US20130037183A1 - Thermal treatment for the stress-relief of titanium alloy parts - Google Patents

Thermal treatment for the stress-relief of titanium alloy parts Download PDF

Info

Publication number
US20130037183A1
US20130037183A1 US13/500,826 US201013500826A US2013037183A1 US 20130037183 A1 US20130037183 A1 US 20130037183A1 US 201013500826 A US201013500826 A US 201013500826A US 2013037183 A1 US2013037183 A1 US 2013037183A1
Authority
US
United States
Prior art keywords
tool
titanium alloy
temperature
creeping
thermal treatment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/500,826
Other languages
English (en)
Inventor
Christophe Daffos
Michel Miquel
Laurent Foucher
Vincent Albert
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Aubert and Duval SA
Original Assignee
Aubert and Duval SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Aubert and Duval SA filed Critical Aubert and Duval SA
Assigned to AUBERT & DUVAL reassignment AUBERT & DUVAL ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: ALBERT, VINCENT, DAFFOS, CHRISTOPHE, FOUCHER, LAURENT, MIQUEL, MICHEL
Publication of US20130037183A1 publication Critical patent/US20130037183A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
    • C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
    • C22F1/16—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of other metals or alloys based thereon
    • C22F1/18—High-melting or refractory metals or alloys based thereon
    • C22F1/183—High-melting or refractory metals or alloys based thereon of titanium or alloys based thereon

Definitions

  • the invention relates to a stress thermal relaxation treatment and to a shaping tool for carrying out this relaxation thermal treatment.
  • the invention relates in particular to a thermal treatment process for slender parts or alternatively parts which are more massive but which comprise significant variations in cross section made of titanium alloy, in particular of the alpha-beta type, that is to say for which the microstructure exhibits, at ambient temperature, both the alpha phase and the beta phase.
  • a widespread alpha-beta alloy is in particular the alloy known under the trade names TA6V or TA6V4 or also Ti-6Al-4V.
  • Alpha-beta titanium alloys and in particular of TA6V type make it possible to produce parts having a good compromise between mechanical strength and toughness, in addition to their low density and their good resistance to corrosion.
  • alloys of TA6V type are used in various fields of application, in particular in the aeronautical field, to produce large parts, such as spars of engine pylons, aircraft door frame elements or also structural frame elements for aircraft.
  • thermomechanical transformation and machining processes with the purpose of obtaining, from titanium alloy billets, large parts which have to exhibit superior mechanical properties and observe precise size tolerances
  • thermomechanical transformation stages forging and/or stamping
  • stress-relieving alpha-beta thermal treatment (less than 730° C.) also know under the name stress relaxation treatment, in order to reduce the stresses of thermal or crystallographic origin inside the part in order to prevent the part from deforming during machining operations.
  • a thermal treatment for improving the mechanical characteristics.
  • the purpose of this treatment is to improve the mechanical characteristics of the alloy and generally comprises the maintenance of the part in a predetermined position (often by virtue of clamping tools).
  • This is a treatment named “beta treatment”, that is to say the treatment above the beta twists temperature.
  • This treatment makes it possible to obtain a structure having coarse grains, making it possible in particular to improve the characteristics of resistances to crack propagations.
  • this treatment also carried out before the machining operations, has the known disadvantage of deforming the part, either by creeping, during the treatment itself above the beta transus, or during the cooling from this temperature.
  • the declamped part has a tendency to be deformed again under the effect of the accumulated internal stresses.
  • the parts are generally deformed and in a different way from one part to another, so that the machining parameters and references have to be adjusted from one part to another in order to avoid obtaining a part which does not observe the final size tolerances required.
  • a purpose of the invention is to overcome the abovementioned disadvantages and to provide a stress-relaxation thermal treatment process which makes it possible to obtain parts which observe the final size tolerances required and which are devoid of residual internal stresses while making it possible to achieve the prescribed mechanical properties.
  • a second purpose of the invention is to solve the new technical problem consisting in providing a shaping tool which makes it possible, with parts made of titanium alloy, to conform, at treatment temperature, to a calibrated pattern cavity and to cool it without generating internal thermal stresses and without deformation, or with a minimum of stresses and deformation, that is to say significantly less than the stresses brought about by a conventional stress-relaxation treatment.
  • Another purpose of the invention is to solve the new technical problem consisting in providing a process for the preparation of a titanium alloy part comprising a stage of thermomechanical transformation and a machining but without it being necessary to carry out beforehand a relaxation treatment stage.
  • a first subject matter of the invention is a process for the preparation of a titanium alloy part, characterized in that the process comprises a thermal treatment for relaxing the internal stresses of a titanium alloy part, for example having been subjected beforehand to one or more thermomechanical transformation stages, in particular bringing about internal stresses, the process being characterized in that the thermal treatment comprises maintaining at a temperature “T 1 ” greater than the beta transus (beta transition) temperature, referred to as “Tbt”, and in that the part is free to deform by creeping.
  • the titanium alloy is of alpha-beta type and in particular of TA6V type.
  • maintaining at the temperature T 1 is carried out for a time sufficient to make possible the complete transformation of the microstructure of the alloy from a dose-packed hexagonal structure to a body-centered cubic structure.
  • the temperature T 1 is greater by at least 5° C. than Tbt and is preferably greater by at least 10° C. than Tbt, and preferably again the process comprises maintaining at the temperature T 1 for a period of time of 5 to 120 minutes, preferably for 15 to 60 minutes, and preferably at temperature from 1010° C. to 1060° C., in particular for an alloy of TA6V type.
  • cooling rate of greater than 5° C./min, preferably of greater than or equal to 10° C./min, preferably of between 10 and 20° C./min, such as, for example, in the air, preferably outside the treatment furnace.
  • the titanium alloy part is positioned for the stress-relaxation treatment in a shaping tool comprising one or more pattern cavities calibrated to receive a part to be relaxed, said shaping tool preferably being made of at least one single or composite material, the thermal inertia of which is greater than that of titanium or of the titanium alloy used and the variations in size of which related to creeping at the temperature T 1 are virtually nonexistent (less than 2 mm rising), indeed even nonexistent.
  • the shaping tool is made of concrete or composite concrete, preferably comprising curved stainless steel fibers, the distribution of which in the material is isotropic.
  • the invention also relates to a process for the preparation of a titanium alloy part comprising one or more rough machining stages prior to the stress-relaxation thermal treatment stage which comprises maintaining at a temperature “T 1 ” greater than the temperature “Tbt”.
  • one or more rough machining stages is understood to mean machinings which make it possible to remove, on one or more given surfaces of the part, at least 70% of material allowances.
  • final machining stages are, for their part, carried out in order to obtain the final dimensions of the part and the final surface condition required by eliminating the remaining allowances, i.e. less than 30% with respect to the starting allowances before the 1 st machining stage.
  • the rough machining stage or stages are carried out in order to treat virtually all, indeed even all, of the surfaces of the parts.
  • the rough machining is carried out on a part which has not been subjected to stress-relaxation treatment, in particular by maintaining at a temperature lower than Tbt and typically lower than 730° C.
  • the part is flattened and shaped against at least one reference support.
  • the part is flattened and shaped against said reference support by flattening, against the reference support, one or more flashes formed around the part and resulting from an upstream stamping stage.
  • the process can comprise one or more stages of final machining of the titanium alloy part which make(s) it possible to treat one or more surfaces of the part in order to remove areas of surface contamination, to obtain a specific roughness and to achieve the final dimensions of the part.
  • the part is a slender part, such as a spar of an engine pylon, a door frame element or a structural frame element for an aircraft.
  • the invention also relates to a shaping tool comprising a shaping region comprising one or more pattern cavities calibrated in order to shape, by creeping, one or more slender parts and/or parts with large differences in cross section of titanium alloy, said shaping tool being composed of at least one single or composite material, the thermal inertia of which is greater than that of titanium or of the titanium alloy and the variations in size of which related to the creeping at a temperature of 1060° C. are virtually nonexistent, indeed even nonexistent.
  • the tool is composed of concrete and optionally comprises, in addition, curved stainless steel fibers distributed isotropically in the concrete.
  • the tool has dimensions so that the cooling rates are substantially constant from one slice, part plus tool, to another.
  • the pattern cavity region is calibrated in order to shape, by creeping, a slender part exhibiting a slenderness of greater than 10 and/or different cross sections, the variation in cross section of which is greater than 2/1, and preferably in order to receive a spar of an engine pylon, a door frame element or a structural frame element for an aircraft.
  • the titanium alloy is of alpha-beta type and is preferably a TA6V alloy.
  • the pattern cavity comprises at least two supporting surfaces on which the part to be relaxed can at least partially rest, said supporting surfaces preferably being positioned so that, when a titanium alloy part is maintained at a temperature T 1 greater than its temperature Tbt, said part can be positioned by creeping with greater contact, virtually complete contact, indeed even complete contact, on the supporting surfaces, in order to correct the deformations, such as the curving or twisting defects related to a prior stage of preparation of the part to be shaped, in particular during a thermomechanical transformation, a cooling or a machining.
  • the pattern cavity comprises a positioning stop formed in each calibrated mold, the other end of the mold being free, that is to say without a stop, in order to allow the part to freely deform by creeping, or comprises a stop positioned by taking into account the creeping and the thermal expansion coefficient of the part to be relaxed before and after relaxation thermal treatment, in particular in order to make possible free deformation by creeping.
  • the pattern cavity comprises a visual marker which makes it possible to position the part in the calibrated pattern cavity.
  • the invention thus also relates to a process for the preparation of a titanium alloy part employing the tool of the invention and in particular as defined in any one of claims 17 to 24 .
  • the invention relates to a thermal treatment process for relaxing thermal stresses in a titanium alloy part which has been subjected to one or more thermomechanical transformation stages, characterized in that the part is free to deform by creeping and the thermal treatment is carried out at a temperature greater than the beta transus (beta transition) temperature of the alloy in order to relax the stresses, that is to say above the point where the alpha phase completely disappears to the advantage of the beta phase and where the microstructure is transformed into a structure of body-centered cubic type.
  • “creeping” is understood to mean the deformation of a part brought about, during maintenance at the temperature greater than the beta transus temperature, by the dead weight of the material or also by exerting a constant stress on the part by applying a load to the latter.
  • the thermal treatment according to the invention makes it possible simultaneously to obtain a coarse-grained structure in order to improve the characteristics of resistances to crack propagations and the relaxation of the internal stresses of thermal and crystallographic origins by leaving the part free to deform without use of specific tools, such as clamps, which, by an external pressure on the part, make it possible to force the latter into a predetermined form.
  • “Coarse-grained structure” is understood to mean a structure which typically has a structure of virtually isotropic grains with a size of less than approximately minus 3 ASTM with regions of grains less than minus 5 ASTM.
  • thermal treatment THT
  • all the residual internal stresses can be eliminated, so that no specific management of the stresses is necessary before the thermal treatment as the thermal stresses are eliminated during the thermal treatment according to the invention. It is, for example, not necessary to take care to eliminate or limit the appearance of internal stresses, to carry out slow coolings or specific relaxation treatments before (rough) machining operations.
  • the alloy By heating the alloy to a temperature which is greater than the beta transus temperature, the alloy is subjected to an allotropic transformation where the alpha phase of close-packed hexagonal crystallographic structure is transformed into a body-centered cubic phase referred to as beta phase.
  • beta phase a body-centered cubic phase
  • the residual stresses which appeared in particular in the part during the preceding thermomechanical transformation stages and which are of thermal and crystallographic origins, are released.
  • the mobility of the dislocations is greater, which also promotes the release of the internal stresses.
  • the part is deposited in a calibrated pattern cavity formed on a shaping tool supporting at least one part and, during the thermal treatment, the part conforms, by creeping, to the calibrated pattern cavity.
  • the body-centered cubic structure is favorable to the creeping of the part.
  • the thermal treatment according to the invention is, contrary to practice, carried out by leaving the part free to deform by creeping, so that, under the effect of its own weight or, if appropriate, by applying an additional load, the part can deform in order to perfectly match the shape of a calibrated pattern cavity produced in the tool supporting the part and corresponding to the required final shape of the part.
  • the part is not prevented from deforming by constraining it using, for example, clamps but, on the contrary, the part is left to freely deform by creeping, so that the part comes to freely (without constraint) match a pattern cavity which is it calibrated.
  • the parts which deform by creeping can be easily shaped to the calibrated pattern cavity in order to take the shape of the targeted final part while making it possible to eliminate internal stresses and while avoiding the generation of new stresses.
  • the calibrated pattern cavities make it possible to control the deformation of the parts by creeping.
  • the calibrated pattern cavities have dimensions in order for the shape and the dimensions of the part obtained after shaping to be those of the final parts, minus the final machining.
  • the dimensions of the calibrated pattern cavity are determined by digital simulation according to the shape of the final part to be obtained and of the kinetics of creeping of titanium or of the titanium alloy and by taking into account the expansion differential, in the vicinity of 1000° C., between the concrete and titanium alloy under consideration.
  • the thermal treatment temperature is maintained for 5 to 120 minutes above the beta transus temperature +5° C. and preferably between 15 and 60 minutes from 1010° C. to 1060° C., for example for an alpha-beta alloy of TA6V type, as defined below, the beta transus of which is, according to the exact composition of the alloy, between 980 and 1000° C.
  • the treatment temperature and time depend on the exact composition of the alloy.
  • a widespread ⁇ + ⁇ alloy is in particular the abovementioned alloy known under the TA6V or TA6V4 or also Ti-6Al-4V trade names, the composition of which, described as percent by weight with respect to the total weight of the alloy, is typically as follows:
  • the remainder being composed of titanium and of purities resulting from the preparation; and preferably a titanium alloy in accordance with AMS 4928 GR5 (Aero Material Specification).
  • the minimum treatment temperature is determined in order to make possible the complete allotropic transformation from a dose-packed hexagonal microstructure to a body-centered cubic microstructure and in order to obtain a beta-grain mesostructure.
  • the maximum treatment temperature is determined in order to avoid coarse-grain growth kinetics with, in some regions of the microstructure, an explosion in the size of the grains which would be harmful to the achievement of good mechanical properties, such as the tensile strength and fatigue strength, and the like.
  • the treatment time depends on the massiveness of the part. Specifically, the greater the equivalent diameter of the part, the longer the treatment time,
  • the treatment time is from 20 to 40 minutes, so as to make possible the complete dissolution of the beta phase in the part and the elimination in the part of the residual thermal stresses and in order to allow the part to creep and to perfectly conform to the calibrated pattern cavity of the tool.
  • the treatment time is approximately 1 hour.
  • the treatment time corresponds to the time during which the core of the part will be at thermal stationary phase temperature.
  • the part is cooled from the treatment temperature according to the invention down to ambient temperature at a rate of greater than 5° C. per minute and preferably of greater than 10° C. per minute.
  • the parts are typically cooled with air outside the treatment furnace.
  • the alloy will pass through the alpha-beta transformation domain during which the alpha phase reappears.
  • the inventors have been able to observe that, in alloys of alpha-beta type, such as TA6V, and when the cooling rates are too slow, the germination of the alpha phase takes place essentially at the beta grain boundaries (intergranular germination) in the form of plates initiated at the beta grain boundaries (known under the name of intergranular Widman Maschinenn morphology) and as thick intragranular plates.
  • the alpha phase appears with an intragranular and intertwined fine needle morphology.
  • the fine needles intertwine randomly, so that the alpha phase forms a network which counteracts any new dislocation movements, thus preventing the part from deforming during the cooling thereof or when it is subsequently mechanically stressed, Furthermore, this morphology confers, on the part, better mechanical characteristics, in particular in tensile strength (Rm>900 MPa), and confers good crack propagation behavior as the pathway for propagation of the cracks is more tortuous, and also good toughness.
  • a second subject matter of the invention is a shaping tool on which the parts to be shaped are positioned.
  • the tool is characterized in that it is made of a material which has a greater thermal inertia than that of titanium or the titanium alloy used and which does not creep up to temperatures of approximately 1060° C.
  • the tool is made of concrete, which can optionally comprise curved stainless steel fibers which have a greater coefficient of expansion than the concrete.
  • Such fibers make it possible to stiffen the structure of the tool (by contraction of the fibers), so as to prevent it from being deformed at high temperatures under the weight of the parts.
  • Use is preferably made of a refractory concrete.
  • the concrete can be a concrete of the MFRRC (Metal Fiber-Reinforced Refractory Concrete) type having a thermal conductivity of approximately 3.5 W.m ⁇ 1 .K ⁇ 1 (watt/(meter*degree kelvin)), a specific heat, measured at 500° C., of approximately 1000 J.kg ⁇ 1 .K ⁇ 1 (joule/(kilogram*degree kelvin)) and a density of approximately 3000 kg/m 3 .
  • MFRRC Metal Fiber-Reinforced Refractory Concrete
  • the tool comprises calibrated pattern cavities, in each of which is deposited a part to be shaped, in order to obtain, after a heat treatment according to the first subject matter of the invention, a part of predetermined shape, the shape of the part minus the final rnachinings, devoid of residual internal (thermal or crystallographic) stresses.
  • a third subject matter of the invention is a process comprising, after thermomechanical transformation, on the one hand, a thermal treatment in accordance with the first subject matter of the invention, in order to relax the residual stresses and to shape the part according to a predetermined shape, and, on the other hand, a rough machining schedule, characterized in that the machining schedule precedes said thermal treatment schedule and in that, during the machining, the part is flattened and shaped against a reference support.
  • the inventors have been able to find that, by virtue of the thermal treatment according to the first subject matter of the invention, it is possible to carry out the rough machining before the thermal stress-relaxation treatment in the part.
  • the rough and final machining be carried out after the relaxation thermal treatments, below the beta transus temperature, for example at temperatures below 730° C., in order to machine a part having, at the start, a minimum of residual internal stresses, so as to prevent the part from cracking and from being deformed during the machining operations.
  • the machinings are carried out after the final thermal treatments in order to eliminate the contaminated surface regions (e.g.: surface oxidations) subsequent to the thermal treatments.
  • the cutting tools exert a high pressure on the part, which generates additional internal stresses, in particular when rough machining operations are concerned, where the machining parameters apply greater forces on the part than in “final” machining.
  • the depths of machining cuts are generally greater than those carried out during the final machining operations.
  • the rates of feed are also faster than in final machining.
  • the inventors have been able to observe that, when the heat treatment makes it possible to efficiently shape the part according to a predetermined shape and makes it possible to sufficiently reduce the internal stresses so as to prevent the part from deforming again after thermal treatment or from cracking prematurely during the use thereof, it is not necessary, before the thermal treatment, to specifically manage the stresses. Consequently, the inventors have been able to determine that it is possible to carry out the rough machining before the relaxation thermal treatment according to the invention provided that, for each part (or at least for the main surfaces of each part), during the rough machining operations, a predetermined and constant size is observed from one part to another, so that the machining parameters and reference frames are repeatable from one part to another and so as to be able to observe the size tolerances required for the final part.
  • the flashes are not removed after the final stamping operation in order to provide regions for gripping between the clamps and the reference support(s) and so as to shape the part as mentioned above without interfering with the machining operations, which can he carried out on either side of the part and flashes on a single occasion, that is to say without being obliged to separate and reposition the part between two machining stages. Furthermore, by gripping the flashes of the part, marking/damaging the ape rational/working surfaces of the part is avoided.
  • the part After machining, the part includes a significant amount of internal stresses which originate:
  • the latter relaxes and is deformed again.
  • the latter defects are corrected during the thermal treatment according to the invention, which allows the part to regain a calibrated shape with a significant reduction in the internal stresses so that the part is not deformed again and does not crack prematurely during the cooling or subsequently when it is subjected to operational thermomechanical stresses.
  • the parts are shaped according to the calibrated pattern cavity formed in a shaping tool.
  • the thermal treatment is followed by a final machining schedule in which the machining parameters (depth of cut, cutting speed, feed motion, and the like) are determined so as not to generate stresses inside the part which might bring about deformations or premature cracks in the part.
  • the final machining operations generate few stresses inside the part.
  • the depths of cut and the rates of feed are lower than during the rough machinings.
  • FIG. 1 is a flowchart showing successive stages employing a process in accordance with the invention in order to obtain a titanium alloy part having the required final mechanical properties and dimensions,
  • FIG. 2 is a diagrammatic isometric view in 3 dimensions of the tool according to the invention.
  • FIG. 3 corresponds to the tool according to FIG. 1 on which is positioned a door frame element to be treated of simplified form.
  • FIG. 4 corresponds to the tool according to FIG. 1 represented according to a transverse cross section and on which several door frame elements are positioned.
  • FIG. 5 represents two tools according to the invention on a car hearth taken out of a treatment furnace.
  • FIGS. 5 a , 5 b and 6 c correspond to the tool according to FIG. 1 represented along a longitudinal cross section passing through a calibration pattern cavity.
  • FIG. 7 represents a part ( 71 ) which is flattened and shaped against one or more reference supports ( 715 ) by gripping its stamping flash ( 75 ).
  • the clamping means or damps ( 710 a —open position (A), and 710 b —closed position (B)), make it possible to hold the part ( 71 ) by gripping against the reference support(s) ( 715 ).
  • the stamping clamps ( 710 b ) exert a series of localized pressures in the closed position (B). It is noted that the reference support or supports ( 715 ) exhibit two localized bearings. The use of one or more reference supports ( 715 ) generally depends on the size of the part.
  • the processes and tool according to the invention have been employed to produce elements forming part of a door frame for an aircraft. These elements have a curved and slender shape, as represented diagrammatically in FIG. 3 , with a mean thickness typically of 25 mm, an equivalent diameter of 50 mm and a length of 4 meters and exhibit a single curve. It should be pointed out, at this stage, that the process according to the invention is suitable for shapes of parts which are more complex, for example exhibiting several curves, with optionally corkscrewed surfaces,
  • the elements were prepared from ingots of titanium alloy TA6V produced in a standard manner ( FIG. 1 , stage “a” of the flowchart).
  • thermomechanical treatment cf. FIG. 1 , unit “b”.
  • Alpha-beta kneading reduction of 4 (reduction in cross section and increase in the height H to 4*H) between 900 and 980° C.
  • the billets obtained were cut up in order to obtain smaller billets of predetermined volume corresponding to the volume of the preform of the door frame element before machining.
  • the billets, of circular cross section were forged in order to obtain square bar products which were stamped in one or more stages in order to obtain half-finished products already having a shape close to that of the finished parts, hereinafter denoted the “preform” of the door frame element.
  • the flashes resulting from the stamping are not removed subsequent to the final stamping stage but are retained in order to provide gripping/clamping regions on a reference support during the machining.
  • the preforms are deformed and include internal stresses.
  • the preforms are prepared in order to be subjected to rough machinings. Contrary to normal practice, the rough machinings of the preforms are carried out in the context of the invention before the thermal stress-relaxation and shaping treatment ( FIG. 1 , unit “c” and then “d”). This is because, although the preforms include internal stresses resulting from the preceding thermomechanical transformation stages, the inventors have been able to observe that, after a succession of transformation stages which are standard for parts of this type, the internal stresses were sufficiently weak not to cause damage to the preforms nor to risk premature breakages of the preforms during the rough machining operations.
  • the preforms ( 71 ) are flattened via their stamping flash ( 75 ) against several reference supports ( 715 ) using clamps ( 710 a , 10 b ) (cf. FIG. 7 ).
  • Each flash ( 75 ) is gripped between clamps ( 710 b, closed position B) and reference supports ( 715 ) with a sufficient force to shape the preforms ( 71 ) according to a predetermined geometry.
  • the fact of gripping the flashes ( 75 ) and not directly each preform ( 71 ) makes it possible to shape the latter without marking the functional surfaces of the preform ( 71 ) and without interfering with the movements of the cutting tools during the machining proper.
  • This configuration makes it possible to retain an unchanging geometry from one preform to another so that the machining parameters and reference frames are repeatable from one prefrom to another and from one series of preforms to another, in order to observe the size tolerances required on the final part,
  • the preforms ( 71 ) are released from the clamps ( 710 a, open position A) and relax in order to resume a deformed shape (see clearance “J”, FIGS. 6 a and 6 b ).
  • the machined preforms ( 20 , 320 , 420 , 620 ) are subsequently prepared in order to be subjected to the thermal stress-relaxation and shaping treatment according to the first subject matter of the invention ( FIG. 1 , unit “d”).
  • the machined preforms ( 20 , 320 , 420 , 620 ) are deposited (cf. FIGS. 2 , 3 and 4 ) in calibrated pattern cavities ( 15 , 315 , 415 , 615 ) formed in a shaping tool ( 10 , 310 , 410 , 610 ).
  • the calibrated pattern cavities ( 15 , 315 , 415 , 615 ) comprise predetermined surfaces ( 317 , 318 , 417 , 418 , 617 ) which correspond to the shapes of the final door frame element to be obtained.
  • each calibrated pattern cavity ( 415 ) exhibits two main supporting surfaces ( 417 , 418 ) on which each machined preform ( 420 ) rests at least partially (as the part is deformed at this stage, cf, FIGS. 6 a and 6 b ).
  • the tool is made of concrete composite material in which curved steel fibers are embedded, which fibers reinforce the tool at high temperatures.
  • This tool makes it possible, as indicated above, to carry out rapid and homogeneous cooling of the machined-treated preforms, making it possible to obtain homogeneous microstructures of the alloy as fine entangled needles, conferring improved mechanical properties and making it possible to prevent, during the cooling, the appearance of internal thermal stresses and uncontrolled deformations of the part during or subsequent to the cooling.
  • the tool comprises a positioning stop formed in each calibrated pattern cavity.
  • the other end of the pattern cavity is free, that is to say without a stop, in order to allow the part to freely deform by creeping.
  • a visual marker on the tool may also be sufficient to position the preforms on the tool for thermal treatment.
  • the tool has dimensions so that the cooling rates are substantially constant whatever the cross section (or slice), part plus tool, under consideration.
  • the thicknesses of the concrete tool are thus given dimensions by taking into account the variations in thickness of the part and the ratio of the thermal diffusion coefficients of the part with respect to the tool.
  • the shaping tool on which the machined preforms rest can, for example, comprise about ten pattern cavities.
  • the shaping tool ( 510 ) is placed with the preforms to be treated in a thermal treatment chamber ( 550 ).
  • the shaping tool ( 510 ) can be placed on a car hearth ( 530 ) with one or more other shaping tools ( 510 ) (cf. FIG. 5 , showing two shaping tools).
  • the relaxation and shaping thermal treatment ( FIG. 1 , unit “d”) was carried out as follows:
  • the machined preforms ( 620 ) before the thermal treatment according to the invention, the machined preforms ( 620 ) exhibited significant deformations, in particular twisting and curving defects, with clearances “J” with respect to the calibrated form ( 615 ) of several millimeters (5 to 30 mm, depending on the preforms) in some regions of the main supporting surfaces ( 617 a, b ).
  • the preforms ( 620 ) were subject to free creeping under the effect of their own weight in order to take the shape of the calibrated pattern cavities ( 615 ) and thus to rest on the main supporting surfaces ( 617 c ) (cf. FIG. 5 c ).
  • the alloy is subjected to an allotropic transformation where the alpha phase of close-packed hexagonal crystallographic structure is converted into a body-centered cubic phase, referred to as beta phase.
  • beta phase a body-centered cubic phase
  • the residual stresses which appeared in particular in the part during the preceding thermomechanical transformation stages and which are of thermal and crystallographic origins, are released.
  • the mobility of the dislocations is greater, which also favors the release of the internal stresses,
  • the preforms were subsequently cooled in the air outside the treatment furnace, i.e. at a cooling rate of between 10 and 30° C./min.
  • the cooling rates inside the preforms were homogeneous, in particular by virtue of the use of the composite tool made of concrete,
  • the rapid cooling of the machined preforms from temperatures greater than the beta transus made it possible to bring about the appearance, in the alpha-beta domain, of the alpha phase with a morphology as fine intragranular and intertwined needles.
  • the needles which are intertwined randomly, counteract any new movement of dislocations and also counteract propagations of cracks, thus preventing the part from deforming during the cooling thereof or at ambient temperature and furthermore conferring, on the part, better mechanical characteristics, in particular of mechanical strength, good crack propagation behavior, as the propagation pathway for the cracks is more tortuous, and good toughness.
  • the homogeneous cooling of the machined preforms obtained in particular by virtue of the material used for the tool makes it possible to prevent the generation of internal thermal stresses and to prevent deformations of the preforms during the cooling or subsequently when the door frame elements are subjected to normal thermomechanical stresses.
  • An advantage of the concrete is also its thermal expansion coefficient, which is dose to that of titanium, allowing the calibrated pattern cavities to have variations in dimensions due to thermal expansions, for example at 1060° C., which are close to those of the parts made of titanium or of titanium alloy according to the invention. Thus, the dimensions of the preforms obtained after treatment are better controlled.
  • the concrete used to produce the tool according to the invention preferably has a thermal expansion coefficient of between approximately 3.5 and 7*10 ⁇ 6 ° K ⁇ 1 , whereas that of titanium is between approximately 8 and 11*10 ⁇ 6 ° K ⁇ 1 , for a T° range of between 100° C. and 1100° C.
  • the thermal treatment associated with the form of the calibrated pattern cavities ( 15 , 315 , 415 , 615 ) comprising, in the present case, two main supporting surfaces ( 317 , 318 , 417 , 418 , 617 ) which intersect has made it possible to correct twisting and curving defects (it is preferable to have at least two supporting surfaces inclined with respect to one another in order to correct twisting defects).
  • the differences measured with respect to the dimensions of the targeted part were less than 4 mm, indeed even less than 2 mm.
  • the preforms thus obtained after treatment according to the invention were thus virtually devoid of deformations, thus making it possible to observe the final size tolerances required.
  • the parts obtained are removed from the concrete shaping tool and placed on the final machining tool.
  • the preforms are subjected to final rnachinings in order to obtain the final form of the door frame elements. Because the machining parameters (depth of cut, cutting speed and rates of feed) during the finishing are not very stressful for the part, it is not necessary to carry out a new stress-relaxation treatment.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Forging (AREA)
  • Heat Treatment Of Nonferrous Metals Or Alloys (AREA)
US13/500,826 2009-10-20 2010-10-20 Thermal treatment for the stress-relief of titanium alloy parts Abandoned US20130037183A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
FR0957356 2009-10-20
FR0957356A FR2951462B1 (fr) 2009-10-20 2009-10-20 Traitement thermique de relaxation des contraintes
PCT/FR2010/052239 WO2011048334A2 (fr) 2009-10-20 2010-10-20 Traitement thermique de relaxation.

Publications (1)

Publication Number Publication Date
US20130037183A1 true US20130037183A1 (en) 2013-02-14

Family

ID=42244544

Family Applications (1)

Application Number Title Priority Date Filing Date
US13/500,826 Abandoned US20130037183A1 (en) 2009-10-20 2010-10-20 Thermal treatment for the stress-relief of titanium alloy parts

Country Status (5)

Country Link
US (1) US20130037183A1 (fr)
EP (1) EP2491158A2 (fr)
JP (1) JP5829213B2 (fr)
FR (1) FR2951462B1 (fr)
WO (1) WO2011048334A2 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017218837A1 (fr) * 2016-06-15 2017-12-21 Ducommun Aerostructures, Inc. Procédé de formage sous vide
US10323312B2 (en) 2014-12-10 2019-06-18 Rolls-Royce Corporation Reducing microtexture in titanium alloys
CN110000248A (zh) * 2019-05-16 2019-07-12 沈阳飞机工业（集团）有限公司 一种钛合金л形焊接件的热校形方法及工装
US11473173B2 (en) 2016-12-22 2022-10-18 Nippon Steel Corporation α+βtitanium alloy extruded shape

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AT512214B1 (de) 2011-12-05 2015-04-15 Siemens Vai Metals Tech Gmbh Prozesstechnische massnahmen in einer stranggiessmaschine bei giessstart, bei giessende und bei der herstellung eines übergangsstücks
JP6288413B2 (ja) 2013-10-11 2018-03-07 三菱重工業株式会社 ステンレス部材の熱処理方法、及びステンレス鍛造品の製造方法。
CA2947981C (fr) * 2014-05-15 2021-10-26 General Electric Company Alliages de titane et leurs procedes de production
CN110918685A (zh) * 2019-11-20 2020-03-27 嘉丰工业科技（惠州）有限公司 用于镁合金超薄笔记本电脑外壳压铸件的模压矫形方法
CN113981348A (zh) * 2021-10-19 2022-01-28 宝鸡钛业股份有限公司 一种降低钛合金板材残余应力的方法
CN114777979B (zh) * 2022-04-25 2023-10-13 中国石油大学(华东) 基于压入能量差法的非均匀焊接接头残余应力测试方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5813276A (en) * 1995-07-13 1998-09-29 Maeda; Naomi Press die of cement composite and a method of producing the same
US20040261912A1 (en) * 2003-06-27 2004-12-30 Wu Ming H. Method for manufacturing superelastic beta titanium articles and the articles derived therefrom
US20080116996A1 (en) * 2004-01-30 2008-05-22 Tdk Corporation Signal Detector

Family Cites Families (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3739617A (en) * 1970-09-21 1973-06-19 Boeing Co High temperature vacuum creep forming fixture
GB1492262A (en) * 1975-05-07 1977-11-16 Imp Metal Ind Kynoch Ltd Titanium base alloy
US4188811A (en) * 1978-07-26 1980-02-19 Chem-Tronics, Inc. Metal forming methods
US4811584A (en) * 1985-06-03 1989-03-14 Brimm Daniel J Thermal processing methods
US4729546A (en) * 1985-12-24 1988-03-08 Ford Motor Company Titanium engine valve and method of making
JPS6428347A (en) * 1987-07-23 1989-01-30 Kobe Steel Ltd Engine valve made of titanium alloy and its production
JP2506517B2 (ja) * 1991-08-07 1996-06-12 日本冶金工業株式会社 コンクリ―ト補強用ステンレス鋼繊維
JP3314408B2 (ja) * 1992-04-24 2002-08-12 大同特殊鋼株式会社 チタン合金部材の製造方法
JPH09136102A (ja) * 1995-11-14 1997-05-27 Nkk Corp α＋β型チタン合金シート材の製造方法
JPH10291029A (ja) * 1997-04-18 1998-11-04 Nippon Steel Corp α＋β型チタン合金製直棒の矯正方法
JPH11199995A (ja) * 1997-11-05 1999-07-27 United Technol Corp <Utc> チタン合金のクリープ特性を改善するための方法及びチタン合金
JP2001071318A (ja) * 1999-09-02 2001-03-21 Takenaka Komuten Co Ltd プレキャストコンクリート板の製造方法
JP4442004B2 (ja) * 2000-08-09 2010-03-31 大同特殊鋼株式会社 耐熱Ｔｉ合金の製造方法
US20060230807A1 (en) * 2005-04-14 2006-10-19 Shultz Stephen W Creep forming a work piece

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5813276A (en) * 1995-07-13 1998-09-29 Maeda; Naomi Press die of cement composite and a method of producing the same
US20040261912A1 (en) * 2003-06-27 2004-12-30 Wu Ming H. Method for manufacturing superelastic beta titanium articles and the articles derived therefrom
US20080116996A1 (en) * 2004-01-30 2008-05-22 Tdk Corporation Signal Detector

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10323312B2 (en) 2014-12-10 2019-06-18 Rolls-Royce Corporation Reducing microtexture in titanium alloys
WO2017218837A1 (fr) * 2016-06-15 2017-12-21 Ducommun Aerostructures, Inc. Procédé de formage sous vide
EP3452626A4 (fr) * 2016-06-15 2019-11-13 Ducommun Aerostructures, Inc. Procédé de formage sous vide
US10677529B2 (en) 2016-06-15 2020-06-09 Ducommun Aerostructures, Inc. Vacuum forming method
EP3964596A1 (fr) * 2016-06-15 2022-03-09 Ducommun Aerostructures, Inc. Procédé de formage sous vide
US11359863B2 (en) 2016-06-15 2022-06-14 Ducommun Aerostructures, Inc. Vacuum forming method
US20220316802A1 (en) * 2016-06-15 2022-10-06 Ducommun Aerostructures, Inc. Vacuum Forming Method
US11703281B2 (en) * 2016-06-15 2023-07-18 Ducommun Aerostructures, Inc. Vacuum forming method
US11473173B2 (en) 2016-12-22 2022-10-18 Nippon Steel Corporation α+βtitanium alloy extruded shape
CN110000248A (zh) * 2019-05-16 2019-07-12 沈阳飞机工业（集团）有限公司 一种钛合金л形焊接件的热校形方法及工装

Also Published As

Publication number Publication date
JP2013508550A (ja) 2013-03-07
WO2011048334A3 (fr) 2011-09-29
FR2951462A1 (fr) 2011-04-22
JP5829213B2 (ja) 2015-12-09
WO2011048334A2 (fr) 2011-04-28
EP2491158A2 (fr) 2012-08-29
FR2951462B1 (fr) 2013-05-10

Similar Documents

Publication Publication Date Title
US20130037183A1 (en) Thermal treatment for the stress-relief of titanium alloy parts
Chi et al. Effects of heat treatment combined with laser shock peening on wire and arc additive manufactured Ti17 titanium alloy: Microstructures, residual stress and mechanical properties
CA2803386C (fr) Redressage par etirage a chaud de titane traite alpha/beta de resistance elevee
JP5681631B2 (ja) アルミニウム合金シート部品成形のための処理
EP3391976B1 (fr) Laminage de tôle en alliage de magnésium et procédé de préparation
TWI483793B (zh) 模鍛造方法以及鍛造品的製造方法
EP3546606B1 (fr) Materiau extrudé en alliage alpha+beta titane
JP7236569B2 (ja) 高強度ステンレス鋼ローター及びその製造方法
CN101294264A (zh) 一种转子叶片用α+β型钛合金棒材制造工艺
CN105543749A (zh) 高熵合金梯度应力改性技术
CN113996812B (zh) 一种提高激光选区熔化α-β型钛合金疲劳性能的热处理方法
CN110468361A (zh) 一种变形高温合金细晶棒材的制备方法
EP3445888A1 (fr) Procédés améliorés de finition de produits extrudés en titane
CN105603258B (zh) 一种高强度锆合金及制备方法
CN109385590A (zh) 一种单晶高温合金再结晶的控制方法
Zhang et al. Characterization of the recasting-affected zone in the nickel-based superalloy upon single-pulse laser treatment
JP6185347B2 (ja) Ｎｉ基超耐熱合金の分塊用中間素材及びその製造方法、Ｎｉ基超耐熱合金の製造方法
CN109797314A (zh) 一种具有纳米级晶粒的高铌TiAl合金及其制备方法
CN112708788B (zh) 一种提高k403合金塑性的方法，模具材料和制品
KR20030069831A (ko) Ｃｕ계 합금 및 이를 이용한 고강도 및 고열전도성단조물의 제조방법
CN114799216A (zh) 钛合金的热处理方法
JP2019167584A (ja) α＋β型チタン合金押出形材
WO2016040996A1 (fr) Procédés de traitement d&#39;alliages de titane bêta metastables
CN117798297A (zh) 一种提高对称型长轴类gh4169合金锻件组织均匀性的锻造方法
CN117181838A (zh) 一种具有混合层片微结构的超塑性TiAl合金板材的制备方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: AUBERT & DUVAL, FRANCE

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:DAFFOS, CHRISTOPHE;MIQUEL, MICHEL;FOUCHER, LAURENT;AND OTHERS;REEL/FRAME:029191/0320

Effective date: 20121024

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION