US20020100691A1 - 3-dimensional imprint tool - Google Patents
3-dimensional imprint tool Download PDFInfo
- Publication number
- US20020100691A1 US20020100691A1 US10/074,212 US7421202A US2002100691A1 US 20020100691 A1 US20020100691 A1 US 20020100691A1 US 7421202 A US7421202 A US 7421202A US 2002100691 A1 US2002100691 A1 US 2002100691A1
- Authority
- US
- United States
- Prior art keywords
- forming
- photoresist layer
- tool
- pattern mask
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The invention is a method for the fabrication of an imprint tool master. The process begins with a metallic substrate. A layer of photoresist is placed onto the metallic substrate and a image pattern mask is then aligned to the mask. The mask pattern has opaque portions that block exposure light and “open” or transparent portions which transmit exposure light. The photoresist layer is then exposed to light transmitted through the “open” portions of the first image pattern mask and the mask is then removed. A second layer of photoresist then can be placed onto the first photoresist layer and a second image pattern mask may be placed on the second layer of photoresist. The second layer of photoresist is exposed to light, as before, and the second mask removed. The photoresist layers are developed simultaneously to produce a multi-level master mandrel upon which a conductive film is formed. A tool master can now be formed onto the conductive film. An imprint tool is then produced from the tool master. In one embodiment, nickel is electroplated onto the tool master to produce a three-dimensional imprint tool.
Description
- [0001] The United States Government has rights in this invention pursuant to Contract No. DE-AC04-94AL85000 between the United States Department of Energy and Sandia Corporation for the operation of Sandia National Laboratories.
- 1. Field of the Invention
- The present invention relates to circuit board fabrication and more specifically, it relates to a method for fabricating three dimensional imprint tools.
- 2. Description of Related Art
- Previous attempts by others in making imprint tools have suffered largely in two areas. Firstly, the process required two plating steps and the adhesion of the nickel layers was insufficient. Secondly, they lacked control of the height/depth and the cross-sectional areas of the features were not accurately reproduces in the thermoset laminate material. These are both serious issues affecting the replication and functionality of the final product.
- One method of making an imprint tool included etching a copper substrate to make a master. A pattern is chemically milled into the copper sheet and a nickel tool is electroformed from the master. Problems with this method include lack of control of the depth of the etch over large areas and the typical rounding of the pattern sidewall from etching. These are both serious problems since etching deeper causes more rounding and greater distortion of the pattern.
- A second method uses a two-step plating process to form the trace and stud/via. This process starts with patterning the traces on a nickel sheet and plating the traces with nickel. This is followed by applying another photoresist layer and patterning the studs. This method suffered from lack of adhesion between the nickel layers, trace/stud, as well as the substrate. It is difficult aligning the second pattern over the first plated layer and it was difficult controlling the height of the studs during the second plating.
- It is desirable to provide methods for making an imprint tool that are superior to the methods described above in eliminating adhesion problems, in controlling the feature height and in providing superior trace and stud cross-sectional areas.
- It is an object of the present invention to provide a process for fabricating three dimensional imprint tools.
- It is another object of the invention to eliminate adhesion issues by electroforming the trace/stud as an integral component.
- Another object of the invention is to provide a method for controlling feature height and for overcoming overplating or geometry current density issues.
- Still another object of the invention is to provide a method for fabricating three dimensional imprint tools having trace and stud cross-sectional areas that are superior over trace and stud cross-sectional areas produced with etching or by the prior art two step process.
- To maintain consistency in the fabricated tool, the present invention provides a method for fabricating a tool Master from which the embossing tool of the present invention are made. The present method allows robustness to be built into the tool Master by making it any desired thickness. The use of two layers of dry film photoresist is unique to this invention. This method provides a tool designer the opportunity to incorporate any combination of embossing features into the design of the tool, including, but not limited to, features as small as a few microns to as much as 50 micron or more. Furthermore, the present invention also affords the flexibility to design tools having features of varying geometry “stacked” one on top of another feature, thus providing for a multi-level imprinting tool.
- The use of liquid photoresist can also be used in this method, as well as the utilization of dry film photoresist. The dry film photoresist is produced with a very controlled manufacturing process that affords control over the thickness or height of the features that are grown.
- Imprint technology can be used in all sectors of government and industry currently using conventional printed circuit technology. The present invention is useful in high density circuit fabrication because the via or plated through-hole is made concurrently with the trace formation. This allows closer spacing of traces and eliminates the need for large angular rings (pads) around the vias. This imprint technology eliminates several wet processing steps used in current technology, resulting in increased production quantity and decreased production cost compared to existing imprint technology.
- The instant invention, therefore, is a method for the fabrication of an imprint tool Master and a method for fabricating an embossing tool using the tool Master. The process begins with a sheet of stainless steel or titanium having a thickness of about 0.090 inches. Stainless steel and titanium, of course, are illustrative materials only. Other choices of materials and material sheet thicknesses are possible so long as the choice is electrically conductive and exhibits a reasonable stiffness-to-weight ratio. A dry photoresist film is first laminated onto the stainless steel or titanium substrate sheet. (Liquid photoresist can also be used in this method, as an alternate to the use of dry film photoresist; however, the dry film photoresist contributes to a very controlled manufacturing process that affords control over the thickness or height of the features that are grown.) A mask comprising a negative trace image of a desired pattern, a circuit pattern for example, is then placed on the dry film photoresist and the film exposed to light through the mask openings. The mask and the Mylar cover sheet are then removed and a second dry film photoresist is laminated onto the first dry photoresist film if a multi-layer structure is desired. In such cases, a second mask comprising a second negative trace image is aligned over the second dry film photoresist and the second film exposed as was the first.
- The next step in this process is to use standard developing methods to develop both of the exposed dry film photoresist layers at the same time. This results in the removal of the unexposed portions of the dry film photoresist layers, leaving only the exposed portions on the stainless steel or titanium substrate sheet. The surface of this sheet and the developed portions of the photoresist are then covered with a copper film in order to form a conductive adhesion layer and a thick plate of nickel electroplated onto the copper layer. This nickel layer is typically about 0.030 inches to about 0.040 inches in thick but thicker or thinner layers are possible, and may be desirable, given a particular end-use circumstance.
- In a final step, the electroplated thick nickel layer is removed from the stainless steel or titanium sheet, is cleaned to remove copper and photoresist residue, and is chemically passivated for further processing.
- The cleaned nickel plate now embodies a tool master, from which an embossing tools can be fabricated.
- FIG. 1A shows the first step in an embodiment of the present method where a sheet of stainless steel or titanium is provided.
- FIG. 1B illustrates the lamination of photoresist film onto the sheet.
- FIG. 1C shows the placement of a negative trace image of a desired circuit pattern on the photoresist.
- FIG. 1D shows the removal of the negative trace image from the photoresist.
- FIG. 2A illustrates the lamination of a second photoresist film onto the first photoresist film.
- FIG. 2B shows the step of aligning a second negative trace image onto the second film of photoresist.
- FIG. 2C shows the removal of the second negative trace image from the second film of photoresist.
- FIG. 2D illustrates the step of developing both of the exposed photoresist films.
- FIG. 3A shows the stainless steel or titanium sheet, upon which is the developed exposed portions of both photoresist layers, upon which copper is deposited.
- FIG. 3B shows a thick plate of nickel electroplated onto the copper layer of FIG. 3A.
- FIG. 3C shows the removal of the thick plate of nickel from the stainless steel or titanium sheet to form the tool master.
- FIG. 3D shows the step of electroplating the tool master with nickel to produce an embossing tool.
- FIG. 3E shows the final embossing tool separated from the tool master.
- The present invention is a process for fabricating three dimensional imprint tools. This process eliminates any adhesion issues by electroforming the trace/stud as an integral component. The feature height is controlled by plating the tool master in reverse order, which removes any overplating or geometry current density issues. The cross-sectional area of the trace and studs are superior over trace and studs produced with etching or by the prior art two step process.
- General Description
- The invention is generally a method for the fabrication of an imprint tool master. The process begins with a metallic substrate. A layer of photoresist is placed onto the metallic substrate and a mask pattern, hereinafter a circuit pattern is described for illustrative purposes, is then aligned to the mask. The circuit pattern mask has opaque portions that block exposure light and “open” or transparent/translucent portions that transmit exposure light. The photoresist layer is then exposed to light transmitted through the “open” or transparent/translucent portions of the first circuit pattern mask and the circuit pattern mask is then removed. A second layer of photoresist is then placed onto the first photoresist layer and a second circuit pattern mask is placed on the second layer of photoresist. The second layer of photoresist is then exposed to light and the second circuit pattern mask is removed. The photoresist layers are developed simultaneously to produce a master mandrel upon which a conductive film is formed. A tool master is then formed onto the conductive film. An imprint tool is produced from the tool master. In one embodiment, nickel is electroplated onto the tool master to produce a three-dimensional imprint tool.
- Specific Description
- An embodiment of the steps of the invention are described with reference to FIGS. 1A through 1D and continues with reference to FIGS. 2A through 2D and is completed in FIGS. 3A through 3E.
- As required, detailed embodiments of the present invention are disclosed herein. However, it is to be understood that the disclosed embodiments are merely exemplary of the present invention which may be embodied in various systems. Therefore, specific details disclosed herein are not to be interpreted as limiting, but rather as a basis for the claims and as a representative basis for teaching one skilled in the art to variously practice the present invention.
- Referring to FIG. 1A, the process begins with a
sheet 10 of stainless steel or titanium, for example. This sheet should be about 0.090 inches thick. Adry photoresist film 12, usually about 0.002 inches thick, is then laminated onto thesheet 10, as shown in FIG. 1B. This dry film photoresist is known as “out of the box dry film.” Dry photoresist film usually includes aMylar cover sheet 14. As discussed above, liquid photoresist can also be used in this method, as an alternate to the use of dry film photoresist; however, the dry film photoresist contributes to a very controlled manufacturing process that affords control over the thickness or height of the features that are grown. - In the next step, as shown in FIG. 1C, a
negative trace image 16 of a desired circuit pattern is placed on thecover sheet 14 of thedry film photoresist 12. The desired circuit pattern will coincide with the clear or transparent/translucent portions of thenegative trace image 16. Thedry film photoresist 12 is then subjected to light exposure through thenegative trace image 16. Referring to FIG. 1D, thenegative trace image 16 and theMylar cover sheet 14 are removed. The clearMylar cover sheet 14 is about 0.001 inches thick. The remaining material comprises stainless steel ortitanium sheet 10, which carriesdry photoresist film 12, which includes exposedportions 12′. - A second dry film photoresist18 (out of the box dry film) with a second clear Mylar cover sheet 20 (about 0.001 inches thick) is then laminated onto the dry photoresist film 12 (which includes exposed
portions 12′), as shown in FIG. 2A.Dry films - The next step of aligning a second
negative trace image 22 onto thedry film photoresist 18 is illustrated in FIG. 2B. The desired stud pattern should coincide with the clear or transparent/translucent portions of thenegative trace image 22. Using a standard circuit board exposure light source, the second dryfilm photoresist layer 18 is then exposed. As shown in FIG. 2C, thenegative trace image 22 and the clearMylar cover sheet 20 then are removed. The remaining material comprises stainless steel ortitanium sheet 10, which carriesdry photoresist film 12, which carriesdry photoresist layer 18, which includes exposedportions 18′. - As shown in FIG. 2D, the next step is to use standard developing methods to develop both of the exposed dry film photoresist layers12 and 18 at the same time. This results in the removal of the unexposed portions of the dry film photoresist layers 12 and 18, leaving only the exposed
portions 18′ on 12′which is onsheet 10. - FIG. 3A illustrates
sheet 10, also referred to as a Master mandrel, upon which is the developed exposedportion 12′ upon which is the developed exposedportions 18′. The surface of thissheet 10 and thedeveloped portions 12′ and 18′ are then covered with a thin electricallyconductive film 24 through a particle vapor deposition (PVD) process, although any other coating process which would provide a thin, continuous layer of material would be equally effective. Such methods include, but are not limited to, sputtering and chemical vapor deposition metal or metalloids, and dipping, spraying, or spin coating materials solutions or suspensions and only require that the coating process not damage the photoresist layer and result in a continuous, conductive layer. - As disclosed herein,
film 24 is copper, but could be any similar material including any of the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, and alloys thereof, certain of the metals and metalloids ofGroups 13 and 14, conductive polymers, as well as colloidal suspensions and paints of any of the foregoing materials. This film is necessary to enable adherence of a firstthick metal layer 26 which is deposited in a subsequent step. In the present invention,layer 26 is nickel but, as before, it could be any similar metal selected from the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, as well as tin, or any alloy thereof providing thatlayer 26 is dissimilar to film 24. - Referring to FIG. 3B, a
thick layer 26 of nickel is electroplated onto thefilm 24 in this subsequent step. The nickel layer of the present invention is here about 0.030 inches to about 0.040 inches thick. The use of nickel and the thickness of this layer is, however, illustrative only.Layer 26 could be nickel or any similar metal selected from the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, as well as tin, or any alloy thereof, depending upon the use desired (if for instance a harder material was required). Thinner or thicker layers are also possible, and may be even be desirable, depending upon the particular circumstance of the intended end-use. - The final step in fabricating a
tool master 30 is illustrated in FIG. 3C where thethick layer 26 of nickel is removed from the stainless steel or titanium sheet (substrate base) 10. Afterlayer 26 is cleaned to remove copper and photoresist residue, it now describes atool master 30 from which embossing tools can be fabricated. - The step of fabricating an
embossing tool 40 from thetool master 30 is illustrated schematically in FIG. 3D. This final step of formingembossing tool 40 by electroplating a desired thickness of a secondthick metal layer 28 onto thetool master 30. Again, as before,layer 28 could be nickel or any similar metal selected from the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, as well as tin, or any alloy thereof. Before electroformingembossing tool 40, however,nickel tool master 30 is dipped into a dilute aqueous solution of sodium dichromate (30 to 60 seconds in 1 gm/l of water) to passivate the plating surface. The choice of passivating solutions, of course, will depend upon the metal chosen to formtool master 30. - Typically, the
tool 40 is electroplated onto thetool master 30 until it reaches a thickness of between 0.010 inches and 0.013 inches. However, thickness greater than these are possible, and may even be desirable. Fabrication of such thick sheets is limited only by the plating apparatus and the plating time necessary to achieve the desired thickness. As shown in FIG. 3E, thefinal tool 40 is then separated from thenickel tool master 30, is cleaned, and is then ready for use as an embossing tool. - The foregoing description of the invention has been presented for purposes of illustration and description and is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching. The embodiments were chosen and described to best explain the principles of the invention and its practical application to thereby enable others skilled in the art to best use the invention in various embodiments and with various modifications suited to the particular use contemplated. The scope of the invention is to be defined by the following claims.
Claims (38)
1. A method for fabricating an imprint tool master, comprising:
providing a metallic substrate;
forming a first photoresist layer onto said substrate;
aligning an image pattern mask onto said photoresist layer, wherein said pattern mask has portions that block exposure light and portions which transmit exposure light;
exposing said photoresist layer with a first exposure of exposure light;
removing said first pattern mask;
developing said first photoresist layer to produce a master mandrel;
forming a conductive film onto said master mandrel; and
forming a tool master on said conductive film.
2. The method of claim 1 , further comprising forming an embossing tool from said tool master.
3. The method of claim 2 , wherein the step of forming an embossing tool comprises:
passivating said tool master;
electroplating a metal layer onto said tool master; and
separating said metal layer from said tool master to provide said embossing tool.
4. The method of claim 3 , wherein the step of electroplating a metal layer includes electroplating a metal selected from the group consisting of the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, tin, and any alloy thereof.
5. The method of claim 3 , wherein the step of electroplating includes electroplating nickel.
6. The method of claim 1 , wherein the step of providing a metallic substrate comprises providing a stainless steel substrate.
7. The method of claim 6 , wherein the step of providing a stainless steel substrate comprises providing a stainless steel substrate that is about 0.090 inches thick.
8. The method of claim 1 , wherein the step of providing a metallic substrate comprises providing a titanium substrate.
9. The method of claim 8 , wherein the step of providing a titanium substrate comprises providing a titanium substrate that is about 0.090 inches thick.
10. The method of claim 1 , wherein the step of forming a first photoresist layer onto said substrate comprises forming a first dry film photoresist layer on said substrate.
11. The method of claim 1 , wherein the step of forming a first photoresist layer onto said substrate comprises forming a first wet photoresist layer onto said substrate.
12. The method of claim 1 , wherein the step of aligning an image pattern mask comprises aligning a positive trace image pattern mask.
13. The method of claim 1 , wherein the step of aligning an image pattern mask comprises aligning a negative trace image pattern mask.
14. The method of claim 1 , wherein the step of forming a second photoresist layer comprises forming a second dry film photoresist layer.
15. The method of claim 1 , wherein the step of forming a second photoresist layer comprises forming a second wet photoresist layer.
16. A method for fabricating an imprint tool master, comprising:
providing a metallic substrate;
forming a first photoresist layer onto said substrate;
aligning an image pattern mask onto said photoresist layer, wherein said pattern mask has first portions that block exposure light and first portions which transmit exposure light;
exposing said photoresist layer with a first exposure of exposure light;
removing said first pattern mask;
forming a second photoresist layer onto said first photoresist layer;
aligning a second pattern mask of a second desired pattern onto said second photoresist layer, wherein said second pattern mask has second portions that block exposure light and second portions which transmit exposure light;
exposing said second photoresist layer with a second exposure of said exposure light transmitted through said second portions;
removing said second pattern mask;
developing both said first photoresist layer and said second photoresist layer to produce a master mandrel;
forming a conductive film onto said master mandrel; and
forming a tool master on said conductive film.
17. The method of claim 16 , further comprising forming an embossing tool from said tool master.
18. The method of claim 17 , wherein the step of forming a tool comprises:
passivating said tool master;
electroplating a metal layer onto said tool master; and
separating said metal from said tool master.
19. The method of claim 18 , wherein the step of electroplating a metal layer includes electroplating The method of claim 3 , wherein the step of electroplating a metal layer includes electroplating a metal selected from the group consisting of the Transition series of metal listed in New IUPAC Group Numbers 4-12 of the Period Table of elements, tin, and any alloy thereof.
20. The method of claim 18 , wherein the step of electroplating a metal layer includes electroplating nickel.
21. The method of claim 16 , wherein the step of providing a metallic substrate comprises providing a stainless steel substrate.
22. The method of claim 21 , wherein the step of providing a stainless steel substrate comprises providing a stainless steel substrate that is about 0.090 inches thick.
23. The method of claim 16 , wherein the step of providing a metallic substrate comprises providing a titanium substrate.
24. The method of claim 23 , wherein the step of providing a titanium substrate comprises providing a titanium substrate that is about 0.090 inches thick.
25. The method of claim 16 , wherein the step of forming a first photoresist layer onto said substrate comprises forming a first dry film photoresist layer on said substrate.
26. The method of claim 16 , wherein the step of forming a first photoresist layer onto said substrate comprises forming a first wet photoresist layer onto said substrate.
27. The method of claim 16 , wherein the step of aligning an image pattern mask comprises aligning a positive trace image pattern mask.
28. The method of claim 16 , wherein the step of aligning an image pattern mask comprises aligning a negative trace image pattern mask.
29. The method of claim 16 , wherein the step of forming a second photoresist layer comprises forming a second dry film photoresist layer.
30. The method of claim 16 , wherein the step of forming a second photoresist layer comprises forming a second wet photoresist layer.
31. The method of claim 16 , wherein the step of aligning a second pattern mask comprises aligning a second positive trace image pattern mask.
32. The method of claim 16 , wherein the step of aligning a second pattern mask comprises aligning a second negative trace image pattern mask.
33. The method of claim 16 , wherein the step of forming a conductive film comprises forming a conductive film by particle vapor deposition.
34. The method of claim 16 , wherein the step of forming a conductive film comprises forming a copper film.
35. A 3 dimensional embossing tool, comprising:
an electroformed metal sheet having a print positive electroformed image of an embossing pattern, said pattern including a plurality of structures having variable geometries and minimum feature dimensions as small as about 0.0005 inches.
36. The embossing tool of claim 35 , wherein said plurality of structures include multi-layered structures.
37. The embossing tool of claim 36 , wherein each of said layers has a thickness ranging from about 0.0005 inch to about 0.01 inch.
38. A tool master for forming a 3 dimensional embossing tool, comprising:
an electroformed metal sheet having a print negative image of an embossing structure formed into said electroformed sheet, said sheet formed by electroplating a thickness of a metal over a print positive image comprising a metallic coated photoresist.