US20070025905A1 - Nanocarbon-producing device - Google Patents
Nanocarbon-producing device Download PDFInfo
- Publication number
- US20070025905A1 US20070025905A1 US10/560,593 US56059305A US2007025905A1 US 20070025905 A1 US20070025905 A1 US 20070025905A1 US 56059305 A US56059305 A US 56059305A US 2007025905 A1 US2007025905 A1 US 2007025905A1
- Authority
- US
- United States
- Prior art keywords
- nanocarbon
- producing apparatus
- laser beam
- graphite target
- graphite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
In a nanocarbon-producing device (173), a plane mirror (169) and a parabolic mirror (171) are arranged in a production chamber (107). Light, emitted from a laser light source (111), transmitted through a ZnSe window (133) is reflected at the plane mirror (169) and the parabolic mirror (171), collected at the parabolic mirror (171), and then irradiated onto the surface of a graphite rod (101).
Description
- The present invention relates to a nanocarbon producing apparatus.
- Recently technological application of nanocarbon is actively studied. The nanocarbon means a carbon substance having a nanoscale fine structure, typified by a carbon nanotube, a carbon nanohorn, and the like. Among others, the carbon nanohorn has a tubular structure in which one end of the carbon nanotube formed by a cylindrically rounded graphite sheet is formed in a circular conic shape. Usually the carbon nanohorns aggregate in a form, in which the circular conic unit is projected from a surface like a horn while the tube is located in the center by Van der Waals force acting between circular conic units. The carbon nanohorn assembly is expected to be applied to various technical fields due to specific characteristics thereof.
- It is reported that the carbon nanohorn assembly is produced by a laser vaporization method of irradiating the carbon substance (hereinafter also referred to as “graphite target”) of a raw material with a laser beam in an inert gas atmosphere (Patent Document 1). In Patent Document 1, a CO2 gas laser ° is illustrated as the laser beam.
- The CO2 gas laser has a wavelength of about 10.6 μm, and ZnSe and the like are preferably used as a material which transmits the CO2 gas laser (Patent Document 2). Therefore, in producing the carbon nanohorn assembly with the CO2 gas laser, it is considered that the laser beam can be focused on a surface of the graphite target by using the ZnSe lens.
- [Patent Document 1] Japanese Laid-open patent publication NO. 2001-64004
- [Patent Document 2] Japanese Laid-open patent publication NO. 2001-51191
- The invention studies the method of producing the carbon nanohorn assembly by providing a window made of ZnSe (also referred to as “laser beam window”) in a producing chamber. Then, it is found that a weight ratio (hereinafter referred to as “yield”) of the carbon nanohorn assembly is decreased in a recovered soot-like substance as an operating time of the laser beam window is lengthened. A lifetime of the laser beam window is relatively shorter, and sometimes the laser beam window failed. As a result, it is found that the apparatus is expensive to maintain and the lifetime of the apparatus becomes shorter. For the ZnSe lens provided outside the chamber, the lifetime is also relatively shorter.
- Therefore, the reason why the yield of the carbon nanohorn assembly is decreased and the reason why the lifetime of the laser beam window or the lens is short are studied. As a result, in irradiating the graphite target with the laser beam, the soot-like substance created from carbon vapor generated from the graphite target adheres to a surface of the laser beam window, and it is found that the adhesive soot-like substance is a possible cause of the reasons. When the soot-like substance adheres to the surface of the laser beam window or the lens, it is also clear that the laser beam window or the lens is heated by generating light absorption in the portion to which the soot-like substance adheres.
- In such cases, there is a possibility that an optical path is shifted by a thermal lens effect. The shift of the optical path may shift a radiation position of the CO2 gas laser in the surface of the graphite target or cause a change in power density of the light with which the surface is irradiated. It is speculated that this is the reason why the yield is decreased as the operating time of the apparatus is increased. Further, it is speculated that the heating of the laser beam window or the lens causes the failure and the like. Therefore, the technology in which the carbon nanohorn assembly is produced without decreasing the yield of the carbon nanohorn assembly is required. In order to lengthen the apparatus lifetime, the technology different from the conventional technology is required.
- The present invention is performed in view of the foregoing circumstances, an object of the invention is to provide a technology in which the nanocarbon is stably obtained at high yield. Another object of the invention is to provide a technology in which the lifetime of the nanocarbon producing apparatus is lengthened.
- The inventor actively has studied on a technique of obtaining the nanocarbon at high yield. As a result of that study, the inventor finds it important that the optical member is shielded from the adhesion of the soot-like substance when the graphite target surface is irradiated with the light outgoing from a light source using the optical members, and the inventor reaches the invention. Further, the inventor finds that the optical member is protected from the adhesion of the soot-like substance by not directly irradiating the graphite target surface with the light outgoing from the light source, but by irradiating the graphite target after the light is reflected to change the optical path, and the inventor reaches the invention.
- According to the invention, there is provided a nanocarbon producing apparatus characterized by including a graphite target; a chamber which accommodates the graphite target; a window unit which is provided in a part of the chamber; a light source which irradiates light onto a surface of the graphite target through the window unit; a recovery unit which recovers a nanocarbon generated from carbon vapor, the carbon vapor being vaporized from the graphite target by the light irradiation; and a shielding member which is located between the window unit and the graphite target.
- In the invention, the shielding member is provided between the window unit and the graphite target. As described above, in the case of the configuration in which the surface of the graphite target is directly irradiated with the light after the light outgoing from the light source is transmitted through the window unit, the soot-like substance obtained from the carbon vapor generated from the surface of the graphite target also flies in a direction in which the soot-like substance returns to the window unit side, so that the soot-like substance is easy to adhere to the surface of the window unit. Therefore, in the case where the optical member made of ZnSe is used, the optical member is easy to be heated.
- On the contrary, in the configuration of the invention, the window unit is configured to be shielded from the surface of the graphite target. Therefore, even if the soot-like substance generated from the surface of the graphite target flies onto the window unit side, since the window unit is shielded by the shielding member, the soot-like substance which is moved toward the window unit to adhere to the surface thereof is suppressed. Accordingly, the power density of the light with which the graphite target is irradiated can be stabilized to stably produce the nanocarbon having the desired property at high yield.
- In the invention, the shielding member is arranged such that the window unit is shrouded against the carbon vapor vaporized from the graphite target. The shielding member can be configured to keep the window unit shrouded so as not to adhere the soot-like substance obtained by the carbon vapor generated from the graphite target surface while causing the light outgoing from the light source to reach the graphite target surface.
- In the invention, the chamber accommodates the graphite target. However, the whole of the graphite target may not be accommodated. A part of the graphite target may be accommodated.
- In the invention, the window unit is the optical member which transmits the light outgoing from the light source. For example, the laser beam window or the lens and the like can be used as the window unit. The window unit is arranged while a part of the window unit is exposed to the inside of the chamber. The window unit may be arranged in an outgoing end face of the light source or the like in the form of a part of the light source, or arranged in a wall surface of the chamber, in which the graphite target is accommodated, in the form of the member independent of the light source.
- In this specification, the term “power density” means the power density of the light with which the graphite target surface is actually irradiated, namely, the power density at a radiation region of the light in the graphite target surface.
- In a nanocarbon producing apparatus of the invention, an optical member for introducing the light to the surface of the graphite target may be included between the window unit and the shielding member. Therefore, the graphite target surface can securely be irradiated with the light, which allows the nanocarbon to be stably produced. In the invention, since the shielding member is provided between the optical member and the graphite target, the soot-like substance which flies in the direction of the window unit without recovering by the recovery unit to adhere to the surface of the optical member can be suppressed. Therefore, the radiation position shift of the laser beam in the graphite target surface caused by the thermal lens effect or the fluctuation in power density of the light in the surface can be suppressed, which allows the nanocarbon having the desired property to be produced stably and continuously. Accordingly, the yield of the nanocarbon can be improved. Since the heating of the optical member is suppressed, the failure of the optical member can be suppressed to lengthen the lifetime of the optical member. The increase in maintenance cost of the apparatus due to exchange of the optical members can be suppressed. Therefore, the apparatus configuration having the excellent endurance and productivity can easily be realized.
- According to the invention, there is provided a nanocarbon producing apparatus characterized by including a graphite target; a chamber which accommodates the graphite target; a window unit which is provided in a part of the chamber; a light source which irradiates light onto a surface of the graphite target through the window unit; a recovery unit which recovers a nanocarbon generated from carbon vapor, the carbon vapor being vaporized from the graphite target by the light irradiation; and a reflecting member which reflects transmitted light transmitted through the window to introduce the transmitted light to the surface of the graphite target.
- In a nanocarbon producing apparatus of the invention, the optical member may include a reflecting member.
- Therefore, the graphite target surface can be irradiated with the light after the optical path of the light transmitted through the window unit is changed, which allows the adhesion of the soot-like substance to the window unit to be securely suppressed.
- In the invention, for example, the surface of the reflecting member can be made of metal, which preferably secures heat radiation property in the surface. Therefore, even if the soot-like substance and the like adhere to the surface, excessive rise in temperature can be suppressed. In the invention, a cooling mechanism for cooling the reflection member may further be provided. Therefore, the reflection member can be cooled more securely, which allows overheating of the reflecting member to be suppressed to improve the lifetime of the reflecting member. The nanocarbon can also stably be produced. In the invention, a cleaning mechanism for removing the soot-like substance adhering to the reflecting member may further be provided. Therefore, the nanocarbon can be produced while removing the soot-like substance at predetermined timing, which allows the yield of the nanocarbon to be further improved.
- In a nanocarbon producing apparatus of the invention, a shielding member located between the reflecting member and the graphite target may further be provided.
- Therefore, the window unit or the optical member can be protected more securely from the adhesion of the soot-like substance, which allows the decrease in yield of the nanocarbon to be suppressed. The lifetime of the optical member can also be lengthened.
- In a nanocarbon producing apparatus of the invention, the reflecting member may have a light focusing function. Therefore, the light can securely be focused at a predetermined position of the graphite target, which allows the nanocarbon to be stably produced. Since the light can be focused onto the graphite target surface without providing the focusing optical member to focus light, the nanocarbon can efficiently be produced with a simple configuration. The reflecting member having the light focusing function may be formed by a single member or the reflecting member may be formed by combination of the plural members.
- For example, the reflecting member can be a concave mirror. In a nanocarbon producing apparatus of the invention, the reflecting member may be a parabolic mirror. Therefore, the reflected light reflected from the concave mirror can securely be focused onto a focal point of the concave mirror. Therefore, the reflected light can be focused more securely on the surface of the graphite target, which allows the nanocarbon to be stably produced.
- In a nanocarbon producing apparatus of the invention, target holding unit which rotates the graphite target having a cylindrical shape around a central axis while holding the graphite target can be included. Therefore, the nanocarbon can continuously be produced, so that the yield of the nanocarbon can be improved.
- In a nanocarbon producing apparatus of the invention, the nanocarbon may be a carbon nanohorn assembly.
- Therefore, the carbon nanohorn assembly can stably be produced at high yield.
- A nanocarbon producing apparatus of the invention may further have an air intake unit which generates air flow along the light traveling direction from the light source side toward the graphite target side. Therefore, the soot-like substance which is moved from the graphite target side toward the light source side to adhere to the window unit or the optical member can be suppressed more securely, which allows the lifetime of the apparatus to be lengthened more securely. The nanocarbon can also be produced more stably.
- Thus, the configurations of the invention are described. However, an arbitrary combination of these configurations is also an effective aspect of the invention. Transformation of expression of the invention into another category is also an effective aspect of the invention.
- As described above, according to the invention, the nanocarbon can be produced at high yield by providing the shielding member between the window unit and the graphite target. Further, according to the invention, the lifetime of the nanocarbon producing apparatus can be lengthened.
- The above and other objects, features, and advantages of the invention will be apparent from the following description of preferred embodiments and appended drawings.
-
FIG. 1 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 2 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 3 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 4 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 5 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 6 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 7 is a view showing a configuration of a nanocarbon producing apparatus according to an embodiment. -
FIG. 8 is a view showing a configuration of a nanocarbon producing apparatus according to Example. -
FIG. 9 is a view showing a configuration of a nanocarbon producing apparatus according to Example. -
FIG. 10 is a view showing a configuration of a nanocarbon producing apparatus according to Example. -
FIG. 11 is a view showing a failure time of a ZnSe window in each apparatus of Example. -
FIG. 12 is a view showing a relationship between a production time and a yield of a carbon nanohorn assembly in Example. - Preferred embodiments of the invention will be described in detail below with reference to the drawings.
- The present embodiment relates to a nanocarbon producing apparatus in which a periphery of an optical path of the light with which the surface of the graphite target is irradiated is shrouded with a cover.
FIG. 1 is a sectional view showing an example of a configuration of a nanocarbon producing apparatus according to the embodiment. In this specification,FIG. 1 and other drawings used for the description of other pieces of producing apparatus are a schematic view, and the dimensions of each component do not always correspond to an actual dimension ratio. - A
nanocarbon producing apparatus 125 ofFIG. 1 includes a producingchamber 107, ananocarbon recovery chamber 119, and atransportation pipe 141 which connects the producingchamber 107 and thenanocarbon recovery chamber 119. The producing apparatus ofFIG. 1 also includes alaser beam source 111 which emits alaser beam 103, a ZnSeplanoconvex lens 131, aZnSe window 133, acover 167, and arotating device 115. Therotating device 115 holds agraphite rod 101, and therotating device 115 rotates thegraphite rod 101 about a central axis of thegraphite rod 101. Further, thenanocarbon producing apparatus 125 includes an inertgas supply unit 127, aflowmeter 129, avacuum pump 143, and apressure gage 145. - In the
nanocarbon producing apparatus 125, the outgoing light from thelaser beam source 111 is focused by the ZnSeplanoconvex lens 131, and thegraphite rod 101 in the producingchamber 107 is irradiated through theZnSe window 133 provided in a wall surface of the producingchamber 107. At this point, thelaser beam 103 passes through thecover 167 provided along the optical path. - The
graphite rod 101 is used as a solid-state carbon single substance which becomes an irradiation target with thelaser beam 103. Thegraphite rod 101 is fixed to therotating device 115, and thegraphite rod 101 can be rotated about the central axis. For example, thegraphite rod 101 can be rotated such that a point irradiated with thelaser beam 103 in the surface of thegraphite rod 101 is separated away from a radiation direction of thelaser beam 103. Specifically, inFIG. 1 , thegraphite rod 101 can be rotated clockwise about the central axis. Therefore, generation of optical feedback can be suppressed more securely. - While the new surface irradiated with the
laser beam 103 is stably provided, acarbon nanohorn assembly 117 can be securely recovered. Thegraphite rod 101 can be rotated about the central axis by fixing thegraphite rod 101 to therotating device 115. For example, thegraphite rod 101 can be configured to be movable in the direction along the central axis. - The
transportation pipe 141 is communicated with the producingchamber 107 and thenanocarbon recovery chamber 119 to connect the producingchamber 107 and thenanocarbon recovery chamber 119. The side face of thegraphite rod 101 is irradiated with thelaser beam 103 from thelaser beam source 111. At this point, thenanocarbon recovery chamber 119 is provided toward the direction, in which aplume 109 is generated, through thetransportation pipe 141. Therefore, the generatedcarbon nanohorn assembly 117 is recovered by thenanocarbon recovery chamber 119. - Because the
plume 109 is generated in the direction perpendicular to a tangent of thegraphite rod 101, that is, a normal direction at the radiation position of thelaser beam 103, when thetransportation pipe 141 is provided in this direction, carbon vapor can efficiently be introduced to thenanocarbon recovery chamber 119 to recover fine particles of thecarbon nanohorn assembly 117. For example, when a radiation angle is set at 45°, thetransportation pipe 141 can be provided in the direction of 45° relative to the normal. - In the
nanocarbon producing apparatus 125, acylindrical cover 167 with which the optical path is shrouded is provided along a passage of thelaser beam 103 from the periphery of theZnSe window 133 to the periphery of the surface of thegraphite rod 101 in the producingchamber 107. Thecover 167 is provided to the periphery of thegraphite rod 101, and an end portion of thecover 167 is opened. Thelaser beam 103 passes through thecover 167, and the surface of thegraphite rod 101 is irradiated with thelaser beam 103. - By providing the
cover 167, theZnSe window 133 can be shielded such that the soot-like substance, obtained from the carbon vapor generated by irradiating the surface of thegraphite rod 101, does not adhere to theZnSe window 133 while irradiation passage of the light to thegraphite rod 101 is secured. Since the soot-like substance adhesion to the surface of theZnSe window 133 is suppressed, absorption of thelaser beam 103 is suppressed in the surface of theZnSe window 133. Therefore, the fluctuation in power density of thelaser beam 103 with which the surface of thegraphite rod 101 is irradiated can be suppressed. Further, excessive rise in temperature of theZnSe window 133 can be suppressed. Therefore, the radiation position shift of thelaser beam 103 due to the thermal lens effect can be suppressed in the surface of thegraphite rod 101. Degradation of theZnSe window 133 due to the overheating and the associated failure or burning can be suppressed. - Therefore, the
nanocarbon producing apparatus 125 can stably produce thecarbon nanohorn assembly 117 at high yield. The apparatus configuration having the excellent endurance can easily be realized. - In the
nanocarbon producing apparatus 125, thetransportation pipe 141 is provided along the direction in which theplume 109 is generated such that theplume 109 is shrouded. Thetransportation pipe 141 is communicated with thenanocarbon recovery chamber 119 provided in the lateral direction of the producingchamber 107. When the surface of thegraphite rod 101 is irradiated with thelaser beam 103, theplume 109 is generated, and the carbon vapor is emitted from theplume 109 to become the soot-like substance. In thenanocarbon producing apparatus 125, since thetransportation pipe 141 is formed toward the direction in which theplume 109 is generated, the soot-like substance is securely introduced to thenanocarbon recovery chamber 119 through thetransportation pipe 141. Therefore, recovery efficiency of thecarbon nanohorn assembly 117 can be improved. Theplume 109 is generated in the direction perpendicular to the tangent of the radiation position of thelaser beam 103 in the surface of thegraphite rod 101. - The
nanocarbon producing apparatus 125 has the configuration in which the side face of thegraphite rod 101 is irradiated with thelaser beam 103 while thegraphite rod 101 is rotated in a circumferential direction. Thegraphite rod 101 is irradiated with thelaser beam 103 in a positional relationship, in which the direction of thelaser beam 103 does not coincide with the direction in which theplume 109 is generated. Therefore, thecarbon nanohorn assembly 117 can efficiently be recovered at the position in which the radiation path of thelaser beam 103 is intercepted. - In the
nanocarbon producing apparatus 125, the angle of theplume 109 generated in the side face of thegraphite rod 101 can previously predicted, which allows the position and angle of thetransportation pipe 141 to be precisely controlled. Therefore, thecarbon nanohorn assembly 117 can efficiently be produced and securely be recovered on the later-mentioned conditions. - Then, a method of producing the
carbon nanohorn assembly 117 with thenanocarbon producing apparatus 125 ofFIG. 1 will specifically be described. - In the
nanocarbon producing apparatus 125, high-purity graphite, for example, rod-shaped sintered carbon or compression molded carbon can be used as thegraphite rod 101. - For example, the high-power CO2 gas laser can be used as the
laser beam 103. Thegraphite rod 101 is irradiated with thelaser beam 103 in the inert gas atmosphere using rare gas such as Ar and He, for example, at a pressure not less than 103 Pa and not more than 105 Pa. It is preferable that the inert gas atmosphere is generated after the producingchamber 107 is previously evacuated, for example, at a pressure not more than 10−2 Pa. - It is preferable that an output, a spot diameter, and the radiation angle of the
laser beam 103 are adjusted such that the power density of thelaser beam 103 is substantially kept constant, for example, not less than 5 kW/cm2 and not more than 25 kW/cm2 at the side face of thegraphite rod 101. - For example, the output of the
laser beam 103 is set in range of not less than 1 kW and not more than 50 kW. For example, the pulse width of thelaser beam 103 is set not less than 0.5 sec, and preferably not less than 0.75 sec. Therefore, cumulative energy of thelaser beam 103 with which the surface of thegraphite rod 101 is irradiated can sufficiently be secured, which allows thecarbon nanohorn assembly 117 to be efficiently be produced. For example, the pulse width of thelaser beam 103 is set not more than 1.5 sec, and preferably not more than 1.25 sec. Therefore, the decrease in yield of the carbon nanohorn assembly, caused by the fluctuation in surface energy density due to the excessive heating of the surface of thegraphite rod 101, can be suppressed. It is more preferable that the pulse width of thelaser beam 103 is set in the range of not less than 0.75 sec and not more than 1 sec. Therefore, both the generation rate and the yield of thecarbon nanohorn assembly 117 can be improved. - For example, a quiescent width is set not less than 0.1 sec, and preferably not less than 0.25 sec. Therefore, the overheating of the surface of the
graphite rod 101 can be suppressed more securely. - The
laser beam 103 irradiates such that the radiation angle is kept constant. Thegraphite rod 101 is rotated about the central axis at a predetermined speed while the radiation angle of thelaser beam 103 is kept constant, which allows a circumferential direction of the side face of thegraphite rod 101 to be continuously irradiated with thelaser beam 103 at constant power density. Further, a lengthwise direction of thegraphite rod 101 can continuously be irradiated with thelaser beam 103 at constant power density by causing thegraphite rod 101 to slide in the lengthwise direction. - In this case, it is preferable that the radiation angle ranges not less than 30° and not more than 60°. The radiation angle shall means the angle formed between a perpendicular to the surface of the graphite target and the
laser beam 103 at the radiation position of thelaser beam 103. In the case of the use of thegraphite rod 101 which is of the cylindrical graphite target, the radiation angle is defined by the angle formed between a horizontal plane and a line segment connecting the radiation position and the center of a circle at cross-section to be perpendicular to the length direction ofgraphite rod 101. - The reflection of the
laser beam 103 with which the graphite rode 101 is irradiated, namely, the generation of the optical feedback can be prevented by setting the radiation angle at least 30°. The generatedplume 109 can also be prevented from directly striking the ZnSeplanoconvex lens 131 through theZnSe window 133. Therefore, it is effective that the ZnSeplanoconvex lens 131 is protected, and it is also effective that thecarbon nanohorn assembly 117 is prevented from adhering to theZnSe window 133. Accordingly, the power density of thelaser beam 103 with which thegraphite rod 101 is irradiated can be stabilized to stably produce thecarbon nanohorn assembly 117 at high yield. - The irradiation of the
graphite rod 101 with thelaser beam 103 at angles not more than 60° enables the generation of amorphous carbon to be suppressed to improve the ratio of thecarbon nanohorn assembly 117 in the product, namely, the yield of thecarbon nanohorn assembly 117. It is particularly preferable that the radiation angle is set at 45°±5°. The irradiation of thegraphite rod 101 with thelaser beam 103 at the angle of about 45° can further improve the ratio of thecarbon nanohorn assembly 117 in the product. - The
nanocarbon producing apparatus 125 has the configuration in which the side face of thegraphite rod 101 is irradiated with thelaser beam 103. Therefore, in the state in which the position of the ZnSeplanoconvex lens 131 is fixed, the radiation angle relative to the side face can be changed by adjusting a height of thegraphite rod 101. When the radiation angle of thelaser beam 103 is changed, a radiation area of thelaser beam 103 is changed in the surface of thegraphite rod 101, which allows the power density to be changed. Therefore, the adjustment can securely be performed. - Specifically, for example, in the case where the position of the ZnSe
planoconvex lens 131 is fixed, the radiation angle is set at 30°, which allows the power density to be increased. For example, the radiation angle is set at 60°, which allows the power density to be controlled low. - While the side face of the
graphite rod 101 is irradiated with thelaser beam 103, the spot diameter can be set in the range of not less than 0.5 mm and not more than 5 mm. - It is preferable that the spot of the
laser beam 103 is moved at a linear speed (circumferential speed) not less than 0.01 mm/sec and not more than 55 mm/sec. When the linear speed is big, the generation of the carbon vaporization from the surface of thegraphite rod 101 is limited to the shallow area from the surface while the length irradiated with thelaser beam 103 becomes longer at one-time pulse irradiation in the surface of thegraphite rod 101 with thelaser beam 103. On the contrary, when the linear speed is small, the vaporization is generated to the deep area from the surface of thegraphite rod 101 while the length irradiated with thelaser beam 103 becomes shorter at one-time pulse irradiation in the surface of thegraphite rod 101. - It is speculated that the generation amount of the soot-like substance per unit time, that is, the generation rate of the soot-like substance and the yield of the
carbon nanohorn assembly 117 in the generated soot-like substance depend on a movement distance of the radiation position and the depth of the carbon vaporization at one-time pulse light irradiation. When the carbon vaporization is excessively deep, substances other than thecarbon nanohorn assembly 117 are generated to decrease the yield. When the carbon vaporization is excessively shallow, thecarbon nanohorn assembly 117 is not sufficiently generated. Setting the linear speed at the above condition allows thecarbon nanohorn assembly 117 to be efficiently produced at high yield. - For example, in the case where the surface of the graphite target having the diameter of 100 mm is irradiated with the
laser beam 103, therotating device 115 rotates thegraphite rod 101 having the diameter of 100 mm in the circumferential direction at a constant speed, and for example the number of revolutions is set in the range of not less than 0.01 rpm and not more than 10 rpm, which allows the above linear speed to be realized. Although the rotating direction of thegraphite rod 101 is not particularly limited, it is preferable that thegraphite rod 101 is rotated in the direction in which the radiation position recedes from thelaser beam 103, that is, in the direction from thelaser beam 103 toward thetransportation pipe 141 as shown by an arrow inFIG. 1 . Therefore, thecarbon nanohorn assembly 117 can be recovered more securely. - The soot-like substance recovered by the
nanocarbon recovery chamber 119 mainly contains thecarbon nanohorn assembly 117. For example, the soot-like substance is recovered as the substance containingcarbon nanohorn assembly 117 not less than 90%. - In producing the nanocarbon with the
nanocarbon producing apparatus 125, the air flow may be formed along the outgoing direction of thelaser beam 103 from theZnSe window 133 to the surface of thegraphite rod 101 or along the direction from the surface of thegraphite rod 101 to thenanocarbon recovery chamber 119 through thetransportation pipe 141. For example, the air intake unit may further be provided. The air intake unit generates the air flow along the traveling direction of thelaser beam 103 from the side of thelaser beam source 111 toward the side of thegraphite rod 101. Therefore, the adhesion of the soot-like substance to the direction of theZnSe window 133 from the surface of thegraphite rod 101 can be suppressed more securely. Further, because the generatedcarbon nanohorn assembly 117 can be introduced more securely from thetransportation pipe 141 to thenanocarbon recovery chamber 119, a yield of thecarbon nanohorn assembly 117 can be improved. - The ZnSe
planoconvex lens 131 and theZnSe window 133 are used in thenanocarbon producing apparatus 125. The ZnSe planoconvex lens may be provided as theZnSe window 133. That is, in this case, the lens is used as the window for sealing the producingchamber 107 while the ZnSeplanoconvex lens 131 is not provided outside the producingchamber 107. Therefore, the simple apparatus configuration having excellent production efficiency is realized. - In the apparatus of
FIG. 1 and the pieces of apparatus described in subsequent embodiments, thelaser beam source 111 is provided above the producingchamber 107. The carbon nanohornassembly 117 generated by the irradiation with thelaser beam 103 is recovered in thenanocarbon recovery chamber 119, provided in the lateral direction of the producingchamber 107, through thetransportation pipe 141. In this embodiment and the subsequent embodiments, the arrangement of thelaser beam source 111 is not always limited to the aspect in which thelaser beam source 111 is provided above the producingchamber 107. - For example,
FIG. 2 is a view showing another configuration of the nanocarbon producing apparatus having thecover 167. In the apparatus ofFIG. 2 , thelaser beam source 111 is provided in the lateral direction of the producingchamber 107, and thelaser beam 103 is emitted from the side face of the producingchamber 107 toward thegraphite rod 101. At this point, theplume 109 is generated in the direction perpendicular to the tangent of the radiation position on thegraphite rod 101. In the positional relationship ofFIG. 2 , theplume 109 is generated toward the direction in which the angle of 450 is formed relative to the upward vertical direction in the producingchamber 107. In the apparatus ofFIG. 2 , similarly to the apparatus ofFIG. 1 , thetransportation pipe 141 is provided from the periphery of the surface of thegraphite rod 101 toward the plume generation direction, and the soot-like substance generated from theplume 109 is recovered by thenanocarbon recovery chamber 119 provided above the producingchamber 107. - In the apparatus of
FIG. 2 , therotating device 115 has a rotating mechanism which holds thegraphite rod 101 and rotates thegraphite rod 101 about the central axis. In the apparatus ofFIG. 2 , similarly to the apparatus ofFIG. 1 , thegraphite rod 101 can also be moved in the direction of the central axis. - In the apparatus of
FIG. 1 , thecover 167 with which the optical path is shrouded is provided along the optical path of thelaser beam 103 outgoing from thelaser beam source 111 as the shielding member for protecting theZnSe window 133. However, the mode of the shielding member is not limited to thecover 167. - For example,
FIG. 3 shows the apparatus having the configuration in which apartition wall 179 is provided instead of thecover 167 of thenanocarbon producing apparatus 125 ofFIG. 1 . Other configurations of the apparatus ofFIG. 3 are similar to thenanocarbon producing apparatus 125. In the apparatus ofFIG. 3 , thepartition wall 179 is provided in the producingchamber 107. Thepartition wall 179 divides the producingchamber 107 into the chamber where theZnSe window 133 is provided and the chamber where thegraphite rod 101 is provided. A hole through which thelaser beam 103 passes thegraphite rod 101 is made in thepartition wall 179. This enables thegraphite rod 101 to be irradiated with the laser beam. The movement of the soot-like substance generated from thegraphite rod 101 side to theZnSe window 133 side can be shielded by providing thepartition wall 179. Therefore, the adhesion of the soot-like substance to the surface of theZnSe window 133 can be suppressed. - In the pieces of apparatus of
FIG. 1 toFIG. 3 , theZnSe window 133 is provided as a window in the wall surface of the producingchamber 107. However, the window is not limited to the configurations of the pieces of apparatus ofFIG. 1 toFIG. 3 as long as a part of the window is exposed into the producingchamber 107. For example, thelaser beam source 111 having the window in the outgoing end face may be arranged in the producingchamber 107. In this case, the adhesion of the soot-like substance to the window of thelaser beam source 111 is suppressed by shielding between thelaser beam source 111 and thegraphite rod 101 with the shielding member such as thecover 167 or thepartition wall 179. The ZnSeplanoconvex lens 131 may be provided in the producingchamber 107. In this case, the adhesion of the soot-like substance to the surface of the ZnSeplanoconvex lens 131 can be suppressed by shielding between the ZnSeplanoconvex lens 131 and thegraphite rod 101 with, e.g., thecover 167 or thepartition wall 179. - The present embodiment relates to a nanocarbon producing apparatus having a configuration in which the surface of the
graphite rod 101 is not directly irradiated with the light outgoing from thelight source 111, but the surface of thegraphite rod 101 is irradiated after the light is reflected to change the optical path. -
FIG. 4 is a sectional view showing a state of ananocarbon producing apparatus 173 according to the embodiment when laterally viewed. In the embodiment, the same component as thenanocarbon producing apparatus 125 described in the first embodiment is designated by the same reference numeral, and the description will be neglected as appropriate. - In the configuration of the nanocarbon producing apparatus 125 (
FIG. 1 ), after thelaser beam 103 outgoing from thelaser beam source 111 is focused by the ZnSeplanoconvex lens 131 such that the spot diameter becomes a predetermined size in the surface of thegraphite rod 101, thelaser beam 103 irradiates the producingchamber 107 through theZnSe window 133. On the other hand, in thenanocarbon producing apparatus 173 ofFIG. 4 , thelaser beam 103 irradiates the producingchamber 107 through theZnSe window 133 with thelaser beam 103 outgoing from thelaser beam source 111 while thelaser beam 103 is not focused. Because thenanocarbon producing apparatus 173 has aplane mirror 169 and aparabolic mirror 171 to change the optical path of thelaser beam 103, thelaser beam 103 is reflected by theplane mirror 169 and further reflected by theparabolic mirror 171 in the producingchamber 107. The light reflected from theparabolic mirror 171 is focused onto the surface of thegraphite rod 101 placed near the focal point of theparabolic mirror 171. - Thus, in the
nanocarbon producing apparatus 173, the surface of thegraphite rod 101 is not directly irradiated with thelaser beam 103 incident into the producingchamber 107 through theZnSe window 133, but the surface of thegraphite rod 101 is irradiated after the optical path is changed by twice of reflection with theplane mirror 169 and theparabolic mirror 171. Since thelaser beam 103 passes through theplane mirror 169 and theparabolic mirror 171, the length of the optical path from theZnSe window 133 to thegraphite rod 101 can be increased in thenanocarbon producing apparatus 173 when compared with thenanocarbon producing apparatus 125. - Therefore, the
nanocarbon producing apparatus 173 has the configuration, in which the adhesion of theplume 109 generated from the surface of thegraphite rod 101 to theZnSe window 133 and the adhesion of the soot-like substance obtained from theplume 109 to theZnSe window 133 are suppressed. Accordingly, even if thenanocarbon producing apparatus 173 is used for a long period, the change in power density of thelaser beam 103 with which the surface of thegraphite rod 101 is irradiated can be suppressed. As a result, the decrease in yield of thecarbon nanohorn assembly 117 can be suppressed, and the continuous production of thecarbon nanohorn assembly 117 can stably be performed. Further, the lifetime of thenanocarbon producing apparatus 173 can be lengthened. - In the
nanocarbon producing apparatus 173, for example, Cu can be used as the material of theplane mirror 169 or theparabolic mirror 171. Since Cu has high thermal conductivity, even if the soot-like substance adheres to the surface, the heat is efficiently radiated. In theplane mirror 169 and theparabolic mirror 171, the surface is coated with, e.g., Au or Mo. The failure of theplane mirror 169 or theparabolic mirror 171 can be suppressed by using these materials. - In the
nanocarbon producing apparatus 173, after the light outgoing from thelaser beam source 111 is reflected twice, the surface of thegraphite rod 101 is irradiated with the light. However, as long as the light reaches the surface of thegraphite rod 101 after changing the optical path of the light outgoing from thelaser beam source 111, the number of reflection times is not particularly limited. Thenanocarbon producing apparatus 173 may be configured to perform the one-time reflection, or irradiate thegraphite rod 101 after the reflection of not less than three times. - In the configuration of the
nanocarbon producing apparatus 173, thelaser beam 103 is focused onto the surface of thegraphite rod 101 by reflecting thelaser beam 103 with theparabolic mirror 171. However, as long as thelaser beam 103 is configured to be able to be focused on the surface of thegraphite rod 101, the shape of the reflecting mirror is not limited to theparabolic mirror 171. For example, a concave mirror having another shape can be used. Thelaser beam 103 may be focused on the surface of thegraphite rod 101 by the combination of the plural reflecting mirrors. - The present embodiment relates to another configuration of a nanocarbon producing apparatus. In the embodiment, the same component as the nanocarbon producing apparatus 125 (
FIG. 1 ) described in the first embodiment or the nanocarbon producing apparatus 173 (FIG. 4 ) described in the second embodiment is designated by the same reference numeral, and the explanation will not be described as appropriate. -
FIG. 5 is a sectional view showing a state of ananocarbon producing apparatus 175 according to the embodiment when laterally viewed. The basic apparatus configuration of thenanocarbon producing apparatus 175 is similar to the nanocarbon producing apparatus 173 (FIG. 4 ). However, thenanocarbon producing apparatus 175 differs from thenanocarbon producing apparatus 173 in that thecover 167 for protecting the passage of thelaser beam 103 is provided. - As described in the first embodiment, the direct adhesion of the soot-like substance, generated from the
plume 109, to theZnSe window 133 can be suppressed more securely by providing thecover 167. The adhesion of the soot-like substance to the surface of theplane mirror 169 or theparabolic mirror 171 can also be prevented more securely. Therefore, the fluctuation in radiation position of thelaser beam 103 or the fluctuation in power density of thelaser beam 103 is suppressed in the surface of thegraphite rod 101, which suppresses the decrease in yield of thecarbon nanohorn assembly 117. Further, the apparatus lifetime can further be lengthened. - In the
nanocarbon producing apparatus 175 ofFIG. 5 , since thecover 167 is provided while being in contact with the wall surface of the producingchamber 107, theZnSe window 133 is provided inside the producingchamber 107. However, as long as the nanocarbon producing apparatus is configured to seal the inert gas in the producingchamber 107, the position of theZnSe window 133 is not limited to the inside of the producingchamber 107. For example, theZnSe window 133 may be provided in the wall surface of the producingchamber 107. For example,FIG. 6 is a view showing ananocarbon producing apparatus 176 in which theZnSe window 133 is provided in the wall surface of the producingchamber 107. - In the above embodiments, the case in which the graphite rod is used is described by way of example. However, in any one of the above embodiments, the shape of the graphite target is not limited to the cylindrical shape. For example, the graphite target may be formed in sheet-like or rod-shaped and the like.
- For example,
FIG. 7 is a view showing the apparatus configuration in the case where the sheet-like graphite target is used in the nanocarbon producing apparatus 175 (FIG. 5 ) described in the third embodiment. - In a
nanocarbon producing apparatus 177 ofFIG. 7 , agraphite target 139 is the solid-state carbon single substance which becomes the target irradiated with thelaser beam 103. Thegraphite target 139 is held by atarget holding unit 153 on atarget supply plate 135. Aplate holding unit 137 horizontally moves thetarget supply plate 135 in a translational manner. Therefore, when thetarget supply plate 135 is moved, thegraphite target 139 placed thereon is also moved, which allows the radiation position of thelaser beam 103 and the surface of thegraphite target 139 to be relatively moved. - For example, screw threads are formed in a bottom surface of the
target supply plate 135 and the surface of theplate holding unit 137, and thetarget supply plate 135 can be moved in the direction from the upper left toward the lower right ofFIG. 7 in a rack and pinion manner. A groove (not shown) or the like is formed in the surface of thetarget supply plate 135, a projection (not shown) is formed in the bottom portion of thetarget holding unit 153 so as to slide the groove, and the projection is set in the groove. Therefore, thegraphite target 139 held by thetarget holding unit 153 and thetarget holding unit 153 can be moved in the direction perpendicular to the sheet plane ofFIG. 7 . - This configuration enables the
graphite target 139 to be supplied to the radiation position of thelaser beam 103 outgoing from thelaser beam source 111. - When the graphite target is formed in sheet-like or rod shaped, a thickness of the graphite target is formed to an extent in which the graphite target is completely vaporized and run out when the graphite target is irradiated with the
laser beam 103 once or several times. Therefore, the yield of thecarbon nanohorn assembly 117 can further be improved. When the graphite target is irradiated with thelaser beam 103 once, the surface of thegraphite rod 101 is roughened, which causes the fluctuation of power density in irradiating thegraphite rod 101 with thelaser beam 103 again. Therefore, thecarbon nanohorn assembly 117 can stably be produced as the number of irradiation times of the surface of thegraphite rod 101 with thelaser beam 103 is decreased. - Thus, the invention is described based on the embodiments. Those skilled in the art will understand that these embodiments are illustrated by way of example only, various modifications could be made, and the modifications are also included in the scope of the invention.
- In the configurations of the pieces of apparatus according to the above embodiments, the soot-like substance obtained by irradiating the graphite target with the
laser beam 103 is recovered by thenanocarbon recovery chamber 119. However, the soot-like substance can be recovered by depositing on a proper substrate, or the soot-like substance can be recovered by the method of recovering fine particles with a dust bag. The inert gas can also be circulated in the reaction chamber to recover the soot-like substance by the flow of the inert gas. - In the above embodiments, when the
carbon nanohorn assembly 117 is produced, the conditions such as the power density, the pulse width, and the quiescent width of the laser beam on the graphite target surface and the moving speed of the graphite target can be appropriately selected according to the shape of the graphite target or the shape of the targetcarbon nanohorn assembly 117. The shape, the diameter, the length, the shape of a leading end portion of the carbon nanohorn constituting thecarbon nanohorn assembly 117, a distance between carbon molecules or the carbon nanohorns, and the like can be variously controlled by the irradiation condition of thelaser beam 103 and the like. - In the pieces of apparatus shown in the second to fourth embodiments (
FIG. 4 toFIG. 7 ), theZnSe window 133 is provided as the window in the wall surface of the producingchamber 107. However, the window is not limited to the configurations of the second to fourth embodiments as long as a part of the window is exposed into the producingchamber 107. For example, thelaser beam source 111 having the window in the outgoing end face may be arranged in the producingchamber 107. In this case, the adhesion of the soot-like substance to the window of thelaser beam source 111 is suppressed by causing the light outgoing from thelaser beam source 111 to reach the surface of thegraphite rod 101 after the light is reflected from the reflecting mirror such as theplane mirror 169 and theparabolic mirror 171. The ZnSeplanoconvex lens 131 may be provided in the producingchamber 107. In this case, the adhesion of the soot-like substance to the surface of the ZnSeplanoconvex lens 131 can be suppressed by causing the light transmitted through the ZnSeplanoconvex lens 131 to reach the surface of thegraphite rod 101 after the light is reflected from the reflecting mirror such as theplane mirror 169 and theparabolic mirror 171. - In the pieces of apparatus shown in the second to fourth embodiments (
FIG. 4 toFIG. 7 ), the cooling mechanism for cooling theparabolic mirror 171 may further be provided. Since the excessive heating is suppressed by cooling theparabolic mirror 171 even if the soot-like substance adheres to the surface of theparabolic mirror 171, the apparatus lifetime can further be lengthened. The cleaning mechanism for removing the soot-like substance adhering to the surface of theparabolic mirror 171 may be provided. Therefore, since the soot-like substance can be removed at predetermined timing even if the soot-like substance adheres to the surface of theparabolic mirror 171, the control can be performed more securely such that the power density of the light with which the surface of thegraphite rod 101 is irradiated is kept constant. Accordingly, the yield of the carbon nanohorn assembly can further be improved. Further, the apparatus lifetime can further be lengthened. In this case, theparabolic mirror 171 is described as examples of the cooling mechanism and the cleaning mechanism. In addition, these mechanisms can be provided to theplane mirror 169 if needed. - The invention will further be described based on Example. However, the invention is not limited to the following Example.
- In Example, the
carbon nanohorn assembly 117 was produced by the laser ablation method using thenanocarbon producing apparatus 126 shown inFIG. 2 and the pieces of nanocarbon producing apparatus shown inFIG. 8 ,FIG. 9 , andFIG. 10 . However, in thenanocarbon producing apparatus 173 shown inFIG. 4 and thenanocarbon producing apparatus 175 shown inFIG. 5 , the pieces of apparatus ofFIG. 8 andFIG. 9 have the configuration in which thelaser beam 103 is incident from the side face of the producingchamber 107 like thenanocarbon producing apparatus 126. The nanocarbon producing apparatus ofFIG. 10 has the configuration similar to thenanocarbon producing apparatus 126 ofFIG. 2 , and differs from thenanocarbon producing apparatus 126 in that the nanocarbon producing apparatus ofFIG. 10 does not have thecover 167. - The rod-shaped sintered carbon having the diameter of 100 mm was used as the solid-state carbon substance. The rod-shaped sintered carbon was placed in the vacuum chamber. After the chamber was evacuated up to 10−2 Pa, the Ar gas was introduced such that the atmospheric pressure became 1.01325×105 Pa. Then, the solid-state carbon substance was irradiated with the high-output CO2 laser beam at room temperature. The laser output was set at 100 W, and the power density was set at 22 kW/cm2 in the surface of the solid-state carbon substance. The pulse width was set at 1 sec, and the quiescent width was set at 250 msec. While the solid-state carbon substance was rotated at 6 rpm, the surface of the solid-state carbon substance was irradiated with the laser beam such that the radiation angle was set at 45°. The laser beam irradiation was performed until the ZnSe window failed, and the time for the ZnSe window to fail was measured in each apparatus.
- Further, in the case where the apparatus of
FIG. 10 and thenanocarbon producing apparatus 173 ofFIG. 8 were used, a relationship between a production time and the yield of thecarbon nanohorn assembly 117 was studied. -
FIG. 11 is a view showing a failure time of the ZnSe window in each apparatus. Referring toFIG. 11 , “ZnSe” is the experimental result for the apparatus ofFIG. 10 . “ZnSe+nanocarbon adhesion prevention corn”, “parabolic mirror”, and “parabolic mirror+nanocarbon adhesion prevention corn” indicate the experimental results for the nanocarbon producing apparatus shown inFIG. 2 ,FIG. 8 , andFIG. 9 respectively. - From
FIG. 11 , in the apparatus configuration in which the light beam was focused with the ZnSeplanoconvex lens 131, it was clear that an endurance time of theZnSe window 133 was increased by providing thecover 167. It was clear that the endurance time of theZnSe window 133 was remarkably increased by the configuration in which the light beam was focused with theparabolic mirror 171, and the endurance time of theZnSe window 133 was increased by further providing thecover 167. - From this result, it was confirmed that the apparatus lifetime was able to be lengthened by the configuration in which the surface of the
graphite rod 101 was irradiated with thelaser beam 103 after reflecting and focusing thelaser beam 103 with theparabolic mirror 171. -
FIG. 12 is a view showing the relationship between a production time and the yield of thecarbon nanohorn assembly 117 for the pieces of apparatus of “ZnSe” and “parabolic mirror” inFIG. 11 , namely, for the pieces of apparatus ofFIG. 10 andFIG. 8 . As can be seen fromFIG. 12 , in the apparatus ofFIG. 10 , the yield of thecarbon nanohorn assembly 117 is decreased as the production time passes. On the contrary, in the case where thenanocarbon producing apparatus 173 ofFIG. 8 is used, even if the production time is lengthened, it is found that the yield of thecarbon nanohorn assembly 117 is not decreased and the yield is kept constant. Therefore, it was clear that the carbon nanohorn assembly was able to be stably produced at high yield by reflecting thelaser beam 103 with theplane mirror 169 and theparabolic mirror 171, or by focusing thelaser beam 103 onto the surface of thegraphite rod 101 with theparabolic mirror 171.
Claims (20)
1. A nanocarbon producing apparatus comprising:
a graphite target;
a chamber which accommodates said graphite target;
a window unit which is provided in a part of said chamber;
a light source which irradiates light onto a surface of said graphite target through said window unit;
a recovery unit which recovers a nanocarbon generated from carbon vapor, said carbon vapor being vaporized from said graphite target by said light irradiation; and
a shielding member which is located between said window unit and said graphite target.
2. The nanocarbon producing apparatus as claimed in claim 1 , comprising an optical member between said window unit and said shielding member, said optical member introducing said light to said surface of said graphite target.
3. The nanocarbon producing apparatus as claimed in claim 1 , wherein said optical member includes a reflecting member.
4. A nanocarbon producing apparatus comprising:
a graphite target;
a chamber which accommodates said graphite target;
a window unit which is provided in a part of said chamber;
a light source which irradiates light onto a surface of said graphite target through said window unit;
a recovery unit which recovers a nanocarbon generated from carbon vapor, said carbon vapor being vaporized from said graphite target by said light irradiation; and
a reflecting member which reflects transmitted light transmitted through said window to introduce the transmitted light to said surface of said graphite target.
5. The nanocarbon producing apparatus as claimed in claim 4 , further comprising a shielding member located between said reflecting member and said graphite target.
6. The nanocarbon producing apparatus as claimed in claim 3 , wherein said reflecting member has a light focusing function.
7. The nanocarbon producing apparatus as claimed in claim 3 , wherein said reflecting member is a parabolic mirror.
8. The nanocarbon producing apparatus as claimed in claim 1 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.
9. The nanocarbon producing apparatus as claimed in claim 1 , wherein said nanocarbon is a carbon nanohorn assembly.
10. The nanocarbon producing apparatus as claimed in claim 2 , wherein said optical member includes a reflecting member.
11. The nanocarbon producing apparatus as claimed in claim 4 , wherein said reflecting member has a light focusing function.
12. The nanocarbon producing apparatus as claimed in claim 5 , wherein said reflecting member has a light focusing function.
13. The nanocarbon producing apparatus as claimed in claim 4 , wherein said reflecting member is a parabolic mirror.
14. The nanocarbon producing apparatus as claimed in claim 5 , wherein said reflecting member is a parabolic mirror.
15. The nanocarbon producing apparatus as claimed in claim 6 , wherein said reflecting member is a parabolic mirror.
16. The nanocarbon producing apparatus as claimed in claim 2 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.
17. The nanocarbon producing apparatus as claimed in claim 3 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.
18. The nanocarbon producing apparatus as claimed in claim 4 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.
19. The nanocarbon producing apparatus as claimed in claim 5 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.
20. The nanocarbon producing apparatus as claimed in claim 6 , comprising target holding unit which rotates said graphite target having a cylindrical shape around an central axis while holding the graphite target.