US20050206014A1 - Semiconductor device and method of manufacturing the same - Google Patents
Semiconductor device and method of manufacturing the same Download PDFInfo
- Publication number
- US20050206014A1 US20050206014A1 US11/119,439 US11943905A US2005206014A1 US 20050206014 A1 US20050206014 A1 US 20050206014A1 US 11943905 A US11943905 A US 11943905A US 2005206014 A1 US2005206014 A1 US 2005206014A1
- Authority
- US
- United States
- Prior art keywords
- conductive pattern
- conductive
- thermosetting resin
- resin layer
- isolation trench
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
As conductive patterns 11A to 11D are formed burying in a insulating resin 10 and a conductive foil 20 is formed being half-etched, thickness of the device is made thin. As an electrode for radiation 11D is provided, a semiconductor device superior in radiation is provided.
Description
- 1. Description of the Related Art
- The present invention relates to a semiconductor device and a method for manufacturing the same, particularly a semiconductor device radiating excellently heat from the semiconductor device and a method for manufacturing the same.
- 2. Description of the Related Art
- In recent years, use of IC package for portable equipment or small, hi-density mounting equipment progresses, and the conventional IC package and its concept of mounting are largely changing. These details are described in CSP technology, and mounting material and device supporting the technology—special issue of DENSHI ZAIRYO (p. 22, September 1998).
-
FIG. 9 is a structure adopting aflexible sheet 50 as an interposer board, a copper foil pattern 51 is put on the flexible sheet through adhesive, and an IC chip is fixed. There is a pad for bonding 53 formed at periphery of the IC chip as the conductive pattern 51. A pad for connectingsolder ball 54 is formed through aconductive path 51B formed in one body (integrally) with the pad for bonding 53. - At backside of the pad for connecting
solder ball 54, an opening 56 where the flexible sheet is opened, and through the opening 56, asolder ball 55 is formed. The entire body is sealed with aninsulating resin 58 using theflexible sheet 50 as a board.Symbol 57 is a bonding wire. - When a semiconductor device is used as an example of circuit devices, a conventional package-type semiconductor device sealed by ordinary transfer molding is popular. This is mounted on a printed substrate PS, as in
FIG. 10 . - In the package-type semiconductor device, the
semiconductor chip 502 is covered with aresin layer 503, and alead terminal 504 for external connection is led out through the side of theresin layer 503. - However, the package-
type semiconductor device 501 does not satisfy the requirements of down-sizing, thickness reduction and weight reduction, since thelead terminal 504 is led outside from theresin layer 503 and since the overall size of the device is large. - Accordingly, various companies have tried various structures, competing with others in order to realize down-sized, thin-walled and lightweight semiconductor devices. Recently, CSP (chip-size packages) have been developed, including wafer scale CSP of which the size is equal to the chip size and other CSP that are larger in some degree than the chip size.
-
FIG. 11 shows a CSP 506 that is larger in some degree than the chip size, in which the glass-epoxy substrate 505 serves as a supporting board. As illustrated, a transistor chip T is mounted on the glass-epoxy substrate 505, and this is described below. - On the surface of the glass-
epoxy substrate 505, afirst electrode 507, asecond electrode 508 and adie pad 509 are formed; and on the back thereof, afirst back electrode 510 and asecond back electrode 511 are formed. Via the through-hole TH, thefirst electrode 507 is electrically connected to thefirst back electrode 510 and thesecond electrode 508 to thesecond back electrode 511. The bare transistor chip T is attached to thedie pad 509. The emitter electrode of the transistor is connected to thefirst electrode 507 via abonding wire 512; and the base electrode thereof is to thesecond electrode 508 via anotherbonding wire 512. Further, aresin layer 513 is formed on the glass-epoxy substrate 505 to cover the transistor chip T. - Though is has the glass-
epoxy substrate 505, the CSP 506 is advantageous in that the extending structure from the chip T to theback electrodes - As in
FIG. 10 , the CSP 506 is mounted on a printed substrate PS. Electrodes and wires are formed on the printed substrate PS to constitute electric circuits; and the CSP 506, the package-type semiconductor device 501 or other devices such as chip resistor CR and chip capacitor CC are electrically connected and fixed to them. - The circuit thus formed on the printed substrate is fitted in various sets.
- A method for manufacturing the CSP is described below with reference to
FIG. 12 andFIG. 13 . - First, a glass-
epoxy substrate 505 as a supporting board is prepared, andCu foils FIG. 12A ). Next, theCu foils resistant resist 522, corresponding to thefirst electrode 507, thesecond electrode 508, thedie pad 509, thefirst back electrode 510 and thesecond back electrode 511, and theCu foil FIG. 12B ). - Next, using a drill or laser, holes for through-holes TH are formed in the glass-epoxy substrate, and these are plated to be through-holes TH. Via each through-hole TH, the
first electrode 507 is electrically connected to thefirst back electrode 510, and thesecond electrode 508 to the second back electrode 510 (FIG. 12C ). - Though not shown, the
first electrode 507 and thesecond electrode 508 to be bonding posts are plated with Ni, thedie pad 509 to be a die bonding post is plated with Au, and a transistor chip T is die-bonded to the diepad 509. - Finally, the emitter electrode of the transistor chip T is connected to the
first electrode 507 and the base electrode thereof to thesecond electrode 508 via abonding wire 512, and this is covered with a resin layer 513 (FIG. 12D ). - The process gives a CSP type electric device that has the supporting
board 505. In this process, a flexible sheet may be used for the supporting board. - On the other hand, a method of manufacturing semiconductor devices on a ceramic substrate is described with reference to the flowchart of
FIG. 13 . A ceramic substrate as supporting board is prepared, and through-holes are formed therein. Next, both surfaces of the substrate are printed with a conductive paste to form face and back electrodes thereon, and these are sintered. After this, the process of this method is the same as that ofFIG. 12 , until the thus-constructed structure is covered with a resin layer. However, the ceramic substrate used herein is extremely brittle and is readily cracked, different from flexible sheets and glass-epoxy substrates, and is therefore problematic in that it is not applicable to resin mold sealing. Accordingly, in this process, the substrate with necessary elements mounted thereon is potted with a sealing resin, cured and flattened by polishing it, and finally this is diced into individual chips with a dicing machine. - However in case of adopting a
flexible sheet 50 as an interposer board, the flexible sheet formed on a rear surface of IC chip is very expensive, and there are problems that cost rises, thickness of the package becomes thick, and weight increases. - There is a problem that heat resistance from a back face of the IC chip to a back face of the package becomes large in a supporting board because the supporting board comprises material other than metal. For said supporting board, there is a flexible sheet, a ceramic board, or a printed board. A heat conduction path comprising material superior in heat conduction is the
bonding wire 57, the copper foil 51, and thesolder ball 55, the above supporting board has a structure not to radiate fully at driving. Therefore there is a problem that driving current does not flow fully because of temperature rise of IC chip at driving. - In
FIG. 11 , the transistor chip T, the connecting means 507 to 512 and theresin layer 513 are all indispensable constitutive elements for electric connection to external units and for transistor protection. Heretofore, It has heretofore been difficult to provide a down-sized, thin-walled and lightweight circuit device that comprises these constitutive elements. - As so mentioned hereinabove, the glass-
epoxy substrate 505 used as supporting board is naturally unnecessary. However, for bonding the electrodes thereto in the process of manufacturing semiconductor devices, the supporting board is used, and the glass-epoxy substrate 505 is indispensable in the manufacturing process. - For these reasons, the glass-
epoxy substrate 505 is indispensably used and it increases the production costs. In addition, since the glass-epoxy substrate 505 is thick, the circuit device comprising it is inevitably thick and is limited in point of down-sizing, thickness reduction and weight reduction. - Further, the glass-epoxy substrate and the ceramic substrate indispensably require a step of forming through-holes through which the electrodes formed on the two surfaces thereof are connected to each other, and therefore manufacturing time is long and industrial-scale mass production is very difficult.
- The invention is carried out in view of the above problems, and intends to obtain a reliable semiconductor device having a small package and a good radiation characteristics.
- The problems are solved having a pad provided facing to a bonding electrode of a semiconductor chip, an electrode for radiation provided at an arranged area of said semiconductor chip, a insulating adhesion means provided on said electrode for radiation, said semiconductor chip fixed to said insulating adhesion means and electrically connected to said pad, and a insulating resin sealing (molding) said semiconductor chip so as to expose a back face of said pad and said insulating adhesion means and to make in one body.
- The problem is solved by that said insulating adhesion means comprises an adhesion sheet or adhesive.
- The problem is solved by that said semiconductor element is mounted in face-up type and that said pad and said bonding electrode are connected with fine metal wires (bonding wires).
- The problem is solved by providing: plural bonding pads provided so as to surround one area; external connection electrodes extended in one body with said bonding pads; an electrode for radiation provided at said one area; a insulating adhesion means provided at said electrode for radiation; a semiconductor chip fixed through said insulating adhesion means; bonding wires connecting said bonding electrodes and said bonding pads on said semiconductor chip; and a insulating resin covering said semiconductor chip, said bonding pads, said electrode for radiation, said external connection electrodes, and said bonding wires and exposing back faces of said external connection electrodes, back faces of said electrodes for radiation, and back faces of said insulating adhesion means.
- The problem is solved by providing: plural pads provided so as to surround one area; an electrode for radiation provided at said one area; a insulating adhesion means provided at said electrode for radiation; a semiconductor chip fixed through said insulating adhesion means; connecting means connecting said bonding electrodes and said pads on said semiconductor chip; and a insulating resin covering said semiconductor chip, said bonding pads, and said connection means, and exposing back faces of said bonding pads and said insulating adhesion means; wherein the back face of said bonding pads are used as the external connection electrode.
- The problem is solved by that said connection means comprises a bonding wire or brazing material.
- The problem is solved by that a side face of said pad, bonding pad, or external connection electrode comprises a curved structure.
- The problem is solved by preparing a conductive foil and half-etching so that a conductive pattern is formed in projection shape;
-
- providing an insulating adhesion means so as to fill in an isolation trench formed by said half-etching;
- fixing a semiconductor chip through said insulating adhesion means so as to connect said conductive pattern electrically and;
- providing a insulating resin at said conductive foil so as to seal said semiconductor chip and said conductive pattern; and
- removing a back face of said conductive foil so as to exposing a back face of said insulating adhesion means and to separate as said conductive pattern.
- The problem is solved by preparing a conductive foil and half-etching so that a conductive pattern comprising at least a pad and an electrode for radiation is formed in projection shape;
-
- forming an insulating adhesion means so as to cover said electrode for radiation and fill in an isolation trench adjacent to the electrode;
- fixing a semiconductor chip through said insulating adhesion means so as to connect said conductive pattern electrically and;
- providing a insulating resin at said conductive foil so as to seal said semiconductor chip and said conductive pad; and
- removing a back face of said conductive foil so as to exposing a back face of said insulating adhesion means and to separate said conductive pattern.
- By providing the semiconductor device, it is possible to transfer heat of a semiconductor chip to an electrode for radiation. As a conductive pattern including the electrode for radiation is formed without using a supporting board, it is possible to decrease cost and to make thickness of the semiconductor device thin.
- The invention is carried out in view of the above problems, and characterized by comprising multiple conductive patterns for element mounting thereon that is electrically separated from each other by a isolation trench, a thermosetting resin layer that fills the isolation trench to cover the surface of the conductive pattern, a circuit element fixed above the thermosetting resin layer, and an insulating resin that covers the circuit element to integrally support the conductive pattern bonded to the thermosetting resin layer.
- In the invention, the conductive foil to be a conductive pattern functions by itself as a supporting board, and the conductive foil supports the entire structure while the isolation trench is formed and while the circuit elements are mounted and covered with an insulating resin. When the conductive foil is separated into individual conductive patterns, the insulating resin functions as the supporting board. Accordingly, the minimum constitutive components—circuit element, conductive foil and insulating resin may be enough for the invention. This means that the invention does not require the supporting board that is indispensable in the related art technology of manufacturing circuit devices, and it reduces the production costs. In the invention, in addition, the supporting board is unnecessary, the conductive pattern is embedded in the insulating resin, and the thickness of the insulating resin and the conductive foil may be varied in any desired manner. Thus characterized by these advantages, still another advantage of the invention is that it produces extremely thin-walled circuit devices.
- The manufacturing method of the invention is characterized by comprising a step of preparing conductive foil, and a step of forming a isolation trench that does not exceed the thickness of the conductive foil in a region thereof at least except the region to be a conductive pattern thereby to form the conductive pattern, and a step of coating at least a part of the surface of the conductive pattern with a thermosetting resin layer to fill the isolation trench, and a step of selectively removing the thermosetting resin layer in the site to which the electrodes of a circuit element mounted on the conductive pattern are bonded, and a step of fixing a circuit element above the conductive pattern and a step of forming a connecting means for electrically connecting the electrodes of the circuit element to the desired site of the conductive pattern, and a step of molding it with an insulating resin that covers the circuit element and bonds to the thermosetting resin layer.
- In the manufacturing method of the invention, since the conductive pattern is coated with a semi-cured thermosetting resin layer immediately after its formation, the isolation trench can be completely filled with a liquid thermosetting resin of low viscosity, and the adhesion strength of the two is significantly increased. In addition, since the thermosetting resin layer covers the conductive pattern immediately after the conductive pattern has been formed, the surface of the conductive pattern is not oxidized in the subsequent heating step for die bonding or wire bonding, and the reliability of the devices fabricated is high.
-
FIG. 1 shows a semiconductor device of the invention. -
FIG. 2 is a view for showing a method for manufacturing the semiconductor device of the invention. -
FIG. 3 is a view for showing a method for manufacturing the semiconductor device of the invention. -
FIG. 4 is a view for showing a method for manufacturing the semiconductor device of the invention. -
FIG. 5 is a view for showing a method for manufacturing the semiconductor device of the invention. -
FIG. 6 is a view for showing a method for manufacturing the semiconductor device of the invention. -
FIG. 7 shows a conductive pattern to be employed in the semiconductor device of the invention. -
FIG. 8 shows a semiconductor device of the invention. -
FIG. 9 shows a conventional semiconductor device. -
FIG. 10 shows a package structure of a conventional circuit device. -
FIG. 11 shows a conventional circuit device. -
FIG. 12 shows a method for manufacturing the conventional circuit device. -
FIG. 13 shows flowcharts of conventional methods of manufacturing circuit devices. -
FIG. 14 shows a circuit device of the invention. -
FIG. 15 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 16 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 17 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 18 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 19 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 20 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 21 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 22 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 23 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 24 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 25 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 26 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 27 shows a circuit device of the invention. -
FIG. 28 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 29 shows a circuit device of the invention. -
FIG. 30 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 31 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 32 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 33 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 34 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 35 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 36 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 37 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 38 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 39 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 40 shows a circuit device of the invention. -
FIG. 41 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 42 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 43 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 44 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 45 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 46 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 47 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 48 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 49 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 50 is a view for showing a method for manufacturing the circuit device of the invention. -
FIG. 51 shows an embodied circuit device of the invention. - First, a semiconductor device of the invention is described referring to
FIG. 1 .FIG. 1A is a plan view of the semiconductor device, andFIG. 1B is a section view cut with A-A line. -
FIG. 1 shows a insulatingresin 10 buried with the following chips. They arepads 11A,conductive paths 11B in one-body with thepads 11A,external connection electrodes 11C provided at the other ends of theconductive paths 11B in one body with theconductive paths 11B. Further an electrode for radiating 11D provided at one area surrounded by theconductive patterns semiconductor chip 12 provided on the electrode for radiating 11D are buried. Thesemiconductor chip 12 is fixed to the electrode for radiating 11D through a insulating adhesion means AD, and is shown with dotted line inFIG. 1A . - A
bonding electrode 13 of thesemiconductor chip 12 and thepad 11A are electrically connected through abonding wire 14. - Side face of said
conductive pattern 11A to 11D is etched with non-anisotropy, and has a curved structure because of being formed with wet etching so as to generate anchor effect by the curved structure. - The structure consists of four materials: the
semiconductor chip 12, pluralconductive patterns 11A to 11C, the electrode forradiation 11D, the insulating adhesion means AD, and the insulatingresin 10 burying them. In arranged area of thesemiconductor chip 12, said insulating adhesion means AD is formed on and between theconductive patterns 11A to 11D, particularly is provided in theisolation trench 15 formed by etching so as to expose the back face. The insulatingresin 10 seals all including these materials.Said pads 11A andsemiconductor chip 12 are supported by the insulatingresin 10. - For the insulating adhesion means, adhesive comprising insulating material and insulating sheet of adhesiveness are desirable. As clear in the description below, material is desirable to bond entire wafer and to pattern by photolithography. For the insulating resin, thermosetting resin such as epoxy resin and thermoplastic resin such as polyimide resin and polyphenylenesulfide are used. All kinds of resin are used if they are resins hardening using a die and covering by dipping and painting. For the
conductive patterns 11A to 11D, conductive foil of Cu as main material, conductive foil of Al as main material, Fe—Ni alloy, laminated product of Cu—Al, or laminated product of Al—Cu—Al is used. Of course, even other material is possible to use, particularly conductive material easy to etch and easy to evaporate by laser is desirable. Considering half-etching ability, forming ability of plating, and thermal stress, conductive material of Cu as main material formed by rolling is desirable. - The invention has a characteristic to prevent remove of the conductive pattern because the insulating
resin 10 and the insulating adhesion means AD are filled into even saidisolation trench 15. By carrying out non-anisotropic etching using dry etching or wet etching for etching, the side faces ofpads 11A are made into curved structure so as to generate anchor effect. As the result, the structure that theconductive patterns 11A to 11D do not come out (remove) from the insulating resin 10 (package) is realized. - Further the back faces of the
conductive patterns 11A to 11D expose at the back face of the package. Accordingly the back face of theelectrode 11D for radiation is fixed with the electrode on the mounting board. The structure can radiate heat generating from thesemiconductor chip 12 on the electrode of the mounting board, can prevent temperature rise of thesemiconductor chip 12, and can increase driving current of thesemiconductor chip 12. The electrode forradiation 11C and thesemiconductor chip 12 may be connected electrically. - Because the
conductive patterns 11A to 11D are supported by insulatingresin 10 in the semiconductor device, a supporting board is not need. This construction is a characteristic of the invention. As described at the prior art, the conductive path of the conventional semiconductor device is supported by a supporting board (flexible sheet, printed board, or ceramic board), or supported by a lead frame, the construction which is not need originally is added. However the circuit device consists of necessary minimum components and does not need the supporting board so that the device has a characteristic to be thin, light, and inexpensive because of low material cost. - At the back face of the package, the
conductive patterns 11A to 11D expose. By covering brazing material such as solder for example, at the area, the brazing material can get wet thickly because area of the electrode forradiation 11D is broad. Therefore brazing material of the back face of theexternal connection electrode 11C is not wet at the electrode of the mounting board at fixing on the mounting board, so it is assumed to become bad connection. - To solve that, a insulating
film 16 is formed at the back face of thesemiconductor device 15. Circles of dotted line shownFIG. 1A show theexternal connection electrodes 11C and electrodes forradiation 11D exposing from the insulatingfilm 16. That is, as the insulatingfilm 16 covers portions except the circles and size of circle portions is substantially same size, thickness of brazing material formed here is substantially same. This is similar as after solder printing and after reflow. This is similar about conductive paste such as Ag, Au, Ag—Au, Ag—Pd and soon. By the structure, bad quality of the electrical connection means 23 are depressed. An exposingportion 17 of the electrode forradiation 11D may be formed larger than exposing size of theexternal connection electrode 11C considering radiation of the semiconductor chip. As all of theexternal connection electrodes 11C are substantially same size, all area of theexternal connection electrodes 11C maybe exposed at entire area, and a part of the back face of the electrode forradiation 11D may be exposed from the insulatingfilm 16 with substantially same size. - By providing the insulating
film 16, it is possible to extend the conductive path provided at the mounting board to the back face of the semiconductor device. Although the conductive path provided at the mounting board side is generally arranged going around the fixed area of said semiconductor device, forming said insulatingfilm 16 can arrange without going around. Further as the insulatingresin 10 and the insulating adhesion means AD project from the conductive pattern, a gap is formed between the conductive path of the mounting board side and the conductive pattern so as to prevent short. - The method for manufacturing shows the method for manufacturing of the
semiconductor chip 15 shown inFIG. 1 , andFIG. 2 toFIG. 6 are section views corresponding to A-A line ofFIG. 1A . - First, a
conductive foil 20 is provided asFIG. 2 . Thickness thereof is desirably 10 μm to 300 μm, here rolled copper foil of 70 μm is used. Next on the front face of theconductive foil 20, aconductive film 21 or a photo resist is formed as etching-resist. - The pattern is same pattern as the
pads 11A inFIG. 11A , theconductive paths 11B, theexternal connection electrode 11C, and the electrodes forradiation 11D. In the case of using the photo resist instead of theconductive film 21, a conductive film such as Au, Ag, Pd or Ni is formed at a part corresponding to at least pad in the lower layer of the photo resist. This is provided to make bonding possible. (ReferFIG. 2 about the above.) - Next, a
conductive foil 20 is half-etched through saidconductive film 21 or photo resist. Depth of etching may be thinner than thickness ofconductive foil 20. The thinner the depth of etching, forming the finer pattern is possible. - By half-etching,
conductive patterns 11A to 11D appear at surface of theconductive foil 20 in projection shape. As above-mentioned, here Cu foil formed by roll and made of Cu as main material is used for theconductive foil 20. For the conductive foil, conductive foil made of AL, conductive foil made of Fe—Ni alloy, layered product of Cu-AL, or layered product of Al—Cu—Al may be used. Especially the layered product of Al—Cu—Al prevents bend appearing by difference of coefficient of thermal expansion. - At part corresponding to dotted line of
FIG. 1 , a insulating adhesion means AD is formed. The insulating adhesion means AD is provided at anisolation trench 15 between the electrode ofradiation 11D and theexternal connection electrode 11C, at anisolation trench 15 between the electrode ofradiation 11D and theconductive path 11B, and on them. (ReferFIG. 3 about the above.) - Next, a
semiconductor chip 12 is fixed at one area providing the insulating adhesion means AD, abonding electrode 13 of thesemiconductor chip 12 and thebonding pad 11A are electrically connected. In the figure, as thesemiconductor chip 12 is mounted in face up type, abonding wire 14 is used for the connection means. - In the bonding, the
bonding pads 11A are in one body with theconductive foil 20, and further a back face of theconductive foil 20 contacts face of table of a bonding machine because the back face is flat. Therefore if theconductive foil 20 is entirely fixed to the bonding table, there is not position shift of thebonding pads 11A, and bonding energy is transferred efficiently to thebonding wire 14 and thebonding pads 11A. Therefore thebonding wire 14 is connected improving fixing strength thereof. Fixing the bonding table is possible by providing plural vacuum suction holes at entire face of the table for example. Theconductive foil 21 may be pushed from upper side. - The semiconductor chip is mounted without using the supporting board, and height of the
semiconductor chip 12 is arranged low as thickness as the supporting board. Therefore it is possible that thickness of the package is made thin. (Refer toFIG. 4 about the above.) - An insulating
resin 10 is formed so as to cover theconductive patterns 11A to 11D formed by half-etched, thesemiconductor chip 12, and thebonding wire 14. For the insulating resin, both of thermoplasticity and thermosetting property may be used. - Transfer molding, injection molding, dipping, or painting realizes the resin. For the resin material, thermosetting resin such as epoxy resin is realized by transfer molding and thermoplastic resin such as liquid polymer and polyphenylenesulfide is realized by injection molding.
- In the mode for carrying out, thickness of the insulating resin is adjusted so as to cover 100 μm upper from an upper limit face of the
bonding wire 14. The thickness may be made thick or thin considering strength of the semiconductor device. - In the injection of resin, as the
conductive patterns 11A to 11D are in one body with the sheet-shapeconductive foil 20, position of theconductive patterns 11A to 11D does not shift at all as long as theconductive foil 20 does not shift. - As above-mentioned, in the insulating
resin 10, theconductive patterns 11A to 11D formed as projection and thesemiconductor chip 12 are buried, and theconductive foil 20 of lower part than the projection exposes at the back face. (ReferFIG. 5 about the above.) - Next, the
conductive foil 20 exposing at the back face of the insulatingresin 10 is removed and theconductive patterns 11A to 11D are individually separated. - Various methods are considered for the separating process, that is, the back face may be separated removing by etching or grinding by polishing or grinding. Both of them may be used. There is a problem that shavings of the
conductive foil 20 and bur-shape rolled metal extended thin to outside cut into the insulatingresin 10 and the insulating adhesion means AD at grinding till the insulatingresin 10 exposes for example. Therefore separating the conductive pattern by etching, the device is formed without that metal of theconductive foil 20 cuts into the insulatingresin 10 existing between theconductive pattern 11A to 11D and the insulating adhesion means AD. Thus short between theconductive pattern 11A to 11D of fine interval is prevented. (ReferFIG. 5 about the above.) - In the case that plural units becoming the
semiconductor device 15 are formed, dicing process is added after the separating process. - Although the units are separated individually using the dicing machine here, it is possible by chocolate breaking, pressing, and cutting.
- Here the insulating
film 16 is formed on theconductive patterns 11A to 11D exposing at the back face separated and is patterned so as to exposes the parts shown in circle of dotted line ofFIG. 1A , and after that, is diced along an arrow shown inFIG. 6 to be each of the semiconductor devices. - The
solder 21 may be formed before or after dicing. - The above method for manufacturing realizes a light, thin, short, small package where a semiconductor chip buried in insulating material.
- The insulating adhesion means AD shown in
FIG. 3 andFIG. 4 may be bonded at the stage of wafer before thesemiconductor 12 is individually separated. That is, if sheet-shaped adhesive is formed on the back face of wafer at the stage wafer and the wafer is cut with the sheet at dicing, the process forming the insulating adhesion means AD on theconductive foil 20, shown inFIG. 3 , is not need. -
FIG. 7 shows a conductive pattern formed on theconductive foil 20. Here four units are formed vertically, and horizontally eight units are formed so as to have a shape like lead frame. -
Symbols Symbols symbols - Next, effect generating by the above method for manufacturing is described.
- First, as the conductive pattern is half-etched and supported in one body of the conductive foil, a board used for supporting past is removed.
- Second, as the pad half-etched to make projection is formed on the conductive foil, it is possible to make the pad fine. Therefore it is possible to make width and gap of the pad narrow so as to form a small package in plan size.
- Third, as the device consists of necessary minimum components: the conductive pattern, the semiconductor chip, the connection means, and sealing material, useless material is removed so as to realize thin semiconductor device extremely depressing cost.
- Fourth, as the pads are formed becoming projection by half-etching and individually separated after sealing, tie bar and hanging lead are not need. Therefore forming and cutting tie bar (hanging lead) is not need at all in the invention.
- Fifth, as the conductive foil is removed from the back face of the insulating resin after the conductive pattern becoming the projection is buried in the insulating resin and is separated, bur of resin generating between leads as the conventional lead framed is removed.
- Sixth, as the semiconductor is fixed to the electrode for radiation through the insulating adhesive means and the electrode for radiation exposes from the back face thereof, heat generating from the semiconductor device is efficiently radiated from the back face thereof. By mixing the under-fill material with filler such as Si oxide film and aluminum oxide, radiation of the device is more improved. By unifying the filler size, it is possible that gap between the
semiconductor chip 12 and the conductive pattern is kept uniform. -
FIG. 8 shows thesemiconductor device 42.FIG. 8A is a plan view of the device, andFIG. 8B is a section view cut by A-A line. - Although the
pad 11A is formed in one body with theconductive path 11B and theexternal connection electrode 11C inFIG. 1 , here the back face of thepad 11A becomes the external connection electrode. - As the back face of the
pad 11A is formed in rectangle, the pattern exposing from the insulatingfilm 16 is formed in same pattern as said rectangle. Thetrenches 43 are formed so that theelectrode 11D for radiation andchip 12 can be adhered appropriately by filling the insulating adhesion means into said trenches. Thereby theelectrode 11D for radiation is divided to plural. - As clear from the above description, in the invention, even the conductive foil (or conductive foil) where the conductive pattern formed in island shape has thickness is buried in the insulating adhesion means and the insulating resin. As the electrode for radiation positioning at the back face of the semiconductor chip, it is possible to improve radiation of the semiconductor chip. Further as the supporting board is not used, it is possible to realize a thin and light package.
- The device consists of necessary minimum components of the conductive pattern, the semiconductor chip, and the insulating resin, and becomes a circuit device useless for resources. Therefore extra components do not exist till completion, and a semiconductor device decreasing cost thereof extremely.
- The fourth embodiment of the circuit device of the invention is described with reference to
FIG. 14 . - The circuit device of the invention comprises multiple conductive patterns for element mounting thereon that is electrically separated from each other by a isolation trench, a thermosetting resin layer that fills the isolation trench to cover the surface of the conductive pattern, a circuit element fixed on the thermosetting resin layer, and an insulating resin that covers the circuit element to integrally support the conductive pattern bonded to the thermosetting resin layer.
-
FIG. 14 shows acircuit device 153 having aconductive pattern 151 embedded in athermosetting resin layer 150A, in which acircuit element 152 is fixed on theconductive pattern 151 and theconductive pattern 151 are supported by an insulatingresin 150B bonded to thethermosetting resin layer 150A. - This structure comprises four elements, the
circuit element 152, the multipleconductive patterns 151, thethermosetting resin layer 150A to envelop theconductive pattern 151, and the insulatingresin 150B that bonds to theresin layer 150A. In this, theconductive patterns 151 are separated by aisolation trench 161 filled with thethermosetting resin layer 150A. Theconductive pattern 151 is supported by thethermosetting resin layer 150A and the insulatingresin 150B. - For the
thermosetting resin layer 150A that characterizes the invention, a thermosetting resin such as epoxy resin is used. The resin fills theisolation trench 161 and covers the surface of theconductive pattern 151. To form thethermosetting resin layer 150A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 161 and theconductive pattern 151, semi-cured to evaporate away the organic solvent, and then finally cured. Preferably, a filler such as silica or alumina is added to thethermosetting resin layer 150A to reduce the thermal expansion difference between thelayer 150A and theconductive pattern 151. In general, the thermal expansion coefficient of epoxy resin is 50 ppm/° C.; that of epoxy resin containing the filler is from 15 to 30 ppm/° C.; and that of copper to form theconductive pattern 151 is 18 ppm/° C. Therefore, the filler may remove the thermal expansion mismatch between epoxy resin and copper. - Since the
thermosetting resin layer 150A is filled into theisolation trench 161 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 161, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. - Another method may be employed for forming the
thermosetting resin layer 150A, which comprises pressing a semi-sheet-like film of thermosetting resin such as epoxy resin against theconductive pattern 151 followed by finally curing it thereon under heat to thereby cover theconductive pattern 151 and fill theisolation trench 161 with the resin. - For the insulating
resin 150B, any of thermosetting resin such as epoxy resin, or thermoplastic resin such as polyphenylene sulfide can be used. Not limited to these, the insulating resin may be any and every resin that may be solidified in molds, or may be applied to semiconductor by dipping or coating. However, in consideration of its bonding strength to thethermosetting resin layer 150A, resin of the same type is preferred for the two. Therefore, in this, thermosetting resin such as epoxy resin is used for the insulatingresin 150B. - For the
conductive pattern 151, for example, any of conductive foil consisting essentially of Cu, conductive foil consisting essentially of Al, or conductive foil consisting essentially of Fe—Ni alloy or the like can be used. Needless to say, any other conductive material may also be used. Especially etchable conductive materials and conductive materials evaporable by laser are preferred. - For connecting the
circuit element 152 to any other element, abonding wire 155 is used in a face-up structure, or a conductive ball of solder, a flattenable conductive ball or other solder material is used in a face-down structure. The connecting means is selected depending on the type of thecircuit element 152 and the mounting method thereof. - The
conductive pattern 151 to which is fitted thebonding wire 155 or solder is selectively exposed out of thethermosetting resin layer 150A, and the exposed surface of theconductive pattern 151 is covered with aconductive film 154. For theconductive film 154, usable is any of Ag, Au, Pt or Pd. Theback electrode 156 is formed on theconductive pattern 151 through low-vacuum or high-vacuum coating, plating or sintering that includes vapor deposition, sputtering, CVD and the like. Theback electrode 156 is formed by selectively exposing out a predetermined region of theconductive pattern 151 with masking the other region thereof with a resistlayer 157, followed by applying a conductive material such as solder to the exposed region, and the back electrodes are protruding electrodes. - In this circuit device, the
conductive pattern 151 is supported by thethermosetting resin layer 150A and the insulatingresin 150B, and therefore does not require a supporting board for it. This constitution characterizes the invention. As so described hereinabove with reference to the related art, the conductive paths in conventional circuit devices are supported by a supporting board or by a lead frame, and they require superfluous structures that are naturally unnecessary. However, the circuit device of the invention is composed of the least necessary constitutive elements, not requiring a supporting board, and it may be thinned and low-priced. - Another advantage of the circuit device of the invention is that the
thermosetting resin layer 150A therein covers thecircuit element 152 and fills theisolation trench 161 between theconductive patterns 151 for individual insulation. - In the circuit device, the
thermosetting resin layer 150A and the insulatingresin 150B integrally support the structure in such a manner that the insulatingresin 150B covers thecircuit element 152 and thethermosetting resin layer 150A fills theisolation trench 161 between theconductive pattern 151 with the back thereof only exposed outside. - The
circuit element 152 is fixed onto thethermosetting resin layer 150A that covers theconductive pattern 151, via an insulatingadhesive 158, and thecircuit element 152 is therefore electrically insulated from theconductive pattern 151. As a result, theconductive pattern 151 to be formed below thecircuit element 152 may be a fine pattern of any form, and the latitude in wiring with the pattern significantly increases. Each electrode pad of thecircuit element 152 is connected to theconductive film 154 that is formed on a part of theconductive pattern 151 around it and serves as a bonding pad, via thebonding wire 155. Accordingly, theback electrode 156 may be formed on theconductive pattern 151 below thecircuit element 152, and this realizes an equivalently two-layered wiring structure. - Exposing the back of the conductive path characterizes the invention. The back of the conductive path may be connected to external elements, therefore not requiring through-holes TH as in the conventional structure in
FIG. 12 . - Moreover, since the
circuit element 152 is disposed on the thinthermosetting resin layer 150A and fixed thereto via the insulatingadhesive 158, the heat generated by thecircuit element 152 may be transferred to the substrate via thethermosetting resin layer 150A and via theconductive pattern 151. In particular, the structure is effective for semiconductor chips that require heat radiation when the driving current increases. - In this circuit device, the surface of the
isolation trench 161 is substantially on the same level as the surface of theconductive pattern 151. This structure characterizes the invention. This does not have a difference in level for theback electrodes FIG. 12 . Therefore, thecircuit device 153 is characterized in that it accepts horizontal movement. - In another embodiment, a UV-curable resin may be used in place of the
thermosetting resin layer 150A. Concretely, a UV-curable resin is applied onto the structure, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin film that covers the desired surface of theisolation trench 161 and theconductive pattern 151. UV-curable resin is a type of epoxy resin, and is therefore effective like thethermosetting resin layer 150A. - One embodiment of manufacturing the circuit device of the invention is described with reference to
FIG. 15 . - The method of the invention comprises a step of preparing conductive foil and forming a isolation trench that does not exceed the thickness of the conductive foil in a region of the conductive foil at least except the region to be a conductive pattern that has a number of parts to carry circuit elements mounted thereon, thereby to form the conductive pattern in multiple blocks; a step of coating the isolation trench and the conductive pattern with a thermosetting resin; a step of exposing a predetermined surface of the conductive pattern through laser etching; a step of forming a conductive film selectively on the exposed conductive pattern; a step of fixing circuit elements on the thermosetting resin layer; a step of forming a connecting means for electrically connecting the electrode of each circuit element to a desired part of the conductive pattern; a step of common-molding it with an insulating resin to collectively cover the circuit element on every element-mounting part and to fill the isolation trench; a step of removing the conductive foil in the thickness part with no isolation trench formed therein; a step of sticking the multiple blocks to an adhesive sheet via the insulating resin of each block; a step of measuring the characteristics of the circuit element on each element-mounting part of each block attached to the adhesive sheet; and a step of dicing the insulating resin into the individual element-mounting parts of each block attached to the adhesive sheet.
- The flowchart of
FIG. 15 does not correspond to the method as above. In this, the two flows of Cu foil and half-etching are to form a conductive pattern. In the next flow of thermosetting resin, the surface of the isolation trench and the conductive pattern is covered with a thermosetting resin. In the two flows of die bonding and wire bonding, a circuit element is fixed onto each element-mounting part, and its electrodes are connected to the conductive pattern. In the flow of transfer molding, an insulating resin is applied to the structure by common molding. In the flow of removing the back Cu foil, the conductive foil in the thickness part with no isolation trench formed therein is etched away. In the flow of back processing, the electrodes of the conductive pattern exposed to the back are processed. In the flow of adhesive sheet, multiple blocks are attached to an adhesive sheet. In the flow of measurement, the circuit elements built in the structure are checked and graded. In the flow of dicing, the insulating resin is diced into individual circuit devices. - Next described are the steps of the invention with reference to
FIG. 14 and FIGS. 16 to 26. - As in
FIG. 16 toFIG. 18 , the first step comprises preparingconductive foil 160, and forming aisolation trench 161 that does not exceed the thickness of theconductive foil 160 in a region of theconductive foil 160 at least except the region to be aconductive pattern 151 that has a number of parts to carrycircuit elements 152 mounted thereon, thereby to form theconductive pattern 151 in multiple blocks. - In this step, a sheet of
conductive foil 160 is prepared, as inFIG. 16A . The material for theconductive foil 160 is selected in consideration of solder adhesiveness thereto and the bondability and the platability thereof. For example, conductive foil of essentially Cu, conductive foil of essentially Al, or conductive foil of essentially Fe—Ni alloy or the like can be used. - The thickness of the conductive foil is preferably from 10 μm to 300 μm or so in view of the easiness in etching it. In this, a copper foil having a thickness of 125 μm is used. Basically, however, the conductive foil may be thicker than 300 μm or thinner than 10 μm. As will be mentioned hereinunder, the thickness of the
conductive foil 160 may be such that it accepts the formation of ashallow isolation trench 161 therein. - The sheet-like
conductive foil sheet 160 may be prepared in the form of a roll having a predetermined width, for example, 45 mm, and this may be fed to each step. Alternatively, strips ofconductive foil 160 cut to have a predetermined size may be prepared and these may be fed to each step. - Concretely, four or five
blocks 162 are formed on aconductive foil strip 160, spaced from each other as inFIG. 16B . Each block shall have a large number of element-mounting parts to be formed therein. Aslit 163 is formed between the neighboringblocks 162, and this acts to absorb the stress of theconductive foil 160 in thermal treatment in the molding step, etc. Index holes 164 are formed at predetermined intervals in the upper and lower peripheries of theconductive foil 160, and these are for determining location in every step. - Next, a
conductive pattern 151 is formed in every block. - As in
FIG. 17 , a photoresist (etching-resistant mask) PR is formed on theCu foil 160, and this is patterned to partly expose theconductive foil 160 except the region to be aconductive pattern 151. Next, as inFIG. 18A , theconductive foil 160 is selectively etched via the photoresist PR. - The depth of the
isolation trench 161 formed by the etching is, for example, from 20 to 30 μm, and the side wall thereof is roughened through oxidation or chemical polishing so as to increase its adhesiveness to thethermosetting resin layer 150A. - The side wall of the
isolation trench 161 is schematically drawn to be straight in the figures, but may have any other structure depending on the method of removing the photoresist for forming it. The method of photoresist removal includes wet etching, dry etching, laser evaporation and dicing. In wet etching, the etchant to be employed is essentially ferric chloride or cupric chloride, and the conductive foil is dipped in or showered with the etchant. In wet etching, in general, the conductive foil is etched non-anisotropically, and its etched side wall is therefore curved. - In dry etching, the conductive foil may be etched anisotropically or non-anisotropically. At present, it is said that Cu could not be removed through reactive ion etching, but it may be removed through sputtering. Depending on the condition of sputtering, Cu may be etched anisotropically or non-anisotropically.
- In laser evaporation, a laser ray may be directly applied to the conductive foil to form the
isolation trench 161. In this case, the side wall of theisolation trench 161 formed may be straight. -
FIG. 18B is a schematic view of theconductive pattern 151. This corresponds to an enlargement of oneblock 162 shown inFIG. 16B . One black section corresponds to one element-mountingpart 165, and the black sections constitute theconductive pattern 151. Oneblock 162 has a large number of element-mountingparts 165 that are aligned in a matrix of 5 lines and 10 rows, and the sameconductive pattern 151 is formed for every element-mountingpart 165. Aframe pattern 166 is formed around every block, andregistration marks 167 for dicing are provided inside it, spaced in some degree from it. Theframe pattern 166 is for engagement of the patterned conductive foil with a mold, and after back etching of theconductive foil 160, it reinforces the insulatingresin 150B. - The second step of the invention is to form the
thermosetting resin layer 150A that covers theisolation trench 161 and the surface of theconductive pattern 151, as inFIG. 19 . - This step characterizes the invention, in which a thermosetting resin such as epoxy resin is used for the
thermosetting resin layer 150A, and this fills theisolation trench 161 and covers the surface of theconductive pattern 151. For forming thethermosetting resin layer 150A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 161 and theconductive pattern 151, heated at 80° C. to 100° C. to semi-cure it with evaporating away the organic solvent, and then further heated at 150° C. to 170° C. for about 1.5 hours to finally cure it. Accordingly, the semi-cured thermosetting resin is in B-stage, and it is not as yet finally set. - Preferably, a filler such as silica or alumina is added to the
thermosetting resin layer 150A to reduce the thermal expansion difference between thelayer 150A and theconductive pattern 151. In general, the thermal expansion coefficient of epoxy resin is 50 ppm/° C.; that of epoxy resin containing the filler is from 15 to 30 ppm/° C.; and that of copper to form theconductive pattern 151 is 18 ppm/° C. Therefore, the filler may remove the thermal expansion mismatch between epoxy resin and copper. - Since the thermosetting resin for the
layer 150A is filled into theisolation trench 161 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 161, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. The depth of theisolation trench 161 is about 60 μm for ensuring the necessary adhesion strength in the related art. However, since the adhesion strength in this embodiment is increased, the depth of theisolation trench 161 may be a half of it in the related art as above, concretely from 20 to 30 μm, and this produces an advantage in that theconductive pattern 151 may be a finer pattern. - Another method may be employed for forming the
thermosetting resin layer 150A, which comprises pressing a semi-cured film sheet of thermosetting resin such as epoxy resin against theconductive pattern 151 followed by finally curing it thereon under heat to thereby cover theconductive pattern 151 and fill theisolation trench 161 with the resin. The surface of the thermosetting resin film is covered with a cushion sheet, and pressed under 100 kg/cm2 under heat at 150° C. to 170° C., and the resin is finally cured while its melt covers theisolation trench 161 and the surface of theconductive pattern 151. - In this step, it is desirable to roughen the inner wall of the
isolation trench 161 for further enhancing the adhesion strength between theisolation trench 161 and thethermosetting resin layer 150A. For it, for example, the inner wall of theisolation trench 161 is oxidized or chemically polished with an organic acid etchant. For the organic acid etchant, for example, usable is Mec's CZ-8100 can be used. The patterned conductive foil is dipped in the etchant for a few minutes to roughen the surface thereof to a degree of from 1 to 2 μm or so. Through the treatment, the inner wall of theisolation trench 161 is roughened, and the adhesion strength between theisolation trench 161 and thethermosetting resin layer 150A is thereby increased. - In another embodiment of this step, a UV-curable resin may be used in place of the thermosetting resin for the
layer 150A. Concretely, a UV-curable resin is applied onto the patterned conductive foil, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin layer that covers the desired surface of theisolation trench 161 and theconductive pattern 151. This embodiment simplifies the process since it covers the next third step. - The third step of the invention comprises exposing the surface of a predetermined area of the
conductive pattern 151 by removing thethermosetting resin layer 150A thereon through laser etching, as inFIG. 20 . - In this step, the
thermosetting resin layer 150A is partly selectively removed through laser etching for direct patterning to thereby partly expose theconductive pattern 151. For the laser, carbon dioxide laser is preferred, but excimer laser and YAG laser may also be used. When the resin still remains on the bottom of the opening after its removal through laser evaporation, it is removed, for example, through wet etching with sodium permanganate or ammonium persulfate or through dry etching with excimer laser. - The fourth step of the invention comprises forming a
conductive film 154 on the exposedconductive pattern 151, as inFIG. 21 . - The remaining
thermosetting resin layer 150A serves as a mask, and the exposedconductive pattern 151 is plated with any of gold, silver or palladium by electrolytic plating or electroless plating to have theconductive film 154 formed thereon. Theconductive film 154 serves as a bonding pad. - For example, a silver film adheres to gold wires and to solder. In addition, fine Au wires may adhere to such a conductive film of silver. Therefore, the
conductive film 154 accepts wire bonding, and its one advantage is that the film may serve directly as a bonding pad. - The fifth step of the invention comprises fixing a
circuit element 152 on thethermosetting resin layer 150 in the element-mountingpart 165 thereof with an insulatingadhesive 158, and forming a connecting means for electrically connecting the electrode of thecircuit element 152 in the element-mountingpart 165 to a desired part of theconductive pattern 151, as inFIG. 22 . - The
circuit element 152 includes semiconductor elements such as transistors, diodes, IC chips. Though thick, face-down semiconductor elements such as CSP or BGA may also be mounted on the structure. Multiple IC chips may be piled up or may be arrayed in plane to constitute thecircuit element 152. - In the illustrated embodiment, a
bare IC chip 152 is fixed onto thethermosetting resin layer 150A with an insulatingadhesive 158 such as epoxy resin, and the electrodes of theIC chip 152 are connected to the correspondingconductive films 154 formed on theconductive pattern 151 around the element-mountingpart 165, via abonding wire 155 bonded to the two by thermal ball bonding or ultrasonic wedge bonding. - A large number of
conductive patterns 151 are integrated in everyblock 162. Therefore, the advantage of this step is that thecircuit elements 152 may be efficiently mounted on the conductive patterns through physical fixation and wire bonding. - The sixth step of the invention comprises common-molding the
circuit elements 152 on the element-mountingparts 163 with an insulatingresin 150B that collectively covers the elements and bonds to thethermosetting resin layer 150A filled in theisolation trench 161, as inFIG. 23 . - The
isolation trench 161 and theconductive pattern 151 are covered with thethermosetting resin layer 150A in the previous step, and the insulatingresin 150B covers thecircuit element 152 and bonds to thethermosetting resin layer 150A remaining in theisolation trench 161 and on the surface of theconductive pattern 151, as inFIG. 23A . In particular, when thermosetting resin of the same type such as epoxy resin is used for both thethermosetting resin layer 150A and the insulatingresin 150B, the two have an affinity for each other and therefore produce a higher adhesion strength between them. For further enhancing the adhesion strength, it is desirable that the surface of thethermosetting resin layer 150A is subjected to UV irradiation or plasma irradiation to activate the polar group of the resin in the surface of thelayer 150A prior to the molding treatment with the insulatingresin 150B. As a result, thethermosetting resin layer 150A is integrated with the insulatingresin 150B to more firmly support theconductive pattern 151. - The treatment of this step may be realized by transfer molding, injection molding or dipping. Regarding the type of the resin material, thermosetting resin such as epoxy resin may be transfer-molded; and thermoplastic resin such as polyimide resin or polyphenylene sulfide may be injection-molded.
- In this step of transfer molding or injection molding, the element-mounting
parts 163 in oneblock 162 are all put in one common mold, and they are common-molded with one insulatingresin 150, as inFIG. 23B . In this step, therefore, the amount of the resin to be used may be reduced significantly, as compared with that in conventional transfer molding, and common molds may be used. - The thickness of the insulating
resin 150B that covers the surface of theconductive foil 160 is so controlled that it is about 100 μm or so from the top of thecircuit element 152. This thickness may be increased or decreased in consideration of the mechanical strength of the resin layer. - This step is characterized in that the
conductive foil 160 to form theconductive pattern 151 serves as a supporting board before it is coated with the insulatingresin 150B. In the related art technology, theconductive paths 507 to 511 are formed by the use of the supportingboard 505 that is naturally unnecessary, as inFIG. 11 . In the invention, however, theconductive foil 160 that serves as the supporting board is a material necessary for electrodes. Accordingly, the invention is advantageous in that the necessary constitutive materials may be reduced to the minimum and the production costs are therefore reduced. - Since the depth of the
isolation trench 161 does not exceed the thickness of theconductive foil sheet 160, theconductive pattern 151 of theconductive foil 160 is not individually separated. Accordingly, the sheet-likeconductive foil 160 can be handled as one sheet as a whole, and when it is molded with the insulatingresin 150B, it may be readily transferred and put into a mold. - The seventh step of the invention comprises removing the
conductive foil 160 in the thickness part not having theisolation trench 161 formed therein, as inFIG. 23A . - In this step, the back of the
conductive foil 160 is chemically and/or physically removed to individually separate theconductive pattern 151. This may be carried out, for example, through polishing, cutting, etching or metal evaporation with laser. - In one example of this process, the entire back of the
conductive foil 160 is cut with a polishing machine or a cutting machine to a depth of about 100 μm or so, whereby thethermosetting resin layer 150A is exposed out of theisolation trench 161. The face to be exposed out through the treatment is represented by the dotted line inFIG. 23A . As a result, theconductive pattern 151 is individually separated to have a thickness of about 30 μm. Apart from it, the entire back of theconductive foil 160 may be wet-etched before thethermosetting resin layer 150A is exposed out, and then it may be cut with a polishing or cutting machine so that thethermosetting resin layer 150A is exposed out. In still another embodiment, the entire back of theconductive foil 160 may be wet-etched to the depth of the dotted line whereby thethermosetting resin layer 150A may also be exposed out. - In the structure thus processed, the back of the
conductive pattern 151 is exposed out of thethermosetting resin layer 150A. Specifically, the face of thethermosetting resin layer 150A filled in theisolation trench 161 is substantially on the same level as that of theconductive pattern 151. Accordingly, thecircuit device 153 of the invention does not have a difference in level for theback electrodes FIG. 12 that indicates a related art technology, and this is characterized in that, when other elements are mounted thereon, it accepts horizontal movement for self-alignment based on the surface tension of solder or the like. - Further, the back of the
conductive pattern 151 is processed to obtain the final structure as inFIG. 14 . Concretely, a part of theconductive pattern 151 to form electrodes is selectively exposed out while the other part thereof is coated with a resistlayer 157, and a conductive material such as solder is applied to it to form backelectrodes 156, thereby completing a final circuit device. - The eighth step of the invention comprises sticking the
multiple blocks 162 to anadhesive sheet 180 via the insulatingresin 150B of each block, as inFIG. 24 . - In the previous step, the back of the
conductive foil 160 is etched and then it is divided intoindividual blocks 162. Since the blocks are connected to each other via thethermosetting resin layer 150A and the insulatingresin 150B and via the remaining part of theconductive foil 160, they may be individually separated from each other by mechanically peeling them from the remaining part of theconductive foil 160, not using a dicing mold. - In this step, the periphery of an
adhesive sheet 180 is stuck to a stainlessmetal ring frame 181, and fourblocks 162 are stuck to the center part of theadhesive sheet 180 via the insulatingresin 150B of each block in such as manner that they are spaced from each other so as not to interfere with the blades for dicing. For theadhesive sheet 180, a UV sheet (by Lintec) may be used. In place of it, however, any other dicing sheet may be used since the insulatingresin 150B ensures good mechanical strength of eachblock 162. - The ninth step of the invention comprises measuring the characteristics of the
circuit element 152 on each element-mountingpart 165 of eachblock 162 attached to theadhesive sheet 180, as inFIG. 25 . As so mentioned hereinabove, the circuit elements in every block are molded all at a time with thethermosetting resin layer 150A and the insulatingresin 150B. - On the back of each
block 162, theback electrodes 156 are exposed out, and the element-mountingparts 165 are aligned in matrix quite similarly to the initialconductive pattern 151, as inFIG. 14 . A probe is applied to theback electrode 156 exposed out of the insulatingresin 150B that covers theconductive pattern 151, and the characteristic parameters of thecircuit element 152 on every element-mountingpart 165 are individually measured for checking the quality of each device. The inferior devices are marked with a magnetic ink or the like. - In this step, the
circuit devices 153 on the element-mountingparts 165 are integrally supported by the insulatingresin 150B as a whole in everyblock 162, and are not individually separated from each other. Accordingly, themultiple blocks 162 attached to theadhesive sheet 180 may be vacuum-sucked to the stand of a tester, and eachblock 162 is moved in the machine direction and in the cross direction, like the arrow, by the size of the element-mountingpart 165 at a predetermined pitch, whereby thecircuit devices 153 on the element-mounting parts in an extremely large number ofblocks 162 may be checked all at a time. This process does not require the discrimination of the back and the face of each circuit device and the recognition of the electrode position that are needed in the related art technology. In addition, the process enables simultaneous treatment of a large number ofmultiple blocks 162 all at a time, and therefore the test time for it may be significantly shortened. - The tenth step of the invention comprises dicing the
thermosetting resin layer 150A and the insulatingresin 150B of theblocks 162 attached to theadhesive sheet 180 into the individual element-mountingparts 165, as inFIG. 26 . - In this step, the
multiple blocks 162 attached to theadhesive sheet 180 are vacuum-sucked to the stand of a dicing machine, and thethermosetting resin layer 150A and the insulatingresin 150B on theisolation trench 161 are diced with adicing blade 169 along the dicingline 170 between the element-mountingparts 165 to thereby individually separate thecircuit devices 153 from each other. - In this step, the
dicing blade 169 completely cut thethermosetting resin layer 150A and the insulatingresin 150B to the depth that reaches the surface of the adhesive sheet, whereby the element-mountingparts 165 are completely separated from each other. In this step, the registration marks 167 made inside the frame pattern around every block in the first step are recognized, and based on these, the block is diced into individual circuit elements. As well known, each block is first diced along every machine-direction dicing line 170, then the stand is rotated by 90 degrees, and the thus-diced pieces are again diced along thecross-direction dicing line 170. - In this step, the dicing
line 170 has only thethermosetting resin layer 150A filled in theisolation trench 161 and the insulatingresin 150B that overlies it, and therefore the dicing blade is worn little and produces little metal burr. The process enables extremely accurate dicing into precision devices. - Even after this step, or that is, even after diced, the individual circuit devices are not scattered since they are supported by the
adhesive sheet 180. In the subsequent taping step, therefore, they are worked efficiently. Concretely, the circuit devices that are integrally supported by theadhesive sheet 180 are screened, and only the good devices thus selected are released from theadhesive sheet 180 and collected in the collection holes of a carrier tape by the action of a suction collet. Accordingly, the process is characterized in that the microstructured circuit devices are not scattered at all throughout the process and they are well held on a tape. - One embodiment of the manufacturing method of the invention has been described hereinabove. Needless to say, the order of the inspection step and the dicing step may be reversed. This is because the diced devices are all supported on the
adhesive sheet 180 and can be tested with no problem. One matter to be specifically taken into consideration in this case is that the diced devices are supported by theadhesive sheet 180 and the deformation of theadhesive sheet 180 must be taken into consideration in the step of inspecting the devices. - In the invention, the conductive foil to be a conductive pattern functions by itself as a supporting board, and the conductive foil supports the entire structure while the isolation trench is formed and while the circuit elements are mounted and covered with an insulating resin. When the conductive foil is separated into the individual conductive pattern, the insulating resin functions as the supporting board. Accordingly, the minimum constitutive components—circuit element, conductive foil and insulating resin may be enough for the invention. This means that the invention does not require the supporting board that is indispensable in the related art technology of manufacturing circuit devices, and it reduces the production costs. In the invention, in addition, the supporting board is unnecessary, the conductive pattern is embedded in the insulating resin, and the thickness of the insulating resin and the conductive foil may be varied in any desired manner. Thus characterized by these advantages, still another advantage of the invention is that it produces extremely thin-walled circuit devices.
- Further, since the isolation trench and the conductive pattern are covered with a thermosetting resin, still another advantage of the invention is that the thermosetting resin of low viscosity may have an increased adhesion strength to the isolation trench. In addition, the thermosetting resin and the insulating resin have an affinity to each other as they are the resins of the same type, and they may firmly bond to each other to realize good resin encapsulation for integrated semiconductor package structures. Accordingly, even though the structure of the invention comprises a one-face molded conductive pattern, it completely overcomes the drawback of peeling of the thermosetting resin layer from the insulating resin at the isolation trench. In addition, since the adhesion strength between the two resins in the structure of the invention is increased, the depth of the isolation trench may be from 20 to 30 μm or so, or that is, a half of ordinary isolation trenches. This produces still another advantage in that the conductive pattern may be a finer pattern.
- Further, since the conductive pattern is covered with a thermosetting resin layer and a conductive film, its surface is protected from oxidation. In particular, when copper foil is used, its surface is more surely protected from oxidation.
- Further, the conductive pattern may be designed in any desired manner below circuit elements. The structure of the invention could not accept multi-layered wiring. However, the single-layered wiring structure of the invention realizes high wiring density like multi-layered wiring structures.
- In the manufacturing method of the invention, since the conductive pattern is coated with a semi-cured thermosetting resin layer immediately after its formation, the isolation trench can be completely filled with a liquid thermosetting resin of low viscosity, and the adhesion strength of the two is significantly increased. In addition, since the thermosetting resin layer covers the conductive pattern immediately after the conductive pattern has been formed, the surface of the conductive pattern is not oxidized in the subsequent heating step for die bonding or wire bonding, and the reliability of the devices fabricated is high.
- Further, the thermosetting resin layer may be readily selectively removed through laser etching, and the remaining thermosetting resin layer may serve as a mask in plating the exposed conductive pattern with a conductive film. Accordingly, the manufacturing process is simplified.
- When an insulating resin is filled into isolation trenches by ordinary transfer molding, it could not be fully filled thereinto since its viscosity is high. Therefore, the problem with the case is that the adhesion strength between the isolation trench and the insulating resin is not good and the insulating resin readily peels from the conductive pattern. The invention has solved the problem by using a semi-cured thermosetting resin of low viscosity, and the adhesion strength between the isolation trench and the thermosetting resin layer in the invention is increased. Specifically, since the thermosetting resin and the insulating resin have an affinity to each other as they are the resins of the same type, and the adhesion strength of the conductive pattern to the thermosetting resin layer and to the insulating resin is greatly increased.
- Further, since multiple blocks are attached to the
adhesive sheet 180, the microstructured circuit devices are not scattered throughout the process of the invention where they are processed, and still another advantage of the manufacturing method that the invention has realized herein is that its mass-producibility is extremely good. - In addition, still another advantage of the invention is that the multiple blocks attached to the adhesive sheet can be processed in the inspecting step and the dicing step all at a time. Accordingly, in the inspection step, an extremely large number of circuit devices on the element-carrying parts in multiple blocks may be inspected all at a time, and the step does not require the discrimination of the back and the face of each circuit device and the recognition of the electrode position that are needed in the related art technology. In addition, the process enables simultaneous treatment of a large number of multiple blocks all at a time, and therefore the test time for it may be significantly shortened. Further, the advantage of the dicing step is that the dicing lines can be rapidly and surely recognized based on the registration marks made in every block. In the dicing step, the insulating resin layer alone is diced but the conductive foil is not diced. In the step, therefore, the life of the dicing blade to be used is prolonged, and the dicing treatment does not produce metal burr that is inevitable in dicing conductive foil.
- The fifth mode of the invention is a modification of the forth mode of the invention, in which the seventh step is modified in the manner mentioned below. In this embodiment, the back of the conductive pattern is exposed out to constitute an external electrode, as illustrated.
- Characterizing this embodiment, the
external electrode 256 is formed of theconductive pattern 251 of theconductive foil 260 that is below theisolation trench 261, and this protrudes from the back of thethermosetting resin layer 250A, as inFIG. 27A . Accordingly, theexternal electrode 256 is a protruding electrode by using a part of theconductive foil 260, having a height of about 100 μm. Thesolder 257 applied to theexternal electrode 256 runs around the side wall of theexternal electrode 256, and enhances the bonding strength of theexternal electrode 256 to the conductive paths of the printed circuit board, as inFIG. 27A . - The
conductive pattern 251 with heat-radiating semiconductor chips or the like fixed thereon may constitute a heat sink along with theexternal electrode 256, having the same thickness as that of theconductive foil 260, and this embodiment may produce a structure of extremely low heat resistance. - Further, when a thin
gold plate layer 257′ is formed on the surface of theexternal electrode 256 as inFIG. 27B , then it realizes a land grid array (LGA) structure. Therefore, the embodiment of this case does not require additional plating to form protruding electrodes. - The seventh step of this embodiment comprises removing the
conductive foil 260 from the area of theisolation trench 261, as inFIG. 28 . - In this step, a resist
layer 259 is applied to the back of theconductive foil 260 except the area corresponding to theisolation trench 261, and theconductive foil 260 is chemically etched with a solution of ferric chloride or the like via the mask of the resistlayer 259. As a result, theconductive foil 260 in the area of theisolation trench 261 is selectively removed and the bottom of thethermosetting resin layer 250A is exposed out. Since the bonding part of theconductive foil 260 now not having theisolation trench 261 therein is removed, theconductive pattern 251 is individually separated to have the thickness of theconductive foil 260. - As a result, the back of the
conductive pattern 251 that is almost filled withthermosetting resin layer 250A is exposed out, and theexternal electrode 256 forms a protruding electrode that protrudes by about 100 μm from the back of thethermosetting resin layer 250A. Specifically, theexternal electrode 256 means that it is formed as a protruding electrode in the bonding area of theconductive foil 260 not having theisolation trench 261 therein. - Further, the back of the
external electrode 256 is processed to obtain the final structure as inFIG. 27 . Concretely, theexternal electrode 256 is coated with a conductive material such as solder, and the circuit device is thus completed. In this case, the conductive material such as solder spreads to cover the side wall of theexternal electrode 256, and the conductive paths of the printed circuit board are fixed to both the surface and the side wall of the external electrode to increase the bonding strength between them. - Further, when the
external electrode 256 is coated with a thingold plate layer 257′, it realizes a land grid array (LGA) structure. - This back treatment does not require a mask since only the
external electrode 256 is exposed out of thethermosetting resin layer 250A and the insulatingresin 250B, and its advantage is that the treatment is extremely simple. - The exposure of the back of the conductive pattern in this embodiment characterizes the invention. The back of the conductive pattern serves as the
external electrode 256 to be connected with external units, and, in addition, theexternal electrode 256 acts as a heat sink and a protruding electrode. - The sixth mode of the circuit device of the invention is described with reference to
FIG. 29 . - The circuit device of the invention comprises a multiple conductive patterns for element mounting thereon that are electrically separated from each other by a isolation trench, a thermosetting resin layer that fills the isolation trench to cover the surface of the conductive pattern, a circuit element fixed on a desired region of the conductive pattern exposed out of the thermosetting resin layer, an insulating resin that covers the circuit element to integrally support the conductive pattern bonded to the thermosetting resin layer, and an external electrode formed by exposing the back of the conductive pattern.
-
FIG. 29 shows acircuit device 353 having a conductive pattern 351 almost embedded in athermosetting resin layer 350A, in which a circuit element 352 is fixed on the conductive pattern 351 and the conductive pattern 351 is supported by an insulatingresin 350B bonded to thethermosetting resin layer 350A. - This structure comprises four types of elements, the
circuit elements conductive patterns thermosetting resin layer 350A to envelop theconductive patterns resin 350B that bonds to theresin layer 350A. In this, the conductive pattern 351 is separated by theisolation trench 361 filled with thethermosetting resin layer 350A. The conductive pattern 351 is supported by thethermosetting resin layer 350A and the insulatingresin 350B. - For the
thermosetting resin layer 350A that characterizes the invention, a thermosetting resin such as epoxy resin is used. The resin fills theisolation trench 361 and covers the surfaces of theconductive patterns thermosetting resin layer 350A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 361 and theconductive patterns thermosetting resin layer 350A to reduce the thermal expansion difference between thelayer 350A and theconductive patterns conductive patterns - Since the thermosetting resin for the
layer 350A is filled into theisolation trench 361 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 361, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. - Another method may be employed for forming the
thermosetting resin layer 350A, which comprises pressing a semi-cured film sheet of thermosetting resin such as epoxy resin against theconductive patterns isolation trench 361 with the resin. - For the insulating
resin 350B, any of thermosetting resin such as epoxy resin, or thermoplastic resin such as polyimide resin or polyphenylene sulfide may be employed. Not limited to these, the insulating resin may be any and every resin that may be solidified in molds, or may be applied to semiconductor by dipping or coating. However, in consideration of its bonding strength to thethermosetting resin layer 350A, resin of the same type is preferred for the two. Therefore, in this, thermosetting resin such as epoxy resin is used for the insulatingresin 350B. - For the conductive pattern 351, for example, any of conductive foil consisting essentially of Cu, conductive foil consisting essentially of Al, or conductive foil consisting essentially of Fe—Ni or the like alloy may be employed. Needless to say, any other conductive material may also be used. Especially preferred are etchable conductive materials and conductive materials evaporable by laser.
- For connecting the circuit element 352 to any other element, any of a
bonding wire 355A, a conductive ball of solder, a flattenable conductive ball, asolder 355B, aconductive paste 355C of Ag or the like, a conductive film or an anisotropic conductive resin may be used. The connecting means is selected depending on the type of the circuit element 352 and the mounting mode thereof. For example, for a baser semiconductor element, a bonding wire is selected for connecting the surface electrode and the conductive pattern 351; and for CSP, a solder ball or a solder bump is selected. For the chip resistor and the chip capacitor, selected is asolder 355B or a silver paste. A semiconductor device package such as BGA may be mounted on the conductive pattern 351 with no problem. In this case, solder is selected for the connecting means. - When the circuit element is fixed to the
conductive pattern 351A not requiring electric connection between them, an insulating adhesive is selected for the fixation. On the other hand, when the fixation requires electric connection, a conductive film is employed for it. In this case, at least one conductive film will be enough. - For the conductive film, any of Ag, Au, Pt or Pd is usable. The conductive film may be formed through low-vacuum or high-vacuum coating, plating or sintering that includes vapor deposition, sputtering, CVD and the like.
- For example, Ag adheres to Au and also to solder. Accordingly, when the back of a chip is coated with Au, the chip may be directly bonded to the
conductive path 351A coated with an Ag film, Au film or solder film, or the chip may also be bonded thereto via solder. The conductive film may be the uppermost layer of a multi-layered conductive film. For example, two layers of Ni film and Au film may be formed in that order on the Cuconductive pattern 351A; or three layers of Ni film, Cu film and solder film may be formed in that order thereon; or two layers of Ag film and Ni film may be formed in that order thereon. Apart from these, there are many different types of conductive films and many different laminate structures thereof, but the description relating to them is omitted herein. - The external electrode 356 characterizes the invention, and it is formed of the
conductive foil 360 of the conductive pattern 351 that remains below theisolation trench 361. This protrudes from the back of thethermosetting resin layer 350A. Accordingly, a part of theconductive foil 360 forms the external electrode 356, which is a protruding electrode having a height of about 100 μm. Therefore, thesolder 357 applied to the external electrode 356 runs around the side wall of the external electrode 356, and enhances the bonding strength of the external electrode 356 to the conductive paths of the printed circuit board, as inFIG. 29A . - The
conductive pattern 351A with heat-radiating semiconductor chips or the like fixed thereon may constitute a heat sink along with theexternal electrode 356A, and this embodiment may produce a structure of extremely low heat resistance. - Further, when a thin
gold plate layer 358 is formed on the surface of the external electrode 356 as inFIG. 29B , then it realizes a land grid array (LGA) structure. Therefore, the embodiment of this case does not require additional plating to form protruding electrodes. - In this circuit device, the conductive pattern 351 is supported by the
thermosetting resin layer 350A and the insulatingresin 350B, and therefore does not require a supporting board for it. This constitution characterizes the invention. As so described hereinabove with reference to the related art, the conductive paths in conventional circuit devices are supported by a supporting board or by a lead frame, and they require superfluous structures that are naturally unnecessary. However, the circuit device of the invention is composed of the least necessary constitutive elements, not requiring a supporting board, and it may be thinned and low-priced. - Another advantage of the circuit device of the invention is that the
thermosetting resin layer 350A therein covers the circuit element 352 and fills theisolation trench 361 between the conductive pattern 351 for individual insulation. - In the circuit device, the
thermosetting resin layer 350A and the insulatingresin 350B integrally support the structure in such a manner that the insulatingresin 350B covers the circuit element 352 and thethermosetting resin layer 350A fills theisolation trench 361 between the conductive pattern 351 with the back alone of the conductive pattern 351 exposed outside. - Exposing the back of the conductive pattern characterizes the invention. The back of the conductive pattern is connected to the external electrode 356 and serves for further connection to other external elements. In addition, the external electrode 356 acts as a heat sink and a protruding electrode.
- In addition, when the circuit element is directly bonded to the structure via a conductive film of solder, Au, Ag or the like, the heat generated by the
circuit element 352A may be transferred to the substrate via theconductive pattern 351A since the back of the conductive pattern 351 is exposed out to form theexternal electrode 356A. Accordingly, the structure of this embodiment is effective for semiconductor chips that require heat radiation when the driving current increases. - In another embodiment, a UV-curable resin may be used in place of the
thermosetting resin layer 350A. Concretely, a UV-curable resin is applied onto the structure, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin film that covers the desired surface of theisolation trench 361 and the conductive pattern 351. UV-curable resin is a type of epoxy resin, and is therefore effective like thethermosetting resin layer 350A. - One embodiment of manufacturing the circuit device of the sixth mode of the invention is described with reference to
FIG. 30 . - The method of the invention comprises a step of preparing conductive foil and forming a isolation trench that does not exceed the thickness of the conductive foil in a region of the conductive foil at least except the region to be a conductive pattern that has a number of parts to carry circuit elements mounted thereon, thereby to form the conductive pattern in multiple blocks; a step of coating the isolation trench and the conductive pattern with a thermosetting resin; a step of exposing a predetermined surface of the conductive pattern through laser etching; a step of forming a conductive film selectively on the exposed conductive pattern; a step of fixing circuit elements on the element-mounting parts of the desired conductive pattern; a step of connecting the electrode of the circuit element to the conductive film of the conductive pattern by wire bonding; a step of common-molding it with an insulating resin to collectively cover the circuit element on every element-mounting part and to fill the isolation trench; a step of removing the conductive foil in the part of the isolation trench; a step of sticking the multiple blocks to an adhesive sheet via the insulating resin of each block; a step of measuring the characteristics of the circuit element on each element-mounting part of each block attached to the adhesive sheet; and a step of dicing the insulating resin into the individual element-mounting parts of each block attached to the adhesive sheet.
- The flowchart of
FIG. 30 does not correspond to the method as above. In this, the two flows of Cu foil and half-etching are to form a conductive pattern. In the next flow of thermosetting resin, the surface of the isolation trench and the conductive pattern are covered with a thermosetting resin. In the two flows of die bonding and wire bonding, a circuit element is fixed on each element-mounting part, and its electrodes are connected to the conductive pattern. In the flow of transfer molding, an insulating resin is applied to the structure by common molding. In the flow of removing the back Cu foil, the conductive foil in the part of the isolation trench is etched away. In the flow of back processing, the external electrodes that protrude from the back of the structure are subjected to surface treatment. In the flow of adhesive sheet, multiple blocks are attached to an adhesive sheet. In the flow of measurement, the circuit elements built in the structure are checked and graded. In the flow of dicing, the insulating resin is diced into individual circuit devices. - Next described are the steps of the invention with reference to
FIG. 29 and FIGS. 31 to 39. - As in
FIG. 31 toFIG. 33 , the first step comprises preparingconductive foil 360, and forming aisolation trench 361 that does not exceed the thickness of theconductive foil 360 in a region of theconductive foil sheet 360 at least except the region to be a conductive pattern 351 that has a number of parts to carry circuit elements 352 mounted thereon, thereby to form the conductive pattern 351 in multiple blocks. - In this step, a sheet like-
conductive foil 360 is prepared, as inFIG. 31A . The material for theconductive foil 360 is selected in consideration of solder adhesiveness thereto and the bondability and the platability thereof. For example, conductive foil of essentially Cu, conductive foil of essentially Al, or conductive foil of essentially Fe—Ni alloy or the like may be used. - The thickness of the conductive foil is preferably from 10 μm to 300 μm or so in view of the easiness in etching it. In this, copper foil having a thickness of 125 μm is used. Basically, however, the conductive foil may be thicker than 300 μm or thinner than 10 μm. As will be mentioned hereinunder, the thickness of the
conductive foil 360 may be such that it accepts the formation of ashallow isolation trench 361 therein. - The
conductive foil sheet 360 may be prepared in the form of a roll having a predetermined width, for example, 45 mm, and this may be fed to each step. Alternatively, strips ofconductive foil 360 cut to have a predetermined size may be prepared and these may be fed to each step. - Concretely, four or five
blocks 362 are formed on aconductive foil strip 360, spaced from each other as inFIG. 31B . Each block shall have a large number of element-mounting parts to be formed therein. Aslit 363 is formed between the neighboringblocks 362, and this acts to absorb the stress of theconductive foil 360 in thermal treatment in the molding step, etc. Index holes 364 are formed at predetermined intervals in the upper and lower peripheries of theconductive foil 360, and these are for location in every step. - Next, a conductive pattern 351 is formed in every block.
- As in
FIG. 32 , a photoresist (etching-resistant mask) PR is formed on theCu foil 360, and this is patterned to partly expose theconductive foil 360 except the region to be a conductive pattern 351. Next, as inFIG. 33A , theconductive foil 360 is selectively etched via the photoresist PR. - The depth of the
isolation trench 361 formed by the etching is, for example, from 20 to 30 μm, and the side wall thereof is roughened through oxidation or chemical polishing so as to increase its adhesiveness to thethermosetting resin layer 350A. - The side wall of the
isolation trench 361 is schematically drawn to be straight in the figures, but may have any other structure depending on the method of removing the photoresist for forming it. The method of photoresist removal includes wet etching, dry etching, laser evaporation and dicing. In wet etching, the etchant to be employed is essentially ferric chloride or cupric chloride, and the conductive foil is dipped in or showered with the etchant. In wet etching, in general, the conductive foil is etched non-anisotropically, and its etched side wall is therefore curved. - In dry etching, the conductive foil may be etched anisotropically or non-anisotropically. At present, it is said that Cu could not be removed through reactive ion etching, but it may be removed through sputtering. Depending on the condition of sputtering, Cu may be etched anisotropically or non-anisotropically.
- In laser evaporation, a laser ray may be directly applied to the conductive foil to form the
isolation trench 361. In this case, the side wall of theisolation trench 361 formed may be straight. -
FIG. 33B is a schematic view of the conductive pattern 351. This corresponds to an enlargement of oneblock 362 shown inFIG. 31B . One black section corresponds to one element-mountingpart 365, and the black sections constitute the conductive pattern 351. Oneblock 362 has a large number of element-mountingparts 365 that are aligned in a matrix of 5 lines and 10 rows, and the same conductive pattern 351 is formed for every element-mountingpart 365. Aframe pattern 366 is formed around every block, andregistration marks 367 for dicing are provided inside it, spaced in some degree from it. Theframe pattern 366 is for engagement of the patterned conductive foil with a mold, and after back etching of theconductive foil 360, it reinforces the insulatingresin 350B. - The second step of the invention is to form the
thermosetting resin layer 350A that covers theisolation trench 361 and the surface of the conductive pattern 351, as inFIG. 34 . - This step characterizes the invention, in which a thermosetting resin such as epoxy resin is used for the
thermosetting resin layer 350A, and this fills theisolation trench 361 and covers the surfaces of theconductive patterns thermosetting resin layer 350A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 361 and theconductive patterns - Preferably, a filler such as silica or alumina is added to the
thermosetting resin layer 350A to reduce the thermal expansion difference between thelayer 350A and theconductive patterns conductive patterns - Since the thermosetting resin for the
layer 350A is filled into theisolation trench 361 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 361, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. The depth of theisolation trench 161 is about 60 μm for ensuring the necessary adhesion strength in the related art. However, since the adhesion strength in this embodiment is increased, the depth of theisolation trench 361 may be a half of it in the related art as above, concretely from 20 to 30 μm, and this produces an advantage in that the conductive pattern 351 may be a finer pattern. - Another method may be employed for forming the
thermosetting resin layer 350A, which comprises pressing a semi-cured film sheet of thermosetting resin such as epoxy resin against theconductive patterns isolation trench 361 with the resin. The surface of the thermosetting resin film is covered with a cushion sheet, and pressed under 100 kg/cm2 under heat at 150° C. to 170° C., and the resin is finally cured while its melt covers theisolation trench 361 and the surfaces of theconductive patterns - In this step, it is desirable to roughen the inner wall of the
isolation trench 361 for further enhancing the adhesion strength between theisolation trench 361 and thethermosetting resin layer 350A. For it, for example, the inner wall of theisolation trench 361 is oxidized or chemically polished with an organic acid etchant. For the organic acid etchant, for example, Mec's CZ-8100 may be used. The patterned conductive foil is dipped in the etchant for a few minutes to roughen the surface thereof to a degree of from 1 to 2 μm or so. Through the treatment, the inner wall of theisolation trench 361 is roughened, and the adhesion strength between theisolation trench 361 and thethermosetting resin layer 350A is thereby increased. - In another embodiment of this step, a UV-curable resin may be used in place of thermosetting resin. Concretely, a UV-curable resin is applied onto the patterned conductive foil, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin layer that covers the desired surface of the
isolation trench 361 and the conductive pattern 351. This embodiment simplifies the process since it covers the next third step. - The third step of the invention comprises exposing the surface of a predetermined area of the conductive pattern 351 by removing the
thermosetting resin layer 350A thereon through laser etching, as inFIG. 35 . - In this step, the
thermosetting resin layer 350A is partly selectively removed through laser etching for direct patterning to thereby partly expose the conductive pattern 351. For the laser, carbon dioxide laser is preferred, but excimer laser and YAG laser may also be used. When the resin still remains on the bottom of the opening after its removal through laser evaporation, it is removed, for example, through wet etching with sodium permanganate or ammonium persulfate or through dry etching with excimer laser. - The fourth step of the invention comprises forming a
conductive film 354 on the exposed conductive pattern 351, as inFIG. 36 . - The remaining
thermosetting resin layer 350A serves as a mask, and the exposed conductive pattern 351 is plated with any of gold, silver or palladium by electrolytic plating or electroless plating to have theconductive film 354 formed thereon. Theconductive film 354 serves as a die pad or a bonding pad. - For example, a silver film adheres to gold wires and to solder. Therefore, when the back of the chip to be applied to the structure of this embodiment is coated with gold, the chip may directly be bonded to the silver film formed on the conductive pattern 351 or may be bonded thereto via solder. In addition, fine Au wires may adhere to the conductive film of silver. Therefore, the
conductive film 354 accepts wire bonding, and its one advantage is that the film may serve directly as a die pad or a bonding pad. - The fifth step of the invention comprises fixing a circuit element 352 on the element-mounting
part 365 of the desired conductive pattern 351, and forming a connecting means for electrically connecting the electrode of the circuit element 352 in the element-mountingpart 365 to a desired part of the conductive pattern 351, as inFIG. 37 . - The circuit element 352 includes semiconductor elements such as transistors, diodes, IC chips, and passive elements such as chip capacitors and chip resistors. Though thick, face-down semiconductor elements such as CSP or BGA may also be mounted on the structure.
- In the illustrated embodiment, a
bare transistor chip 352A is die-bonded to theconductive film 354 on theconductive pattern 351A, and its emitter electrode is bonded to theconductive film 354 on theconductive pattern 351B with its base electrode to theconductive film 354 on theconductive pattern 351B, via abonding wire 355A bonded to the two by thermal ball bonding or ultrasonic wedge bonding. 352B is a chip capacitor or a passive element, and it is bonded to the structure via solder orconductive paste 355B. - A large number of conductive patterns 351 are integrated in every
block 362. Therefore, the advantage of this step is that the circuit elements 352 may be efficiently mounted on the conductive patterns through physical fixation and wire bonding. - The sixth step of the invention comprises common-molding the circuit elements 352 on the element-mounting
parts 363 with an insulatingresin 350B that collectively covers the elements and bonds to thethermosetting resin layer 350A filled in theisolation trench 361, as inFIG. 38 . - The
isolation trench 361 and the multipleconductive patterns thermosetting resin layer 350A in the previous step, and the insulatingresin 350B covers the circuit element 352 and bonds to thethermosetting resin layer 350A remaining in theisolation trench 361 and on the surface of the conductive pattern 351, as inFIG. 38A . In particular, when thermosetting resin of the same type such as epoxy resin is used for both thethermosetting resin layer 350A and the insulatingresin 350B, the two have an affinity for each other and therefore produce a higher adhesion strength between them. For further enhancing the adhesion strength, it is desirable that the surface of thethermosetting resin layer 350A is subject to UV irradiation or plasma irradiation to activate the polar group of the resin in the surface of thelayer 350A prior to the molding treatment with the insulatingresin 350B. As a result, thethermosetting resin layer 350A is integrated with the insulatingresin 350B to more firmly support the conductive pattern 351. - The treatment of this step may be realized by transfer molding, injection molding or dipping. Regarding the type of the resin material, thermosetting resin such as epoxy resin may be transfer-molded; and thermoplastic resin such as polyimide resin or polyphenylene sulfide may be injection-molded.
- In this step of transfer molding or injection molding, the element-mounting
parts 363 in oneblock 362 are all put in one common mold, and they are common-molded with one insulatingresin 350, as inFIG. 38B . In this step, therefore, the amount of the resin to be used maybe reduced significantly, as compared with that in conventional transfer molding, and common molds may be used. - The thickness of the insulating
resin 350B that covers the surface of theconductive foil 360 is so controlled that it is about 100 μm or so from the top of the circuit element 352. This thickness may be increased or decreased in consideration of the mechanical strength of the resin layer. - This step is characterized in that the
conductive foil 360 to form the conductive pattern 351 serves as a supporting board before it is coated with the insulating resin 130B. In the related art technology, theconductive paths 507 to 511 are formed by the use of the supportingboard 505 that is naturally unnecessary, as inFIG. 11 . In the invention, however, theconductive foil 360 that serves as the supporting board is a material necessary for electrodes. Accordingly, the invention is advantageous in that the necessary constitutive materials may be reduced to the minimum and the production costs are therefore reduced. - Since the depth of the
isolation trench 361 does not exceed the thickness of theconductive foil 360, the conductive pattern 351 of theconductive foil 360 is not individually separated. Accordingly, theconductive foil 360 can be handled as one sheet as a whole, and when it is molded with the insulatingresin 350B, it may be readily transferred and put into a mold. - The seventh step of the invention comprises removing the
conductive foil 360 in the part of theisolation trench 361, as inFIG. 39 . - In this step, a resist
layer 359 is formed on the back of theconductive foil 360 except a part thereof that corresponds to theisolation trench 361. Via the resistlayer 359 that serves as a mask, theconducive foil 360 is chemically etched with an etchant of ferric chloride or the like. As a result, theconductive foil 360 corresponding to the part of theisolation trench 361 is selectively removed, and the bottom of thethermosetting resin layer 350A in that part is exposed out. In this step, the joint part of theconductive foil 360 not having theisolation trench 361 is removed, and the conductive pattern 351 of which the thickness corresponds to that of theconductive foil 360 is separated from each other. - In the structure thus processed, the back of the conductive pattern 351 that is almost completely embedded in the
thermosetting resin layer 350A is exposed out. As a result, protrudingexternal electrodes thermosetting resin layer 350A by about 100 μm are formed. This means that theexternal electrodes conductive foil 360 not having theisolation trench 361. - Further, the back of the
external electrodes FIG. 39 . Concretely, theexternal electrodes external electrodes external electrodes - Further, when the
external electrodes - Through the back treatment, only the
external electrodes thermosetting resin layer 350A and the insulatingresin 350B, and this embodiment is advantageous in that it does not require a mask and is therefore simple. - The eighth to tenth steps of this mode are the same as those of the fourth mode described hereinabove.
- In the invention, the conductive foil to be a conductive pattern functions by itself as a supporting board, and the conductive foil supports the entire structure while the isolation trench is formed and while the circuit elements are mounted and covered with an insulating resin. When the conductive foil is separated into the individual conductive pattern, the insulating resin functions as the supporting board. Accordingly, the minimum constitutive components—circuit element, conductive foil and insulating resin may be enough for the invention. This means that the invention does not require the supporting board that is indispensable in the related art technology of manufacturing circuit devices, and it reduces the production costs. In the invention, in addition, the supporting board is unnecessary, the conductive pattern is embedded in the insulating resin, and the thickness of the insulating resin and the conductive foil may be varied in any desired manner. Thus characterized by these advantages, still another advantage of the invention is that it produces extremely thin-walled circuit devices.
- Further, since the isolation trench and the conductive pattern are covered with a thermosetting resin, still another advantage of the invention is that the thermosetting resin of low viscosity may have an increased adhesion strength to the isolation trench. In addition, the thermosetting resin and the insulating resin have an affinity to each other as they are the resins of the same type, and they may firmly bond to each other to realize good resin encapsulation for integrated semiconductor package structures. Accordingly, even though the structure of the invention comprises a one-face molded conductive pattern, it completely overcomes the drawback of peeling of the thermosetting resin layer from the insulating resin at the isolation trench. In addition, since the adhesion strength between the two resins in the structure of the invention is increased, the depth of the isolation trench may be from 20 to 30 μm or so, or that is, a half of ordinary isolation trenches. This produces still another advantage in that the conductive pattern may be a finer pattern.
- Further, since the conductive pattern is covered with a thermosetting resin layer and a conductive film, its surface is protected from oxidation. In particular, when copper foil is used, its surface is more surely protected from oxidation.
- Further, since the external electrodes are formed of the joint part of the conductive foil not having the isolation trench, they may be protruding electrodes with ease. When they serve as a heat sink, the heat radiation of the circuit device may be improved.
- In the manufacturing method of the invention, since the conductive pattern is coated with a semi-cured thermosetting resin layer immediately after its formation, the isolation trench can be completely filled with a liquid thermosetting resin of low viscosity, and the adhesion strength of the two is significantly increased. In addition, since the thermosetting resin layer covers the conductive pattern immediately after the conductive pattern has been formed, the surface of the conductive pattern is not oxidized in the subsequent heating step for die bonding or wire bonding, and the reliability of the devices fabricated is high.
- Further, the thermosetting resin layer may be readily selectively removed through laser etching, and the remaining thermosetting resin layer may serve as a mask in plating the exposed conductive pattern with a conductive film. Accordingly, the manufacturing process is simplified.
- When an insulating resin is filled into isolation trenches by ordinary transfer molding, it could not be fully filled thereinto since its viscosity is high. Therefore, the problem with the case is that the adhesion strength between the isolation trench and the insulating resin is not good and the insulating resin readily peels from the conductive pattern. The invention has solved the problem by using a semi-cured thermosetting resin of low viscosity, and the adhesion strength between the isolation trench and the thermosetting resin layer in the invention is increased. Specifically, since the thermosetting resin and the insulating resin have an affinity to each other as they are the resins of the same type, and the adhesion strength of the conductive pattern to the thermosetting resin layer and to the insulating resin is greatly increased.
- Further, since the external electrodes are formed by selectively etching the joint part of the conductive foil in the isolation trench area, they do not require plating treatment and may be readily protruding electrodes.
- The seventh mode of the circuit device of the invention is described with reference to
FIG. 40 . - The circuit device of the invention comprises a first multiple conductive patterns for element mounting thereon that are electrically separated from each other by a isolation trench, a thermosetting resin layer that fills the isolation trench to cover the surface of the first conductive pattern, a second conductive pattern formed on the thermosetting resin layer and connected to desired region of the first conductive pattern, a circuit element fixed on the second conductive pattern while insulated from it, and an insulating resin that covers the circuit element to integrally support the first and second conductive patterns bonded to the thermosetting resin layer.
-
FIG. 40 shows acircuit device 453 having a first conductive pattern 351 almost embedded in athermosetting resin layer 450A, in which a secondconductive pattern 471 is formed on thethermosetting resin layer 450A, acircuit element 452 is fixed onto the secondconductive pattern 451 while electrically insulated from it, and the firstconductive pattern 451 is supported by an insulatingresin 450B bonded to thethermosetting resin layer 450A. - This structure comprises four types of elements, the
circuit element 452, the first multipleconductive pattern 451 and the secondconductive pattern 471, thethermosetting resin layer 450A to envelop the firstconductive pattern 451, and the insulatingresin 450B that bonds to theresin layer 450A. In this, the firstconductive pattern 451 is separated by theisolation trench 461 filled with thethermosetting resin layer 450A. The firstconductive pattern 451 and the secondconductive pattern 471 are supported by thethermosetting resin layer 450A and the insulatingresin 450B. - For the
thermosetting resin layer 450A that characterizes the invention, a thermosetting resin such as epoxy resin is used. The resin fills theisolation trench 461 and covers the surface of the firstconductive pattern 451. To form thethermosetting resin layer 450A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 461 and the firstconductive pattern 451, semi-cured to evaporate away the organic solvent, and then finally cured. Preferably, a filler such as silica or alumina is added to thethermosetting resin layer 450A to reduce the thermal expansion difference between thelayer 450A and the firstconductive pattern 451. In general, the thermal expansion coefficient of epoxy resin is 50 ppm/° C.; that of epoxy resin containing the filler is from 15 to 30 ppm/° C.; and that of copper to form the firstconductive pattern 451 is 18 ppm/° C. Therefore, the filler may remove the thermal expansion mismatch between epoxy resin and copper. - Since the thermosetting resin for the
layer 450A is filled into theisolation trench 461 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 461, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. - Another method may be employed for forming the
thermosetting resin layer 450A, which comprises pressing a semi-cured film sheet of thermosetting resin such as epoxy resin against the firstconductive pattern 451 followed by finally curing it thereon under heat to thereby cover the conductive pattern and fill theisolation trench 461 with the resin. - For the insulating
resin 450B, any of thermosetting resin such as epoxy resin, or thermoplastic resin such as polyphenylene sulfide may be employed. Not limited to these, the insulating resin maybe any and every resin that may be solidified in molds, or may be applied to semiconductor by dipping or coating. However, in consideration of its bonding strength to thethermosetting resin layer 450A, resin of the same type is preferred for the two. Therefore, in this, thermosetting resin such as epoxy resin is used for the insulatingresin 450B. - For the first
conductive pattern 451, for example, any of conductive foil consisting essentially of Cu maybe employed, conductive foil consisting essentially of Al, or conductive foil consisting essentially of Fe—Ni alloy or the like may be used. Needless to say, any other conductive material may also be used. Especially preferred are etchable conductive materials and conductive materials evaporable by laser. - For the second
conductive pattern 471, a conductive film of Cu may be used which is formed on the surface of thethermosetting resin layer 450A through electrolytic or electroless plating with Cu thereon. Thethermosetting resin layer 450A is selectively removed from the spots of the firstconductive pattern 451 for electric bonding thereof to the second conductive pattern. - For connecting the
circuit element 452 to any other element, abonding wire 455 is used in a face-up structure, or a conductive ball of solder, a flattenable conductive ball or other solder material in a face-down structure. The connecting means is selected depending on the type of thecircuit element 452 and the mounting mode thereof. - The second
conductive pattern 471 to which thebonding wire 455 or solder is bonded is selectively exposed out of the insulatingfilm 472, and aconductive film 454 is formed on the surface of the thus-exposed secondconductive pattern 471. The material for theconductive film 454 is, for example, any of Ag, Au, Pt or Pd. The conductive film may be formed through low-vacuum or high-vacuum coating, plating or sintering that includes vapor deposition, sputtering, CVD and the like. - The
back electrode 456 is formed by selectively exposing out a predetermined region of the firstconductive pattern 451 with masking the other region thereof with a resistlayer 457, followed by applying a conductive material such as solder to the exposed region, and the back electrodes are protruding electrodes. - In this circuit device, the first
conductive pattern 451 and the secondconductive pattern 471 are supported by thethermosetting resin layer 450A and the insulatingresin 450B, and therefore do not require a supporting board for them. This constitution characterizes the invention. As so described hereinabove with reference to the related art, the conductive paths in conventional circuit devices are supported by a supporting board or by a lead frame, and they require superfluous structures that are naturally unnecessary. However, the circuit device of the invention is composed of the least necessary constitutive elements, not requiring a supporting board, and it may be thinned and low-priced. - Another advantage of the circuit device of the invention is that the
thermosetting resin layer 450A therein covers thecircuit element 452 and fills theisolation trench 461 between the firstconductive patterning 451 for individual insulation. - In the circuit device, the
thermosetting resin layer 450A and the insulatingresin 450B integrally support the structure in such a manner that the insulatingresin 450B covers thecircuit element 452 and thethermosetting resin layer 450A fills theisolation trench 461 between the firstconductive pattern 451 with the back alone of the firstconductive pattern 451 exposed outside. - The
circuit element 452 is bonded onto the insulatingfilm 472 that covers the secondconductive pattern 471, via an insulatingadhesive 458, and thecircuit element 452 is electrically insulated from the secondconductive pattern 471. Accordingly, the firstconductive pattern 451 and the secondconductive pattern 471 may be wired in any desired manner below thecircuit element 452, and this realizes multi-layer wiring. Each electrode pad of thecircuit element 452 is connected to theconductive film 454 formed of a part of the secondconductive pattern 471 around the circuit element and serving as a bonding pad, via abonding wire 455. - Exposing the back of the first
conductive pattern 451 characterizes the invention. The back of the conductive path may be connected to external elements, therefore not requiring through-holes TH as in the conventional structure inFIG. 11 . - In this circuit device, the surface of the
isolation trench 461 is substantially on the same level as the back of the firstconductive pattern 451. This structure characterizes the invention. This does not have a difference in level for theback electrodes FIG. 11 . Therefore, thecircuit device 453 is characterized in that it accepts horizontal movement. - In another embodiment, a UV-curable resin may be used in place of the
thermosetting resin layer 450A. Concretely, a UV-curable resin is applied onto the structure, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin film that covers the desired surface of theisolation trench 461 and the firstconductive pattern 451. UV-curable resin is a type of epoxy resin, and is therefore effective like thethermosetting resin layer 450A. - One embodiment of manufacturing the circuit device of the invention is described with reference to
FIG. 41 . - The method of the invention comprises a step of preparing conductive foil and forming a isolation trench that does not exceed the thickness of the conductive foil in a region of the conductive foil at least except the region to be a first conductive pattern that has a number of parts to carry circuit elements mounted thereon, thereby to form the first conductive pattern in multiple blocks; a step of coating the isolation trench and the first conductive pattern with a thermosetting resin; a step of exposing a predetermined surface of the first conductive pattern through laser etching; a step of forming a conductive film of Cu plate on the surface of the thermosetting resin layer in contact with the exposed first conductive pattern, followed by etching it in a predetermined pattern to form a second conductive pattern; a step of forming a conductive film selectively on the exposed second conductive pattern; a step of fixing circuit elements onto the insulating film that covers the second conductive pattern; a step of forming a connecting means for electrically connecting the electrode of each circuit element to a desired part of the second conductive pattern; a step of common-molding it with an insulating resin to collectively cover the circuit element on every element-mounting part; a step of removing the conductive foil in the thickness part with no isolation trench formed therein; a step of sticking the multiple blocks to an adhesive sheet via the insulating resin of each block; a step of measuring the characteristics of the circuit element on each element-mounting part of each block attached to the adhesive sheet; and a step of dicing the insulating resin into the individual element-mounting parts of each block attached to the adhesive sheet.
- The flowchart of
FIG. 41 does not correspond to the method as above. In this, the two flows of Cu foil and half-etching are to form a conductive pattern. In the next flow of thermosetting resin, the surface of the isolation trench and the first conductive pattern is covered with a thermosetting resin. In the flows of laser etching, Cu plating and etching, the second conductive pattern is formed. In the flow of Au plating, a bonding pad is selectively formed in the second conductive pattern. In the two flows of die bonding and wire bonding, a circuit element is fixed onto each element-mounting part, and its electrodes are connected to the second conductive pattern. In the flow of transfer molding, an insulating resin is applied to the structure by common molding. In the flow of removing the back Cu foil, the conductive foil in the thickness part with no isolation trench therein is etched away. In the flow of back processing, the electrodes of the first conductive pattern exposed to the back are processed. In the flow of adhesive sheet, multiple blocks are attached to an adhesive sheet. In the flow of measurement, the circuit elements built in the structure are checked and graded. In the flow of dicing, the insulating resin is diced into individual circuit devices. - Next described are the steps of the invention with reference to
FIG. 40 and FIGS. 42 to 50. - As in
FIG. 42 toFIG. 44 , the first step comprises preparingconductive foil 460, and forming aisolation trench 461 that does not exceed the thickness of theconductive foil 460 in a region of theconductive foil 460 at least except the region to be a firstconductive pattern 451 that has a number of parts to carrycircuit elements 452 mounted thereon, thereby to form the firstconductive pattern 451 in multiple blocks. - In this step, a sheet of
conductive foil 460 is prepared, as inFIG. 42A . The material for theconductive foil 460 is selected in consideration of solder adhesiveness thereto and the bondability and the platability thereof. For example, usable is conductive foil of essentially Cu, conductive foil of essentially Al, or conductive foil of essentially Fe—Ni or the like alloy. - The thickness of the conductive foil is preferably from 10 μm to 300 μm or so in view of the easiness in etching it. In this, used is copper foil having a thickness of 125 μm. Basically, however, the conductive foil may be thicker than 300 μm or thinner than 10 μm. As will be mentioned hereinunder, the thickness of the
conductive foil 460 may be such that it accepts the formation of ashallow isolation trench 461 therein. - The
conductive foil sheet 460 may be prepared in the form of a roll having a predetermined width, for example, 45 mm, and this may be fed to each step. Alternatively, strips ofconductive foil 460 cut to have a predetermined size may be prepared and these may be fed to each step. - Concretely, four or five
blocks 462 are formed on aconductive foil strip 460, spaced from each other as inFIG. 42B . Each block shall have a large number of element-mounting parts to be formed therein. Aslit 463 is formed between the neighboringblocks 462, and this acts to absorb the stress of theconductive foil 460 in thermal treatment in the molding step, etc. Index holes 464 are formed at predetermined intervals in the upper and lower peripheries of theconductive foil 460, and these are for location in every step. - Next, a first
conductive pattern 451 is formed in every block. - As in
FIG. 43 , a photoresist (etching-resistant mask) PR is formed on theCu foil 460, and this is patterned to partly expose theconductive foil 460 except the region to be a firstconductive pattern 451. Next, as inFIG. 44A , theconductive foil 460 is selectively etched via the photoresist PR. - The depth of the
isolation trench 461 formed by the etching is, for example, from 20 to 30 μm, and the side wall thereof is roughened through oxidation or chemical polishing so as to increase its adhesiveness to thethermosetting resin layer 450A. - The side wall of the
isolation trench 461 is schematically drawn to be straight in the figures, but may have any other structure depending on the method of removing the photoresist for forming it. The method of photoresist removal includes wet etching, dry etching, laser evaporation and dicing. In wet etching, the etchant to be employed is essentially ferric chloride or cupric chloride, and the conductive foil is dipped in or showered with the etchant. In wet etching, in general, the conductive foil is etched non-anisotropically, and its etched side wall is therefore curved. - In dry etching, the conductive foil may be etched anisotropically or non-anisotropically. At present, it is said that Cu could not be removed through reactive ion etching, but it may be removed through sputtering. Depending on the condition of sputtering, Cu may be etched anisotropically or non-anisotropically.
- In laser evaporation, a laser ray may be directly applied to the conductive foil to form the
isolation trench 461. In this case, the side wall of theisolation trench 461 formed may be straight. -
FIG. 44B is a schematic view of the firstconductive pattern 451. This corresponds to an enlargement of oneblock 462 shown inFIG. 42B . One black section corresponds to one element-mountingpart 465, and the black sections constitute the firstconductive pattern 451. Oneblock 462 has a large number of element-mountingparts 465 that are aligned in a matrix of 5 lines and 10 rows, and the same firstconductive pattern 451 is formed for every element-mountingpart 465. Aframe pattern 466 is formed around every block, andregistration marks 467 for dicing are provided inside it, spaced in some degree from it. Theframe pattern 466 is for engagement of the patterned conductive foil with a mold, and after back etching of theconductive foil 460, it reinforces the insulatingresin 450B. - The second step of the invention is to form the
thermosetting resin layer 450A that covers theisolation trench 461 and the surface of the firstconductive pattern 451, as inFIG. 45 . - This step characterizes the invention, in which a thermosetting resin such as epoxy resin is used for the
thermosetting resin layer 450A, and this fills theisolation trench 461 and covers the surface of the firstconductive pattern 451. For forming thethermosetting resin layer 450A, a liquid material prepared by dissolving a thermosetting resin in an organic solvent is cast over theisolation trench 461 and the firstconductive pattern 451, heated at 80° C. to 100° C. to semi-cure it with evaporating away the organic solvent, and then further heated at 150° C. to 170° C. for about 1.5 hours to finally cure it. Accordingly, the semi-cured thermosetting resin is in B-stage, and it is not as yet finally set. - Preferably, a filler such as silica or alumina is added to the
thermosetting resin layer 450A to reduce the thermal expansion difference between thelayer 450A and the firstconductive pattern 451. In general, the thermal expansion coefficient of epoxy resin is 50 ppm/° C.; that of epoxy resin containing the filler is from 15 to 30 ppm/° C.; and that of copper to form theconductive pattern 451 is 18 ppm/° C. Therefore, the filler may remove the thermal expansion mismatch between epoxy resin and copper. - Since the thermosetting resin for the
layer 450A is filled into theisolation trench 461 while it is a liquid of low viscosity, it may well adhere to the inner walls of theisolation trench 461, as compared with epoxy resin to be transfer-molded, and the adhesion strength between the two may be increased significantly. The depth of theisolation trench 461 is about 60 μm for ensuring the necessary adhesion strength in the related art. However, since the adhesion strength in this embodiment is increased, the depth of theisolation trench 461 may be a half of it in the related art as above, concretely from 20 to 30 μm, and this produces an advantage in that the firstconductive pattern 451 may be a finer pattern. - Another method may be employed for forming the
thermosetting resin layer 450A, which comprises pressing a semi-cured film sheet of thermosetting resin such as epoxy resin against the firstconductive pattern 451 followed by finally curing it thereon under heat to thereby cover the firstconductive pattern 451 and fill theisolation trench 461 with the resin. The surface of the thermosetting resin film is covered with a cushion sheet, and pressed under 100 kg/cm2 under heat at 150° C. to 170° C., and the resin is finally cured while its melt covers theisolation trench 461 and the surface of the firstconductive pattern 451. - In this step, it is desirable to roughen the inner wall of the
isolation trench 461 for further enhancing the adhesion strength between theisolation trench 461 and thethermosetting resin layer 450A. For it, for example, the inner wall of theisolation trench 461 is oxidized or chemically polished with an organic acid etchant. For the organic acid etchant, for example, usable is Mec's CZ-8100. The patterned conductive foil is dipped in the etchant for a few minutes to roughen the surface thereof to a degree of from 1 to 2 μm or so. Through the treatment, the inner wall of theisolation trench 461 is roughened, and the adhesion strength between theisolation trench 461 and thethermosetting resin layer 450A is thereby increased. - In another embodiment of this step, a UV-curable resin may be used in place of the thermosetting resin for the
layer 450A. Concretely, a UV-curable resin is applied onto the patterned conductive foil, using a vacuum laminator, and then cured through exposure to UV rays and development to thereby form a cured UV resin layer that covers the desired surface of theisolation trench 461 and the firstconductive pattern 451. This embodiment simplifies the process since it covers the next third step. - The third step of the invention comprises exposing the surface of a predetermined area of the first
conductive pattern 451 by removing thethermosetting resin layer 450A thereon through laser etching, followed by applying a conductive plate film 474 thereto for forming a secondconductive pattern 471 thereon, as inFIG. 46 . - In this step, the
thermosetting resin layer 450A is partly selectively removed through laser etching for direct patterning to thereby partly expose the firstconductive pattern 451 with forming through-holes 473 therein. For the laser, carbon dioxide laser is preferred, but excimer laser and YAG laser may also be used. When the resin still remains on the bottom of the opening after its removal through laser evaporation, it is removed, for example, through wet etching with sodium permanganate or ammonium persulfate or through dry etching with excimer laser. - Next, a conductive plate film 474 is formed to cover the through-holes 474 and the surface of the
thermosetting resin layer 450A, as inFIG. 46 . - Concretely, a conductive plate film 474 is formed over the entire surface of the structure including the through-
holes 473 and thethermosetting resin layer 450A, with no mask. The conductive plate film 474 may be formed in any mode of electroless plating or electrolytic plating. In this case, it is formed through electroless plating with Cu to have a thickness of about 2 μm, and it covers the entire surface of the structure including the through-holes 473 and thethermosetting resin layer 450A. Accordingly, the conductive plate film 474 is electrically connected to the firstconductive pattern 451. Using the firstconductive pattern 451 formed of theconductive foil 460 as an electrode, this is further electrolytically plated with Cu to form thereon a Cu plate having a thickness of about 20 μm. As a result, the through-holes 473 are all filled with the conductive plate film 474. Cu is used for the conductive plate film 474, for which, however, any other of Au, Ag or Pd may also be used. As the case may be, the structure may be partly plated via a mask. - The fourth step of the invention comprises etching the conductive plate film 474 in a predetermined pattern to form the second
conductive pattern 471, as inFIG. 47 . - The conductive plate film 474 is coated with a photoresist layer of a predetermined pattern, and this is chemically etched to form the
conductive film 454 that is to be a bonding pad and the secondconductive pattern 471 that extends toward the center from the bonding pad. The conductive plate film 474 is formed of a material of essentially Cu, and the etchant for it may be ferric chloride or cupric chloride. - The thickness of the conductive plate film 474 is approximately from 5 to 20 μm. Therefore, its advantage is that the second
conductive pattern 471 may be a fine pattern of at most 20 μm. - The fifth step of the invention comprises forming a
conductive film 454 on the exposed secondconductive pattern 471, as inFIG. 48 . - The second
conductive pattern 471 is coated with an insulatingfilm 475 such as overcoating resin. For forming the insulatingfilm 475, for example, epoxy resin or the like dissolved in a solvent may be applied to the structure by screen-printing and then thermally cured. Alternatively, a photo-solder resist may be used for the insulatingfilm 475, and it may be partly left through exposure and development. - Next, the second
conductive pattern 471 is masked with a photoresist layer except the part thereof to be a bonding pad, and the insulating film 474 is selectively removed through laser etching whereby the secondconductive pattern 471 is selectively exposed out. For the laser, carbon dioxide laser is preferred, but excimer layer and YAG laser may also be used. When the insulating resin still remains on the bottom of the opening after its removal through laser evaporation, it is removed, for example, through wet etching with sodium permanganate or ammonium persulfate or through dry etching with excimer laser. - The remaining insulating
film 475 serves as a mask, and theconductive film 454 is plated with any of gold, silver or palladium by electrolytic plating or electroless plating. Thus plated, it may serve as a bonding pad. - For example, a silver film adheres to gold wires and to solder. In addition, fine Au wires may adhere to such a conductive film of silver. Therefore, the conductive film 554 accepts wire bonding, and its one advantage is that the film may serve directly as a bonding pad.
- The sixth step of the invention comprises fixing a
circuit element 452 onto the insulatingfilm 457 in the element-mountingpart 465 thereof with a conductive or insulatingadhesive 458, and forming a connecting means for electrically connecting the electrode of thecircuit element 452 in the element-mountingpart 465 to a desired part of the secondconductive pattern 471, as inFIG. 49B . - The
circuit element 452 includes semiconductor elements such as transistors, diodes, IC chips. Though thick, face-down semiconductor elements such as CSP or BGA may also be mounted on the structure. Multiple IC chips may be piled up or may be arrayed in plane to constitute thecircuit element 452. - In the illustrated embodiment, a
bare IC chip 452 is fixed onto insulatingfilm 457 with an insulatingadhesive 458 such as epoxy resin, and the electrodes of theIC chip 452 are connected to the correspondingconductive films 454 formed on the secondconductive pattern 471 around the element-mountingpart 465, via abonding wire 455 bonded to the two by thermal ball bonding or ultrasonic wedge bonding. - A large number of second
conductive patterns 471 are integrated in everyblock 462. Therefore, the advantage of this step is that thecircuit elements 452 may be efficiently mounted on the second conductive patterns through physical fixation and wire bonding. - The seventh step of the invention comprises common-molding the
circuit elements 452 on the element-mountingparts 463 with an insulatingresin 450B that collectively covers the elements and bonds to thethermosetting resin layer 450A filled in theisolation trench 461, as inFIG. 50 . - The
isolation trench 461 and the multipleconductive patterns 451 are covered with thethermosetting resin layer 450A in the previous step, and the insulatingresin 450B covers thecircuit element 452 and bonds to thethermosetting resin layer 450A remaining in theisolation trench 461 and on the surface of the firstconductive pattern 451, as inFIG. 50A . The insulatingresin 475 exists between thethermosetting resin layer 450A and the insulatingresin 450B, but this is extremely thin and is formed of epoxy resin, a type of thermosetting resin. Therefore, they are well compatible with each other and produce a strong adhesion strength. For further enhancing the adhesion strength, it is desirable that the surface of the insulatingfilm 475 is subject to UV irradiation or plasma irradiation to activate the polar group of the resin in the surface of the insulatingfilm 475 prior to the molding treatment with the insulatingresin 450B. As a result, thethermosetting resin layer 450A is integrated with the insulatingresin 450B to more firmly support the firstconductive pattern 451. - In this step, when direct bonding between the
thermosetting resin layer 450A and the insulatingresin 450B is desired, it is preferable that the part of the insulatingfilm 475 not having the secondconductive pattern 471 therein is removed in the treatment of etching the insulatingfilm 475 in the previous step. - The treatment of this step may be realized by transfer molding, injection molding or dipping. Regarding the type of the resin material, thermosetting resin such as epoxy resin may be transfer-molded; and thermoplastic resin such as polyimide resin or polyphenylene sulfide may be injection-molded.
- In this step of transfer molding or injection molding, the element-mounting
parts 463 in oneblock 462 are all put in one common mold, and they are common-molded with one insulatingresin 450B, as inFIG. 50B . In this step, therefore, the amount of the resin to be used may be reduced significantly, as compared with that in conventional transfer molding, and common molds may be used. - The thickness of the insulating
resin 450B that covers the surface of theconductive foil 460 is so controlled that it is about 100 μm or so from the top of thecircuit element 452. This thickness may be increased or decreased in consideration of the mechanical strength of the resin layer. - This step is characterized in that the
conductive foil 460 to form the firstconductive pattern 451 serves as a supporting board before it is coated with the insulatingresin 450B. In the related art technology, theconductive paths 507 to 511 are formed by the use of the supportingboard 505 that is naturally unnecessary, as inFIG. 10 . In the invention, however, theconductive foil 460 that serves as the supporting board is a material necessary for electrodes. Accordingly, the invention is advantageous in that the necessary constitutive materials may be reduced to the minimum and the production costs are therefore reduced. - Since the depth of the
isolation trench 461 does not exceed the thickness of theconductive foil 460, the firstconductive pattern 451 of theconductive foil 460 is not individually separated. Accordingly, theconductive foil 460 can be handled as one sheet as a whole, and when it is molded with the insulatingresin 450B, it may be readily transferred and put into a mold. - The seventh step of the invention comprises removing the
conductive foil 460 in the thickness part not having theisolation trench 461 formed therein, as inFIG. 50A . - In this step, the back of the
conductive foil 460 is chemically and/or physically removed to individually separate theconductive pattern 451. This may be carried out, for example, through polishing, cutting, etching or metal evaporation with laser. - In one example of this process, the entire back of the
conductive foil 460 is cut with a polishing machine or a cutting machine to a depth of about 100 μm or so, whereby thethermosetting resin layer 450A is exposed out of theisolation trench 461. The face to be exposed out through the treatment is represented by the dotted line inFIG. 50A . As a result, the firstconductive pattern 451 is individually separated to have a thickness of about 30 μm. Apart from it, the entire back of theconductive foil 460 maybe wet-etched before thethermosetting resin layer 450A is exposed out, and then it may be cut with a polishing or cutting machine so that thethermosetting resin layer 450A is exposed out. In still another embodiment, the entire back of theconductive foil 460 may be wet-etched to the depth of the dotted line whereby thethermosetting resin layer 450A may also be exposed out. - In the structure thus processed, the back of the first
conductive pattern 451 is exposed out of thethermosetting resin layer 450A. Specifically, the face of thethermosetting resin layer 450A filled in theisolation trench 461 is substantially on the same level as that of the firstconductive pattern 451. Accordingly, thecircuit device 453 of the invention does not have a difference in level for theback electrodes FIG. 12 that indicates a related art technology, and this is characterized in that, when other elements are mounted thereon, it accepts horizontal movement for self-alignment based on the surface tension of solder or the like. - Further, the back of the first
conductive pattern 451 is processed to obtain the final structure as inFIG. 40 . Concretely, a part of the firstconductive pattern 451 to form electrodes is selectively exposed out while the other part thereof is coated with a resistlayer 457, and a conductive material such as solder is applied to it to form backelectrodes 456, thereby completing a final circuit device. - The eighth to tenth steps of this mode are the same as those of the fourth mode described hereinabove.
-
FIG. 51 is referred to, which shows an embodied circuit device of the invention. In this, the pattern indicated by solid lines is the secondconductive pattern 471, and the pattern indicated by dotted lines are the firstconductive pattern 451. The secondconductive pattern 471 is worked to form theconductive film 454 that serves as a bonding pad around thebare semiconductor chip 452. This partly has a two-layered structure, corresponding to thebare semiconductor chip 452 with multiple pads therearound. The bonding pad is connected to thecorresponding electrode pad 475 of thebare semiconductor chip 452 via thebonding wire 455. Many fine patterns, secondconductive patterns 471 extend from the bonding pad to the area below thebare semiconductor chip 452, and these are connected to the firstconductive pattern 451 through the through-holes 473 shown by black spots. - Having the constitution, even a semiconductor circuit device having 200 or more pads may be connected to the desired first conductive pattern via the fine patterns, second
conductive patterns 471, by multi-layered wiring connection, and theback electrode 456 fitted to the first conductive pattern may be connected to other external circuits. InFIG. 51 , thethermosetting resin layer 450A and the insulatingresin 450B are omitted for simplifying the description.
Claims (17)
1. A circuit device comprising:
plurality of conductive patterns for element mounting thereon and electrically separated from each other by a isolation trench;
a thermosetting resin layer filling the isolation trench to cover at least a part of the surface of the conductive pattern;
a circuit element fixed above the conductive pattern; and
an insulating resin covering the circuit element to integrally support the conductive pattern bonded to the thermosetting resin layer.
2. The circuit device as claimed in claim 1 , wherein the thermosetting resin layer is provided between the circuit element and the conductive pattern.
3. The circuit device as claimed in claim 1 , wherein the back of the conductive pattern is exposed out to form external electrodes.
4. The circuit device as claimed in claim 1 , wherein the circuit element is fixed on a desired region of the conductive pattern exposed from the thermosetting resin layer.
5. The circuit device as claimed in claim 1 , further comprising:
a second conductive pattern formed on the thermosetting resin layer and connected to the conductive pattern at desired sites;
wherein the circuit element is fixed on the second conductive pattern while insulated from the second conductive pattern; and
wherein the insulating resin integrally supports the conductive pattern and the second conductive pattern.
6. The circuit device as claimed in claim 1 , wherein the insulating resin covers the circuit element and bonds to the thermosetting resin layer to integrally support the conductive pattern with the back alone of the conductive pattern being exposed out.
7. The circuit device as claimed in claim 1 , further comprising a connecting means for connecting the electrodes of the circuit element to the other conductive pattern.
8. The circuit device as claimed in claim 1 , wherein the conductive pattern is formed of conductive foil of any of copper, aluminum or iron-nickel.
9. The circuit device as claimed in claim 1 , wherein a conductive film of a metal material that differs from the material of the conductive pattern is provided on a desired region of the conductive pattern exposed from the thermosetting resin layer.
10. The circuit device as claimed in claim 9 , wherein the conductive film is formed of a plating layer of gold, silver or palladium.
11. The circuit device as claimed in claim 1 , wherein the circuit element comprises either one or both of a bare semiconductor chip and a chip circuit part.
12. The circuit device as claimed in claim 7 , wherein the connecting means is formed of a bonding wire.
13. The circuit device as claimed in claim 1 , wherein the back of the conductive pattern and the back of the thermosetting resin layer that fills the isolation trench are substantially flattened.
14. The circuit device as claimed in claim 1 , wherein the conductive pattern is used for electrodes and bonding pads.
15-34. (canceled)
35. A circuit device comprising:
multiple conductive pattern for element mounting thereon;
a circuit element fixed above at least a part of the conductive pattern;
a conductive adhesion means for connecting the conductive pattern to the circuit element and adhering the conductive pattern and the circuit element;
an insulating resin that covers the circuit element to integrally support the conductive pattern and the circuit element.
36. A method for manufacturing circuit devices, comprising the step of:
preparing conductive foil;
forming multiple conductive pattern for element mounting thereon;
fixing a circuit element to at least a part of the conductive pattern via a conductive adhesion means electrically connecting the two and adhering the two; and
providing an insulating resin to seal the circuit element and the conductive pattern.