WO1999002576A1 - Procede de preparation de compositions de resine de vinyle modifiee au caoutchouc aromatique modifiee au caoutchouc - Google Patents
Procede de preparation de compositions de resine de vinyle modifiee au caoutchouc aromatique modifiee au caoutchouc Download PDFInfo
- Publication number
- WO1999002576A1 WO1999002576A1 PCT/JP1998/003029 JP9803029W WO9902576A1 WO 1999002576 A1 WO1999002576 A1 WO 1999002576A1 JP 9803029 W JP9803029 W JP 9803029W WO 9902576 A1 WO9902576 A1 WO 9902576A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- monomer
- aromatic vinyl
- rubber
- meth
- weight
- Prior art date
Description
Claims