US20100139816A1 - Cold rolled and continuously annealed high strength steel strip and method for producing said steel - Google Patents
Cold rolled and continuously annealed high strength steel strip and method for producing said steel Download PDFInfo
- Publication number
- US20100139816A1 US20100139816A1 US12/523,924 US52392408A US2010139816A1 US 20100139816 A1 US20100139816 A1 US 20100139816A1 US 52392408 A US52392408 A US 52392408A US 2010139816 A1 US2010139816 A1 US 2010139816A1
- Authority
- US
- United States
- Prior art keywords
- steel strip
- zinc alloy
- coating layer
- zinc
- unavoidable impurities
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C18/00—Alloys based on zinc
- C22C18/02—Alloys based on zinc with copper as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
Definitions
- This invention relates to cold rolled and continuously annealed high strength steel strip provided with a zinc alloy coating layer and to a method for producing it.
- High strength steels are increasingly being used in automotive and building applications as a result of the drive towards weight reduction. To compensate for the resulting decreasing thickness of the materials used in constructing the vehicles, materials having a higher strength are considered. However, the higher strength usually comes at a cost with regard to formability. As a result, many high strength steels having good formability are currently being looked at. These steel developments usually result in steels having a very specific combination of microstructure and chemical composition, and are produced in carefully designed and controlled production processes.
- the object according to the invention is reached by a cold rolled and continuously annealed high strength steel strip comprising (all percentages in wt % unless otherwise indicated):
- An additional element that could be added in a small amount, less than 0.2 weight %, could be Pb or Sb, Ti, Ca, Mn, Sn, La, Ce, Cr, Ni, Zr or Bi. Pb, Sn, Bi and Sb are usually added to form spangles.
- the total amount of additional elements in the zinc alloy is at most 0.2%. These small amounts of an additional element do not alter the properties of the coating nor the bath to any significant extent for the usual applications.
- the thickness of the zinc alloy coating layer is preferably between 3 and 12 ⁇ m because thicker coatings are not necessary for most applications.
- the zinc alloy coating layer according to the invention improves the protection against corrosion that a thickness of at most 12 ⁇ m is sufficient for almost all applications.
- a thin coating layer is also beneficial for welding together two sheets of steel with the coating layer according to the invention, for instance by laser welding.
- the zinc alloy coating layer has a thickness of 3-10 ⁇ m, this being a preferred thickness range for automotive applications. According to a further preferred embodiment, the zinc alloy coating layer has a thickness of 3-8 ⁇ m or even 7 ⁇ m. This thickness is preferred when improved laser welds which are produced without a spacer are of importance.
- the steel according to the invention provides an excellent substrate wettability for the zinc alloy coating layer according to the invention, despite the high levels of alloying elements which are known to adversely affect the wettability of the steel substrate. It is important to note that the steel according to the invention does not contain Nickel as an alloying element, because Nickel forms a compound with Mg: MgNi 2 and Mg 2 Ni. If the Nickel from the steel forms these compounds with the Mg from the plating bath, undesirable dross formation occurs in combination with an undesirable Mg-depletion of the plating bath. So for processing reasons, a nickel-containing substrate is undesirable.
- the microstructure comprises between 90 and 65% of ferrite, preferably between 85 and 70%, more preferably between 80 to 75%.
- the austenite fraction, present prior to the cooling immediately after inter-critical annealing OAT is preferably completely transformed to non-ferrite microstructurel components, preferably bainite, martensite, acicular ferrite or is partly preserved as retained austenite.
- the steel strip comprises between 90 and 65% of ferrite, the remainder of the structure being acicular ferrite, bainite, martensite or retained austenite.
- the microstructure does not contain pearlite, although iron-carbide precipitates, such as cementite not in the form of lamellae in pearlite, may be present in the steel.
- the higher contact pressures during forming of high strength steel components in a forming operation do not lead to damage of the coating such as often happens with a galveannealed coating layer, and it does not scrape off as easily as a normal galvanised zinc layer does. This may be because Mg additions are believed to be beneficial in promoting lubrication between the coated steel and (hot) shaping tools.
- the inventors believe that the Mg-oxide forming on the zinc-bath protects against evaporation of the zinc during coating. Reduced zinc evaporation is also beneficial in the snout area during hot dip galvanising. The snout is the location where the strip enters the zinc bath.
- the coating layer always contains some iron, even though the bath from which the coating layer was deposited does not contain iron as an additional element as defined above.
- the iron constitutes an unavoidable impurity because of the fact that a steel substrate is used.
- the iron is not an additional element and should preferably not exceed 1.5% or more preferably 1.0%.
- the iron content in the coating layer is limited to below 0.6%, preferably to below 0.4%. Even more preferably the amount is limited to below 0.2%.
- the steel substrate consists only of the alloying elements that are expressly claimed.
- Other elements such as oxygen or rare earth elements, may only be present as unavoidable impurities, and the balance is iron.
- the minimum level of aluminium of 0.05% can be used, as it is not important to prevent all reactions between Fe and Zn. Without any aluminium, thick solid Fe—Zn alloys grow on the steel surface and the coating thickness cannot be regulated smoothly by wiping with a gas.
- An aluminium content of 0.05% is enough to prevent problematic Fe—Zn alloy formation.
- the aluminium content is at least 0.3%.
- the phosphatability of the steel is improved as a result of the addition of Mg.
- the zinc alloy comprises 0.3-2.3 weight % magnesium and 0.6-2.3 weight % aluminium.
- the magnesium level By limiting the magnesium level to at most 2.3% the formation of oxidic dross on the zinc bath is reduced whilst retaining the corrosion protection at a sufficiently high level.
- the aluminium content By limiting the aluminium content, the weldability is improved.
- the silicon content in the zinc alloy layer is below 0.0010 weight %.
- the steel strip has been provided with a zinc alloy coating layer in which the zinc alloy contains 1.6-2.3 weight % magnesium and 1.6-2.3 weight % aluminium.
- the zinc alloy contains 1.6-2.3 weight % magnesium and 1.6-2.3 weight % aluminium.
- the steel strip has been provided with a zinc alloy coating layer in which the zinc alloy contains 0.6-1.3 weight % aluminium and/or 0.3-1.3 weight % magnesium.
- the zinc alloy contains 0.6-1.3 weight % aluminium and/or 0.3-1.3 weight % magnesium.
- magnesium at levels between 0.3 and 1.3 weight % improves the corrosion resistance considerably.
- more than 0.5 weight % of aluminium has to be added to prevent that more oxidic dross is formed on the bath than for conventional baths; dross can lead to defects in the coating.
- the coatings with these amounts of magnesium and aluminium are optimal for applications with high demands on surface quality and improved corrosion resistance.
- the zinc alloy contains 0.8-1.2 weight % aluminium and/or 0.8-1.2 weight % magnesium. These amounts of magnesium and aluminium are optimal to provide a coating with both a high corrosion resistance, an excellent surface quality, an excellent formability, and a good weldability at limited extra costs as compared to conventional hot dipped galvanising.
- the steel strip has been provided with a hot dip galvanized zinc alloy coating layer in which the amount of aluminium in weight % is the same as the amount of magnesium in weight % plus or minus a maximum of 0.3 weight %. It has been found that the dross formed on the bath is suppressed to a considerable level when the amount of aluminium equals or almost equals the amount of magnesium.
- the steel strip coated with a zinc alloy coating according to the invention comprises 0.07-0.16% C, 1.4-2.0% Mn, preferably 1.5-1.8% Mn, 0.2-0.4% Si, preferably at least 0.25% Si, 0.5-1.5% Al, 0.4-0.8% Cr, 0-0.05% Ti, 0-0.03% Nb, 0-0.01% N, 0-0.002% B and V as impurity.
- boron is not added as an alloying element but, if present, is present only as an impurity. Boron is known to affect hardenability considerably, thereby stimulating martensite formation at the expense of retained austenite, and thereby impairing formability of the steel.
- the microstructure of the steel according to this embodiment is pearlite free and comprises ferrite, bainite, martensite and retained austenite.
- the volume fraction of retained austenite is between 1 and 10%, preferably about 5%.
- the bainite is preferably carbide free.
- the steel strip comprises 0.07-0.12% C and 0.5-1.0% Al.
- the tensile strength of the steel according to this embodiment is somewhat lower, and is about 600 MPa.
- the reduction in alloying elements means that the annealing treatment after cold rolling has to be adapted in order to still obtain a pearlite free microstructure comprising ferrite, bainite, martensite and retained austenite.
- a steel strip provided with a zinc alloy coating layer according to the invention comprises 0.07-0.20% C, 1.2-3.5% Mn, 0-1.5% Al, 0-0.15% Ti, 0-0.002% B.
- boron is not added as an alloying element but, if present, is present only as an impurity.
- the microstructure of the steel according to this embodiment is pearlite free and comprises ferrite, martensite and carbides.
- the volume fraction of ferrite is between 70 and 95%, preferably about 80%.
- the application of the zinc alloy coating layer provides a high strength steel with good ductility.
- the steel strip comprises 0.07-0.17% C, 1.2-2.5% Mn and 0-1.0% Al. More preferably the steel strip comprises 0.07-0.12% C, 1.2-2.0% Mn, 0-0.4% Si, 0-1.0% Al, 0-0.05% Ti, 0-0.07% Nb, 0-0.01% N. Both preferred embodiments provide a somewhat lower tensile strength in combination with a higher ductility and excellent corrosion resistance and weldability.
- the steel strip coated with a zinc alloy coating according to the invention comprises 0.15-0.30% C, 1.5-3.5% Mn, 0.5-2.0% Al, 0-0.05% Nb, 0-0.01% N, 0-0.002% B.
- boron is not added as an alloying element but, if present, is present only as an impurity.
- the microstructure of the steel according to this embodiment is pearlite free and comprises ferrite, bainite, martensite and retained austenite. This steel is sometimes referred to as a TRIP-steel.
- the volume fraction of retained austenite is between 1 and 10%, preferably about 5%.
- the bainite is preferably carbide free.
- the application of the zinc alloy coating layer provides a high strength steel with good ductility and excellent corrosion resistance and weldability.
- the steel strip comprises 0.15-0.24% C, 1.5-2.0% Mn, 0.2-0.8% Si, preferably 0.2-0.6% Si, preferably at least 0.25% Si, 0.5-1.5% Al, 0-0.05% Nb, preferably max. 0.03%.
- the steel strip comprises 0.15-0.20% C.
- a method for producing a cold rolled and continuously annealed high strength steel strip comprising the subsequent steps of:
- the substantially ferritic steel matrix transforms partly to austenite, depending on the IAT and the annealing time at the IAT.
- the IAT can be chosen constant as schematically depicted in FIG. 1 , although it is also possible to heat the strip quickly to a temperature somewhat below IAT followed by a slow heat to a peak IAT and followed by a slow cool to a temperature again somewhat below IAT so as to attain the desired ratio of ferrite to austenite at the end of the annealing treatment at the IAT as schematically depicted in FIG. 2 .
- the volume fraction of austenite content prior to the cooling to the OAT is at most 50%.
- the volume fraction is preferably between 10 and 35%, preferably between 15 to 30%, preferably between 20 to 25%.
- the AIT is between 750 and 850° C., preferably between 780 and 830° C.
- the steel substrate consists only of the alloying elements that are expressly claimed.
- Other elements such as oxygen or rare earth elements, may only be present as unavoidable impurities, and the balance is iron.
- the heating step to the IAT is performed quickly to a temperature above Ac 1 with an overheating of between Ac 1 +20 and Ac 1 +80 so as to effect a fast nucleation of austenite.
- the inventors found that this fast heating step, which in most annealing devices coincides with the heating in a direct fired furnace (DFF), and therefore the fast heating step ends at the exit of the DFF, results in an increase of strength with maintenance or even improvement in ductility via a refinement of microstructure and promotion of band free structures.
- This effect of the fast heating combined with the overheating above Ac 1 has been found for all embodiments of the invention.
- the improvement in ultimate tensile strength ranges from 30 to 120 MPa depending on chemistry.
- the heating rate is between 10 and 50° C./s, more preferably between 15 and 40° C.
- a suitable value for the heating rate was found to be between 15 and 25° C./s, for example about 20° C./s.
- the over-aging temperature OAT is at most 150° C. lower than the GT, preferably at most 100° C. lower than the GT, more preferably at most 70° C. lower than the GT, even more preferably at most 50° C. lower than the GT.
- the process can be tailored to achieve the desired microstructure after the cooling from the IAT and the over-aging treatment at the OAT independently from the subsequent hot dip coating. It was found that overageing at a temperature below the GT provides a very good combination of strength and ductility.
- the hot dip treatment can be optimised so as to achieve the best corrosion protection, coating coverage and coating adhesion.
- the OAT is at least 10° C. lower than the GT, preferably at least 20° C. lower, more preferably at least 30° C. lower than the GT.
- the temperature increase from the OAT to the GT is achieved by an induction heating step. Induction heating is a fast and clean heating process, so as not to contaminate the surface of the steel strip to be hot dip coated and a very short heating section is sufficient. There is no limit to the heating step that can be achieved to heat the steel strip from the OAT to the GT, but the inventors found that a temperature difference of between 10 and 75° C. between OAT and GT can be economically bridged by inductive heating.
- the zinc-bath temperature ZBT is at most 25° C. lower than the GT, preferably at most 20° C., more preferably at most 15° C., even more preferably at most 10° C.
- the temperature GT of the steel strip before entering the bath of molten zinc alloy is between 380° C. and 850° C., more preferably between the temperature of the bath of molten zinc alloy and 25° C. above the bath temperature.
- the temperature of the steel strip should not be lower than the melting point of the zinc alloy to avoid local solidification of the zinc bath. High steel strip temperatures will lead to higher evaporation of the zinc, resulting in dust formation. High steel strip temperatures can also heat up the zinc bath, requiring continuous cooling of the zinc in the bath, which is expensive. For these reasons a temperature of the steel strip just above the bath temperature is preferred.
- the OAT is between 350 and 450° C., preferably between 380 and 430° C. It was found that an OAT within these temperature boundaries provides an optimal microstructure for achieving high strength and ductility.
- the ZBT is between 430 and 490° C., preferably between 440 and 480, more preferably between 450 and 470 ° C.
- the temperature of the bath of molten zinc ZBT is kept between 380° C. and 550° C., preferably between 430° C. and 490° C.
- a lower limit of 440° C. is absolutely safe to avoid any solidification.
- Increasing the zinc bath temperature increases the zinc evaporation and leads to dust formation in the galvanising line, giving rise to surface defects.
- the upper limit should thus be reasonably low, for which 550° C. is fair, and preferably 480° C. as a technically possible upper limit.
- a method for producing a cold rolled and continuously annealed high strength steel strip according to the process described hereinabove wherein the steel strip comprises, preferably consists of, in wt %:
- boron is not added as an alloying element but, if present, is present only as an impurity.
- This combination of steel substrate composition, annealing treatment, hot dip coating treatment and the ability to control the microstructure independently from the hot dip coating treatment provides a high strength steel strip of excellent strength, consistency and ductility, whereas the coating treatment can be performed independently from the over-ageing treatment so as to obtain the best quality of the coating.
- This is a big advantage because normally the microstructure components and hence the mechanical properties which are produced in the initial stages of the annealing process are adversely affected in the later stage of the galvanizing treatment.
- the heating of the strip between the overageing and the hot dip coating is prefereably obtained by induction heating.
- the steel strip comprises 0.04-0.12% C, or even 0.8 to 0.12% C.
- the inventors found that when the OAT is selected between 380 and 430° C. for an over-aging time of between 40 seconds and 150 seconds, preferably between 60 and 100 seconds, more preferably between 70 and 90 seconds a very good combination of strength and ductility for this particular composition was achieved, particularly for steels having an aluminium content between 0.3 and 0.7%.
- the aluminium content of the steel is about 1%, an annealing time of 120 seconds at an OAT between 400 and 420 provided good results.
- a galvannealing step after the zinc alloy coating step and prior to the cooling step to ambient temperature can be used.
- a galvannealing step may comprise the heating of the strip for instance for 20 to 40 seconds at 470 to 550° C., immediately following the hot dipping so as to achieve an iron content in the zinc alloy coating of up to 15%, preferably between 7 and 13%, for instance about 10%.
- the zinc alloy consists of 0.3-4.0% Mg and 0.3-6.0% Al; optionally at most 0.2% of one or more additional elements; unavoidable impurities; the remainder being zinc.
- the zinc alloy consists of: 0.3-2.3 weight % magnesium; 0.5-2.3 weight % aluminium; optional ⁇ 0.2 weight % of one or more additional elements; unavoidable impurities; the remainder being zinc.
- the zinc alloy comprises less than 0.0010 weight % of silicon.
- the zinc alloy bath contains 1.5-2.3 weight % magnesium and 1.5-2.3 weight % aluminium.
- the zinc alloy bath contains 0.6-1.3 weight % aluminium, and preferably contains 0.7-1.2 weight % aluminium and/or the zinc alloy bath contains 0.3-1.3 weight % magnesium, and preferably contains 0.7-1.2 weight % magnesium.
- Industrial tests were performed with various steel substrates having compositions in accordance with the invention.
- the zinc alloy coating layers comprised substantially equal aluminium and magnesium contents ranging between 1.5 and 2% each. The adhesion was found to be excellent and independent of the composition of the steel substrate, despite the use of significant amount of alloying elements.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Sheet Steel (AREA)
Applications Claiming Priority (5)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP07003811 | 2007-02-23 | ||
EP07003811.2 | 2007-02-23 | ||
EP07004331 | 2007-03-02 | ||
EP07004331.0 | 2007-03-02 | ||
PCT/EP2008/052195 WO2008102009A1 (fr) | 2007-02-23 | 2008-02-22 | Feuillard d'acier à résistance élevée, laminé à froid et trempé en continu, et procédé de fabrication dudit feuillard |
Publications (1)
Publication Number | Publication Date |
---|---|
US20100139816A1 true US20100139816A1 (en) | 2010-06-10 |
Family
ID=39473952
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US12/523,924 Abandoned US20100139816A1 (en) | 2007-02-23 | 2008-02-22 | Cold rolled and continuously annealed high strength steel strip and method for producing said steel |
Country Status (11)
Country | Link |
---|---|
US (1) | US20100139816A1 (fr) |
EP (2) | EP2115178B1 (fr) |
JP (1) | JP5586007B2 (fr) |
KR (1) | KR20090122346A (fr) |
CN (1) | CN101627142B (fr) |
BR (1) | BRPI0807957A2 (fr) |
ES (1) | ES2683010T3 (fr) |
HK (1) | HK1139714A1 (fr) |
MX (2) | MX366540B (fr) |
RU (1) | RU2464338C2 (fr) |
WO (1) | WO2008102009A1 (fr) |
Cited By (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20120288733A1 (en) * | 2009-12-21 | 2012-11-15 | Tata Steel Ijmuiden B.V. | High strength hot dip galvanised steel strip |
CN104046889A (zh) * | 2014-06-09 | 2014-09-17 | 首钢总公司 | 一种导轨用冷轧连续退火带钢及其生产方法 |
CN104755646A (zh) * | 2012-09-03 | 2015-07-01 | 奥钢联钢铁公司 | 对扁钢产品涂覆保护涂层的方法和具有相应保护涂层的扁钢产品 |
WO2016187576A1 (fr) * | 2015-05-20 | 2016-11-24 | Ak Steel Properties, Inc. | Acier haute résistance amélioré de troisième génération faiblement allié |
US9593400B2 (en) | 2012-04-05 | 2017-03-14 | Tata Steel Ijmuiden Bv | Steel strip having a low Si content |
CN107252818A (zh) * | 2017-08-02 | 2017-10-17 | 安徽骏达起重机械有限公司 | 交通轨道的加工方法 |
WO2018031523A1 (fr) * | 2016-08-08 | 2018-02-15 | John Speer | Revêtements modifiés de galvanisation par immersion à chaud présentant une basse température de liquidus, procédés pour leur fabrication et leur utilisation |
DE102017202586B3 (de) | 2017-02-17 | 2018-03-29 | Zf Friedrichshafen Ag | Verfahren zur Herstellung eines Bauteils aus einem mikrolegierten Stahl |
US10907243B2 (en) | 2015-12-24 | 2021-02-02 | Posco | Plated steel material having excellent friction resistance and white rust resistance and method for preparing same |
US10947608B2 (en) | 2015-10-05 | 2021-03-16 | Arcelormittal | Steel sheet coated with a metallic coating based on aluminum and comprising titanium |
US11060157B2 (en) * | 2016-03-31 | 2021-07-13 | Jfe Steel Corporation | Steel sheet, coated steel sheet, method for producing hot-rolled steel sheet, method for producing full hard cold-rolled steel sheet, method for producing steel sheet, and method for producing coated steel sheet |
US11066716B2 (en) * | 2016-08-10 | 2021-07-20 | Jfe Steel Corporation | Steel sheet and method for producing the same |
US11149325B2 (en) | 2014-07-03 | 2021-10-19 | Arcelormittal | Method for manufacturing a high strength steel sheet and sheet obtained |
US11306381B2 (en) | 2015-12-24 | 2022-04-19 | Posco | High-strength hot-dip zinc plated steel material having excellent plating properties and method for preparing same |
US11312212B2 (en) * | 2015-03-31 | 2022-04-26 | Arcelormittal | Panel for vehicle comprising a coated steel sheet locally reinforced |
US11396691B2 (en) | 2016-12-22 | 2022-07-26 | Posco | Alloy-plated steel material having excellent corrosion resistance and high surface quality |
US11505858B2 (en) | 2016-12-22 | 2022-11-22 | Posco | Alloy-plated steel material having excellent crack resistance, and method for manufacturing same |
Families Citing this family (42)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
MX366540B (es) | 2007-02-23 | 2019-07-12 | Tata Steel Ijmuiden Bv | Tira de acero de alta resistencia laminada en frio y recocida en continuo, y metodo para producirla. |
DE102009018577B3 (de) | 2009-04-23 | 2010-07-29 | Thyssenkrupp Steel Europe Ag | Verfahren zum Schmelztauchbeschichten eines 2-35 Gew.-% Mn enthaltenden Stahlflachprodukts und Stahlflachprodukt |
DE102011117572A1 (de) | 2011-01-26 | 2012-08-16 | Salzgitter Flachstahl Gmbh | Höherfester Mehrphasenstahl mit ausgezeichneten Umformeigenschaften |
CN102140609A (zh) * | 2011-01-29 | 2011-08-03 | 首钢总公司 | 硅铝复合添加590MPa级相变诱发塑性钢及制备方法 |
WO2012141659A1 (fr) * | 2011-04-13 | 2012-10-18 | U.S. STEEL KOŠICE, s.r.o. | Procédé de fabrication de produits en acier plat galvanisé à chaud avec une résistance améliorée à la corrosion |
TR201807970T4 (tr) | 2012-08-27 | 2018-06-21 | Tata Steel Ijmuiden Bv | Avantajlı özelliklere sahip kaplanan çelik şerit veya levha. |
MX2015003103A (es) * | 2012-09-14 | 2015-10-22 | Salzgitter Mannesmann Prec Gmbh | Aleacion de acero para un acero de alta resistencia, de baja aleacion. |
WO2015001368A1 (fr) * | 2013-07-04 | 2015-01-08 | Arcelormittal Investigaciòn Y Desarrollo Sl | Procédé de traitement d'une tôle pour réduire son noircissement ou son ternissement lors de son stockage et tôle traitée par un tel procédé |
WO2015011511A1 (fr) * | 2013-07-24 | 2015-01-29 | Arcelormittal Investigación Y Desarrollo Sl | Tôle d'acier à très hautes caractéristiques mécaniques de résistance et de ductilité, procédé de fabrication et utilisation de telles tôles |
CN104419867B (zh) * | 2013-09-05 | 2016-09-07 | 鞍钢股份有限公司 | 1250MPa级超高强锌铝镁镀层钢板及其生产方法 |
CN103757536B (zh) * | 2014-01-24 | 2016-10-05 | 宝山钢铁股份有限公司 | 抗拉强度≥1100MPa的薄带连铸经济性高强捆带及其制造方法 |
WO2015124322A1 (fr) * | 2014-02-20 | 2015-08-27 | Tata Steel Ijmuiden B.V. | Traitement d'activation de substrats d'acier revêtus |
CN103882292B (zh) * | 2014-03-05 | 2016-03-30 | 首钢总公司 | 一种冷轧碳素结构钢生产方法 |
WO2016072681A1 (fr) * | 2014-11-03 | 2016-05-12 | 주식회사 포스코 | Tige de fil métallique présentant une résistance et une ténacité améliorées et son procédé de préparation |
JP7051436B2 (ja) | 2014-12-24 | 2022-04-11 | ポスコ | 溶接性及び加工部耐食性に優れた亜鉛合金めっき鋼材及びその製造方法 |
KR101758529B1 (ko) | 2014-12-24 | 2017-07-17 | 주식회사 포스코 | 인산염 처리성과 스폿 용접성이 우수한 아연합금도금강판 및 그 제조방법 |
CN104630626B (zh) * | 2015-02-06 | 2017-04-12 | 铜陵百荣新型材料铸件有限公司 | 一种耐高温铸钢及其生产方法 |
JP2017066508A (ja) * | 2015-10-02 | 2017-04-06 | 株式会社神戸製鋼所 | 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法 |
US20210115527A1 (en) | 2016-11-29 | 2021-04-22 | Tata Steel Ijmuiden B.V. | Method for manufacturing a hot-formed article, and obtained article |
EP3327152B1 (fr) | 2016-11-29 | 2023-10-11 | Tata Steel UK Limited | Procédé de formage à chaud d'une ébauche d'acier |
WO2019122964A1 (fr) * | 2017-12-19 | 2019-06-27 | Arcelormittal | Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication |
WO2019155014A1 (fr) | 2018-02-08 | 2019-08-15 | Tata Steel Ijmuiden B.V. | Procédé de façonnage d'un article à partir d'une ébauche d'acier revêtue de zinc ou d'alliage de zinc |
CN108642422A (zh) * | 2018-05-17 | 2018-10-12 | 马钢(集团)控股有限公司 | 一种热成形钢板用镀液、热成形钢板及热成形部件 |
WO2020058330A1 (fr) * | 2018-09-19 | 2020-03-26 | Sms Group Gmbh | Acier avancé à haute limite d'élasticité, bande en acier composée de cet acier ainsi que procédé pour la fabrication d'une bande en acier |
CN109365606A (zh) * | 2018-11-30 | 2019-02-22 | 宝山钢铁股份有限公司 | 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法 |
CN109680213A (zh) * | 2019-02-19 | 2019-04-26 | 江苏东恒光电有限公司 | 一种用于高压金具的金属配方 |
CN110004362B (zh) * | 2019-04-01 | 2021-06-18 | 山东钢铁集团日照有限公司 | 一种提高冷轧dp780钢屈强比和扩孔性能的生产方法 |
CN111763875A (zh) * | 2019-04-02 | 2020-10-13 | 上海梅山钢铁股份有限公司 | 一种瓶盖用高硬度冷轧电镀锡基板及其生产方法 |
CN112522580A (zh) * | 2019-09-19 | 2021-03-19 | 宝山钢铁股份有限公司 | 一种马氏体钢带及其制造方法 |
EP3816319B1 (fr) | 2019-10-29 | 2022-09-14 | Salzgitter Flachstahl GmbH | Procédé de fabrication d'une bande en acier haute résistance à adhésion améliorée des enrobages par galvanisation à chaud à base de zinc |
WO2021089851A1 (fr) * | 2019-11-08 | 2021-05-14 | Ssab Technology Ab | Produit en acier au manganèse à haute résistance et son procédé de fabrication |
CN110964989A (zh) * | 2019-11-13 | 2020-04-07 | 浙江金洲管道科技股份有限公司 | 用于核电的超重荷型刚性钢导管及其制造方法 |
CN110863149A (zh) * | 2019-11-13 | 2020-03-06 | 浙江金洲管道科技股份有限公司 | 一种热镀锌钢管及其制造方法 |
CN110804715A (zh) * | 2019-12-10 | 2020-02-18 | 马鞍山钢铁股份有限公司 | 一种255MPa级含硼高强韧性热镀锌结构钢及其生产方法 |
CN111254351B (zh) * | 2020-01-21 | 2021-07-20 | 鞍钢股份有限公司 | 一种高性能热轧耐磨钢薄板及其生产方法 |
MX2022009852A (es) | 2020-02-11 | 2022-08-17 | Tata Steel Ijmuiden Bv | Acero ductil laminado en caliente de ultra alta resistencia con alta capacidad de bridado, metodo de fabricacion de dicho acero laminado en caliente y uso del mismo. |
CN112159931B (zh) * | 2020-09-28 | 2022-08-12 | 首钢集团有限公司 | 一种具有连续屈服的1000MPa级中锰TRIP钢及其制备方法 |
KR20230045648A (ko) * | 2021-09-27 | 2023-04-05 | 주식회사 포스코 | 구멍확장성 및 연성이 우수한 고강도 후물 강판 및 이의 제조방법 |
WO2023144019A1 (fr) | 2022-01-25 | 2023-08-03 | Tata Steel Ijmuiden B.V. | Bande d'acier à haute résistance laminée à chaud |
KR20230166682A (ko) * | 2022-05-31 | 2023-12-07 | 현대제철 주식회사 | 초고강도 냉연강판 및 그 제조방법 |
WO2024032949A1 (fr) | 2022-08-09 | 2024-02-15 | Tata Steel Ijmuiden B.V. | Bande d'acier à haute résistance laminée à chaud |
KR20240106697A (ko) * | 2022-12-29 | 2024-07-08 | 현대제철 주식회사 | 초고강도 냉연강판 및 그 제조방법 |
Citations (12)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH10130776A (ja) * | 1996-10-23 | 1998-05-19 | Sumitomo Metal Ind Ltd | 高延性型高張力冷延鋼板 |
EP1154028A1 (fr) * | 2000-05-12 | 2001-11-14 | Corus Staal BV | Acier à plusieurs phases et procédé pour sa fabrication |
US6517955B1 (en) * | 1999-02-22 | 2003-02-11 | Nippon Steel Corporation | High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof |
JP2003055751A (ja) * | 2001-06-06 | 2003-02-26 | Nippon Steel Corp | 高加工時のめっき密着性および延性に優れた高強度溶融Znめっき鋼板及びその製造方法 |
US20030047258A1 (en) * | 2000-04-27 | 2003-03-13 | Kei Sakata | High tensile cold-rolled steel sheet excellent in ductility and in strain aging hardening properties, and method for producing the same |
US6706419B2 (en) * | 2000-08-04 | 2004-03-16 | Nippon Steel Corporation | Cold-rolled steel sheet or hot-rolled steel sheet excellent in painting bake hardenability and anti aging property at room temperature, and method of producing the same |
US20040055667A1 (en) * | 2000-12-29 | 2004-03-25 | Yoshihisa Takada | High-strength molten-zinc-plated steel plate excellent in deposit adhesion and suitability for press forming and process for producing the same |
US20040234807A1 (en) * | 2002-03-01 | 2004-11-25 | Yoshitsugu Suzuki | Surface treated steel plate and method for production thereof |
US20040238082A1 (en) * | 2002-06-14 | 2004-12-02 | Jfe Steel Corporation | High strength cold rolled steel plate and method for production thereof |
US20050139293A1 (en) * | 2003-12-25 | 2005-06-30 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | High-strength cold-rolled steel sheet excellent in coating film adhesion |
US20060140814A1 (en) * | 2002-12-20 | 2006-06-29 | Usinor S.A. | Steel composition for the production of cold rolled multiphase steel products |
US7686896B2 (en) * | 2003-09-26 | 2010-03-30 | Jfe Steel Corporation | High-strength steel sheet excellent in deep drawing characteristics and method for production thereof |
Family Cites Families (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4913746A (en) * | 1988-08-29 | 1990-04-03 | Lehigh University | Method of producing a Zn-Fe galvanneal on a steel substrate |
SU1752823A1 (ru) * | 1990-07-03 | 1992-08-07 | Череповецкий Металлургический Комбинат Им.50-Летия Ссср | Сталь |
JP2783453B2 (ja) * | 1990-10-09 | 1998-08-06 | 新日本製鐵株式会社 | 溶融Zn−Mg−Alめっき鋼板及びその製造方法 |
JP4218598B2 (ja) * | 1994-02-15 | 2009-02-04 | Jfeスチール株式会社 | めっき特性に優れる高張力合金化溶融亜鉛めっき鋼板 |
JP3596316B2 (ja) * | 1997-12-17 | 2004-12-02 | 住友金属工業株式会社 | 高張力高延性亜鉛めっき鋼板の製造方法 |
JPH11279682A (ja) * | 1998-03-27 | 1999-10-12 | Nippon Steel Corp | 加工性とスポット溶接性の良い高強度鋼板とその製造方法 |
JP2001140022A (ja) * | 1999-08-27 | 2001-05-22 | Nippon Steel Corp | プレス成形性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 |
JP2001323355A (ja) * | 2000-05-11 | 2001-11-22 | Nippon Steel Corp | めっき密着性と塗装後耐食性の良好なSi含有高強度溶融亜鉛めっき鋼板と塗装鋼板およびその製造方法 |
JP2001335909A (ja) * | 2000-05-26 | 2001-12-07 | Kobe Steel Ltd | 溶融亜鉛めっき鋼板の製造方法 |
JP3702193B2 (ja) * | 2001-04-06 | 2005-10-05 | 新日本製鐵株式会社 | 加工後の加工部の耐食性に優れた非脱膜型潤滑めっき鋼板 |
JP3715220B2 (ja) * | 2001-06-22 | 2005-11-09 | 日新製鋼株式会社 | 耐食性に優れたZn−Al−Mg系溶融めっき鋼材 |
JP3547414B2 (ja) * | 2001-08-17 | 2004-07-28 | 新日本製鐵株式会社 | 加工部の耐食性に優れ環境負荷の小さい非脱膜型潤滑めっき鋼板 |
JP2003138385A (ja) * | 2001-10-29 | 2003-05-14 | Nippon Steel Corp | 塗膜密着性と加工部の耐食性に優れ環境負荷の小さい非脱膜型潤滑めっき鋼板 |
JP4123976B2 (ja) * | 2002-03-01 | 2008-07-23 | Jfeスチール株式会社 | 溶融亜鉛めっき鋼板及びその製造方法 |
RU2212457C1 (ru) * | 2002-06-04 | 2003-09-20 | ООО "Сорби стил" | Способ производства холоднокатаных полос из сверхнизкоуглеродистой стали |
JP3921136B2 (ja) * | 2002-06-18 | 2007-05-30 | 新日本製鐵株式会社 | バーリング加工性に優れた高強度高延性溶融亜鉛めっき鋼板とその製造方法 |
JP2004270029A (ja) * | 2003-02-18 | 2004-09-30 | Nippon Steel Corp | 耐亜鉛揮発性に優れた亜鉛系めっき鋼板 |
CN101027421A (zh) * | 2004-06-29 | 2007-08-29 | 克里斯塔尔公司 | 具有热浸镀锌合金镀层的钢片及其制备方法 |
EP1621645A1 (fr) * | 2004-07-28 | 2006-02-01 | Corus Staal BV | Feuille d'acier galvanisé à chaud recouverte de zinc allié. |
JP4544579B2 (ja) * | 2004-09-29 | 2010-09-15 | 日新製鋼株式会社 | 高強度溶融Zn−Al−Mg合金めっき鋼板の製造方法 |
JP5250938B2 (ja) * | 2005-03-31 | 2013-07-31 | Jfeスチール株式会社 | 延性に優れる低降伏比型高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP4940813B2 (ja) * | 2006-03-06 | 2012-05-30 | Jfeスチール株式会社 | TS×Elの値が21000MPa・%以上である溶融亜鉛めっき鋼板の製造方法 |
MX366540B (es) | 2007-02-23 | 2019-07-12 | Tata Steel Ijmuiden Bv | Tira de acero de alta resistencia laminada en frio y recocida en continuo, y metodo para producirla. |
-
2008
- 2008-02-22 MX MX2009008194A patent/MX366540B/es active IP Right Grant
- 2008-02-22 BR BRPI0807957-9A patent/BRPI0807957A2/pt not_active Application Discontinuation
- 2008-02-22 ES ES08717056.9T patent/ES2683010T3/es active Active
- 2008-02-22 US US12/523,924 patent/US20100139816A1/en not_active Abandoned
- 2008-02-22 EP EP08717056.9A patent/EP2115178B1/fr active Active
- 2008-02-22 EP EP18178558.5A patent/EP3421634A1/fr active Pending
- 2008-02-22 CN CN2008800058518A patent/CN101627142B/zh active Active
- 2008-02-22 WO PCT/EP2008/052195 patent/WO2008102009A1/fr active Application Filing
- 2008-02-22 JP JP2009550723A patent/JP5586007B2/ja active Active
- 2008-02-22 KR KR1020097017762A patent/KR20090122346A/ko not_active Application Discontinuation
- 2008-02-22 MX MX2019008366A patent/MX2019008366A/es unknown
- 2008-02-22 RU RU2009135411/02A patent/RU2464338C2/ru not_active IP Right Cessation
-
2010
- 2010-06-09 HK HK10105680.2A patent/HK1139714A1/xx not_active IP Right Cessation
Patent Citations (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH10130776A (ja) * | 1996-10-23 | 1998-05-19 | Sumitomo Metal Ind Ltd | 高延性型高張力冷延鋼板 |
US6517955B1 (en) * | 1999-02-22 | 2003-02-11 | Nippon Steel Corporation | High strength galvanized steel plate excellent in adhesion of plated metal and formability in press working and high strength alloy galvanized steel plate and method for production thereof |
US20030047258A1 (en) * | 2000-04-27 | 2003-03-13 | Kei Sakata | High tensile cold-rolled steel sheet excellent in ductility and in strain aging hardening properties, and method for producing the same |
US6692584B2 (en) * | 2000-04-27 | 2004-02-17 | Jfe Steel Corporation | High tensile cold-rolled steel sheet excellent in ductility and in strain aging hardening properties, and method for producing the same |
EP1154028A1 (fr) * | 2000-05-12 | 2001-11-14 | Corus Staal BV | Acier à plusieurs phases et procédé pour sa fabrication |
US6706419B2 (en) * | 2000-08-04 | 2004-03-16 | Nippon Steel Corporation | Cold-rolled steel sheet or hot-rolled steel sheet excellent in painting bake hardenability and anti aging property at room temperature, and method of producing the same |
US6911268B2 (en) * | 2000-12-29 | 2005-06-28 | Nippon Steel Corporation | High strength hot-dip galvanized or galvannealed steel sheet having improved plating adhesion and press formability and process for producing the same |
US20040055667A1 (en) * | 2000-12-29 | 2004-03-25 | Yoshihisa Takada | High-strength molten-zinc-plated steel plate excellent in deposit adhesion and suitability for press forming and process for producing the same |
JP2003055751A (ja) * | 2001-06-06 | 2003-02-26 | Nippon Steel Corp | 高加工時のめっき密着性および延性に優れた高強度溶融Znめっき鋼板及びその製造方法 |
US20040234807A1 (en) * | 2002-03-01 | 2004-11-25 | Yoshitsugu Suzuki | Surface treated steel plate and method for production thereof |
US7074497B2 (en) * | 2002-03-01 | 2006-07-11 | Jfe Steel Corporation | Coated steel sheet and method for manufacturing the same |
US20040238082A1 (en) * | 2002-06-14 | 2004-12-02 | Jfe Steel Corporation | High strength cold rolled steel plate and method for production thereof |
US20060140814A1 (en) * | 2002-12-20 | 2006-06-29 | Usinor S.A. | Steel composition for the production of cold rolled multiphase steel products |
US7686896B2 (en) * | 2003-09-26 | 2010-03-30 | Jfe Steel Corporation | High-strength steel sheet excellent in deep drawing characteristics and method for production thereof |
US20050139293A1 (en) * | 2003-12-25 | 2005-06-30 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) | High-strength cold-rolled steel sheet excellent in coating film adhesion |
Non-Patent Citations (2)
Title |
---|
NPL: machine translation of JP 10130776A ,05-1998 * |
NPL:machine translation of Fujita et al, JP-2003055751A, 02,2003 * |
Cited By (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20120288733A1 (en) * | 2009-12-21 | 2012-11-15 | Tata Steel Ijmuiden B.V. | High strength hot dip galvanised steel strip |
US8882938B2 (en) * | 2009-12-21 | 2014-11-11 | Tata Steel Ijmuiden B.V. | High strength hot dip galvanised steel strip |
US9677150B2 (en) | 2009-12-21 | 2017-06-13 | Tata Steel Ijmuiden B.V. | High strength hot dip galvanised steel strip |
US9593400B2 (en) | 2012-04-05 | 2017-03-14 | Tata Steel Ijmuiden Bv | Steel strip having a low Si content |
US9695493B2 (en) | 2012-04-05 | 2017-07-04 | Tata Steel Ijmuiden Bv | Steel strip having a low Si content |
US20170240990A1 (en) * | 2012-04-05 | 2017-08-24 | Tata Steel Ijmuiden Bv | Steel strip having a low si content |
CN104755646A (zh) * | 2012-09-03 | 2015-07-01 | 奥钢联钢铁公司 | 对扁钢产品涂覆保护涂层的方法和具有相应保护涂层的扁钢产品 |
CN104046889A (zh) * | 2014-06-09 | 2014-09-17 | 首钢总公司 | 一种导轨用冷轧连续退火带钢及其生产方法 |
US11339454B2 (en) | 2014-07-03 | 2022-05-24 | Arcelormittal | Method for manufacturing a high strength steel sheet and sheet obtained |
US11149325B2 (en) | 2014-07-03 | 2021-10-19 | Arcelormittal | Method for manufacturing a high strength steel sheet and sheet obtained |
US11312212B2 (en) * | 2015-03-31 | 2022-04-26 | Arcelormittal | Panel for vehicle comprising a coated steel sheet locally reinforced |
TWI631219B (zh) * | 2015-05-20 | 2018-08-01 | Ak鋼鐵資產公司 | 低合金第三代先進高強度鋼及使彼等退火之方法 |
AU2016264749B2 (en) * | 2015-05-20 | 2019-02-14 | Ak Steel Properties, Inc. | Low alloy third generation advanced high strength steel |
AU2016264749C1 (en) * | 2015-05-20 | 2019-10-03 | Ak Steel Properties, Inc. | Low alloy third generation advanced high strength steel |
US10633727B2 (en) | 2015-05-20 | 2020-04-28 | Ak Steel Properties, Inc. | Low alloy third generation advanced high strength steel |
WO2016187576A1 (fr) * | 2015-05-20 | 2016-11-24 | Ak Steel Properties, Inc. | Acier haute résistance amélioré de troisième génération faiblement allié |
US10947608B2 (en) | 2015-10-05 | 2021-03-16 | Arcelormittal | Steel sheet coated with a metallic coating based on aluminum and comprising titanium |
US11306381B2 (en) | 2015-12-24 | 2022-04-19 | Posco | High-strength hot-dip zinc plated steel material having excellent plating properties and method for preparing same |
US10907243B2 (en) | 2015-12-24 | 2021-02-02 | Posco | Plated steel material having excellent friction resistance and white rust resistance and method for preparing same |
US11692259B2 (en) | 2015-12-24 | 2023-07-04 | Posco | High-strength hot-dip zinc plated steel material having excellent plating properties and method for preparing same |
US11060157B2 (en) * | 2016-03-31 | 2021-07-13 | Jfe Steel Corporation | Steel sheet, coated steel sheet, method for producing hot-rolled steel sheet, method for producing full hard cold-rolled steel sheet, method for producing steel sheet, and method for producing coated steel sheet |
WO2018031523A1 (fr) * | 2016-08-08 | 2018-02-15 | John Speer | Revêtements modifiés de galvanisation par immersion à chaud présentant une basse température de liquidus, procédés pour leur fabrication et leur utilisation |
US11066716B2 (en) * | 2016-08-10 | 2021-07-20 | Jfe Steel Corporation | Steel sheet and method for producing the same |
US11396691B2 (en) | 2016-12-22 | 2022-07-26 | Posco | Alloy-plated steel material having excellent corrosion resistance and high surface quality |
US11505858B2 (en) | 2016-12-22 | 2022-11-22 | Posco | Alloy-plated steel material having excellent crack resistance, and method for manufacturing same |
DE102017202586B3 (de) | 2017-02-17 | 2018-03-29 | Zf Friedrichshafen Ag | Verfahren zur Herstellung eines Bauteils aus einem mikrolegierten Stahl |
CN107252818A (zh) * | 2017-08-02 | 2017-10-17 | 安徽骏达起重机械有限公司 | 交通轨道的加工方法 |
Also Published As
Publication number | Publication date |
---|---|
CN101627142A (zh) | 2010-01-13 |
MX2009008194A (es) | 2009-08-12 |
WO2008102009A1 (fr) | 2008-08-28 |
MX2019008366A (es) | 2019-09-16 |
BRPI0807957A2 (pt) | 2014-07-01 |
MX366540B (es) | 2019-07-12 |
ES2683010T3 (es) | 2018-09-24 |
EP2115178A1 (fr) | 2009-11-11 |
RU2464338C2 (ru) | 2012-10-20 |
EP3421634A1 (fr) | 2019-01-02 |
JP5586007B2 (ja) | 2014-09-10 |
RU2009135411A (ru) | 2011-03-27 |
HK1139714A1 (en) | 2010-09-24 |
CN101627142B (zh) | 2012-10-03 |
JP2010519415A (ja) | 2010-06-03 |
KR20090122346A (ko) | 2009-11-27 |
EP2115178B1 (fr) | 2018-06-20 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP2115178B1 (fr) | Feuillard d'acier à résistance élevée, laminé à froid et trempé en continu, et procédé de fabrication dudit feuillard | |
EP2126144B1 (fr) | Procédé de mise en forme thermomécanique d'un produit final à très haute résistance et produit obtenu selon ledit procédé | |
US8592049B2 (en) | High strength hot dip galvanized steel sheet and high strength galvannealed steel sheet excellent in shapeability and plateability | |
CA2695138C (fr) | Acier au silicium galvanise ou recuit par galvanisation | |
JP2019521257A (ja) | 低密度溶融亜鉛めっき鋼及びその製造方法 | |
WO2009081997A1 (fr) | Procédés de fabrication d'une feuille d'acier galvanisé à chaud à haute résistance et feuille d'acier recuit après galvanisation à haute résistance | |
KR20100055389A (ko) | Dff 조절에 의한 합금화 아연도금 강판의 제조 방법 | |
JP2006307325A (ja) | 延性に優れる低降伏比型高強度合金化溶融亜鉛めっき鋼板およびその製造方法 | |
KR20150000896A (ko) | Si 함량이 낮은 강 스트립 | |
US20240110257A1 (en) | Galvannealed steel sheet | |
US20230272516A1 (en) | Hot-dip coated steel substrate | |
CN100529116C (zh) | 加工性优异的高强度合金化热浸镀锌钢板及其制造方法 | |
US11590734B2 (en) | Hot-dip coated steel sheet | |
KR101647225B1 (ko) | 표면품질 및 내파우더링성이 우수한 고강도 합금화용융아연도금강판 및 그 제조방법 | |
JPH11131145A (ja) | 高強度高延性溶融亜鉛めっき鋼板の製造方法 | |
JP4846550B2 (ja) | 合金化溶融亜鉛めっき用鋼板及び合金化溶融亜鉛めっき鋼板 | |
JP7480928B2 (ja) | 合金化溶融亜鉛めっき鋼板の製造方法 | |
JP4592000B2 (ja) | 加工性に優れた高強度合金化溶融亜鉛めっき鋼板の製造方法 | |
JPS624860A (ja) | 高張力合金化溶融亜鉛めつき鋼板の製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: CORUS STAAL BV,NETHERLANDS Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HANLON, DAVID NEAL;VLOT, MARGOT JULIA;SIGNING DATES FROM 20100203 TO 20100204;REEL/FRAME:023962/0480 |
|
AS | Assignment |
Owner name: TATA STEEL IJMUIDEN B.V., NETHERLANDS Free format text: CHANGE OF NAME;ASSIGNOR:CORUS STAAL B.V.;REEL/FRAME:025742/0883 Effective date: 20100928 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |