WO2004087796A1 - Nouveau procede de synthese/fabrication de films acryliques - Google Patents
Nouveau procede de synthese/fabrication de films acryliques Download PDFInfo
- Publication number
- WO2004087796A1 WO2004087796A1 PCT/FR2004/000713 FR2004000713W WO2004087796A1 WO 2004087796 A1 WO2004087796 A1 WO 2004087796A1 FR 2004000713 W FR2004000713 W FR 2004000713W WO 2004087796 A1 WO2004087796 A1 WO 2004087796A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film according
- monomers
- weight
- block
- chosen
- Prior art date
Abstract
Description
Claims