WO2005009921A2 - Structure composite thermostructurale a gradient de composition et son procede de fabrication - Google Patents
Structure composite thermostructurale a gradient de composition et son procede de fabrication Download PDFInfo
- Publication number
- WO2005009921A2 WO2005009921A2 PCT/FR2004/001876 FR2004001876W WO2005009921A2 WO 2005009921 A2 WO2005009921 A2 WO 2005009921A2 FR 2004001876 W FR2004001876 W FR 2004001876W WO 2005009921 A2 WO2005009921 A2 WO 2005009921A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ceramic
- preform
- structure according
- stiffeners
- intermediate layers
- Prior art date
Abstract
Description
Claims