US20040255805A1 - Method of manufacturing a printing substrate - Google Patents
Method of manufacturing a printing substrate Download PDFInfo
- Publication number
- US20040255805A1 US20040255805A1 US10/895,768 US89576804A US2004255805A1 US 20040255805 A1 US20040255805 A1 US 20040255805A1 US 89576804 A US89576804 A US 89576804A US 2004255805 A1 US2004255805 A1 US 2004255805A1
- Authority
- US
- United States
- Prior art keywords
- substrate
- layer
- porcelain enamel
- inorganic ceramic
- subraster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An optical scanning system and method for laser engraving a plurality of data subrasters into a substrate to form a raster of engraved data defining an image on the substrate. Each subraster has a length dimension and a width dimension. The system includes a transport assembly having an objective lens and a mirror, the mirror capable of reflecting a substantially collimated scanning beam incident thereon in a direction transverse to an axis of the incident beam such that it is directed to the objective lens. The objective lens is capable of focusing the scanning beam on the substrate to engrave a set of data in the width dimension of the subraster and the objective lens and mirror combination is capable of moving along the axis of the incident beam to allow subsequent engraving of other sets of data in the width dimension until a complete subraster is formed along its length dimension. The objective lens and mirror combination is also capable of returning to its starting position to begin engraving of a subsequent subraster of the plurality of subrasters forming the raster of engraved data. A thermoset plastic substrate and a substrate having a an inorganic ceramic material are also identified as being suitable for use in a printing process, and particularly suitable for use with the aforementioned system and method.
Description
- This application is a continuation-in-part of U.S. patent application Ser. No. 10/159,492, filed May 31, 2002, upon which a claim of priority is based.
- This invention relates to direct laser engraving of a flat substrate for use in a printing process, such as intaglio printing. More particularly, the invention relates to an optical scanning system and substrate material particularly suitable for high-speed and high-resolution engraving.
- Many printing processes utilize substrates, platens or forms as printing surfaces to transfer an image to a printable medium. One such process is called intaglio printing. Intaglio printing involves application of printed indicia or images below the surface of a platen or substrate that is utilized as a printing surface. Traditionally, intaglio substrates have been prepared by mechanically engraving or chemically etching a recessed pattern into the printing surface of the substrate, which defines an image. The pattern may comprise an array of dots in the printing surface of the substrate. The recessed pattern, such as the array of dots, define tiny recesses within which ink is held and transferred to the printable medium, such as a sheet or surface. This intaglio process is typically used in die stamping or in engraved processes, sometimes referred to as copper plate printing. It is also used in connection with pad printing, which is typically used to decorate plastic surfaces, as well as in the gravure printing process.
- Mechanical engraving and chemical etching techniques are time-consuming processes. Mechanical techniques are typically slow due to limitations of engraving equipment. A mechanical stylus must be used to engrave the image into the substrate, which requires a certain amount of time to penetrate and cut the substrate material. Furthermore, accuracy of the engraving becomes an issue when the stylus becomes worn and dull. On the other hand, chemical etching is time consuming due to the many steps involved. Chemical etching is a multi-step process that first involves producing the image onto a film negative, such as with an imagesetter. Once the film is produced, it becomes a mask that can be laid on top of a copper or steel substrate having a thin film coating of sensitizing material. The substrate and mask combination is exposed to light for subsequent chemical development, which transfers the mask to the copper plate. After development, the substrate is ready for acid etching to complete the process. Accuracy is also an issue with chemical etching, due to the limited controllability of the chemical-etching process.
- Another technique involves direct laser etching, which is a single-step process that requires much less time than mechanical engraving and chemical etching techniques. In this technique, a laser is used to directly engrave the substrate material. However, because metals have a high reflectance, the laser/metal interaction is not conducive to producing plates having sharp engravings. With metals and a majority of plastics, direct laser engraving causes the material to melt, which creates the recessed areas, but also creates pooling of melted material around these recessed areas. This pooling of material acts as a ridge surrounding the recessed areas, which adversely affects the accuracy and usefulness of the printing surface of the substrate. Thus, accuracy remains an issue. Furthermore, although the direct laser technique is only a single-step process, the speed of the engraving process still remains an issue at higher resolution levels, which require the laser to engrave a higher number of tightly focused dots to achieve such resolutions. With presently known systems, the engraving process time is increased when the resolution level is increased.
- The system and method of the present invention addresses these and other problems associated with direct laser engraving of substrates.
- An optical scanning system for laser engraving a plurality of data subrasters into a substrate to form a raster of engraved data defining an image on the substrate. Each subraster has a length dimension and a width dimension. The system includes a transport assembly having an objective lens and a mirror, the mirror capable of reflecting a substantially collimated scanning beam incident thereon in a direction transverse to an axis of the incident beam such that it is directed to the objective lens. The objective lens is capable of focusing the scanning beam on the substrate to engrave a set of data in the width dimension of the subraster and the objective lens and mirror combination is capable of moving along the axis of the incident beam to allow subsequent engraving of other sets of data in the width dimension until a complete subraster is formed along its length dimension. The objective lens and mirror combination is also capable of returning to its starting position to begin engraving of a subsequent subraster of the plurality of subrasters forming the raster of engraved data.
- In a particular embodiment, an optical scanning system for laser engraving of a plurality of subrasters of data into a substrate to form a raster of engraved data is provided and includes a scanner capable of deflecting an input laser beam incident thereon from a first beam direction to create a scanning beam. The system also includes a beam expander capable of receiving the scanning beam and expanding it to create an expanded scanning beam. A transport assembly of the system has an objective lens and a mirror, wherein the mirror is capable of reflecting the expanded scanning beam in a second beam direction transverse to the first beam direction such that it is incident on the objective lens. The objective lens and mirror is capable of moving along an axis defined by the first beam direction. The objective lens is capable of focusing the expanded scanning beam on the substrate to engrave a set of data oriented in a width dimension of the subraster and is also capable of moving along the first beam axis to allow subsequent engraving of other sets of data oriented in the width dimension until a complete subraster is formed to define a length dimension of the subraster. The objective lens and mirror combination is further capable of returning to its starting position to initiate engraving of a subsequent subraster.
- According to another aspect of the invention, an optical scanning system is provided that is capable of engraving at two different resolutions.
- According to another aspect of the invention, a substrate is provided for use with a direct laser engraving process to create an intaglio printing substrate. The substrate consists essentially of a thermoset plastic which substantially vaporizes in response to an impinging laser beam that engraves portions of the substrate, thereby substantially eliminating the formation of slag material adjacent to engraved portions of the substrate.
- According to another aspect of the invention, a substrate is provided for use with a direct laser engraving process to create a printing substrate, wherein the substrate comprises a base material and an inorganic ceramic material disposed on the base material.
- According to yet another aspect of the invention, methods of manufacturing such a substrate and methods for making such a substrate into a printing substrate in accordance with the principles of the present invention are provided.
- According to yet another aspect of the invention, a method of laser engraving a substrate for use in a printing process is provided. The method comprises the steps of: (a) directing a substantially collimated scanning beam having a beam axis to an objective lens that is movable along the beam axis, wherein the scanning beam defines a scan width; (b) focusing the scanning beam through the objective lens and onto the substrate; (c) engraving onto the substrate a set of subraster width data having a width equal to the scan width of the beam; (d) continuously moving the objective lens along the beam axis to subsequent positions relative to the substrate and engraving subsequent sets of subraster width data to form a complete subraster; (e) incrementing the substrate and engraving an additional subraster adjacent to the previously completed subraster; and (f) repeating the steps of incrementing the substrate and engraving an additional subraster until a complete raster made up of a plurality of subrasters is created that defines an engraved image on the substrate.
- These and other aspects of the invention will become apparent from the specification, drawings and claims.
- FIG. 1 is a schematic diagram of an embodiment of a direct laser engraving system in accordance with the present invention.
- FIG. 2 is a top plan view of a portion of the system of FIG. 1.
- FIG. 3 is a side elevational view of the portion of the system shown in FIG. 2
- FIG. 4 is a detailed top plan view of the scanner and first lens of the beam expander shown in FIG. 2.
- FIG. 5 is a schematic diagram of a byte and bit layout of a sampling of data sets of a subraster in a
sample 1200 dpi scan in accordance with the principles of the present invention. - FIG. 6 is a functional block diagram of data handling of the system of FIG. 1.
- FIG. 7 is a schematic diagram of an embodiment of a substrate in accordance with a particular aspect of the present invention.
- While this invention is susceptible of embodiments in many different forms, there is shown in the drawings and will herein be described in detail one or more preferred embodiments of the invention with the understanding that the present disclosure is to be considered as an exemplification of the principles of the invention and is not intended to limit the broad aspect of the invention to the embodiments illustrated.
- FIG. 1 depicts a schematic diagram of an embodiment of an
optical scanning system 10 in accordance with the principles of the present invention. Thesystem 10 can be utilized for laser engraving a substrate for use in a printing process. A particular feature of thesystem 10 is the ability to engrave at two different resolutions with the same optical system. In a preferred embodiment, thesystem 10 is capable of engraving at 1200 dpi and 2400 dpi. Referring to FIG. 1, thesystem 10 includes apolygon scanner 20, abeam expander 22 and a transport (or trolley)assembly 24. Areceptor assembly 26 is disposed adjacent to thetransport assembly 24 and supports the substrate to be engraved. Thereceptor assembly 26 is capable of incrementally translating the substrate with respect to thetransport assembly 24 via a stepped transport. As will be discussed in more detail below, thetransport assembly 24 includes amirror 27 and anobjective lens 28 that are also movable to facilitate the engraving process. - The
system 10 requires aninput beam 30. Alaser assembly 31 is provided to produce theinput beam 30, which is incident on thescanner 20 from a first beam direction. Thelaser assembly 31 includes a laser 32 (preferably a DC excited CO2 laser), abeam compressor 34 and amodulator 36 driven by amodulator driver 38. Referring to FIG. 1, thelaser 32 produces a beam 40 (having a beam width A) that is shaped by thebeam compressor 34 to produce a compressed beam 41 (having a beam width B). Thecompressed beam 41 is modulated by themodulator 36 to produce the input beam 30 (having a beam width C). Preferably, the beam width A of thebeam 40 is 8mm, the beam width B of the compressedbeam 41 is 1 mm, and the beam width C of the input beam is 1 mm. Theinput beam 30 is scanned by thescanner 20 to produce ascanning beam 42, which is directed to thebeam expander 22. As will be explained in more detail below, thebeam expander 22 produces a substantially collimated expanded scanning beam 50 (having a beam width D), which is directed to themirror 27 andobjective lens 28 combination of thetransport assembly 24. Themirror 27 reflects thebeam 50 to theobjective lens 28, which focuses the beam onto the substrate. Preferably, the beam width D of the expandedscanning beam 50 is 20 mm and themirror 27 is angled at 45 degrees. Essentially, thebeam expander 22 expands thescanning beam 42 and relays it to create the expandedscanning beam 50, which has a substantially constant width over an extended distance. - FIGS. 2 and 3 depict the
system 10 in more detail. FIG. 2 is a top plan view of thesystem 10 and FIG. 3 is a side view of FIG. 2. In a preferred embodiment, thescanner 20 is a polygon scanner having 15 facets and is rotatable in a direction indicated by rotational arrows in FIGS. 2 and 3. In a preferred embodiment, the scanner rotates at either 10,000 rpm or 20,000 rpm, depending on desired resolution. Considering thescanner 20 as a nutating mirror executing ±10° mechanical deflection of theinput beam 30, theinput beam 30 is deflected ±20° due to mirror doubling to produce thescanning beam 42. As shown in FIGS. 2 and 3, thebeam expander 22 includes a first lens L1 and a second lens L2. Referring to the detailed view of thescanner 20 and the first lens L1 of thebeam expander 22 in FIG. 4, thescanning beam 42, which is a substantially collimated beam having a beam width C and deflected ±20°, is directed to be incident on lens L1. In a preferred embodiment, lens L1 has a focal length of 15 mm. The lens L1 is located one focal length f1 from the scanner surface and acts telecentrically such that the ±20° beams continue to the right of the lens L1 and remain substantially parallel to alens axis 60, while deflected components of the beams converge to afocal plane 64 one focal length f1 beyond the lens L1. Referring to FIG. 2, beyond thefocal plane 64, anupper limit beam 66 and alower limit beam 68 of the deflected beam components expand. Referring to FIG. 3, thefocal plane 64 acts as a plane of beam symmetry, as shown in FIG. 3. - The
upper limit beam 66 and thelower limit beam 68 expand until they reach a second lens L2, which is spaced a focal length f2 from thefocal plane 64 of the first lens L1. In a preferred embodiment, the focal length f2 is 300 mm. Utilizing the preferred pair of lenses L1 (15 mm focal length) and L2 (300 mm focal length), thebeam expander 22 acts as a 20× beam expander (300/15=20). Thus, thebeam expander 22 in the preferred embodiment expands the 1mm input beam to a substantially collimated 20mm output beam. A fundamental consequence of beam expansion is a complimentary compression of scan angle of the beam (in the preferred embodiment, compression from ±20° to ±1°). This reduction in scan angle imparts a practical field angle to theobjective lens 28. - Another consequence of this configuration in the preferred embodiment is the relaying of a1mm beam aperture at the
scanner 20 to a 20 mm beam aperture at the 300 mm focal distance of lens L2. Thus, as shown in FIG. 2, although the beams shift laterally (due to deflection) in the long region between thescanner 20 and theobjective lens 28, the beam shift reduces to zero at a distance E beyond lens L2 (300 mm in a preferred embodiment). In other words, the stability of the 1 mm beam at the scanner 20 (scanning beam 42) is transferred as a stable 20 mm beam (expanded scanning beam 50) at theobjective lens 28. As explained in more detail below, in a preferred embodiment, the 300 mm distance is a nominal beam travel length for theobjective lens 28 with respect to its movement on thetransport assembly 24 along a beam axis 70 of the expandedscanning beam 50. - Referring again to FIGS. 2 and 3, the
transport assembly 24 facilitates movement of themirror 27 and theobjective lens 28 along the beam axis 70 of the expandedbeam 50. Themirror 27 and theobjective lens 28 combination are movable within thetransport assembly 24 in both directions for a distance F along the beam axis from the nominal position, for a total travel of 2F. In a preferred embodiment, thetransport assembly 24 facilitates movement of themirror 27 and theobjective lens 28 for 4 inches (F=4 inches) in each direction for a total range of travel of 8 inches (2F), which corresponds to a dimension of an image format size, which is 8″×10″ in a preferred embodiment. Of course, other format sizes could be accommodated through adjustment of the system in accordance with the principles of the present invention. - Referring to FIG. 3, the expanded
scanning beam 50 is intercepted by themirror 27 and reflected, thereby folding thebeam 50 so that it is incident on aprincipal plane 80 of theobjective lens 28. Thebeam 50 is intercepted by themirror 27 at a nominal position of G, folding the remaining length (E-G) to complete the nominal distance E (300 mm in a preferred embodiment) to theprincipal plane 80 of theobjective lens 28. At theobjective lens 28, the beam width of beam 50 (20 mm in a preferred embodiment) is converged over a focal distance (f3) of thelens 28 to an energetic focal point to engrave the surface of the substrate material. Thetransport assembly 24 transports themirror 27 and theobjective lens 28 over a dimension of the format size (2F). For simplicity of illustration, the limit positions of themirror 27 and theobjective lens 28 are represented in FIG. 3 by the two mirrors shown in phantom lines. It is understood that themirror 27 and theobjective lens 28 move in combination. - Referring to the right side of FIG. 2, it is noteworthy that with a collimated beam incident on the
objective lens 28, even though the beam position in the aperture of thelens 28 shifts slightly during transport, the fundamental criterion for accurate placement of the engraving focal point, which is the angle of the collimated beam with respect to the lens axis, remains a constant of the system. As explained below, this establishes uniformity of a width dimension of each of a plurality of subrasters of data engraved to form, in combination, an engraved image. - The present invention utilizes a method of engraving the substrate wherein a plurality of data subrasters are engraved to form individual swaths, which, in combination form a complete raster of data representing an image to be engraved. Referring to the schematic diagram of FIG. 5, a byte and bit layout of a sampling of
data sets 102 of a subraster in asample 1200 dpi scan is shown in accordance with the principles of the present invention. Each data bit of the data sets 102 represents a point, or dot, of the image to be engraved. As shown in FIG. 5, eachsubraster 104 comprises a plurality of data sets in a width dimension of the subraster. In the 1200 dpi resolution example, eachdata set 102 comprises 40 dots across the width dimension of the subraster (5 sets of 8 dots). In a 2400 dpi example (not shown), each data set comprises 80 dots across the width dimension of the subraster (10 sets of 8 dots). The expandedscanning beam 50 engraves each data set across the subraster width as thetransport assembly 24 moves themirror 27 andobjective lens 28 combination in a direction along the length dimension of the subraster 104 (denoted by X in FIG. 5) until thesubraster 104 is completed. The objective lens and mirror combination returns to its starting position and thereceptor assembly 26 incrementally translates the substrate in a direction along the width dimension of the subraster 104 (denoted by Y in FIG. 5) to initiate engraving of a subsequent subraster. The translation increment is equal to the width dimension of thesubraster 104. In a preferred embodiment, the width dimension of each subraster is about 33.3 mils and a total of 300 subrasters are utilized to form the raster. Although the movement of the objective lens and mirror combination is described herein in various phases or steps of the engraving process, it is understood that movement of these components is continuous throughout the engraving process. Table 1 below shows the data point content for both 1200 dpi and 2400 dpi images in an 8′×10′ image format.TABLE 1 Operational Data Point Content for 8″ × 10″ Image Format Each Data Subraster Data Data Total Data Points Per Total Data Points Resolution Points Sets Subraster 300 Subrasters 1200 dpi 40 9,600 384,000 115,200,000 2400 dpi 80 19,200 1,536,000 460,800,000 - During engraving, the
laser 32 remains on. Instead of turning thelaser 32 on and off, themodulator 36 shifts thebeam 30 to a position analogous to ON. An unshifted beam position is analogous to OFF. During engraving, this shift happens at a very high rate. In the OFF position, thebeam 30 exits themodulator 36, strikes a dump mirror (not shown), and deflects into a beam dump (not shown) to absorb unwanted laser power. When themodulator 36 shifts thebeam 30 in an ON position, the shiftedbeam 30 bypasses the dump mirror and impinges on thescanner 20. Based on these ON and OFF positions, each data point or dot can represent an engraved point (ON) or an unengraved point (OFF) on the surface of the substrate. - FIG. 6 depicts a functional block diagram of data handling of the system. As shown in FIG. 6, a
master clock 200 operates at 480 kHz, which is the data rate for 2400 dpi resolution. Themaster clock 200 is stepped down to 120 kHz for 1200 dpi resolution. The data rate clocks clock anX-Y transport logic 210, which in turn drives an X-Y transport controller 212 for the transport assembly 24 (which moves themirror 27 andobjective lens 28 in the X-direction) and the receptor assembly 26 (which incrementally translates the substrate in the Y-direction). The data rate clocks also clock amodulation logic 310, which in turn operates themodulator driver 38 that drives themodulator 36. Themaster clock 200 is stepped down further to provide a motor control, as shown in FIG. 6. Thescanner 20 rotates at either 10,000 rpm (1200 dpi) or 20,000 rpm (2400 dpi). A motor controller 410 is clocked at 6 kHz for 20,000 rpm and 3 kHz for 10,000 rpm to control amotor 412 that drives thescanner 20. An encoder signal is provided back to the motor controller from thescanner 20. S.O.S (Start of Scan) pulses from thescanner 20 and are fed to themodulation logic 310 and theX-Y transport logic 210. Each S.O.S. pulse initiates the first data point of each data set in the width dimension of the subrasters. Each S.O.S pulse also triggers the modulation sequence for each data set. - As already mentioned, a particular advantage of the
system 10 is its ability to provide two different resolutions with the same optical system (1200 dpi and 2400 dpi in a preferred embodiment). This is accomplished by narrowing the modulation pulse width at 2400 dpi to half of the modulation pulse width at 1200 dpi, while doubling its repetition rate, which doubles the dot count along the subraster width from 40 to 80. Correspondingly, the motor speed of the scanner is doubled from 10,000 rpm to 20,000 rpm, which provides a full double-resolution dot array (data set) across the width dimension of the subraster. The modulation pulse width is narrowed by reducing the intensity of the beam. Since the dots are formed by a Gaussian focused beam contour, reducing the pulse duration by one half reduces the dot exposure (intensity) on the substrate, which, in turn, sufficiently reduces the dot width to facilitate the double-resolution engraving. The repetition rate of the modulation pulse width is changed via software control. Since the exposure (intensity) is reduced at the 2400 dpi resolution, the total energy remains the same as that at 1200 dpi resolution. Since the total energy is the same, the total engraving duration is the same. Thus, the system is capable of doubling its engraving resolution without increasing engraving time. - From the foregoing description, it is apparent that changing the resolution of the system is rapidly accomplished without the need for critical mechanical changes, such as changing the objective lens to focus to a smaller dot size, which can be very costly. Furthermore, two different resolutions can be engraved with the same optical system, which creates the same subraster format to cover the same total area during the same total time, and the same laser providing the same optical power.
- As yet another aspect of the present invention, it has been found that the use of a thermoset plastic material as the substrate substantially eliminates unwanted slag formation around the engraved points of the substrate. The thermoset plastic material substantially vaporizes in response to the impinging laser beam that engraves points of the substrate, thereby substantially eliminating the formation of the slag material. Desirable results have been achieved by including a mineral filler with the thermoset material. Preferably, the mineral filler has a grain size smaller than a smallest feature of the engraved portions of the substrate. Preferably, the grain size is in the range of about 3 to 5 microns. However, the grain size can be varied to match a particular resolution. The filler adds strength to the substrate material, thereby maintaining the accuracy and detail of the engraved portions of the substrate. In a preferred embodiment, silica is utilized as a filler for the thermoset material. Additionally, a flame retardant can be included to minimize flame and smoke formation from the impinging laser beam.
- Thermoset plastics provide for more accurate laser engraving due, in part, to their strength and resistance to flow. The polymer component consists of molecules with permanent cross-links between linear chains that form a rigid three-dimensional network structure which cannot flow. The tightly cross-linked structure of thermosetting polymers immobilizes the molecules, providing hardness, strength at relatively high temperature, insolubility, good heat and chemical resistance, and resistance to creep. The use of a thermoset plastic material for a substrate has a significant impact on the cost of printing processes that utilize such substrates. Thermoset plastic substrates are much less expensive than copper or steel substrates and they do not sacrifice engraving accuracy, and hence, printing accuracy.
- It is contemplated that a variety of thermoset plastic materials can be utilized in accordance with the principles of the present invention. Such materials include epoxies, unsaturated polyesters, phenolics, amino resins (such as urea- and melamine-formaldehyde), alkyds, allyl family (such as diallyphthalate), silicone molding compounds, and polyimides (such as bimaleimides).
- In cases where durability is a priority, it has further been found that a substrate having an inorganic ceramic material is suitable for a printing process, and particularly suitable for use in the system and process described herein. In an embodiment as shown in FIG. 7, a
substrate 400 comprises abase material 402 and an inorganicceramic material 404 disposed on, and preferably bonded to, thebase material 402. Preferably, thebase material 402 comprises a metal, such as, for example, steel, aluminum, copper, iron or any other metal suitable for use in a printing substrate. Theceramic material 404 provides a surface for formation of an image to be printed to a medium during a printing process. It is to be understood that other additional materials or layers may be incorporated into thesubstrate 400, with theceramic material 404 providing the printing surface. - An inorganic ceramic material component, layer or coating of a printing substrate provides excellent resistance to abrasion encountered during the printing process. Among other things, ink ingredients used in printing processes can cause wear to the substrate. The ceramic material of the substrate is more resistant to abrasion than the thermoset substrates, while offering excellent engraving accuracy. The substrate incorporating the inorganic ceramic material provides an excellent alternative to the thermoset substrates. It has been found that an inorganic ceramic material that is vitreous in nature offers particularly excellent resistance to abrasion and is particularly suitable for use in a printing substrate.
- By way of background and example, a particular inorganic ceramic material for use in a substrate for a printing process will now be described with the understanding that the particular example is but one embodiment of many as understood by one of ordinary skill in the art that can be utilized in accordance with the principles of the present invention. In this particular example, the inorganic ceramic material is in the form of a porcelain enamel disposed on a metallic substrate, such as a steel or iron substrate. Porcelain enamels for steel and iron substrates are typically classified as either ground-coat or cover-coat enamels. Ground-coat enamels contain metallic oxides, such as cobalt oxide and/or nickel oxide, that promote adherence of the glass/enamel to the metal substrate. Cover-coat enamels are applied over fired ground coats to improve the properties of the coating. In addition, cover-coat enamels may be applied over unfired ground coats, with both coats being fired at the same time. This is referred to as a two-coat/one-fire system. Cover coats may also be applied directly to properly prepared decarburized steel substrates. Porcelain enamels for aluminum substrates are typically one-coat systems that are applied by spraying. However, two-coat systems can also be utilized. It should be understood, however, that any number of application systems, alone or in combination, can be utilized on various substrate materials to achieve a porcelain-coated substrate.
- The basic material of the porcelain enamel coating is called frit, which is a smelted complex borosilicate glass. Frits are produced by quenching a molten glassy mixture that is compounded from numerous components, sometimes more than 20 different components, depending upon the application. Thus, the composition of the frit can be customized and optimized to exhibit certain desired properties for a particular application. As already mentioned, in cases where increased adherence to a steel substrate is desired, for example, cobalt oxide and/or nickel oxide may be included in the frit. In accordance with the principles of the present invention, the frit can be optimized for properties conducive to use as a printing substrate, including, but not limited to, hardness, abrasion resistance, strength at relatively high temperature, heat and chemical resistance, etc. Examples of oxide components that may be utilized include, but are not limited to, SiO2, B2O3, Na2O, K2O, Li2O, CaO, ZnO, Al2O3, ZrO2, TiO2, CuO, MnO2, NiO, Co3O4, P2O5, MgO, PbO, Sb2O3, Sb2O5, ZrO2, BaO and F2. Additives may be added to the frit to further influence various properties of the enamel, such as clay, bentonite, electrolytes, fluxes, and coloring oxides.
- In a preferred embodiment, the porcelain enamel has a low glass content, i.e., less than 50% by weight, preferably in the range of 35-40% by weight. However, other percentages can also be utilized, as long as the glass content is not too low, which weakens the enamel. Typical porcelain enamels have a glass content between 50% and 60% by weight.
- The porcelain enamel may be applied to the substrate by either a wet process or a dry process. Wet process methods include manual spraying, electrostatic spraying, dipping, flow coating, and electrodeposition (electrophoresis). Dry process methods include electrostatic dry powder spraying and sprinkling onto a heated substrate. In a preferred embodiment, the porcelain enamel is applied electrostatically.
- Since subsurface abrasion resistance varies with processing variables that affect the bubble structure of the enamel (i.e., gas bubbles that get trapped in the enamel during cooling), it is preferable that gas bubbles are minimized. Enamel compositions may contain crystalline particles (from mill additions or devitrification heat treatment) that can increase abrasion resistance by as much as 50%. In a preferred embodiment, calcium carbonate is included as a filler additive, which increases abrasion resistance.
- It should be understood that any inorganic ceramic material can be utilized in accordance with the principles of the present invention. However, it is preferable to utilize a porcelain enamel, particularly one having low glass content and exhibiting excellent abrasion resistance.
- While some substrate materials—such as thermoset plastics—can accommodate and take advantage of the faster engraving speeds and fast trolley return speeds associated with the
system 10 depicted in FIGS. 1-6 (wherein only the objective lens and the mirror are carried on the trolley assembly and moveable rapidly in the X direction while the substrate is stepped short distances moveable in the Y direction) other materials cannot be optimally engraved at higher speeds. In such cases, an alternate embodiment system 600 may be utilized as shown in FIG. 8, which is substantially identical to thesystem 10, with the primary difference residing between thebeam expander 22 and thereceptor assembly 26, wherein themirror 27 and the objective lens 28 (also referred to as “mirror/objective lens combination”) remain in a fixed position within the system 600. To simplify the descriptions herein, elements that are identical insystem 10 and system 600 share the same reference indicia. - Referring to FIG. 8, the mirror/objective lens combination are in a fixed position and remain at a fixed distance with respect to the
beam expander 22 within the system 600. In this embodiment, thereceptor assembly 26 supports the substrate to be engraved and is capable of incrementally translating the substrate with respect to the mirror/objective lens via a stepped transport in both the X and Y directions. Thus, the engraving process is facilitated by translating the substrate in both directions while the mirror/objective lens combination remains fixed to direct a fixed beam onto the substrate. This embodiment has been found to be effective with certain materials dictating slower engraving speeds. - Software that facilitates the system to skip over non-engraved areas of the substrate at higher speeds can be incorporated into controls of both systems, the system having a moveable objective lens and the system having a fixed objective lens, to compensate for the slower engraving speeds dictated to these embodiments by the materials they are engraving.
- It is understood that, given the above description of the embodiments of the invention, various modifications may be made by one skilled in the art. Such modifications are intended to be encompassed by the claims below.
Claims (45)
1. A substrate for use with a direct laser engraving process to create a printing substrate, the substrate comprising:
a base material; and
an inorganic ceramic material disposed on the base material.
2. The substrate of claim 1 , wherein the base material comprises a metal.
3. The substrate of claim 1 , wherein the inorganic ceramic material is vitreous.
4. The substrate of claim 1 , wherein the inorganic material is bonded to the base material.
5. The substrate of claim 1 , wherein the base material is selected from the group consisting of steel, aluminum, copper and iron.
6. The substrate of claim 1 , wherein the inorganic ceramic material comprises a porcelain enamel.
7. The substrate of claim 6 , wherein the porcelain enamel has a glass content less than 50 percent by weight.
8. The substrate of claim 6 , wherein the porcelain enamel has a glass content generally between 35 to 40 percent by weight.
9. The substrate of claim 6 , wherein the porcelain enamel comprises an oxide selected from the group consisting of SiO2, B2O3, Na2O, K2O, Li2O, CaO, ZnO, Al2O3, ZrO2, TiO2, CuO, MnO2, NiO, Co3O4, P2O5, MgO, PbO, Sb2O3, Sb2O5, ZrO2, BaO and F2.
10. The substrate of claim 6 , wherein the porcelain enamel includes a mineral filler.
11. The substrate of claim 10 , wherein the mineral filler comprises calcium carbonate.
12. A printing substrate comprising:
a base material; and
an inorganic ceramic material disposed on the base material and having a formation defining an image to be printed on a medium during a printing process.
13. The substrate of claim 12 , wherein the base material comprises a metal.
14. The substrate of claim 12 , wherein the inorganic ceramic material is vitreous.
15. The substrate of claim 12 , wherein the inorganic material is fused to the base material.
16. The substrate of claim 12 , wherein the formation defining the image is a laser-engraved formation.
17. The substrate of claim 12 , wherein the base material is selected from the group consisting of steel, aluminum, copper and iron.
18. The substrate of claim 12 , wherein the inorganic ceramic material comprises a porcelain enamel.
19. The substrate of claim 18 , wherein the porcelain enamel has a glass content less than 50 percent by weight.
20. The substrate of claim 18 , wherein the porcelain enamel has a glass content generally between 35 to 40 percent by weight.
21. The substrate of claim 18 , wherein the porcelain enamel comprises an oxide selected from the group consisting of SiO2, B2O3, Na2O, K2O, Li2O, CaO, ZnO, Al2O3, ZrO2, TiO2, CuO, MnO2, NiO, Co3O4, P2O5, MgO, PbO, Sb2O3, Sb2O5, ZrO2, BaO and F2.
22. The substrate of claim 18 , wherein the porcelain enamel includes a mineral filler.
23. The substrate of claim 22 , wherein the mineral filler comprises calcium carbonate.
24. A substrate for use with a direct laser engraving process to create a printing substrate, the substrate comprising:
a metal layer; and
a porcelain enamel layer bonded to the metal layer.
25. The substrate of claim 24 , wherein the porcelain enamel has a glass content less than 50 percent by weight.
26. The substrate of claim 24 , wherein the porcelain enamel has a glass content generally between 35 to 40 percent by weight.
27. The substrate of claim 24 , wherein the porcelain enamel includes an oxide selected from the group consisting of SiO2, B2O3, Na2O, K2O, Li2O, CaO, ZnO, Al2O3, ZrO2, TiO2, CuO, MnO2, NiO, Co3O4, P2O5, MgO, PbO, Sb2O3, Sb2O5, ZrO2, BaO and F2.
28. The substrate of claim 24 , wherein the porcelain enamel includes a mineral filler.
29. The substrate of claim 28 , wherein the mineral filler comprises calcium carbonate.
30. A printing substrate comprising:
a metal layer; and
a porcelain enamel layer bonded to the metal layer and having a laser-engraved image to be printed on a medium during a printing process.
31. The substrate of claim 30 , wherein the metal layer is selected from the group consisting of steel, aluminum, copper and iron.
32. The substrate of claim 30 , wherein the porcelain enamel layer has a glass content less than 50 percent by weight.
33. The substrate of claim 30 , wherein the porcelain enamel layer has a glass content generally between 35 to 40 percent by weight.
34. The substrate of claim 30 , wherein the porcelain enamel layer includes an oxide selected from the group consisting of SiO2, B2O3, Na2O, K2O, Li2O, CaO, ZnO, Al2O3, ZrO2, TiO2, CuO, MnO2, NiO, Co3O4, P2O5, MgO, PbO, Sb2O3, Sb2O5, ZrO2, BaO and F2.
35. The substrate of claim 30 , wherein the porcelain enamel layer includes a mineral filler.
36. The substrate of claim 35 , wherein the mineral filler is calcium carbonate.
37. The substrate of claim 30 , wherein the porcelain enamel layer has been electrostatically applied to the base layer.
38. The substrate of claim 30 , wherein the porcelain enamel is formulated to be abrasive resistant.
39. The substrate of claim 38 , wherein the porcelain enamel is formulated to be abrasive resistant by a reduction of formation of gas bubbles within the enamel during application to the metal layer.
40. A substrate for use in an intaglio printing process, the substrate comprising:
a metallic base layer; and
a porcelain enamel layer bonded to the base layer and having an engraved image created by laser engraving a plurality of subrasters each having a width and a length, each subraster defined by a plurality of data point sets each scanned across the width of the subraster by a scanning beam incident to the substrate, each of the data point sets having data points that create one of either an engraved point or an unengraved point defined by a state of the scanning beam, the plurality of subrasters combining to form a raster defining the engraved image.
41. A method of manufacturing a substrate for use with a direct laser engraving process to create a printing substrate, the method comprising the steps of:
providing a metallic layer; and
disposing an inorganic ceramic layer on the metallic layer.
42. A method of making a printing substrate for use in a printing process, the method comprising the steps of:
providing a substrate comprising a metallic layer and an inorganic ceramic layer disposed on the metallic layer; and
forming an image on the inorganic ceramic layer to be printed on a medium during a printing process.
43. The method of claim 42 , wherein the step of forming the image on the inorganic ceramic layer comprises the step of engraving the image in the inorganic ceramic layer.
44. The method of claim 42 , wherein the step of forming the image on the inorganic ceramic layer comprises the step of laser engraving the image in the inorganic ceramic layer.
45. A method of making a printing substrate for use in a printing process, the method comprising the steps of:
providing a substrate comprising a metallic layer and an inorganic ceramic layer disposed on the metallic layer; and
engraving the inorganic ceramic layer with a plurality of subrasters each having a width and a length, each subraster defined by a plurality of data point sets each scanned across the width of the subraster by a scanning beam incident to the substrate, each of the data point sets having data points that create one of either an engraved point or an unengraved point defined by a state of the scanning beam, the plurality of subrasters combining to form a raster defining the engraved image.