US20100244079A1 - Semiconductor light emitting element and method for fabricating the same - Google Patents
Semiconductor light emitting element and method for fabricating the same Download PDFInfo
- Publication number
- US20100244079A1 US20100244079A1 US12/814,962 US81496210A US2010244079A1 US 20100244079 A1 US20100244079 A1 US 20100244079A1 US 81496210 A US81496210 A US 81496210A US 2010244079 A1 US2010244079 A1 US 2010244079A1
- Authority
- US
- United States
- Prior art keywords
- light emitting
- emitting element
- periodic structure
- dimensional periodic
- semiconductor light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Projections/depressions forming a two-dimensional periodic structure are formed in a surface of a semiconductor multilayer film opposing the principal surface thereof, while a metal electrode with a high reflectivity is formed on the other surface. By using the diffracting effect of the two-dimensional periodic structure, the efficiency of light extraction from the surface formed with the projections/depressions can be improved. By reflecting light emitted toward the metal electrode to the surface formed with the projections/depressions by using the metal electrode with the high reflectivity, the foregoing effect achieved by the two-dimensional periodic structure can be multiplied.
Description
- The present application claims priority under 35 U.S.C. §119(a) to Japanese Patent Application JP 2004-189892, filed Jun. 28, 2004 and Japanese Patent Application JP 2005-188335, filed Jun. 28, 2005, the entire content of which is incorporated herein by reference.
- 1. Technical Field to Which the Invention Pertains
- The present invention relates to a light emitting element using a semiconductor and to a method for fabricating the same.
- 2. Prior Art
- The use of a nitride-based compound semiconductor represented by AlInGaN has enabled the commercialization of light emitting elements which output light at the ultraviolet, blue, and green wavelengths from which it has heretofore been difficult to obtain a sufficient emission intensity, such as a light emitting diode (LED) and a semiconductor laser, so that research and development thereof has been conducted vigorously. Among light-emitting elements, an LED is easier to fabricate and control than a semiconductor laser and longer in lifespan than a fluorescent lamp so that the LED, particularly using a nitride-based compound semiconductor, is considered to be promising as a light source for illumination.
-
FIG. 35 is a perspective view showing a conventional nitride-based compound semiconductor LED. The conventional LED has a structure in which an n-type GaN layer 1002, an InGaNactive layer 1003, and a p-type GaN layer 1004 are formed successively through crystal growth on asapphire substrate 1001. Each of the InGaNactive layer 1003 and the p-type GaN layer 1004 has been removed partly by etching so that the n-type GaN layer 1002 is exposed. An n-side electrode 1006 is formed on the exposed portion of the n-type GaN layer 1002. A p-side bonding electrode 1007 is provided on the p-type GaN layer 1004. - The following is the operation of the LED.
- First, holes injected from the p-
side bonding electrode 1007 are diffused laterally in a p-sidetransparent electrode 1005 to be injected from the p-type GaN layer 1004 into the InGaNactive layer 1003. - On the other hand, electrons injected from the n-
side electrode 1006 are further injected into the InGaNactive layer 1003 through the n-type GaN layer 1002. The recombination of the holes and the electrons in the InGaNactive layer 1003 causes light emission. The light is emitted to the outside of the LED through the p-sidetransparent electrode 1005. - However, it cannot be said that such a conventional structure has sufficiently high light extraction efficiency. The light extraction efficiency is the ratio of light generated in the active layer and emitted from the LED into an air to all the light generated in the active layer. The cause of the low light extraction efficiency of the conventional LED is the refractive index of a semiconductor which is higher than that of the air so that the light from the active layer is totally reflected by the interface between the semiconductor and the air and confined to the inside of the LED. For example, the refractive index of GaN is about 2.45 at a wavelength of 480 nm so that a critical angle of refraction at which total reflection occurs is as small as about 23 degrees. That is, the light emitted from the active layer at an angle larger than the critical refraction angle in terms of a normal to the interface between the semiconductor and the air is totally reflected by the interface between the semiconductor and the air so that the light emitted from the active layer and extractable to the outside of the LED accounts for only about 4% of all the light emitted from the active layer. Accordingly, the problem is encountered that external quantum efficiency (the ratio of light that can be extracted from the LED to currents supplied to the LED) is low and power conversion efficiency (the ratio of a light output that can be produced to all the supplied power) is lower than that of a fluorescent lamp.
- As a solution to the problem, a technology which forms a photonic crystal at the surface of the LED has been proposed, as disclosed in Japanese Laid-Open Patent Publication No. 2000-196152.
-
FIG. 36 is a perspective view showing a conventional LED having an upper surface formed with a photonic crystal. As shown in the drawing, two-dimensional periodic projections/depressions are formed in the p-type GaN layer 1004 according to the conventional embodiment. In the structure, even light emitted from the active layer at an angle larger than the critical refraction angle in terms of the normal to the interface between the semiconductor and the air can have the direction of emission at an angle smaller than the critical refraction angle due to diffraction by the periodic projection/depressions. This increases the ratio of light emitted to the outside of the LED without being totally reflected and improves the light extraction efficiency. In the present specification, the wording “two-dimensional periodic” indicates that a structure is formed to have given spacings (a given period) along a first direction in a plane, while it is also formed to have given spacings (a given period) along a second direction crossing the first direction. - However, there are cases where the following problems occur when projections/depressions are formed in the surface of the LED close to the active layer, such as in the p-type GaN layer.
- Since the p-
type GaN layer 1004 has a high resistivity, the film thickness thereof is preferably as thin as about 0.2 μm in terms of reducing the series resistance of the LED and achieving high-efficiency light emission. To form the projections/depressions in the upper surface of the p-type GaN layer 1004, however, it is necessary to increase the film thickness of the p-type GaN layer 1004. As a result, there are cases where the series resistance of a conventional LED as shown inFIG. 35 increases and the power conversion efficiency thereof lowers. In addition, dry etching for forming the projections/depressions in the p-type GaN layer 1004 causes a crystal defect in the surface of the p-type GaN layer 1004. Since such a crystal defect functions as an electron donor, an electron density in the surface of the n-type GaN layer 1002 increases and the contact resistance thereof lowers. In the p-type GaN layer 1004, however, the crystal defect resulting from an etching damage compensates for the holes so that the formation of an ohmic electrode becomes difficult. This leads to the problem that the contact resistivity increases and the power conversion efficiency lowers. Since the projections/depressions are close to the active layer, etching-induced damage occurs in the active layer during the formation of the projections/depressions. Consequently, the problems of a reduction in internal quantum efficiency (the ratio of electron-hole pairs that are recombined in the active layer and converted to photons to all the electron-hole pairs recombined in the active layer) in the active layer and a reduction in the light emission efficiency of the LED are also likely to occur. - The surface of the LED in which a two-dimensional photonic crystal can conceivably be formed is the main or back surface thereof. In this case, the back surface of the substrate and the interface between the substrate and the semiconductor can be considered as two locations at either of which the photonic crystal is to be formed. In either case, however, the following problem is encountered when the photonic crystal is formed by using the conventional technology. In the case of forming the photonic crystal at the back surface of the substrate, total reflection occurs at the interface between the semiconductor and the substrate so that the effect of improving the light extraction efficiency achieved by the photonic crystal formed in the back surface of the substrate is lower than when the photonic crystal is formed in the semiconductor. In the case of forming the photonic crystal at the interface between the semiconductor and the substrate, on the other hand, the efficiency of diffraction by the periodic projections/depressions lowers due to a small refractive index difference between the semiconductor and the substrate so that the effect of improving the light extraction efficiency is lower than when the photonic crystal is formed at the uppermost surface of the LED.
- It is therefore an object of the present invention to provide a semiconductor light emitting element with a light extraction efficiency higher than achieved conventionally.
- A first semiconductor light emitting element according to the present invention is a semiconductor light emitting element comprising: multiple semiconductor layers formed on a substrate and then delaminated therefrom, wherein a two-dimensional periodic structure is formed in a first principal surface of the multiple semiconductor layers which was in contact with the substrate.
- The arrangement reduces the possibility of damage to the back surface of the multiple semiconductor layers during the fabrication of the element and thereby improves power conversion efficiency to a level higher than achieved conventionally.
- The substrate may be made appropriately of sapphire or the like but is preferably made of silicon. A silicon substrate is more excellent in heat conduction than a sapphire substrate. This makes it possible to cause uniform heat generation throughout the entire two-dimensional periodic structure at the time of delamination (e.g., heat of reaction when the silicon substrate is removed by wet etching).
- A second semiconductor light emitting element according to the present invention is a semiconductor light emitting element comprising: a substrate having a two-dimensional periodic structure in a first principal surface thereof; and multiple semiconductor layers formed over the first principal surface of the substrate and including an active layer for generating light, wherein the substrate is made of silicon.
- The arrangement allows the improvement of the diffraction efficiency without removing the substrate and thereby allows easier fabrication than in the case where the substrate is removed.
- The present inventors have found that the use of silicon for the substrate is appropriate by the following procedure.
- During crystal growth, a silicon substrate is exposed to a high temperature and residual oxygen in a crystal growth furnace forms an extremely thin SiO2 film on the surface of the silicon substrate (the surface of the two-dimensional periodic structure). In contrast to the refractive index of silicon which is about 3.3, the refractive index of SiO2 is about 1.4. Since the refractive index of a light emitting semiconductor layer is typically 2.4 to 3.3, the SiO2 film increases a change in the refractive index of the two-dimensional periodic structure. Because the diffraction efficiency is higher as the refractive index change is larger, the light emission efficiency can further be increased.
- A method for fabricating a semiconductor light emitting element according to the present invention comprises the steps of: (a) forming a first two-dimensional periodic structure in a principal surface of a substrate; and (b) forming multiple semiconductor layers over the first two-dimensional periodic structure.
- The method allows the formation of a structure such as a two-dimensional periodic structure without damaging the back surface of the multiple semiconductor layers and thereby allows the fabrication of a semiconductor light emitting element with an improved light extraction efficiency.
-
FIG. 1 is a perspective view showing a semiconductor light emitting element according to a first embodiment of the present invention; -
FIG. 2 is a view showing the result of theoretically calculating the incident-angle dependence of an amount of light emitted to the outside of the semiconductor light emitting element; -
FIG. 3A is a view showing a structure of an LED in a real space andFIGS. 3B and 3C are views each showing a structure of the light emitting element in a wave-number space; -
FIGS. 4A and 4B are views each showing a structure of the wave-number space when a two-dimensional periodic structure with a 0.1-μm period has been formed in the surface of an n-type GaN layer; -
FIG. 5 is a view showing a refractive index at each portion of a semiconductor layer having a surface formed with a periodic structure; -
FIGS. 6A to 6C are views each showing a structure of the wave-number space when a two-dimensional periodic structure with a 0.2-μm period has been formed on the surface of the n-type GaN layer; -
FIG. 7 is a view showing a structure of the wave-number space when a two-dimensional periodic structure with a 0.4-μm period has been formed in the surface of the n-type GaN layer; -
FIG. 8 is a view for illustrating a solid angle used to calculate light extraction efficiency; -
FIG. 9 is a view showing a value obtained by normalizing light extraction efficiency obtained by using numerical calculation to light extraction efficiency when the surface of the n-type GaN layer is flat; -
FIGS. 10A and 10B are plan views each showing the arrangement of a two-dimensional periodic structure formed in the surface of the n-type GaN layer; -
FIGS. 11A to 11F are perspective views illustrating a method for fabricating the semiconductor light emitting element according to the first embodiment; -
FIG. 12A is a view showing the respective current-voltage characteristics of a conventional semiconductor light emitting element and the semiconductor light emitting element according to the first embodiment andFIG. 12B is a view showing the respective current-light output characteristics of the conventional semiconductor light emitting element and the semiconductor light emitting element according to the first embodiment; -
FIGS. 13A and 13B are perspective views each showing a variation of the semiconductor light emitting element according to the first embodiment; -
FIG. 14 is a perspective view showing a variation of the semiconductor light emitting element according to the first embodiment; -
FIGS. 15A and 15B are perspective views each showing a variation of the semiconductor light emitting element according to the first embodiment; -
FIGS. 16A and 16B are perspective views each showing a variation of the semiconductor light emitting element according to the first embodiment; -
FIG. 17 is a view showing the result of theoretically calculating the dependence of light extraction efficiency on the tilt angle of a depression; -
FIGS. 18A to 18F are perspective views illustrating a second method for fabricating the semiconductor light emitting element shown inFIG. 1 according to the first embodiment; -
FIG. 19A is a perspective view showing a semiconductor light emitting element according to a second embodiment of the present invention andFIG. 19B is a plan view when the semiconductor light emitting element according to the second embodiment is viewed from above; -
FIG. 20A is a view showing the result of theoretically calculating the transmittance T of light incident on the surface of an n-type GaN layer when the surface (back surface) of the n-type GaN layer is formed with projections configured as hexagonal pyramids andFIG. 20B is a view showing the relationship between the period of a two-dimensional periodic structure and light extraction efficiency; -
FIGS. 21A to 21F are perspective views illustrating a method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIGS. 22A to 22C are views illustrating a variation of the method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIGS. 23A and 23B are views illustrating a variation of the method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIGS. 24A and 24B are views illustrating the variation of the method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIGS. 25A and 25B are views illustrating a variation of the method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIGS. 26A to 26C are views illustrating a variation of the method for fabricating the semiconductor light emitting element according to the second embodiment; -
FIG. 27 is a perspective view showing a semiconductor light emitting device according to a third embodiment of the present invention; -
FIG. 28A is a view showing the result of theoretically calculating the transmittance of light when a semiconductor light emitting element is molded with a resin andFIG. 28B is a view showing the result of theoretically calculating the dependence of light extraction efficiency on the period of a two-dimensional periodic structure in the semiconductor light emitting element according to the third embodiment; -
FIGS. 29A to 29D are perspective views illustrating a method for fabricating the semiconductor light emitting element according to the third embodiment; -
FIG. 30 is a cross-sectional view showing a part of a semiconductor light emitting element according to a fourth embodiment of the present invention; -
FIGS. 31A to 31E are cross-sectional views illustrating a method for fabricating the semiconductor light emitting element according to the fourth embodiment; -
FIGS. 32A to 32E are perspective views illustrating a method for fabricating a semiconductor light emitting element according to a fifth embodiment of the present invention; -
FIGS. 33A to 33G are perspective views illustrating a method for fabricating a semiconductor light emitting element according to a sixth embodiment of the present invention; -
FIG. 34 is a perspective view showing a semiconductor light emitting element according to a seventh embodiment of the present invention; -
FIG. 35 is a perspective view showing a conventional semiconductor light emitting element; and -
FIG. 36 is a perspective view showing a conventional semiconductor light emitting element having an upper surface formed with a photonic crystal. - The present invention will be described more specifically in accordance with the individual embodiments thereof. In the present specification, the surface of a semiconductor layer formed by epitaxial growth which is opposite to the principal surface thereof in the direction of crystal growth will be termed a back surface.
-
FIG. 1 is a perspective view showing a semiconductor light emitting element according to a first embodiment of the present invention. As shown in the drawing, the semiconductor light emitting element according to the present embodiment comprises: a p-type GaN layer (first semiconductor layer) 3 formed by epitaxial growth and having a thickness of 200 nm; a high-reflection p electrode (first electrode) 2 formed on the crystal growing surface (principal surface) of the p-type GaN layer 3, made of platinum (Pt) and gold (Au) which are stacked in layers, and having a thickness of 1 μm; anAu plating layer 1 formed on the lower surface of the high-reflection p electrode 2 and having a thickness of 10 μm; a non-doped InGaNactive layer 4 formed on the back surface of the p-type GaN layer 3 and having a thickness of 3 nm; an n-type GaN layer (second semiconductor layer) 5 formed on the back surface of the non-doped InGaNactive layer 4, having a back surface formed with a projecting two-dimensionalperiodic structure 6, and having a thickness of 4 μm; and an n electrode (second electrode) 7 formed on the back surface of the n-type GaN layer 5, made of titanium (Ti) and Al which are stacked in layers, and having a thickness of 1 μm. The lower surface used herein indicates the surface positioned in the, lower part ofFIG. 1 . In the example shown inFIG. 1 , the high-reflection p electrode 2 is provided on the entire principal surface of the p-type GaN layer 3 and then electrode 7 is provided on a part of the back surface of the n-type GaN layer 5. The wording “non-doped” indicates that intentional doping has not been performed with respect to a layer of concern. - The semiconductor light emitting element according to the present embodiment functions as an LED from which light is extracted through the back surface of the n-
type GaN layer 5. The PL peak wavelength of the non-doped InGaNactive layer 4 is 405 nm. As will be described layer, MOCVD (Metal-Organic Chemical Vapor Deposition), MBE (Molecular Beam Epitaxy), or the like will be used as a method for the crystal growth of a nitride-based compound semiconductor composing the semiconductor light-emitting element. - The period of the two-dimensional
periodic structure 6 formed in the back surface of the n-type GaN layer 5, i.e., the spacing between the respective centers of adjacent projections in a two-dimensional plane is 0.4 μm and the height of each of the projections is 150 nm. - —Description of Diffraction at Surface of n-Type GaN Layer—
- A description will be given next to diffraction at the surface (back surface) of the n-type GaN layer of the semiconductor light emitting element according to the present embodiment based on the result of simulation.
FIG. 2 is a view showing the result of theoretically calculating the incident-angle dependence of the transmittance of light emitted from the non-doped InGaN active layer and incident on the back surface (the upper surface in the drawing) of the n-type GaN layer, i.e., an amount of light emitted to the outside of the LED. For the theoretical calculation, numerical analysis in accordance with a FDTD (Finite Difference Time Domain) method was used. It is assumed that the incident angle when the light is incident perpendicularly to the back surface of the n-type GaN layer is zero degree. - As shown in
FIG. 2 , when the surface of the n-type GaN layer is smooth and flat, the transmittance is constant when the incident angle is in the range of zero degree to a total reflection critical angle θc (since the refractive index of GaN is about 2.5, θc=sIn−1 (1/2.5)=about 23 degrees is satisfied) and the value thereof is about 90%. The cause of the reflection of 10% of generated light and the returning of the reflected light to the inside of the LED is Fresnel reflection resulting from the refractive index difference between GaN and the air. The reason for the transmittance which becomes approximately zero when the incident angle exceeds the total reflection critical angle is that total reflection occurs at the interface between GaN and the air. The cause of the occurrence of the total reflection will be described with reference toFIG. 3 . -
FIG. 3A is a view showing a structure of the LED in an actual space (1) andFIGS. 3B and 3C are views each showing a structure of the light emitting element in a wave-number space.FIG. 3B shows the case where the incident angle of light is small andFIG. 3C shows the case where the incident angle of light is large. The semi-circle in each ofFIGS. 3B and 3C is an equi-frequency surface, which indicates the magnitude (Wave Number k=2πn/λ where n is a refractive index and λ is a wavelength in vacuum) of a wave vector to be satisfied by an incident wave, a reflected wave, and a transmitted wave in the LED and in the air. The semi-circle indicates the conservation law of photon energy (hω)2π, h is the Planck's constant). This is because the relationship given by k=ωn/c is established (c is a velocity of light in vacuum). When the structure in the actual space has translational symmetry relative to a horizontal direction as in the case (1) shown inFIG. 3A , there is the conservation law of a wave number component in the horizontal direction which should be observed by each of the incident wave, the reflected wave, and the transmitted wave (which is related to the phase continuity of an electromagnetic wave). The incident angle and an emission angle are determined to satisfy the foregoing two laws. - When the incident angle of light is small as shown in
FIG. 3B , the light can be emitted into the air because the emission angle which satisfies the foregoing two laws exists. When the incident angle of light is large as shown inFIG. 3C , however, there is no emission angle which satisfies the wave number component in the horizontal direction so that the light cannot be emitted into the air. In this case, the transmittance T satisfies T=0 so that, when there is no absorption at the interface between the LED and the air, the reflectivity R satisfies R=1 since the conservation law of optical energy, which is T+R=1, should be satisfied. Consequently, light is totally reflected by the interface between the LED and the air. Even if a structure which reduces Fresnel reflection, such as a no-reflection film, is introduced into the interface between the LED and the air, R=1 is inevitably satisfied under a condition which satisfies the transmittance T=0 so that total reflection is inevitable. -
FIGS. 4A and 4B are views showing a structure of the wave-number space when a two-dimensional periodic structure with a 0.1-μm period is formed in the surface of the n-type GaN. The periodic structure formed in the surface causes diffraction so that it is necessary for a wave number k1// in the horizontal direction of the incident wave and a wave number kk//, in the horizontal direction of the transmitted wave to satisfy the following condition based on Diffraction Vector G=2π/Λ (Λ is a period): -
k 2// =k 1// ±mG (m is an order of diffraction and m=0, ±1, ±2, . . . ). - The transmitted wave occurs when the wave number k2// which satisfies the foregoing expression and the condition for the equi-frequency surface mentioned above exists.
- As shown in
FIG. 4A , when the period of the structure is 0.1 μm and the incident angle is zero degree, the magnitude of the diffraction vector is excessively large so that, if it is assumed that the transmitted wave is diffracted, total reflection occurs since k2// is larger than the equi-frequency surface in the air. In this case, therefore, no diffraction occurs. When the incident angle is 70 degrees at which a 0-order transmitted wave is totally reflected, as shown inFIG. 4B , the condition for total reflection is satisfied even if the light is diffracted. In the case with the period, therefore, total reflection occurs at an incident angle not less than the total reflection critical angle in the same manner as when the surface is flat. -
FIG. 5 is a view showing a refractive index at each portion of a semiconductor layer having a surface formed with the periodic structure. As shown inFIG. 5 , when the period of the periodic structure is smaller than the wavelength of light, the effective refractive index of the two-dimensional periodic structure in the surface of the semiconductor layer lowers due to the projections/depressions thereof so that the two- dimensional periodic structure functions as a layer having a refractive index in the middle of the refractivities of the air and the LED. In this case, the refractive index difference between the air and the LED is reduced so that it becomes possible to suppress Fresnel reflection which occurs when the incident angle is smaller than the total reflection critical angle and improve the transmittance of light when the incident angle is smaller than the total reflection critical angle, as shown inFIG. 2 . - A description will be given next to the case where the surface (back surface) of the n-type GaN layer has a two-dimensional periodic structure with a 0.2-μm period.
FIGS. 6A to 6C are views showing a structure of the wave-number space when the two-dimensional periodic structure with a 0.2-μm period has been formed in the surface of the n-type GaN layer. - Under this condition, total reflection occurs since k2// when light is diffracted is larger than the equi-frequency surface in the air provided that the incident angle of the light is zero degree so that no diffraction occurs. In this case, a 0-order transmitted wave passes through the interface between the n-type GaN layer and the air.
- By contrast, when the surface is flat and the incident angle at which total reflection occurs is 30 degrees or 70 degrees, k2// is smaller than the equi-frequency surface in the air so that the diffracted transmitted wave (the order of diffraction: −1) is allowed to pass through the interface, as shown in
FIGS. 6B and 6C . As a result, the transmittance does not become zero even at an angle not less than the total reflection critical angle, as shown inFIG. 2 . Since the diffraction efficiency also contributes to an actual transmittance, the transmittance presents a complicated curve. In this case, the diffraction vector is relatively large so that diffraction of an order not lower than second does not contribute to transmission. -
FIG. 7 is a view showing a structure of the wave-number space when a two-dimensional periodic structure with a 0.4-μm period has been formed in the surface of the n-type GaN layer. Since the diffraction vector is relatively small with this period, first-order diffraction is related to transmission even when the incident angle of light is zero degree as shown inFIG. 7A . When the incident angle is 35 degrees as shown inFIG. 7B , first- and second-order diffraction contributes to transmission, while second- and third-order diffraction contributes to transmission when the incident angle is 70 degrees as shown inFIG. 7C . As a result, the transmittance becomes relatively high even at an angle not less than the total reflection critical angle, as shown inFIG. 2 . - Thus, as the period of the structure formed in the surface of the n-type GaN layer becomes larger, higher-order diffraction is involved and the behavior of light becomes more complicated.
- Based on the result of the foregoing, analysis, it is assumed that, in the semiconductor light emitting element according to the present embodiment, 0.5λ/N<Λ<20λ/N is satisfied when the refractive index of the semiconductor layer formed with the two-dimensional periodic structure is N and the period of the two-dimensional periodic structure is A. If 0.5λ/N>Λ is satisfied, an angle change caused by diffraction is large and the diffracted light is at an angle over the total reflection critical angle so that the diffracted light is not emitted to the outside of the semiconductor light emitting element. In this case, diffraction with a two-dimensional period cannot improve the light extraction efficiency. If Λ>20λ/N is satisfied, the period becomes extremely larger than the wavelength of light emitted from the active layer so that the effect of diffraction is hardly expected. In view of the foregoing, the condition defined by 0.5λ/N<Λ<20λ/N is preferably satisfied to validate the effect of the two-dimensional periodic structure.
-
FIG. 8 is a view for illustrating a solid angle used to calculate light extraction efficiency. As shown in the drawing, it is necessary to obtain actuallight extraction efficiency 11 by integrating a theoretical reflectivity with an incident angle in consideration of the effect of a solid angle on a transmittance T (θ) at each incident angle. Specifically, η can be derived from the following numerical expression: -
η=∫2πT(θ)·θ·dθ. -
FIG. 9 is a view showing a value obtained by normalizing light extraction efficiency obtained from the foregoing numerical expression to light extraction efficiency when the surface of the n-type GaN layer is flat. As the parameters of calculation, the period A and the height h of each of the projections/depressions are considered. According to the result, the light extraction efficiency is maximum when the height of each of the projections in the surface of the GaN layer is 150 nm. This is because, when the height h of each of the projections/depressions is λ/{2(n2−n1)} (where λ is a light emission wavelength in an air or in vacuum, n1 is the refractive index of the air, and n2 is the refractive index of a semiconductor), the phase of the light component of light passing through the projections/depressions which passes through each of the projections and the phase of the light component thereof which passes through each of the depressions intensify each other through interference so that the diffraction effect achieved by the projections/depression becomes maximum. In this case, h=about 130 nm is satisfied, which nearly coincides with the result of numerical calculation in accordance with the FDTD method. Thus, in the semiconductor light emitting element according to the present embodiment, h is most preferably in the vicinity of an integral multiple of λ/{2(n2−n1)}. It is assumed herein that h approximates to λ/{2(n2−n1)} by considering general performance variations resulting from the fabrication process. - It can be seen from
FIG. 9 that, when the height h of each of the projections/depression is 150 nm, the light extraction efficiency is improved by 2.6 times at the maximum compared with the case where the surface of the n-type GaN layer is flat provided that period Λ is 0.4 to 0.5 μm. To circumvent total reflection, it is necessary to use higher-order diffraction as the period Λ is longer. However, since the diffraction efficiency becomes lower as the order of diffraction is higher, the light extraction efficiency becomes lower as the period is longer when the period Λ is in the range not less than 0.4 μm. For example, when the period of the structure shown inFIG. 2 is 2.0 μm, the transmittance of light at an incident angle not smaller than the total reflection critical angle is lower than that with a 0.4-μm period. -
FIGS. 10A and 10B are plan views showing the arrangement of the two-dimensional periodic structure formed in the surface of the n-type GaN layer. As shown in the drawings, the two-dimensional periodic structure formed in the semiconductor light emitting element according to the present embodiment may be either a tetragonal lattice or a triangular lattice. -
FIGS. 11A to 11F are perspective views illustrating a method for fabricating the semiconductor light emitting element according to the present embodiment which is shown inFIG. 1 . - First, as shown in
FIG. 11A , thesapphire substrate 8 is prepared and theAlGaN layer 9 with a thickness of 1 μm is formed through crystal growth by MOCVD (Metal Organic Chemical Vapor Deposition) on the principal surface of thesapphire substrate 8. If the thickness of theAlGaN layer 9 is 1 μm, crystal defects occurring therein are reduced. The composition of Al in theAlGaN layer 9 is assumed herein to be 100%, though theAlGaN layer 9 may have any Al composition provided that it is transparent to the wavelength of light used for a laser lift-off process performed later. - Next, as shown in
FIG. 11B , the depressed-type two-dimensionalperiodic structure 10 is formed in the principal surface of the AlGaN layer through patterning. In the present step, a resist for an etching mask is patterned by using electron beam exposure, a stepper, and the like. Then, the etching of the AlGaN layer can be performed by using a dry etching technology such as RIE (Reactive Ion Etching) or ion milling, by photoelectrochemical etching performed under the irradiation of ultraviolet light, or by using a wet etching technology such as etching using a heated acid/alkali solution for the etching of the nitride-based compound semiconductor. In this example, the two-dimensionalperiodic structure 10 is formed by electron beam exposure and RIE. It is assumed that the period of the two-dimensionalperiodic structure 10 is 0.4 μm and the depth of each of the depressions is 150 nm. Although the configuration of the two-dimensionalperiodic structure 10 is not particularly limited, the depression has a cylindrical hole in the example shown inFIG. 11B . - Next, as shown in
FIG. 11C , an n-type GaN layer 11 (corresponding to the n-type GaN layer 5 inFIG. 1 ), a non-doped InGaN active layer 12 (corresponding to the non-doped InGaN active layer 4), and a p-type GaN layer 13 (corresponding to the p-type GaN layer 3) are formed in this order by MOCVD over the principal surface of theAlGaN layer 9 formed with the two-dimensionalperiodic structure 10. It is assumed herein that the respective thicknesses of the n-type GaN layer 11, the non-doped InGaNactive layer 12, and the p-type GaN layer 13 are 4 μm, 3 nm, and 200 nm. In the present step, the crystal growth of the n-type GaN layer 11 is performed by setting conditions for the growth such that the two-dimensionalperiodic structure 10 is filled therewith. - Thereafter, the Pt/Au high-reflection p electrode 2 (composed of a multilayer film of Pt and Au) is formed on the principal surface of the p-
type GaN layer 13 by, e.g., electron beam vapor deposition. Further, theAu plating layer 15 with a thickness of about 50 μm is formed by using the Au layer of the high-reflection p electrode 2 as an underlying electrode. - Subsequently, as shown in
FIG. 11D , a KrF excimer laser (at a wavelength of 248 nm) is applied to the back surface of thesapphire substrate 8 for its irradiation in such a manner as to scan the surface of a wafer. The laser beam used for irradiation is not absorbed by thesapphire substrate 8 and theAlGaN layer 9 but is absorbed only by the n-type GaN layer 11 so that GaN is unbonded by local heat generation in the vicinity of the interface with theAlGaN layer 9. As a result, it becomes possible to separate theAlGaN layer 9 and thesapphire substrate 8 from the n-type GaN layer 11 and a device structure made of a GaN-based semiconductor is obtainable. The light source used herein may be any light source provided that it supplies light at a wavelength absorbed by the GaN layer and transparent to the AlGaN layer and the sapphire layer. It is also possible to use a third harmonic (at a wavelength of 355 nm) of a YAG laser or an emission line of a mercury lamp (at a wavelength of 365 nm). - Next, as shown in
FIG. 11E , thesapphire substrate 8 and theAlGaN layer 9 are removed from the state shown inFIG. 11D . As a result, the projecting-type two-dimensionalperiodic structure 6 is formed by self alignment in the back surface of the n-type GaN layer. Since such a semiconductor multilayer film (i.e., a multilayer film composed of the n-type GaN layer 11, the non-doped InGaNactive layer 12, and the p-type GaN layer 13) resulting from the removal of the substrate is an extremely thin film with a thickness of about 5 μm, it has been difficult to form an extremely fine structure such as a photonic crystal by using a conventional photolithographic technology. However, the method according to the present invention allows easy transfer of the extremely fine structure to the surface (back surface) of the semiconductor multilayer film by merely depositing the semiconductor multilayer film over the depressed two-dimensionalperiodic structure 10 formed preliminarily in the substrate and removing the substrate thereafter. - Then, as shown in
FIG. 11F , the Ti/Al n electrode 7 having a thickness of 1 μm is formed on the region of the back surface of the n-type GaN layer 11 in which the two-dimensionalperiodic structure 6 is not formed by vapor deposition and lithography or the like, whereby the semiconductor light emitting element according to the present embodiment is fabricated. -
FIGS. 12 show the characteristics of the semiconductor light emitting element thus obtained, of whichFIG. 12A is a view showing the respective current-voltage characteristics of the semiconductor light emitting elements according to the conventional and present embodiments andFIG. 12B is a view showing the respective current-light output characteristics of the semiconductor light emitting elements according to the conventional and present embodiments. In the drawings, the graphs of the dotted lines represent the characteristics of the semiconductor element having the conventional structure in which the surface of the LED is flat and from which the sapphire substrate has not been removed and the graphs of the solid lines represent the characteristics of the semiconductor light emitting element according to the present embodiment. - From the current-voltage characteristics shown in
FIG. 12A , it will be understood that the semiconductor light emitting elements according to the present and conventional embodiments have substantially equal current-voltage characteristics including substantially the same rising voltages. From the comparison with the conventional embodiment in which the projections/depressions are not formed in the surface of the n-type GaN layer, it will be understood that, in the semiconductor light emitting element fabricated by the method according to the present embodiment, the semiconductor multilayer film receives no processing-induced damage resulting from the formation of the two-dimensional periodic structure. Although thesapphire substrate 8 can be removed by polishing and theAlGaN layer 9 can be removed by etching in the substrate separating step shown inFIGS. 11D and 11E , a method which uses a laser is more preferable because it is completed in a shorter period of time. - From the current-light output characteristic shown in
FIG. 12B , on the other hand, it will be understood that, under the same current, the light output of the semiconductor light emitting element according to the present embodiment has increased to a value substantially five times the light output of the semiconductor light emitting element according to the conventional embodiment. The value is about double the theoretically calculated value shown inFIG. 2 . This is because, due to the two-dimensional periodic structure in the surface of the LED, the efficiency of light extraction from the surface has increased to about 2.5 times the efficiency of light extraction from the flat surface of the conventional LED and, in addition, a high-reflection p electrode 14 formed on the lower surface of the LED (the back surface of the p-type GaN layer 13) allows the light emitted from the non-doped InGaNactive layer 12 toward the high-reflection p electrode 14 to be reflected efficiently to the two-dimensionalperiodic structure 6. - From
FIG. 12B , it will also be understood that the light output of the conventional structure is saturated under a large current, while the light output of the element according to the present embodiment is not saturated even under a large current over 100 mA. This is because heat generated in the active layer of the conventional structure is dissipated through the n-type semiconductor layer as thick as several micrometers and through the sapphire substrate with a poor heat conduction property. This is also because the light emitting element according to the present embodiment has an excellent heat dissipation property because heat from the active layer can be dissipated from the p-type semiconductor as thin as submicron meters through the Au plating layer with a high thermal conductivity. - Thus, even under a large current, the
Au plating layer 15 allows the retention of the improved light extraction efficiency achieved by the two-dimensionalperiodic structure 6. -
FIG. 13A and 13B ,FIG. 14 , andFIGS. 15A and 15B are perspective views showing variations of the semiconductor light emitting element according to the present embodiment.FIGS. 16A and 16B are perspective views each showing a variation of the method for fabricating the semiconductor light emitting element according to the present embodiment. - Although the projecting-type two-dimensional
periodic structure 6 has been formed by using the depressed-type two-dimensionalperiodic structure 10 formed in the surface of theAlGaN layer 9 on thesapphire substrate 8 as a “mold” in the semiconductor light emitting element according to the present embodiment, the same effects are also achievable by forming the projecting-type two-dimensionalperiodic structure 16 in the surface of theAlGaN layer 9 and thereby forming a depressed-type two dimensionalperiodic structure 17 in the surface of the LED, as shown inFIGS. 13A and 13B . That is, the incident light can be diffracted provided that the two-dimensional periodic structure has been formed whether the structure in the surface of the LED is of the projecting type or the depressed type. - Besides the method which forms the projections/depressions in the
AlGaN layer 9, a method as shown inFIG. 14 which forms the projecting or depressed two-dimensionalperiodic structure 16 in the principal surface of thesapphire substrate 8 also allows the implementation of a semiconductor light emitting element in which the projecting-type or depressed-type two-dimensional periodic structure is formed in the surface of theAlGaN layer 9 by using the projecting or depressed two-dimensionalperiodic structure 16 as a mold. - Alternatively, as shown in
FIG. 15A , it is also possible to form the projecting-type two-dimensionalperiodic structure 16 structure by forming an oxide film such as a SiO2 film, a nitride film such as a SiN film, or a metal film such as a tungsten (W) film on thesapphire substrate 8 and then patterning the formed film. As shown inFIG. 15B , a light emitting element having the same characteristics as the semiconductor light emitting element according to the present embodiment can also be fabricated by forming the projecting two-dimensionalperiodic structure 16 composed of an oxide film, a nitride film, or a metal film in the principal surface of theAlGaN layer 9. - If a SiC substrate is used in place of the sapphire substrate, the substrate can be removed by selective dry etching performed with respect to SiC and GaN. If a Si substrate is used, the substrate can easily be removed by wet etching. An additional detailed description will be given later to the case where the Si substrate is used.
- In the case where the depressed two-dimensional
periodic structure 17 formed in the back surface (upper surface) of the n-type GaN layer 11 through the removal of the substrate has a small depth or the inclination of the inner tilted surface of each of the depressions is not perpendicular, the configuration of the depression can be adjusted by performing processes as shown inFIGS. 16A and 16B after the removal of the substrate. - Specifically, as shown in
FIG. 16A , an LED structure and a counter electrode made of Pt or the like are immersed in an electrolytic solution such as an aqueous KOH solution and a voltage is applied between the LED and the counter electrode by using the p side of the LED as a positive electrode. Consequently, anodic oxidation causes the etching of GaN, as shown inFIG. 16B , but only the depression is etched due to the localization of an electric field so that the depth of the depression is increased successfully. The localization of the electric field to the depression also causes the etching resulting from the anodic oxidation to proceed perpendicularly. As a result, the depression having a perpendicular tilted surface can be formed by the etching resulting from the anodic oxidation even when the inner tilted surface of the depression after the removal of the substrate is not vertical. -
FIG. 17 is a view showing the result of theoretically calculating the dependence of the light extraction efficiency on the tilt angle of the depression. It is assumed herein that the tilt angle is obtained by subtracting, from 180 degrees, the angle formed between the side surface of the depression and the upper surface of the n-type GaN layer 11 in a vertical cross section, as shown in the left part of the drawing. From the result shown inFIG. 17 , it will be understood that the light extraction efficiency lowers abruptly when the tilt angle becomes 50 degrees or less. That is, when the tilt angle of the two-dimensional periodic structure that can be formed after the removal of the substrate is small, the tilt angle can be increased by the anodic oxidation etching described above and the high light extraction efficiency can be implemented. Thus, in the semiconductor light emitting element according to the present embodiment, the tilt angle of the two-dimensional periodic structure is adjusted preferably to 50 degrees or more. Even when the two-dimensional periodic structure has a projecting configuration, the tilt angle is preferably 50 degrees or more in terms of improving the light extraction efficiency. -
FIGS. 18A to 18F are perspective views illustrating a second method for fabricating the semiconductor light emitting element shown inFIG. 1 according to the first embodiment. - First, as shown in
FIG. 18B , the depressed-type two-dimensionalperiodic structure 10 is formed in the principal surface of aSi substrate 51 through patterning. In the present step, a resist for an etching mask is patterned by using electron beam exposure, a stepper, and the like. Then, in the present step, the etching of theSi substrate 51 can be performed by using a dry etching technology such as RIE (Reactive Ion Etching) or ion milling, by photoelectrochemical etching performed under the irradiation of ultraviolet light, or by using a wet etching technology such as etching using a heated acid/alkali solution. In this example, the two-dimensionalperiodic structure 10 is formed in theSi substrate 51 by electron beam exposure and RIE. It is assumed that the period of the two-dimensionalperiodic structure 10 is 0.4 μm and the depth of each of the depressions is 150 nm. Although the configuration of the two-dimensionalperiodic structure 10 is not particularly limited, the depression has a cylindrical hole in the example shown inFIG. 18B . - Next, as shown in
FIG. 18C , the n-type GaN layer 11 (corresponding to the n-type GaN layer 5 inFIG. 1 ), the non-doped InGaN active layer 12 (corresponding to the non-doped InGaNactive layer 4 inFIG. 1 ), and the p-type GaN layer 13 (corresponding to the p-type GaN layer 3 inFIG. 1 ) are formed in this order by MOCVD over the principal surface of theSi substrate 51 formed with the two-dimensionalperiodic structure 10. It is assumed herein that the respective thicknesses of the n-type GaN layer 11, the non-doped InGaNactive layer 12, and the p-type GaN layer 13 are 4 μm, 3 nm, and 200 nm. In the present step, the crystal growth of the n-type GaN layer 11 is performed by setting conditions for the growth such that the two-dimensionalperiodic structure 10 is filled therewith. - Thereafter, as shown in
FIG. 18D , the Pt/Au high-reflection p electrode 14 (composed of a multilayer film of Pt and Au) is formed on the principal surface of the p-type GaN layer 13 by, e.g., electron beam vapor deposition. Further, theAu plating layer 15 with a thickness of about 50 μm is formed by using the Au layer of the high-reflection p electrode 14 as an underlying electrode. - Subsequently, as shown in
FIG. 18E , theSi substrate 51 is removed by using an etchant containing a HF/HNO3 mixture. As a result, the projecting-type two-dimensionalperiodic structure 6 is formed by self alignment in the back surface of the n-type GaN layer 11. Since such a semiconductor multilayer film (i.e., a multilayer film composed of the n-type GaN layer 11, the non-doped InGaNactive layer 12, and the p-type GaN layer 13) resulting from the removal of the substrate is an extremely thin film with a total thickness of about 4 μm to 5 μm, it has been difficult to form an extremely fine structure such as a photonic crystal by using a conventional photolithographic technology. However, the method according to the present invention allows easy transfer of the extremely fine structure to the surface (back surface) of the semiconductor multilayer film by merely depositing the semiconductor multilayer film over the depressed two-dimensionalperiodic structure 10 formed preliminarily in the substrate and removing the substrate thereafter. - Then, as shown in
FIG. 18F , the Ti/Al n electrode 7 having a thickness of 1 μm is formed on the region of the back surface of the n-type GaN layer 11 in which the two-dimensionalperiodic structure 6 is not formed by vapor deposition and lithography or the like, whereby the semiconductor light emitting element according to the present embodiment is fabricated. - Since Si is excellent in heat conduction, it becomes possible to cause uniform heat generation throughout the entire two-dimensional periodic structure at the time of delamination (e.g., heat of reaction when the Si substrate is removed by wet etching). As a result, a chemical reaction occurs evenly when the
Si substrate 51 is delaminated and damage to the two-dimensionalperiodic structure 6 at the time of delamination can be prevented. - In general, a semiconductor light emitting element is made of a group III-V semiconductor which does not achieve lattice matching with Si and has a thermal expansion coefficient different from that of Si. Accordingly, extremely small defects occur at the projecting/depressed interface to allow easy separation of the
Si substrate 51 from the semiconductor multilayer film. - The Si substrate is not flat and has a projecting/depressed structure so that at least two or more crystal planes exist at the projecting/depressed interface. Since the wet etching speed of Si differs from one crystal plane to another, the etching speed changes periodically in the two-dimensional
periodic structure 10 to cause an extremely slight stir and allow higher-speed etching. - By thus using the Si substrate as a substrate for forming the two-dimensional periodic structure, the productivity of the semiconductor light emitting element can be improved.
-
FIG. 19A is a perspective view showing a semiconductor light emitting element according to a second embodiment of the present invention.FIG. 19B is a plan view when the semiconductor light emitting element according to the second embodiment is viewed from above. The semiconductor light emitting element according to the present embodiment is different from the semiconductor light emitting element according to the first embodiment in that a projecting two-dimensionalperiodic structure 18 formed in the upper surface (back surface) of the n-type GaN layer 5 is configured as polygonal pyramids. - As shown in
FIGS. 19A and 19B , the semiconductor light emitting element according to the present embodiment comprises: the p-type GaN layer 3 formed by epitaxial growth and having a thickness of 200 nm; the high-reflection p electrode 2 formed on the crystal growing surface of the p-type GaN layer 3, made of platinum (Pt) and gold (Au) which are stacked in layers, and having a thickness of 1 μm; theAu plating layer 1 formed on the lower surface of the high-reflection p electrode 2 and having a thickness of 10 μm; the non-doped InGaNactive layer 4 formed on the back surface of the p-type GaN layer 3 and having a thickness of 3 nm; the n-type GaN layer 5 formed on the back surface of the non-doped InGaNactive layer 4, having a back surface formed with a two-dimensionalperiodic structure 18 composed of projections each configured as a hexagonal pyramid, and having a thickness of 4 μm; and then electrode 7 formed on the back surface of the n-type GaN layer 5, made of titanium (Ti) and Al which are stacked in layers, and having a thickness of 1 μm. In the same manner as in the first embodiment, the PL peak wavelength of the non-doped InGaNactive layer 4 is 405 nm. The side surface of the projecting structure in the back surface of the n-type GaN layer 5 is composed of the {10−1−1} plane of GaN. The period of the two-dimensionalperiodic structure 18, i.e., the spacing between the respective centers of the adjacent projections in a two-dimensional plane is 1.0 μm and the height of each of the projections is 950 nm. -
FIG. 20A is a view showing the result of theoretically calculating the transmittance T of light emitted from the active layer and incident on the surface of the n-type GaN layer when the projections each configured as the hexagonal pyramid are formed in the surface (back surface) of the n-type GaN layer.FIG. 20B is a view showing the relationship between the period of the two-dimensional periodic structure and the light extraction efficiency.FIG. 20B assumes 1 when the surface of the n-type GaN layer is flat and shows, for comparison, the cases where the two-dimensional periodic structure has a projecting configuration and a projecting/depressed configuration (the same configuration as shown in the first embodiment). - From the result shown in
FIG. 20A , it will be understood that, even when the period of the two-dimensional periodic structure is as long as 1.0 μm, the projecting structure shows a high transmittance at an incident angle in the vicinity of 45 degrees. Thus, in the semiconductor light emitting element according to the present embodiment in which the cross section of the two-dimensional periodic structure is configured as a triangular waveform, the angle between the tilted surface of the two-dimensional periodic structure and the incident light approaches 90 degrees when the angle of light emitted from the active layer and incident upon the two-dimensional periodic structure in the surface of the semiconductor light emitting element is large so that the diffraction efficiency is increased. Since the light at a large incident angle accounts for a large proportion in the light emitted from the active layer, high light extraction efficiency is achieved. - From the result shown in
FIG. 20B , it will be understood that the projecting structure shows the same high light emission efficiency as achieved by the projecting/depressed structure and particularly retains the effect of increasing the light extraction efficiency even with a longer period. It is to be noted that, with a period of 1.0 μm, the light extraction efficiency obtained from the surface formed with the two-dimensional periodic structure increases to 2.7 times the original light extraction efficiency. - A description will be given next to a method for fabricating the semiconductor light emitting element according to the present embodiment.
-
FIGS. 21A to 21F are perspective views illustrating the method for fabricating the semiconductor light emitting element according to the present embodiment. In the fabrication method according to the present embodiment, the steps shown inFIGS. 21A to 21E are substantially the same as those in the fabrication method according to the first embodiment shown inFIG. 11 so that the description thereof will be omitted. However, it is assumed that the period of the depressed-type two-dimensionalperiodic structure 10 formed in the principal surface of theAlGaN layer 9 is 1.0 μm and the depth of the depression is 150 nm. - That is, in the fabrication method according to the present embodiment, the
sapphire substrate 8 is removed from the main body of the light emitting element in the steps prior to and inclusive of that shown inFIG. 21E so that the two-dimensionalperiodic structure 6 composed of, e.g., cylindrical projections is formed by self alignment on the back surface of the n-type GaN layer 11. - Next, in the step shown in
FIG. 21F , wet etching using an aqueous KOH solution is performed with respect to the n-type GaN layer 11 formed with the projecting-type two-dimensionalperiodic structure 6. It is well known that, in an etching process using KOH, an etching speed has different conditions depending on crystal planes. Under such conditions, the projecting-type two-dimensionalperiodic structure 6 described above is changed by etching to the two-dimensionalperiodic structure 18 of a hexagonal pyramid type as shown inFIG. 20F . In the embodiment shown herein, etching is performed by using an aqueous KOH solution at a concentration of 0.1 M to form the two-dimensionalperiodic structure 18 composed of hexagonal pyramids each using the crystal plane {10−1−1} as a tilted surface. The fabrication method is characterized in that, since the specified crystal plane is used as the tilted surface, the two-dimensional periodic structure having a triangular cross section can be formed easily with high reproducibility. - In the semiconductor light emitting element according to the present embodiment, the light extraction efficiency is improved to about double the result of the theoretical calculation shown in
FIG. 20B (about 5.3 times the light extraction efficiency achieved in the conventional embodiment) since, compared with the case where the surface of the n-type GaN layer is flat, reflection from the high-reflection p electrode 2 can also be used. In addition, heat generated in the active layer can be dissipated through the p-type GaN layer 13 which is as thin as submicron meters and through theAu plating layer 15 having a high thermal conductivity. Accordingly, the effect of improving the light extraction efficiency achieved by the two-dimensional periodic structure is also retained even when a large current of 100 mA flows in the semiconductor light emitting element according to the present embodiment. Although the high-reflection p electrode 2 may also be composed of a material other than a multilayer film consisting of Pt and Au films, it is preferable in terms of practical use for the high-reflection p electrode 2 to have a reflectivity of 80% or more with respect to the peak wavelength of light generated in the active layer. Specifically, the high-reflection p electrode 2 is preferably a metal film containing at least one of an Au film, a Pt film, a Cu film, an Ag film, and a Rh film. - To retain the excellent heat dissipation property, the
Au plating layer 15 preferably has a thickness of 10 gm or more. As the material of theAu plating layer 15, Au is most preferable but a metal such as Cu or Ag can also be used because of the relatively high thermal conductivity thereof. - The fabrication method described above can reduce the damage to the n-type GaN layer compared with the method which forms the two-dimensional periodic structure directly by etching so that the current-voltage characteristic is substantially the same as when the two-dimensional periodic structure is not formed.
-
FIGS. 22A to 22C ,FIGS. 23A and 23B ,FIGS. 24A and 24B ,FIGS. 25A and 25B , andFIGS. 26A to 26C are views showing variations of the method for fabricating the semiconductor light emitting device according to the present embodiment. - Although the fabrication method according to the present embodiment has formed the two-dimensional periodic structure having a triangular vertical cross section in the surface of the semiconductor (n-type GaN layer 11) by using the
sapphire substrate 8 or theAlGaN layer 9 formed with the depressed two-dimensional periodic structure, the depressed two-dimensionalperiodic structure 17 may also be transferred to the semiconductor surface by using thesapphire substrate 8 or theAlGaN layer 9 formed with a projecting two-dimensionalperiodic structure 16 as shown inFIGS. 22A to 22C . The method allows a depressed-type two-dimensionalperiodic structure 19 having a triangular vertical cross section to be formed in the semiconductor surface by using the wet etching process described above. Even in the case where each of the depressions of the two-dimensionalperiodic structure 19 has a configuration obtained by hollowing a hexagonal pyramid, the same high light extraction efficiency as achieved by the semiconductor light emitting element according to the present embodiment is achievable. - If the two-dimensional
periodic structure 20 is preliminarily formed in the surface of theAlGaN layer 9 to have a triangular vertical cross-sectional configuration as shown inFIGS. 23A and 23B andFIGS. 24A and 24B , the two-dimensionalperiodic structures sapphire substrate 8 and theAlGaN layer 9 are removed. - If the material of the layer in which the two-dimensional periodic structure is formed is a hexagonal system semiconductor such as AlGaN, hexagonal pyramids each having a tilted surface composed of a specific crystal plane can be formed by the same method as described above. For example, when a Ti film having an opening corresponding to a portion to be processed into a depressed configuration is formed as an
etching mask 21 on the AlGaN surface, as shown inFIG. 25A , and then etching is performed using an aqueous KOH solution at 100° C., the two-dimensionalperiodic structure 20 is formed in the surface theAlGaN layer 9. In this case also, the two-dimensional periodic structure can be formed with high reproducibility since the tilted surface is composed of a specific crystal plane such as {10−1−1}. - In the case where a substrate to be formed with the two-dimensional periodic structure is made of a tetragonal system semiconductor, such as a Si substrate using the (001) plane for the principal surface, the
etching mask 21 made of Ti is formed into a tetragonal lattice configuration with a two-dimensional period, as shown inFIG. 26A , and then etched in an aqueous KOH solution at 70° C. This allows the two-dimensionalperiodic structure 20 configured as square pyramids to be formed easily in the substrate with high reproducibility, as shown inFIG. 26B , and also allows the two-dimensionalperiodic structure 18 composed of holes configured as square pyramids to be transferred from the substrate to the semiconductor surface, as shown inFIG. 26C . -
FIG. 27 is a perspective view showing a semiconductor light emitting device according to a third embodiment of the present invention. The semiconductor light emitting device according to the present embodiment is a resin-molded semiconductor light emitting device obtained by mounting the semiconductor light emitting element according to the first or second embodiment on a mountingsubstrate 22 and then molding the periphery of the light emitting element with a hemispherical dome-shapedresin 23. In.FIG. 27 , those of the components of the semiconductor light emitting element which are the same as shown inFIG. 1 are designated by the same reference numerals. - By thus molding the light emitting element with the dome-shaped resin, the light extraction efficiency of the semiconductor light emitting element can be improved, as will be described herein below.
-
FIG. 28A is a view showing the result of theoretically calculating the transmittance of light when the semiconductor light emitting element is molded with the resin.FIG. 28B is a view showing the result of theoretically calculating the dependence of light extraction efficiency on the period of a two-dimensional periodic structure in the semiconductor light emitting device according to the present embodiment. For comparison,FIG. 28A also shows the case where the semiconductor light emitting element is not molded with the resin and the case where the surface of the semiconductor light emitting element is flat. In the calculation the result of which is shown in the drawings, it is assumed that the refractive index of the resin is 1.5. In the calculation the result of which is shown inFIG. 28B , it is assumed that projections/depressions each having a perpendicularly tilted surface are arranged to forth a two-dimensional periodic structure and the height of each of the projections is 150 nm. - From the result shown in
FIG. 28A , it will be understood that, when the two-dimensional periodic structure with a 0.4-μm period is provided, the transmittance of incident light is higher at substantially every angle in the semiconductor light emitting element molded with the resin than in the semiconductor light emitting element which is not molded with the resin. Since resin molding can also increase the transmittance of light even in the semiconductor light emitting element in which the two-dimensional periodic structure is not provided, it will be understood that the transmittance of light can significantly be improved by resin molding irrespective of the period of the two-dimensional periodic structure. - The reason for the improved transmittance of light is that, even when the surface of the semiconductor light emitting element is flat, the total reflection critical angle is enlarged by resin molding and Fresnel reflection is reduced thereby even at an incident angle not more than the total reflection critical angle. In other words, the transmittance of light is improved due to a reduction in the difference between the refractive index (which is 2.5) of the inside of the semiconductor light emitting element and the refractive index (which is 1.5) of the outside thereof.
- From the result shown in
FIG. 28B , it will be understood that resin molding can further enhance the effect of improving the light extraction efficiency achieved by the two-dimensional periodic structure and, at the maximum, the light extraction efficiency has become 3.8 times the light extraction efficiency achieved in the conventional embodiment. This is because the molding resin is shaped like a hemispherical dome so that the light extracted from the semiconductor light emitting element into the resin is incident perpendicularly to the interface between the resin and the air due to the two-dimensional periodic structure in the surface of the semiconductor light emitting element and emitted into the air with approximately 100% efficiency. By thus molding the light emitting element formed with the two-dimensional periodic structure with the dome-shaped resin, the light extraction efficiency of the semiconductor light emitting device according to the present embodiment has been improved greatly. - In the semiconductor light emitting device according to the present embodiment, an actually measured value of the light extraction efficiency has improved to about double the result of the theoretical calculation shown in
FIG. 28B (7.5 times the light extraction efficiency achieved in the conventional embodiment) since, compared with the case with the flat surface, reflection from the back surface formed with the two-dimensional periodic structure due to the high-reflection p electrode 2 can also be used. In addition, due to excellent heat dissipation from the p-type semiconductor, which is as thin as submicron meters, through the Au plating layer with a high thermal conductivity, the effect of enhancing the light extraction efficiency allows the retention of the improved light extraction efficiency achieved by the two-dimensional periodic structure even when a large current of 100 mA flows in the electrode. - A description will be given next to a method for fabricating the semiconductor light emitting device according to the present embodiment.
-
FIGS. 29A to 29D are perspective views illustrating the method for fabricating the semiconductor light emitting device according to the present embodiment. - First, as shown in
FIG. 29A , the semiconductor light emitting element according to the first or second embodiment is fabricated by using the method for fabricating the semiconductor light emitting element according to the first embodiment shown inFIGS. 11 or the method for fabricating the semiconductor light emitting element according to the second embodiment shown inFIGS. 21 . - Next, as shown in
FIG. 29B , the semiconductor light emitting element is mounted on the mountingsubstrate 22. Thereafter, theresin 23 is applied dropwise to the semiconductor light emitting element. - Then, as shown in
FIG. 29C , theresin 23 is pressed by using amold die 24 provided with a hemispherical cavity during the period after the semiconductor light emitting element is covered with theresin 23 and before theresin 23 is set. As a result, theresin 23 is molded into a hemispherical dome-shaped configuration, as shown inFIG. 29D . Thereafter, the resin is set under ultraviolet light. By the method described above, the semiconductor light emitting device according to the present embodiment is fabricated. - Although it has been difficult to form the resin into a hemispherical configuration with high reproducibility by using a conventional technology which simply applies and molds a resin, the fabrication method according to the present embodiment enables stable molding of a resin into the same configuration.
- It is to be noted that a method which molds a resin into a hemispherical configuration using a mold die as described above is also applicable to a semiconductor light emitting element according to an embodiment other than the first and second embodiments of the present invention.
-
FIG. 30 is a cross-sectional view showing a part of a semiconductor light emitting element according to a fourth embodiment of the present invention. The semiconductor light emitting element according to the present embodiment is different from the first and second semiconductor light emitting elements in that thesapphire substrate 8 and theAlGaN layer 9 remain mounted on the amountingsubstrate 22 without being removed and that the high-reflection p electrode 2 and then electrode 7 are formed on the same side when viewed from the n-type GaN layer 5. - Specifically, the semiconductor light emitting element according to the present embodiment shown in
FIG. 30 comprises: the p-type GaN layer 3 formed by epitaxial growth and having a thickness of 200 nm; the high-reflection p electrode 2 formed on the crystal growing surface (principal surface) of the p-type GaN layer 3, made of platinum (Pt) and gold (Au) which are stacked in layers, and having a thickness of 1 μm; the non-doped InGaNactive layer 4 formed on the back surface of the p-type GaN layer 3 and having a thickness of 3 nm; an n-type GaN layer 5 formed on the back surface of the non-doped InGaNactive layer 4 and having a thickness of 4 μm; then electrode 7 formed under the n-type GaN layer 5, made of Ti and Al which are stacked in layers, and having a thickness of 1 μm; theAlGaN layer 9 provided on the back surface of then-type GaN layer 5 and having a principal surface (surface facing the n-type GaN layer 5) formed with the projecting-type two-dimensionalperiodic structure 16; and thesapphire substrate 8 disposed on the back surface of theAlGaN layer 9. In the example shown inFIG. 30 , the semiconductor light emitting element has been mounted on the mountingsubstrate 22 and the high-reflection p electrode 2 and then electrode 7 are particularly connected to the mountingsubstrate 22 viabumps 25 made of Au. The period of the two-dimensionalperiodic structure 16, i.e., the spacing between the respective centers of the adjacent projections in a two-dimensional plane is 0.4 μm and the height of each of the projections/depressions is 150 nm. In the example shown inFIG. 30 , the n-type GaN layer 5 is formed not to be buried in the two-dimensionalperiodic structure 16. If the n-type GaN layer 5 is formed to be buried in the two-dimensionalperiodic structure 16, the light extraction efficiency lowers so that it is formed preferably not to be buried therein. - By thus mounting the semiconductor light emitting element with the substrate made of sapphire or the like being left, the light emitted from the non-doped InGaN
active layer 4 propagates in the light emitting element without undergoing a loss caused by total reflection or Fresnel reflection since there is substantially no refractive index difference till theAlGaN layer 9 is reached. In the conventional structure, however, the refractive index difference between the sapphire substrate (with a refractive index of 1.6) and the AlGaN layer (with a refractive index of 2.5) is large so that light at a large incident angle is totally reflected at the interface between the sapphire substrate and the AlGaN layer, returns to the inside of the semiconductor multilayer film, and is therefore unextractable to the outside of the LED. By contrast, if a two-dimensional periodic structure is formed in the back surface of an AlGaN layer as in the semiconductor light emitting element according to the present embodiment, diffraction by the two-dimensional periodic structure changes the direction of propagation. As a result, if the back surface of the AlGaN layer is flat, the light at a large incident angle that has been totally reflected at the interface between the sapphire substrate and the AlGaN layer and occupying a large proportion in the solid angle is allowed to be incident on the sapphire substrate without being totally reflected. Since the sapphire substrate is transparent and the refractive index difference between itself and the air is small, the majority of the light incident upon the sapphire substrate is emitted into the air. - In the case where resin molding is performed, the refractive index difference between the sapphire substrate and a resin (with a refractive index of about 1.5) is further reduced and, if the resin is configured as a hemispherical dome, the light extraction efficiency can further be improved.
- A description will be given next to a method for fabricating the semiconductor light emitting element according to the present embodiment.
FIGS. 31A to 31E are cross-sectional views illustrating the method for fabricating the semiconductor light emitting element according to the present embodiment. - First, as shown in
FIG. 31A , theAlGaN layer 9 is formed through crystal growth by, e.g., MOCVD on thesapphire substrate 8. The thickness of theAlGaN layer 9 is assumed herein to be 1μm for a reduction in crystal defects. The composition of Al in theAlGaN layer 9 is assumed herein to be 100%, though theAlGaN layer 9 may have any Al composition provided that it is transparent relative to the wavelength of light used in a laser lift-off process performed later. Subsequently, the AlGaN layer is pattered into the depressed- or projecting-type two-dimensionalperiodic structure 16 by exposure using a stepper and RIE. It is assumed herein that the period of the two-dimensionalperiodic structure 16 is 0.4 μm and the depth of each of the depressions (or the height of each of the projections) is 150 nm. - Next, as shown in
FIG. 31B , the n-type GaN layer 5, the non-doped InGaNactive layer 4, the p-type GaN layer 3 are formed successively by MOCVD on the principal surface of theAlGaN layer 9 formed with the two-dimensionalperiodic structure 16. The crystal growth of the n-type GaN layer 5 is performed by setting conditions for the growth such that the two-dimensional periodic structure is not filled therewith. - Thereafter, etching is performed with respect to a region to partially expose the principal surface of the n-
type GaN layer 5, as shown inFIG. 31C . Then, the Pt/Au high-reflection p electrode 2 is formed on the principal surface of the p-type GaN layer 3, while the Ti/Al n electrode 7 is formed on the exposed portion of the principal surface of the n-type GaN layer 5, each by electron beam vapor deposition. - Next, as shown in
FIG. 31D , the semiconductor light emitting element is mounted on the mountingsubstrate 22 formed with thebumps 25 for the n electrode and for the high-reflection p electrode, whereby the semiconductor light emitting element according to the fourth embodiment shown inFIG. 31E is obtained. - In the semiconductor light emitting element thus fabricated, the light extraction efficiency is improved to about double the result of the theoretical calculation shown in
FIG. 28B (quadruple the light extraction efficiency achieved in the conventional light emitting element) since, compared with the case where the principal surface of theAIGaN layer 9 is flat, light reflected from the lower surface of the LED due to the high-reflection p electrode 2 can also be used. - In addition, the heat generated in the active layer can be dissipated from the p-
type GaN layer 3 as thin as submicron meters through thebumps 25 each having a high thermal conductivity so that an excessive temperature increase is prevented in the semiconductor light emitting element according to the present embodiment. Moreover, the increase rate of the light output from the semiconductor light emitting element to an input current thereto when the input current is small remains unchanged even when a large current of 100 mA flows in the electrode. - Although the present invention has formed the two-dimensional periodic structure in the principal surface of the
AlGaN layer 9 on thesapphire substrate 8, the two-dimensional periodic structure may also be formed in the principal surface of thesapphire substrate 8. The substrate may also be composed of any material other than sapphire provided that it is transparent to the light emitted from the active layer. - When the back surface (principal surface) of the
sapphire substrate 8 is rough, the light extraction efficiency is improved to 4.5 times the light extraction efficiency achieved in the conventional structure. This is because the presence of the rough back surface reduces a loss resulting from total reflection at the interface between the sapphire substrate and the air. When the back surface of thesapphire substrate 8 is rough, the autocorrelation distance T in the back surface of thesapphire substrate 8 preferably satisfies 0.5λ/N<T<20λ/N and a height distribution D in a perpendicular direction preferably satisfies 0.5λ/N<D<20λ/N in terms of sufficiently reducing the loss. - When the semiconductor light emitting element is molded with a hemispherical resin, the light extraction efficiency is improved to 6 times the light extraction efficiency achieved in the conventional structure. This is because the small refractive index difference between the resin and the sapphire reduces the loss resulting from total reflection at the interface between the sapphire substrate and the resin.
- In the semiconductor light emitting element according to the present embodiment, a substrate made of one selected from the group consisting of GaAs, InP, Si, SiC, and AlN may also be used instead of the sapphire substrate.
- Although the example shown in
FIG. 30 has formed the two-dimensionalperiodic structure 16 in the principal surface of theAlGaN layer 9, if a Si substrate is used in place of the sapphire substrate, the two-dimensional periodic structure may also be formed appropriately in the principal surface of the Si substrate. During crystal growth, the Si substrate is exposed to a high temperature and residual oxygen in a crystal growth furnace forms an extremely thin SiO2 film on the surface of the Si substrate (the surface of the two-dimensional periodic structure). In contrast to the refractive index of Si which is about 3.3, the refractive index of SiO2 is about 1.4. Since the refractive index of a light emitting semiconductor layer is typically 2.4 to 3.3, the SiO2 film increases a change in the refractive index of the two-dimensional periodic structure. Because the diffraction efficiency is higher as the refractive index change is larger, the light emission efficiency can further be increased. -
FIGS. 32A to 32E are perspective views illustrating a method for fabricating a semiconductor light emitting element according to a fifth embodiment of the present invention. The fabrication method according to the present embodiment is a method for forming a two-dimensional periodic structure in the principal surface of a substrate by using a nano-printing method. - First, as shown in
FIGS. 32A and 32B , a Si substrate or a SiC substrate formed with a two-dimensionalperiodic structure 28 composed of projections each at a height of 400 nm and having a period of 0.4 μm is prepared. Then, the substrate is pressed as amold 26 against the principal surface of thesapphire substrate 8 coated with a resist 27 having a film thickness of 600 nm. - When the
mold 26 is removed from thesapphire substrate 8 thereafter, a depressed two-dimensional periodic structure (the depth of each of holes is 400 nm and the period is 0.4 μm) is transferred to the resist 27, as shown inFIG. 32C . Next, as shown inFIG. 32D , the resist remaining at the bottom of each of the holes in the resist 27 is removed by O2 dry etching. - Next, as shown in
FIG. 32E , dry etching is performed by using the resist 27 as an etching mask and then the resist 27 is removed, whereby the two-dimensional periodic structure composed of depressions each at a depth of 150 nm and having a period of 0.4 μm is formed in the principal surface of thesapphire substrate 8. - By thus using the nano-printing method, an extremely fine structure on a submicron order can be formed through patterning without using a high-cost manufacturing apparatus such as a stepper or an EB exposure system. In addition, the fabrication method according to the present embodiment can be implemented by merely pressing the mold so that high-speed patterning is performed. If the substrate produced by the foregoing process is used as a mold, the semiconductor light emitting elements according to the first to fourth embodiments can be fabricated at a low cost.
-
FIGS. 33A to 33G are perspective views illustrating a method for fabricating a semiconductor light emitting element according to a sixth embodiment of the present invention. The method for fabricating the semiconductor light emitting element according to the present embodiment is a method for forming a two-dimensional periodic structure in the principal surface of a semiconductor thin film by using a soft mold method. - First, as shown in
FIG. 33A , a soft mold used for micro-processing is produced. In the present step, a two-dimensionalperiodic structure 31 composed of holes (depressions) each at a depth of 400 nm and having a period of 0.4 μm is formed in aresin 30 such as polysilane coated on asubstrate 29 such as a Si substrate or a SiC substrate by using a photolithographic, EB lithographic, or nano-printing process. The substrate with the resin thus produced is used as the soft mold for a micro-processing step performed later. - Next, as shown in
FIG. 33B , a thin-film semiconductor multilayer film having theAu plating layer 15 is formed by the method described in the first embodiment. In the method according to the present embodiment, however, the surface of the substrate used for the formation of the semiconductor multilayer film is flat so that the surface of the semiconductor multilayer film is also flat. - Next, as shown in
FIG. 33C , the resist 27 is coated on the principal surface of the semiconductor multilayer film. However, evaporation of a solvent in the resist 27 by baking is not performed herein. The soft mold described above is placed on the resist 27. In this case, the soft mold is placed to exert minimum pressure on the semiconductor multilayer film having a thickness of several micro meters and thereby prevent the destruction thereof. - As a result, capillarity occurs as a result of the absorption of the solvent in the resist 27 by the
resin 30 so that the resist 27 penetrates in the resin of the soft mold in such a manner as to fill in the holes of the two-dimensional periodic structure, as shown inFIG. 33D . - Thereafter, when the mold is removed from the semiconductor multilayer film, a projecting two-dimensional periodic structure (the height of each of the projections is 400 nm and the period is 0.4 μm) is transferred to the resist 27, as shown in
FIG. 33E . - Next, as shown in
FIG. 33F , the resist 27 remaining at the bottom of each of the holes in the resist is removed by O2 dry etching. - Thereafter, as shown in
FIG. 33G , dry etching is performed with respect to the principal surface of the semiconductor multilayer film by using the resist 27 as an etching mask and then the resist is removed, whereby the two-dimensional periodic structure (the height of each of projections is 150 nm and the period is 0.4 μm) is formed in the principal surface of the semiconductor multilayer film. - By thus using the soft mold method, micro-processing on a submicron order can be performed even with respect to a thin film which is extremely difficult to process, such as a semiconductor multilayer film having a thickness on the order of submicron meters. In this case, since a flat substrate can be used satisfactorily for the crystal growth of the semiconductor multilayer film, the crystal growth becomes easier than in the case of crystal growth on a substrate formed with projections/depressions.
- Although the embodiments described heretofore have particularly disclosed the nitride-based compound semiconductor which is difficult to process or the case where the period of the projections/depressions becomes smaller in response to the oscillation wavelength of a shorter wavelength of blue or purple light so that micro-processing thereof becomes difficult, the design of the present invention is also applicable to a semiconductor light emitting element which emits infrared light or red light using AlGaAs (with a refractive index of 3.6) or AlGaInP (with a refractive index of 3.5) as a semiconductor.
-
FIG. 34 is a perspective view showing a semiconductor light emitting element according to a seventh embodiment of the present invention. As shown in the drawing, the semiconductor light emitting element according to the present embodiment comprises: a p-type AlGaN layer (first semiconductor layer) 43 formed by epitaxial growth and having a thickness of 200 nm; a high-reflection p electrode (first electrode) 42 formed on the crystal growing surface (principal surface) of the p-type AlGaN layer 43, made of Al, and having a thickness of 0.5 μm; anAu plating layer 41 formed on the lower surface of the high-reflection p electrode 42 and having a thickness of 10 μm; a non-doped AlInGaNactive layer 44 formed on the back surface of the p-type AlGaN layer 43 and having a thickness of 3 nm; an n-type AlGaN layer (second semiconductor layer) 45 formed on the back surface of the non-doped AlInGaNactive layer 44, having a back surface formed with a projecting-type two-dimensionalperiodic structure 46, and having a thickness of 4 μm; and an n electrode (second electrode) 47 formed on the back surface of the n-type AlGaN layer 45, made of titanium (Ti) and Al which are stacked in layers, and having a thickness of 1 μm. The lower surface used herein indicates a surface of a certain layer located in the lower part ofFIG. 34 . - The semiconductor light emitting element according to the present embodiment functions as an ultraviolet LED from which light is extracted through the back surface of the n-
type AlGaN layer 45 and the PL peak wavelength of the non-doped AlInGaNactive layer 44 is 350 nm. - The period of the two-dimensional
periodic structure 46 formed in the back surface of the n-type AlGaN layer 45, i.e., the spacing between the respective centers of adjacent projections in a two-dimensional plane is 0.3 μm and the height of each of the projections is 130 nm. - The nitride-based compound semiconductor composing the semiconductor light emitting element according to the present embodiment can also be formed by MOCVD or MBE, similarly to the nitride-based compound semiconductor composing the semiconductor light emitting element according to the first embodiment.
- The semiconductor light emitting element according to the present embodiment also achieves the same high light extraction efficiency and excellent heat dissipation property as achieved by the semiconductor light emitting element according to the first embodiment. Since the high-
reflection p electrode 42 is made of Al, the light generated in the non-doped AlInGaNactive layer 44 can be reflected with a particularly high efficiency. - Thus, the structure of a semiconductor light emitting element according to the present invention is also applied effectively to a light emitting element which emits light at an emission wavelength having a peak in the ultraviolet region.
- In the semiconductor light emitting element functioning as the ultraviolet LED according to the present embodiment, the high-reflection p electrode (first electrode) 42 may also be made of Al.
- Thus, the semiconductor light emitting element according to the present invention is useful as a light source having high emission efficiency.
Claims (6)
1-14. (canceled)
15. A semiconductor light emitting element for emitting light, comprising:
a metal layer,
multiple group-III nitride semiconductor layers located on the metal layer and having an active layer, a first principle surface with projections and a second principle surface facing the metal layer and located under the first principle surface;
wherein the metal layer has approximately the same area as the second principle surface, and
the distance between the active layer and the first principle surface is larger than the distance between the active layer and the second principle surface.
16. The semiconductor light emitting element of claim 15 , wherein:
a first electrode being in contact with the first principle surface; and
a second electrode being in contact with the second principle surface.
17. The semiconductor light emitting element of claim 15 , wherein:
the distance between the active layer and the bottom surface of the projections is larger than the distance between the active layer and the second principle surface.
18. The semiconductor light emitting element of claim 15 , wherein:
0.5 λ/N≦L≦20 λ/N is satisfied where L is a distance between the nearest two projections, λ is a wavelength of emitted light from the active layer, and N is a refractive index of the group-III nitride semiconductor comprising the projections.
19. The semiconductor light emitting element of claim 15 , wherein:
0.5 λ/N≦L≦4 λ/N is satisfied where L is a distance between the nearest two projections, λ is a wavelength of emitted light from the active layer, and N is a refractive index of the group-III nitride semiconductor comprising the projections.