール単 位の割合は、ポリエステル樹脂の耐熱性、透湿性の面から 1〜25モル%とするのが 好ましぐ 3〜25モル%とするのがより好ましぐ 5〜22モル%とするのが更に好まし い。
[0009] 本発明に使用するポリエステル樹脂のジオール構成単位中の環状ァセタール骨格 を有するジオール単位としては一般式(1):
[0010] または一般式
[0011] で表される化合物に由来する単位が好ましい。一般式(1)と(2)において、 R1および R2はそれぞれ独立して、炭素数が;!〜 10の脂肪族炭化水素基、炭素数が 3〜; 10の 脂環式炭化水素基、及び炭素数が 6〜; 10の芳香族炭化水素基からなる群から選ば れる炭化水素基を表す。 R1および R2は、各々メチレン基、エチレン基、プロピレン基、 基、又はこれらの構造異性体が好ましい。これらの構造異性体としては、例
えば、イソプロピレン基、イソブチレン基が例示される。 R3は炭素数が 1〜; 10の脂肪 族炭化水素基、炭素数が 3〜; 10の脂環式炭化水素基、及び炭素数が 6〜; 10の芳香 族炭化水素基からなる群から選ばれる炭化水素基を表す。 R3は、メチル基、ェチル 基、プロピル基、ブチル基、又はこれらの構造異性体が好ましい。これらの構造異性 体としては、例えば、イソプロピル基、イソブチル基が例示される。一般式(1)及び(2 )の各々の化合物としては、 3, 9 ビス(1 , 1 ジメチルー 2 ヒドロキシェチル)ー2 , 4, 8, 10 テトラオキサスピロ〔5· 5〕ゥンデカン、 5 メチロール一 5 ェチル 2 ー(1 , 1 ジメチルー 2 ヒドロキシェチル) 1 , 3 ジォキサン等が特に好ましい。 上記環状ァセタール骨格を有するジオール単位は 1種類から構成されても、 2種類 以上から構成されてもよい。
また、環状ァセタール骨格を有するジオール単位以外のジオール構成単位として は、特に制限はされないが、エチレングリコール、トリメチレングリコール、 1 , 4—ブタ ンジオール、 1 , 5—ペンタンジオール、 1 , 6—へキサンジオール、ジエチレングリコ ール、プロピレングリコール、ネオペンチルダリコール等の脂肪族ジオール類; 1 , 3— シクロへキサンジメタノーノレ、 1 , 4ーシクロへキサンジメタノーノレ、 1 , 2 デカヒドロナ タレンジメタノール、 1 , 5—デカヒドロナフタレンジメタノール、 1 , 6—デカヒドロナフタ レンジメタノール、 2, 7 デカヒドロナフタレンジメタノール、テトラリンジメタノール、ノ ール等の脂環式ジオール類;ポリエチレングリコール、ポリプロピレングリコール、ポリ ブチレングリコール等のポリエーテル化合物類; 4, 4'一(1ーメチルェチリデン)ビス フエノーノレ、メチレンビスフエノール(ビスフエノール F)、 4, 4'—シクロへキシリデンビ スフエノール(ビスフエノール Z)、 4, 4'—スルホニルビスフエノール(ビスフエノール S )等のビスフエノール類;前記ビスフエノール類のアルキレンォキシド付加物;ヒドロキ ノン、レゾルシン、 4, 4'ージヒドロキシビフエニル、 4, 4'ージヒドロキシジフエニルェ 一テル、 4, 4'ージヒドロキシジフエニルベンゾフエノン等の芳香族ジヒドロキシ化合物 ;及び前記芳香族ジヒドロキシ化合物のアルキレンォキシド付加物等に由来するジォ ール単位が例示できる。ポリエステル樹脂の機械強度、耐熱性、及びジオールの入
手の容易さを考慮するとエチレングリコール、トリメチレングリコール、 1 , 4 ブタンジ オール、 1 , 4ーシクロへキサンジメタノール等に由来するジオール単位が好ましぐ エチレングリコール単位が特に好ましい。上記環状ァセタール骨格を有するジォー ル単位以外のジオール構成単位は 1種類から構成されても、 2種類以上から構成さ れてもよい。
[0013] 一方、本発明に用いるポリエステル樹脂中のナフタレン骨格を有するジカルボン酸 単位の割合は 70モル%以上である。ナフタレン骨格を有するジカルボン酸単位を 70 モル%以上含むことにより、ポリエステル樹脂のガラス転移温度の上昇、すなわち耐 熱性の向上と、透湿係数の低下、酸素透過係数の低下が同時に達成される。一方、 ポリエステル樹脂中のナフタレン骨格を有するジカルボン酸単位の割合が 70モル% 未満であるとポリエステル樹脂の透湿係数、酸素透過係数が増加し、耐熱性が低下 すこととなり、好ましくない場合がある。従って、ナフタレン骨格を有するジカルボン酸 単位の割合は、ポリエステル樹脂の耐熱性、透湿性、酸素透過性の面から 85モル% 以上とするのが好ましぐ 95モル%以上とするのがより好ましい。
[0014] 本発明に用いるポリエステル樹脂中のナフタレン骨格を有するジカルボン酸構成 単位としては、 1 , 3—ナフタレンジカルボン酸、 1 , 4 ナフタレンジカルボン酸、 1 , 5 —ナフタレンジカルボン酸、 2, 6 ナフタレンジカルボン酸、 2, 7 ナフタレンジ力ノレ ボン酸等に由来する単位が例示できる。ポリエステル樹脂中のナフタレン骨格を有す るジカルボン酸単位は 1種類から構成されても、 2種類以上から構成されても良い。 耐熱性、低透湿性の面から上記した中では 2, 6 ナフタレンジカルボン酸に由来す る単位が最も好ましい。
[0015] 本発明に用いるポリエステル樹脂のナフタレン骨格を有するジカルボン酸単位以 外のジカルボン酸単位としては、特に制限はされないが、コハク酸、ダルタル酸、アジ ピン酸、ピメリン酸、スベリン酸、ァゼライン酸、セバシン酸、デカンジカルボン酸、ドデ カンジカルボン酸、シクロへキサンジカルボン酸、デカリンジカルボン酸、ノルボルナ
3, 9 ビス(1 , 1 ジメチルー 2 カルボキシェチル) 2, 4, 8, 10 テトラォキサ スピロ〔5. 5〕ゥンデカン、 5 カルボキシー5 ェチルー 2—(1 , 1 ジメチルー 2—
カルボキシェチル) 1, 3—ジォキサン、ダイマー酸等の脂肪族ジカルボン酸に由 来する単位;テレフタル酸、イソフタル酸、フタル酸、 2—メチルテレフタル酸、ビフエ ニルジカルボン酸、テトラリンジカルボン酸等の芳香族ジカルボン酸に由来する単位 が例示できる。ポリエステル樹脂の機械強度、耐熱性を考慮すると芳香族ジカルボン 酸に由来する単位が好ましく、ジカルボン酸の入手の容易さを考慮するとテレフタル 酸、又はイソフタル酸に由来する単位が特に好ましい。なお、ポリエステル樹脂のナ フタレン骨格を有するジカルボン酸以外のジカルボン酸構成単位は 1種類から構成 されても、 2種類以上から構成されても良い。
[0016] ポリエステル樹脂には、溶融粘弾性や分子量などを調整するために、本発明の目 的を損なわない範囲でブチルアルコール、へキシルアルコール、ォクチルアルコー ルなどのモノアルコールに由来する単位やトリメチロールプロパン、グリセリン、 1, 3, 5—ペンタントリオール、ペンタエリスリトールなどの 3価以上の多価アルコールに由 来する単位、安息香酸、プロピオン酸、酪酸などのモノカルボン酸に由来する単位、 トリメリット酸、ピロメリット酸などの多価カルボン酸に由来する単位、グリコール酸、乳 酸、ヒドロキシ酪酸、 2—ヒドロキシイソ酪酸、ヒドロキシ安息香酸などのォキシ酸に由 来する単位を含んでもよい。
[0017] 本発明に用いるポリエステル樹脂は、特に高耐熱性、低透湿性、低酸素透過性、 機械的性能などを考慮すると,環状ァセタール骨格を有するジオール単位が 3, 9— ビス(1, 1ージメチノレー 2 ヒドロキシェチノレ) 2, 4, 8, 10 テトラオキサスピロ〔5· 5〕ゥンデカンに由来する単位であり、環状ァセタール骨格を有するジオール単位以 外のジオール構成単位がエチレングリコールに由来する単位であり、ジカルボン酸 構成単位の全てが 2, 6 ナフタレンジカルボン酸に由来する単位であることが好まし い。
[0018] 本発明に用いるポリエステル樹脂は、下記式 (i)〜(iii)をいずれも満たすも
のである。
ω示差走査熱量計で測定したガラス転移温度が 1 io°c以上
(ii)透、湿係数が lg 'mm m /日以下
(iii)酸素透過係数が 1 Occ · mm/m2/日 /atm以下
上述の通り、本発明に用いるポリエステル樹脂のガラス転移温度は、示差走査熱量 計で測定した値が 110°C以上であり、好ましくは 115°C以上、より好ましくは 120°C以 上である。ポリエステル樹脂のガラス転移温度が上記範囲にある場合、本発明のプレ フィルドシリンジは煮沸消毒が可能となる。なお、ポリエステル樹脂のガラス転移温度 は前述したように環状ァセタール骨格を有するジオール、及びナフタレン骨格を有す るジカルボン酸を適宜選択することで上記範囲内の値とすることができる。なお、ガラ ス転移温度の上限値は、特に制限はないが、ポリエステル樹脂の構成単位の種類、 その組成を考慮すると、通常 160°Cである。
[0019] 本発明に用いるポリエステル樹脂の透湿係数は 40°C、 90%RHの条件下で lg'm m/m2/日以下であり、好ましくは 0. 9g'mm/m2/日以下、より好ましくは 0. 8g- mm/m2/日以下である。ポリエステル樹脂の透湿係数が上記範囲にある場合、本 発明のプレフィルドシリンジは薬液の長期保存が可能となる。なお、ポリエステル樹脂 の透湿係数は前述したように環状ァセタール骨格を有するジオール、及びナフタレ ン骨格を有するジカルボン酸を適宜選択することで上記範囲内の値とすることができ
[0020] 本発明に用いるポリエステル樹脂の酸素透過係数は 23°C、 65%RHの条件下で 1 Occ 'mm m 日 z atm以! "であり、好まし < ま 7cc 'mmz m 日 atmw下、よ り好ましくは 5cc ' mm/m2/日 /atm以下である。ポリエステル樹脂の酸素透過係 数が上記範囲にあることで薬液の酸化劣化を防ぎ、保存安定性を向上することがで きる。ポリエステル樹脂の酸素透過係数は前述したように環状ァセタール骨格を有す るジオール、及びナフタレン骨格を有するジカルボン酸を適宜選択することで上記範 囲内の値とすることができる。
[0021] 本発明に用いるポリエステル樹脂は他のポリエステル樹脂同様に低吸着性である。
例えばビタミン Dゃリモネンは実質的に吸着しない。
本発明に用いるポリエステル樹脂の極限粘度(IV)は成形方法や用途に応じて適 宜選択することができ、フエノールと 1 , 1 , 2, 2—テトラクロロェタンとの質量比 6 : 4の 混合溶媒を用いた 25°Cでの測定値で 0. 5〜; 1. 5dl/gの範囲であることが好ましぐ より好ましく (ま 0. 5~1. 2dl/gであり、更 ίこ好ましく (ま 0. 5~1. Odl/gである。極限
粘度がこの範囲にある場合、本発明に用いるポリエステル樹脂は成形性及び機械的 性能のバランスに優れる。
[0022] 本発明に用いるポリエステル樹脂を製造する方法は特に制限はなぐ従来公知の ポリエステルの製造方法をいずれも適用することができる。例えばエステル交換法、 直接エステル化法等の溶融重合法、又は溶液重合法等を挙げる事ができる。直接ェ ステル化法にお!/、ては、ジカルボン酸を環状ァセタール骨格を有しな!/、ジオールで エステル化した後、低酸価化してから環状ァセタール骨格を有するジオールを反応 させること力 S必要な場合もある。上記したポリエステル樹脂の製造方法の中で、原料 入手の容易さの点から、エステル交換法が好まし!/、。
[0023] ポリエステル樹脂の製造時に用いるエステル交換触媒、エステル化触媒、重縮合 触媒等の各種触媒、エーテル化防止剤、熱安定剤、光安定剤等の各種安定剤、重 合調整剤等も従来公知のものをいずれも用いることができ、これらは反応速度やポリ エステル樹脂の色調、安全性、熱安定性、耐候性、自身の溶出性などに応じて適宜 選択される。例えば上記各種触媒としては、亜鉛、鉛、セリウム、カドミウム、マンガン 、コバルト、リチウム、ナトリウム、カリウム、カルシウム、ニッケル、マグネシウム、バナジ ゥム、アルミニウム、チタン、アンチモン、スズ等の金属の化合物(例えば、脂肪酸塩、 炭酸塩、リン酸塩、水酸化物、塩化物、酸化物、アルコキシド)や金属マグネシウムな どが挙げられ、これらは単独で用いることもできるし、複数のものを組み合わせて用い ることもできる。エステル交換法におけるエステル交換触媒としては、活性が高ぐ副 反応が少ないことから、上記した中でマンガンの化合物が好ましぐ重縮合触媒とし ては上記した中でアンチモン、チタンの化合物が好ましい。
[0024] 本発明に用いるポリエステル樹脂には、酸化防止剤、光安定剤、紫外線吸収剤、 可塑剤、増量剤、艷消し剤、乾燥調節剤、帯電防止剤、沈降防止剤、界面活性剤、 流れ改良剤、乾燥油、ワックス類、フィラー、着色剤、補強剤、表面平滑剤、レベリン グ剤、硬化反応促進剤、増粘剤などの各種添加剤、成形助剤を添加することができ
[0025] 次いで、本発明のプレフィルドシリンジについて述べる。
本発明のプレフィルドシリンジは射出成形法にて製造される。本発明のプレフィルド
シリンジは一般的な注射容器となんら変わるものではなぐ少なくとも薬液を充填する 為のバレル、バレルの一端に注射針を接合する為の接合部及び使用時に薬液を押 出す為のプランジャーから構成され、少なくともバレル及び接合部は本発明で用いら れる前記ポリエステル樹脂を含む樹脂から成形される必要がある。
ポリエステル樹脂を含む樹脂には、本発明の効果の点から、前記ポリエステル樹脂 を、 60質量%以上含有することが好ましぐより好ましくは 80質量%以上、特に好ま しくは 100質量%含有する。ポリエステル樹脂以外の樹脂としては、例えば、ポリプロ ピレン、ポリエチレン、ポリカーボネート、シクロォレフインポリマー等を含有することが できる。
[0026] 本発明のプレフィルドシリンジにおいては、バレルと接合部は一体のものとして成形 しても良いし、別々に成形した物を接合しても良い。接合部の先端は封をする必要が ある力 その方法は接合部先端の樹脂を溶融状態に加熱、ペンチ等で挟み込んで 融着させる等すればよい。
[0027] 本発明のプレフィルドシリンジはプランジャーとバレルとの密着性を増す為にパツキ ンを用いても良レ、。パッキンとしては本発明に用レ、るポリエステル樹脂を使用しても良 いが、ゴム弾性材料の方が好ましぐブチルゴム、イソプレンゴム、熱可塑性エラスト マー等を挙げることができる。パッキン等の使用によりプランジャーと内容物が接しな い場合は、プランジャーに使用しうる樹脂としては本発明のポリエステル樹脂の他に ポリプロピレン、ポリエチレン、ポリカーボネート、シクロォレフインポリマー等を例示す ることができる力 プランジャーと内容物が接触する場合にはプランジャーは本発明 で用いるポリエステル樹脂を使用することが好ましレ、。
本発明のプレフィルドシリンジはガラス製注射容器以上の十分な耐衝撃性を有する
[0028] 本発明のプレフィルドシリンジの充填物としては特に制限はないが、本発明の効果 の点から、例えば脂溶性の化合物が好ましぐその化合物の有用性の面からテルぺ ン類、タンパク質等が好ましく挙げられる。より具体的にはテルペン類としては、ビタミ ン k ビタミン D、ビタミン E、ビタミン Kなどの脂溶性ビタミン、リモネン、メントール、ミ ノレセン、オシメン、コスメン等のモノテルペン、フアルネソーノレ、ネロリドーノレ、 β -シネ
ンサール、カリオフィレン等のセスキテルペン、ジテルペン、セスタテルペン、トリテノレ ペン、テトラテルペン等が好ましく挙げられる。タンパク質としては卵アルブミン、血清 アルブミン、乳アルブミン等のアルブミン等が挙げられる。ペプチド結合を有する化合 物で修飾されたテルペン類も充填物として好ましぐパクリタキセル等が挙げられる。 本発明のプレフィルドシリンジは、これらの化合物を充填した場合に、これらの化合物 の吸着量が少なくなる。
実施例
[0029] 以下に、実施例を挙げて本発明を更に具体的に説明するが、本発明はこれらの実 施例によりその範囲を限定されるものではない。
本実施例で使用したポリエステル樹脂およびプレフィルドシリンジの評価方法は以 下の通りである。
[0030] <ポリエステル樹脂の評価方法〉
(1)環状ァセタール骨格を有するジオール単位と、ナフタレン骨格を有するジカルボ ン酸単位の割合
ポリエステル樹脂中の環状ァセタール骨格を有するジオール単位と、ナフタレン骨 格を有するジカルボン酸単位の割合は1 H— NMR測定にて算出した。測定装置は 日本電子(株) tilNM— AL400を用い、 400MHzで測定した。溶媒には重クロロホ ルムを用いた。
[0031] (2)ガラス転移温度 (Tg)
ポリエステル樹脂のガラス転移温度は島津製作所製 DSC/TA— 50WSを使用し 、ポリエステル樹脂約 10mgをアルミニウム製非密封容器に入れ、窒素ガス(30ml/ min)気流中、昇温速度 20°C/minで 280°Cまで加熱、溶融したものを急冷して測 定用試料とした。該試料を同条件で測定し、 DSC曲線の転移前後における基線の 差の 1/2だけ変化した温度をガラス転移温度とした。
[0032] (3)極限粘度(IV)
極限粘度測定の試料はポリエステル樹脂 0. 5gをフエノールと 1 , 1 , 2, 2—テトラク ロロェタンの混合溶媒 (質量比 = 6 : 4) 120gに加熱溶解し、濾過後、 25°Cまで冷却 して調製した。測定装置は (株)柴山科学機械製作所製、毛細管粘度計自動測定装
置 SS— 300— LIを用い、温度 25°Cで測定を行った。
[0033] (4)透湿係数
溶融押出成形にて得た 200 m厚のフィルムを測定用試料としてポリエステル樹脂 の透湿度を測定した。測定条件は 40°C、 90%RHである。測定装置は LYSSY社製 水蒸気透過度計 L80— 4005Lである。測定で得られた透湿度から透湿係数を下記 式より算出した。
透湿係数(g · mm/m /日) =透湿度(g/m /日) X厚さ(mm)
[0034] (5)酸素透過係数
溶融押出成形にて得た 200 m厚のフィルムを測定用試料としてポリエステル樹脂 の酸素透過度を測定した。測定条件は 23°C、 65%RHである。測定装置は MOCO N社製 OX— TRAN2/21である。測定で得られた酸素透過度から酸素透過係数を 下記式より算出した。
酸素透過係数 (cc · mm/ m Z日/ atm) =酸素; 過度 (cc m 日/ atm) X ^- (mm;
(6)水の蒸散率
水を充填し、封をしたプレフィルドシリンジを 40°C、 75%RHの恒温恒湿機中で 3ケ 月間保持した。保持前後の内容物を含めたシリンジの質量 W1 (保持前)、 W2 (保持 後)及び初期の水の充填量 (wl)から以下の式にて蒸散率を測定した。
水の蒸散率(%) = [ ( 1 W2) /wl] X 100
[0036] (7)タンパク質吸着試験での窒素増量
タンパク質水溶液を充填したプレフィルドシリンジを 23°C、 50%RHで 8日間保存し た。保存後のプレフィルドシリンジを純水で 5回洗浄後、窒素元素分析にて窒素量( N2)を定量した。 N2とタンパク質水溶液充填前の窒素元素量 (N1)との差分をタン パク質吸着試験での窒素増量とした。タンパク質水溶液としてはシグマアルドリッチジ ャパン製アルブミン (ゥシ由来、粉末)、フラクション Vの lwt%水溶液を使用した。元 素分析には三菱化成製全窒素分析計 TN— 10を使用した。
[0037] (8)ビタミン Dの保持率
ビタミン Dを所定量 (Ml)含有した溶液を充填したプレフィルドシリンジを 23°C、 50 %RHで 8日間保存した。保存後の内容物のビタミン D量 (M2)を液体クロマトグラフ にて定量し、以下の式からビタミン Dの保持率を算出した。
ビタミン Dの保持率(%) = [1—(Ml— M2) /M1] X 100
[0038] (9)落下試験
水を充填したプレフィルドシリンジを 1. 5mの高さから 5回連続して自由落下させた 。 10個のサンプルに対して途中で割れたものが一つもない場合を合格とした。
(10)煮沸試験
水を充填したプレフィルドシリンジを沸騰水中 10分間煮沸消毒した後、プランジャ 一とバレルの間からの漏れや、白化などの外観変化を観察した。いずれも認められな いものを合格とした。
[0039] 実施例;!〜 3及び比較例 1、 2
〔ポリエステル樹脂の製造、評価〕
充填塔式精留塔、分縮器、全縮器、コールドトラップ、撹拌機、加熱装置、窒素導 入管を備えた 0. 15立方メートルのポリエステル製造装置に表 1に記載の原料モノマ 一を仕込み、ジカルボン酸成分に対し酢酸マンガン四水和物 0. 03モル%の存在下 、窒素雰囲気下で 215°C迄昇温してエステル交換反応を行った。ジカルボン酸成分 の反応転化率を 90%以上とした後、ジカルボン酸成分に対して、酸化アンチモン (II 1) 0. 02モノレ0 /0とリン酸トリェチノレ 0. 06モル0 /0を加え、昇温と減圧を徐々に行い、最 終的に 280°C、 0. IkPa以下で重縮合を行った。適度な溶融粘度になった時点で反 応を終了し、ポリエステル樹脂を製造した。
[0040] 得られたポリエステル樹脂を Tダイを備えた 25mm単軸押出機にて 240〜260°Cで 溶融押出成形し、 200 ,1 m厚のフィルムを得た。
得られたポリエステル樹脂及びフィルムにつ!/、て、前記の評価を行レ、その結果を表 1に示す。
尚、表中の略記の意味は下記の通りである。
NDCM : 2, 6—ナフタレンジカルボン酸ジメチル
DMT:テレフタル酸ジメチル
EG :エチレングリコール
SPG : 3, 9 ビス(1 , 1ージメチノレー 2 ヒドロキシェチノレ) 2, 4, 8, 10 テトラ ォキサスピロ〔5. 5〕ゥンデカン
[0041] 〔プレフィルドシリンジの作製、評価〕
上記のように得られたポリエステル樹脂を型締め力 100トンの射出成形機にて 240 〜260°Cの温度条件で射出成形して接合部一体型のバレル、プランジャーとした。 プランジャー先端にブチルゴム製のパッキンを取り付け、容量 5mlの注射容器を準備 した。得られた注射容器について、前記の評価を行いその結果を表 1に示す。
[0042] 比較例 3
実施例 1にお!/、て、ポリエステル樹脂に代えてプライムポリマー社製ポリプロピレン J — 452HPを使用した以外は実施例 1と同様に注射容器を準備し、評価を行った。評 価結果を表 2に示す。
[0043] 比較例 4
実施例 1において、ポリエステル樹脂に代えて Ticona GmbH社製シクロォレフィ ンコポリマー TOPAS6013を使用した以外は実施例 1と同様に注射容器を準備し、 評価を行った。評価結果を表 2に示す。
[0044] [表 1]
表
比較例 3 比較例 4 樹脂の評価結果
ガラス転移点 (T g) CC) < 20 145 透湿係数 (g · mm/m2 日) 0.28 0.06
酸素透過係数
75 40 ( c c · mm/ m2/曰 Z a t m)
プレフィルドシリンジの評価結果
水の蒸散率(%) 0.2 0.1 窒素増量(ppm) 31 9 ビタミン D保持率 (%) 89 89 落下試験 合格 合格 、沸 験 合格 合格
Claims
[1] 少なくともバレル及び接合部のそれぞれを構成する樹脂力 ジオール単位中の;!〜
30モル%が環状ァセタール骨格を有するジオール単位であり、ジカルボン酸単位中 の 70モル%以上がナフタレン骨格を有するジカルボン酸単位であり、下記式( から (iii)を!、ずれも満たすポリエステル樹脂を含むであるプレフィルドシリンジ。
(i)示差走査熱量計で測定したガラス転移温度が 110°C以上
(ii)透、湿係数が lg 'mm m /日以下
(iii)酸素透過係数が 1 Occ · mm/m2/日 /atm以下
[2] 環状ァセタール骨格を有するジオール単位が一般式(1):
(式中、 R1および R2はそれぞれ独立して、炭素数が;!〜 10の脂肪族炭化水素基、炭 素数が 3〜; 10の脂環式炭化水素基及び炭素数が 6〜; 10の芳香族炭化水素基から なる群から選ばれる炭化水素基を表す。 )
または一般式(2) :
[化 2]
(式中、 R1は前記と同様であり、 R3は炭素数が;!〜 10の脂肪族炭化水素基、炭素数 力 ¾〜; 10の脂環式炭化水素基及び炭素数が 6〜; 10の芳香族炭化水素基からなる群 から選ばれる炭化水素基を表す。 )
で表されるジオールに由来するジオール単位である、請求項 1記載のプレフィルドシ [3] 環状ァセタール骨格を有するジオール単位が、 3, 9 ビス(1 , 1 ジメチルー 2—
ヒドロキシェチノレ) 2, 4, 8, 10 テトラオキサスピロ〔5· 5〕ゥンデカン、または 5 メ チロールー5—ェチルー 2—(1 , 1 ジメチルー 2—ヒドロキシェチル) 1 ,
3—ジォ キサンに由来するジオール単位である、請求項 1記載のプレフィルドシリンジ。
[4] ジカルボン酸単位が 1 , 3—ナフタレンジカルボン酸、 1 , 4 ナフタレンジカルボン 酸、 1 , 5 ナフタレンジカルボン酸、 2, 6 ナフタレンジカルボン酸、及び 2, 7 ナ フタレンジカルボン酸からなる群から選ばれる 1種以上のジカルボン酸に由来する、 請求項 1記載のプレフィルドシリンジ。
[5] ジカルボン酸単位が 2, 6—ナフタレンジカルボン酸に由来する、請求項 1記載のプ
[6] ポリエステル樹脂の 25°Cでの極限粘度(IV)が、 0. 5〜; 1. 5dl/gの範囲である、 請求項 1記載のプレフィルドシリンジ。
[7] ポリエステル樹脂がエステル交換法を用いて製造されたものである、請求項 1記載