TWI504577B - A glass substrate manufacturing method and a glass substrate manufacturing apparatus - Google Patents
A glass substrate manufacturing method and a glass substrate manufacturing apparatus Download PDFInfo
- Publication number
- TWI504577B TWI504577B TW103111536A TW103111536A TWI504577B TW I504577 B TWI504577 B TW I504577B TW 103111536 A TW103111536 A TW 103111536A TW 103111536 A TW103111536 A TW 103111536A TW I504577 B TWI504577 B TW I504577B
- Authority
- TW
- Taiwan
- Prior art keywords
- glass
- molten glass
- heating
- glass substrate
- temperature
- Prior art date
Description
本發明係關於一種製造玻璃基板之玻璃基板之製造方法及實施該製造方法之玻璃基板製造裝置。The present invention relates to a method for producing a glass substrate for producing a glass substrate and a glass substrate manufacturing apparatus for carrying out the method.
近年來,於顯示面板之領域中,為了提高畫質而像素之高精細化不斷推進。隨著該高精細化之發展,對於顯示面板所使用之玻璃基板亦期待高品質。例如,謀求如於面板之製造步驟中經高溫熱處理之玻璃基板不易產生尺寸變化般熱收縮較小之玻璃基板。又,就防止TFT(Thin Film Transistor,薄膜電晶體)之特性劣化之觀點而言,液晶顯示面板所使用之玻璃基板使用不含包含Li2 O、Na2 O、K2 O之鹼金屬氧化物或即便含有亦幾乎不含之玻璃。In recent years, in the field of display panels, in order to improve the image quality, the pixel is highly refined. With the development of this high definition, high quality is also expected for the glass substrate used for the display panel. For example, a glass substrate which is subjected to a high-temperature heat treatment in a manufacturing process of a panel is less likely to have a small heat shrinkage as a dimensional change. Further, from the viewpoint of preventing deterioration of characteristics of a TFT (Thin Film Transistor), the glass substrate used in the liquid crystal display panel does not contain an alkali metal oxide containing Li 2 O, Na 2 O, and K 2 O. Or even contain glass that is almost free.
一般而言,上述之玻璃基板之熱收縮係玻璃之應變點越高則越小。又,已知玻璃基板之熱收縮係將玻璃基板之製造步驟中之緩冷速度設得越小則越小。因此,即便玻璃組成相同,亦可藉由充分地減小緩冷速度而將熱收縮降低至所要求之等級。尤其是於利用浮式法由熔融玻璃製造玻璃基板之情形時,可相對較容易地加長緩冷爐而減小緩冷速度,但於使用下拉法製造玻璃基板之情形時,就設備上或作業操作上之方面而言難以加長緩冷爐。因此,於利用下拉法製造滿足對熱收縮之要求之玻璃基板時,利用與先前之玻璃組成相比應變點較高之玻璃組成的玻璃(專利文獻1)。In general, the higher the strain point of the heat shrinkable glass of the above glass substrate, the smaller the strain point. Further, it is known that the heat shrinkage of the glass substrate is smaller as the slow cooling rate in the manufacturing step of the glass substrate is smaller. Therefore, even if the glass composition is the same, the heat shrinkage can be reduced to the required level by sufficiently reducing the slow cooling rate. In particular, when a glass substrate is produced from molten glass by a floating method, it is relatively easy to lengthen the slow cooling furnace to reduce the slow cooling rate, but when the glass substrate is manufactured by the down-draw method, it is on the equipment or the operation. In terms of operation, it is difficult to lengthen the slow cooling furnace. Therefore, when a glass substrate satisfying the heat shrinkage requirement is produced by the down-draw method, a glass having a higher strain point than the previous glass composition is used (Patent Document 1).
又,上述不含鹼金屬氧化物或即便含有亦幾乎不含之公知之玻 璃(專利文獻2)一般而言與即便含有鹼金屬氧化物亦無影響之鹼玻璃相比,玻璃之熔融溫度較高,且為難熔性。於使用此種玻璃之情形時,為了使玻璃原料充分地熔解,防止成為玻璃基板之缺陷之未熔解物流出至後續步驟,必須使熔融步驟中之熔融玻璃溫度高於鹼玻璃。Further, the above-mentioned glass containing no alkali metal oxide or containing almost no known glass Glass (Patent Document 2) Generally, the glass has a higher melting temperature and is refractory than an alkali glass which does not have an influence even if it contains an alkali metal oxide. In the case of using such a glass, in order to sufficiently melt the glass raw material and prevent the unmelted stream which is a defect of the glass substrate from proceeding to the subsequent step, it is necessary to make the temperature of the molten glass in the melting step higher than that of the alkali glass.
[專利文獻1]日本專利特開2010-6649號公報[Patent Document 1] Japanese Patent Laid-Open Publication No. 2010-6649
[專利文獻2]日本專利特開2010-235444號公報[Patent Document 2] Japanese Patent Laid-Open Publication No. 2010-235444
然而,若以應變點變高之方式調整玻璃組成,則高溫域(例如,1,500℃以上之溫度)下之黏度變高而成為難熔性之玻璃。若高溫域下之熔融玻璃之黏度變高,則為了使玻璃原料充分地熔解,防止成為玻璃基板之缺陷之未熔解物流出至後續步驟,必須使熔融步驟中之熔融玻璃溫度高於先前。However, when the glass composition is adjusted so that the strain point becomes high, the viscosity in a high temperature range (for example, a temperature of 1,500 ° C or higher) becomes high and becomes a refractory glass. When the viscosity of the molten glass in the high temperature range is high, in order to sufficiently melt the glass raw material and prevent the unmelted stream which is a defect of the glass substrate from flowing to the subsequent step, it is necessary to make the temperature of the molten glass in the melting step higher than the previous one.
一般而言,於在熔解槽中由玻璃原料製造熔融玻璃之情形時,於熔解槽內之氣相空間,例如藉由利用使用燃燒氣體之燃燒器之加熱使氣相溫度高溫化而提高熔解槽之壁之溫度,利用來自該壁之輻射熱使投入之玻璃原料熔解。進而,於熔解槽中,利用上述輻射熱對熔解而形成之熔融玻璃進行加熱,且經由位於熔解槽之液相中之電極對進行通電加熱,藉此使熔融玻璃成為所期望之溫度及黏度。In general, when a molten glass is produced from a glass raw material in a melting tank, the melting zone is raised in the gas phase space in the melting tank, for example, by heating the gas phase by heating with a burner using a combustion gas. The temperature of the wall is such that the radiant heat from the wall is used to melt the input glass material. Further, in the melting tank, the molten glass formed by the radiant heat is heated, and the electrode pair located in the liquid phase of the melting tank is electrically heated, whereby the molten glass is brought to a desired temperature and viscosity.
但是,若提高上述熔解步驟中之熔融玻璃之溫度,則本來於澄清步驟中使泡產生並促進脫泡之澄清劑於熔融步驟中以懸浮於熔融玻璃之液面之狀態產生氧並使該氧釋出至熔融玻璃外。因此,存在澄清劑之澄清能力下降而於澄清步驟中無法充分地減少泡之問題。However, if the temperature of the molten glass in the above-mentioned melting step is increased, the clarifying agent which originally causes the bubble generation and promotes defoaming in the clarification step generates oxygen and suspends the oxygen in a state of being suspended in the liquid surface of the molten glass in the melting step. Released to the outside of the molten glass. Therefore, there is a problem that the clarifying ability of the clarifying agent is lowered and the bubble cannot be sufficiently reduced in the clarification step.
又,於製造不含鹼金屬氧化物或即便含有亦幾乎不含之難熔性 之玻璃之玻璃基板之情形時,若於製作熔融玻璃之熔融步驟中過度提高熔融玻璃之溫度,則本來於澄清步驟中使泡產生並促進脫泡之澄清劑於熔融步驟中使泡產生並使該泡釋出至熔融玻璃外。因此,存在於澄清步驟中無法充分地減少泡之問題。Moreover, in the manufacture of refractory properties which do not contain an alkali metal oxide or which are contained almost without In the case of a glass substrate of glass, if the temperature of the molten glass is excessively increased in the melting step of producing the molten glass, the clarifying agent which originally generates bubbles and promotes defoaming in the clarification step causes bubbles to be generated in the melting step and The bubble is released outside the molten glass. Therefore, there is a problem that the bubble cannot be sufficiently reduced in the clarification step.
又,近年來,根據下述情況,上述泡之問題變得更顯著。Further, in recent years, the problem of the above-described bubble has become more remarkable in the following cases.
.就環境問題之觀點而言,使用澄清效果與As2 O3 相比較差之氧化錫而並非使用澄清效果較大之As2 O3 ,因此於澄清步驟中無法進行充分之脫泡,從而泡之問題變得顯著。. From the viewpoint of environmental problems, it is not necessary to use a tin oxide having a clarifying effect as compared with As 2 O 3 and not using As 2 O 3 having a large clarifying effect, so that sufficient defoaming cannot be performed in the clarification step, so that the bubble is formed. The problem has become significant.
.由於高溫域下之熔融玻璃之黏度較高,故而澄清步驟中之泡之浮起速度變慢。因此,於澄清步驟中無法進行充分之脫泡,從而泡之問題變得顯著。. Since the viscosity of the molten glass in the high temperature region is high, the floating speed of the bubbles in the clarification step becomes slow. Therefore, sufficient defoaming cannot be performed in the clarification step, so that the problem of foaming becomes remarkable.
因此,本發明之目的在於提供一種即便於使用難熔性之玻璃製造玻璃基板之情形時亦可減少未熔解物之產生且可藉由充分地發揮澄清劑之效果而減少泡之產生的玻璃基板之製造方法及玻璃基板製造裝置。Therefore, an object of the present invention is to provide a glass substrate which can reduce the generation of unmelted substances and can reduce the generation of bubbles by sufficiently exhibiting the effect of a clarifying agent even when a glass substrate is produced using refractory glass. Manufacturing method and glass substrate manufacturing apparatus.
本發明之一態樣係一種玻璃基板之製造方法,包含以下形態。One aspect of the present invention is a method for producing a glass substrate, which comprises the following aspects.
(形態1)(Form 1)
一種玻璃基板之製造方法,其特徵在於包括:熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有氧化錫且黏度為102.5 泊時之溫度為1580℃以上之玻璃之方式熔解玻璃原料;及澄清步驟,其係利用氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之 發熱量的比成為1.0以上且2.8以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in a melting tank, which is heated by combustion heating in a gas phase using a combustion mechanism and electric heating by flowing a current to the molten glass a glass raw material in which tin oxide has a viscosity of 102.5 poise at a temperature of 1580 ° C or more; and a clarification step of clarifying the molten glass by a redox reaction of tin oxide; and is caused by the above combustion heating The combustion heating and the energization heating are performed so that the ratio of the amount of heat generated to the amount of heat generated by the electric conduction heating is 1.0 or more and 2.8 or less.
(形態2)(Form 2)
一種玻璃基板之製造方法,其特徵在於包括:熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有SnO2 且黏度為102.5 泊時之溫度為1580度以上之玻璃之方式熔解玻璃原料;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.5以上且2.8以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in a melting tank, which is heated by combustion heating in a gas phase using a combustion mechanism and electric heating by flowing a current to the molten glass embodiment SnO 2 and the viscosity temperature poise of 2.5 10 not less than 1580 degrees glass melting glass raw materials; and with heat caused by the above-described combustion heating with respect to the amount of heat caused by the above-described electrical heating ratio becomes 1.5 or more and 2.8 The above-described combustion heating and the above-described electric heating are carried out in the following manner.
(形態3)(Form 3)
如形態1或2中記載之玻璃基板之製造方法,其中上述玻璃基板之應變點為680℃以上。The method for producing a glass substrate according to Aspect 1 or 2, wherein the glass substrate has a strain point of 680 ° C or higher.
(形態4)(Form 4)
一種玻璃基板之製造方法,其特徵在於包括: 熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有氧化錫且應變點為680℃以上之玻璃之方式熔解玻璃原料;及澄清步驟,其係利用氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且2.8以下之方式進行上述燃燒加熱及上述通電加熱。A method for manufacturing a glass substrate, comprising: The melting step is carried out in a melting tank, and is heated by combustion in a gas phase using a combustion mechanism and electric conduction by flowing a current to the molten glass to obtain a glass containing tin oxide and having a strain point of 680 ° C or higher. a method of melting a glass raw material; and a clarifying step of clarifying the molten glass by a redox reaction of tin oxide; and a ratio of a calorific value caused by the combustion heating to a calorific value caused by the electric heating is 1.0 or more The combustion heating and the above-described electric heating are performed in a manner of 2.8 or less.
(形態5)(Form 5)
如形態1至4中任一項中記載之玻璃基板之製造方法,其中上述 澄清步驟中之上述熔融玻璃之最高溫度高於上述熔解槽中之上述熔融玻璃之最高溫度。The method for producing a glass substrate according to any one of aspects 1 to 4, wherein the above The highest temperature of the molten glass in the clarification step is higher than the highest temperature of the molten glass in the melting tank.
(形態6)(Form 6)
如形態1至5中任一項中記載之玻璃基板之製造方法,其中覆蓋上述熔解槽之氣相空間之頂面之槽頂部之溫度為1610℃以下。The method for producing a glass substrate according to any one of the aspects 1 to 5, wherein a temperature of the top of the groove covering the top surface of the vapor phase space of the melting tank is 1610 ° C or lower.
(形態7)(Form 7)
如形態1至6中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板中之鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下。The method for producing a glass substrate according to any one of the aspects of the present invention, wherein the content of the alkali metal oxide in the glass substrate is 0% by mole or more and 0.4% by mole or less.
(形態8)(Form 8)
如形態1至7中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板至少含有SiO2 、Al2 O3 、B2 O3 及RO(R為Mg、Ca、Sr及Ba中含有於上述玻璃基板中之全部元素),B2 O3 之含有率為0~7莫耳%。The method for producing a glass substrate according to any one of the aspects 1 to 7, wherein the glass substrate contains at least SiO 2 , Al 2 O 3 , B 2 O 3 and RO (R is contained in Mg, Ca, Sr and Ba). The content of B 2 O 3 in all the elements in the above glass substrate is 0 to 7 mol%.
(形態9)(Form 9)
如形態1至8中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板至少含有SiO2 、Al2 O3 、B2 O3 及RO(R為Mg、Ca、Sr及Ba中含有於上述玻璃基板中之全部元素)。The method for producing a glass substrate according to any one of the aspects 1 to 8, wherein the glass substrate contains at least SiO 2 , Al 2 O 3 , B 2 O 3 and RO (R is contained in Mg, Ca, Sr, and Ba). All of the elements in the above glass substrate).
(形態10)(Form 10)
如形態9中記載之玻璃基板之製造方法,其中B2 O3 之含有率為0~10莫耳%或0~5莫耳%。The method for producing a glass substrate according to aspect 9, wherein the content of B 2 O 3 is 0 to 10 mol% or 0 to 5 mol%.
(形態11)(Form 11)
如形態9或10中記載之玻璃基板之製造方法,其中SiO2 之含有率為68~75莫耳%。The method for producing a glass substrate according to Aspect 9 or 10, wherein the content of SiO 2 is 68 to 75 mol%.
(形態12)(Form 12)
如形態9至11中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板含有B2 O3 及RO(RO為MgO、CaO、SrO及BaO之合計量),且 含有SiO2 及Al2 O3 中之任一者,莫耳比((2×SiO2 )+Al2 O3 )/((2×B2 O3 )+RO)為4.5以上。The method for producing a glass substrate according to any one of aspects 9 to 11, wherein the glass substrate contains B 2 O 3 and RO (RO is a total amount of MgO, CaO, SrO, and BaO), and contains SiO 2 and Al. In any of 2 O 3 , the molar ratio ((2 × SiO 2 ) + Al 2 O 3 ) / ((2 × B 2 O 3 ) + RO) is 4.5 or more.
(形態13)(Form 13)
如形態1至12中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板含有MgO、CaO、SrO及BaO中之至少任一者,莫耳比(BaO+SrO)/RO(RO為MgO、CaO、SrO及BaO之合計量)為0.1以上。The method for producing a glass substrate according to any one of aspects 1 to 12, wherein the glass substrate contains at least one of MgO, CaO, SrO, and BaO, and a molar ratio (BaO+SrO)/RO (RO is The total amount of MgO, CaO, SrO, and BaO is 0.1 or more.
(形態14)(Form 14)
如形態1至13中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板中之鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下。The method for producing a glass substrate according to any one of the aspects of the present invention, wherein the content of the alkali metal oxide in the glass substrate is 0% by mole or more and 0.4% by mole or less.
再者,於本說明書中,所謂鹼金屬氧化物之含有率,係表示Li2 O、Na2 O及K2 O之含有率之合計量。In the present specification, the content ratio of the alkali metal oxide is a total of the contents of Li 2 O, Na 2 O, and K 2 O.
(形態15)(Form 15)
如形態1至14中任一項中記載之玻璃基板之製造方法,其中構成上述玻璃基板之玻璃於為1550℃之熔融玻璃時之電阻率(以下亦稱為比電阻)為100Ω.cm以上。The method for producing a glass substrate according to any one of the aspects 1 to 4, wherein a resistivity (hereinafter also referred to as a specific resistance) of the glass constituting the glass substrate at a molten glass of 1550 ° C is 100 Ω. More than cm.
(形態16)(Form 16)
如形態1至15中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板含有:SiO2 60~80莫耳%、Al2 O3 10~20莫耳%、B2 O3 0~10莫耳%、RO 0~17莫耳%(RO為MgO、CaO、SrO及BaO之合計量)。The method for producing a glass substrate according to any one of the aspects 1 to 15, wherein the glass substrate comprises: SiO 2 60 to 80 mol%, Al 2 O 3 10 to 20 mol%, and B 2 O 3 0~ 10 mole %, RO 0~17 mole % (RO is the total amount of MgO, CaO, SrO and BaO).
(形態17)(Form 17)
如形態1至16中任一項中記載之玻璃基板之製造方法,其中上述玻璃基板亦可為平板顯示器用玻璃基板。又,上述玻璃基板為LTPS(Low Temperature Poly-Silicon,低溫多晶矽).TFT(Thin Film Transistor)顯示器用玻璃基板或有機EL(Electroluminescence,電致發 光)顯示器用玻璃基板。The method for producing a glass substrate according to any one of the aspects 1 to 16, wherein the glass substrate may be a glass substrate for a flat panel display. Moreover, the glass substrate is LTPS (Low Temperature Poly-Silicon, low temperature polysilicon). TFT (Thin Film Transistor) display with glass substrate or organic EL (Electroluminescence) Light) Glass substrate for display.
(形態18)(Form 18)
如形態1至17中任一項中記載之玻璃基板之製造方法,其中上述澄清步驟包括:脫泡處理,其係於上述熔解步驟後,使上述熔融玻璃之溫度以2℃/分鐘以上之升溫速度升溫至1630℃以上,藉此使上述熔融玻璃中產生泡並進行脫泡;及吸收處理,其係於上述脫泡處理後,使上述熔融玻璃降溫,藉此使上述熔融玻璃中之泡被上述熔融玻璃吸收。The method for producing a glass substrate according to any one of aspects 1 to 17, wherein the clarification step includes a defoaming treatment, wherein the temperature of the molten glass is raised by 2 ° C / min or more after the melting step. Increasing the temperature to 1630 ° C or higher, thereby generating bubbles in the molten glass and performing defoaming; and absorbing treatment, after the defoaming treatment, cooling the molten glass to thereby cause bubbles in the molten glass The above molten glass is absorbed.
(形態19)(Form 19)
如形態18中記載之玻璃基板之製造方法,其中上述脫泡處理係使上述熔融玻璃之溫度以2.5℃/分鐘以上之升溫速度升溫至1630℃以上。The method for producing a glass substrate according to aspect 18, wherein the defoaming treatment is performed to raise the temperature of the molten glass to a temperature increase rate of 2.5 ° C /min or more to 1630 ° C or higher.
(形態20)(Form 20)
如形態1至19中任一項中記載之玻璃基板之製造方法,其中上述澄清步驟包括:脫泡處理,其係使上述熔融玻璃之溫度升溫至1630℃以上,藉此使上述熔融玻璃中產生泡並進行脫泡;及吸收處理,其係於上述脫泡處理後,使上述熔融玻璃於1600℃至1500℃之溫度範圍以2℃/分鐘以上之降溫速度降溫,藉此使上述熔融玻璃中之泡被上述熔融玻璃吸收。The method for producing a glass substrate according to any one of the aspects 1 to 19, wherein the clarification step includes a defoaming treatment for raising a temperature of the molten glass to 1630 ° C or higher, thereby producing the molten glass. And defoaming; and absorbing treatment, after the defoaming treatment, cooling the molten glass at a temperature lowering temperature of 1600 ° C to 1500 ° C at a temperature lowering rate of 2 ° C / min or more, thereby making the molten glass The bubbles are absorbed by the molten glass.
(形態21)(Form 21)
一種玻璃基板之製造方法,其特徵在於包括:熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,熔解以成為含有氧化錫且鹼金屬氧化物之含有率為0~0.4莫耳%之玻璃基板之方式調製而成之玻璃原料;及澄清步驟,其係利用氧化錫之氧化還原反應進行上述熔融玻璃 之澄清;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in which a melting step is performed by combustion heating in a gas phase using a combustion mechanism and electric heating by flowing a current to the molten glass to melt a glass raw material prepared by disposing a tin oxide substrate and having a content of an alkali metal oxide of 0 to 0.4 mol%; and a clarification step of performing the above molten glass by a redox reaction of tin oxide In the clarification, the combustion heating and the energization heating are performed so that the ratio of the amount of heat generated by the combustion heating to the amount of heat generated by the electric conduction heating is 1.0 or more and 3.4 or less.
(形態22)(Form 22)
一種玻璃基板之製造方法,其特徵在於包括:熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,熔解以成為含有氧化錫且鹼金屬氧化物之含有率為0~0.4莫耳%之玻璃基板之方式調製而成之玻璃原料;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.5以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in which a melting step is performed by combustion heating in a gas phase using a combustion mechanism and electric heating by flowing a current to the molten glass to melt a glass raw material prepared by disposing a tin oxide and having an alkali metal oxide content of 0 to 0.4 mol%; and the calorific value caused by the above combustion heating is relative to the calorific value caused by the electric heating The above-described combustion heating and the above-described electric heating are performed so that the ratio is 1.5 or more and 3.4 or less.
(形態23)(Form 23)
一種玻璃基板之製造方法,其特徵在於包括:熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有氧化錫且黏度為102.5 泊時之溫度為1500℃以上之玻璃之方式熔解玻璃原料;及澄清步驟,其係利用氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in a melting tank, which is heated by combustion heating in a gas phase using a combustion mechanism and electric heating by flowing a current to the molten glass a glass raw material in which tin oxide has a viscosity of 10 2.5 poise and a temperature of 1500 ° C or more; and a clarification step of clarifying the molten glass by a redox reaction of tin oxide; and is caused by the above combustion heating The combustion heating and the energization heating are performed so that the ratio of the amount of heat generated to the amount of heat generated by the electric conduction heating is 1.0 or more and 3.4 or less.
(形態24)(Form 24)
一種玻璃基板之製造方法,其特徵在於包括: 熔解步驟,其係於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有氧化錫且黏度為102.5 泊時之溫度為1500℃以上之玻璃之方式熔解玻璃原料;且以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.5以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A method for producing a glass substrate, comprising: a melting step in which a heating step is performed by combustion heating in a gas phase using a combustion mechanism and electric heating is performed by flowing a current to the molten glass to be contained The glass raw material is melted in the form of a tin oxide having a viscosity of 10 2.5 poise and a temperature of 1500 ° C or higher; and the ratio of the calorific value caused by the above combustion heating to the calorific value caused by the electric heating is 1.5 or more and 3.4. The above-described combustion heating and the above-described electric heating are carried out in the following manner.
(形態25)(Form 25)
一種玻璃基板製造裝置,其特徵在於包括:熔解槽本體,其具有氣相空間,貯存熔融玻璃;燃燒機構,其於上述氣相空間中進行燃燒加熱而加熱玻璃原料及/或上述熔融玻璃;電極對,其設置於與熔融玻璃接觸之壁,用以對上述玻璃原料及/或上述熔融玻璃進行通電加熱;及澄清槽,其利用上述熔融玻璃中所含之氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且於以成為黏度為102.5 泊時之溫度為1580℃以上之玻璃之方式利用上述燃燒加熱及上述通電加熱製作上述熔融玻璃時,以使上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且2.8以下之方式進行上述燃燒加熱及上述通電加熱。A glass substrate manufacturing apparatus, comprising: a melting tank body having a gas phase space for storing molten glass; and a burning mechanism for heating and heating the glass raw material and/or the molten glass in the gas phase space; Further, it is disposed on a wall in contact with the molten glass for electrically heating the glass raw material and/or the molten glass; and a clarification tank which performs the above melting by a redox reaction of tin oxide contained in the molten glass The glass is clarified; and when the molten glass is produced by the above-described combustion heating and the above-described electric heating at a temperature of 1580 ° C or higher at a viscosity of 10 2.5 poise, the calorific value caused by the combustion heating is relative to The combustion heating and the energization heating are performed so that the ratio of the amount of heat generation due to the electric conduction heating is 1.0 or more and 2.8 or less.
(形態26)(Form 26)
一種玻璃基板製造裝置,其特徵在於包括:熔解槽本體,其具有氣相空間,貯存熔融玻璃;燃燒機構,其於上述氣相空間中進行燃燒加熱而加熱玻璃原料及/或上述熔融玻璃;電極對,其設置於與熔融玻璃接觸之壁,以對上述玻璃原料及/ 或上述熔融玻璃進行通電加熱;及澄清槽,其利用上述熔融玻璃中所含之氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且於以成為應變點為680℃以上之玻璃之方式利用上述燃燒加熱及上述通電加熱製作上述熔融玻璃時,以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且2.8以下之方式進行上述燃燒加熱及上述通電加熱。A glass substrate manufacturing apparatus, comprising: a melting tank body having a gas phase space for storing molten glass; and a burning mechanism for heating and heating the glass raw material and/or the molten glass in the gas phase space; Yes, it is placed on the wall in contact with the molten glass to the above glass raw materials and / Or the above-mentioned molten glass is electrically heated; and the clarification tank is used for clarification of the molten glass by a redox reaction of tin oxide contained in the molten glass; and the glass is used as a strain point of 680 ° C or higher. When the above-described molten glass is produced by the combustion heating and the above-described electric heating, the combustion heating and the electric conduction heating are performed so that the ratio of the calorific value due to the combustion heating to the calorific value due to the electric conduction heating is 1.0 or more and 2.8 or less.
(形態27)(Form 27)
一種玻璃基板製造裝置,其特徵在於包括:熔解槽本體,其具有氣相空間,貯存熔融玻璃;燃燒機構,其於上述氣相空間中進行燃燒加熱而加熱玻璃原料及/或上述熔融玻璃;電極對,其設置於與熔融玻璃接觸之壁,以對上述玻璃原料及/或上述熔融玻璃進行通電加熱;及澄清槽,其利用上述熔融玻璃中所含之氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且於以成為鹼金屬氧化物之含有率為0~0.4莫耳%之玻璃基板之方式利用上述燃燒加熱及上述通電加熱製作上述熔融玻璃時,以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A glass substrate manufacturing apparatus, comprising: a melting tank body having a gas phase space for storing molten glass; and a burning mechanism for heating and heating the glass raw material and/or the molten glass in the gas phase space; Further, it is provided on a wall in contact with the molten glass to electrically heat the glass raw material and/or the molten glass, and a clarification tank which performs the above-described molten glass by a redox reaction of tin oxide contained in the molten glass. In the case where the molten glass is produced by the above-described combustion heating and the above-described electric heating so as to be a glass substrate having an alkali metal oxide content of 0 to 0.4 mol%, the calorific value caused by the combustion heating is relatively The combustion heating and the energization heating are performed so that the ratio of the amount of heat generation due to the electric conduction heating is 1.0 or more and 3.4 or less.
(形態28)(Form 28)
一種玻璃基板製造裝置,其特徵在於包括:熔解槽本體,其具有氣相空間,貯存熔融玻璃;燃燒機構,其於上述氣相空間中進行燃燒加熱而加熱玻璃原料及/或上述熔融玻璃;電極對,其設置於與熔融玻璃接觸之壁,以對上述玻璃原料及/ 或上述熔融玻璃進行通電加熱;及澄清槽,其利用上述熔融玻璃中所含之氧化錫之氧化還原反應進行上述熔融玻璃之澄清;且於以成為黏度為102.5 泊時之溫度為1500℃以上之玻璃之方式利用上述燃燒加熱及上述通電加熱製作上述熔融玻璃時,以上述燃燒加熱所引起之發熱量相對於上述通電加熱所引起之發熱量的比成為1.0以上且3.4以下之方式進行上述燃燒加熱及上述通電加熱。A glass substrate manufacturing apparatus, comprising: a melting tank body having a gas phase space for storing molten glass; and a burning mechanism for heating and heating the glass raw material and/or the molten glass in the gas phase space; Further, it is provided on a wall in contact with the molten glass to electrically heat the glass raw material and/or the molten glass; and a clarification tank which performs the above-described molten glass by a redox reaction of tin oxide contained in the molten glass In the case where the molten glass is produced by the above-described combustion heating and the above-described electric heating in the case where the temperature is 1500 ° C or higher at a temperature of 10 2.5 poise, the amount of heat generated by the combustion heating is increased with respect to the electric current. The above-described combustion heating and the above-described electric heating are performed so that the ratio of the amount of heat generated by heating is 1.0 or more and 3.4 or less.
根據上述形態之玻璃基板之製造方法及玻璃基板製造裝置,即便於使用難熔之玻璃製造玻璃基板之情形時,亦可減少未熔解物之產生,且可藉由充分地發揮澄清劑之效果而減少泡之產生。According to the method for producing a glass substrate and the glass substrate manufacturing apparatus of the above aspect, even when a glass substrate is produced using refractory glass, the generation of unmelted material can be reduced, and the effect of the clarifying agent can be sufficiently exhibited. Reduce the generation of bubbles.
100‧‧‧熔解裝置100‧‧‧melting device
101‧‧‧熔解槽101‧‧‧melting tank
101a‧‧‧螺旋給料機101a‧‧‧Spiral feeder
101b‧‧‧原料投入口101b‧‧‧ raw material input
101c‧‧‧底壁101c‧‧‧ bottom wall
102‧‧‧澄清槽102‧‧‧Clarification tank
102a、102b‧‧‧金屬製凸緣102a, 102b‧‧‧Metal flange
102c‧‧‧透氣管102c‧‧‧ Breathable tube
103‧‧‧攪拌槽103‧‧‧Stirring tank
103a‧‧‧攪拌器103a‧‧‧Agitator
104、105、106‧‧‧玻璃供給管104, 105, 106‧‧‧ glass supply tube
104a‧‧‧流出口104a‧‧‧Exit
110‧‧‧熔解槽本體110‧‧‧melting tank body
112‧‧‧燃燒器112‧‧‧ burner
112a‧‧‧氣體源112a‧‧‧ gas source
112b‧‧‧流量調整裝置112b‧‧‧Flow adjustment device
114‧‧‧電極對114‧‧‧electrode pair
116‧‧‧氣相空間隔離壁116‧‧‧ gas phase space partition
118‧‧‧槽頂部118‧‧‧Slot top
118a‧‧‧溫度感測器118a‧‧‧Temperature Sensor
120‧‧‧控制單元120‧‧‧Control unit
122‧‧‧電腦122‧‧‧ computer
124‧‧‧鋪墊部124‧‧‧Bedding Department
126‧‧‧底部126‧‧‧ bottom
200‧‧‧成形裝置200‧‧‧Forming device
210‧‧‧成形體210‧‧‧Formed body
300‧‧‧切斷裝置300‧‧‧cutting device
MG‧‧‧熔融玻璃MG‧‧‧ molten glass
SG‧‧‧平板玻璃SG‧‧ ‧ flat glass
圖1係表示本實施形態之玻璃基板之製造方法之流程的圖。Fig. 1 is a view showing the flow of a method for producing a glass substrate of the present embodiment.
圖2係模式性地表示進行本實施形態中之熔解步驟~切斷步驟之玻璃基板製造裝置之一例的圖。Fig. 2 is a view schematically showing an example of a glass substrate manufacturing apparatus which performs the melting step to the cutting step in the embodiment.
圖3係說明本實施形態中熔解步驟至成形步驟之熔融玻璃之溫度歷程之較佳形態之例的圖。Fig. 3 is a view showing an example of a preferred embodiment of the temperature history of the molten glass in the melting step to the forming step in the embodiment.
圖4係說明本實施形態之玻璃基板製造裝置所使用之澄清槽之一例的圖。Fig. 4 is a view showing an example of a clarification tank used in the glass substrate manufacturing apparatus of the embodiment.
圖5係說明本實施形態之玻璃基板之製造方法所使用之熔解槽之熔解槽本體及其周邊之構造之概略的立體圖。Fig. 5 is a perspective view showing the structure of the melting tank main body of the melting tank used in the method for producing the glass substrate of the embodiment and the structure around the same.
圖6係說明圖5所示之熔解槽之剖面的圖。Fig. 6 is a view showing a cross section of the melting tank shown in Fig. 5.
以下,對本實施形態之玻璃基板之製造方法及玻璃基板製造裝置進行說明。Hereinafter, a method of producing a glass substrate and a glass substrate manufacturing apparatus of the present embodiment will be described.
(玻璃基板之製造方法之整體概要)(Overall outline of the manufacturing method of the glass substrate)
圖1係表示本實施形態之玻璃基板之製造方法之流程的圖。Fig. 1 is a view showing the flow of a method for producing a glass substrate of the present embodiment.
玻璃基板之製造方法主要包括:熔解步驟(ST1)、澄清步驟(ST2)、均質化步驟(ST3)、供給步驟(ST4)、成形步驟(ST5)、緩冷步驟(ST6)及切斷步驟(ST7)。此外,亦包括研削步驟、研磨步驟、洗淨步驟、檢查步驟及捆包步驟等。The manufacturing method of the glass substrate mainly includes a melting step (ST1), a clarification step (ST2), a homogenization step (ST3), a supply step (ST4), a molding step (ST5), a slow cooling step (ST6), and a cutting step ( ST7). In addition, the grinding step, the grinding step, the washing step, the inspection step, and the packing step are also included.
熔解步驟(ST1)係於熔解槽中進行。於熔解槽中,將玻璃原料投入至熔解槽中,藉由進行加熱而使其熔解,製造含有氧化錫之熔融玻璃。該熔融玻璃於某形態中係黏度為102.5 泊時之溫度為1580℃以上之高溫黏性較高之熔融玻璃。又,於另一形態中,係成為應變點(相當於黏度為1014.5 dPa.秒之溫度)為680℃以上之玻璃之熔融玻璃。此外,於另一實施形態中,係黏度為102.5 泊時之溫度為1500℃以上之高溫黏性較高之熔融玻璃。於另一形態中,係成為鹼金屬氧化物之含有率為0~0.4莫耳%之玻璃基板之熔融玻璃。以形成此種熔融玻璃之方式預先調製玻璃原料。進而,使貯存於熔解槽之熔融玻璃自設置於熔解槽之內側側壁之一底部之流出口朝向下游步驟流動。The melting step (ST1) is carried out in a melting tank. In the melting tank, the glass raw material is placed in a melting tank, and is melted by heating to produce molten glass containing tin oxide. The molten glass is a molten glass having a high viscosity at a temperature of 10,500 ° C or higher at a viscosity of 10 2.5 poise in a certain form. Further, in another embodiment, it is a molten glass of glass having a strain point (corresponding to a temperature of 10 14.5 dPa.sec.) of 680 ° C or higher. Further, in another embodiment, the molten glass having a high viscosity at a temperature of 1500 ° C or higher at a viscosity of 10 2.5 poise is used. In another embodiment, it is a molten glass of a glass substrate having an alkali metal oxide content of 0 to 0.4 mol%. The glass raw material is prepared in advance so as to form such molten glass. Further, the molten glass stored in the melting tank is caused to flow from the outlet opening provided at the bottom of one of the inner side walls of the melting tank toward the downstream step.
熔解槽之熔融玻璃之加熱例如係利用使用由燃燒器產生之燃燒氣體之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱而進行,藉此製作特定之黏度之熔融玻璃。具體而言,投入之玻璃原料係懸浮於貯存之熔融玻璃之液面,利用來自熔解槽之氣相空間或燃燒器之火焰之熱輻射傳熱進行加熱,又,利用經通電加熱之熔融玻璃進行加熱,從而使其熱分解而熔解。以如此之方式形成之熔融玻璃被通電加熱至更高溫。又,熔融玻璃係利用來自熔解槽之氣相空間之壁面或燃燒器之火焰之熱輻射傳熱被加熱至更高溫。熔融玻璃含有氧化錫作為澄清劑。關於As2 O3 、Sb2 O3 ,就環境負荷之方面而言,較佳為熔融玻璃中實質上不含。所謂實質上不含,係指即便含有該等物質,亦以雜質之形式含有,具體而言,該等物質較佳為0.1莫耳%以 下。就該方面而言,至少使用氧化錫作為澄清劑。再者,亦可於玻璃原料中預先添加澄清劑。於熔解槽中,以玻璃原料之熔解殘留不流出之方式使玻璃原料完全熔解,並且以成為使後續步驟得以適當進行之特定之黏度之方式加熱熔融玻璃。The heating of the molten glass in the melting tank is performed, for example, by combustion heating in a gas phase using a combustion gas generated by a burner and electric heating by flowing a current to the molten glass, thereby producing a specific viscosity molten glass. . Specifically, the input glass raw material is suspended in the liquid surface of the stored molten glass, and is heated by heat radiation heat transfer from a gas phase space of the melting tank or a flame of the burner, and is further performed by using the molten glass heated by electric conduction. It is heated to cause it to thermally decompose and melt. The molten glass formed in such a manner is electrically heated to a higher temperature. Further, the molten glass is heated to a higher temperature by heat radiation heat transfer from the wall surface of the gas phase space of the melting tank or the flame of the burner. The molten glass contains tin oxide as a fining agent. As 2 O 3 and Sb 2 O 3 , it is preferable that the molten glass is substantially not contained in terms of environmental load. The term "substantially free" means that the substance is contained in the form of impurities even if it is contained. Specifically, the substance is preferably 0.1 mol% or less. In this respect, at least tin oxide is used as a fining agent. Further, a clarifying agent may be added to the glass raw material in advance. In the melting tank, the glass raw material is completely melted so that the melting residue of the glass raw material does not flow out, and the molten glass is heated so as to have a specific viscosity which allows the subsequent step to be appropriately performed.
澄清步驟(ST2)至少於澄清槽中進行。於澄清步驟中,於具有與大氣連通之氣相空間之澄清槽內使熔融玻璃升溫,藉此熔融玻璃中所含之含O2 、CO2 或SO2 之泡之體積因吸收澄清劑藉由還原反應而釋出之氧而變大。因此,泡之浮起速度上升,泡浮起至熔融玻璃之液面,藉此釋出至氣相空間(脫泡處理)。進而,於澄清步驟中,藉由降低熔融玻璃之溫度而使利用澄清劑之還原反應而獲得之還原物質發生氧化反應。藉此,殘存於熔融玻璃之泡中之氧等氣體成分被再吸收至熔融玻璃中而使泡消亡(吸收處理)。利用澄清劑之氧化反應及還原反應係藉由控制熔融玻璃之溫度而進行。再者,於澄清步驟中至少使用氧化錫作為澄清劑。The clarification step (ST2) is carried out at least in the clarification tank. In the clarification step, the molten glass is heated in a clarification tank having a gas phase space in communication with the atmosphere, whereby the volume of the bubbles containing O 2 , CO 2 or SO 2 contained in the molten glass is absorbed by the clarifying agent. The oxygen released by the reduction reaction becomes large. Therefore, the floating speed of the bubble rises, and the bubble floats up to the liquid surface of the molten glass, thereby being released to the gas phase space (defoaming treatment). Further, in the clarification step, the reducing substance obtained by the reduction reaction using the clarifying agent is oxidized by lowering the temperature of the molten glass. Thereby, the gas component such as oxygen remaining in the bubble of the molten glass is reabsorbed into the molten glass to cause the bubble to die (absorption treatment). The oxidation reaction and the reduction reaction using the clarifying agent are carried out by controlling the temperature of the molten glass. Further, at least tin oxide is used as a fining agent in the clarification step.
於均質化步驟(ST3)中,使用攪拌器對自澄清槽通過延伸之配管供給之攪拌槽內之熔融玻璃進行攪拌,藉此進行玻璃成分之均質化。藉此,可減少作為條紋等之原因之玻璃之組成不均。In the homogenization step (ST3), the molten glass in the stirring tank supplied from the clarification tank through the extending pipe is stirred by a stirrer to homogenize the glass component. Thereby, the composition unevenness of the glass which is a cause of a stripe etc. can be reduced.
於供給步驟(ST4)中,自攪拌槽通過延伸之配管將熔融玻璃供給至成形裝置。In the supply step (ST4), the molten glass is supplied from the stirring tank to the forming apparatus through the extending pipe.
於成形裝置中,進行成形步驟(ST5)及緩冷步驟(ST6)。In the molding apparatus, a forming step (ST5) and a slow cooling step (ST6) are performed.
於成形步驟(ST5)中,使熔融玻璃成形為平板玻璃而製作平板玻璃之流。成形係使用溢流下拉法。In the molding step (ST5), the molten glass is formed into a flat glass to produce a flow of flat glass. The forming system uses an overflow down-draw method.
於緩冷步驟(ST6)中,將成形而流動之平板玻璃以成為所期望之厚度,不產生內部變形,進而不產生翹曲之方式進行冷卻。In the slow cooling step (ST6), the sheet glass which is formed and flows is cooled to a desired thickness without causing internal deformation and without warping.
於切斷步驟(ST7)中,於切斷裝置中,將自成形裝置供給之平板玻璃切斷成特定之長度,藉此獲得板狀之玻璃基板。In the cutting step (ST7), the sheet glass supplied from the forming apparatus is cut into a specific length in the cutting device, whereby a plate-shaped glass substrate is obtained.
圖2係模式性地表示進行本實施形態中之熔解步驟(ST1)~切斷步驟(ST7)之玻璃基板製造裝置之一例的圖。如圖2所示,該裝置主要包括熔解裝置100、成形裝置200、切斷裝置300。熔解裝置100包括熔解槽101、澄清槽102、攪拌槽103及玻璃供給管104、105、106。FIG. 2 is a view schematically showing an example of a glass substrate manufacturing apparatus that performs the melting step (ST1) to the cutting step (ST7) in the present embodiment. As shown in FIG. 2, the apparatus mainly includes a melting apparatus 100, a forming apparatus 200, and a cutting apparatus 300. The melting apparatus 100 includes a melting tank 101, a clarification tank 102, a stirring tank 103, and glass supply pipes 104, 105, and 106.
於圖2所示之熔解裝置101中,玻璃原料之投入使用螺旋給料機101a進行,以藉由該玻璃原料之熔解而獲得之熔融玻璃MG成為特定之黏度之方式加熱熔融玻璃MG。於澄清槽102中,調整熔融玻璃MG之溫度,利用澄清劑之氧化還原反應進行熔融玻璃MG之澄清。進而,於攪拌槽103中,利用攪拌器103a攪拌熔融玻璃MG而使其均質化。於成形裝置200中,利用使用成形體210之溢流下拉法自熔融玻璃MG成形平板玻璃SG。In the melting apparatus 101 shown in FIG. 2, the glass raw material is placed in the screw feeder 101a, and the molten glass MG is heated so that the molten glass MG obtained by melting the glass raw material becomes a specific viscosity. In the clarification tank 102, the temperature of the molten glass MG is adjusted, and the clarification of the molten glass MG is performed by the oxidation-reduction reaction of a clarifier. Further, in the stirring tank 103, the molten glass MG is stirred by the agitator 103a to be homogenized. In the molding apparatus 200, the sheet glass SG is formed from the molten glass MG by the overflow down-draw method using the molded body 210.
圖3係說明本實施形態中之熔解步驟至成形步驟之熔融玻璃之溫度歷程之較佳形態之例的圖。Fig. 3 is a view showing an example of a preferred embodiment of the temperature history of the molten glass in the melting step to the forming step in the embodiment.
於熔解槽101中,自投入玻璃原料之時點之溫度T1起至進入至玻璃供給管104之時點之溫度T3為止,具有熔融玻璃MG之溫度平穩地上升的溫度歷程。再者,於圖3中,為T1<T2<T3,但亦可為T2=T3或T2>T3,只要至少T1<T3即可。In the melting tank 101, the temperature history of the molten glass MG rises steadily from the temperature T1 at the time of input of the glass raw material to the temperature T3 at the time of entering the glass supply pipe 104. Further, in FIG. 3, T1 < T2 < T3, but T2 = T3 or T2 > T3 may be used as long as at least T1 < T3.
圖4係說明澄清槽102之一例的圖。澄清槽102例如係包含鉑或金合金等之圓筒狀之容器,長度方向(圖4之左右方向)之兩端分別連接有玻璃供給管104、105。於澄清槽102之長度方向之兩端分別設置有自澄清槽102之表面向外周側突出之圓板狀之金屬製凸緣102a、102b。於澄清槽102之長度方向之兩端間之中途之頂部設置有將氣相空間與外部氛圍連通之透氣管102c。自熔融玻璃釋出之氣體通過透氣管102c排出至外部。FIG. 4 is a view showing an example of the clarification tank 102. The clarification tank 102 is, for example, a cylindrical container including platinum or a gold alloy, and glass supply pipes 104 and 105 are connected to both ends in the longitudinal direction (the horizontal direction in FIG. 4). Disc-shaped metal flanges 102a and 102b projecting from the surface of the clarification tank 102 toward the outer peripheral side are provided at both ends in the longitudinal direction of the clarification tank 102, respectively. A vent pipe 102c that communicates the gas phase space with the outside atmosphere is provided at the top of the middle of the longitudinal direction of the clarification tank 102. The gas released from the molten glass is discharged to the outside through the vent pipe 102c.
於金屬製凸緣102a、102b分別安裝有未圖示之電極,使來自電極之電流均勻地擴散至澄清槽102之圓周上。藉由於安裝於金屬製凸緣 102a、102b之兩個電極之間通電而使澄清槽102發熱,從而加熱澄清槽102內之熔融玻璃MG。此種金屬製凸緣及電極亦設置於玻璃供給管104。Electrodes (not shown) are attached to the metal flanges 102a and 102b, respectively, and the current from the electrodes is uniformly diffused to the circumference of the clarification tank 102. By mounting on a metal flange The two electrodes 102a and 102b are energized to heat the clarification tank 102, thereby heating the molten glass MG in the clarification tank 102. Such a metal flange and an electrode are also provided in the glass supply tube 104.
於玻璃供給管104之未圖示之金屬製凸緣與澄清槽102之金屬製凸緣102a之間流通一定之電流而對玻璃供給管104之鉑或鉑合金管進行通電加熱,進而於澄清槽102之金屬製凸緣102a與澄清槽102之金屬製凸緣102b之間流通一定之電流而進行加熱,藉此自溫度T3起至氧化錫急遽釋出氧之溫度T4(例如為1630℃以上,更佳為1630~1700℃,進而較佳為1650~1700℃)為止,將熔融玻璃MG之升溫速度較佳為設為2℃/分鐘以上,更佳為設為2.5℃/分鐘以上。更佳為使熔融玻璃MG之溫度以2.5℃/分鐘以上之升溫速度升溫至1630℃以上。此時,較佳為將升溫速度設為上述範圍之原因在於藉由將升溫速度設為上述範圍,O2 氣體之釋出量極為急遽地變大。再者,溫度T3與溫度T4之差越大,熔融玻璃MG中之氧化錫所釋出之O2 之量越多,從而促進脫泡。因此,溫度T4較佳為較溫度T3高例如50℃以上。因此,進行澄清時之熔融玻璃之最高溫度較佳為高於熔解槽中之熔融玻璃之最高溫度。A platinum or platinum alloy tube of the glass supply tube 104 is electrically supplied to the clarification tank by flowing a constant current between the metal flange (not shown) of the glass supply tube 104 and the metal flange 102a of the clarification tank 102. The metal flange 102a of 102 and the metal flange 102b of the clarification tank 102 are heated by a constant current, and the temperature T4 from the temperature T3 to the rapid release of oxygen by the tin oxide (for example, 1630 ° C or more, More preferably, the temperature rise rate of the molten glass MG is preferably 2 ° C / min or more, and more preferably 2.5 ° C / min or more, from 1630 to 1700 ° C, more preferably from 1650 to 1700 ° C. More preferably, the temperature of the molten glass MG is raised to 1630 ° C or higher at a temperature increase rate of 2.5 ° C / min or more. In this case, it is preferable that the temperature increase rate is set to the above range, and the amount of release of the O 2 gas is extremely rapidly increased by setting the temperature increase rate to the above range. Further, the larger the difference between the temperature T3 and the temperature T4, the larger the amount of O 2 released by the tin oxide in the molten glass MG, thereby promoting defoaming. Therefore, the temperature T4 is preferably higher than the temperature T3 by, for example, 50 °C or higher. Therefore, the maximum temperature of the molten glass at the time of clarification is preferably higher than the highest temperature of the molten glass in the melting tank.
進而,使進入至澄清槽102中之熔融玻璃MG自溫度T4起維持在與溫度T4大致相同之溫度T5。再者,關於溫度T3~溫度T5之熔融玻璃MG之溫度調節,於本實施形態中,使用對澄清槽進行通電加熱之方式,但並不限定於該方式。例如,亦可使用利用配置於澄清槽周圍之未圖示之加熱器之間接加熱而進行上述溫度調節。Further, the molten glass MG entering the clarification tank 102 is maintained at a temperature T5 substantially the same as the temperature T4 from the temperature T4. In the temperature adjustment of the molten glass MG of the temperature T3 to the temperature T5, in the present embodiment, the clarification tank is electrically heated, but the method is not limited thereto. For example, the above-described temperature adjustment may be performed by using a heater that is disposed between the heaters (not shown) disposed around the clarification tank.
此時,熔融玻璃MG被加熱至1630℃以上,藉此促進作為澄清劑之氧化錫之氧釋出之反應。藉此,大量之氧釋出至熔融玻璃MG中。熔融玻璃MG中之既存之泡藉由起因於熔融玻璃MG之溫度上升的泡內之氣體成分之壓力上升之效果而使泡徑擴大,於此基礎上疊加地藉由 上述澄清劑之反應而釋出之氧擴散而進入至泡內,從而藉由該協同效果而使泡徑擴大。At this time, the molten glass MG is heated to 1630 ° C or higher, thereby promoting the reaction of releasing oxygen of tin oxide as a fining agent. Thereby, a large amount of oxygen is released into the molten glass MG. The existing bubble in the molten glass MG expands the bubble diameter by the effect of increasing the pressure of the gas component in the bubble due to the temperature rise of the molten glass MG, and superimposes on the basis of The oxygen released by the reaction of the clarifying agent diffuses into the bubble, thereby expanding the bubble diameter by the synergistic effect.
關於泡徑擴大之泡,依據Stokes定律,泡之浮起速度變快,從而促進泡之浮起、破泡。Regarding the bubble whose bubble diameter is enlarged, according to Stokes' law, the floating speed of the bubble becomes faster, thereby promoting the floating and breaking of the bubble.
於澄清槽102中,熔融玻璃MG亦持續維持在1630℃以上之高溫,因此熔融玻璃MG中之泡浮起至熔融玻璃MG之液表面並於液表面破泡,藉此進行熔融玻璃MG之脫泡。In the clarification tank 102, since the molten glass MG is maintained at a high temperature of 1630 ° C or more, the bubble in the molten glass MG floats up to the surface of the molten glass MG and is broken on the surface of the liquid, thereby performing the detachment of the molten glass MG. bubble.
於圖3中,脫泡處理係於熔融玻璃MG之溫度自溫度T3上升至溫度T4,其後維持在與溫度T4大致相同之溫度T5之期間進行。圖3中,T4與T5大致相同,但可T4<T5,亦可T4>T5。In FIG. 3, the defoaming treatment is performed while the temperature of the molten glass MG rises from the temperature T3 to the temperature T4, and thereafter is maintained at a temperature T5 which is substantially the same as the temperature T4. In Fig. 3, T4 and T5 are substantially the same, but T4 < T5 or T4 > T5.
再者,熔融玻璃MG之溫度達到溫度T4之場所可為玻璃供給管104,亦可為澄清槽102內。Further, the place where the temperature of the molten glass MG reaches the temperature T4 may be the glass supply pipe 104 or the inside of the clarification tank 102.
又,熔融玻璃MG流經玻璃供給管104時之熔融玻璃MG之第1最高溫度較佳為與流經澄清槽102內時之熔融玻璃MG之第2最高溫度同等、或高於該第2最高溫度。藉此,於熔融玻璃MG自玻璃供給管104移動至澄清槽102時,熔融玻璃MG之溫度足夠高而維持在使澄清劑之釋出氧之反應發生之溫度以上,因此澄清槽102無需用以將熔融玻璃MG進一步升溫之加熱。因此,可將澄清槽102之加熱溫度抑制為低於先前。因此,可抑制鉑自包含鉑或鉑合金之澄清槽102揮發,從而可製造因鉑之揮發而附著於澄清槽102內之內壁面之鉑結晶物等異物混入至熔融玻璃MG中而形成之缺陷,即起因於異物之缺陷較少之玻璃基板。較佳為於熔融玻璃MG流經玻璃供給管104之中途,熔融玻璃MG之溫度達到第1最高溫度。此情形與熔融玻璃在玻璃供給管104與澄清槽102之連接位置達到第1最高溫度及第2最高溫度之情形相比,澄清槽102之加熱溫度降低,因此可更容易地抑制鉑自包含鉑或鉑合金之澄清槽102揮發。Further, the first maximum temperature of the molten glass MG when the molten glass MG flows through the glass supply pipe 104 is preferably equal to or higher than the second highest temperature of the molten glass MG when flowing through the clarification tank 102. temperature. Accordingly, when the molten glass MG is moved from the glass supply tube 104 to the clarification tank 102, the temperature of the molten glass MG is sufficiently high to be maintained at a temperature higher than the temperature at which the reaction of releasing the clarifying agent to oxygen occurs, so that the clarification tank 102 is not required to be used. The molten glass MG is further heated by heating. Therefore, the heating temperature of the clarification tank 102 can be suppressed to be lower than the previous one. Therefore, it is possible to suppress the volatilization of platinum from the clarification tank 102 containing platinum or a platinum alloy, and it is possible to produce a defect in which foreign matter such as platinum crystals adhering to the inner wall surface of the clarification tank 102 due to volatilization of platinum is mixed into the molten glass MG. That is, a glass substrate which is caused by a defect of foreign matter is less. Preferably, the molten glass MG flows through the glass supply pipe 104, and the temperature of the molten glass MG reaches the first highest temperature. In this case, the heating temperature of the clarification tank 102 is lowered as compared with the case where the connection position of the molten glass at the glass supply pipe 104 and the clarification tank 102 reaches the first highest temperature and the second highest temperature, so that the platinum self-contained platinum can be more easily suppressed. Or the clarification tank 102 of the platinum alloy is volatilized.
繼而,對於自澄清槽102進入至玻璃供給管105之熔融玻璃MG,為了吸收殘存之泡,而將其自溫度T5,經由溫度T6(例如,1600℃),冷卻至溫度T7(為適於攪拌步驟之溫度,根據玻璃種類及攪拌裝置103之類型而有所不同,例如為1500℃)。Then, the molten glass MG entering the glass supply tube 105 from the clarification tank 102 is cooled from the temperature T5 to the temperature T7 (for 1600 ° C) to absorb the remaining bubbles (for stirring) The temperature of the step varies depending on the type of the glass and the type of the stirring device 103, for example, 1500 ° C).
藉由使熔融玻璃MG之溫度降低,在不產生泡之浮起、脫泡下,殘存於熔融玻璃MG之小泡中之氣體成分之壓力亦降低,從而泡徑不斷變小。進而,若熔融玻璃MG之溫度成為1600℃以下,則釋出氧之氧化錫之一部分欲吸收氧而恢復為原本之氧化錫。因此,熔融玻璃MG中所殘存之泡內之氧被再吸收至熔融玻璃MG中,從而使小泡進一步變小。該小泡被熔融玻璃MG吸收而最終消亡。By lowering the temperature of the molten glass MG, the pressure of the gas component remaining in the vesicles of the molten glass MG is also lowered without causing bubbling or defoaming, and the bubble diameter is continuously reduced. Further, when the temperature of the molten glass MG is 1600 ° C or lower, one part of the tin oxide which releases oxygen is to absorb oxygen and return to the original tin oxide. Therefore, the oxygen in the bubbles remaining in the molten glass MG is reabsorbed into the molten glass MG, so that the vesicles are further reduced. The vesicles are absorbed by the molten glass MG and eventually die.
該藉由SnO吸收氧之反應而吸收作為泡內之氣體成分之氧的處理為吸收處理,於自溫度T5經由溫度T6而降低至溫度T7之期間進行。於圖3中,溫度T5~T6之降溫速度與溫度T6~T7之降溫速度相比較快,但溫度T5~T6之降溫速度與溫度T6~T7之降溫速度相比可較慢,亦可同等。較佳為至少於該吸收處理期間,使熔融玻璃MG之溫度於1600℃至1500℃之溫度範圍內以2℃/分鐘以上之降溫速度降溫,更佳之降溫速度為2.5℃/分鐘以上。於吸收處理中,熔融玻璃MG為1500℃以下(具體而言,為1500℃至供給至成形步驟時之熔融玻璃溫度為止之範圍,例如為1500℃~1300℃)之溫度範圍中之降溫速度較佳為與1600℃至1500℃之溫度範圍中之降溫速度相比較慢。The treatment of absorbing oxygen as a gas component in the bubble by the reaction of absorbing oxygen by SnO is an absorption treatment, and is performed while decreasing from temperature T5 to temperature T7 via temperature T6. In Fig. 3, the temperature drop rate of temperature T5~T6 is faster than the temperature drop rate of temperature T6~T7, but the temperature drop rate of temperature T5~T6 can be slower than the temperature drop rate of temperature T6~T7, and can be equal. Preferably, at least during the absorption treatment, the temperature of the molten glass MG is lowered in a temperature range of 1600 ° C to 1500 ° C at a temperature drop rate of 2 ° C / min or more, and more preferably, the temperature drop rate is 2.5 ° C / min or more. In the absorption treatment, the molten glass MG has a temperature drop rate in a temperature range of 1500 ° C or lower (specifically, a range from 1500 ° C to a molten glass temperature supplied to the forming step, for example, 1500 ° C to 1300 ° C). The temperature is slower than the temperature drop in the temperature range of 1600 ° C to 1500 ° C.
再者,就提高玻璃基板之生產性及削減設備成本之方面而言,於吸收處理中,熔融玻璃MG為1500℃以下(具體而言,為1500℃至供給至成形步驟時之熔融玻璃溫度為止之範圍,例如為1500℃~1300℃)之溫度範圍中之降溫速度較佳為與1600℃至1500℃之溫度範圍中之降溫速度相比較快。再者,於進行此種熔融玻璃MG之溫度控制之情形時,較佳為設置調整供給至成形步驟之熔融玻璃MG之量的流量 調整裝置。In addition, in the absorption treatment, the molten glass MG is 1500 ° C or lower (specifically, it is 1500 ° C until the molten glass temperature is supplied to the molding step) in terms of improving the productivity of the glass substrate and reducing the equipment cost. The range of temperature drop in the range of, for example, 1500 ° C to 1300 ° C is preferably faster than the temperature drop in the temperature range of 1600 ° C to 1500 ° C. Further, in the case of performing temperature control of the molten glass MG, it is preferable to provide a flow rate for adjusting the amount of the molten glass MG supplied to the forming step. Adjust the device.
於上述吸收處理後、或吸收處理之中途,熔融玻璃MG進入至攪拌槽103中。攪拌槽103減小熔融玻璃MG中之組成不均而使熔融玻璃MG均質化。再者,亦可於攪拌槽103中繼續進行上述吸收處理。其後,將熔融玻璃MG降溫,直至成為適於成形步驟中之成形的溫度T8,例如1200~1300℃為止。The molten glass MG enters the stirring tank 103 after the above-described absorption treatment or during the absorption treatment. The agitation vessel 103 reduces the composition unevenness in the molten glass MG to homogenize the molten glass MG. Further, the above-described absorption treatment may be continued in the agitation vessel 103. Thereafter, the molten glass MG is cooled until it reaches a temperature T8 suitable for molding in the molding step, for example, 1200 to 1300 °C.
經由以上之熔融玻璃MG之溫度歷程而將熔融玻璃MG供給至成形裝置200。The molten glass MG is supplied to the forming apparatus 200 through the temperature history of the molten glass MG described above.
於以此種玻璃基板之製造方法及玻璃基板製造裝置進行之熔解玻璃原料而製作熔融玻璃、進而加熱熔融玻璃之熔解步驟中,如上所述,利用使用由燃燒器產生之氣體之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱。尤其是為了製作熱收縮較小之玻璃基板,利用難熔性之玻璃,例如黏度為102.5 泊時之溫度為1580℃以上之高溫黏性較高之玻璃、以及應變點為680℃以上之玻璃、黏度為102.5 泊時之溫度為1500℃以上之高溫黏性較高之玻璃組成之玻璃、鹼金屬氧化物之含有率為0~0.4莫耳%且熔融溫度較高之玻璃組成之玻璃(無鹼玻璃或含有微量鹼之玻璃)之情形與先前之非難熔、且高溫黏性不高、且應變點不高之玻璃組成之玻璃,以及含有多於0.4莫耳%之鹼金屬氧化物之鹼玻璃之情形相比,使利用燃燒器之燃燒加熱及通電加熱之發熱量增大。In the melting step of producing the molten glass and further heating the molten glass by the method for producing a glass substrate and the glass substrate manufacturing apparatus, as described above, in the gas phase using the gas generated by the burner Combustion heating and energization heating by flowing a current through the molten glass. Especially in order to produce small heat shrinkage of the glass substrate, the glass is difficult to use the infusible, for example a temperature viscosity of 10 2.5 poise or higher temperature of 1580 deg.] C higher viscosity of the glass, and the strain point of the glass 680 ℃ The glass having a viscosity of 10 2.5 poises and having a high temperature viscosity of 1500 ° C or higher, glass having an alkali metal oxide content of 0 to 0.4 mol %, and a glass having a higher melting temperature ( An alkali-free glass or a glass containing a small amount of alkali) and a glass composed of a glass which is not refractory, has high viscosity at a high temperature, and has a low strain point, and an alkali metal oxide containing more than 0.4 mol%. In the case of alkali glass, the amount of heat generated by combustion heating and electric heating by the burner is increased.
此時,於本實施形態中,規定燃燒加熱所引起之發熱量相對於通電加熱所引起之發熱量的比(以下稱為發熱量比)而進行燃燒加熱及通電加熱。以下,詳細地說明熔解槽中之熔融玻璃之加熱。In this case, in the present embodiment, the ratio of the amount of heat generated by the combustion heating to the amount of heat generated by the electric heating (hereinafter referred to as the calorific value) is defined to perform combustion heating and electric heating. Hereinafter, the heating of the molten glass in the melting tank will be described in detail.
(熔解槽)(melting tank)
圖5係說明熔解槽101之熔解槽本體及其周邊之構造之概略的立體圖,圖6係說明熔解槽101之剖面的圖。將自玻璃原料之投入口朝向 熔融玻璃流向後續步驟之流出口的方向稱為熔解槽101之長度方向時,圖6所示之剖面為圖5所示之設置有電極114之長度方向之位置之熔解槽101之剖面。Fig. 5 is a schematic perspective view showing a structure of a melting tank main body of the melting tank 101 and its periphery, and Fig. 6 is a view showing a cross section of the melting tank 101. Oriented from the input port of the glass raw material When the direction in which the molten glass flows to the outlet of the subsequent step is referred to as the longitudinal direction of the melting tank 101, the cross section shown in Fig. 6 is a cross section of the melting tank 101 in the longitudinal direction of the electrode 114 shown in Fig. 5.
於本實施形態中,熔解槽101主要包括熔解槽本體110、燃燒器112、電極對114及槽頂部118。In the present embodiment, the melting tank 101 mainly includes a melting tank body 110, a burner 112, an electrode pair 114, and a tank top 118.
熔解槽本體110於上部具有氣相空間,於下部具有貯存熔融玻璃之部分。熔解槽本體110貯存含有氧化錫且黏度為102.5 泊時之溫度為1580度以上的熔融玻璃。於熔解槽本體110中,將調製而成之玻璃原料投入至已貯存之熔融玻璃MG之液面而浮於該液面之一部分。該玻璃原料熔解而成為熔融玻璃。由於玻璃原料浮起至熔融玻璃之液面之一部分,因此自熔融玻璃產生之氣體或未充分熔解之雜質混合存在而形成於液面之發泡層僅存在於液面之一部分。因此,玻璃原料除了受到後述之氣相空間之輻射熱以外,亦受到經由經通電加熱之熔融玻璃而流動之熱而使玻璃原料熔解。The melting tank body 110 has a gas phase space at the upper portion and a portion for storing the molten glass at the lower portion. The melting tank body 110 stores molten glass containing tin oxide and having a viscosity of 102.5 poise at a temperature of 1,580 degrees or more. In the melting tank main body 110, the prepared glass raw material is put into the liquid surface of the stored molten glass MG and floats on a part of the liquid surface. This glass raw material melts and becomes molten glass. Since the glass raw material floats up to a part of the liquid surface of the molten glass, a gas generated from the molten glass or an impurity which is not sufficiently melted is mixed and the foamed layer formed on the liquid surface exists only in one part of the liquid surface. Therefore, in addition to the radiant heat of the gas phase space to be described later, the glass raw material is also melted by the heat flowing through the molten glass heated by the electric current to melt the glass raw material.
燃燒器112於包圍熔解槽本體110之氣相空間之氣相空間隔離壁116中相互對向之壁上之長度方向之三個不同之位置,於相互對向之壁設置有三對。圖5中僅表示設置於熔解槽本體110之內側之燃燒器112。燃燒器112使混合有燃料氣體及氧等之燃燒氣體燃燒而產生火焰。自氣體源112a(參照圖5)供給至燃燒器112之燃燒氣體於中途使用流量調整裝置112b進行流量調整。流量調整裝置112b藉由來自電腦122之控制信號控制燃燒氣體之流量。燃燒氣體為例如甲烷與氧之混合氣體。再者,燃料氣體之種類並不限定於甲烷。又,代替將燃料氣體與氧混合,可將燃料氣體與空氣混合,或者亦可不混合而分別送入至熔解槽內。The burners 112 are disposed at three different positions in the longitudinal direction of the wall opposite to each other in the gas phase space partition wall 116 surrounding the gas phase space of the melting tank body 110, and three pairs are provided on the mutually opposing walls. Only the burner 112 disposed inside the melting tank body 110 is shown in FIG. The burner 112 burns a combustion gas mixed with a fuel gas and oxygen to generate a flame. The flow rate is adjusted by the flow rate adjusting device 112b in the middle of the combustion gas supplied from the gas source 112a (see FIG. 5) to the burner 112. The flow rate adjusting device 112b controls the flow of the combustion gas by a control signal from the computer 122. The combustion gas is, for example, a mixed gas of methane and oxygen. Furthermore, the type of fuel gas is not limited to methane. Further, instead of mixing the fuel gas with oxygen, the fuel gas may be mixed with the air or may be separately fed into the melting tank without mixing.
電極對114係於熔解槽本體110之側壁部之長度方向之三個不同之位置,以隔著熔融玻璃而相互對向之方式設置有3對,以對熔融玻璃 進行通電加熱。圖5中僅表示設置於熔解槽本體110之近前側之側壁部之電極對114之電極。電極對114使用例如氧化錫或鉬等具有耐熱性之導電性材料。電極對114連接於電流控制裝置120而接受由電流控制裝置120控制之電流之供給。電流控制裝置120與電腦122連接,並利用電腦122之控制信號控制流通於電極對114之電量。如此,電腦122產生控制上述燃燒氣體之流量的控制信號及控制流通於電極對114之電流的控制信號。The electrode pair 114 is disposed at three different positions in the longitudinal direction of the side wall portion of the melting tank body 110, and is provided with three pairs facing each other with the molten glass interposed therebetween. Electric heating is performed. In Fig. 5, only the electrodes of the electrode pairs 114 provided on the side wall portions on the near side of the melting tank body 110 are shown. The electrode pair 114 is made of a conductive material having heat resistance such as tin oxide or molybdenum. The electrode pair 114 is connected to the current control device 120 to receive the supply of current controlled by the current control device 120. The current control device 120 is connected to the computer 122 and controls the amount of electricity flowing through the electrode pair 114 by the control signal of the computer 122. In this manner, the computer 122 generates a control signal for controlling the flow rate of the combustion gas and a control signal for controlling the current flowing through the electrode pair 114.
此時,以上述發熱量比包含在預先設定之範圍內之方式控制燃燒氣體之流量及電流之流量。於本實施形態中,電腦122控制燃燒氣體之流量及電流之流量,但亦可操作員設定而控制燃燒氣體之流量及電流之流量。於此情形時,亦以上述發熱量比成為1.0~3.4、較佳為成為1.5~3.4之方式控制燃燒氣體之流量及電流之流量。At this time, the flow rate of the combustion gas and the flow rate of the current are controlled such that the above-described heat generation ratio is included in a predetermined range. In the present embodiment, the computer 122 controls the flow rate of the combustion gas and the flow rate of the current, but the flow rate of the combustion gas and the flow rate of the current can be controlled by the operator. In this case, the flow rate of the combustion gas and the flow rate of the current are also controlled so that the calorific value is 1.0 to 3.4, preferably 1.5 to 3.4.
再者,於本實施形態中,使用使燃燒氣體燃燒而產生火焰之燃燒器112作為燃燒機構,但於本實施形態中,燃燒機構並不限定於燃燒器112,只要為於氣相中進行燃燒加熱者即可。又,圖5中列舉具備三對燃燒器112之例進行說明,但燃燒器112亦可僅配置於單側之壁面,或於兩側之壁面相互交錯地配置。又,燃燒器112及電極對114之個數並無特別限定,只要為至少2以上即可。Further, in the present embodiment, the burner 112 that burns the combustion gas to generate a flame is used as the combustion mechanism. However, in the present embodiment, the combustion mechanism is not limited to the burner 112, and combustion is performed in the gas phase. It can be heated. 5, an example in which three pairs of burners 112 are provided will be described. However, the burners 112 may be disposed only on one side of the wall surface or on the wall surfaces on both sides. Further, the number of the burners 112 and the electrode pairs 114 is not particularly limited, and may be at least two or more.
氣相空間隔離壁116係熔解槽本體110之一部分,為設置於熔融玻璃之貯存部分之上部的壁。於該壁設置有燃燒器112。又,於氣相空間隔離壁116設置有原料投入口101b,藉由螺旋給料機101a(參照圖2)通過該原料投入口101b供給玻璃原料。於與熔解槽本體110之原料投入口101b對向之側壁之熔解槽本體110之底部附近設置有流出口104a。熔解槽101係使熔融玻璃自流出口104a朝向後續步驟流動。再者,原料投入亦可利用螺旋給料機以外之投入方法進行。又,原料投入口101b之位置亦並不限定於圖5所示之位置,亦可設置於氣相空間 隔離壁116之任何位置。The gas phase space partition wall 116 is a portion of the melting tank body 110 and is a wall provided on the upper portion of the storage portion of the molten glass. A burner 112 is provided on the wall. Moreover, the raw material input port 101b is provided in the gas phase space partitioning wall 116, and the glass raw material is supplied through the raw material input port 101b by the screw feeder 101a (refer FIG. 2). An outlet port 104a is provided in the vicinity of the bottom of the melting tank main body 110 facing the side wall of the raw material input port 101b of the melting tank main body 110. The melting tank 101 causes the molten glass to flow from the outflow port 104a toward the subsequent step. Further, the raw material input can also be carried out by an input method other than the screw feeder. Moreover, the position of the raw material input port 101b is not limited to the position shown in FIG. 5, and may be set in the gas phase space. Any location of the partition wall 116.
槽頂部118係將熔解槽101之氣相空間封閉之頂壁。於槽頂部118之頂部設置有溫度感測器118a(參照圖6)。再者,溫度感測器118a亦可安裝於槽頂部118之頂部以外,又,更佳為於槽頂部118之長度方向設置複數個。The trough top 118 is the top wall that closes the gas phase space of the melting tank 101. A temperature sensor 118a (refer to FIG. 6) is disposed at the top of the trough top 118. Furthermore, the temperature sensor 118a can also be mounted on top of the top of the trough top 118, and more preferably in the longitudinal direction of the trough top 118.
熔解槽本體110及槽頂部118均使用對熔融玻璃之溫度具有耐熱性之耐火磚。Both the melting tank body 110 and the tank top 118 use refractory bricks which have heat resistance to the temperature of the molten glass.
於熔解槽本體110之下部設置有包含耐火磚之積層構造之鋪墊部124。鋪墊部124於圖6所示之例中具有4層構造之隔熱層。鋪墊部124之層構造並不限定於4層構造。於熔解槽101之底壁110c使用與鋪墊部124所使用之耐火磚相比耐熱溫度較高之耐火磚。耐熱溫度較高之耐火磚為氣孔率較低之緻密之耐火磚,因此導熱率相對較高。因此,為了提高隔熱性,鋪墊部124使用與底壁110c所使用之耐火磚相比導熱率較低、隔熱性較高之耐火磚。導熱率較低之耐火磚為氣孔率較高之耐火磚,因此與導熱率較高之耐火磚相比耐熱溫度較低。此種層構造被熔解槽110採用。於本實施形態中,將包括熔解槽本體110之底壁110c及鋪墊部124之部分稱為熔解槽110之底部126。A bedding portion 124 including a laminated structure of refractory bricks is disposed at a lower portion of the melting tank body 110. The padding portion 124 has a heat insulating layer having a four-layer structure in the example shown in FIG. The layer structure of the mat portion 124 is not limited to the four-layer structure. The bottom wall 110c of the melting tank 101 is made of a refractory brick having a higher heat resistance temperature than the refractory brick used for the bedding portion 124. The refractory brick having a higher heat resistance temperature is a dense refractory brick having a lower porosity, and thus the thermal conductivity is relatively high. Therefore, in order to improve the heat insulating property, the mat portion 124 uses a refractory brick having a lower thermal conductivity and a higher heat insulating property than the refractory brick used for the bottom wall 110c. The refractory brick having a lower thermal conductivity is a refractory brick having a higher porosity, and thus has a lower heat resistance temperature than a refractory brick having a higher thermal conductivity. This layer configuration is employed by the melting tank 110. In the present embodiment, the portion including the bottom wall 110c of the melting tank main body 110 and the mating portion 124 is referred to as the bottom portion 126 of the melting tank 110.
於此種熔解槽101中,熔解玻璃原料而製作熔融玻璃時,以燃燒加熱所引起之發熱量相對於通電加熱所引起之發熱量的比即發熱量比成為1.0以上且3.4以下,較佳為成為1.5以上且3.4以下之方式進行燃燒加熱及通電加熱。具體而言,於高精細顯示器所使用之玻璃基板使用黏度為102.5 泊時之溫度為1580℃以上之高溫黏性較高之玻璃、或應變點為680℃以上之玻璃之情形時,以使燃燒加熱所引起之發熱量相對於通電加熱所引起之發熱量的比即發熱量比成為1.0以上且2.8以下、較佳為成為1.5以上且2.8以下之方式進行燃燒加熱及通電加熱。又,於使用黏度為102.5 泊時之溫度為1500℃以上之高溫黏性較高之玻 璃組成之玻璃、鹼金屬氧化物之含有率為0~0.4莫耳%之玻璃之情形時,以使上述發熱量比成為1.0以上且3.4以下、較佳為成為1.5以上且3.4以下之方式進行燃燒加熱及通電加熱。此種加熱係利用由電腦122產生之控制信號、或利用操作員之設定控制燃燒氣體之供給量及電流之供給量而得以實現。In the melting tank 101, when the glass raw material is melted and the molten glass is produced, the ratio of the calorific value of the calorific value caused by the combustion heating to the calorific value due to the electric heating is 1.0 or more and 3.4 or less, preferably Combustion heating and electric heating are performed in a manner of 1.5 or more and 3.4 or less. Specifically, in the case where the glass substrate used for the high-definition display uses a glass having a viscosity of 10 2.5 poise at a temperature of 1580° C. or higher, or a glass having a strain point of 680° C. or higher, Combustion heating and electric heating are performed so that the ratio of the calorific value of the heat generated by the combustion heating to the calorific value due to the electric heating is 1.0 or more and 2.8 or less, preferably 1.5 or more and 2.8 or less. Further, when a glass having a viscosity of 10 2.5 poise and a temperature of 1500 ° C or higher and a glass having a high temperature viscosity of 1500 ° C or higher is used, the content of the alkali metal oxide is 0 to 0.4 mol %, so that The heat generation ratio is 1.0 or more and 3.4 or less, preferably 1.5 or more and 3.4 or less, and is performed by heating and heating. Such heating is achieved by using a control signal generated by the computer 122 or by controlling the supply amount of the combustion gas and the supply amount of the current by the operator's setting.
通電加熱所引起之發熱量可根據未圖示之電力計計測消耗電力而求出耗電量。由耗電量(kW)轉換為通電加熱所引起之發熱量(kcal/小時)(1kW=860kcal/小時)。再者,消耗電力亦可根據電極114之外加電壓及流通於電極114之電流求出。The amount of heat generated by the energization heating can be calculated from the power consumption measured by a power meter (not shown). The power consumption (kW) is converted into the calorific value (kcal/hour) caused by the energization heating (1 kW = 860 kcal / hour). Further, the power consumption can be obtained from the voltage applied to the electrode 114 and the current flowing through the electrode 114.
使用燃燒氣體之燃燒加熱之發熱量可藉由將燃燒氣體之燃燒所引起之每單位體積之發熱量乘以單位時間之燃燒氣體之供給量(燃燒氣體之流量)而算出。例如,若將所使用之燃燒氣體之發熱量設為8900kcal/Nm3 ,流量設為50Nm3 /小時,則發熱量=8900×50/860=517.4kW。燃燒加熱所引起之發熱量例如亦可利用氣體卡路里控制器以成為固定之方式進行控制。然而,氣體卡路里控制器於本實施形態中亦可不設置,可使用氣體之經控制之流量求出。The calorific value of the combustion heat using the combustion gas can be calculated by multiplying the calorific value per unit volume caused by the combustion of the combustion gas by the supply amount of the combustion gas per unit time (the flow rate of the combustion gas). For example, when the calorific value of the combustion gas to be used is 8900 kcal/Nm 3 and the flow rate is 50 Nm 3 /hr, the calorific value = 8900 × 50 / 860 = 517.4 kW. The amount of heat generated by combustion heating can be controlled, for example, by means of a gas calorie controller. However, the gas calorie controller may not be provided in the present embodiment, and may be obtained by using a controlled flow rate of the gas.
本實施形態中所使用之發熱量比係每固定時間之發熱量之平均值的比。此處,固定時間可為1小時亦可為1天。於以下之說明中,以每1天之平均值之發熱量之比為例進行說明。用以求出發熱量比之發熱量可使用以kcal/小時為單位之值,亦可使用以kW為單位之值。The heat generation ratio used in the present embodiment is a ratio of the average value of the calorific value per fixed time. Here, the fixed time may be 1 hour or 1 day. In the following description, the ratio of the calorific value per one day average is taken as an example. The calorific value can be used to determine the calorific value, and the value in kcal/hour can also be used, and the value in kW can also be used.
此處,於上述發熱量比超過3.4之情形時,燃燒加熱所引起之發熱量之貢獻變大,氣相空間之溫度變高,因此以熔融玻璃之液面上之玻璃原料之狀態作為澄清劑包含於玻璃原料中之氧化錫向氣相空間中釋出氧而使氧擴散。因此,於作為後續步驟之澄清步驟中使熔融玻璃脫泡時,使包含於熔融玻璃之泡吸收氧而成長,而無法自包含於熔融玻璃之澄清劑供給充分之氧,從而無法充分地使泡浮起至熔融玻璃之 液面而釋出。即,無法充分地進行脫泡處理。Here, when the calorific value is more than 3.4, the contribution of the calorific value caused by the combustion heating becomes large, and the temperature of the gas phase space becomes high, so that the state of the glass raw material on the liquid surface of the molten glass is used as a fining agent. The tin oxide contained in the glass raw material releases oxygen into the gas phase space to diffuse oxygen. Therefore, when the molten glass is defoamed in the clarification step of the subsequent step, the bubbles contained in the molten glass absorb oxygen and grow, and the clarifying agent contained in the molten glass cannot be supplied with sufficient oxygen, so that the bubbles cannot be sufficiently obtained. Float to molten glass Released from the liquid surface. That is, the defoaming treatment cannot be sufficiently performed.
另一方面,於發熱量比未達1.0之情形時,通電加熱所引起之發熱量之貢獻相對增大,用以通電加熱而流通之電流增多。若電流增多,則電極之侵蝕量增多,又,構成熔解槽101之耐火磚之侵蝕量增多,因此熔解槽101之壽命變短。On the other hand, when the heat generation ratio is less than 1.0, the contribution of the heat generation due to the electric heating is relatively increased, and the current flowing through the electric heating is increased. When the current is increased, the amount of erosion of the electrode is increased, and the amount of erosion of the refractory brick constituting the melting tank 101 is increased, so that the life of the melting tank 101 is shortened.
本實施形態中所使用之實質上不含鹼金屬氧化物或鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下之玻璃、或黏度為102.5 泊時之溫度為1500℃以上之高溫黏性較高之玻璃組成之玻璃、即主動矩陣型平板顯示器用之玻璃基板所使用之玻璃存在熔融玻璃之比電阻較大之傾向,若為貯存於熔解槽101之熔融玻璃之溫度則成為與熔解槽101之底壁110c之耐火磚之比電阻大致相同之程度。該傾向對於如含有氧化錫且黏度為102.5 泊時之溫度為1580℃以上或應變點為680℃以上之玻璃變得尤為顯著。因此,供給至電極對114之電流之一部分並未流通於熔融玻璃,而是流通於熔解槽本體110之底壁110c從而對底壁110c進行通電加熱。因此,於利用熔解槽101製作電阻率較高之上述玻璃之熔融玻璃之情形時,對電極對114供給大量電流,因此亦大量流通於底壁110c,其結果,底壁110c之通電加熱所引起之發熱量變大。由於該底壁110c之發熱量之增大,因熔解槽101之底部126之隔熱特性而產生熱之閉塞不通。該熱之閉塞不通有減弱底部126之耐火磚之機械強度而產生熱蠕變,從而使底部126變形之虞。進而,亦有因熱之閉塞不通而使耐火磚之溫度超過耐熱溫度從而發生熔損之虞。因此,通電加熱所引起之發熱量的貢獻變得過大這一情況欠佳。就該方面而言,上述發熱量比設為1.0以上,較佳為設為1.5以上。將發熱量比設為1.0~3.4,較佳為設為1.5~3.4,藉此利用通電加熱自玻璃原料下方之熔融玻璃之液面附近對玻璃原料進行加熱而使玻璃原料之溫度上升。因此,玻璃原料中之氧化錫中欲釋出氧之氧化錫之大部分並 非位於玻璃原料中,而是位於玻璃原料下方之熔融玻璃之液面附近。因此,即便氧化錫釋出氧,釋出之氧亦不會釋出至氣相空間,而變得容易被取入至熔融玻璃中。又,即便不於熔融玻璃之液面附近,而於熔融玻璃之液面之下方,氧化錫發生氧化還原反應而釋出氧,氧之泡之浮起速度亦不足夠快,因此熔融玻璃中之氧不釋出至氣相空間而殘存,殘存之氧可於澄清步驟中使用。就該方面而言,將發熱量比設為1.0~3.4,較佳為設為1.5~3.4。The glass used in the present embodiment does not substantially contain an alkali metal oxide or an alkali metal oxide having a content of 0 mol% or more and 0.4 mol% or less, or a temperature of 10 2.5 poise at a temperature of 1500 ° C. The glass of the glass having a high temperature and high viscosity is used, that is, the glass used for the glass substrate for the active matrix flat panel display has a tendency that the specific resistance of the molten glass is large, and is the temperature of the molten glass stored in the melting tank 101. Then, the specific resistance of the refractory brick of the bottom wall 110c of the melting tank 101 is substantially the same. This tendency is particularly remarkable for a glass having a temperature of 1580 ° C or higher or a strain point of 680 ° C or higher when the viscosity is 10 2.5 poise. Therefore, part of the current supplied to the electrode pair 114 does not flow through the molten glass, but flows through the bottom wall 110c of the melting tank main body 110 to electrically heat the bottom wall 110c. Therefore, when the molten glass of the glass having a high specific resistance is produced by the melting tank 101, a large amount of current is supplied to the electrode pair 114, and therefore a large amount flows to the bottom wall 110c, and as a result, the electric heating of the bottom wall 110c is caused. The heat is increased. Due to the increase in the amount of heat generated by the bottom wall 110c, heat clogging is caused by the heat insulating properties of the bottom portion 126 of the melting tank 101. The thermal occlusion does not open the mechanical strength of the refractory bricks of the bottom 126 to cause thermal creep, thereby deforming the bottom portion 126. Further, there is also a possibility that the temperature of the refractory brick exceeds the heat-resistant temperature due to heat clogging, and melting occurs. Therefore, the contribution of the amount of heat generation caused by the electric heating is excessively large, which is not preferable. In this respect, the calorific value is set to 1.0 or more, preferably 1.5 or more. The heat generation ratio is set to 1.0 to 3.4, preferably 1.5 to 3.4, whereby the glass raw material is heated from the vicinity of the liquid surface of the molten glass below the glass raw material by electric heating to raise the temperature of the glass raw material. Therefore, most of the tin oxide to be released from the tin oxide in the glass raw material is not located in the glass raw material, but is located near the liquid surface of the molten glass below the glass raw material. Therefore, even if the tin oxide releases oxygen, the released oxygen is not released to the gas phase space, and becomes easily taken into the molten glass. Further, even if it is not in the vicinity of the liquid surface of the molten glass, and under the liquid surface of the molten glass, tin oxide undergoes a redox reaction to release oxygen, and the floating speed of the bubble of oxygen is not sufficiently fast, so that it is in the molten glass. Oxygen does not remain in the gas phase space and remains, and the remaining oxygen can be used in the clarification step. In this respect, the calorific value is set to 1.0 to 3.4, preferably 1.5 to 3.4.
於此情形時,設置於槽頂部118(參照圖6)之溫度感測器118a所計測之氣相空間之溫度較佳為限制在1610℃以下,更佳為限制在1600℃以下。藉此,可抑制於熔融玻璃之液面自氧化錫釋出氧。藉此,可抑制於位於熔融玻璃之液面之玻璃原料之上方自氧化錫釋出氧,從而可減少玻璃基板中之泡之產生。In this case, the temperature of the gas phase space measured by the temperature sensor 118a provided at the groove top 118 (refer to FIG. 6) is preferably limited to 1610 ° C or lower, more preferably 1600 ° C or lower. Thereby, it is possible to suppress the release of oxygen from the tin oxide on the liquid surface of the molten glass. Thereby, it is possible to suppress the release of oxygen from the tin oxide above the glass raw material located on the liquid surface of the molten glass, thereby reducing the generation of bubbles in the glass substrate.
如上所述,於本實施形態中,將發熱量比設定為1.0~3.4、較佳為1.5~3.4而進行熔解槽之加熱,因此可抑制於熔解步驟中氧自氧化錫釋出至氣相空間。因此,可有效地進行澄清步驟中之脫泡處理。進而,將發熱量比設為1.0~3.4、較佳為1.5~3.4而進行加熱,即一面使通電加熱與燃燒加熱之發熱量保持平衡一面進行加熱,因此可抑制熔融玻璃中之氧化錫向氣相空間釋出氧,並且提高熔融玻璃之溫度。As described above, in the present embodiment, since the calorific value is set to 1.0 to 3.4, preferably 1.5 to 3.4, the melting tank is heated, so that the release of oxygen from the tin oxide to the gas phase space in the melting step can be suppressed. . Therefore, the defoaming treatment in the clarification step can be performed efficiently. Further, heating is performed by setting the calorific value to 1.0 to 3.4, preferably 1.5 to 3.4, that is, heating while maintaining the balance between the energization heating and the heat of combustion, thereby suppressing the tin oxide in the molten glass. The phase space releases oxygen and raises the temperature of the molten glass.
再者,最佳之發熱量比亦可使用電腦模擬來確定。使用玻璃原料、熔解槽之構造(大小或通電加熱所使用之電極之位置)等資訊進行模式化,使發熱量比變化而確認熔解槽之溫度或熔融玻璃之對流之狀況,藉此可確定最佳之發熱量比。Furthermore, the optimal heat generation ratio can also be determined using computer simulations. By using information such as the structure of the glass material and the melting tank (the size of the electrode used for heating or heating), the temperature is changed to confirm the temperature of the melting tank or the convection of the molten glass, thereby determining the most Good heat ratio.
(玻璃組成1)(glass composition 1)
作為由此種熔融玻璃製作之玻璃基板,例示以下之玻璃組成1之玻璃基板。即,以玻璃基板具有以下之玻璃組成之方式調製玻璃原料。As the glass substrate produced from such molten glass, the following glass substrate of the glass composition 1 is exemplified. That is, the glass raw material is prepared so that the glass substrate has the following glass composition.
SiO2 60~80莫耳%、Al2 O3 10~20莫耳%、B2 O3 0~10莫耳%、RO 0~17莫耳%(RO為MgO、CaO、SrO及BaO之合計量)。SiO 2 60~80 mol%, Al 2 O 3 10-20 mol%, B 2 O 3 0-10 mol%, RO 0-17 mol% (RO is the total of MgO, CaO, SrO and BaO the amount).
又,亦可MgO 0~10莫耳%、CaO 0~10莫耳%、SrO 0~5%、BaO 0~10%。Further, MgO 0 to 10 mol%, CaO 0 to 10 mol%, SrO 0 to 5%, and BaO 0 to 10% may be used.
此時,若SiO2 為65~75莫耳%,進而為68~75莫耳%,則減少泡及未熔解物之產生之本實施形態之效果變得顯著。又,B2 O3 為0~7莫耳%、0~5莫耳%、0~2莫耳%即變得越少,減少泡及未熔解物之產生之本實施形態之效果變得越顯著。At this time, when SiO 2 is 65 to 75 mol% and further 68 to 75 mol%, the effect of the present embodiment which reduces the generation of bubbles and unmelted substances becomes remarkable. Further, B 2 O 3 is 0 to 7 mol%, 0 to 5 mol%, and 0 to 2 mol%, that is, the smaller the effect, the more the effect of the present embodiment which reduces the generation of bubbles and unmelted substances becomes Significant.
此時,即便至少含有SiO2 、Al2 O3 、B2 O3 及RO(RO為MgO、CaO、SrO及BaO之合計量),莫耳比((2×SiO2 )+Al2 O3 )/((2×B2 O3 )+RO)為4.5以上,亦可達成作為本實施形態之效果之減少泡及未熔解物之產生之效果。即,莫耳比((2×SiO2 )+Al2 O3 )/((2×B2 O3 )+RO)為4.5以上之玻璃雖為高溫黏性較高之玻璃,但關於此種玻璃,藉由將發熱量比設為1.0~2.8、較佳為1.5~2.8,而與發熱量比在1.0~2.8之範圍以外之情形相比,進而與發熱量比在1.5~2.8之範圍外之情形相比,減少泡及未熔解物之產生之本實施形態之效果變得顯著。又,雖然含有MgO、CaO、SrO及BaO中之至少任一者,莫耳比(BaO+SrO)/RO(RO為CaO、MgO、SrO及BaO之合計量)為0.1以上,但就可於不使熔解性過度惡化之情況下使應變點上升之方面而言較佳。In this case, even if at least SiO 2 , Al 2 O 3 , B 2 O 3 and RO (RO is a total amount of MgO, CaO, SrO and BaO), Mohr ratio ((2 × SiO 2 ) + Al 2 O 3 When /((2 × B 2 O 3 ) + RO) is 4.5 or more, the effect of reducing foam and unmelted material which is an effect of the present embodiment can be achieved. That is, a glass having a molar ratio of (2 × SiO 2 ) + Al 2 O 3 ) / ((2 × B 2 O 3 ) + RO) of 4.5 or more is a glass having a high viscosity at a high temperature, but The glass is set to have a calorific value of 1.0 to 2.8, preferably 1.5 to 2.8, and the heat generation ratio is outside the range of 1.0 to 2.8, and the heat generation ratio is outside the range of 1.5 to 2.8. In contrast, the effect of the present embodiment which reduces the generation of bubbles and unmelted substances is remarkable. Further, although at least one of MgO, CaO, SrO, and BaO is contained, the molar ratio (BaO+SrO)/RO (RO is a total amount of CaO, MgO, SrO, and BaO) is 0.1 or more, but It is preferable in terms of increasing the strain point without excessively deteriorating the meltability.
又,莫耳%表示之B2 O3 之含有率之2倍與莫耳%表示之上述RO之含有率的合計為30莫耳%以下,較佳為10~30莫耳%。Further, the total content of B 2 O 3 expressed by mol% and the content ratio of RO described by mol % is 30 mol% or less, preferably 10 to 30 mol%.
又,即便上述玻璃組成1之玻璃基板中之鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下,亦可達成可減少泡及未熔解物之產生之本實施形態之效果。鹼金屬氧化物之含有率越小,高溫黏性及比 電阻越高,因此與鹼金屬氧化物之含有率超過0.4莫耳%之玻璃相比,鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下之玻璃之高溫黏性及比電阻較高。高溫黏性越高,熔融玻璃中之泡之浮起速度越慢,因此澄清容易變得不充分。於使用該高溫黏性較高之玻璃時,藉由將發熱量比設為1.0~2.8、更佳為1.5~2.8,而與發熱量比在上述範圍以外之情形相比,減少泡及未熔解物之產生之本實施形態之效果變得顯著。又,即便於使用比電阻較高之玻璃時,亦可防止熔解槽之熔損或壽命之縮短。In addition, even if the content of the alkali metal oxide in the glass substrate of the glass composition 1 is 0 mol% or more and 0.4 mol% or less, the effect of the embodiment which can reduce the occurrence of bubbles and unmelted substances can be achieved. . The smaller the content of alkali metal oxide, the higher the viscosity and the ratio The higher the electric resistance, the higher the viscosity and the ratio of the glass having an alkali metal oxide content of 0 mol% or more and 0.4 mol% or less, compared with the glass having an alkali metal oxide content of more than 0.4 mol%. The resistance is higher. The higher the viscosity at high temperature, the slower the floating speed of the bubbles in the molten glass, so the clarification tends to be insufficient. When the glass having a high viscosity is used, the heat generation ratio is set to 1.0 to 2.8, more preferably 1.5 to 2.8, and the foaming and unmelting are reduced as compared with the case where the heat generation ratio is outside the above range. The effect of this embodiment of the object is remarkable. Further, even when a glass having a higher specific resistance is used, the melting loss or the life of the melting tank can be prevented from being shortened.
(玻璃組成2)(glass composition 2)
又,作為玻璃基板,例示以下之玻璃組成2之玻璃基板。因此,以玻璃基板具有以下之玻璃組成之方式調製玻璃原料。Moreover, as a glass substrate, the following glass substrate of the glass composition 2 is illustrated. Therefore, the glass raw material is prepared in such a manner that the glass substrate has the following glass composition.
SiO2 :55~75莫耳%、Al2 O3 :5~20莫耳%、B2 O3 :0~15莫耳%、RO:5~20莫耳%SiO 2 : 55 to 75 mol %, Al 2 O 3 : 5 to 20 mol %, B 2 O 3 : 0 to 15 mol %, RO: 5 to 20 mol %
(RO為MgO、CaO、SrO及BaO之合計量)、R'2 O:0~0.4莫耳%(R'為Li、K、及Na之中玻璃基板中所含之全部元素)。(RO is the total amount of MgO, CaO, SrO, and BaO), and R' 2 O: 0 to 0.4 mol% (R' is all the elements contained in the glass substrate among Li, K, and Na).
此時,亦可含有SiO2 、Al2 O3 、B2 O3 及RO(R為Mg、Ca、Sr及Ba中含有於上述玻璃基板中之全部元素)中之至少任一者,莫耳比((2×SiO2 )+Al2 O3 )/((2×B2 O3 )+RO)為4.0以上,可達成作為本實施形態之效果之減少泡及未熔解物之產生的效果。即,莫耳比((2×SiO2 )+Al2 O3 )/((2×B2 O3 )+RO)為4.0以上之玻璃為高溫黏性較高之玻璃之1例,關於此種玻璃,亦藉由將發熱量比設為1.0~3.4、較佳為1.5~3.4,而與發熱量比在1.0~3.4之範圍以外的情形,進而與發熱量比在1.5~3.4之範圍外的情形相比,減少泡及未熔解物之產生之本實施形 態之效果變得顯著。In this case, at least one of SiO 2 , Al 2 O 3 , B 2 O 3 , and RO (R is all of the elements contained in the glass substrate of Mg, Ca, Sr, and Ba) may be contained. When the ratio ((2 × SiO 2 ) + Al 2 O 3 ) / ((2 × B 2 O 3 ) + RO) is 4.0 or more, the effect of reducing the generation of bubbles and unmelted substances which are the effects of the present embodiment can be attained. . That is, a glass having a molar ratio of (2 × SiO 2 ) + Al 2 O 3 ) / ((2 × B 2 O 3 ) + RO) of 4.0 or more is one of high-viscosity glass, and The glass is also set to have a calorific value of 1.0 to 3.4, preferably 1.5 to 3.4, and the ratio of the calorific value to the range of 1.0 to 3.4, and the ratio of the calorific value to the range of 1.5 to 3.4. In the case of this, the effect of the present embodiment which reduces the generation of bubbles and unmelted substances becomes remarkable.
即便上述玻璃組成2之玻璃基板中之鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下,亦可減少泡及未熔解物之產生。鹼金屬氧化物之含有率越小,高溫黏性越高,因此鹼金屬氧化物之含有率為0莫耳%以上且0.4莫耳%以下之玻璃與鹼金屬氧化物之含有率超過0.4莫耳%之玻璃相比,高溫黏性較高。於使用該高溫黏性較高之玻璃時,藉由將發熱量比設為1.0~3.4、較佳為1.5~3.4,而與發熱量比在1.0~3.4之範圍以外之情形相比,進而與發熱量比在1.5~3.4之範圍外之情形相比,減少泡及未熔解物之產生之本實施形態之效果變得顯著。又,即便於使用比電阻較高之玻璃時,亦可防止熔解槽之熔損或壽命之縮短。Even if the content of the alkali metal oxide in the glass substrate of the glass composition 2 is 0 mol% or more and 0.4 mol% or less, generation of bubbles and unmelted substances can be reduced. The smaller the content of the alkali metal oxide is, the higher the viscosity at high temperature is. Therefore, the content of the alkali metal oxide is 0 mol% or more and the content of the glass and the alkali metal oxide of 0.4 mol% or less exceeds 0.4 mol. Compared with the glass of %, the viscosity at high temperature is higher. When the glass having a high viscosity is used, the heat generation ratio is set to 1.0 to 3.4, preferably 1.5 to 3.4, and the heat generation ratio is outside the range of 1.0 to 3.4, and further The effect of the present embodiment which reduces the generation of bubbles and unmelted substances is remarkable as compared with the case where the amount of heat generation is outside the range of 1.5 to 3.4. Further, even when a glass having a higher specific resistance is used, the melting loss or the life of the melting tank can be prevented from being shortened.
(玻璃基板之特性)(Characteristics of glass substrate)
關於本實施形態之玻璃基板,黏度為102.5 泊時之溫度可為1500~1700℃,亦可為1590~1700℃或1550~1650℃。黏度為102.5 泊時之溫度越高之玻璃,即,越為高溫黏性之玻璃組成,藉由使發熱量比在上述範圍內而減少泡及未熔解物之產生的本實施形態之效果越顯著。In the glass substrate of the present embodiment, the temperature at a viscosity of 10 2.5 poise may be 1500 to 1700 ° C, or 1590 to 1700 ° C or 1550 to 1650 ° C. The glass having a higher viscosity at a temperature of 10 2.5 poise, that is, a glass composition having a higher temperature and a higher viscosity, and the effect of the present embodiment in which the generation of the foam and the unmelted substance is reduced by making the calorific value smaller than the above range Significant.
即,可於不過度地縮短熔解槽之壽命之情況下,於熔解槽中,利用使用燃燒機構之氣相中之燃燒加熱及藉由對熔融玻璃流通電流而進行之通電加熱,以成為含有氧化錫且黏度為102.5 泊時之溫度為1500℃以上之玻璃之方式熔解玻璃原料。In other words, in the case where the life of the melting tank is not excessively shortened, the melting tank can be oxidized by combustion heating in the gas phase using the combustion mechanism and electric conduction by flowing a current to the molten glass. The glass material is melted in such a manner that the tin has a viscosity of 10 2.5 poise and the temperature is 1500 ° C or more.
製作本實施形態之玻璃基板之熔融玻璃之應變點可為650℃以上,更佳為660℃以上,進而更佳為680℃以上,尤佳為設為720℃以上。又,應變點較高之玻璃有黏度為102.5 泊時之熔融玻璃之溫度變高之傾向,因此本實施形態之效果變得顯著。又,應變點越高,越可減少面板製造時之熱收縮,因此適合用作作為高精細顯示器之LTPS.TFT顯示器及有機EL顯示器用之玻璃基板。The strain point of the molten glass for producing the glass substrate of the present embodiment may be 650 ° C or higher, more preferably 660 ° C or higher, still more preferably 680 ° C or higher, and particularly preferably 720 ° C or higher. Further, in the glass having a high strain point, the temperature of the molten glass having a viscosity of 10 2.5 poise tends to increase, so that the effect of the present embodiment is remarkable. Moreover, the higher the strain point, the more the heat shrinkage during panel manufacture can be reduced, so it is suitable for use as a high-definition display LTPS. A glass substrate for a TFT display and an organic EL display.
再者,玻璃基板之熱收縮率較佳為0~20ppm,更佳為0~10ppm,進而較佳為0~5ppm。上述之熱收縮率可於對玻璃基板,實施以10℃/分鐘之升降溫速度於4500℃下保持1小時之熱處理後利用下述式而求出。Further, the heat shrinkage rate of the glass substrate is preferably from 0 to 20 ppm, more preferably from 0 to 10 ppm, still more preferably from 0 to 5 ppm. The heat shrinkage rate described above can be obtained by heat-treating the glass substrate at 4500 ° C for 1 hour at a temperature rise and fall speed of 10 ° C /min.
熱收縮率(ppm)={熱處理前後之玻璃之收縮量/熱處理前之玻璃之長度}×106 Heat shrinkage rate (ppm) = {shrinkage of glass before and after heat treatment / length of glass before heat treatment} × 10 6
又,構成本實施形態中之玻璃基板之玻璃於為1550℃之熔融玻璃時之比電阻可為50Ω.cm以上而可設為50~350Ω.cm,又,亦可為100Ω.cm以上而可設為100~350Ω.cm,進而可設為150~350Ω.cm。上述比電阻越高,熔解槽之熔損或壽命之縮短之問題變得越顯著,因此可防止熔解槽之熔損或壽命之縮短之本實施形態之效果變得顯著。再者,若欲將玻璃基板之應變點設為較高,則存在上述比電阻及黏度為102.5 泊時之熔融玻璃之溫度變高之傾向。Moreover, the specific resistance of the glass constituting the glass substrate of the present embodiment at a molten glass of 1550 ° C may be 50 Ω. Above cm, it can be set to 50~350Ω. Cm, again, can also be 100Ω. Above cm, it can be set to 100~350Ω. Cm, which can be set to 150~350Ω. Cm. The higher the specific resistance, the more the problem of the melting loss or the shortening of the life of the melting tank becomes more conspicuous. Therefore, the effect of the present embodiment which can prevent the melting loss or the shortening of the life of the melting tank becomes remarkable. Further, if the strain point of the glass substrate is to be made high, the temperature of the molten glass having a specific resistance and a viscosity of 10 2.5 poise tends to increase.
本實施形態中製造之玻璃基板適於平板顯示器用玻璃基板。又,本實施形態中製造之玻璃基板適合作為液晶顯示器用玻璃基板、或有機EL顯示器用之玻璃基板。進而,本實施形態中製造之玻璃基板尤其適合作為LTPS.TFT顯示器用玻璃基板、或氧化物半導體.TFT顯示器用之玻璃基板。又,本實施形態中製造之玻璃基板亦適於要求鹼金屬氧化物之含量極少的液晶顯示器用玻璃基板。The glass substrate produced in the present embodiment is suitable for a glass substrate for a flat panel display. Further, the glass substrate produced in the present embodiment is suitable as a glass substrate for a liquid crystal display or a glass substrate for an organic EL display. Further, the glass substrate produced in the present embodiment is particularly suitable as an LTPS. A glass substrate for a TFT display or a glass substrate for an oxide semiconductor or TFT display. Further, the glass substrate produced in the present embodiment is also suitable for a glass substrate for a liquid crystal display which requires a very small content of an alkali metal oxide.
[實驗例1][Experimental Example 1]
為了確認本實施形態之效果,利用熔解槽製作熔融玻璃而製作玻璃基板。具體而言,使用圖5、6所示之熔解槽101熔解玻璃原料而製作熔融玻璃,其後進行澄清步驟,經由圖1所示之步驟製造玻璃基板。In order to confirm the effect of the present embodiment, a molten glass was produced by a melting tank to prepare a glass substrate. Specifically, the glass raw material is melted by using the melting tank 101 shown in FIGS. 5 and 6, and molten glass is produced, and then the clarification process is performed, and the glass substrate is manufactured through the procedure shown in FIG.
所製造之玻璃基板之玻璃組成如下。The glass composition of the produced glass substrate was as follows.
SiO2 70.5莫耳%、 Al2 O3 10.9莫耳%、B2 O3 7.4莫耳%、MgO、CaO、SrO及BaO之合計量10.9莫耳%。The total amount of SiO 2 70.5 mol %, Al 2 O 3 10.9 mol%, B 2 O 3 7.4 mol%, MgO, CaO, SrO and BaO was 10.9 mol%.
又,所製造之玻璃基板之應變點為709℃,1550℃下之熔融玻璃之比電阻為195Ω.cm。Moreover, the strain point of the manufactured glass substrate is 709 ° C, and the specific resistance of the molten glass at 1550 ° C is 195 Ω. Cm.
再者,於熔解步驟中,於使上述發熱量比變化之以下之熔解條件下製作熔融玻璃,調查殘存於所製造之玻璃基板內之泡及未熔解物之缺陷數。將熔解條件及評價結果示於下述之表1。再者,表中之槽頂部溫度係利用設置於槽頂部118之溫度感測器118a(參照圖6)而計測之氣相空間內之溫度。關於燃燒加熱之發熱量,根據燃燒氣體之每單位時間之供給量及每單位體積之燃燒氣體之發熱量求出1天之發熱量。關於通電加熱所引起之發熱量,計測流通於電極對114之電流及電極對114間之電壓而求出熔解槽110中之通電加熱下1天之發熱量。Further, in the melting step, molten glass was produced under the melting conditions in which the above-described calorific value was changed, and the number of defects of the bubbles and the unmelted material remaining in the produced glass substrate was examined. The melting conditions and evaluation results are shown in Table 1 below. Further, the temperature at the top of the tank in the table is the temperature in the gas phase space measured by the temperature sensor 118a (refer to FIG. 6) provided at the top portion 118 of the tank. Regarding the calorific value of the combustion heating, the calorific value per day is determined from the supply amount per unit time of the combustion gas and the calorific value of the combustion gas per unit volume. The amount of heat generated by the energization heating is measured, and the current flowing through the electrode pair 114 and the voltage between the electrode pairs 114 are measured to determine the amount of heat generated by the energization heating in the melting tank 110 for one day.
所製造之玻璃基板之泡個數及未熔解成分缺陷數係藉由目視而計數。下述表1中之泡數以將實施例1中之泡數設為1之情形的比率表示。比率越大表示泡數越多。The number of bubbles and the number of defects of the unmelted component of the produced glass substrate were counted by visual observation. The number of bubbles in the following Table 1 is represented by a ratio of the case where the number of bubbles in Example 1 is set to 1. The larger the ratio, the more the number of bubbles.
又,特定出將熔解槽用於熔解步驟後之熔解槽之侵蝕量,以等級A、B、C3個等級對熔解槽壽命進行評價。等級A表示侵蝕量極少,熔解槽壽命極長,等級B表示雖然有侵蝕量,但熔解槽壽命為容許等級之壽命長度,等級C表示侵蝕量較多,熔解槽壽命較短,不在容許範圍內。Further, the amount of erosion of the melting tank after the melting tank was used for the melting step was specified, and the life of the melting tank was evaluated at three levels of grades A, B, and C. Grade A indicates that the amount of erosion is extremely small, and the life of the melting tank is extremely long. Grade B indicates that although there is erosion, the life of the melting tank is the allowable grade life length, grade C indicates that the erosion amount is large, and the life of the melting tank is short, which is not within the allowable range. .
如表1、2所記載,藉由實施例1、2、3獲得之玻璃基板就泡個數及未熔解物之缺陷數之方面而言,相對於藉由比較例1獲得之玻璃基板較為優異。又,於比較例2中,熔解槽壽命並非為容許範圍,於實施例1~3中之任一例中,熔解槽壽命均極長,又,為容許等級之壽命長度。根據上表可明確本實施形態之效果。As described in Tables 1 and 2, the glass substrates obtained in Examples 1, 2, and 3 were superior to the glass substrate obtained by Comparative Example 1 in terms of the number of bubbles and the number of defects of the unmelted material. . Further, in Comparative Example 2, the life of the melting tank was not within the allowable range, and in any of the examples 1 to 3, the life of the melting tank was extremely long, and the life of the melting level was also an acceptable level. The effect of this embodiment can be clarified based on the above table.
[實驗例2][Experimental Example 2]
進而,使用與實驗例1所使用之玻璃組成不同之玻璃組成2,以與實驗例1相同之方法製造玻璃基板。實驗例2之玻璃組成如下。Further, a glass substrate was produced in the same manner as in Experimental Example 1 using the glass composition 2 different from the glass composition used in Experimental Example 1. The glass composition of Experimental Example 2 is as follows.
SiO2 66.6莫耳%、Al2 O3 10.6莫耳%、B2 O3 11.0莫耳%、MgO、CaO、SrO及BaO之合計量11.4莫耳%。The total amount of SiO 2 66.6 mol %, Al 2 O 3 10.6 mol %, B 2 O 3 11.0 mol%, MgO, CaO, SrO and BaO was 11.4 mol%.
又,所製造之玻璃基板之應變點為660℃,於為1550℃之熔融玻璃時之比電阻為165Ω.cm。Moreover, the strained point of the glass substrate produced was 660 ° C, and the specific resistance at a molten glass of 1550 ° C was 165 Ω. Cm.
再者,以與實驗例1相同之方法調查殘存於使熔解步驟中之熔解條件發生各種變化而製造之玻璃基板內的泡及未熔解物之缺陷數。發熱量比、槽頂部溫度係利用與實驗例1相同之方法求出。表3、4中之 泡數係以將實施例4中之泡數設為1之情形時之比率表示。比率越大表示泡數越多。又,利用與實驗例1相同之方法對熔解槽壽命進行評價。Further, in the same manner as in Experimental Example 1, the number of defects of the bubbles and the unmelted material remaining in the glass substrate which were produced by various changes in the melting conditions in the melting step was examined. The calorific value and the temperature at the top of the tank were determined in the same manner as in Experimental Example 1. In Tables 3 and 4 The number of bubbles is expressed by the ratio when the number of bubbles in the embodiment 4 is set to 1. The larger the ratio, the more the number of bubbles. Further, the life of the melting tank was evaluated by the same method as Experimental Example 1.
藉由實施例4~7而獲得之玻璃基板就泡個數及未熔解物之缺陷數之方面而言,相對於藉由比較例3獲得之玻璃基板較為優異。又,於比較例4中,熔解槽壽命並非為容許範圍,但於實施例4~7中之任一例中,熔解槽壽命均極長。根據上表可明確本實施形態之效果。The glass substrate obtained in Examples 4 to 7 was superior to the glass substrate obtained in Comparative Example 3 in terms of the number of bubbles and the number of defects of the unmelted material. Further, in Comparative Example 4, the life of the melting tank was not within the allowable range, but in any of Examples 4 to 7, the life of the melting tank was extremely long. The effect of this embodiment can be clarified based on the above table.
以上,詳細地說明了本發明之玻璃基板之製造方法及玻璃基板製造裝置,但本發明並不限定於上述實施形態,當然亦可在不脫離本發明之主旨之範圍內進行各種改良或變更。In the above, the method of manufacturing the glass substrate of the present invention and the glass substrate manufacturing apparatus are described in detail. However, the present invention is not limited to the above-described embodiments, and various modifications and changes can be made without departing from the spirit and scope of the invention.
101‧‧‧熔解槽101‧‧‧melting tank
101b‧‧‧原料投入口101b‧‧‧ raw material input
104‧‧‧玻璃供給管104‧‧‧Glass supply tube
104a‧‧‧流出口104a‧‧‧Exit
110‧‧‧熔解槽本體110‧‧‧melting tank body
112‧‧‧燃燒器112‧‧‧ burner
112a‧‧‧氣體源112a‧‧‧ gas source
112b‧‧‧流量調整裝置112b‧‧‧Flow adjustment device
114‧‧‧電極對114‧‧‧electrode pair
116‧‧‧氣相空間隔離壁116‧‧‧ gas phase space partition
118‧‧‧槽頂部118‧‧‧Slot top
120‧‧‧控制單元120‧‧‧Control unit
122‧‧‧電腦122‧‧‧ computer
MG‧‧‧熔融玻璃MG‧‧‧ molten glass
Claims (11)