US20170221684A1 - Plasma processing method - Google Patents
Plasma processing method Download PDFInfo
- Publication number
- US20170221684A1 US20170221684A1 US15/484,264 US201715484264A US2017221684A1 US 20170221684 A1 US20170221684 A1 US 20170221684A1 US 201715484264 A US201715484264 A US 201715484264A US 2017221684 A1 US2017221684 A1 US 2017221684A1
- Authority
- US
- United States
- Prior art keywords
- gas
- plasma
- processing
- upper electrode
- experimental examples
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This is a divisional application of U.S. patent application Ser. No. 14/521,737, filed on Oct. 23, 2014, which claims the benefit of Japanese Patent Application Nos. 2013-221468 and 2014-164369 filed on Oct. 24, 2013, and Aug. 12, 2014, respectively, the entire disclosures of which are incorporated herein by reference.
- The embodiments described herein pertain generally to a plasma processing method.
- In a semiconductor manufacturing process, a plasma processing apparatus configured to perform a plasma process for a thin film deposition or an etching is widely used. Such a plasma processing apparatus includes, for example, a plasma CVD (Chemical Vapor Deposition) apparatus configured to perform a thin film deposition process, a plasma etching apparatus configured to perform an etching process, and so forth.
- Such a plasma processing apparatus includes a processing vessel for performing therein a plasma process on a processing target object, a sample table for holding the processing target object within the processing vessel, a gas supply system for introducing a required processing gas for a plasma reaction into the processing vessel, and so forth. Further, to excite the processing gas within the processing vessel into plasma, the plasma processing apparatus also includes a plasma generation device configured to supply electromagnetic energy such as a microwave or a RF wave, a bias voltage application device configured to apply a bias voltage to the sample table to accelerate ions in the plasma toward the processing target object held on the sample table, and so forth.
- In the plasma processing apparatus, however, as the processing target object is plasma-processed, various kinds of deposits (reaction products, reaction by-products, etc) adhere to members (hereinafter, referred to as “in-vessel member”) provided within the processing vessel. These deposits may be etched to be dispersed as contaminants when a next substrate is processed. Further, as substrates are processed, the deposits may be deposited within the processing vessel and fall down later, so that particles are generated. Accordingly, the deposits need to be removed. In this regard, Patent Document 1 describes a technique of removing a metal-containing deposit, which is generated when a processing target object containing a metal film such as a transition metal is plasma-processed and adheres to in-vessel members, by using plasma of a chlorine-based gas or a nitrogen-based gas.
- Patent Document 1: Japanese Patent Laid-open Publication No. 2006-179834
- Patent Document 2: Japanese Patent Laid-open Publication No. 2006-165246
- However, in the conventional technique of using the chlorine-based gas or the nitrogen-based gas, the metal-containing deposit may not be removed efficiently if a metal having resistance to the plasma of the chlorine based gas or the nitrogen-based gas is contained in the deposit.
- In one example embodiment, a plasma processing method includes removing a deposit, which adheres to a member within a processing vessel and contains at least one of a transition metal and a base metal, by plasma of a processing gas containing a CxFy gas, in which x is an integer equal to or less than 2 and y is an integer equal to or less than 6, and without containing a chlorine-based gas and a nitrogen-based gas.
- In accordance with the example embodiment, a deposit, which adheres to a member within a processing vessel and contains at least one of a transition metal and a base metal, is removed by plasma of a processing gas containing a CxFy gas, in which x is an integer equal to or less than 2 and y is an integer equal to or less than 6, and without containing a chlorine-based gas and a nitrogen-based gas.
- The processing gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas may be at least one of a CF4 gas, a CF4/CO gas, a CF4/CO2 gas, a CF4/Ar gas, a CF4/CO/Ar gas, a CF4/CO2/Ar gas, a C2F6 gas, a C2F6/CO gas, a C2F6/CO2 gas, a C2F6/Ar gas, a C2F6/CO/Ar gas, and a C2F6/CO2/Ar gas.
- The transition metal may be at least one of Ti, Hf and Ta.
- The base metal may be Al.
- The plasma of the processing gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas may be generated by applying high frequency powers to two facing electrodes within the processing vessel, respectively, and the deposit may be removed by the generated plasma.
- The deposit may be removed by the plasma of the processing gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas while applying a negative DC voltage to the member within the processing vessel.
- In another example embodiment, a plasma processing method includes removing a deposit, which adheres to a member within a processing vessel and includes at least one of a transition metal and a base metal, by plasma of a processing gas, wherein the processing gas includes Ar gas and a CHzFw gas, in which z is an integer equal to or less than 3 and w is also an integer equal to or less than 3, and does not includes a chlorine-based gas and a nitrogen-based gas. The deposit is removed by the plasma of the processing gas while applying a negative DC voltage to the member within the processing vessel, and the negative DC voltage is set to be equal to or less than −100V such that argon ions in the plasma of the processing gas collide with the member within the processing vessel and the deposit is removed by sputtering of the argon ions.
- The processing gas may be at least one of a CHF3/Ar/O2 gas, a CH2F2/Ar/O2 gas and a CH3F/Ar/O2 gas. The transition metal may be at least one of Ti, Hf and Ta. The base metal may be Al.
- In yet another example embodiment, a plasma processing apparatus includes a processing vessel configured to perform therein a plasma process on a processing target object; a gas exhaust unit configured to depressurize an inside of the processing vessel; a gas supply unit configured to supply a processing gas into the processing vessel; and a controller configured to remove a deposit, which adheres to a member within the processing vessel and contains at least one of a transition metal and a base metal, by plasma of a processing gas containing a CxFy gas, in which x is an integer equal to or less than 2 and y is an integer equal to or less than 6, and without containing a chlorine-based gas and a nitrogen-based gas.
- In yet another example embodiment, a plasma processing apparatus includes a processing vessel configured to perform therein a plasma process on a processing target object; a gas exhaust unit configured to depressurize an inside of the processing vessel; a gas supply unit configured to supply a processing gas into the processing vessel; and a controller configured to remove a deposit, which adheres to a member within the processing vessel and contains at least one of a transition metal and a base metal, by plasma of a processing gas containing a CHzFw gas, in which z is an integer equal to or less than 3 and w is also an integer equal to or less than 3, and without containing a chlorine-based gas and a nitrogen-based gas while applying a negative DC voltage to the member within the processing vessel.
- According to various aspects and example embodiments, a plasma processing method and a plasma processing apparatus capable of removing a metal-containing deposit efficiently are provided.
- The foregoing summary is illustrative only and is not intended to be in any way limiting. In addition to the illustrative aspects, embodiments, and features described above, further aspects, embodiments, and features will become apparent by reference to the drawings and the following detailed description.
- In the detailed description that follows, embodiments are described as illustrations only since various changes and modifications will become apparent to those skilled in the art from the following detailed description. The use of the same reference numbers in different figures indicates similar or identical items.
-
FIG. 1 is a simplified cross sectional view schematically illustrating a plasma processing apparatus in which a plasma processing method is performed in accordance with a first example embodiment; -
FIG. 2 is a schematic cross sectional view illustrating a configuration of the plasma processing apparatus in which the plasma processing method is performed in accordance with the first example embodiment; -
FIG. 3 is a flowchart for describing an example processing sequence of the plasma processing method performed in the plasma processing apparatus in accordance with the first example embodiment; -
FIG. 4A is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply a single RF power to a lower electrode; -
FIG. 4B is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply a single RF power to a lower electrode and a negative DC voltage to an upper electrode; -
FIG. 5 is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply dual RF powers to a lower electrode; -
FIG. 6 is a diagram showing processing results in experimental examples 1 to 6 and comparative examples 1 to 12; -
FIG. 7 is a diagram showing processing results in the experimental examples 1 to 6 and the comparative examples 1 to 12; -
FIG. 8 is a diagram showing processing results in experimental examples 7 to 16 and comparative examples 13 and 14; -
FIG. 9 is a diagram showing processing results in experimental examples 17 and 18; -
FIG. 10 is a diagram showing processing results in experimental examples 19 to 33; -
FIG. 11 is a diagram showing processing results in experimental examples 34 and 35 and a comparative example 15; and -
FIG. 12 is a diagram showing processing results in experimental examples 36 to 45 and comparative examples 16 and 17. - In the following detailed description, reference is made to the accompanying drawings, which form a part of the description. In the drawings, similar symbols typically identify similar components, unless context dictates otherwise. Furthermore, unless otherwise noted, the description of each successive drawing may reference features from one or more of the previous drawings to provide clearer context and a more substantive explanation of the current example embodiment. Still, the example embodiments described in the detailed description, drawings, and claims are not meant to be limiting. Other embodiments may be utilized, and other changes may be made, without departing from the spirit or scope of the subject matter presented herein. It will be readily understood that the aspects of the present disclosure, as generally described herein and illustrated in the drawings, may be arranged, substituted, combined, separated, and designed in a wide variety of different configurations, all of which are explicitly contemplated herein.
- Hereinafter, a plasma processing method and a plasma processing apparatus will be described in detail with reference to the accompanying drawings, which form a part hereof. In the drawings, same or corresponding parts will be assigned same reference numerals.
- (Plasma Processing Apparatus in First Example Embodiment)
-
FIG. 1 is a simplified cross sectional view schematically illustrating a plasma processing apparatus in which a plasma processing method in accordance with a first example embodiment is performed. As depicted inFIG. 1 , the plasma processing apparatus as a plasma etching apparatus is configured to apply dual RF powers to an upper electrode and a lower electrode, respectively. That is, the plasma processing apparatus is configured to apply a high frequency power RF for plasma generation having a frequency of, e.g., 40 MHz to anupper electrode 34 from a first highfrequency power supply 89 and, also, apply a high frequency power RF for ion attraction having a frequency of, e.g., 2 MHz to alower electrode 16 from a second highfrequency power supply 90. In this plasma etching apparatus, a variableDC power supply 50 is connected with theupper electrode 34, and a preset DC voltage is applied thereto, as illustrated. -
FIG. 2 is a schematic cross sectional view illustrating a configuration of the plasma processing apparatus in which the plasma processing method in accordance with the first example embodiment is performed. The plasma processing apparatus is configured as a capacitively coupled parallel plate type plasma processing apparatus and includes a substantially cylindrical chamber (processing vessel) 10 made of, but not limited to, anodically oxidized aluminum. Thechamber 10 is grounded. - A columnar
susceptor supporting member 14 is provided on an insulatingplate 12 made of, e.g., ceramics on a bottom of thechamber 10. Thelower electrode 16, which is made of, but not limited to, aluminum, is provided on thesusceptor supporting member 14, and a semiconductor wafer W as a processing target object is mounted on thelower electrode 16. - An
electrostatic chuck 18 configured to attract and hold the semiconductor wafer W by an electrostatic force is provided on a top surface of thelower electrode 16. Theelectrostatic chuck 18 has a structure in which anelectrode 20 made of a conductive film is provided between a pair of insulating layers or insulating sheets. Theelectrode 20 is electrically connected with aDC power supply 22. The insulating layers or insulating sheets may be made of, but not limited to, a dielectric material such as Al2O3 or Y2O3. The semiconductor wafer W is attracted to and held on theelectrostatic chuck 18 by the electrostatic force such as a Coulomb force generated by applying a DC voltage from theDC power supply 22. - A conductive focus ring (correction ring) 24 configured to improve etching uniformity is provided on the top surface of the
lower electrode 16 to surround the electrostatic chuck 18 (semiconductor wafer W). By way of example, but not limitation, the focus ring (correction ring) 24 may be made of silicon. A cylindricalinner wall member 26 made of, for example, quartz is provided on side surfaces of thelower electrode 16 and thesusceptor supporting member 14. - A
coolant path 28 is provided within thesusceptor supporting member 14, for example, along the circumference thereof. A coolant of a preset temperature is supplied into and circulated through thecoolant path 28 from a non-illustrated external chiller unit viapipelines susceptor 16 is controlled to be in the range from, e.g., −20° C. to 200° C. by adjusting the temperature of the coolant. - Further, a heat transfer gas such as, but not limited to, a He gas from a non-illustrated heat transfer gas supply device is supplied into a gap between a top surface of the
electrostatic chuck 18 and a rear surface of the semiconductor wafer W through agas supply line 32. - The
upper electrode 34 is provided above thelower electrode 16 to face thelower electrode 16 in parallel. A plasma generation space is formed between theupper electrode 34 and thelower electrode 16. Theupper electrode 34 serves as a surface, i.e., a surface which faces the semiconductor wafer W on thelower electrode 16 and is in contact with the plasma generation space. - The
upper electrode 34 is supported at a top portion of thechamber 10 via an insulatingmember 42. Theupper electrode 34 faces thelower electrode 16. Theupper electrode 34 includes anelectrode plate 36 having a multiple number of gas discharge holes 37; and anelectrode supporting body 38 configured to support theelectrode plate 36 in a detachable manner. Theelectrode supporting body 38 is made of a conductive material and has a water cooling structure. The conductive material of theelectrode supporting body 38 is, by way of example, but not limitation, aluminum having an anodically oxidized surface. Theelectrode plate 36 is made of a silicon-containing material, for example, silicon. Theelectrode supporting body 38 has therein agas diffusion space 40, and a multiple number of gas throughholes 41 communicating with the gas discharge holes 37 are extended downward from thegas diffusion space 40. - The
electrode supporting body 38 has a gas inlet opening 62 through which a processing gas is introduced into thegas diffusion space 40. The gas inlet opening 62 is connected with agas supply line 64, and thegas supply line 64 is connected with agas supply source 66. Thegas supply line 64 is equipped with a mass flow controller (MFC) 68 and an opening/closingvalve 70 in sequence from the upstream side thereof. As a processing gas for etching, a fluorocarbon gas CxFy such as a CF4 gas or a gas containing CHzFw gas such as CHF3 is introduced into thegas diffusion space 40 from thegas supply source 66 through thegas supply line 64 and then is discharged into the plasma generation space through the gas throughholes 41 and the gas discharge holes 37, in a shower device. That is, theupper electrode 34 serves as a shower head to supply the processing gas. - Further, a processing gas for performing a plasma process on the semiconductor wafer W, a processing gas for use in removing a deposit adhering to a member within the
chamber 10, and so forth are also supplied from the processinggas supply source 66, as will be described later. Detailed description of the processing gases supplied from the processinggas supply source 66 will be elaborated later. - A variable
DC power supply 50 is electrically connected with theupper electrode 34 via a low pass filter (LPF) 46 a. Here, the variableDC power supply 50 may be a bipolar power supply. The variableDC power supply 50 is turned on and off by an on/offswitch 52. A polarity and a current/voltage of the variableDC power supply 50 and an on/off operation of the on/offswitch 52 are controlled by a controller (control device) 51. - The low pass filter (LPF) 46 a is configured to trap high frequency powers supplied from a first high frequency power supply and a second high frequency power supply to be described below. Desirably, the low pass filter (LPF) 46 a may be composed of a LR filter or a LC filter.
- A cylindrical cover (grounding conductor) 10 a is extended upward from a sidewall of the
chamber 10 to be positioned higher than theupper electrode 34. Thecover 10 a has a shield function to suppress a high frequency power from being leaked. - The
upper electrode 34 is electrically connected with a first highfrequency power supply 89 via amatching device 87, and thelower electrode 16 is electrically connected with a second highfrequency power supply 90 via amatching device 88. The first highfrequency power supply 89 is configured to output a high frequency power of a frequency equal to or higher than 27 MHz, e.g., 40 MHz. The second highfrequency power supply 90 is configured to output a high frequency power of a frequency equal to or lower than 13.56 MHz, e.g., 2 MHz. The first highfrequency power supply 89 is for plasma generation, and the second highfrequency power supply 90 is for bias application to the processing target object. - The
matching device 87 and thematching device 88 are configured to match a load impedance with internal (or output) impedances of the first highfrequency power supply 89 and the second highfrequency power supply 90, respectively. Thematching device 87 and thematching device 88 serve to control the internal impedances of the first highfrequency power supply 89 and the second highfrequency power supply 90 to be apparently matched with the load impedances, respectively, when generating plasma. - A
gas exhaust opening 80 is formed on a bottom portion of thechamber 10. Agas exhaust device 84 is connected with thegas exhaust opening 80 via agas exhaust line 82. Thegas exhaust device 84 includes a vacuum pump such as a turbo molecular pump and is configured to depressurize an inside of thechamber 10 to a required vacuum level. Further, a loading/unloading opening 85 for the semiconductor wafer W is formed at the sidewall of thechamber 10, and the loading/unloading opening 85 is opened or closed by agate valve 86. Further, adeposition shield 11 configured to suppress an etching byproduct (deposit) from adhering to thechamber 10 is detachably provided along an inner wall of thechamber 10. That is, thedeposition shield 11 forms a chamber wall. Thedeposition shield 11 is also provided at a periphery of theinner wall member 26. Further, at the bottom portion of thechamber 10, agas exhaust plate 83 is provided between thedeposition shield 11 at the side of the chamber wall and thedeposition shield 11 at the side of theinner wall member 26. Desirably, thedeposition shield 11 and thegas exhaust plate 83 may be made of, but not limited to, aluminum coated with ceramics such as Y2O3. - A conductive member (GND block) 91 which is DC-connected with the ground is provided at a portion of the
deposition shield 11 forming the inner wall of thechamber 10 to be located at a height position substantially same as the height position of the semiconductor wafer W. Thisconductive member 91 has an effect of suppressing an abnormal discharge, as will be described later. Theconductive member 91 may be provided within a gas exhaust path under the lower electrode in a ring shape with respect to the lower electrode. - Individual components of the plasma processing apparatus are connected with and controlled by a controller (overall control device) 95. Further, connected with the
controller 95 is auser interface 96 including a keyboard through which a process manager inputs a command to manage the plasma processing apparatus; a display that visually displays an operational status of the plasma processing apparatus, and so forth. - Also connected with the
controller 95 is astorage unit 97 that stores therein control programs for implementing various processes in the plasma processing apparatus under the control of thecontroller 95, or programs for implementing a process in each component of the plasma processing apparatus according to processing conditions, i.e., processing recipes. The processing recipes may be stored in a hard disk or a semiconductor memory, or may be set at a preset position of thestorage unit 97 while recorded on a computer-readable portable storage medium such as a CD-ROM or a DVD. - A preset recipe may be retrieved from the
storage unit 97 as necessary and executed by thecontroller 95 in response to an instruction from theuser interface 96 or the like, so that a desired process is performed in the plasma processing apparatus under the control of thecontroller 95. - By way of example, the
controller 95 controls the individual components of the plasma processing apparatus to perform a plasma processing method to be described later. As a specific example, under the control of thecontroller 95, a deposit adhering to a member within thechamber 10 and containing at least one of a transition metal and a base metal is removed by being etched with the plasma of a processing gas containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) or a CHzFw gas (z is an integer equal to or less than 3 and w is an integer equal to or less than 3) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Here, the member within thechamber 10 may include, for example, the inner wall of thechamber 10, thelower electrode 16 provided within thechamber 10, and theupper electrode 34 facing thelower electrode 16 within thechamber 10. Hereinafter, the member within thechamber 10 may be referred to as “in-chamber member.” Here, a processing target object may be, by way of example, but not limitation, the semiconductor wafer W. - In the plasma processing apparatus having the above-described configuration, to perform an etching process on the processing target object, the
gate valve 86 is opened, and the semiconductor wafer W as an etching target object is loaded into thechamber 10 through the loading/unloading opening 85 to be mounted on thelower electrode 16. Then, while supplying the processing gas for etching into thegas diffusion space 40 from the processinggas supply source 66 at a preset flow rate and, then, into thechamber 10 through the gas throughholes 41 and the gas discharge holes 37, the inside of thechamber 10 is evacuated by thegas exhaust device 84, and an internal pressure of thechamber 10 is controlled to be a set value in the range from, e.g., 0.1 Pa to 150 Pa. - With the etching gas introduced into the
chamber 10, the high frequency power for plasma generation is applied from the first highfrequency power supply 89 to theupper electrode 34 at a preset power level, and the high frequency power for ion attraction is applied from the second highfrequency power supply 90 to thelower electrode 16 at a certain power level. When necessary, a preset DC voltage is applied to theupper electrode 34 from the variableDC power supply 50. Further, the DC voltage is also applied to theelectrode 20 of theelectrostatic chuck 18 from theDC power supply 22 for theelectrostatic chuck 18, so that the semiconductor wafer W is firmly held on thelower electrode 16 by the electrostatic force. - The processing gas discharged from the gas discharge holes 37 formed in the
electrode plate 36 of theupper electrode 34 is excited into plasma between theupper electrode 34 and thelower electrode 16 by the high frequency power, and a processing target surface of the semiconductor wafer W is etched by radicals or ions in the plasma. - In the plasma processing apparatus, since the high frequency power in a high frequency range (e.g., 10 MHz or higher) is applied to the
upper electrode 34 from the first highfrequency power supply 89, the plasma can be highly densified in a desirable state. Accordingly, it is possible to generate the plasma with the high density under a lower pressure condition. - (Plasma Processing Method in First Example Embodiment)
-
FIG. 3 is a flowchart for describing an example processing sequence of a plasma processing method performed in the plasma processing apparatus in accordance with the first example embodiment. As will be described in detail below, the plasma processing apparatus performs a series of processes on a processing target object including a film containing at least one of a transition metal and a base metal as an etching mask or a stop layer. - Here, the transition metal refers to at least one of, by way of example, but not limitation, Ti, Hf and Ta. Further, the base metal is, for example, Al.
- As depicted in
FIG. 3 , the plasma processing apparatus performs a plasma process in which the processing target object is processed by plasma of a first processing gas (process S101 (Process Processing Target Object Including Film Containing at least One of Transition Metal and Base Metal as Etching Mask or Stop Layer by Plasma)). The first processing gas is, for example, a N2/O2 gas. - A more detailed example will be described. The
controller 95 of the plasma processing apparatus loads the processing target object into thechamber 10 through the loading/unloading opening 85 and thegate valve 86 and mounts the loaded processing target object on theelectrostatic chuck 18. Thereafter, thecontroller 95 supplies the first processing gas into thechamber 10 from the processinggas supply source 66, applies the first high frequency power for plasma generation from the first highfrequency power supply 89 and applies the second high frequency power for ion attraction from the second highfrequency power supply 90. As a result, the plasma of the first processing gas is generated within the chamber, and the processing target object is etched by the plasma. Accordingly, at least one of the transition metal and the base metal is dispersed from the etching mask or the stop layer of the processing target object, and a deposit containing at least one of the transition metal and the base metal adheres to the in-chamber member. - Then, the plasma processing apparatus performs a removing process in which the deposit containing the at least one of the transition metal and the base metal is removed by plasma of a second processing gas containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing a chlorine-based gas and a nitrogen-based gas (process S102 (Remove Deposit Adhering to In-Chamber Member and Containing at least one of Transition Metal and Base Metal by Plasma of Processing Gas Containing CxFy Gas and without Containing Chlorine-based Gas and Nitrogen-based Gas)). The second processing gas containing the CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing the chlorine-based gas and the nitrogen-based gas may be at least one of, but not limited to, a CF4 gas, a CF4/CO gas, a CF4/CO2 gas, a CF4/Ar gas, a CF4/CO/Ar gas, a CF4/CO2/Ar gas, a C2F6 gas, a C2F6/CO gas, a C2F6/CO2 gas, a C2F6/Ar gas, a C2F6/CO/Ar gas and a C2F6/CO2/Ar gas. Further, in the removing process, the internal pressure of the
chamber 10 may be set to be in the range from 4 Pa to 13.3 Pa, desirably, and, more desirably, higher than 6.7 Pa and equal to or less than 13.3 Pa. Further, in the removing process, the high frequency power for plasma generation applied from the first highfrequency power supply 89 and the high frequency power for ion attraction applied from the second highfrequency power supply 90 may be set to be equal to or larger than 500 W and equal to or less than 2000 W, desirably. Furthermore, in case that the second processing gas used in the removing process contains CF4, it may be desirable that a flow rate of the CF4 is set to be equal to or larger than 300 sccm and equal to or less than 600 sccm. Further, in case that the second processing gas used in the removing process contains CO, it may be desirable that a flow rate of the CO is set to be equal to or larger than 150 sccm and equal to or less than 300 sccm. Further, in case that the second processing gas used in the removing process contains Ar, it may be desirable that a flow rate of the Ar is set to be equal to or larger than 50 sccm and equal to or less than 500 sccm. - A more detailed example will be described. The
controller 95 of the plasma processing apparatus unloads the processing target object from thechamber 10 through the loading/unloading opening 85 and thegate valve 86. Then, thecontroller 95 supplies the second processing gas into thechamber 10 from the processinggas supply source 66, applies the first high frequency power for plasma generation from the first highfrequency power supply 89 and applies the second high frequency power for ion attraction from the second highfrequency power supply 90. As a result, the deposit containing the at least one of the transition metal and the base metal, which adheres to the in-chamber member, reacts with the plasma of the second processing gas, so that the deposit is removed from the in-chamber member. - As stated above, in accordance with the first example embodiment, the deposit containing at least one of the transition metal and the base metal is removed by the plasma of the processing gas containing the CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing the chlorine-based gas and the nitrogen-based gas. As a result, in case that the deposit contains a metal having resistance to the plasma of the chlorine-based gas or the nitrogen-based gas, the reaction between the plasma of the processing gas and the deposit can be accelerated. That is, the deposit containing the metal can be removed efficiently. Further, in accordance with the first example embodiment, since the deposit can be removed by performing the etching process without using a corrosion gas such as the chlorine-based gas or the nitrogen-based gas, modification of the specification of the apparatus for improving corrosion resistance or the like may not be required.
- Furthermore, in accordance with the first example embodiment, the processing gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas may be at least one of, but not limited to, a CF4 gas, a CF4/CO gas, a CF4/CO2 gas, a CF4/Ar gas, a CF4/CO/Ar gas, a CF4/CO2/Ar gas, a C2F6 gas, a C2F6/CO gas, a C2F6/CO2 gas, a C2F6/Ar gas, a C2F6/CO/Ar gas, and a C2F6/CO2/Ar gas. Thus, the deposit containing a metal including at least one of the transition metal and the base metal can be removed by plasma etching more efficiently.
- In addition, according to the first example embodiment, the transition metal is at least one of Ti, Hf and Ta. Accordingly, even if a deposit containing at least one of Ti, Hf and Ta adheres to the in-chamber member of the plasma processing apparatus as a result of plasma-processing the processing target object including a film containing at least one of Ti, Hf and Ta as a mask or a stop layer, it is still possible to remove the deposit efficiently by plasma etching.
- Further, in accordance with the first example embodiment, the base metal is Al. Accordingly, even if a deposit containing Al adheres to the in-chamber member of the plasma processing apparatus as a result of plasma-processing the processing target object including an Al-containing film as a mask or a stop layer, it is still possible to remove the deposit efficiently by plasma etching.
- Furthermore, in accordance with the first example embodiment, by applying the high frequency powers to the
lower electrode 16 and theupper electrode 34 facing each other within thechamber 10, respectively, the plasma of the processing gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas is generated, and the deposit is removed by the generated plasma. As a result, an absolute value of a self-bias voltage in the surface of the in-chamber member can be increased, so that the deposit adhering to the in-chamber member can be appropriately sputtered and a surface of the in-chamber member can be cleaned. - In the above, the plasma processing method and the plasma processing apparatus in accordance with the first example embodiment have been described. However, the example embodiment may not be limited thereto. Below, other example embodiments will be described.
- (DC Voltage)
- For example, in a removing process, it is possible to remove a deposit from the in-chamber member, which is a target of which deposit is removed (“deposit removal target”), by plasma of a processing gas containing a CxFy gas and without containing a chlorine-based gas and a nitrogen-based gas while applying a negative DC voltage to the in-chamber member. Desirably, the negative DC voltage applied to the in-chamber member is equal to or less than −100 V.
- A more detailed example will be explained. Here, it is assumed that the in-chamber member as the deposit removal target is the
upper electrode 34. Thecontroller 95 of the plasma processing apparatus unloads a processing target object from thechamber 10 through the loading/unloading opening 85 and thegate valve 86. Then, thecontroller 95 supplies a second processing gas into thechamber 10 from the processinggas supply source 66, applies a first high frequency power for plasma generation from the first highfrequency power supply 89 and applies a second high frequency power for ion attraction from the second highfrequency power supply 90. Here, the second processing gas is, by way of example, but not limitation, a gas containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing a chlorine-based gas and a nitrogen-based gas. Here, at least one of a CF4/Ar gas, a CF4/CO/Ar gas, a CF4/CO2/Ar gas, a C2F6/Ar gas, a C2F6/CO/Ar gas, and a C2F6/CO2/Ar gas is supplied into thechamber 10 as the second processing gas. Further, thecontroller 95 connects the variableDC power supply 50 with theupper electrode 34 as the deposit removal target and applies a preset DC voltage to theupper electrode 34. That is, thecontroller 95 applies a negative DC voltage having preset polarity and magnitude to theupper electrode 34 from the variableDC power supply 50 when plasma is generated. More desirably, the negative DC voltage is applied to theupper electrode 34 from the variableDC power supply 50 such that a self-bias voltage (Vdc) in the surface of theelectrode plate 36 is increased to achieve a sputtering effect on the surface of theelectrode plate 36 serving as the surface of theupper electrode 34, i.e., such that an absolute value of the self-bias voltage Vdc in the surface of theupper electrode 34 is increased. Here, as the negative DC voltage, a DC voltage equal to or less than, e.g., −100 V is applied to theupper electrode 34. - As a result, collision of ions against the surface of the
upper electrode 34 is accelerated, so that the amount of the deposit removed from the surface of theupper electrode 34 is increased. By way of example, argon ions in the plasma may collide with the surface of theupper electrode 34, so that the deposit adhering to theupper electrode 34 would be appropriately sputtered and, thus, the surface of theupper electrode 34 can be cleaned. - (Kinds of Processing Gas)
- In the first example embodiment as described above, the gas containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas is used as a processing gas for removing the deposit. However, the processing gas may not be limited thereto. By way of example, a gas containing a CHzFw gas (z is an integer equal to or less than 3 and w is also an integer equal to or less than 3) and without containing the chlorine-based gas and the nitrogen-based gas may also be used as the processing gas for removing the deposit. In this case, in the removing process, the plasma processing apparatus removes the deposit by plasma of the processing gas containing the CHzFw gas and without containing the chlorine-based gas and the nitrogen-based gas while applying the negative DC voltage to the in-chamber member which is a deposit removal target. The processing gas containing the CHzFw gas and without containing the chlorine-based gas and the nitrogen-based gas may be at least one of, but not limited to, a CHF3 gas, a CHF3/Ar/O2 gas, a CH2F2 gas, a CH2F2/Ar/O2 gas, a CH3F gas, and a CH3F/Ar/O2 gas. Further, the negative DC voltage applied to the in-chamber member is desirably equal to or less than −100 V.
- A more detailed example will be explained. Here, it is assumed that the in-chamber member as the deposit removal target is the
upper electrode 34. Thecontroller 95 of the plasma processing apparatus unloads a processing target object from thechamber 10 through the loading/unloading opening 85 and thegate valve 86. Then, thecontroller 95 supplies a second processing gas into thechamber 10 from the processinggas supply source 66, applies a first high frequency power for plasma generation from the first highfrequency power supply 89 and applies a second high frequency power for ion attraction from the second highfrequency power supply 90. Here, the second processing gas is, by way of example, but not limitation, a gas containing a CHzFw gas (z is an integer equal to or less than 3 and w is also an integer equal to or less than 3) and without containing a chlorine-based gas and a nitrogen-based gas. Here, at least one of a CHF3/Ar/O2 gas, a CH2F2/Ar/O2 gas, a CH3F gas, and a CH3F/Ar/O2 gas is supplied into thechamber 10 as the second processing gas. Further, thecontroller 95 connects the variableDC power supply 50 with theupper electrode 34 as the deposit removal target and applies a preset DC voltage to theupper electrode 34. That is, thecontroller 95 applies a negative DC voltage having preset polarity and magnitude to theupper electrode 34 from the variableDC power supply 50 when plasma is generated. More desirably, the negative DC voltage is applied to theupper electrode 34 from the variableDC power supply 50 such that a self-bias voltage (Vdc) in the surface of theelectrode plate 36 is increased to achieve a sputtering effect on the surface of theelectrode plate 36 serving as the surface of theupper electrode 34, i.e., such that an absolute value of the self-bias voltage Vdc in the surface of theupper electrode 34 is increased. Here, as the negative DC voltage, a DC voltage equal to or less than, e.g., −100 V is applied to theupper electrode 34. - As a result, collision of ions against the surface of the
upper electrode 34 is accelerated, so that the amount of the deposit removed from the surface of theupper electrode 34 is increased. By way of example, argon ions in the plasma may collide with the surface of theupper electrode 34, so that the deposit adhering to theupper electrode 34 would be appropriately sputtered and, thus, the surface of theupper electrode 34 can be cleaned. - (Kinds of Plasma Processing Apparatus) In the first example embodiment, the plasma etching apparatus configured to apply a single RF power and a DC voltage to the upper electrode and apply a single RF power to the lower electrode, as shown in
FIG. 1 , is used as the plasma processing apparatus in which the plasma processing method is performed. However, the plasma processing apparatus may not be limited thereto. By way of example, a plasma etching apparatus configured to apply a single RF power to a lower electrode, a plasma etching apparatus configured to apply a single RF power to a lower electrode and apply a negative DC voltage to an upper electrode, a plasma etching apparatus configured to apply dual RF powers to a lower electrode and a DC voltage to an upper electrode, a plasma etching apparatus configured to apply dual RF powers to an upper electrode and a lower electrode, respectively, and apply a DC voltage to the upper electrode, an ICP (Inductively Coupled Plasma) etching apparatus, a microwave plasma etching apparatus, or the like may also be applicable. -
FIG. 4A is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply a single RF power to a lower electrode. InFIG. 4A , the same parts as those shown inFIG. 1 are assigned same reference numerals, and redundant description is omitted. As depicted inFIG. 4A , the plasma etching apparatus configured to apply a single RF power to the lower electrode applies a high frequency (RF) power of, e.g., 40 MHz for plasma generation to alower electrode 16 from a first highfrequency power supply 89. In this configuration, a variableDC power supply 50 and a second highfrequency power supply 90 are omitted. -
FIG. 4B is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply a single RF power to a lower electrode and a negative DC voltage to an upper electrode. InFIG. 4B , the same parts as those shown inFIG. 1 are assigned same reference numerals, and redundant description is omitted. The plasma etching apparatus shown inFIG. 4B is configured to apply a high frequency (RF) power of, e.g., about 40 MHz for plasma generation to alower electrode 16 from a first highfrequency power supply 89. Further, as depicted inFIG. 4B , a variableDC power supply 50 is connected with anupper electrode 34, and a preset DC voltage is applied to theupper electrode 34. In this configuration, a second highfrequency power supply 90 is omitted. -
FIG. 5 is a simplified cross sectional view schematically illustrating a plasma etching apparatus configured to apply dual RF powers to a lower electrode. InFIG. 5 , the same parts as those shown inFIG. 1 are assigned same reference numerals, and redundant description is omitted. As shown inFIG. 5 , the plasma etching apparatus depicted inFIG. 5 is configured to apply, to alower electrode 16, a high frequency (RF) power of, e.g., 40 MHz for plasma generation from a first highfrequency power supply 89 and a high frequency (RF) power of, e.g., 2 MHz for ion attraction from a second highfrequency power supply 90. Further, as illustrated inFIG. 5 , a variableDC power supply 50 is connected with anupper electrode 34, and a preset DC voltage is applied to theupper electrode 34. - Below, the above-stated plasma processing method will be discussed in further detail with reference to experimental examples. Here, however, the plasma processing method is not limited to the experimental examples.
- A semiconductor wafer W including a film containing a transition metal X is plasma-processed. Then, there is performed a removing process in which a deposit containing the transition metal X and adhering to an
upper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply dual RF powers to an upper electrode and a lower electrode, respectively
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 500 W/250 W
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Time: 180 seconds
- Further, in the experimental examples 1 to 4, following metals are used as the transition metal X.
- Experimental examples 1 and 2: Ti (Titanium)
- Experimental examples 3 and 4: Hf (Hafnium)
- In addition, in the experimental examples 1 to 4, following gases having flow rates as specified below are used as the processing gas G1.
- Experimental examples 1 and 3: CF4/CO=300 sccm/300 sccm
- Experimental examples 2 and 4: CF4/CO/Ar=300 sccm/300 sccm/300 sccm
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - A semiconductor wafer W including a film containing a transition metal X is plasma-processed. Then, there is performed a removing process in which, while applying a negative DC voltage to an
upper electrode 34, a deposit containing the transition metal X and adhering to anupper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply dual RF powers to the upper electrode and the lower electrode, respectively
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 500 W/250 W
- DC voltage applied to upper electrode: −500 V
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Time: 180 seconds
- Further, in the experimental examples 5 and 6, following metals are used as the transition metal X.
- Experimental example 5: Ti (Titanium)
- Experimental example 6: Hf (Hafnium)
- In addition, in the experimental examples 5 and 6, following gases having flow rates as specified below are used as the processing gas G1.
- Experimental examples 5 and 6: CF4/CO/Ar=300 sccm/300 sccm/300 sccm
- After the completion of the removing process in each comparative example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - In comparative examples 1 to 6, unlike in the experimental examples 1 and 2, there is performed a removing process in which a deposit adhering to an
upper electrode 34 and containing a transition metal X is removed by plasma of a processing gas G2 containing a chlorine-based gas or a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply dual RF powers to a lower electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 1000 W/250 W
- Temperature (upper/sidewall/lower): 100° C./80° C./25° C.
- Time: 180 seconds
- In addition, in the comparative examples 1 to 6, following gases having flow rates as specified below are used as the processing gas G2. The other processing conditions in the comparative examples 1 to 6 are the same as those in the experimental examples 1 and 2.
- Comparative example 1: NF3=120 sccm
- Comparative example 2: BCl3=200 sccm
- Comparative example 3: Cl2=200 sccm
- Comparative example 4: BCl3/Ar=125 sccm/75 sccm
- Comparative example 5: BCl3/Cl2=125 sccm/75 sccm
- Comparative example 6: Cl2/NF3=150 sccm/50 sccm
- In comparative examples 7 to 12, unlike in the experimental examples 3 and 4, there is performed a removing process in which a deposit adhering to an
upper electrode 34 and containing a transition metal X is removed by plasma of a processing gas G2 containing a chlorine-based gas or a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of the plasma processing apparatus: a plasma etching apparatus configured to apply dual RF powers to a lower electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 1000 W/250 W
- Temperature (upper/sidewall/lower): 100° C./80° C./25° C.
- Time: 180 seconds
- In addition, in the comparative examples 7 to 12, following gases having flow rates as specified below are used as the processing gas G2. The other processing conditions in the comparative examples 7 to 12 are the same as those in the experimental examples 3 and 4.
- Comparative example 7: NF3=120 sccm
- Comparative example 8: BCl3=200 sccm
- Comparative example 9: Cl2=200 sccm
- Comparative example 10: BCl3/Ar=125 sccm/75 sccm
- Comparative example 11: BCl3/Cl2=125 sccm/75 sccm
- Comparative example 12: Cl2/NF3=150 sccm/50 sccm
- (Processing Results in Experimental Examples 1 to 6 and Comparative Examples 1 to 12)
-
FIG. 6 andFIG. 7 are diagrams showing processing results in the experimental examples 1 to 6 and the comparative examples 1 to 12. Traceddrawings 211 ofFIG. 6 andFIG. 7 show surface states of Si substrates for testing before performing the removing processes in the experimental examples 1 and 2 and the comparative examples 1 to 6. Traceddrawings 221 show a surface state of a Si substrate for testing before performing the removing processes in the experimental examples 3 and 4 and the comparative examples 7 to 12. Further, traceddrawings FIG. 6 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 1 to 4, respectively. Traceddrawings FIG. 6 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 5 and 6, respectively. Further, traced diagrams 312 to 317 ofFIG. 7 show surface states of the Si substrates for testing after performing the removing processes in the comparative examples 1 to 6, respectively. Traceddrawings 322 to 327 ofFIG. 7 show surface states of the Si substrates for testing after performing the removing processes in the comparative examples 7 to 12, respectively. In each traced drawing, a metal contamination amount (×1010 atms/cm2) is also specified. - As depicted in
FIG. 6 andFIG. 7 , in the removing processes of removing Ti, the metal contamination amounts are found to be reduced in the experimental examples 1 and 2 in which the processing gas G1 containing the CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing a chlorine-based gas and a nitrogen-based gas is used, as compared to the comparative examples 1 to 6 in which the processing gas G2 containing the chlorine-based gas or the nitrogen-based gas is used. That is to say, in the experimental examples 1 and 2, a deposit containing Ti as the transition metal can be removed efficiently, as compared to the comparative examples 1 to 6. - Further, as depicted in
FIG. 6 andFIG. 7 , in the removing processes of removing Hf, the metal contamination amounts are found to be reduced in the experimental examples 3 and 4 in which the processing gas G1 containing the CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and without containing a chlorine-based gas and a nitrogen-based gas is used, as compared to the comparative examples 7 to 12 in which the processing gas G2 containing the chlorine-based gas or the nitrogen-based gas is used. That is to say, in the experimental examples 3 and 4, a deposit containing Hf as the transition metal can be removed efficiently, as compared to the comparative examples 7 to 12. - Moreover, as can be seen from
FIG. 6 , in the removing processes of removing Ti, the metal contamination amount in the experimental example 5 in which the negative DC voltage is applied to theupper electrode 34 is found to be reduced to the substantially same level as those in the experimental examples 1 and 2 in which the negative DC voltage is not applied to theupper electrode 34. - In addition, as depicted in
FIG. 6 , in the removing processes of removing Hf, the metal contamination amount in the experimental example 6 in which the negative DC voltage is applied to theupper electrode 34 is found to be reduced to the substantially same level as those in the experimental examples 3 and 4 in which the negative DC voltage is not applied to theupper electrode 34. - In experimental examples 7 to 10, unlike in the experimental examples 3 and 4, following gases having flow rates as specified below are utilized as the processing gas G1. The other processing conditions are the same as those in the experimental examples 1 and 2.
- Experimental example 7: CF4/Ar=300 sccm/300 sccm
- Experimental example 8: CF4/CO2/Ar=300 sccm/300 sccm/300 sccm
- Experimental example 9: CF4/CO/Ar=100 sccm/100 sccm/100 sccm
- Experimental example 10: CF4=300 sccm
- A semiconductor wafer W including a film containing Al (aluminum), which is a base metal, is plasma-processed. Then, there is performed a removing process in which a deposit containing Al and adhering to an
upper electrode 34 is removed by being etched with plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply dual RF powers to an upper electrode and a lower electrode, respectively
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 500 W/250 W
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Further, in the experimental examples 11 to 16, following gases having flow rates as specified below are used as the processing gas G1.
- Experimental example 11: CF4/CO/Ar=300 sccm/300 sccm/300 sccm
- Experimental example 12: CF4/Ar=300 sccm/300 sccm
- Experimental example 13: CF4/CO=300 sccm/300 sccm
- Experimental example 14: CF4/CO2/Ar=300 sccm/300 sccm/300 sccm
- Experimental example 15: CF4/CO/Ar=100 sccm/100 sccm/100 sccm
- Experimental example 16: CF4=300 sccm
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - In a comparative example 13, unlike in the experimental example 9, there is performed a removing process in which a deposit adhering to the
upper electrode 34 and containing Hf, which is a transition metal, is removed by being etched with plasma of a processing gas containing a nitrogen-based gas, i.e., NF3/CO/Ar=100 sccm/100 sccm/100 sccm. The other processing conditions are the same as those in the experimental example 9. - In a comparative example 14, unlike in the experimental example 15, there is performed a removing process in which a deposit adhering to the
upper electrode 34 and containing Al, which is a base metal, is removed by being etched by plasma of a processing gas containing a nitrogen-based gas, i.e., NF3/CO/Ar=100 sccm/100 sccm/100 sccm. The other processing conditions are the same as those in the experimental example 15. - (Processing Results in Experimental Examples 7 to 16 and Comparative Examples 13 and 14)
-
FIG. 8 is a diagram showing processing results in the experimental examples 7 to 16 and the comparative examples 13 and 14. A traced drawing 221 ofFIG. 8 corresponds to the traced drawing 221 inFIG. 6 andFIG. 7 . Further, a traced drawing 231 inFIG. 8 shows surface states of Si substrates for testing before performing the removing processes in the experimental examples 7 to 16. Traceddrawings drawings 422 to 427 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 11 to 16. Traceddrawings - As depicted in
FIG. 6 andFIG. 8 , by using CF4/Ar in the removing processes of removing Hf or Al, it is possible to reduce the metal contamination amounts to the substantially same level as those in case of using CF4/CO or CF4/CO/Ar. - Further, as shown in
FIG. 6 andFIG. 8 , by using CF4/CO2/Ar in the removing processes of removing Hf or Al, it is possible to reduce the metal contamination amounts to the substantially same level as those in case of using CF4/CO or CF4/CO/Ar. - Moreover, as shown in
FIG. 6 andFIG. 8 , by using CF4 in the removing processes of removing Hf or Al, it is possible to reduce the metal contamination amounts to the substantially same level as those in case of using CF4/CO or CF4/CO/Ar. - In addition, as depicted in
FIG. 8 , by using CF4/CO/Ar in the removing processes of removing Hf or Al, the metal contamination amounts are found to be reduced, as compared to the case of using NF3/CO/Ar. That is to say, in the experimental examples 9 and 15, a deposit containing Hf as a transition metal or a deposit containing Al as a base metal can be removed efficiently, as compared to the comparative examples 13 and 14. - In experimental examples 17 and 18, unlike in the experimental examples 1 to 16, a series of processes are performed by using a plasma etching apparatus configured to apply a single RF power to a lower electrode instead of the plasma etching apparatus configured to apply dual RF powers to the upper electrode and the lower electrode, respectively. That is, a semiconductor wafer W including a film containing Hf, which is a transition metal, is plasma-processed. Then, there is performed a removing process in which a deposit containing Hf and adhering to an
upper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply a single RF power to a lower electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power: 1000 W
- Temperature (upper/sidewall/lower): 100° C./60° C./0° C.
- Time: 180 seconds
- Further, in the experimental examples 17 and 18, following gases having flow rates as specified below are used as the processing gas G1.
- Experimental example 17: CF4/CO/Ar=300 sccm/300 sccm/300 sccm
- Experimental example 18: CF4/CO=300 sccm/300 sccm
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - (Processing Results in Experimental Examples 17 and 18)
-
FIG. 9 is a diagram showing processing results in the experimental examples 17 and 18. A traced drawing 221 ofFIG. 9 corresponds to the traceddrawings 221 ofFIG. 6 andFIG. 7 . Further, traceddrawings - As shown in
FIG. 9 , when the plasma etching apparatus configured to apply a single RF power to the lower electrode is used, the metal contamination amounts are also found to be reduced, as in the case of using the plasma etching apparatus configured to apply dual RF powers to the upper electrode and the lower electrode, respectively. That is, even when a self-bias voltage is not generated in the surface of theupper electrode 34, it is still possible to efficiently remove a deposit containing Hf which is a transition metal. - A semiconductor wafer W including a film containing a transition metal X, is plasma-processed. Then, there is performed a removing process in which a deposit containing the transition metal X and adhering to an
upper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas while applying a negative DC voltage to theupper electrode 34. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configure to apply dual RF powers to an upper electrode and a lower electrode, respectively
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 500 W/250 W
- DC voltage applied to upper electrode: −500 V
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Time: 180 seconds
- Processing gas and flow rate of processing gas: CF4/CO/Ar=100 sccm/100 sccm/100 sccm
- Further, in the experimental examples 19 to 21, following metals are used as the transition metal X.
- Experimental example 19: Ti (Titanium)
- Experimental example 20: Hf (Hafnium)
- Experimental example 21: Ta (Tantalum)
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - In experimental examples 22 to 33, unlike in the experimental examples 19 to 21, there is performed a removing process in which, while applying a negative DC voltage to an
upper electrode 34, a deposit containing a transition metal X and adhering to theupper electrode 34 is removed by using plasma of a processing gas G3 containing a CHzFw gas (z and w are integers equal to or less than 3) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configure to apply dual RF powers to an upper electrode and a lower electrode, respectively
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 500 W/250 W
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Time: 180 seconds
- Further, in the experimental examples 22 to 33, following metals are used as the transition metal X.
- Experimental examples 22, 25, 28, 31: Ti (Titanium)
- Experimental examples 23, 26, 29, 32: Hf (Hafnium)
- Experimental examples 24, 27, 30, 33: Ta (Tantalum)
- Further, in the experimental examples 22 to 33, following gases having flow rates as specified below are used as the processing gas G3.
- Experimental examples 22 to 24 and 31 to 33: CHF3/Ar/O2=100 sccm/100 sccm/100 sccm
- Experimental examples 25 to 27: CHF3/Ar/O2=100 sccm/500 sccm/100 sccm
- Experimental examples 28 to 30: CHF3/Ar/O2=100 sccm/800 sccm/100 sccm
- Furthermore, in the experimental examples 22 to 33, DC voltages as specified below are applied to the
upper electrode 34. - Experimental examples 22 to 30: −400 V
- Experimental examples 31 to 33: −900 V
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - (Processing Results in Experimental Examples 19 to 33)
-
FIG. 10 is a diagram showing processing results in the experimental examples 19 to 33. A traced drawing 711 ofFIG. 10 shows a surface state of a Si substrate for testing before performing the removing processes in the experimental examples 19, 22, 25, 28 and 31. A traced drawing 721 shows a surface state of the Si substrate for testing before performing the removing processes in the experimental examples 20, 23, 26, 29 and 32. Further, a traced drawing 731 shows a surface state of the Si substrate for testing before performing the removing processes in the experimental examples 21, 24, 27, 30 and 33. Further, traceddrawings 712 to 716 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 19, 22, 25, 28 and 31, respectively. Traceddrawings 722 to 726 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 20, 23, 26, 29 and 32, respectively. Further, traceddrawings 732 to 736 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 21, 24, 27, 30 and 33, respectively. In each traced drawing, a metal contamination amount (×1010 atms/cm2) is also specified. - As can be seen from
FIG. 10 , in the removing processes of removing Ti, Hf or Ta as the transition metal, by applying the negative DC voltage to theupper electrode 34, the metal contamination amounts can be reduced regardless of the kind of the transition metal. - Further, as shown in
FIG. 10 , in the removing processes of removing Ti, the metal contamination amounts in the experimental examples 22, 25, 28 and 31 in which the processing gas G3 containing the CHzFw gas and without containing the chlorine-based gas and the nitrogen-based gas is used are found to be reduced to the substantially same level as that of the experimental example 19 in which the processing gas G1 containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas is used. - Moreover, as shown in
FIG. 10 , in the removing processes of removing Hf, the metal contamination amounts in the experimental examples 23, 26, 29 and 32 in which the processing gas G3 containing the CHzFw gas and without containing the chlorine-based gas and the nitrogen-based gas is used are found to be reduced to the substantially same level as that of the experimental example 20 in which the processing gas G1 containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas is used. - In addition, as can be seen from
FIG. 10 , in the removing processes of removing Ta, the metal contamination amounts in the experimental examples 24, 27, 30 and 33 in which the processing gas G3 containing the CHzFw gas and without containing the chlorine-based gas and the nitrogen-based gas is used are found to be reduced to the substantially same level as that of the experimental example 21 in which the processing gas G1 containing the CxFy gas and without containing the chlorine-based gas and the nitrogen-based gas is used. - A semiconductor wafer W including a film containing Al (aluminum), which is a base metal, is plasma-processed. Then, there is performed a removing process in which, while applying a negative DC voltage to an
upper electrode 34, a deposit containing Al and adhering to theupper electrode 34 is removed by using plasma of a processing gas G3 containing a CHzFw gas (z and w are integers equal to or less than 3) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configure to apply dual RF powers to a lower electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power (HF/LF): 1000 W/250 W
- Temperature (upper/sidewall/lower): 60° C./60° C./20° C.
- Time: 180 seconds
- Processing gas and flow rate of processing gas: CHF3/Ar/O2=100 sccm/100 sccm/100 sccm
- Further, in the experimental examples 34 and 35, DC voltages as specified below are applied to the
upper electrode 34. - Experimental example 34: −150 V
- Experimental example 35: −300 V
- After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - In a comparative example 15, unlike in the experimental examples 34 and 35, a negative DC voltage is not applied to an
upper electrode 34 in a removing process. The other processing conditions are the same as those in the experimental examples 34 and 35. - (Processing Results in Experimental Examples 34 and 34 and Comparative Example 15)
-
FIG. 11 is a diagram showing processing results in the experimental examples 34 and 35 and the comparative example 15. A traced drawing 741 ofFIG. 11 shows a surface state of a Si substrate for testing before performing the removing processes in the experimental examples 34 and 35 and the comparative example 15. A traced drawing 742 shows a surface state of the Si substrate for testing after performing the removing processes in the comparative example 15. Further, traceddrawings - As shown in
FIG. 11 , in the removing processes of removing Al, the metal contamination amounts are found to be reduced in the experimental examples 34 and 35 in which the negative DC voltage is applied to theupper electrode 34, as compared to that in case of the comparative example 15 in which a negative DC voltage is not applied to theupper electrode 34. That is, in the experimental examples 34 and 35, it is possible to efficiently remove a deposit containing Al, which is a base metal, as compared to the comparative example 15. - A semiconductor wafer W including a film containing Al, which is a base metal, is plasma-processed. Then, there is performed a removing process in which, while applying a negative DC voltage to an
upper electrode 34, a deposit containing Al and adhering to theupper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply a single RF power to a lower electrode and a negative DC voltage to an upper electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power: 1 kW
- Temperature (upper/sidewall/lower): 20° C./-/20° C.
- Time: 180 seconds
- Processing gas and flow rate of processing gas: CF4=500 sccm
- Further, in the experimental examples 36 to 39, DC voltages as specified below are applied to the
upper electrode 34. - Experimental example 36: −100 V
- Experimental example 37: −150 V
- Experimental example 38: −300 V
- Experimental example 39: −500 V
- A semiconductor wafer W including a film containing Hf, which is a transition metal, is plasma-processed. Then, there is performed a removing process in which, while applying a negative DC voltage to an
upper electrode 34, a deposit containing Hf and adhering to theupper electrode 34 is removed by using plasma of a processing gas G1 containing a CxFy gas (x is an integer equal to or less than 2 and y is an integer equal to or less than 6) and, also, without containing a chlorine-based gas and a nitrogen-based gas. Processing conditions for the removing process are as follows. - Kind of plasma processing apparatus: a plasma etching apparatus configured to apply a single RF power to a lower electrode and a negative DC voltage to an upper electrode
- Pressure: 4.0 Pa (30 mT)
- High frequency power: 1 kW
- Temperature (upper/sidewall/lower): 20° C./-/20° C.
- Time: 180 seconds
- Processing gas and flow rate of processing gas: CF4=500 sccm
- Further, in the experimental examples 40 to 44, DC voltages as specified below are applied to the
upper electrode 34. - Experimental example 40: −50 V
- Experimental example 41: −100 V
- Experimental example 42: −150 V
- Experimental example 43: −300 V
- Experimental example 44: −500 V
- In an experimental example 45, unlike in the experimental examples 40 to 44, a negative DC voltage is not applied to an
upper electrode 34 in a removing process. The other processing conditions are the same as those in the experimental examples 40 to 44. - After the completion of the removing process in each experimental example, a metal contamination amount on the surface of the
upper electrode 34 is measured. The metal contamination amount is an index indicating an adhesion amount of metal atoms per a unit area. In measuring the metal contamination amount, the metal contamination amount on the surface of theupper electrode 34 is not directly measured. That is, a Si substrate for testing is provided on the surface of theupper electrode 34, and a metal contamination amount on the surface of the Si substrate for testing is measured as the metal contamination amount on the surface of theupper electrode 34. - In a comparative example 16, unlike in the experimental examples 36 to 39, a negative DC voltage is not applied to an
upper electrode 34 in a removing process. The other processing conditions are the same as those in the experimental examples 36 to 39. - In a comparative example 17, unlike in the experimental examples 36 to 39, a negative DC voltage of −50 V is applied to an
upper electrode 34 in a removing process. The other processing conditions are the same as those in the experimental examples 36 to 39. - (Processing Results in Experimental Examples 36 to 45 and Comparative Examples 16 and 17)
-
FIG. 12 is a diagram showing processing results in the experimental examples 36 to 45 and the comparative examples 16 and 17. A traced drawing 761 ofFIG. 12 shows a surface state of a Si substrate for testing before performing the removing processes in the experimental examples 36 to 39 and the comparative examples 16 and 17. A traced drawing 771 shows a surface state of the Si substrate for testing before performing the removing processes in the experimental examples 40 to 45. Further, traceddrawings drawings 764 to 767 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 36 to 39. Further, traceddrawings 773 to 77 show surface states of the Si substrates for testing after performing the removing processes in the experimental examples 40 to 44, respectively. A traced drawing 772 shows a surface state of the Si substrate for testing after performing the removing process in the experimental example 45. In each traced drawing, a metal contamination amount (×1010 atms/cm2) is also specified. - As shown in
FIG. 12 , in the removing processes of removing Al, the metal contamination amounts are found to be reduced in the experimental examples 36 to 39 in which the negative DC voltage equal to or less than −100 V is applied to theupper electrode 34, as compared to the comparative example 16 in which a negative DC voltage is not applied to theupper electrode 34 and in the comparative example 17 in which the negative DC voltage higher than −100 V is applied to theupper electrode 34. That is, it is found out that the deposit containing Al as a base metal can be removed efficiently by setting the negative DC voltage to be applied to theupper electrode 34 to be equal to or less than −100 V. - Further, as depicted in
FIG. 12 , in the removing processes of removing Hf, the metal contamination amounts are found to be reduced, regardless of whether or not the negative DC voltage is applied to theupper electrode 34. - From the foregoing, it will be appreciated that various embodiments of the present disclosure have been described herein for purposes of illustration, and that various modifications may be made without departing from the scope and spirit of the present disclosure. Accordingly, the various embodiments disclosed herein are not intended to be limiting, with the true scope and spirit being indicated by the following claims.
Claims (4)