WO2006004262A1 - Panneau avant destine a un ecran a plasma a haute efficacite contenant des nanopointes, et procede de preparation correspondant - Google Patents

Panneau avant destine a un ecran a plasma a haute efficacite contenant des nanopointes, et procede de preparation correspondant Download PDF

Info

Publication number
WO2006004262A1
WO2006004262A1 PCT/KR2005/000868 KR2005000868W WO2006004262A1 WO 2006004262 A1 WO2006004262 A1 WO 2006004262A1 KR 2005000868 W KR2005000868 W KR 2005000868W WO 2006004262 A1 WO2006004262 A1 WO 2006004262A1
Authority
WO
WIPO (PCT)
Prior art keywords
nanotips
dielectric layer
front panel
panel according
pdp
Prior art date
Application number
PCT/KR2005/000868
Other languages
English (en)
Inventor
Yong Seog Kim
Sung Won Cho
Original Assignee
Yong Seog Kim
Sung Won Cho
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yong Seog Kim, Sung Won Cho filed Critical Yong Seog Kim
Publication of WO2006004262A1 publication Critical patent/WO2006004262A1/fr

Abstract

L'invention concerne un panneau avant destiné à un écran à plasma (PDP) permettant d'augmenter la puissance d'émission et d'abaisser considérablement la tension d'entraînement d'un PDP. Le panneau avant comprend un substrat transparent, des électrodes d'entretien, des électrodes de bus, des couches diélectriques et une couche protectrice dans laquelle des groupes de pointes sont formés dans des zones d'une couche diélectrique supérieure correspondant aux électrodes d'entretien, chacun des groupes de pointes consistant en une ou plusieurs nanopointes au moins partiellement en saillie à partir de la surface de la couche protectrice des nanopointes, ces nanopointes étant espacées les unes des autres par au moins une distance par laquelle l'amélioration de champ est entraînée et des nanopointes sont revêtues d'un film protecteur de sorte à être protégées contre la pulvérisation de plasma. L'invention concerne enfin un procédé destiné à fabriquer ce panneau avant.
PCT/KR2005/000868 2004-03-26 2005-03-25 Panneau avant destine a un ecran a plasma a haute efficacite contenant des nanopointes, et procede de preparation correspondant WO2006004262A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
KR10-2004-0020758 2004-03-26
KR1020040020758A KR20050095381A (ko) 2004-03-26 2004-03-26 나노 팁을 포함하고 있는 고효율 플라즈마 디스플레이소자용 전면판 및 그것의 제조방법

Publications (1)

Publication Number Publication Date
WO2006004262A1 true WO2006004262A1 (fr) 2006-01-12

Family

ID=35783044

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/KR2005/000868 WO2006004262A1 (fr) 2004-03-26 2005-03-25 Panneau avant destine a un ecran a plasma a haute efficacite contenant des nanopointes, et procede de preparation correspondant

Country Status (2)

Country Link
KR (1) KR20050095381A (fr)
WO (1) WO2006004262A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1796126A3 (fr) * 2005-12-12 2009-05-27 Samsung SDI Co., Ltd. Dispositif d'affichage

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100777727B1 (ko) * 2005-11-24 2007-11-19 삼성에스디아이 주식회사 디스플레이 장치
KR100759447B1 (ko) * 2005-11-30 2007-09-20 삼성에스디아이 주식회사 평판 표시 장치 및 그 제조방법
KR100730182B1 (ko) * 2005-12-12 2007-06-19 삼성에스디아이 주식회사 표시 장치
KR100824259B1 (ko) * 2007-06-12 2008-04-24 (주)우진기계 리크테스터용 일체형 매니폴더와 컨버터의 정렬장치

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07122196A (ja) * 1993-10-26 1995-05-12 Matsushita Electric Ind Co Ltd プラズマ表示パネル及びその駆動方法
JP2001176398A (ja) * 1999-12-16 2001-06-29 Toray Ind Inc プラズマディスプレイ用部材およびプラズマディスプレイ
JP2001222944A (ja) * 2000-02-07 2001-08-17 Samsung Sdi Co Ltd カーボンナノチューブを採用した２次電子増幅構造体及びこれを用いたプラズマ表示パネル及びバックライト
JP2001266752A (ja) * 2000-03-24 2001-09-28 Dainippon Printing Co Ltd プラズマディスプレイパネル用の背面板及びそれを用いたプラズマディスプレイパネル
JP2003272512A (ja) * 2002-03-15 2003-09-26 Kanekkusu:Kk 表示装置の電極及びその製造方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07122196A (ja) * 1993-10-26 1995-05-12 Matsushita Electric Ind Co Ltd プラズマ表示パネル及びその駆動方法
JP2001176398A (ja) * 1999-12-16 2001-06-29 Toray Ind Inc プラズマディスプレイ用部材およびプラズマディスプレイ
JP2001222944A (ja) * 2000-02-07 2001-08-17 Samsung Sdi Co Ltd カーボンナノチューブを採用した２次電子増幅構造体及びこれを用いたプラズマ表示パネル及びバックライト
JP2001266752A (ja) * 2000-03-24 2001-09-28 Dainippon Printing Co Ltd プラズマディスプレイパネル用の背面板及びそれを用いたプラズマディスプレイパネル
JP2003272512A (ja) * 2002-03-15 2003-09-26 Kanekkusu:Kk 表示装置の電極及びその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1796126A3 (fr) * 2005-12-12 2009-05-27 Samsung SDI Co., Ltd. Dispositif d'affichage

Also Published As

Publication number Publication date
KR20050095381A (ko) 2005-09-29

Similar Documents

Publication Publication Date Title
US7956540B2 (en) Plasma display panel
JP4927046B2 (ja) 電子放出促進物質を有するＭｇＯ保護膜、その製造方法及び該保護膜を備えたプラズマディスプレイパネル
CN1269177C (zh) 图像显示装置及其制造方法
JP2004006308A (ja) 炭素ナノチューブを用いたプラズマディスプレイパネル及びその前面パネル製造方法
WO2005117055A1 (fr) Procédé de traitement d’un écran cathodique, affichage à émission par effet de champ, et son procédé de fabrication
KR100709188B1 (ko) 평판 표시 장치 및 그의 제조방법
WO2006004262A1 (fr) Panneau avant destine a un ecran a plasma a haute efficacite contenant des nanopointes, et procede de preparation correspondant
WO2004086449A1 (fr) Panneau avant d'ecran au plasma haute efficacite equipe de nano-extremites, et procede d'elaboration
KR100285760B1 (ko) 플라즈마 디스플레이 패널용 격벽제조방법 및 이를 이용한 플라즈마 디스플레이 패널 소자
JP2004119118A (ja) プラズマ表示装置およびその製造方法
JP2011181413A (ja) 保護膜、保護膜の製造方法、プラズマディスプレイパネルおよびプラズマディスプレイパネルの製造方法
KR100738234B1 (ko) 플라즈마 디스플레이 패널 제조용 그린 쉬트 및 플라즈마 디스플레이 패널
JP2002083551A (ja) プラズマディスプレイパネルの背面基板とその製造方法、および、プラズマディスプレイパネルとその製造方法
JP2002042663A (ja) 交流駆動型プラズマ表示装置及びその製造方法
JP2006139999A (ja) プラズマディスプレイパネル用保護膜およびその形成方法並びにプラズマディスプレイパネル
JP2002338959A (ja) 蛍光体粒子及びその製造方法、表示用パネル及びその製造方法、並びに、平面型表示装置及びその製造方法
JP2002170494A (ja) 気体放電表示装置及び放電灯
KR100824705B1 (ko) 플라즈마 디스플레이 패널 및 이의 제조방법
JP2007323922A (ja) プラズマディスプレイパネル
KR100759447B1 (ko) 평판 표시 장치 및 그 제조방법
JP2008186749A (ja) ディスプレイ用部材の形成方法。
KR100333413B1 (ko) 플라즈마 표시소자 제조방법
KR20000003384A (ko) 플라즈마 디스플레이 패널용 격벽 제조방법 및이를 이용한 플라즈마 디스플레이 패널 소자
KR100326859B1 (ko) 플라즈마 표시장치용 격벽 제조방법
US20070132391A1 (en) Plasma display panel

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SM SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

122 Ep: pct application non-entry in european phase