WO2007080804A1 - 防汚性を有する複合部材 - Google Patents
防汚性を有する複合部材 Download PDFInfo
- Publication number
- WO2007080804A1 WO2007080804A1 PCT/JP2006/326224 JP2006326224W WO2007080804A1 WO 2007080804 A1 WO2007080804 A1 WO 2007080804A1 JP 2006326224 W JP2006326224 W JP 2006326224W WO 2007080804 A1 WO2007080804 A1 WO 2007080804A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- inorganic fine
- fine particles
- composite member
- substrate
- antifouling
- Prior art date
Abstract
Description
Claims