WO2005097872A1 - Dispergiermittel für pigmentkonzentrate, seine verwendung und das dispergiermittel enthaltende masterbatches - Google Patents
Dispergiermittel für pigmentkonzentrate, seine verwendung und das dispergiermittel enthaltende masterbatches Download PDFInfo
- Publication number
- WO2005097872A1 WO2005097872A1 PCT/EP2005/002515 EP2005002515W WO2005097872A1 WO 2005097872 A1 WO2005097872 A1 WO 2005097872A1 EP 2005002515 W EP2005002515 W EP 2005002515W WO 2005097872 A1 WO2005097872 A1 WO 2005097872A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pigments
- acid
- pigment
- hydroxyl groups
- parts
- Prior art date
Abstract
Description
Claims