WO2000027615A1 - Articles fabriques a partir de compositions interpolymeres d'alpha-olefine/vinyle ou de vinylidene aromatique et/ou de vinyle ou de vinylidene aliphatique ou cycloaliphatique encombres steriquement - Google Patents
Articles fabriques a partir de compositions interpolymeres d'alpha-olefine/vinyle ou de vinylidene aromatique et/ou de vinyle ou de vinylidene aliphatique ou cycloaliphatique encombres steriquement Download PDFInfo
- Publication number
- WO2000027615A1 WO2000027615A1 PCT/US1999/025073 US9925073W WO0027615A1 WO 2000027615 A1 WO2000027615 A1 WO 2000027615A1 US 9925073 W US9925073 W US 9925073W WO 0027615 A1 WO0027615 A1 WO 0027615A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ethylene
- styrene
- component
- fabricated article
- vinyl
- Prior art date
Abstract
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP99958674A EP1126969A1 (fr) | 1998-11-06 | 1999-10-26 | Articles fabriques a partir de compositions interpolymeres d'alpha-olefine/vinyle ou de vinylidene aromatique et/ou de vinyle ou de vinylidene aliphatique ou cycloaliphatique encombres steriquement |
AU15988/00A AU1598800A (en) | 1998-11-06 | 1999-10-26 | Fabricated articles produced from alpha-olefin/vinyl or vinylidene aromatic and/or hindered aliphatic or cycloaliphatic vinyl or vinylidene interpolymer compositions |
JP2000580822A JP2002529547A (ja) | 1998-11-06 | 1999-10-26 | α−オレフィン/ビニルもしくはビニリデン芳香族及び/又は立体障害のある脂肪族もしくは脂環式ビニルもしくはビニリデンインターポリマー組成物から製造される加工品 |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10731098P | 1998-11-06 | 1998-11-06 | |
US60/107,310 | 1998-11-06 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2000027615A1 true WO2000027615A1 (fr) | 2000-05-18 |
WO2000027615A9 WO2000027615A9 (fr) | 2002-08-29 |
Family
ID=22315984
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1999/025073 WO2000027615A1 (fr) | 1998-11-06 | 1999-10-26 | Articles fabriques a partir de compositions interpolymeres d'alpha-olefine/vinyle ou de vinylidene aromatique et/ou de vinyle ou de vinylidene aliphatique ou cycloaliphatique encombres steriquement |
Country Status (5)
Country | Link |
---|---|
EP (1) | EP1126969A1 (fr) |
JP (1) | JP2002529547A (fr) |
AR (1) | AR021231A1 (fr) |
AU (1) | AU1598800A (fr) |
WO (1) | WO2000027615A1 (fr) |
Cited By (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2000066651A1 (fr) * | 1999-04-30 | 2000-11-09 | The Dow Chemical Company | Film aux proprietes ameliorees |
US7547745B2 (en) | 2002-11-26 | 2009-06-16 | Dow Global Technologies, Inc. | Epoxy resin hardener of anhydride copolymer and anhydride-elastomer copolymer |
CN101062601B (zh) * | 2006-04-28 | 2010-11-24 | 财团法人工业技术研究院 | 阻气结构 |
US7855316B2 (en) * | 2002-12-20 | 2010-12-21 | Kimberly-Clark Worldwide, Inc. | Preferentially stretchable laminates with perforated layers |
US8993681B2 (en) | 2011-07-14 | 2015-03-31 | Exxonmobil Research And Engineering Company | Dendritic ethylene polymers and processes for making |
CN105504739A (zh) * | 2014-09-24 | 2016-04-20 | 沈阳宏伟塑料制品有限公司 | 一种无卤阻燃abs/pc合金树脂及其制备方法 |
CN109627745A (zh) * | 2018-12-27 | 2019-04-16 | 武汉德航联合科技有限公司 | 一种用于跑道的填充颗粒及其制备方法 |
WO2020088454A1 (fr) * | 2018-10-30 | 2020-05-07 | 中国石油化工股份有限公司 | Copolymère de dioléfine conjuguée/styrène hydrogéné, matériau moussant de celui-ci et son application |
CN114736511A (zh) * | 2022-04-29 | 2022-07-12 | 浙江新力新材料股份有限公司 | 一种低模垢耐高温有卤阻燃增强高温尼龙材料及其制备方法 |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN103724782A (zh) * | 2013-12-10 | 2014-04-16 | 芜湖佳诚电子科技有限公司 | 一种综合性良好的无卤阻燃聚乙烯电缆料及其制备方法 |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4107130A (en) * | 1976-06-07 | 1978-08-15 | Shell Oil Company | Multicomponent polyolefin-block copolymer-polymer blends |
WO1995013321A1 (fr) * | 1993-11-12 | 1995-05-18 | Exxon Chemical Patents Inc. | Films thermosoudables et articles obtenus a partir de ceux-ci |
WO1996007681A1 (fr) * | 1994-09-02 | 1996-03-14 | The Dow Chemical Company | Elastomeres thermodurcis |
WO1998010015A1 (fr) * | 1996-09-04 | 1998-03-12 | The Dow Chemical Company | MELANGES A BASE DE COPOLYMERES DE MONOMERES AROMATIQUES D'α-OLEFINE/VINYLIDENE OU DE MONOMERES VINYLIDENE ALIPHATIQUES EMPECHES, ET DE POLYOLEFINES |
WO1998027156A1 (fr) * | 1996-12-17 | 1998-06-25 | The Dow Chemical Company | Copolymeres plastifies de monomere aromatique alpha-olefine/vinylidene ou de monomere vinylidene inhibe aliphatique ou cycloaliphatique |
EP0906932A2 (fr) * | 1997-10-01 | 1999-04-07 | Denki Kagaku Kogyo Kabushiki Kaisha | Feuille et feuille pour emballage sous tension |
-
1999
- 1999-10-26 AU AU15988/00A patent/AU1598800A/en not_active Abandoned
- 1999-10-26 JP JP2000580822A patent/JP2002529547A/ja active Pending
- 1999-10-26 EP EP99958674A patent/EP1126969A1/fr not_active Withdrawn
- 1999-10-26 WO PCT/US1999/025073 patent/WO2000027615A1/fr not_active Application Discontinuation
- 1999-11-05 AR ARP990105617 patent/AR021231A1/es unknown
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4107130A (en) * | 1976-06-07 | 1978-08-15 | Shell Oil Company | Multicomponent polyolefin-block copolymer-polymer blends |
WO1995013321A1 (fr) * | 1993-11-12 | 1995-05-18 | Exxon Chemical Patents Inc. | Films thermosoudables et articles obtenus a partir de ceux-ci |
WO1996007681A1 (fr) * | 1994-09-02 | 1996-03-14 | The Dow Chemical Company | Elastomeres thermodurcis |
WO1998010015A1 (fr) * | 1996-09-04 | 1998-03-12 | The Dow Chemical Company | MELANGES A BASE DE COPOLYMERES DE MONOMERES AROMATIQUES D'α-OLEFINE/VINYLIDENE OU DE MONOMERES VINYLIDENE ALIPHATIQUES EMPECHES, ET DE POLYOLEFINES |
WO1998027156A1 (fr) * | 1996-12-17 | 1998-06-25 | The Dow Chemical Company | Copolymeres plastifies de monomere aromatique alpha-olefine/vinylidene ou de monomere vinylidene inhibe aliphatique ou cycloaliphatique |
EP0906932A2 (fr) * | 1997-10-01 | 1999-04-07 | Denki Kagaku Kogyo Kabushiki Kaisha | Feuille et feuille pour emballage sous tension |
Non-Patent Citations (1)
Title |
---|
C.F. DIEHL ET AL: "BLENDS OF ETHYLENE/STYRENE INTERPOLYMERS AND OTHER POLYMERS: BENEFITS IN APPLICATIONS", ANTEC '99 PROCEEDINGS, vol. 2, - 6 May 1999 (1999-05-06), NEW YORK, pages 2149 - 2153, XP000878849 * |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2000066651A1 (fr) * | 1999-04-30 | 2000-11-09 | The Dow Chemical Company | Film aux proprietes ameliorees |
US7547745B2 (en) | 2002-11-26 | 2009-06-16 | Dow Global Technologies, Inc. | Epoxy resin hardener of anhydride copolymer and anhydride-elastomer copolymer |
US7855316B2 (en) * | 2002-12-20 | 2010-12-21 | Kimberly-Clark Worldwide, Inc. | Preferentially stretchable laminates with perforated layers |
CN101062601B (zh) * | 2006-04-28 | 2010-11-24 | 财团法人工业技术研究院 | 阻气结构 |
US8993681B2 (en) | 2011-07-14 | 2015-03-31 | Exxonmobil Research And Engineering Company | Dendritic ethylene polymers and processes for making |
CN105504739A (zh) * | 2014-09-24 | 2016-04-20 | 沈阳宏伟塑料制品有限公司 | 一种无卤阻燃abs/pc合金树脂及其制备方法 |
WO2020088454A1 (fr) * | 2018-10-30 | 2020-05-07 | 中国石油化工股份有限公司 | Copolymère de dioléfine conjuguée/styrène hydrogéné, matériau moussant de celui-ci et son application |
US11897988B2 (en) | 2018-10-30 | 2024-02-13 | China Petroleum & Chemical Corporation | Hydrogenated styrene/conjugated diolefin copolymer, foaming material thereof, and application thereof |
CN109627745A (zh) * | 2018-12-27 | 2019-04-16 | 武汉德航联合科技有限公司 | 一种用于跑道的填充颗粒及其制备方法 |
CN114736511A (zh) * | 2022-04-29 | 2022-07-12 | 浙江新力新材料股份有限公司 | 一种低模垢耐高温有卤阻燃增强高温尼龙材料及其制备方法 |
CN114736511B (zh) * | 2022-04-29 | 2023-11-21 | 浙江新力新材料股份有限公司 | 一种低模垢耐高温有卤阻燃增强高温尼龙材料及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
WO2000027615A9 (fr) | 2002-08-29 |
JP2002529547A (ja) | 2002-09-10 |
AU1598800A (en) | 2000-05-29 |
EP1126969A1 (fr) | 2001-08-29 |
AR021231A1 (es) | 2002-07-03 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US6103803A (en) | Filled polymer compositions | |
AU712414B2 (en) | Floor, wall or ceiling covering | |
US6254956B1 (en) | Floor, wall or ceiling covering | |
US6362270B1 (en) | Thermoplastic compositions for durable goods applications | |
CA2322569A1 (fr) | Fibres fabriquees a partir de copolymeres aromatiques d'alpha-olefine/de vinyle ou de vinylidene et/ou de copolymeres encombres cycloaliphatiques ou aliphatiques de vinyle ou de vinylidene | |
WO2001012708A1 (fr) | Compositions presentant une resistance amelioree a l'inflammation | |
US5741857A (en) | Blends of elastomer block copolymer and aliphatic α-olefin/monovinylidene aromatic monomer and/or hindered aliphatic vinylidene monomer interpolymer | |
US6166145A (en) | Blends of α-olefin/vinyl aromatic monomer and/or aliphatic or cycloaliphatic vinyl or vinylidene monomer interpolymers | |
EP1157048B1 (fr) | Procede d'elaboration a plusieurs systemes catalytiques pour la production d' interpolymeres d'alpha-olefines et de monomeres aromatoques insatures | |
WO2000027615A1 (fr) | Articles fabriques a partir de compositions interpolymeres d'alpha-olefine/vinyle ou de vinylidene aromatique et/ou de vinyle ou de vinylidene aliphatique ou cycloaliphatique encombres steriquement | |
US6201067B1 (en) | Polymeric blend compositions of α-olefin/vinylidene aromatic monomer interpolymers and aromatic polyethers | |
EP1023385A1 (fr) | Compositions thermoplastiques d'interpolymeres de monomeres d'alpha-olefines avec un ou plusieurs monomeres vinyliques ou vinylidene aromatiques et/ou un ou plusieurs monomeres vinyliques ou vinylydene aliphatiques ou cycloaliphatiques entraves melanges a des homopolymeres et des copolymeres d'halog | |
WO2002026882A2 (fr) | Melanges compatibles de polymeres aromatiques d'alcenyles, interpolymeres d'alpha-olefine/vinyle ou de vinylidene et copolymeres styreniques sequences | |
AU2001263430A1 (en) | Substantially random interpolymer grafted with one or more olefinically unsaturated organic monomers | |
WO1999064500A1 (fr) | Films conservant la forme qui leur est donnee, fabriques a partir d'interpolymeres aromatiques alpha-olefiniques/vinyliques et/ou vinyliques ou vinylideniques aliphatiques ou cycloaliphatiques | |
MXPA99011695A (en) | Filled polymer compositions | |
MXPA99002106A (en) | Floor, wall or ceiling covering | |
EP1290049A1 (fr) | Interpolymere sensiblement aleatoire greffe a un ou a plusieurs monomeres organiques alceniques | |
MXPA00006956A (en) | Thermoplastic blends of alpha-olefin/vinylidene aromatic monomer interpolymers with aromatic polyethers | |
MXPA00003675A (en) | Thermoplastic compositions of interpolymers of&agr;-olefin monomers with one or more vinyl or vinylidene aromatic monomers and/or one or more hindered aliphatic or cycloaliphatic vinyl or vinylidene monomers blended with vinyl halide homopolymers and co | |
CZ20001372A3 (cs) | Termoplastické kompozice interpolymerů alfaolcfínových monomerů a jednoho nebo více vinylaromatických nebo vinylidenaromatických monomerů a/nebo jednoho nebo více stericky bráněných alifatických nebo cykloalifatických vinylových nebo vinylidenových monomerů ve směsi s vinylhalogenidovými homopolymery a kopolymery |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
ENP | Entry into the national phase |
Ref country code: AU Ref document number: 2000 15988 Kind code of ref document: A Format of ref document f/p: F |
|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
ENP | Entry into the national phase |
Ref country code: JP Ref document number: 2000 580822 Kind code of ref document: A Format of ref document f/p: F |
|
WWE | Wipo information: entry into national phase |
Ref document number: 1999958674 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1999958674 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
AK | Designated states |
Kind code of ref document: C2 Designated state(s): AE AL AM AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ DE DK DM EE ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT TZ UA UG US UZ VN YU ZA ZW |
|
AL | Designated countries for regional patents |
Kind code of ref document: C2 Designated state(s): GH GM KE LS MW SD SL SZ TZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG |
|
COP | Corrected version of pamphlet |
Free format text: PAGE 1/1, DRAWINGS, REPLACED BY A NEW PAGE 1/1; DUE TO LATE TRANSMITTAL BY THE RECEIVING OFFICE |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1999958674 Country of ref document: EP |