WO2003093375A1 - Beschichtete federn für fahrzeuge und verfahren zu ihrer herstellung - Google Patents
Beschichtete federn für fahrzeuge und verfahren zu ihrer herstellung Download PDFInfo
- Publication number
- WO2003093375A1 WO2003093375A1 PCT/EP2003/004391 EP0304391W WO03093375A1 WO 2003093375 A1 WO2003093375 A1 WO 2003093375A1 EP 0304391 W EP0304391 W EP 0304391W WO 03093375 A1 WO03093375 A1 WO 03093375A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- springs
- primer
- coating
- powder coating
- springs according
- Prior art date
Abstract
Description
Claims