TW201905264A - 自捲曲薄膜及其製備方法和自捲曲方法 - Google Patents
自捲曲薄膜及其製備方法和自捲曲方法Info
- Publication number
- TW201905264A TW201905264A TW106120992A TW106120992A TW201905264A TW 201905264 A TW201905264 A TW 201905264A TW 106120992 A TW106120992 A TW 106120992A TW 106120992 A TW106120992 A TW 106120992A TW 201905264 A TW201905264 A TW 201905264A
- Authority
- TW
- Taiwan
- Prior art keywords
- nanofiber
- film
- self
- polymer
- deformable
- Prior art date
Abstract
一種自捲曲薄膜的製備方法,包括:提供靜電紡絲裝置,包括收集器;採用靜電紡絲方法在收集器上製備納米纖維基體薄膜,由高分子納米纖維按第一排列方式排列而成,第一排列方式為納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列;採用靜電紡絲方法在該納米纖維基體薄膜上製備一納米纖維可變形薄膜,從而得到納米纖維複合膜,該納米纖維可變形薄膜由高分子納米纖維按第二排列方式排列而成,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料;將該納米纖維複合膜從該收集器上分離並裁剪為所需尺寸。
Description
本發明涉及薄膜製備領域,尤其涉及一種自捲曲薄膜以及該自捲曲薄膜的製備方法和自捲曲方法。
聚合物材料由於具有較好的柔軟性,使其在人工血管、人工肌肉、智慧識別、回應、機器人以及感測器等領域都具有一定應用。然,諸如塑膠、橡膠等聚合物材料中,極少能夠在受到外界刺激後自動捲曲,而且捲曲過程和捲曲度不可控,使其大大限制了聚合物材料在這些領域更進一步的應用。
有鑑於此,有必要提供一種自捲曲薄膜的製備方法和自捲曲方法,能夠解決以上問題。
另,還有必要提供一種由上述製備方法制得的自捲曲薄膜。
本發明提供一種自捲曲薄膜的製備方法,包括:提供一靜電紡絲裝置,該靜電紡絲裝置包括一收集器;採用靜電紡絲方法在該收集器上製備一納米纖維基體薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列;採用靜電紡絲方法在該納米纖維基體薄膜遠離該收集器的表面製備一納米纖維可變形薄膜,從而得到一複合膜,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹;以及將該納米纖維複合膜從該收集器上分離並裁剪為所需尺寸,從而制得所述自捲曲薄膜。
本發明還提供一種自捲曲薄膜的自捲曲方法,包括:提供一靜電紡絲裝置,該靜電紡絲裝置包括一收集器;採用靜電紡絲方法在該收集器上製備一納米纖維基體薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列;採用靜電紡絲方法在該納米纖維基體薄膜遠離該收集器的表面製備一納米纖維可變形薄膜,從而得到一納米纖維複合膜,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹;將該納米纖維複合膜從該收集器上分離並裁剪為所需尺寸,從而制得所述自捲曲薄膜;以及將所述自捲曲薄膜進行加熱或紫外光照射,使該納米纖維可變形薄膜收縮或膨脹,從而,該自捲曲薄膜捲曲而制得一套管。
本發明還提供一種自捲曲薄膜,包括一納米纖維基體薄膜以及結合於所述納米纖維基體薄膜上的一納米纖維可變形薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,其中,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹。
通過在可變形薄膜中引入環境敏感型材料,控制可變形薄膜收縮或膨脹,從而使該自捲曲薄膜捲曲為套管,獲得所需的理想的形態和彎曲性,其中,通過控制該納米纖維基體薄膜中的高分子納米纖維沿同一方向有序排列,從而有利於控制該納米纖維可變形薄膜的捲曲方向,而該納米纖維可變形薄膜所需的捲曲程度可通過控制其自身的高分子納米纖維的排列方式而獲得。
請參閱圖1至圖4,本發明一較佳實施方式提供一種自捲曲薄膜100的製備方法,其包括如下步驟:
步驟一,請參閱圖1,提供一靜電紡絲裝置1,該靜電紡絲裝置1包括一收集器2。
步驟二,請參閱圖2,採用靜電紡絲方法在該收集器2上製備一納米纖維基體薄膜10。所述納米纖維基體薄膜10由高分子納米纖維按第一排列方式排列而成。所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向有序排列。
步驟三,請參閱圖3,採用靜電紡絲方法在該納米纖維基體薄膜10遠離該收集器2的表面製備一納米纖維可變形薄膜21,從而得到一納米纖維複合膜30。該納米纖維可變形薄膜21由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成。其中,該納米纖維可變形薄膜21的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜21可在環境溫度升高或紫外光照射條件下收縮或膨脹。
步驟三,請參閱圖4,將該納米纖維複合膜30從該收集器2上分離並裁剪為所需尺寸,從而得到所述自捲曲薄膜100。
請參閱圖1至圖7,本發明一較佳實施方式還提供一種自捲曲薄膜100的捲曲方法,其包括如下步驟:
步驟一,請參閱圖1,提供一靜電紡絲裝置1,該靜電紡絲裝置1包括一收集器2。
步驟二,請參閱圖2,採用靜電紡絲方法在該收集器2上製備一納米纖維基體薄膜10。所述納米纖維基體薄膜10由高分子納米纖維按第一排列方式排列而成。所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向有序排列。
步驟三,請參閱圖3,採用靜電紡絲方法在該納米纖維基體薄膜10遠離該收集器2的表面製備一納米纖維可變形薄膜21,從而得到一複合膜30。該納米纖維可變形薄膜21由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成。其中,該納米纖維可變形薄膜21的高分子納米纖維包括一環境敏感型材料,使納米纖維該納米纖維可變形薄膜21可在環境溫度升高或紫外光照射條件下收縮或膨脹。
步驟三,請參閱圖4,將該納米纖維複合膜30從該收集器2上分離並裁剪為所需尺寸,從而得到所述自捲曲薄膜100。
步驟四,請參閱圖5和圖6,將所述自捲曲薄膜100進行加熱或紫外光照射,使該納米纖維可變形薄膜21收縮(參圖5)或膨脹(參圖6)。從而,該自捲曲薄膜100捲曲而制得一套管200。
在本實施方式中,所述納米纖維基體薄膜10的高分子納米纖維的材質可以聚乙二醇,當然,也可以為其它高分子材料。所述納米纖維可變形薄膜21的高分子納米纖維的材質為聚(N-異丙基丙烯醯胺)。其中,聚(N-異丙基丙烯醯胺)作為環境敏感型材料,可在溫度升高至32度時發生可逆相變,從而使該納米纖維可變形薄膜21收縮。在這種情況下,收縮後的該納米纖維可變形薄膜21位於所述套管200的內側(參圖5)。
更具體的,將聚乙二醇和溶劑混合以配製第一電紡溶液,通過該第一電紡溶液製備該納米纖維基體薄膜10。將聚(N-異丙基丙烯醯胺)和溶劑混合以配製第二電紡溶液,通過該第二電紡溶液製備該納米纖維可變形薄膜21。所述溶劑可選自甲酸、乙酸、乙醇、丙酮、二甲基甲醯胺、二甲基乙醯胺、四氫呋喃、二甲基亞碸、六氟異丙醇、三氟乙醇、二氯甲烷、三氯甲烷、甲醇、乙醇、氯仿、二惡烷、三氟乙烷、三氟乙酸以及水中的至少一種。
在另一實施方式中,所述納米纖維基體薄膜10的高分子納米纖維的材質可以為聚氨基甲酸酯(PU),其具有較高的彈性,當然,也可以為其它高分子材料。該納米纖維可變形薄膜21的高分子納米纖維的材質為光可分解型感光高分子,更具體的,為結合有香豆素(化學結構式為)的聚氨基甲酸酯。結合有香豆素的聚氨基甲酸酯納米纖維的結構如下:。
請同時參照圖7,該香豆素作為環境敏感型材料,可在紫外光照條件下分解,從而使該納米纖維可變形薄膜21膨脹。在這種情況下,膨脹後的該納米纖維可變形薄膜21位於所述套管200的外側(參圖6)。
更具體的,將聚氨基甲酸酯和溶劑混合以配製第一電紡溶液,通過該第一電紡溶液製備該納米纖維基體薄膜10。將結合有香豆素的聚氨基甲酸酯和溶劑混合以配製第二電紡溶液,通過該第二電紡溶液製備該納米纖維可變形薄膜21。所述溶劑可選自甲酸、乙酸、乙醇、丙酮、二甲基甲醯胺、二甲基乙醯胺、四氫呋喃、二甲基亞碸、六氟異丙醇、三氟乙醇、二氯甲烷、三氯甲烷、甲醇、乙醇、氯仿、二惡烷、三氟乙烷、三氟乙酸以及水中的至少一種。
請參閱圖8,在本實施方式中,所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向有序排列,所述第二排列方式為該納米纖維可變形薄膜21的高分子納米纖維無序排列。請參閱圖9,在另一實施方式中,所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向(第一方向)有序排列,所述第二排列方式為該納米纖維可變形薄膜21的高分子納米纖維沿與該第一方向垂直的第二方向有序排列。請參閱圖10,在又一實施方式中,所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向(第一方向)有序排列,所述第二排列方式為該納米纖維可變形薄膜21的高分子納米纖維沿與該第一方向呈45度的第二方向有序排列。請參閱圖10,在其它實施方式中,所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向(第一方向)有序排列,所述第二排列方式為該納米纖維可變形薄膜21的高分子納米纖維沿與該第一方向平行或呈其它角度的第二方向有序排列。其中,可通過控制該收集器2的轉速控制該納米纖維有序或無序排列。例如,當收集器2轉速為100rpm時,高分子納米纖維無序排列;當收集器轉速為1500rpm時,高分子納米纖維有序排列。更進一步的,可通過控制該收集器2的收集時間控制所述納米纖維基體薄膜10以及所述納米纖維可變形薄膜21的厚度和密度。在本實施方式中,所述納米纖維基體薄膜10和所述納米纖維可變形薄膜21的厚度約為50μm。
通過靜電紡絲方法能夠精確控制所述納米纖維基體薄膜10以及所述納米纖維可變形薄膜21的高分子纖維排列方向,同時,通過控制該納米纖維基體薄膜10中的高分子納米纖維沿同一方向有序排列,可有利於控制該納米纖維可變形薄膜21的捲曲方向,而該納米纖維可變形薄膜21的所需捲曲程度(即該套管200的捲曲程度)可通過控制其自身的高分子納米纖維的排列方式而獲得。具體的,由於該納米纖維基體薄膜10中的高分子納米纖維沿同一方向有序排列,當該納米纖維可變形薄膜21在溫度升高或紫外光照條件下捲曲時,該納米纖維可變形薄膜21垂直於該納米纖維基體薄膜10中的高分子納米纖維的排列方向的側邊受到的阻力較大,而該納米纖維可變形薄膜21垂直於該納米纖維基體薄膜10中的高分子納米纖維的排列方向的側邊受到的阻力較小而發生捲曲。即,該納米纖維可變形薄膜21的捲曲方向與該納米纖維基體薄膜10中的高分子納米纖維的排列方向相互垂直。特別的,當該納米纖維可變形薄膜21的高分子納米纖維沿與該納米纖維基體薄膜10中的高分子納米纖維呈45度的另一方向有序排列時,該自捲曲薄膜100會捲曲為螺旋狀的套管200。
當該納米纖維基體薄膜10中的高分子納米纖維無序排列時,若該納米纖維可變形薄膜21在溫度升高或紫外光照條件下捲曲,該納米纖維可變形薄膜21無特定的捲曲方向。
下面通過實施例來對本發明進行具體說明。
實施例1
控制該收集器2的轉速為100rpm,收集時間為1h,在該收集器2上製備納米纖維基體薄膜10,該納米纖維基體薄膜10中的納米纖維無序排列;控制該收集器2的轉速為100rpm,收集時間為45min,在該納米纖維基體薄膜10上製備該納米纖維可變形薄膜21,該納米纖維可變形薄膜21中的納米纖維無序排列;將該納米纖維複合膜30從該收集器2上分離並裁剪為1×1cm2
的自捲曲薄膜100;將自捲曲薄膜100暴露於波長為254nm紫外光照條件下,該納米纖維複合膜30捲曲,而捲曲無特定方向。
實施例2
控制該收集器2的轉速為1500rpm,收集時間為1h,在該收集器2上製備納米纖維基體薄膜10,該納米纖維基體薄膜10中的納米纖維沿同一方向有序排列;控制該收集器2的轉速為100rpm,收集時間為45min,在該納米纖維基體薄膜10上製備納米纖維可變形薄膜21,該納米纖維可變形薄膜21中的納米纖維無序排列;將該納米纖維複合膜30從該收集器2上分離並裁剪為1×1cm2
的自捲曲薄膜100;將自捲曲薄膜100暴露於波長為254nm紫外光照條件下,從而制得直徑為3mm,長度為1cm的套管200。
實施例3
控制該收集器2的轉速為1500rpm,收集時間為1h,在該收集器2上製備納米纖維基體薄膜10,該納米纖維基體薄膜10中的納米纖維沿第一方向有序排列;將該收集器2旋轉90度,控制該收集器2的轉速為1500rpm,收集時間為1h,在該納米纖維基體薄膜10上製備可變形薄膜21,該納米纖維可變形薄膜21中的納米纖維沿與該第一方向垂直的第二方向有序排列;將該納米纖維複合膜30從該收集器2上分離並裁剪為1×1cm2
的自捲曲薄膜100;將自捲曲薄膜100暴露於波長為254nm紫外光照條件下,從而制得直徑為2mm,長度為1cm的套管200。
實施例4
控制該收集器2的轉速為1500rpm,收集時間為1h,在該收集器2上製備納米纖維基體薄膜10,該納米纖維基體薄膜10中的納米纖維沿第一方向有序排列;將該收集器2旋轉45度,控制該收集器2的轉速為1500rpm,收集時間為1h,在該納米纖維基體薄膜10上製備納米纖維可變形薄膜21,該納米纖維可變形薄膜21中的納米纖維沿與該第一方向呈45度的第二方向有序排列;將該納米纖維複合膜30從該收集器2上分離並裁剪為2×0.5cm2
的自捲曲薄膜100;將自捲曲薄膜100暴露於波長為254nm紫外光照條件下,從而制得螺旋狀的套管200。
請參閱圖4,本發明一較佳實施方式還提供一種由上述製備方法制得的自捲曲薄膜100,其包括位於一納米纖維基體薄膜10以及結合於所述納米纖維基體薄膜10上的一納米纖維可變形薄膜21。所述納米纖維基體薄膜10由高分子納米纖維按第一排列方式排列而成。所述第一排列方式為該納米纖維基體薄膜10的高分子納米纖維沿同一方向有序排列。該納米纖維可變形薄膜21由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成。其中,該納米纖維可變形薄膜21的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜21可在環境溫度升高或紫外光照射條件下收縮或膨脹。
在本實施方式中,該納米纖維基體薄膜10的高分子納米纖維的材質可以聚乙二醇。所述納米纖維可變形薄膜21的高分子納米纖維的材質為聚(N-異丙基丙烯醯胺)。其中,聚(N-異丙基丙烯醯胺)作為環境敏感型材料,可在溫度升高至32度時發生可逆相變,從而使該納米纖維可變形薄膜21收縮。
在另一實施方式中,所述納米纖維基體薄膜10的高分子納米纖維的材質可以為聚氨基甲酸酯(PU)。該納米纖維可變形薄膜21的高分子納米纖維的材質為光可分解型感光高分子,更具體的,為結合有香豆素的聚氨基甲酸酯。該香豆素作為環境敏感型材料,可在紫外光照條件下分解,從而使該納米纖維可變形薄膜21膨脹。
通過在納米纖維可變形薄膜21中引入環境敏感型材料,控制該納米纖維可變形薄膜21收縮或膨脹,從而使該自捲曲薄膜100捲曲為套管200,獲得所需的理想的形態和彎曲性。其中,通過控制該納米纖維基體薄膜10中的高分子納米纖維沿同一方向有序排列,從而有利於控制該納米纖維可變形薄膜21的捲曲方向,而該納米纖維可變形薄膜21所需的捲曲程度可通過控制其自身的高分子納米纖維的排列方式而獲得。再者,可根據所需套管200的大小裁剪該自捲曲薄膜100,即套管200的尺寸可控,從而滿足不同用戶的個性化需求。
最後需要指出,以上實施例僅用以說明本發明的技術方案而非限制,儘管參照以上較佳實施例對本發明進行了詳細說明,本領域的普通技術人員應當理解,可以對本發明的技術方案進行修改或等同替換都不應脫離本發明技術方案的精神和範圍。
1‧‧‧靜電紡絲裝置
2‧‧‧收集器
10‧‧‧納米纖維基體薄膜
21‧‧‧納米纖維可變形薄膜
30‧‧‧納米纖維複合膜
100‧‧‧自捲曲薄膜
200‧‧‧套筒
圖1為本發明一較佳實施方式的自捲曲薄膜的製備方法所使用的靜電紡絲裝置的結構示意圖。
圖2為使用圖1所示的製備納米纖維基體薄膜後的結構示意圖。
圖3為圖2所示的納米纖維基體薄膜上製備納米纖維可變形薄膜後獲得的納米纖維複合膜的結構示意圖。
圖4對圖3所示的納米纖維複合膜進行裁剪後得到的自捲曲薄膜的結構示意圖。
圖5為對圖4所示的自捲曲薄膜進行加熱後得到的套筒的結構示意圖。
圖6為對圖4所示的自捲曲薄膜進行紫外光照射後得到的套筒的結構示意圖。
圖7為圖6所示的自捲曲薄膜進行紫外光照射的反應原理圖。
圖8為圖4所示的納米纖維複合膜的納米纖維基體薄膜和納米纖維可變形薄膜沿第一種方式排列的結構示意圖。
圖9為圖4所示的納米纖維複合膜的納米纖維基體薄膜和納米纖維可變形薄膜沿第二種方式排列的結構示意圖。
圖10為圖4所示的納米纖維複合膜的納米纖維基體薄膜和納米纖維可變形薄膜沿第三種方式排列的結構示意圖。
無
無
Claims (14)
- 一種自捲曲薄膜的製備方法,包括: 提供一靜電紡絲裝置,該靜電紡絲裝置包括一收集器; 採用靜電紡絲方法在該收集器上製備一納米纖維基體薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列; 採用靜電紡絲方法在該納米纖維基體薄膜遠離該收集器的表面製備一納米纖維可變形薄膜,從而得到一納米纖維複合膜,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹;以及 將該納米纖維複合膜從該收集器上分離並裁剪為所需尺寸,從而制得所述自捲曲薄膜。
- 如申請專利範圍第1項所述的自捲曲薄膜的製備方法,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚乙二醇,所述納米纖維可變形薄膜的高分子納米纖維的材質為聚(N-異丙基丙烯醯胺),所述聚(N-異丙基丙烯醯胺)作為所述環境敏感型材料。
- 如申請專利範圍第1項所述的自捲曲薄膜的製備方法,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚氨基甲酸酯,該納米纖維可變形薄膜的高分子納米纖維的材質為光可分解型感光高分子。
- 如申請專利範圍第3項所述的自捲曲薄膜的製備方法,其中,所述光可分解型感光高分子為結合有香豆素的聚氨基甲酸酯,所述香豆素作為所述環境敏感型材料。
- 如申請專利範圍第4項所述的自捲曲薄膜的製備方法,其中,將聚氨基甲酸酯和溶劑混合以配製第一電紡溶液,通過該第一電紡溶液製備該納米纖維基體薄膜,將結合有香豆素的聚氨基甲酸酯和溶劑混合以配製第二電紡溶液,通過該第二電紡溶液製備該納米纖維可變形薄膜。
- 一種自捲曲薄膜的自捲曲方法,包括: 提供一靜電紡絲裝置,該靜電紡絲裝置包括一收集器; 採用靜電紡絲方法在該收集器上製備一納米纖維基體薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列; 採用靜電紡絲方法在該納米纖維基體薄膜遠離該收集器的表面製備一納米纖維可變形薄膜,從而得到一複合膜,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹; 將該納米纖維複合膜從該收集器上分離並裁剪為所需尺寸,從而制得所述自捲曲薄膜;以及 將所述自捲曲薄膜進行加熱或紫外光照射,使該納米纖維可變形薄膜收縮或膨脹,從而,該自捲曲薄膜捲曲而制得一套管。
- 如申請專利範圍第6項所述的自捲曲薄膜的自捲曲方法,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚乙二醇,所述納米纖維可變形薄膜的高分子納米纖維的材質為聚(N-異丙基丙烯醯胺),所述聚(N-異丙基丙烯醯胺)作為所述環境敏感型材料。
- 如申請專利範圍第6項所述的自捲曲薄膜的自捲曲方法,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚氨基甲酸酯,該納米纖維可變形薄膜的高分子納米纖維的材質為光可分解型感光高分子。
- 如申請專利範圍第7或8項所述的自捲曲薄膜的自捲曲方法,其中,所述第二排列方式為該納米纖維可變形薄膜的高分子納米纖維無序排列。
- 如申請專利範圍第7或8項所述的自捲曲薄膜的自捲曲方法,其中,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿第一方向有序排列,所述第二排列方式為該納米纖維可變形薄膜的高分子納米纖維沿與該第一方向垂直的第二方向有序排列。
- 如申請專利範圍第7或8項所述的自捲曲薄膜的自捲曲方法,其中,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿第一方向有序排列,所述第二排列方式為該納米纖維可變形薄膜的高分子納米纖維沿與該第一方向呈45度的第二方向有序排列。
- 一種自捲曲薄膜,包括一納米纖維基體薄膜以及結合於所述納米纖維基體薄膜上的一納米纖維可變形薄膜,所述納米纖維基體薄膜由高分子納米纖維按第一排列方式排列而成,所述第一排列方式為該納米纖維基體薄膜的高分子納米纖維沿同一方向有序排列,該納米纖維可變形薄膜由高分子納米纖維按與該第一排列方式相同或不同的第二排列方式排列而成,其中,該納米纖維可變形薄膜的高分子納米纖維包括一環境敏感型材料,使該納米纖維可變形薄膜在環境溫度升高或紫外光照射條件下收縮或膨脹。
- 如申請專利範圍第12項所述的自捲曲薄膜,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚乙二醇,所述納米纖維可變形薄膜的高分子納米纖維的材質為聚(N-異丙基丙烯醯胺),所述聚(N-異丙基丙烯醯胺)作為所述環境敏感型材料。
- 如申請專利範圍第12項所述的自捲曲薄膜,其中,所述納米纖維基體薄膜的高分子納米纖維的材質為聚氨基甲酸酯,該納米纖維可變形薄膜的高分子納米纖維的材質為光可分解型感光高分子。