US20100096262A1 - Electrostatic chuck - Google Patents
Electrostatic chuck Download PDFInfo
- Publication number
- US20100096262A1 US20100096262A1 US12/647,719 US64771909A US2010096262A1 US 20100096262 A1 US20100096262 A1 US 20100096262A1 US 64771909 A US64771909 A US 64771909A US 2010096262 A1 US2010096262 A1 US 2010096262A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- electrostatic chuck
- conductor film
- projections
- projection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An electrostatic chuck (8) includes a dielectric board (14) having an upper surface on which a plurality of projections (17 a) for supporting a substrate on top surfaces and recesses (17 b) surrounding the projections (17 a) are formed, an electrode (15) formed inside the dielectric board (14), and an external power supply (15) which applies a voltage to the electrode (15). The dielectric board (14) includes a conductor film (19) formed on at least the top surface of each projection (17 a), and has a three-dimensional structure which causes the conductor film (19) to generate a Johnson-Rahbeck force between the substrate (9) and conductor film (19) when a voltage is applied to the electrode (15).
Description
- This application is a continuation of PCT/JP2008/066340, filed on Sep. 10, 2008, which claims the benefit of Japanese Patent Application No. 2007-234968, filed Sep. 11, 2007, which is hereby incorporated by reference herein in its entirety.
- The present invention relates to an electrostatic chuck to be used to hold a substrate on a support member when processing the substrate in a semiconductor fabrication step or in an electronic part manufacturing step which manufactures a magnetic head or the like and has a step similar to the semiconductor fabrication step.
- Conventionally, an electrostatic chuck disclosed in, for example,
patent reference 1 is known as an electrostatic chuck. This electrostatic chuck includes a dielectric board having projections and recesses formed on the upper surface by embossing, an electrode formed inside the dielectric board, and an external power supply for applying a voltage to the electrode. Also, the top surface (substrate supporting surface) of each projection is covered with a conductor line. This conductor line electrically connects the substrate supporting surfaces of the projections, and the electrostatic chuck has a switch for grounding or floating the conductor line. Furthermore, those portions of the electrode which are close to the individual projections are removed in one-to-one correspondence with the projections. - The above-mentioned electrostatic chuck has as its main purpose to prevent the generation of particles by friction between a substrate and the projections, and prevents the electrostatic chucking force from acting between the substrate supporting surfaces of the projections and a substrate. That is, when holding a substrate by applying a voltage to the electrode, the substrate supporting surface of each projection and the lower surface of the substrate in contact with the substrate supporting surface are set at the same potential by moving electric charge through the conductor line, thereby preventing the Johnson-Rahbeck force from acting between them (see paragraph [0022] of patent reference 1). The substrate is held by the spatial Coulomb force between the recesses of the upper surface of the dielectric board and the lower surface of the substrate (see paragraph [0040] of patent reference 1). Also, when unloading the substrate, the substrate can be separated by rapidly moving electric charge by grounding the conductor line (see paragraph of patent reference 1).
- Furthermore, in an electrostatic chuck disclosed in
patent reference 2, an arrangement in which a separation mask has an insulating material such as diamond and a mask made of a metal such as titanium or titanium nitride is disclosed. - Patent reference 1: Japanese Patent Laid-Open No. 2004-22889
- Patent reference 2: Japanese Patent Laid-Open No. 10-70180
- In
patent reference 1, however, the Johnson-Rahbeck force acting between the substrate supporting surface of each projection and the lower surface of a substrate in contact with the substrate supporting surface is a very large chucking force. Therefore, the chucking force is often insufficient in a conventional electrostatic chuck in which no Johnson-Rahbeck force acts. This problem can be solved by allowing the Johnson-Rahbeck force to act by removing the conductor line covering the substrate supporting surfaces of the projections. When removing the conductor line covering the substrate supporting surfaces of the projections, however, electric charge cannot rapidly be moved any longer by grounding the conductor line by the switch. Consequently, the residual electric charge delays the time at which the substrate can be separated. In addition, to remove electric charge when unloading a substrate, the conventional electrostatic chuck must have a special wiring structure in which the conductor line covering and electrically connecting the substrate supporting surfaces of the projections is formed and connected to the switch. This complicates the structure. - Also, when a material different from the material of the electrostatic chuck is used as the insulating material as disclosed in
patent reference 2, electric charge on the lower surface of a substrate is trapped, and as a consequence the residual chucking force remains on the substrate. This makes the separation of the substrate from the electrostatic chuck unstable. - The present invention has been made in consideration of the above conventional problems, and has as its object to obtain a sufficient electrostatic chucking force and achieve rapid unloading of a substrate from an electrostatic chuck (improve the stability of substrate separation) by a simple structure.
- An electrostatic chuck according to the present invention which achieves the above object is comprises a dielectric board having an upper surface on which a plurality of projections for supporting a substrate on top surfaces and recesses surrounding the projections are formed, an electrode formed inside the dielectric board, and an external power supply which applies a voltage to the electrode, wherein the dielectric board includes a conductor film formed on at least the top surface of each projection, and has a three-dimensional structure which causes the conductor film to generate a Johnson-Rahbeck force between the substrate and the conductor film when a voltage is applied to the electrode.
- A gap is formed between the recess around the projection on the upper surface of the dielectric board and the lower surface of a substrate. Therefore, when different electric charges are stored on the upper surface of the dielectric board and the lower surface of the substrate by applying a voltage to the electrode, the spatial Coulomb force acts between the recess of the upper surface of the dielectric board and the lower surface of the substrate. Also, the same electric charge as that on the upper surface of the dielectric board is stored on the upper surface of the conductor film. Between the conductor film on the top surface of the projection and the lower surface of the substrate, fine three-dimensional structures of the top surfaces microscopically form contact points and a fine gap. Accordingly, the Johnson-Rahbeck force acts in this fine gap between the conductor film and substrate. That is, in the present invention, the substrate is chucked by both the spatial Coulomb force acting between the recess of the upper surface of the dielectric board and the lower surface of the substrate, and the Johnson-Rahbeck force acting between the conductor film on the projection of the upper surface of the dielectric board and the lower surface of the substrate. As a consequence, a sufficient substrate holding force is obtained in the present invention.
- On the other hand, when the voltage application to the electrode is stopped, the lower surface of the substrate and the conductor films on the top surfaces of the plurality of projections are going to have the same potential via the contact points between the conductor films and the lower surface of the substrate, thereby removing electric charge. This makes it possible to eliminate the residual chucking force on the substrate, and rapidly unload the substrate after the voltage application to the electrode is stopped. To enable rapid charge removal, it is advantageous to increase the number of contact points between the substrate and conductor films, and the conductor films are preferably as smooth as possible. Even when the conductor films are smoothened, the gap between the conductor films and the lower surface of the substrate does not microscopically disappear, but the width of the gap further decreases, and the Johnson-Rahbeck force acting in this gap increases.
- Furthermore, the generation of particles can be suppressed by selecting a film having a high wear resistance as the conductor film.
- The accompanying drawings, which are incorporated in and constitute a part of the specification, illustrate embodiments of the invention and, together with the description, serve to explain the principles of the invention.
-
FIG. 1 is an exemplary sectional view of a sputtering apparatus including an electrostatic chuck according to an embodiment of the present invention; -
FIG. 2 is a partially enlarged exemplary sectional view of the electrostatic chuck according to the embodiment of the present invention; -
FIG. 3 is a partially enlarged exemplary sectional view of an electrostatic chuck according to another embodiment of the present invention; -
FIG. 4A is a view showing the states of electric charge on the upper surface of a conductor film of the electrostatic chuck shown inFIG. 2 and the lower surface of a substrate when it is chucked; -
FIG. 4B is a view showing the states of electric charge on the upper surface of the conductor film of the electrostatic chuck shown inFIG. 2 and the lower surface of a substrate when it is separated; -
FIG. 5A is a view showing the states of electric charge on the upper surface of a conductor film of the electrostatic chuck shown inFIG. 3 and the lower surface of a substrate when it is chucked; -
FIG. 5B is a view showing the states of electric charge on the upper surface of the conductor film of the electrostatic chuck shown inFIG. 3 and the lower surface of a substrate when it is separated; -
FIG. 6 is a graph showing the states of the supporting force (chucking force) when the conductor film is formed and not formed; -
FIG. 7 is a graph plotting the results of calculations of the chucking forces of a projection and recess in the electrostatic chuck based on this embodiment; and -
FIG. 8 is a graph showing the results of measurements of times before a substrate can be separated by applying a reverse voltage to the electrostatic chuck for a predetermined time immediately before an external power supply is turned off. - Embodiments of the present invention will be explained in detail below. However, constituent elements described in the embodiments are merely examples, and the technical scope of the present invention is determined by the scope of the appended claims and is not limited by the following individual embodiments.
- An electrostatic chuck of the present invention will be explained below by taking a case in which the electrostatic chuck is applied to a sputtering apparatus as an example.
-
FIG. 1 is an exemplary sectional view of a sputtering apparatus including an electrostatic chuck according to an embodiment of the present invention.FIG. 2 is a partially enlarged exemplary sectional view of the electrostatic chuck according to the embodiment of the present invention.FIG. 3 is a partially enlarged exemplary sectional view of an electrostatic chuck according to another embodiment of the present invention.FIG. 4A is a view showing the states of electric charge on the upper surface of a conductor film of the electrostatic chuck shown inFIG. 2 and the lower surface of a substrate when it is chucked.FIG. 4B is a view showing the states of electric charge on the upper surface of the conductor film of the electrostatic chuck shown inFIG. 2 and the lower surface of a substrate when it is separated.FIG. 5A is a view showing the states of electric charge on the upper surface of a conductor film of the electrostatic chuck shown inFIG. 3 and the lower surface of a substrate when it is chucked.FIG. 5B is a view showing the states of electric charge on the upper surface of the conductor film of the electrostatic chuck shown inFIG. 3 and the lower surface of a substrate when it is separated. - First, an outline of the sputtering apparatus will be explained with reference to
FIG. 1 . The sputtering apparatus shown inFIG. 1 includes avessel 1 that can be evacuated by an external evacuating mechanism (not shown), and atarget 3 attached to the ceiling of thevessel 1 with a ring-like insulatingmember 2 interposed between them.Magnets 5 fixed on ayoke plate 4 are arranged to face the lower surface of thetarget 3. Also, a sputteringpower supply 6 for applying a voltage is connected to thetarget 3. - In a position opposite to the
target 3, anelectrostatic chuck 8 is installed on a substratetemperature adjusting unit 7 fixed to the bottom of thevessel 1, and asubstrate 9 is placed on theelectrostatic chuck 8. In addition, acylindrical shielding member 10 is formed along the inner surface of the circumferential wall of thevessel 1 between thetarget 3 andelectrostatic chuck 8. - The substrate
temperature adjusting unit 7 is a member that controls the temperature of thesubstrate 9 via theelectrostatic chuck 8, and includes athermocouple 12 and heating/cooling portions 13 connected to a temperature controlpower supply mechanism 11. In the substratetemperature adjusting unit 7, the temperature controlpower supply mechanism 11 operates the heating/cooling portions 13 based on a temperature detected by thethermocouple 12, thereby heating or cooling theelectrostatic chuck 8. - The
electrostatic chuck 8 installed on the substratetemperature adjusting unit 7 includes adielectric board 14 having an embossed surface (upper surface), anelectrode 15 formed inside thedielectric board 14, and anexternal power supply 16 for applying a predetermined voltage to theelectrode 15. - The upper surface of the
dielectric board 14 has a plurality ofprojections 17 a and surroundingrecesses 17 b formed by embossing. On the edge of the upper surface of thedielectric board 14, an outerperiphery protruding portion 18 is formed to surround the region where theprojections 17 a and recesses 17 b are formed. Theprojections 17 a and outerperiphery protruding portion 18 have top surfaces on which thesubstrate 9 is placed, and have almost the same height. - A
conductor film 19 is formed to cover at least the top surface of eachprojection 17 a, except for therecesses 17 b. Eachconductor film 19 has a three-dimensional structure that generates the Johnson-Rahbeck force between thesubstrate 9 andconductor film 19 when a voltage is applied to the electrode 15 (to be described later). This three-dimensional structure functions as a Johnson-Rahbeck force generating portion. Eachconductor film 19 may cover not only the top surface of theprojection 17 a but also its circumferential surface. However, eachconductor film 19 is not formed in therecess 17 b and is electrically isolated fromother conductor films 19. - In the example shown in
FIG. 1 , theconductor film 19 is formed on the top surface of the outerperiphery protruding portion 18 as well. Theconductor film 19 on the outerperiphery protruding portion 18 is preferably formed to facilitate equalizing the overall heights of the outerperiphery protruding portion 18 andprojections 17 a, but may also be omitted. - The
electrode 15 is a monopolar electrode and connected to theexternal power supply 16 as a DC power supply via aswitch 20. A predetermined negative voltage is applied to theelectrode 15 by turning on theswitch 20. Although theelectrode 15 shown inFIG. 1 is a monopolar electrode, it is also possible to form bipolar electrodes on the inner and outer peripheries of thedielectric board 14, and apply a negative voltage to one electrode and a positive voltage to the other. Furthermore, theelectrode 15 has a diameter smaller than that of the outerperiphery protruding portion 18. Therefore, theelectrode 15 exists only below the region where theprojections 17 a and recesses 17 b are formed, and does not exist near the portion immediately below the outerperiphery protruding portion 18. Since theelectrode 15 does not exist below the outerperiphery protruding portion 18, the outerperiphery protruding portion 18 does not contribute to chucking of thesubstrate 9. - As described previously, the
substrate 9 is placed on the top surfaces of theprojections 17 a and outerperiphery protruding portion 18. Between thesubstrate 9 anddielectric board 14, therefore, therecesses 17 b form a gap in the region surrounded by the outerperiphery protruding portion 18. Agas supply source 22 is connected to this gap via agas supply path 21, so a gas (e.g., argon gas) can be supplied to the gap. By thus supplying the gas to the gap, it is possible to conduct the heat of the substratetemperature adjusting unit 7 to thesubstrate 9 by thermal conduction of theelectrostatic chuck 8 and the gas in the gap, thereby maintaining thesubstrate 9 at a predetermined temperature. - The
electrostatic chuck 8 will be explained in more detail below with reference toFIGS. 1 to 3 . Theprojection 17 a is normally a column and preferably has a diameter of 0.7 mm or less. The lower limit is determined by, for example, the necessary mechanical strength of theprojection 17 a and the limitations on processing, and generally about 0.3 mm. If the diameter of theprojection 17 a increases, it becomes difficult to rapidly remove electric charge when separating thesubstrate 9. This is so presumably because many contact points between thesubstrate 9 and theconductor films 19 formed on the top surfaces of theprojections 17 a achieve rapid charge removal, although details are unknown. When the diameter of theprojection 17 a is small, the maximum surface roughness (Ry) of the microscopic three-dimensional structure, which functions as a Johnson-Rahbeck force generating portion, of the top surface of theprojection 17 a decreases from the viewpoint of probability, and the upper surface smoothness of theconductor film 19 increases. This perhaps increases the number of contact points between thesubstrate 9 andconductor film 19. When the smoothness of theconductor film 19 increases, the width of the gap formed by the microscopic three-dimensional structure, which functions as a Johnson-Rahbeck force generating portion, of the top surface of theprojection 17 a decreases, and the Johnson-Rahbeck force acting between thesubstrate 9 andconductor film 19 increases. - To obtain favorable chucking and separating actions, the top surface of the
projection 17 a preferably has a smooth surface, and preferably has an Ry (maximum surface roughness) of 2.5 μm or less and an Ra (central line average roughness) of 0.25 μm or less. Since it is practically impossible to form a completely smooth surface, the lower limit is not particularly restricted. From the viewpoint of a practical smoothing limit, however, the Ry is 0.2 μm or more, and the Ra is 0.02 μm or more. - The height of the
projections 17 a and outerperiphery protruding portion 18 is preferably 15 μm or less, provided that the chuckedsubstrate 9 is not in contact with therecesses 17 b. The Coulomb force acting between thesubstrate 9 and recesses 17 b can be increased by decreasing the height of theprojections 17 a and outerperiphery protruding portion 18. The lower limit of the height is generally about 6.5 μm. - To obtain an appropriate chucking force and achieve rapid charge removable, the
projections 17 a are preferably formed such that the total area of the top surfaces of theprojections 17 a is 1% to 2% of the overall planar area of thedielectric board 14. - The
conductor film 19 is made of, for example, a metal, metal oxide, or metal nitride as an electrical conductor having a resistivity of 10E−4 μΩ·cm or less, and the resistivity is preferably 400 μΩ·cm or less, and particularly preferably, 350 μΩ·cm or less. The electrostatic chuck according to this embodiment is formed as a bulk (plate). Therefore, it is unnecessary to use any dissimilar insulating material unlike in the separation mask ofpatent reference 2 described earlier. The material of the electrostatic chuck has a volume resistivity capable of achieving a Johnson-Rahbeck force of E+8 to E+10 Ω·cm. It is normally possible to maintain a predetermined chucking force by the Johnson-Rahbeck force and spatial Coulomb force without any conductor film on the upper surface of an electrostatic chuck (back side pressure=30 to 50 torr). The conductor film stores the same electric charge as that on the dielectric surface of the electrostatic chuck, and secures the chucking force when there is no conductor film. In addition, during substrate separation in which a substrate is unloaded from the electrostatic chuck, the residual chucking force of the substrate is eliminated by setting the substrate lower surface and conductor film at the same potential. By thus eliminating the residual chucking force of the substrate, it is possible to smoothly unload the substrate from the electrostatic chuck, that is, increase the stability of substrate separation. - Setting the resistivity of the conductor film at, for example, 350 μΩ·cm or less facilitates setting the lower surface of the substrate and the conductor film on the upper surface of the electrostatic chuck at the same potential. Consequently, it is possible to eliminate the residual chucking force of the substrate from which electric charge is removed, and smoothly unload (separate) the substrate from the electrostatic chuck.
- By contrast, if the resistivity is high, the electric charge on the substrate lower surface is trapped, and as a consequence the residual chucking force remains on the substrate. This makes separation of the substrate from the electrostatic chuck unstable.
- Examples of the material of the
conductor film 19 are metals such as titanium and tungsten, and oxides or nitrides of these metals. Materials such as titanium and tungsten are strong against thermal strain among other metals, and hardly deform because they have high wear resistances. Accordingly, these materials can suppress particles generated by, for example, contact between a substrate and the conductor film of the electrostatic chuck, or friction caused by a linear expansion difference, and increase the wear resistance. - The
conductor film 19 can be a single-layered film as shown inFIG. 2 , and can also be a multi-layered film (afirst layer 19 a andsecond layer 19 b) as shown inFIG. 3 . When depositing the multilayered film (thefirst layer 19 a andsecond layer 19 b) as shown inFIG. 3 , thefirst layer 19 a as an inside layer is preferably made of a metal such as titanium or tungsten, and thesecond layer 19 b formed on thefirst layer 19 a is preferably made of an oxide or nitride of a metal such as titanium or tungsten. By using a metal oxide or metal nitride having a high wear resistance as thesecond layer 19 b, it is possible to suppress the generation of particles when thesubstrate 9 is loaded and unloaded, and increase the wear resistance. - The
conductor film 19 can be formed by a film formation method such as sputtering or ion plating. The thickness of theconductor film 19 is preferably 1.5 μm or less in order to decrease the resistance of theconductor film 19 in the film thickness direction to about 10Ω. If the thickness of theconductor film 19 exceeds 1.5 μm, the resistance of the conductor film increases, and film pealing readily occurs owing to the film stress. A practical lower limit is about 0.5 μm. - The
conductor film 19 need only be formed on at least the top surface of theprojection 17 a except for therecesses 17 b, but can also be formed to the circumferential surface of theprojection 17 a as described previously. When theconductor film 19 is formed to the circumferential surface, the deposition state can be stabilized. Theconductor film 19 may also be formed on the top surface and side surfaces of the outerperiphery protruding portion 18. - Note that
FIG. 1 shows none of a substrate transfer robot, a loading/unloading gate, lift pins for loading and unloading thesubstrate 9 onto and from theelectrostatic chuck 8, a mechanism related to discharge, a discharge gas supply mechanism, and the like. - In the sputtering apparatus shown in
FIG. 1 , the substrate transfer robot loads thesubstrate 9 from the loading/unloading gate onto theelectrostatic chuck 8 in thevessel 1. When thevessel 1 is set in a predetermined vacuum ambient and a voltage is applied to theelectrode 15 by turning on theswitch 20, different electric charges are stored on the upper surfaces of thedielectric board 14 andconductor films 19 and the lower surface of thesubstrate 9.FIGS. 4A and 5A illustrate the states of electric charge on the upper surface of theconductor film 19 and the lower surface of thesubstrate 9 when theswitch 20 is turned on. In these states, the spatial Coulomb force acts between therecesses 17 b of the upper surface of thedielectric board 14 and the lower surface of thesubstrate 9, and the Johnson-Rahbeck force acts in a fine gap between theconductor films 19 on the top surfaces of theprojections 17 a and the lower surface of thesubstrate 9. Thesubstrate 9 is strongly chucked to the electrostatic chuck by the spatial Coulomb force and Johnson-Rahbeck force. - After the
substrate 9 is chucked to theelectrostatic chuck 8, thegas supply source 22 supplies a necessary amount of gas to the gap between theelectrostatic chuck 8 andsubstrate 9. At the same time, the temperature controlpower supply mechanism 11 operates the heating/cooling portions 13 to hold the temperature of thesubstrate 9 constant, a discharge gas is supplied into thevessel 1, and sputtering is performed by turning on the sputteringpower supply 6. - When this sputtering is complete, the sputtering
power supply 6 is turned off, and the voltage application to theelectrode 15 is stopped by turning off theswitch 20. Consequently, the lower surface of thesubstrate 9 and theconductor films 19 on the top surfaces of the plurality ofprojections 17 a are going to have the same potential through the contact points between theconductor films 19 and the lower surface of thesubstrate 9, thereby removing electric charge. Accordingly, thesubstrate 9 can be rapidly unloaded after the voltage application to theelectrode 15 is stopped.FIGS. 4B and 5B illustrate the states of electric charge on the upper surface of theconductor film 19 and the lower surface of thesubstrate 9 when theswitch 20 is turned off. - By the charge removing action described above, the
substrate 9 can be unloaded from theelectrostatic chuck 8 within a short time after theswitch 20 is turned off. The substrate transfer robot carries the unloadedsubstrate 9 outside thevessel 1 from the loading/unloading gate. - Next, a more practical embodiment of the electrostatic chuck will be explained.
- In this embodiment, 384
columnar projections 17 a having a diameter of 0.4 mm±0.15 mm and a height of 8.5 μm±2 μm and the outerperiphery protruding portion 18 having the same height as that of theprojections 17 a and a width of 1 mm±0.3 mm were formed on the upper surface of thedielectric board 14 of theelectrostatic chuck 8 in order to hold a 300-mm substrate 9 (silicon wafer). The total area of the top surfaces of theprojections 17 a was set at 1.5% of the overall planar area of thedielectric board 14. - In this embodiment, the
electrode 15 of theelectrostatic chuck 8 was not placed immediately below the outerperiphery protruding portion 18 in order to obtain an appropriate holding force. - The Ry and Ra of the top surface of each
projection 17 a were respectively adjusted to 2.5 μm or less and 0.25 μm or less. - Titanium films and titanium nitride films were sequentially formed as the
conductor films 19 near only the top surfaces of theprojections 17 a and outerperiphery protruding portion 18. The thickness of the titanium film was 1.0 μm, and that of the titanium nitride film was 0.3 μm. - Practical results of the above embodiment will be explained below with reference to a graph shown in
FIG. 6 . - The states of the supporting force (chucking force) when the
conductor films 19 are formed on the top surfaces of theprojections 17 a and outerperiphery protruding portion 18 and noconductor films 19 are formed will be explained below with reference toFIG. 6 . A graph shown inFIG. 6 indicates the relationship between the voltage applied to theelectrode 15 of theelectrostatic chuck 8 of the sputtering apparatus as shown inFIG. 1 , that is, the chucking voltage (V), and the pressure (Pa) of a gas (argon gas) sealed between theelectrostatic chuck 8 andsubstrate 9, that is, the chucking force. Thesubstrate 9 is a 300-mm silicon substrate covered with silicon nitride. -
FIG. 6 reveals that almost identical supporting forces can be obtained with and without theconductor films 19. A larger supporting force is obtained with theconductor films 19 in some measurement points. The supporting force is inversely proportional to the square of the distance between theelectrostatic chuck 8 andsubstrate 9. In this embodiment, a 1.3-μmthick conductor film 19 was formed on the top surface of theprojection 17 a having a height of 8.5 μm, and the distance was 9.8 μm. Therefore, a supporting force (obtained by the spatial Coulomb force) F of therecess 17 b of theelectrostatic chuck 8 presumably decreases from 1.59E2 (N) to 1.19E2 (N) on calculation. - This experimental result will be described below with reference to a graph shown in
FIG. 7 . -
FIG. 7 is a graph plotting the results of calculations of the chucking forces of theprojection 17 a andrecess 17 b of theelectrostatic chuck 8 based on this embodiment. The comparison of the chucking forces of theprojection 17 a andrecess 17 b demonstrates that the chucking force of theprojection 17 a abruptly increases when the distance, that is, the microscopically formed gap decreases. Note that the chucking force (F) is a value obtained from F=E(V2/L2)A/2 (E=dielectric constant of gap, V=voltage, L=gap (distance), and A=electrode area), and the unit is Newton (N). - As already explained, the upper surface roughness of the
projection 17 a has a large influence on the chucking force of theprojection 17 a. This result indicates that theconductor film 19 formed on theprojection 17 a improves the upper surface roughness and increases the chucking force of theprojection 17 a. That is, theconductor film 19 does not decrease the chucking force by its thickness, but has the effect of increasing the chucking force. - The present inventor has found from the experimental results that the chucking force remains unchanged even when the
conductor films 19 are formed on theprojections 17 a, so theelectrostatic chuck 8 of the present invention achieves the chucking force even with theprojections 17 a. Theconductor film 19 presumably increases the chucking force by improving the upper surface roughness of theprojection 17 a (i.e., shortening the practical distance between thesubstrate 9 and theconductor film 19 on the top surface of theprojection 17 a). In addition, thesubstrate 9 andconductor films 19 have many contact points. This perhaps makes it possible to move the electric charge near the contact points toward theelectrostatic chuck 8 when theexternal power supply 16 is turned off. - A graph shown in
FIG. 8 indicates the effect of improving separation, as the effect of the present invention, and explains the states of separation when theconductor film 19 is formed on the top surface of theprojection 17 a and noconductor film 19 is formed. - In this experiment, a monopolar
electrostatic chuck 8 was used, and a 300-mm silicon wafer having a lower surface covered with silicon nitride was used as thesubstrate 9. A reverse voltage was applied to theelectrostatic chuck 8 for a predetermined time immediately before theexternal power supply 16 was turned off, and the time before thesubstrate 9 was separated was measured. - When no
conductor film 19 was formed, the separation time shortened as the reverse voltage was increased to 150 V, but a separation time of about 5 sec was necessary even when a reverse voltage of 150 V or more was applied. On the other hand, when theconductor film 19 was formed, it was possible to separate thesubstrate 9 immediately after theexternal power supply 16 was turned off regardless of the condition. Also, easy separation was observed even at 20° C. to −30° C. at which the volume resistivity increases. As described earlier, this demonstrates that the residual electric charge, which had a large influence on chucking, of theprojection 17 a rapidly reduced, that is, charge removal was rapidly performed. - As described above, the electrostatic chuck of the present invention controls the residual electric charge on the embossed projection of a Johnson-Rahpeck type electrostatic chuck using a dielectric material having an appropriately low volume resistivity, and is applicable to both a monopolar chuck and bipolar chuck. The electrostatic chuck can be applied not only to a sputtering apparatus but also to a CVD apparatus for depositing a thin film on a substrate or an etching apparatus for processing a thin film. Furthermore, since the electrostatic chuck has an effect on the separation of a substrate covered with a high-k silicon nitride film, the electrostatic chuck is also applicable to a substrate, such as a glass substrate, made of a material having a high-k upper surface, as well as a silicon substrate.
- The preferred embodiments of the present invention have been explained above with reference to the accompanying drawings. However, the present invention is not limited to these embodiments and can be changed into various forms within the technical scope grasped from the description of the scope of the appended claims.
- The present invention is not limited to the above embodiment and various changes and modifications can be made without departing from the spirit and scope of the invention. Therefore, to apprise the public of the scope of the present invention, the following claims are appended.
Claims (1)
1. A sputtering apparatus including
a vessel which is configured to be evacuated by an external evacuating mechanism,
a target arranged in said vessel and connected to a sputtering power supply which applies a voltage,
a magnet fixed to a lower surface side of said target, and
an electrostatic chuck arranged in a position facing an upper surface side of said target and configured to support a substrate thereon,
wherein said electrostatic chuck comprises a dielectric board having an upper surface formed with a plurality of projections for supporting the substrate on top surfaces thereof and recesses around the projections, and an electrode formed in said dielectric board and receiving a voltage from an external power supply,
said dielectric board comprises a conductor film formed on at least the top surface of each projection, and
the top surface of each projection having said conductor film has a three-dimensional pattern whose Ry (maximum surface roughness) is not more than 2.5 m and Ra (central line average roughness) is not more than 0.25 m.