WO2007142203A1 - 量子ドット発光型無機el素子 - Google Patents
量子ドット発光型無機el素子 Download PDFInfo
- Publication number
- WO2007142203A1 WO2007142203A1 PCT/JP2007/061314 JP2007061314W WO2007142203A1 WO 2007142203 A1 WO2007142203 A1 WO 2007142203A1 JP 2007061314 W JP2007061314 W JP 2007061314W WO 2007142203 A1 WO2007142203 A1 WO 2007142203A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- light emitting
- quantum dot
- inorganic
- insulating layer
- layer
- Prior art date
Abstract
Description
Claims