WO2002031080A1 - Zusammensetzung zur herstellung schwerbenetzbarer oberflächen - Google Patents
Zusammensetzung zur herstellung schwerbenetzbarer oberflächen Download PDFInfo
- Publication number
- WO2002031080A1 WO2002031080A1 PCT/EP2001/011847 EP0111847W WO0231080A1 WO 2002031080 A1 WO2002031080 A1 WO 2002031080A1 EP 0111847 W EP0111847 W EP 0111847W WO 0231080 A1 WO0231080 A1 WO 0231080A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- range
- composition
- coating
- hydrophobic
- inorganic powder
- Prior art date
Abstract
Description
Claims