WO2003054040A1 - Continuous dosing of extremely fast initiators during polymerization reactions - Google Patents
Continuous dosing of extremely fast initiators during polymerization reactions Download PDFInfo
- Publication number
- WO2003054040A1 WO2003054040A1 PCT/EP2002/014518 EP0214518W WO03054040A1 WO 2003054040 A1 WO2003054040 A1 WO 2003054040A1 EP 0214518 W EP0214518 W EP 0214518W WO 03054040 A1 WO03054040 A1 WO 03054040A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- initiator
- polymerization
- dosed
- hour
- initiators
- Prior art date
Abstract
Description
Claims