US20120115367A1 - Method for integrating and erecting carbon nanotube column - Google Patents
Method for integrating and erecting carbon nanotube column Download PDFInfo
- Publication number
- US20120115367A1 US20120115367A1 US13/292,050 US201113292050A US2012115367A1 US 20120115367 A1 US20120115367 A1 US 20120115367A1 US 201113292050 A US201113292050 A US 201113292050A US 2012115367 A1 US2012115367 A1 US 2012115367A1
- Authority
- US
- United States
- Prior art keywords
- cnt
- electrode
- conductive layer
- water
- integrating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for integrating and erecting CNT column, comprises following steps of: 1) providing a conductive layer; 2) applying a non-conductive layer over the conductive layer; 3) forming a via on the non-conductive substrate; 4) placing an electrode above the via; 5) deploying dispersive liquid containing CNT powder into the via; 6) applying a predetermined AC electric field between the conductive substrate and the electrode for integrating and erecting the CNT powder into CNT column under electric field force.
Description
- 1. Field of the Invention
- The present invention relates to a method for integrating carbon nanotube column, and more particularly to a method using vertical electricfield for integrating carbon nanotube column thus achieving erect nanotube column.
- 2. Description of the Prior Art
- Since carbon nanotube (CNT) was discovered and reported by Japanese physical spiciest Sumio Iijima in 1991, the physical and electrical properties of the CNT is more and more appreciated by the industry as more and more genuine applications are introduced.
- However, the CNT must be integrated/assembled before it is used in a certain application. At present, a conventional method called dielectrophoresis (DEP) is used to integrate the CNT into an unitary structure. As shown in
FIG. 1 , the conventional method uses two electrodes disposed on a same side of a substrate and spaced to each other. Dispersive liquid with CNT powder will be dropped into a cavity disposed between the two electrodes. When an AC electric field is applied between the two electrodes, the CNT powder will be integrated into CNT column under electric field force. Such CNT column is suit for some applications, e.g., chemical sensor, but is not suit for application which needs the CNT having a three-dimensional structure. For example, contact of electrical connector for connecting Integrated Circuit (IC) package usually needs a three-dimensional structure. Therefore, the CNT art is hard to be used in electrical connector field. - U.S. Pat. No. 6,626,684 issued to Stickler on Sep. 30, 2003 disclosed a nanotube socket system using three-dimensional nanotube column for transmitting electric signal. However, Stickler is silent on how to integrate the nanotube into CNT-column.
- Therefore, it is needed to find a new method to overcome the problems mentioned above.
- Accordingly, an object of the present invention is to provide a method for integrating nanotubes column, and more particularly to a method using vertical electric field for integrating and erecting nanotubes column thus achieving erect nanotubes column which can be used in electric socket field.
- In order to achieve the object set forth, a method for integrating and erecting CNT column, comprises following steps of: 1) providing a conductive layer; 2) applying a non-conductive layer over the conductive layer; 3) forming a via on the non-conductive substrate; 4) placing an electrode above the via; 5) deploying dispersive liquid containing CNT powder into the via; 6) applying a predetermined AC electric field between the conductive substrate and the electrode for integrating and erecting the CNT powder into CNT column under electric field force.
-
FIG. 1 is a sketch view of a conventional method for integrating CNT; -
FIG. 2 shows a schematic diagram of a method for integrating and erecting CNT column of the present invention; -
FIG. 3A andFIG. 3B shows an integrate process for integrating CNT by using the method of the present invention in accordance with a first preferred embodiment; -
FIG. 4 is a photograph of a CNT-column made by the method of the present invention. -
FIG. 5A andFIG. 5B shows an integrate process for integrating CNT by using the method of the present invention in accordance with a second preferred embodiment; -
FIG. 6 is an isometric view of an electrical socket of the present invention in accordance with the second preferred embodiment; and -
FIG. 7 is an exploded view of the electrical socket shown inFIG. 6 . - Reference will now be made to the drawings to describe the present invention in detail.
- Referring to
FIG. 2( a)-(b), schematic diagram of the present invention is shown. As we know, when an AC electric field is applied between two electrodes, the CNT powder will be moved under electric field force along direction of the electric field. Such phenomenon is called dielectrophoresis (DEP). - Referring to
FIGS. 3A-3B , a method called vertical DEP in accordance with a first preferred embodiment of the present invention is shown, which uses vertical electric field to integrate and erect CNT powder into CNT columns with erect structure. According to the method, firstly, abase substrate 11 is provided with a number ofvias 11 a (only one is shown). Thevias 11 a are arranged in a manner of matrix or other layout. Then, afirst electrode 10 and asecond electrode 12 is disposed at two sides of thebase substrate 11 respectively and corresponding to a via 11 a. According to a preferred embodiment of the present invention, thebase substrate 11 is made from non-conductive matters. Thefirst electrode 10 is a substrate made from gold and covering on a lower surface of thesubstrate 11. Specially, thefirst electrode 10 and thebase substrate 11 is disposed on a surface of awafer 16. Thesecond electrode 12 is a conductor and of an acicular or columnar shape. According to the preferred embodiment of the invention, diameter of thesecond electrode 12 is smaller than that of thevia 11 a, so as to control diameter of the CNT column, which will be erected. Thesecond electrode 12 has a plate structure on a top end thereof for pulling updispersive liquid 13 containingCNT powder 13 a to form liquid column, thus increasing volume of thedispersive liquid 13 and the number ofCNT powder 13 a involved/used in the vertical DEP process. In the preferred embodiment of the present invention, only onesecond electrode 12 is shown. In fact, number of thesecond electrode 12 is equal to number of thevias 11 a. - Thirdly, the
dispersive liquid 13 havingCNT powder 13 a will be dropped into thevia 11 a. Preparation of thedispersive liquid 13 will be described later. At last, an AC electric field is applied between thefirst electrode 10 and thesecond electrode 12. Accordingly, theCNT powder 13 a contained in thedispersive liquid 13 will be integrated and erected into a CNT column 14 (as shown inFIG. 4 ) under electric field force. - As shown in
FIG. 4 , theCNT column 14 formed from the vertical DEP solution is of an erect structure and can be used in more application, e.g. electrical connector field. Contrarily, CNT column from the conventional DEP art has a sheet structure and has a limited application. - In the preferred embodiment, preparation of the
dispersive liquid 13 comprises steps of mixing and dispersing theCNT powder 13 a into a miscible liquid which is consisted of 50% distilled water in volume and 50% alcohol in volume, and a process of ultrasonic shock wash 1.5 hours. According to the preferred embodiment, ratio by volume of the water and alcohol may be between 1:1 and 1:3. Moreover, because volume and quality of theCNT powder 13 a are very small, molecular force between theCNT powder 13 a may becomes strong during process of theCNT powder 13 a mixed and dispersed into the miscible liquid containing distilled water and alcohol, which will make theCNT powder 13 a easily intertwined. Therefore, before the actual mixed and dispersed process of the application, the best to be addressed, theCNT powder 13 a are experienced a process of acid treatment. The acid treatment is a known art and uses nitric acid and sulphuric acid for purifying theCNT powder 13 a. Use of the aforementioned dispersive way of CNT powder, can achieve a very good dispersive result. - Referring to
FIGS. 5A-5B , a method called vertical DEP in accordance with a second preferred embodiment of the present invention is shown, which uses vertical electric field to integrate and erect CNT powder into CNT columns with erect structure. According to the method, firstly, abase substrate 11′ is provided with a number ofvias 11 a′ (only one is shown). The vias 11 a′ are arranged in a manner of matrix or other layout. Then, afirst electrode 10 and asecond electrode 12′ is disposed at two sides of thebase substrate 11′ respectively and corresponding to a via 11 a′. According to a preferred embodiment of the present invention, thebase substrate 11′ is made from non-conductive matters. Thefirst electrode 10′ is a substrate made from gold and covering on a lower surface of thesubstrate 11′. Thesecond electrode 12′ is a conductor and of an acicular or columnar shape. According to the preferred embodiment of the invention, diameter of thesecond electrode 12′ is smaller than that of the via 11 a′, so as to control diameter of the CNT column, which will be erected. Thesecond electrode 12′ has a plate structure on a top end thereof for pulling up dispersive liquid 13′ containingCNT powder 13 a′ to form liquid column, thus increasing volume of the dispersive liquid 13′ and the number ofCNT powder 13 a′ involved/used in the vertical DEP process. In the preferred embodiment of the present invention, only onesecond electrode 12′ is shown. In fact, number of thesecond electrode 12′ is equal to number of the vias 11 a′. - Thirdly, the dispersive liquid 13′ having
CNT powder 13 a′ will be dropped into the via 11 a′. Preparation of the dispersive liquid 13′ will be described later. At last, an AC electric field is applied between thefirst electrode 10 and thesecond electrode 12′. Accordingly, theCNT powder 13 a′ contained in the dispersive liquid 13′ will be integrated and erected into a CNT column 14 (as shown inFIG. 4 ) under electric field force. - As shown in
FIG. 4 , theCNT column 14 formed from the vertical DEP solution is of an erect structure and can be used in more application, e.g. electrical connector field. Contrarily, CNT column from the conventional DEP art has a sheet structure and has a limited application. - In the preferred embodiment, preparation of the dispersive liquid 13′ comprises steps of mixing and dispersing the
CNT powder 13 a′ into a miscible liquid which is consisted of 50% distilled water in volume and 50% alcohol in volume, and a process of ultrasonic shock wash 1.5 hours. Moreover, because volume and quality of theCNT powder 13 a′ are very small, molecular force between theCNT powder 13 a′ may becomes strong during process of theCNT powder 13 a′ mixed and dispersed into the miscible liquid containing distilled water and alcohol, which will make theCNT powder 13 a′ easily intertwined. Therefore, before the actual mixed and dispersed process of the application, the best to be addressed, theCNT powder 13 a′ are experienced a process of acid treatment. The acid treatment is a known art and uses nitric acid and sulphuric acid for purifying theCNT powder 13 a′. Use of the aforementioned dispersive way of CNT powder, can achieve a very good dispersive result. - Method for integrating and erecting CNT column can be used in electrical socket field for making an electrical socket. Referring to
FIGS. 6-7 , firstly, aninsulative substrate 2 will be provided. Theinsulative substrate 2 has oppositeupper surface 20,lower surface 22 and a number of throughholes 24 extending through both the surfaces. Then, thefirst electrode 10′ and thesecond electrode 12′ will be disposed at two sides of theinsulative substrate 2 respectively and corresponding to a throughhole 24. Thirdly, the dispersive liquid 13′ havingCNT powder 13 a will be dropped into the throughhole 24. At last, an AC electric field is applied between thefirst electrode 10′ and thesecond electrode 12′. Accordingly, theCNT powder 13 a′ contained in the dispersive liquid 13′ will be integrated and erected into aCNT column 14 along the through hole under electric field force. Accordingly, an electrical socket having CNT structure is provided. - Although the present invention has been described with reference to particular embodiments, it is not to be construed as being limited thereto. Various alterations and modifications can be made to the embodiments without in any way departing from the scope or spirit of the present invention as defined in the appended claims.
Claims (20)
1. A method for integrating and erecting CNT column, comprising:
providing a conductive layer;
applying a non-conductive layer over the conductive layer;
forming a via on the non-conductive layer;
placing an electrode above the via;
deploying dispersive liquid containing CNT powder into the via; and
applying a predetermined AC electric field between the conductive substrate and the electrode for integrating and erecting the CNT powder into CNT column under electric field force.
2. The method as claimed in claim 1 , wherein the conductive layer is made from gold.
3. The method as claimed in claim 1 , wherein the conductive layer and the non-conductive layer is placed on an upper surface of a wafer.
4. The method as claimed in claim 1 , wherein preparation of the dispersive liquid is formed by mixing the CNT powder into a miscible liquid consisted of water and alcohol.
5. The method as claimed in claim 4 , wherein ratio by volume of the water and alcohol is between 1:1 and 1:3.
6. The method as claimed in claim 4 , wherein the water is distilled water.
7. The method as claimed in claim 4 , wherein the CNT powder are experienced a processes of acid treatment before it is mixed into the miscible liquid containing water and alcohol.
8. The method as claimed in claim 1 , wherein the electrode is of an acicular shape.
9. The method as claimed in claim 8 , wherein the electrode is provided with a plate structure on a top end thereof.
10. A method for integrating and erecting CNT column, comprising:
providing an insulative substrate, the insulative substrata having an upper surface, a lower surface and at least one through hole through both the surfaces;
placing a first electrode above upper surface and a second electrode below the lower surface, the first electrode and the second electrode being arranged corresponding to the through hole;
dropping dispersive liquid containing CNT powder into the through hole; and
applying a predetermined AC electric field between the conductive substrate and the electrode for integrating and erecting the CNT powder into CNT column under electric field force along the through hole.
11. The method as claimed in claim 10 , wherein preparation of the dispersive liquid is formed by mixing the CNT powder into a miscible liquid consisted of water and alcohol.
12. The method as claimed in claim 11 , wherein ratio by volume of the water and alcohol is between 1:1 and 1:3.
13. The method as claimed in claim 11 , wherein the water is distilled water.
14. The method as claimed in claim 11 , wherein the CNT powder are experienced a processes of acid treatment before it is mixed into the miscible liquid containing water and alcohol.
15. The method as claimed in claim 10 , wherein the upper surface of the insulative substrate defines a guiding slot communicated with the through hole.
16. The method as claimed in claim 15 , wherein the guiding slot is gradually reduced along an upper-to-lower direction.
17. An electrical connector comprising:
an insulative substrate defining opposite upper and bottom surfaces thereon;
upper and bottom layers applied upon the upper and bottom surfaces, respectively;
a plurality of passageways defined in the substrate, each of said passageways including an upper funnel section extending through the upper layer and a lower slit section extending through the lower layer; and
a carbon nanotube applied upon and filled within the lower slit section; wherein
an upper end of the carbon nanotube extending upwardly beyond an upper end of the lower slit section and into the upper funnel section, a lower end of the carbon nanotube extending downwardly beyond a lower end of the lower slit section.
18. The electrical connector as claimed in claim 17 , wherein the lower end of the carbon nanotube extending downwardly beyond the lower layer.
19. The electrical connector as claimed in claim 17 , wherein the upper tunnel section is asymmetrically arranged with regard to the corresponding lower slit section below.
20. The electrical connector as claimed in claim 17 , wherein the carbon nanotube is formed via electric filed force.