US20100117268A1 - Fine mold and method for regenerating fine mold - Google Patents
Fine mold and method for regenerating fine mold Download PDFInfo
- Publication number
- US20100117268A1 US20100117268A1 US12/691,685 US69168510A US2010117268A1 US 20100117268 A1 US20100117268 A1 US 20100117268A1 US 69168510 A US69168510 A US 69168510A US 2010117268 A1 US2010117268 A1 US 2010117268A1
- Authority
- US
- United States
- Prior art keywords
- film
- light shielding
- fine mold
- shielding unit
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A fine mold comprises a regeneration target film forming a convex part of a formation surface, and a light shielding unit that is configured deeper than a bottom of the formation surface and that regenerates the regeneration target film. A manufacturing cost of a product having a three-dimensional structure can be reduced.
Description
- This application is a divisional of co-pending U.S. patent application Ser. No. 12/604,315, filed Oct. 22, 2009, which is a divisional of Ser. No. 11/860,182, filed Sep. 24, 2007, the entirety of which are incorporated herein by reference.
- A) Field of the Invention
- This invention relates to a fine mold for nanoimprinting, etc., a method for regenerating and a transferring method with the fine mold.
- Priority is claimed to Japanese Patent Application No. 2006-258571, filed on Sep. 25, 2006, the entire contents of which are incorporated herein by reference.
- B) Description of the Related Art
- Conventionally, a transfer imprinting method with a fine mold is well-known. For example, refer to JP H05-241011, JP 2004-304097 and FUJIWARA et al “Tan-itsu shinkin saibo no shuushukuryoku wo sokuteisuru rikigaku sensa no kaihatsu (Development of Dynamic Sensor for Measuring Contraction Power of Single Cardiac Myocyte)” Denkigakkai Bio-Microsystem Kenkyu-kai Shiryo, BMS-05-3, p10-12. A product having a fine three-dimensional structure such as a storage medium, micro electro mechanical systems (MEMS), a micro lens, etc. can be manufactured at a low cost by a transfer imprinting method with the fine mold.
- A fine mold may be damaged by a hard alien substance on a surface or inside of a forming material when the fine mold is pushed to the forming material. Fine molds are expensive because various types of them are manufactured only in small number by using a fine processing technique such as a photolithography technique, an electron beam exposing technique, a laser-beam direct writing method, etc.
- It is an object of the present invention to reduce a manufacturing cost of a product having a three-dimensional structure.
- According to one aspect of the present invention, there is provided a fine mold, comprising: a regeneration target film forming a convex part of a formation surface; and a light shielding unit that is configured deeper than a bottom of the formation surface and that regenerates the regeneration target film.
- This fine mold has the light shielding unit that is configured deeper than the bottom of the forming surface to regenerate the regeneration target film forming the convex part of the firming surface, that is, the light shielding unit is configured in a layer near a reverse of the forming surface. Therefore, the fine mold can regenerate the convex part by using the light shielding unit, equipped to the fine mold, as a mask even if the convex part is damaged. That is, a fine processing technique is not necessary for this fine mold to regenerate the convex part. Therefore, a cost for manufacturing a product having a fine three-dimensional structure can be reduced by using this fine mold in comparison to the conventional fine mold.
- The light shielding unit of the fine mold according to the invention may be formed of an opaque film. In this case, a convex part having a rectangle shaped cross section can be regenerated by using the light shielding unit as a mask.
- The light shielding unit of the fine mold according to the invention may be a gradation mask. In this case, a forming surface of which surface is gently curved can be regenerated. For example, an opaque gray tone mask having slits below a resolution of an exposure device or a half-transparent half tone mask can be used as the gradation mask.
- According to the present invention, the shallowest depth of the light shielding unit may be the same as the deepest depth of the regeneration target film. In this case, there will be no decline in a resolution caused by diffraction and dispersion when a photosensitive for forming the regeneration target film is exposed by using the light shielding unit as a mask.
- The fine mold according to the present invention may further comprise a transparent protection film that is harder than the regeneration target film and configured between the forming surface and the light shielding unit. In this case, damage to the light shielding unit can be prevented so that the regeneration of the forming surface will not be impossible.
- The fine mold according to the present invention may further comprise a transparent reinforcement plate having a concave part in which the light shielding unit is embedded, and the protection film may be embedded in the reinforcement plate between the light shielding unit and the forming surface and formed of transparent material having a lower refractive index than the reinforcement plate. In this case, although the light shielding unit is separated from the regeneration target film, total internal reflection happens at a side of the reinforcement plate of a boundary of the reinforcement plate and the transparent film so that there will be no decline in a resolution caused by diffraction and dispersion when a photosensitive for forming the regeneration target film is exposed by using the light shielding unit as a mask.
- The fine mold according to the present invention may further comprise a transparent reinforcement plate configured at a deeper place than the light shielding unit. In this case, strength of the fine mold will increase.
- According to another aspect of the present invention, there is provided a method of regenerating the above-described fine mold, comprising the steps of: removing the regeneration target film; forming a photosensitive film on a surface from which the regeneration target film is removed; and exposing the photosensitive film by using the light shielding unit as a mask to develop the photosensitive film.
- According to the above-described method of regenerating the fine mold, the regeneration target film can be regenerated without forming a mask for forming the regeneration target film so that a cost for manufacturing a fine structure by the transfer imprinting method can be reduced in comparison to the conventional method. Further, in this regeneration method according to the present invention, the developed photosensitive film may be used as a regeneration target film, and a regeneration target film may be formed in an opening part of the developed photosensitive film.
- The above-described method of regenerating the fine mold may further comprise the step of pushing the fine mold to forming material.
- In this specification, a “forming surface” refers to a surface of a fine mold composing a boundary of forming material and the fine mold. “Transparent” a concept depending on wavelength of light; however, in this specification, “transparent” refers to a condition in which light of wavelengths to be used for exposure of a photosensitive film can pass through with little or no interruption or distortion. Similar to that, “light shielding” refer to a condition in which the light to be used for exposure is interrupted.
-
FIG. 1A toFIG. 1C are cross sectional views showing a fine mold and a transfer imprinting method by using the fine mold according to a first embodiment of the present invention. -
FIG. 2A toFIG. 2C are cross sectional views showing a manufacturing method of the fine mold according to the first embodiment of the present invention. -
FIG. 3A toFIG. 3C are cross sectional views showing the manufacturing method of the fine mold according to the first embodiment of the present invention. -
FIG. 4A toFIG. 4C are cross sectional views showing a regeneration method of the fine mold according to the first embodiment of the present invention. -
FIG. 5A toFIG. 5D are cross sectional views showing a fine mold according to a second embodiment of the present invention. -
FIG. 6A toFIG. 6C are cross sectional views showing a fine mold according to a third embodiment of the present invention. -
FIG. 7A toFIG. 7D are cross sectional views showing a manufacturing method of a fine mold according to a fourth embodiment of the present invention. -
FIG. 8A toFIG. 8D are cross sectional views showing a manufacturing method of a fine mold according to a fifth embodiment of the present invention. -
FIG. 9A andFIG. 9B are cross sectional views showing the manufacturing method of the fine mold according to the fifth embodiment of the present invention. -
FIG. 10A toFIG. 10D are cross sectional views showing a manufacturing method of a fine mold according to a sixth embodiment of the present invention. -
FIG. 11A toFIG. 11C are cross sectional views showing the manufacturing method of the fine mold according to the sixth embodiment of the present invention. -
FIG. 12A toFIG. 12D are cross sectional views showing a manufacturing method of a fine mold according to a seventh embodiment of the present invention. -
FIG. 13A toFIG. 13D are cross sectional views showing a manufacturing method of a fine mold according to an eighth embodiment of the present invention. -
FIG. 14A toFIG. 14C are cross sectional views showing the manufacturing method of the fine mold according to the eighth embodiment of the present invention. - The embodiments of the present invention will be described below with reference to the drawings. In each embodiment, same reference numbers refer to same components, and explanations for the same components are omitted to avoid redundant.
-
FIG. 1A toFIG. 1C are cross sectional views showing a fine mold and a transfer imprinting method by using the fine mold according to a first embodiment of the present invention. - The
fine mold 1 is composed by laminating alight shielding unit 10 on atransparent substrate 11 as a reinforcement plate, atransparent protection film 12, aresin film 13 as a regeneration target film and ahard film 14. Since thelight shielding unit 10 is configured on a layer deeper than a bottom of aformation surface 15 having a concave part and a convex part, aresin film 13 can be regenerated by using thelight shielding unit 10 as a mask. That is, theresin film 13 can be regenerated without forming the mask by using an expensive device for patterning theresin film 13 forming the fine concave part and the convex part of the formation surface, and manufacturing cost of the fine mold is lower than that of the conventional one. The regenerating method of thefine mold 1 will be described later with explanation of its manufacturing method. Moreover, thelight shielding unit 10 is not exposed on the formingsurface 15 in order not to avoid damage of thelight shielding unit 10 even if the forming surface is damaged by the alien substance between thefine mold 1 and the forming target substance, and not only thehard film 14 but also theprotection film 12 harder than theresin film 13 are between thelight shielding unit 10 and the formingsurface 15. - Next, a transfer method used the
fine mold 1 will be explained as an example of nanoimprinting. - As shown in
FIG. 1A , a formingmaterial 91 is applied on a surface of asubstrate 92 composed of silicon wafer, etc. by spin coating, etc. Thermoplastic resin, thermosetting resin, photocurable resin or glass can be used as the forming material. Moreover, the silicon wafer can be used as the forming material. - As shown in
FIG. 1B , thefine mold 1 is pushed to the formingmaterial 91. At this time, because the forming material must be softened, the thermoplastic resin is heated to the glass transition point or more in advance. There are a method to push the formingmaterial 91 and thefine mold 1 with two plates parallel to each other and a method to push the formingmaterial 91 and thefine mold 1 by compressed air as the method to push thefine mold 1. - Next, the forming
material 91 is formed by hardening. For example, the formingmaterial 91 is hardened by cooling in case of the thermoplastic resin, by heating in case of the thermosetting resin, and by irradiating ultraviolet rays in case of the photocurable resin. Then, the concave part and the convex part of the formingsurface 15 of thefine mold 1 are transferred to the formingmaterial 91. - Finally, as shown in
FIG. 1C , thefine mold 1 is exfoliated from the formingmaterial 91. -
FIG. 2A toFIG. 3C are cross sectional views showing a manufacturing method of the fine mold according to the first embodiment of the present invention. - First, the
light shielding unit 10 is formed on thetransparent substrate 11. Quartz, soda-lime glass, transparent crystallized glass, ceramics, resin, clay, alumina, sapphire, etc. can be used as the material of thetransparent substrate 11. For example, thickness of thetransparent substrate 11 is 2 mm. Metals such as Cr, CrO2, Cu, etc., metal oxide, etc., which are opaque material to ultraviolet rays can be used for the material of thelight shielding unit 10. These materials can form a film on thetransparent substrate 11 by sputtering, evaporation and CVD. For example, thickness of thelight shielding unit 10 is 0.1 μm. A lamination of Cr and CrOx on the quartz and the glass used as a mask and reticle can be used as a lamination of thelight shielding unit 10 on thetransparent substrate 11. - Next, as shown in
FIG. 2B , thelight shielding unit 10 is patterned by using aphotoresist 50. For example, thephotoresist 50 is exposed by a stepper, an aligner or an electron beam exposure device, and a developed pattern of thephotoresist 50 is transferred to thelight shielding unit 10. In the etching of thelight shielding unit 10, for example, thelight shielding unit 10 consisting of Cr is anisotropically etched by ion milling or cerium ammonium nitrite solution. Thelight shielding unit 10 may be patterned by the laser direct writing method without using thephotoresist 50. In the manufacture of the mold producing various kinds and small amount with less usage times of the reticles, the laser direct writing method is effective for reducing the manufacturing cost. - Next, as shown in
FIG. 2C , thetransparent protection film 12 is formed to cover thelight shielding unit 10. SiN, a glass with a low-melting point, AlN, SiON, TaO2, TiO2, ceramics, resin, clay, etc., can be used as the material of thetransparent protection film 12. It is preferable that hardness of theprotection film 12 is harder than the resin film that is a regeneration target. For example, as the film-forming method, plasma CVD is used when SiN is the material. A surface of theprotection film 12 may be planarized by CMP and etched-back after forming theprotection film 12. - Next, as shown in
FIG. 2D , thephotosensitive film 51 is formed on theprotection film 12. For example, thephotosensitive film 51 is formed by applying a negative-typed photo resist with thickness of 70 μm to heat and harden. - Thereafter, as shown in
FIG. 3A , an ultraviolet rays is irradiated from a reverse side of thetransparent substrate 11, that is, from thephotosensitive film 51 of thetransparent substrate 11 and the reverse side, to expose thephotosensitive film 51. At this time, thephotosensitive film 51 is exposed only in aexposure region 53 that is not shaded by thelight shielding unit 10, and thephotosensitive film 51 is not exposed in anunexposed region 52 that is shaded by thelight shielding unit 10. The light used for the exposure is not limited and can be arbitrary selected corresponding to a design rule such as an ultraviolet ray, a far ultraviolet ray, a deep ultraviolet ray, an extreme ultraviolet ray and an x-ray. Of course, material of thelight shielding unit 10 can be selected corresponding to wavelength of the light used for the exposure. - Next, when the
photosensitive film 51 is developed, aresin film 13 having a fixed pattern is formed as shown inFIG. 3B . InFIG. 3B , aphotosensitive region 53 of the negative-typed photoresist remains. InFIG. 3B , an example that thephotosensitive region 53 becomes theresin film 13 to be the regenerating target is shown, however; needless to say, a positive-typed photoresist can be used as thephotosensitive film 51. - Finally, as shown in
FIG. 3C , ahard film 14 is formed on a whole surface of thefine mold 1. Other inorganic material such as metal, a metal compound, ceramics, etc. can be used as the material of thehard film 14. Sputtering, plating and evaporation can be used for formation of thehard film 14. A fluorine film may be formed on thehard film 14 in order to improve mold release property on the surface of thehard film 14. -
FIG. 4A toFIG. 4C are cross sectional views showing a regeneration method of the fine mold according to the first embodiment of the present invention. As shown inFIG. 4A , thehard film 14 and theresin film 13 may be deformed by alien substance between thefine mold 1 and the forming material. When thefine mold 1 is used in a state that thehard film 14 and theresin film 13 are deformed, the shape of the deformed formingsurface 15 is transferred to the forming material. Since thefine mold 1 has thelight shielding unit 10 as the light shielding unit on a surface deeper than the bottom of the formingsurface 15, the formingsurface 15 can be regenerated as described below. - First, as shown in
FIG. 4B , thehard film 14 is removed. When thehard film 14 is made of Ni, the hard film can be removed by using aqueous ferric chloride solutions for etchant. - Next, as shown in
FIG. 4C , theresin film 13 is removed. For example, theresin film 13 made of a photoresist is removed by using N-Methyl-2-pyrrolidone (NMP) and acetone. This state is just before forming thephotosensitive film 51 shown inFIG. 2D in the manufacturing process of thefine mold 1, and after patterning thelight shielding unit 10 that becomes a mask for exposing and developing thephotosensitive film 51. - Then, as explained with reference to
FIG. 2D ,FIG. 3A ,FIG. 3B andFIG. 3C , when thephotosensitive film 51 is formed, and thephotosensitive film 51 is exposed from the reverse side of thetransparent substrate 11 to develop and form thehard film 14, thefine mold 1 is regenerated. Moreover, theprotection film 12 may be removed and reformed, and the surface may be planalized before forming thephotosensitive film 51. Since the stepper and reticle are not used, a processing cost after the process to form thephotosensitive film 51 shown inFIG. 2D is considerably lower than a manufacturing cost in case of manufacturing the entirefine mold 1. That is, since the regeneration cost of thefine mold 1 is considerably lower than the manufacturing cost of thefine mold 1, the manufacturing cost of the substance having fine three-dimensional shape can be further lower than the conventional imprinting method by using thefine mold 1. -
FIG. 5A toFIG. 5D are cross sectional views showing a fine mold according to a second embodiment of the present invention. A fine mold 2 is different from the first embodiment in a point that the fine mold 2 has gently curving concave and convex parts on the formingsurface 15. The gently curving concave and convex parts of the formingsurface 15 depend on a cross-sectional shape of theresin film 13. As same as the first embodiment, in the second embodiment, a dome-shapedresin film 13 is formed by exposing thephotosensitive film 51 as shown inFIG. 5A and baking annon-exposing region 52 of thephotosensitive film 51 to reflow as shown inFIG. 5C after developing thephotosensitive film 51 as shown inFIG. 5B . -
FIG. 6A toFIG. 6C are cross sectional views showing a fine mold according to a third embodiment of the present invention. A fine mold 3 is different from the second embodiment in a point that thelight shielding unit 10 for forming thephotosensitive film 51 is structured as a gray tone mask. A plurality ofslits 111 with a width below a resolution of the exposure device are formed on thelight shielding unit 10 that is the gradation mask. A half-exposing region is formed on thephotosensitive film 51 corresponding to the width and the interval of theslits 111. The concave part and the convex part gently curving along the surface of theresin film 13 obtained by developing thephotosensitive film 51 inFIG. 6B can be formed by setting the width and the interval of theslits 11 so that the exposed condition of the half-exposed region continuously changes. Thephotosensitive film 51 may be exposed from thetransparent substrate 12 in a condition that a reflection prevention film is formed on the surface of thephotosensitive film 51. Moreover, distribution of photosensitivity (reactivity) caused by a standing wave inside thephotosensitivity film 51 may be dissolved by baking thephotosensitive film 51 after exposing thephotosensitive film 51. The formingsurface 15 having an earthenware-mortar-shaped concave part can be formed by forming plurality of theslits 111 in concentric circles. -
FIG. 7A toFIG. 7D are cross sectional views showing a manufacturing method of a fine mold according to a fourth embodiment of the present invention. - A fine mold 4 has a
half tone mask 19, theresin film 13 formed by using thehalf tone mask 19 and thehard film 14 covering theresin film 13. The gently curving formingsurface 15 is formed by theresin film 13 formed by using thehalf tone mask 19 that is the gradation mask. The manufacturing method of the fine mold 4 is as follow. - First, a transmission factor of an ultraviolet ray of the
half tone mask 19 shown inFIG. 7A is set to be a desired value by an electron beam exposure. At this time, an earthenware-mortar-shaped concave part can be formed on the surface of theresin film 14 exposed and developed by using thehalf tone mask 19 as the mask by the exposure so that the transmission factor of the ultraviolet ray from the surface of thehalf tone mask 19 decreases in proportion to the distance from a certain point. - Next, as shown in
FIG. 7B , thephotosensitive film 51 is applied, and an ultra violet ray is irradiated from the reverse side (that is, the reverse side of the surface where thephotosensitive film 51 is laminated) of thehalf tone mask 19. Then, thephotosensitive film 51 is exposed corresponding to the light transmission factor of thehalf tone mask 19. Thephotosensitive film 51 may be exposed in a state of being formed the reflection prevention film on the surface of thephotosensitive film 51. - Next, when the
photosensitive film 51 is developed, as shown inFIG. 7C , the resin film whose surface gently curves is formed. Thephotosensitive film 51 may be baked in order to resolve distribution of the photosensitivity (reactivity) of the photosensitive film caused by the standing wave inside thephotosensitive film 51 before developing. - Finally, when the
hard film 14 is formed on the surface of theresin film 13, the fine mold 4 shown inFIG. 7D is completed. - In the fine mold 4, the
half tone mask 19 and theresin film 13 are contacting with each other. That is, the deepest point of the resin film as a regeneration target film and the shallowest point of thehalf tone mask 19 as the light shielding unit to work as a mask for forming theresin film 13 are agreed with each other. Therefore, at the time of manufacturing and regenerating the fine mold 4, when thephotosensitive film 51 is exposed from the reverse side of thehalf tone mask 19, that is, the reverse side of thephotosensitive film 51, there will be no decline in a resolution caused by diffraction and dispersion of the ultraviolet ray. -
FIG. 8A toFIG. 9D are cross sectional views showing a manufacturing method of a fine mold according to a fifth embodiment of the present invention. It is different from the first embodiment in a point that afine mold 5 includes thelight shielding unit 10 as the light shielding unit and theprotection film 20 which are embedded in thetransparent substrate 11. Moreover, it is different from the first embodiment in a point that the depth of the shallowest point of thelight shielding unit 10 agrees with the depth of the deepest point of theresin film 13. That is, thelight shielding unit 10 is jointed to the whole part of the wall of the concave part of thetransparent substrate 11, and the concave part of thetransparent substrate 11 is completely re-embedded by theprotection film 20 formed on thelight shielding unit 10. The manufacturing method of thefine mold 5 is as follow. - First, as shown in
FIG. 8A , concave parts for embedding the light shielding unit are formed on the surface of thetransparent substrate 11. For example, the concave parts may be formed by photolithography using thephotoresist mask 54, and the concave parts may be formed by the laser-beam direct writing method. - Next, as shown in
FIG. 8B , thelight shielding unit 10 is formed on the surface of thetransparent substrate 11. Thelight shielding unit 10 works as a seed layer of theprotection film 20 and as the light shielding unit, for example, thelight shielding unit 10 is formed by laminating TiNX on the surface of thetransparent substrate 11 by sputtering. An adhering layer made of Ti, Cr, etc. may be formed between the TiNx and thetransparent substrate 11. - Then, as shown in
FIG. 8C , theprotection film 20 is formed on the surface of thelight shielding unit 10. For example, theprotection film 20 is formed by depositing W, Ta, Ti, Mo, Cu, TiN, TaN, MoN, etc. with a thickness of 50 μm by the CVD. Theopaque protection film 20 works also as the light shielding unit. Theprotection film 20 may be formed by electrolysis plating of alloy such as NiP, NiW, NiCo, NiFe, NiMn, NiMo, etc. and metal such as Ni, Cr. - Thereafter, as shown FIG. in 8D, the
protection film 20 and thelight shielding unit 10 are removed until thetransparent substrate 11 is exposed by grinding and polishing. - Finally, as same as the first embodiment, and as shown in
FIG. 9A andFIG. 9B , when theresin film 13 and thehard film 14 are formed, thefine mold 5 is completed. -
FIG. 10A toFIG. 11C are cross sectional views showing a manufacturing method of a fine mold according to a sixth embodiment of the present invention. It is different from the fifth embodiment in a point that thetransparent substrate 11 of a fine mold 6 is made of a photosensitive glass having a crystallizingregion 21 andnon-crystallizing region 22. The crystallizingregion 21 may be half-transparent or opaque. The manufacturing method of the fine mold 6 is as follow. - First, as shown in
FIG. 10A , thetransparent substrate 11 formed of the photosensitive glass is heated after exposing a part of thetransparent substrate 11 by using, for example, thephoto mask 55 having the light shielding unit (pattern) made of CrO2 on the quartz substrate, and a crystallite is generated in the exposing region. The exposing region becomes acrystallization region 21. At this time, the crystallite is not generated in the unexposed region. - Next, as shown in
FIG. 10B ,concave parts 24 are formed by selectively etching the crystallizingregion 21 of thetransparent substrate 11 by using diluted hydrofluoric acid. - Then, as shown in
FIG. 10C , thelight shielding unit 10 is formed. For example, thelight shielding unit 10 may be formed by accumulating Ni, Co, and Cu by electroless plating, or thelight shielding unit 10 made of Ag may be formed by Tollens test. - Thereafter, as shown in
FIG. 10D , theprotection film 20 made of low-melting point glass is formed on thelight shielding unit 10, and theconcave parts 24 are completely buried. - Then, the
protection film 20 and thelight shielding unit 10 are removed until thetransparent substrate 11 is exposed by grinding and polishing. - Finally, as same as the first embodiment, and as shown in
FIG. 11A ,FIG. 11B andFIG. 11C , when theresin film 13 and thehard film 14 are formed, the fine mold 6 is completed. -
FIG. 12A toFIG. 12D are cross sectional views showing a manufacturing method of a fine mold according to a seventh embodiment of the present invention. It is different from the first embodiment in a point that thelight shielding unit 10 of a fine mold 7 is exposed on the reverse side of the mold and that thetransparent substrate 11 itself works as the protection film of thelight shielding unit 10. The manufacturing method of the fine mold 7 is as follow. - First, as same as the first embodiment, and as shown in
FIG. 12A , thelight shielding unit 10 is formed on thetransparent substrate 11. - Next, as shown in
FIG. 12B , thephotosensitive film 51 is formed on the reverse side of thelight shielding unit 10 of thetransparent substrate 11, and an ultraviolet ray is irradiated from thelight shielding unit 10 side to expose a part of thephotosensitive film 51. - Then, as same as the first embodiment,
unexposed region 52 of thephotosensitive film 51 is removed, and theresin film 13 formed of the exposingregion 53 is formed. Thereafter, when thehard film 14 is formed, the fine mold 7 is completed. -
FIG. 13A toFIG. 14C are cross sectional views showing a manufacturing method of a fine mold according to an eighth embodiment of the present invention. The shallowest part of thelight shielding unit 10 of a fine mold 8 is positioned at deeper than the deepest point of theresin film 13 that is the regeneration film, and it is different from other embodiments in a point that the decline of the resolution by those embodiments is structurally prevented. - For example, the
light shielding unit 10 as the light shielding unit is connected with the bottom of the concave part of thetransparent layer 27 as the reinforcement plate, and the concave part of thetransparent layer 27 is completely buried with thetransparent substrate 11 remained on thelight shielding unit 10, and the depth of the shallowest part of thetransparent substrate 11 is same as the depth of the deepest part of theresin film 13. Thetransparent substrate 11 works as the transparent protection film of thelight shielding unit 10. The material of thetransparent substrate 11 and the material of thetransparent layer 27 are selected so that a refractive index of thetransparent substrate 11 is smaller than a refractive index of thetransparent layer 27. - As described in the above, a total internal reflection occurs on both interfaces (refer to
FIG. 14A ) at the time of exposing of thephotosensitive film 51 by setting the refractive index of thetransparent substrate 11 and the refractive index of thetransparent layer 27. Therefore, the resolution will not decline even though thelight shielding unit 10 is positioned at deeper than theresin film 13 that is the regenerating target film. The manufacturing method of the fine mold 8 is as follow. - First, the
light shielding unit 10 is formed on thetransparent substrate 11 as same as the first embodiment. - Next, as shown in
FIG. 13A , areinforcement substrate 26 is joined to the reverse side of thelight shielding unit 10 of thetransparent substrate 11. For example, thereinforcement substrate 26 made of glass, ceramics, metal or the likes is adhered to thetransparent substrate 11. Moreover, a metal film made of Cu or Sn may be formed on the reverse of thetransparent substrate 11 before forming thelight shielding unit 10, and this metal film may be used as thereinforcement substrate 26. - Next, as shown in
FIG. 13B , a part of thetransparent substrate 11 is removed by anisotropic etching by using thelight shielding unit 10 as the mask. At this time, it is preferable to remove thetransparent substrate 11 until thereinforcement substrate 26 is exposed; however, an ending point of the etching may be controlled to a depth not to expose thereinforcement substrate 26. For example, when thetransparent substrate 11 is quartz or glass, thetransparent substrate 11 is etched by RIE by using a gas of which main component is CF4. Moreover, for example, when thetransparent substrate 11 is resin, thetransparent substrate 11 is etched by RIE by using a gas of which main component is O2. - Next, as shown in
FIG. 13C , thetransparent layer 27 is formed to bury thetransparent substrate 11 and thelight shielding unit 10. Resin, glass, ceramics, clay, etc. may be used as the material of thetransparent layer 27. After forming thetransparent layer 27, it may be planarized by grinding, polishing and etching-back the surface. - Then, as shown in
FIG. 13D , thereinforcement substrate 26 is removed. - Thereafter, as same as the first embodiment, and as shown in
FIG. 14A ,FIG. 14B andFIG. 14C , when theresin film 13 and thehard film 14 are formed, the fine mold 8 is completed. - The present invention has been described in connection with the preferred embodiments. The invention is not limited only to the above embodiments. It is apparent that various modifications, improvements, combinations, and the like can be made by those skilled in the art.
- For example, the
hard film 14 is not always necessary, and theprotection film 12 is not always necessary. Moreover, the resin film formed of the photosensitive film does not have to work as the regeneration target film, but the regeneration target film may be formed by a lift-off process by using the resin film as the mask. Moreover, materials of the substrate and the film composing a fine mold according to the embodiments are arbitrary selected corresponding to the functions to be required for the fine mold, and it is natural that the forming method and the forming conditions of the films are arbitrary selected depending on the material of the film and the characteristics of the film that has already been formed. - Moreover, it is natural that the shapes and the sizes of the forming surface of the fine molds are designed corresponding to the shapes of what to be formed by using those molds and the design rules. Furthermore, although the explanations of the regeneration method of the fine mold according to the embodiments of the present invention except the first embodiment have been omitted, it is same as the first embodiment in a point that the regenerating target film and the hard film are regenerated by using the light shielding unit after removing the regenerating target film and the hard film, and the fine mold according to each embodiment can be regenerated by executing the latter manufacturing method explained in each embodiment.
Claims (9)
1. A method of manufacturing a fine mold comprising:
forming a light shielding unit on a transparent substrate;
forming a transparent protection film on the light shielding unit; and
forming a target film on the transparent protection film, the target film forming a convex part of a formation surface.
2. The method of manufacturing a fine mold according to claim 1 , wherein the act of forming the light shielding unit further comprises forming the light shield unit as an opaque film.
3. The method of manufacturing a fine mold according to claim 1 , wherein the act of forming the light shielding unit further comprises forming the light shield unit as a gradation mask.
4. The method of manufacturing a fine mold according to claim 1 , further comprising forming a shallowest depth of the light shielding unit the same as deepest depth of the target film.
5. The method of manufacturing a fine mold according to claim 1 , wherein the transparent protection film is harder than the target film.
6. The method of manufacturing a fine mold according to claim 1 , further comprising:
forming the transparent substrate as a transparent reinforcement plate having a concave part in which the light shielding unit is embedded, and
wherein the transparent protection film is embedded in the transparent reinforcement plate between the light shielding unit and the forming surface and is formed of transparent material having a lower refractive index than the transparent reinforcement plate.
7. The method of manufacturing a fine mold according to claim 1 , wherein the act of forming the light shielding unit further comprises:
forming a film on the transparent substrate; and
patterning the film to form the light shielding unit.
8. The method of manufacturing a fine mold according to claim 1 , wherein the act of forming the target film further comprises:
forming a photosensitive film on the transparent protective film;
exposing the photosensitive film to light through the light shielding unit; and
developing the photosensitive film to form the target film.
9. The method of manufacturing a fine mold according to claim 1 , further comprising forming a hard film on the target film.