US20020129621A1 - Method of manufacturing optical lens - Google Patents
Method of manufacturing optical lens Download PDFInfo
- Publication number
- US20020129621A1 US20020129621A1 US10/140,282 US14028202A US2002129621A1 US 20020129621 A1 US20020129621 A1 US 20020129621A1 US 14028202 A US14028202 A US 14028202A US 2002129621 A1 US2002129621 A1 US 2002129621A1
- Authority
- US
- United States
- Prior art keywords
- optical
- optical lens
- preform
- optical member
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
An optical lens manufacturing method according to the present invention is characterized by including the first optical member preform forming step of forming a first optical member preform 40 formed of a first transparent material into a columnar shape and having a first optical acting portion 11 that forms a curved surface on a side surface thereof, the primary drawing step of drawing the first optical member preform formed by the first optical member preform forming step, and the first optical member forming step of slicing the first optical member preform drawn 40 in the primary drawing step, thus forming a first optical member 2 with a columnar shape. According to this optical lens manufacturing method, the shape of the optical lens, and particularly the shape of the first optical acting portion 11, can be determined at the stage of the preform before primary drawing. Thus, the preform can be machined with a sufficiently large size, and machining operations can be performed simply and accurately.
Description
- This is a Continuation-In-Part application of International Patent application serial No. PCT/JP00/07955 filed on Nov. 10, 2000, now pending.
- 1. Field of the Invention
- The present invention relates to a method of manufacturing an optical lens that acts on a light beam emitted from a light-emitting device and, more particularly, to a method of manufacturing an optical lens that acts on light beams emitted from a light-emitting device in which a plurality of light-emitting portions are arrayed.
- 2. Related Background Art
- In the manufacture of an optical lens for a semiconductor laser array in which a plurality of light-emitting portions are arrayed, conventionally, the manufacture with a precision mold or manufacture by applying a silicon semiconductor manufacturing process or LIGA process has been performed.
- In the conventional optical lens manufacturing method, the size itself of the required optical lens is very small, and accordingly it is very difficult to form an optical acting portion that collimates or condenses light beams emitted from the light-emitting portions of the semiconductor laser array.
- It is, therefore, an object of the present invention to provide an optical lens manufacturing a method which can form an optical acting portion easily.
- In order to achieve the above object, an optical lens manufacturing method according to the present invention is characterized by comprising the first optical member preform forming step of forming a first optical member preform formed of a first transparent material into a columnar shape and having a first optical acting portion that forms a curved surface on a side surface thereof, the primary drawing step of drawing the first optical member preform formed in the first optical member preform forming step, and the first optical member forming step of slicing the first optical member preform drawn in the primary drawing step, thus forming a first optical member with a columnar shape.
- According to this optical lens manufacturing method, the shape of the optical lens, and particularly the shape of the first optical acting portion, can be determined at the stage of the preform before primary drawing. Thus, the preform can be machined with a sufficiently large size. Note that the “optical acting portion” refers to a portion that can emit an incident divergent light beam after reducing its divergent angle. The “first optical member” is included in the optical lens. Concerning a term with a prefix “first”, the portion corresponding to the “first” may be omitted if consideration is made with only the contents described above.
- The optical lens manufacturing method may comprise the optical lens preform forming step of forming an optical lens preform formed such that a first optical member array formed by arraying a predetermined number of first optical members fabricated in the first optical member forming step in one or two rows is surrounded by a second optical member made of a second transparent material, the secondary drawing step of drawing the optical lens preform fabricated in the optical member preform forming step, the optical lens form forming step of slicing the optical lens preform drawn in the secondary drawing step, thereby forming an optical lens form, and the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
- According to this optical lens manufacturing method, an optical lens in which one optical member is buried in the other optical member is fabricated. The first optical member array can be arranged to be surrounded by the second optical member at the stage of the preform before the secondary drawing step. Thus, the arranging operations can be performed with a sufficiently large size.
- For example, the second optical member may have a cylindrical tube and a plurality of spacers arranged to fill a gap between the cylindrical tube and one or two rows of first optical member arrays inserted at a center in the cylindrical tube. Since the second optical member is divided into a plurality of portions, it can be arranged more easily.
- The first transparent material preferably has a thermal expansion coefficient which is higher than that of the second transparent material. When an optical lens is manufactured by covering a material with a high thermal expansion coefficient with a material with a low thermal expansion coefficient, a strong structure which is not broken easily can be obtained due to a caulking effect.
- The first transparent material preferably has a refractive index which is different from that of the second transparent material. Then, the operation with the optical acting portion functions effectively by utilizing a difference in refractive index.
- The first transparent material preferably has a yielding point which is higher than a temperature necessary for the secondary drawing step, and the second transparent material preferably has a yielding point which is lower than a temperature necessary for the secondary drawing step. Then, in the secondary drawing step, while the first optical member made of the first transparent material maintains its shape, the second optical member made of the second transparent material is dissolved, and the second transparent material fills the gap between the first and second optical members.
- When the optical lens preform is to be sliced in the optical lens form forming step, it may be sliced while inclined with respect to a drawing direction. Then, an optical lens in which first optical members are arrayed to be inclined with respect to the axial direction of the first optical member array can be fabricated.
- The optical lens manufacturing method may comprise the optical lens preform forming step of forming an optical lens preform formed such that the first optical member array formed by arraying a predetermined number of first optical members fabricated in the first optical member forming step in one or two rows is surrounded by a second optical member, the heating/compressing step of heating and compressing the optical lens preform fabricated in the optical lens preform forming step, the optical lens form forming step of slicing the optical lens preform heated and compressed in the heating/compressing step, thereby forming an optical lens form, and the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
- According to this manufacturing method, an optical lens can be fabricated by performing drawing operation once.
- The first transparent material preferably has a yielding point which is higher than a temperature necessary for the heating/compressing step, and the second transparent material preferably has a yielding point which is lower than a temperature necessary for the heating/compressing step. Then, in the heating/compressing step, while the first optical member made of the first transparent material maintains its shape, the second optical member made of the second transparent material is dissolved, and the second transparent material fills the gap between the first and second optical members.
- The optical lens manufacturing method may comprise the optical lens preform forming step of solidifying a first optical member array, formed by arraying a predetermined number of first optical members fabricated in the first optical member forming step in one or two rows, with a light-transmitting resin from around, thereby forming an optical lens preform, the optical lens form forming step of slicing the optical lens preform fabricated in the optical lens preform forming step, thereby forming an optical lens form, and the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
- According to this manufacturing method, an optical lens can be fabricated by performing drawing operation once. Also, since the resin used for hardening transmits light, it serves as an optical member.
- The first optical member preform described above has, e.g., a semicircular cylindrical shape. Note that the “semicircular cylindrical shape” refers to a columnar shape, as shown in FIG. 1A, with one side surface (the bottom surface in FIG. 1A) that forms a flat surface and the other side surface (the upper surface in FIG. 1A) that forms a convex curved surface. The curved surface may be aspherical, and a pair of
side surfaces 42 formed of flat surfaces may be formed, as shown in FIG. 1A. - The first optical member preform described above may alternatively have a cylindrical shape.
- The first transparent material preferably has a refractive index which is different from that of the second transparent material. Then, the operation with the optical acting portion functions effectively.
- The optical lens form machining step may include machining such that either one of respective side surfaces of the first optical member array which does not have a first optical acting portion is exposed. When a portion with no optical acting portion is removed, the optical lens can be downsized.
- The optical lens form machining step may include the second optical acting portion forming step of forming a second optical acting portion by polishing the second optical member. Alternatively, the optical lens form machining step may include the second optical acting portion forming step of forming a second optical acting portion by adhering an optical member made of the second transparent material to the second optical member. Then, optical acting portions are formed on the first and second optical members, respectively, so an optical lens that can optically act on the incident light beams in various manners is realized.
- An optical member manufacturing method according to the present invention comprises the first optical member preform forming step of forming a first optical member preform formed of a first transparent material into a columnar shape and having a side surface including a plurality of curved surface portions formed parallel to the column axis and arranged in contact with each other, the first drawing step of drawing the first optical member preform formed in the first optical member preform forming step, and the first optical member forming step of slicing the first optical member preform drawn in the first drawing step, thus forming a first optical member with a columnar shape.
- An optical lens manufacturing method according to the present invention comprises the optical lens preform forming step of forming an optical lens preform formed such that the first optical member formed in the optical member manufacturing method according to the present invention is surrounded by a second optical member made of a second transparent material, the secondary drawing step of drawing the optical lens preform fabricated in the optical lens preform forming step, the optical lens form forming step of slicing the optical lens preform drawn in the secondary drawing step, thereby forming an optical lens form, and the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
- FIGS. 1A to1C are schematic views showing the steps in a method of manufacturing an optical lens according to the first embodiment;
- FIGS. 2A to2C are schematic views showing the steps in a method of manufacturing an optical lens according to the first embodiment which is an example different from that shown in FIG. 1;
- FIGS. 3A to3C are schematic views showing the steps in a method of manufacturing an optical lens according to the first embodiment which is an example different from those shown in FIGS. 1 and 2;
- FIGS. 4A and 4B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment;
- FIGS. 5A and 5B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment which is an example different from that shown in FIG. 4;
- FIGS. 6A and 6B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment which is an example different from those shown in FIGS. 4 and 5;
- FIGS. 7A to7D are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment;
- FIGS. 8A and 8B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment which is an example different from that shown in FIG. 7;
- FIGS. 9A and 9B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment which is an example different from those shown in FIGS. 7 and 8;
- FIGS. 10A to10D are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the second embodiment; and
- FIGS. 11A to11C are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the third embodiment.
- The embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following description, the same or identical portions are denoted by the same reference numerals, and a repetitive explanation will be omitted.
- FIGS. 1A to1C are schematic views showing the steps in a method of manufacturing an optical lens according to the first embodiment. First, an optical material made of a first transparent material (glass material) is prepared, and is molded into a semicircular cylindrical shape with a
bottom surface 41 and convexcurved surface 43, as shown in FIG. 1A, to form a firstoptical member preform 40. The upper convexcurved surface 43 is a portion that forms a first optical actingportion 11 in a firstoptical member 2 as an optical lens to be formed. In this manner, in an optical lens manufacturing method employing drawing, the shape of an optical lens to be fabricated, and particularly the shape of an optical acting portion, can be formed at the stage of the firstoptical member preform 40 with a sufficiently large size. Thus, the operations of forming the shape of the optical lens and the shape of the optical acting portion can be performed easily and accurately. As shown in FIG. 1B, the molded firstoptical member preform 40 is fused by heating in anelectric furnace 35 or the like and is subjected to primary drawing to obtain a desired diameter. That portion which has been subjected to primary drawing to reach the desired diameter is cut to form the first optical member 2 (this will be called the “core 45” in the description from FIG. 4). Because of the characteristics of the drawing process, the firstoptical member 2 has the same sectional shape as that of the firstoptical member preform 40. The firstoptical member 2 fabricated in this manner collimates anincident light beam 6 with the first optical actingportion 11 formed on the light-incident side and then emits anexit light beam 7. - FIGS. 2A to2C and 3A to 3C show examples in which first optical member preforms 40 have different shapes. As shown in FIG. 2A, the first
optical member preform 40 may be formed into a cylindrical shape. In this case, as shown in FIG. 2C, a firstoptical member 2 to be manufactured has first optical actingportions 11 on both the light-incident and light-exit sides. Each first optical actingportion 11 collimates a divergent incidentlight beam 6 and emits an emerginglight beam 7. As shown in FIG. 3A, the firstoptical member preform 240 may be fabricated by a plurality of first optical member preforms 40 with a semicircular cylindrical shape shown in FIG. 1A, which are arrayed side by side in tight contact with each other. The firstoptical preform 240 thus fabricated has a side surface including a plurality of curved surface portions formed parallel to the column axis and arranged in contact with each other. In this case, as shown in FIG. 3C, a first optical member with a plurality of first optical actingportions 11 is formed. Thus, one first optical member can cope with a semiconductor laser array serving as a light-emitting device in which a plurality of light-emitting portions are arrayed. - FIGS. 4A and 4B are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment. FIG. 4A shows the overall image of an
optical lens preform 50. First,cores 45 each formed as shown in FIG. 1B are arrayed, with a second optical member, in one row at the center in acylindrical pipe 47 which has thesame length 31 as those of the cores 45 (the alignedcores 45 form a first optical member array 9). The second transparent material (example: BK7 (available from Schott), with a refractive index of 1.52, thermal expansion coefficient of 71×10−7/K, and yielding point of 614° C.) has a refractive index which is lower than that of the first transparent material (example: LaSFn14 (SUMITA KOGAKU), with a refractive index of 1.83, thermal expansion coefficient of 82×10−7/K, and yielding point of 689° C.) (if the refractive index of the first transparent material is higher than that of the second transparent material, the curved surfaces of first optical actingportions 11 are formed into convex curved surfaces; if the refractive index of the first transparent material is lower than that of the second transparent material, the curved surfaces of the first optical actingportions 11 are formed into concave curved surfaces). When aligning thecores 45, a central axis O47 of thecylindrical pipe 47 and central axes O45 of the plurality ofcores 45 are parallel to each other and are also directed in the same direction as that of secondary drawing to be described next. The plurality ofcores 45 are aligned such that their side surfaces 42 come into contact with each other. When a cylindrical one shown in FIG. 2A is to be used as each core 45, the vertical directions of thecores 45 need not be considered, and it suffices if thecores 45 are aligned such that their side surfaces come into contact with each other. Then, to fix the positions of the plurality of alignedcores 45, a pair ofspacers 46 made of the same constituent material as that of a secondoptical member 3, i.e., the second transparent material, are inserted in the gap of thecylindrical pipe 47 to sandwich the plurality ofcores 45 aligned in one row, thus forming theoptical lens preform 50. Theoptical lens preform 50 is subjected to secondary drawing until a desired diameter is obtained, as shown in FIG. 4B, and is cut off theoptical lens preform 50, thus obtaining arod portion 48. - Since the operations of aligning the plurality of
cores 45 and arranging thecores 45 andspacers 46 in thecylindrical pipe 47, as described above, are performed at the stage before the secondary drawing process, they are done with a sufficiently large size. As in an optical path converter disclosed in Japanese Patent Laid-Open No. 7-98402, first optical members may be arranged one by one in an array to correspond to the respective light-emitting portions of a semiconductor laser array. It is, however, very difficult to perform such operation within a very small area. With the optical lens manufacturing method according to this embodiment, the alignment operation and arranging operation as described above can be performed with a sufficiently large size. Hence, the above inconvenience is eliminated. - Alternatively, as shown in FIGS. 5A and 5B,
cores 45 may be aligned in two rows at the center of acylindrical pipe 47 made of the second transparent material such that the two rows are parallel to each other, and gaps may be filled with threespacers 46, thus forming an optical lens preform 51 (see FIG. 5A). In this case, an optical lens is formed in which two rows of the firstoptical member arrays 9 are buried in the second optical member. Alternatively, as shown in FIGS. 6A and 6B, anoptical lens preform 52 may be formed by usingcores 245 shown in FIG. 3B. As has been described earlier, thecores 245 are integrally molded, so the step of aligning a plurality of cores in acylindrical pipe 47 can be omitted. - FIGS. 7A to7D are schematic views showing the steps in a method of manufacturing a buried type optical lens according to the first embodiment, which follow the step in FIG. 4B. The
rod portion 48 obtained in FIG. 4B is subjected to slicing (note that the step of cutting thecores 45 androd portion 48 off the drawn optical lens preform may also be included in this “slicing”), to obtain anoptical lens form 60 shown in FIG. 7A. Theoptical lens form 60 is subjected to cutting to remove unnecessary portions of aspacer 46, and its outer portion is polished, thus forming anoptical lens 1 with a desired size (see FIG. 7B). - Since the
optical lens 1 fabricated in this manner has a firstoptical member array 9 formed by arraying firstoptical members 2, it can cope with a semiconductor laser array in which a plurality of light-emitting portions are arrayed. As the firstoptical member array 9 is buried in a secondoptical member 3, the uneven portions of first optical actingportions 11 are not exposed to the outside. Hence, dust will not be accumulated in the uneven portions to form a shadow, and theoptical lens 1 with a good light-emitting performance is realized. As theoptical lens 1 is reinforced by the secondoptical member 3, it has a large strength as well. - With the optical lens manufacturing method according to the first embodiment, the manufacture is performed by using two optical members. Thus, the manufacture can be performed by appropriately setting the refractive indices of the two optical members, and particularly by setting a large difference between the refractive indices. As is disclosed in Japanese Patent Laid Open Nos. 7-287104 and 7-98402, lenses with different refractive indices may be formed on the outer surface of one optical lens by utilizing ion exchange. In this case, however, a sufficiently large refractive index difference cannot be provided between that portion which has been subjected to ion exchange and that portion which has not, which is inconvenient. In the optical lens manufacturing method according to this embodiment, since the optical lens can be formed of different optical members, this inconvenience is solved.
- Furthermore, the temperature required for the secondary drawing process is set to be lower than the yielding point of the first transparent material and higher than that of the second transparent material. Thus, the first
optical members 2 made of the first transparent material are not dissolved in the secondary drawing process, and the secondoptical member 2 made of the second transparent material is dissolved in the secondary drawing process. The dissolved optical member fills the gap between the first and secondoptical members - In the first embodiment, a second optical acting
portion 12 is formed by cutting and polishing thespacer 46 portion in the final process, so theoptical lens 1 as shown in FIG. 7C can be fabricated. Alternatively, a second optical actingportion 12 may be formed by adhering optical members made of the second transparent material. As a result, the first and second optical acting portions are respectively formed on the firstoptical member 2 and the second optical member, so anoptical lens 71 capable of optically acting on the incident light beams in various manners is realized. Furthermore, at the stage of theoptical lens form 60, machining may be performed so that any one of the respective side surfaces of the firstoptical member array 9 which does not have a first optical acting portion may be exposed, thereby forming anoptical lens 72 as shown in FIG. 7D. As the portion not having an optical acting portion is removed, the optical lens can be downsized. - As shown in FIGS. 8A and 8B, when the
rod portion 48 obtained in FIG. 4B is to be sliced, slicing may be performed thick to form an optical lens form 61 (see FIG. 8A). Then, anoptical lens 73 that can cope even with a semiconductor laser array formed by stacking a plurality of stages is realized. As shown in FIGS. 9A and 9B, when therod portion 48 is to be sliced, slicing may be performed to be inclined by 45° with respect to the axial direction (i.e., the drawing direction of secondary drawing) of therod portion 48. Then, anoptical lens form 63 in which the respective first optical members are arrayed to be inclined with respect to the axial directions of firstoptical member arrays 9 can be fabricated. FIG. 9B shows anoptical lens 74 fabricated by cutting thisoptical lens form 63. In theoptical lens 74, two rows of firstoptical member arrays 9, in each of which respective firstoptical members 2 are inclined by 45°, are arrayed. The light beams becoming incident on anoptical lens 1 are rotated by the two rows of the firstoptical member arrays 9 through 90° about the optical axis as the central axis, and are emitted. - FIGS. 10A to10D are schematic views showing the steps in a method of manufacturing an optical lens according to the second embodiment. A plurality of first
optical members 2 each fabricated by either one of the methods of FIGS. 1 to 3 are arrayed in one row, as shown in FIG. 10A, to form a firstoptical member array 9. The firstoptical member array 9 is vertically sandwiched by a pair of secondoptical members 3, thereby forming an optical lens preform 50 (see FIG. 10B; in FIG. 10B, theoptical lens preform 50 is mounted in a heating compressor 80 (to be described later)). Each firstoptical member 2 fabricated by either one of the methods of FIGS. 1 to 3 has been subjected to drawing until it corresponds to the pitch width of each light-emitting portion of the semiconductor laser array. In the second embodiment, the first transparent material as the material that forms the firstoptical members 2 and the second transparent material as the material that forms the secondoptical members 3 may be glass or a plastic material. Theoptical lens preform 50 is set in theheating compressor 80, as shown in FIG. 10C, and is heated (700° C. ) and compressed (50 kg/cm2) from the above and below, the forward and backward, and the left and right. In this manner, anoptical lens form 64 is formed (see FIG. 10D). The subsequent steps are the same as those in the first embodiment. With the manufacturing method according to the second embodiment, an optical lens can be fabricated by performing drawing operation once. - FIGS. 11A to11C are schematic views showing the steps in a method of manufacturing an optical lens according to the third embodiment. A plurality of first
optical members 2 each fabricated by either one of the methods of FIGS. 1 to 3 are arrayed in one row, as shown in FIG. 11A, to form a firstoptical member array 9. The firstoptical member array 9 is solidified with atransparent resin 90 from around to form anoptical lens preform 50. In the same manner as in the second embodiment, each firstoptical member 2 fabricated by any one of the methods of FIGS. 1 to 3 has been subjected to drawing until it corresponds to the pitch width of each light-emitting portion of the semiconductor laser array. In the third embodiment, the first transparent material as the material that forms the firstoptical members 2 may be glass or a plastic material. Thisoptical lens preform 50 is sliced to obtain anoptical lens form 65 as shown in FIG. 11C. The subsequent steps are the same as those in the first embodiment. With the manufacturing method according to the third embodiment, an optical lens can be fabricated by performing drawing operation once, in the same manner as in the second embodiment. Since the resin used for hardening transmits light, it serves as an optical member, and can also form the second optical actingportion 12 as shown in FIG. 7C. - As has been described above, with the optical lens manufacturing methods according to the respective embodiments of the present invention, the shape of the optical lens, and particularly the shape of the first optical acting portion, can be determined at the stage of the preform before primary drawing. Thus, the preform is machined with a sufficiently large size. Therefore, the machining operations can be performed simply and accurately, and the burden in the manufacture is also reduced.
- With the buried type optical lens manufacturing methods according to the respective embodiments of the present invention, at the stage of the preform before secondary drawing, the first optical member array can be arranged to be surrounded by the second optical member. Thus, the preform is fabricated with a sufficiently large size. Therefore, the arranging operations can be performed simply and accurately, and the burden in the manufacture is also reduced.
- Although the present invention has been described in detail by means of the first to third embodiments, note that the present invention is not limited to these embodiments that merely indicate the best mode in practicing the present invention, but incorporates any modifications of the present invention within the scope of the claims of the present invention, and that the shape, size, arrangement, and constitution of the present invention can be changed.
- For example, as the action against the light beam, a case has been described wherein the light beams emitted from the respective light-emitting portions of a semiconductor laser array are collimated and emitted. Alternatively, the light beams may be condensed in place of being collimated.
- As described above, the optical lens manufacturing method according to the present invention is suitable for acting on a light beam emitted from a light-emitting device, and particularly suitable for acting on light beams emitted from the respective light-emitting portions of a light-emitting device in which a plurality of light-emitting portions are arrayed.
Claims (22)
1. An optical lens manufacturing method characterized by comprising:
the first optical member preform forming step of forming a first optical member preform formed of a first transparent material into a columnar shape and having a first optical acting portion that forms a curved surface on a side surface thereof;
the first drawing step of drawing the first optical member preform formed in the first optical member preform forming step;
the first optical member forming step of slicing the first optical member preform drawn in the first drawing step, thus forming a first optical member with a columnar shape;
the optical lens preform forming step of forming an optical lens preform formed such that a first optical member array, formed by arraying a predetermined number of first optical members fabricated in the first optical member forming step in one or two rows is surrounded by a second optical member made of a second transparent material;
the secondary drawing step of drawing the optical lens preform fabricated in the optical member preform forming step;
the optical lens form forming step of slicing)the optical lens preform drawn in the secondary drawing step, thereby forming an optical lens form; and
the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
2. An optical lens manufacturing method according to claim 1 , wherein the second optical member has a cylindrical tube and a plurality of spacers arranged to fill a gap between the cylindrical tube and one or two rows of the first optical member arrays inserted at a center in the cylindrical tube.
3. An optical lens manufacturing method according to claim 1 , wherein the first transparent material has a thermal expansion coefficient which is higher than that of the second transparent material.
4. An optical lens manufacturing method according to claim 1 , wherein the first transparent material has a refractive index which is different from that of the second transparent material.
5. An optical lens manufacturing method according to claim 1 , wherein the first transparent material has a yielding point which is higher than a temperature necessary for the secondary drawing step, and the second transparent material has a yielding point which is lower than a temperature necessary for the secondary drawing step.
6. An optical lens manufacturing method according to claim 1 , wherein when the optical lens preform is to be sliced in the optical lens form forming step, the optical lens preform is sliced while inclined with respect to a drawing direction.
7. An optical lens manufacturing method according to claim 1 , wherein the first optical member preform has a semicircular cylindrical shape.
8. An optical lens manufacturing method according to claim 1 , wherein the first optical member preform has a cylindrical shape.
9. An optical lens manufacturing method according to claim 1 , wherein the first transparent material has a refractive index which is different from that of the second transparent material.
10. An optical lens manufacturing method according to claims 1, wherein the optical lens form machining step includes machining such that either one of respective side surfaces of the first optical member array which does not have a first optical acting portion is exposed.
11. An optical lens manufacturing method according to claim 1 , wherein the optical lens form machining step includes the second optical acting portion forming step of forming a second optical acting portion by polishing the second optical member.
12. An optical lens manufacturing method according to claims 1, wherein the optical lens form machining step includes the second optical acting portion forming step of forming a second optical acting portion by adhering an optical member made of the second transparent material to the second optical member.
13. An optical lens manufacturing method characterized by comprising:
the first optical member preform forming step of forming a first optical member preform formed of a first transparent material into a columnar shape and having a first optical acting portion that forms a curved surface on a side surface thereof;
the first drawing step of drawing the first optical member preform formed in the first optical member preform forming step;
the first optical member forming step of slicing the first optical member preform drawn in the first drawing step, thus forming a first optical member with a columnar shape;
the optical lens preform forming step of forming an optical lens preform formed such that the first optical member array, formed by arraying a predetermined number of first optical members fabricated in the first optical member forming step in one or two rows is surrounded by a second optical member made of a second transparent material;
the heating/compressing step of heating and compressing the optical lens preform fabricated in the optical lens preform forming step;
the optical lens form forming step of slicing the optical lens preform heated and compressed in the heating/compressing step, thereby forming an optical lens form; and
the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.
14. An optical lens manufacturing method according to claim 13 , wherein the first transparent material has a yielding point which is higher than a temperature necessary for the heating/compressing step, and the second transparent material has a yielding point which is lower than a temperature necessary for the heating/compressing step.
15. An optical lens manufacturing method according to claim 13 , wherein the first optical member preform has a semicircular cylindrical shape.
16. An optical lens manufacturing method according to claim 13 , wherein the first optical member preform has a cylindrical shape.
17. An optical lens manufacturing method according to claim 13 , wherein the first transparent material has a refractive index which is different from that of the second transparent material.
18. An optical lens manufacturing method according to claim 13 , wherein the optical lens form machining step includes machining such that either one of respective side surfaces of the first optical member array which does not have a first optical acting portion is exposed.
19. An optical lens manufacturing method according to claim 13 , wherein the optical lens form machining step includes the second optical acting portion forming step of forming a second optical acting portion by polishing the second optical member.
20. An optical lens manufacturing method according to claim 13 , wherein the optical lens form machining step includes the second optical acting portion forming step of forming a second optical acting portion by adhering an optical member made of the second transparent material to the second optical member.
21. An optical member manufacturing method comprising:
the first optical member preform forming step of forming a first optical member preform formed of a first transparent material into a columnar shape and having a side surface including a plurality of curved surface portions formed parallel to the column axis and arranged in contact with each other;
the first drawing step of drawing the first optical member preform formed in the first optical member preform forming step; and
the first optical member forming step of slicing the first optical member preform drawn in the first drawing step, thus forming a first optical member with a columnar shape.
22. An optical lens manufacturing method comprising:
the optical lens preform forming step of forming an optical lens preform formed such that the first optical member formed in the optical member manufacturing method according to claim 21 is surrounded by a second optical member made of a second transparent material;
the secondary drawing step of drawing the optical lens preform fabricated in the optical lens preform forming step;
the optical lens form forming step of slicing the optical lens preform drawn in the secondary drawing step, thereby forming an optical lens form; and
the optical lens form machining step of cutting the optical lens form fabricated in the optical lens form forming step, thereby forming an optical lens with a desired shape.