WO2006120222A1 - Verfahren und vorrichtung zum thermischen fügen von werkstoffen mit hochschmelzenden oxidbehafteten oberflächen - Google Patents
Verfahren und vorrichtung zum thermischen fügen von werkstoffen mit hochschmelzenden oxidbehafteten oberflächen Download PDFInfo
- Publication number
- WO2006120222A1 WO2006120222A1 PCT/EP2006/062225 EP2006062225W WO2006120222A1 WO 2006120222 A1 WO2006120222 A1 WO 2006120222A1 EP 2006062225 W EP2006062225 W EP 2006062225W WO 2006120222 A1 WO2006120222 A1 WO 2006120222A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- laser beam
- materials
- arc
- joint
- oxide layer
- Prior art date
Abstract
Description
Claims