WO2005118924A1 - Loaded polymer fibre, method for the production thereof, use of the same, and composition comprising such fibres - Google Patents
Loaded polymer fibre, method for the production thereof, use of the same, and composition comprising such fibres Download PDFInfo
- Publication number
- WO2005118924A1 WO2005118924A1 PCT/FR2005/050364 FR2005050364W WO2005118924A1 WO 2005118924 A1 WO2005118924 A1 WO 2005118924A1 FR 2005050364 W FR2005050364 W FR 2005050364W WO 2005118924 A1 WO2005118924 A1 WO 2005118924A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fiber
- fibers
- charged
- polymer
- fiber according
- Prior art date
Abstract
Description
Claims