TW201504377A - Adhesive composition, adhesive agent and adhesive sheet - Google Patents
Adhesive composition, adhesive agent and adhesive sheet Download PDFInfo
- Publication number
- TW201504377A TW201504377A TW103118214A TW103118214A TW201504377A TW 201504377 A TW201504377 A TW 201504377A TW 103118214 A TW103118214 A TW 103118214A TW 103118214 A TW103118214 A TW 103118214A TW 201504377 A TW201504377 A TW 201504377A
- Authority
- TW
- Taiwan
- Prior art keywords
- adhesive
- mass
- meth
- monomer
- acrylate
- Prior art date
Abstract
Description
本發明是關於一種黏接性組合物、黏接劑(使黏接性組合物架橋的材料)以及黏接片,特別是關於一種適合作為偏光板等的光學構件用的黏接性組合物、黏接劑以及黏接片。 The present invention relates to an adhesive composition, an adhesive (a material for bridging an adhesive composition), and an adhesive sheet, and more particularly to an adhesive composition suitable for use as an optical member such as a polarizing plate. Adhesive and adhesive sheet.
近年在各種電子設備中,多使用兼具顯示裝置與輸入手段的觸控面板。觸控面板的種類主要有電阻式、電容式、光學式以及超聲波式。電阻式觸控面板有模擬數據電阻式以及母體電阻式。電容式觸控面板有表面型以及投影型。 In recent years, in various electronic devices, a touch panel having both a display device and an input means has been frequently used. The types of touch panels are mainly resistive, capacitive, optical, and ultrasonic. The resistive touch panel has analog data resistance and mother resistance. The capacitive touch panel has a surface type and a projection type.
最近受到注目的智慧手機、平板電腦終端等移動式電子設備的觸控面板,多使用投影型電容式的觸控面板。作為上述移動電子設備的投影型電容式觸控面板,例如,有研究提出了從下向上按順序積層液晶顯示裝置(LCD)、黏接劑層、透明導電膜(氧化銦錫:ITO)、玻璃基板、透明導電膜(ITO)、以及強化玻璃等保護層的觸控面板。 The touch panel of mobile electronic devices such as smart phones and tablet terminals that have recently attracted attention has mostly used projection type capacitive touch panels. As a projection type capacitive touch panel of the above mobile electronic device, for example, research has been proposed to laminate a liquid crystal display device (LCD), an adhesive layer, a transparent conductive film (indium tin oxide: ITO), and a glass in order from bottom to top. A touch panel of a protective layer such as a substrate, a transparent conductive film (ITO), or a tempered glass.
作為構成上述液晶顯示裝置的光學構件,一般使用液晶組件。液晶組件一般是將形成配向層的兩片透明電極基板的配向層作為內側,通過間隔片,以形成所定間隔的方式,進行配置,將其周邊密封,在兩片透明電極基板之間夾持液晶材料的組件。通常,在液晶組件中的兩片透明電極基板的外側 ,分別通過黏接劑而黏接偏光板。 As the optical member constituting the liquid crystal display device described above, a liquid crystal module is generally used. In the liquid crystal module, the alignment layer of the two transparent electrode substrates forming the alignment layer is generally disposed inside, and is disposed so as to form a predetermined interval by the spacers, and the periphery thereof is sealed to sandwich the liquid crystal between the two transparent electrode substrates. The components of the material. Usually, outside the two transparent electrode substrates in the liquid crystal module The polarizing plate is bonded by an adhesive.
在此,如上所述,將液晶顯示裝置的偏光板,通過黏接劑層,在透明導電膜(ITO)上貼合的構成中,黏接劑直接與ITO接觸。因此,在大量包含酸成分羧基的黏接劑中,會發生腐蝕ITO或使ITO的電阻值發生變化的問題。 Here, as described above, in the configuration in which the polarizing plate of the liquid crystal display device is bonded to the transparent conductive film (ITO) through the adhesive layer, the adhesive is directly in contact with the ITO. Therefore, in a large amount of the binder containing the carboxyl group of the acid component, there is a problem that the ITO is corroded or the resistance value of the ITO is changed.
作為光學用的黏接劑,例如,已知有專利文獻1記述的黏接劑。該黏接劑,由50質量%~90質量%(甲基)丙烯酸的碳原子數為4~12的烷基酯單體、3質量%~10質量%(甲基)丙烯酸的脂環式烷基酯單體、0.1質量%~1.0質量%(甲基)丙烯酸的羥烷基酯單體、以及3質量%~10質量%(甲基)丙烯酸的碳原子數為1~3的烷基酯單體(合計100質量%)構成的共聚物(共聚物中雖然含有羥基,但不含有羧基,重均分子量為70萬~120萬)、架橋劑(相對於共聚物100質量份,為0.02質量份~1質量份)以及架橋助劑(相對於共聚物100質量份,為0.5質量份~5.0質量份)所構成。該黏接劑由於不含有酸成分羧基,因此不易發生上述問題。 As an adhesive for optics, for example, the adhesive described in Patent Document 1 is known. The adhesive is composed of 50% by mass to 90% by mass of an alkyl ester monomer having 4 to 12 carbon atoms of (meth)acrylic acid and 3 to 10% by mass of an alicyclic alkane of (meth)acrylic acid. a hydroxyalkyl ester monomer of 0.1% by mass to 1.0% by mass of (meth)acrylic acid, and an alkyl ester having 1 to 3 carbon atoms of 3 to 10% by mass of (meth)acrylic acid a copolymer composed of a monomer (total 100% by mass) (the copolymer contains a hydroxyl group, but does not contain a carboxyl group, and has a weight average molecular weight of 700,000 to 1,200,000), and a bridging agent (0.02 mass based on 100 parts by mass of the copolymer) 1 part by mass) and a bridging aid (0.5 parts by mass to 5.0 parts by mass based on 100 parts by mass of the copolymer). Since the adhesive does not contain an acid component carboxyl group, the above problem is less likely to occur.
【專利文獻1】日本特開2012-001647號公報 [Patent Document 1] Japanese Patent Laid-Open Publication No. 2012-001647
另一方面,隨著近年移動式電子設備的薄型化,組成構件偏光板也開始薄型化。具體而言,使用在兩側維持偏光子聚乙烯醇的保護薄膜的厚度減少的偏光板。上述偏光板, 由於保護薄膜,防止偏光子熱收縮的能力下降,熱收縮有比原來變大的傾向。另外,作為上述保護薄膜的材質,也使用環烯烴聚合物(COP)等易於發生脫氣的光學功能性薄膜等代替三醋酸纖維素。因此,用於這些的黏接劑中,要求具有比現在更高的信賴性(耐久性.耐漏光性)。 On the other hand, with the thinning of mobile electronic devices in recent years, the constituent member polarizing plates have also begun to be thinned. Specifically, a polarizing plate having a reduced thickness of a protective film that maintains polarized polyvinyl alcohol on both sides is used. The above polarizing plate, Due to the protective film, the ability to prevent thermal contraction of the polarizer is lowered, and the heat shrinkage tends to be larger than the original. In addition, as the material of the protective film, an optical functional film which is likely to be deaerated, such as a cycloolefin polymer (COP), or the like, is used instead of cellulose triacetate. Therefore, among the adhesives used for these, it is required to have higher reliability (durability and light leakage resistance) than now.
但是,在如上所述的偏光板中,使用專利文獻1的黏接劑的情況時,耐久性不充分,在高溫條件下或濕熱條件下,會發生浮起或剝離。另外,專利文獻1的黏接劑中,薄型化的偏光板在耐熱條件下發生大的收縮應力時,難以緩和該收縮應力,會因光學軸錯位而產生光洩露,或液晶組件等發生變形。由此,會有給液晶顯示裝置的顯示性帶來不良影響的情況。 However, in the case of using the adhesive of Patent Document 1 in the polarizing plate as described above, the durability is insufficient, and floating or peeling occurs under high temperature conditions or under moist heat conditions. Further, in the adhesive of Patent Document 1, when a thinned polarizing plate generates a large shrinkage stress under heat-resistant conditions, it is difficult to alleviate the shrinkage stress, and light leakage may occur due to displacement of the optical axis, or the liquid crystal module or the like may be deformed. Therefore, there is a case where the display performance of the liquid crystal display device is adversely affected.
本發明是鑒於這樣的現狀而進行的,目的在於提供一種不會給透明導電膜等的被黏物帶來不良影響,同時,耐久性、耐漏光性以及包含黏接劑層的積層體的耐變形性優異的黏接性組合物、黏接劑以及黏接片。 The present invention has been made in view of the above circumstances, and it is an object of the invention to provide a laminate which does not adversely affect an adherend such as a transparent conductive film, and which has durability, light leakage resistance, and a laminate including an adhesive layer. Adhesive composition, adhesive, and adhesive sheet excellent in deformability.
為了達成上述目的,第一,本發明提供一種黏接性組合物,其含有重均分子量為140萬~250萬,作為構成聚合物的單體單元,含有具有羥基的單體、具有芳香環的單體、具有羧基的單體的(甲基)丙烯酸酯聚合物(A)、異氰酸酯類架橋劑(B)和具有巰基的矽烷偶聯劑(C),上述(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有1質量%~5質量%上述具有羥基的單體、5質量%~30質量%上述具有芳 香環的單體、0.1質量%~0.8質量%上述具有羧基的單體(發明1)。 In order to achieve the above object, first, the present invention provides an adhesive composition comprising a weight average molecular weight of from 1.4 to 2.5 million, as a monomer unit constituting a polymer, a monomer having a hydroxyl group, and having an aromatic ring. a (meth) acrylate polymer (A) having a monomer, a carboxyl group, an isocyanate bridging agent (B), and a decane coupling agent (C) having a mercapto group, and the above (meth) acrylate polymer ( A), as a monomer unit constituting the polymer, 1% by mass to 5% by mass of the monomer having a hydroxyl group, and 5% by mass to 30% by mass of the above-mentioned aromatic group Monomer of the scented ring, 0.1% by mass to 0.8% by mass of the above monomer having a carboxyl group (Invention 1).
將上述發明(發明1)所述黏接性組合物架橋所得到的黏接劑,通過使(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,分別以所定量含有具有羥基的單體、具有芳香環的單體以及具有羧基的單體,以及具有巰基的矽烷偶聯劑(C)發揮優異的偶聯效果等,耐久性、耐漏光性以及包含黏接劑層的積層體的耐變形性優異。另外,由於(甲基)丙烯酸酯聚合物(A)中包含的羧基的量抑制在較低的程度,因此可抑制由於酸產生的透明導電膜等被黏物的缺陷。 The adhesive obtained by bridging the adhesive composition according to the above invention (Invention 1) is obtained by using the (meth) acrylate polymer (A) as a monomer unit constituting the polymer. A monomer having a hydroxyl group, a monomer having an aromatic ring, a monomer having a carboxyl group, and a decane coupling agent (C) having a mercapto group exhibit excellent coupling effects, durability, light leakage resistance, and an adhesive containing The laminate of the layer is excellent in deformation resistance. In addition, since the amount of the carboxyl group contained in the (meth) acrylate polymer (A) is suppressed to a low level, defects of an adherend such as a transparent conductive film due to an acid can be suppressed.
上述發明(發明1)中,上述異氰酸酯類架橋劑(B),優選為三羥甲基丙烷改性甲次苯基二異氰酸酯(發明2)。 In the above invention (Invention 1), the isocyanate-based bridging agent (B) is preferably trimethylolpropane-modified methylphenylene diisocyanate (Invention 2).
上述發明(發明1,發明2)中,上述黏接性組合物中上述異氰酸酯類架橋劑(B)的含有量,相對於上述(甲基)丙烯酸酯聚合物(A)100質量份,優選為0.01質量份~1質量份(發明3)。 In the above invention (Invention 1 and Invention 2), the content of the isocyanate-based bridging agent (B) in the adhesive composition is preferably 100 parts by mass based on 100 parts by mass of the (meth)acrylate polymer (A). 0.01 parts by mass to 1 part by mass (Invention 3).
上述發明(發明1~發明3)中,上述黏接性組合物中上述矽烷偶聯劑(C)的含有量,相對於上述(甲基)丙烯酸酯聚合物(A)100質量份,優選為0.01質量份~0.4質量份(發明4)。 In the above invention (Invention 1 to Invention 3), the content of the decane coupling agent (C) in the adhesive composition is preferably 100 parts by mass based on 100 parts by mass of the (meth) acrylate polymer (A). 0.01 parts by mass to 0.4 parts by mass (Invention 4).
上述發明(發明1~發明4)中,上述具有芳香環的單體,優選為(甲基)丙烯酸2-苯基乙基酯(發明5)。 In the above invention (Invention 1 to Invention 4), the monomer having an aromatic ring is preferably 2-phenylethyl (meth)acrylate (Invention 5).
第二,本發明提供一種將上述黏接性組合物(發明1~發明5)架橋所構成的黏接劑(發明6)。 Secondly, the present invention provides an adhesive comprising the above-mentioned adhesive composition (Invention 1 to Invention 5). (Invention 6).
上述發明(發明6)中,凝膠分率優選為55%~80%(發明7)。 In the above invention (Invention 6), the gel fraction is preferably from 55% to 80% (Invention 7).
第三,本發明提供一種黏接片,其特徵在於:具備基材和黏接劑層,上述黏接劑層由上述黏接劑(發明6,發明7)構成(發明8)。 Thirdly, the present invention provides a bonding sheet comprising a substrate and an adhesive layer, and the adhesive layer is composed of the above-mentioned adhesive (Invention 6, Invention 7) (Invention 8).
上述發明(發明8)中,上述基材優選為光學構件(發明9)。 In the above invention (Invention 8), the substrate is preferably an optical member (Invention 9).
上述發明(發明9)中,上述光學構件優選為偏光板(發明10)。 In the above invention (Invention 9), the optical member is preferably a polarizing plate (Invention 10).
第四,本發明提供一種黏接片,其特徵在於:其具備兩片剝離片和以與上述兩片剝離片的剝離面相接的方式夾持上述剝離片的黏接劑層,上述黏接劑層由上述黏接劑(發明6,發明7)構成(發明11)。 Fourthly, the present invention provides a bonding sheet comprising two release sheets and an adhesive layer for holding the release sheets in contact with the release faces of the two release sheets, the bonding The agent layer is composed of the above-mentioned binder (Invention 6, Invention 7) (Invention 11).
上述發明(發明8~發明11)中,對上述黏接劑層和透明導電膜的積層體,在65℃、95%RH的氣氛下,進行曝露500小時的濕熱促進試驗時,上述透明導電膜根據以下算式算出的電阻值增加率優選為15%以下(發明12)。 In the above invention (Invention 8 to Invention 11), the transparent conductive film is used when the laminate of the adhesive layer and the transparent conductive film is exposed to a moist heat promotion test for 500 hours in an atmosphere of 65 ° C and 95% RH. The increase rate of the resistance value calculated by the following formula is preferably 15% or less (Invention 12).
電阻值增加率(%)={(R-R0)/R0}×100(算式中,R0為濕熱促進試驗前的初始電阻值,R為濕熱促進試驗後的電阻值。) Resistance increase rate (%) = {(RR 0 ) / R 0 } × 100 (In the formula, R 0 is the initial resistance value before the damp heat promotion test, and R is the resistance value after the damp heat promotion test.)
根據本發明所述黏接性組合物、黏接劑以及黏接片,不會給透明導電膜等的被黏物帶來不良影響,同時,耐久性、耐漏光性以及包含黏接劑層的積層體的耐變形性優異。 The adhesive composition, the adhesive, and the adhesive sheet according to the present invention do not adversely affect the adherend such as a transparent conductive film, and at the same time, durability, light leakage resistance, and an adhesive layer containing the adhesive. The laminate is excellent in deformation resistance.
1A,1B‧‧‧黏接片 1A, 1B‧‧‧bonding strips
1A’‧‧‧附有黏接劑層的偏光板 1A'‧‧‧Polarizer with adhesive layer
11‧‧‧黏接劑層 11‧‧‧Adhesive layer
12,12a,12b‧‧‧剝離片 12,12a,12b‧‧‧ peeling film
13‧‧‧基材 13‧‧‧Substrate
13’‧‧‧偏光板 13’‧‧‧Polar plate
21‧‧‧PET薄膜 21‧‧‧PET film
21a,21b‧‧‧面 21a, 21b‧‧‧
22‧‧‧ITO膜 22‧‧‧ITO film
22a‧‧‧面 22a‧‧‧ face
23‧‧‧玻璃板 23‧‧‧ glass plate
23a‧‧‧面 23a‧‧‧ face
24‧‧‧黏接膠帶 24‧‧‧Adhesive tape
25‧‧‧電極 25‧‧‧Electrode
30‧‧‧數字測高儀 30‧‧‧Digital altimeter
S‧‧‧電阻值測定用樣品 S‧‧‧Resistance measurement sample
圖1為本發明第1實施形態所有關的黏接片的剖面圖。 Fig. 1 is a cross-sectional view showing an adhesive sheet according to a first embodiment of the present invention.
圖2為本發明第2實施形態所有關的黏接片的剖面圖。 Fig. 2 is a cross-sectional view showing a bonding sheet according to a second embodiment of the present invention.
圖3為試驗例3中製作的電阻值測定樣品的剖面圖。 Fig. 3 is a cross-sectional view showing a sample for measuring a resistance value produced in Test Example 3.
圖4為對試驗例3的試驗方法進行說明的斜視圖。 Fig. 4 is a perspective view for explaining a test method of Test Example 3.
圖5為表示在附有黏接劑層的偏光板上進行漏光性試驗(肉眼)的評價基準的圖(顏色)。 Fig. 5 is a view (color) showing the evaluation criteria of the light leakage test (the naked eye) on the polarizing plate with the adhesive layer.
以下,關於本發明的實施形態進行說明。 Hereinafter, embodiments of the present invention will be described.
〔黏接性組合物〕 [adhesive composition]
本實施形態所有關的黏接性組合物(以下稱為「黏接性組合物P」。),含有重均分子量為140萬~250萬,作為構成聚合物的單體單元,含有具有羥基的單體(含羥基單體)、具有芳香環的單體(含芳香環單體)、具有羧基的單體(含羧基單體)的(甲基)丙烯酸酯聚合物(A)、異氰酸酯類架橋劑(B)和具有巰基的矽烷偶聯劑(C)。另外,(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有1質量%~5質量%含羥基單體、含有5質量%~30質量%含芳香環單體,含有0.1質量%~0.8質量%含羧基單體。另外,本說明書中,所說的(甲基)丙烯酸酯,指丙烯酸酯以及甲基丙烯酸酯的兩方。其他的類似用語也同樣。另外,在「聚合物」中,也包括「共聚物」的概念。 The adhesive composition according to the present embodiment (hereinafter referred to as "adhesive composition P") contains a weight average molecular weight of 1.4 million to 2.5 million, and contains a hydroxyl group as a monomer unit constituting the polymer. Monomer (hydroxyl-containing monomer), monomer having an aromatic ring (containing an aromatic ring monomer), monomer having a carboxyl group (carboxyl-containing monomer), (meth) acrylate polymer (A), isocyanate bridging Agent (B) and a decane coupling agent (C) having a mercapto group. Further, the (meth) acrylate polymer (A) contains, as a monomer unit constituting the polymer, 1% by mass to 5% by mass of a hydroxyl group-containing monomer, and 5% by mass to 30% by mass of an aromatic ring-containing monomer. It contains 0.1% by mass to 0.8% by mass of a carboxyl group-containing monomer. In the present specification, the term "(meth)acrylate" means both acrylate and methacrylate. The same is true for other similar terms. In addition, the concept of "copolymer" is also included in "polymer".
在上述黏接性組合物P中,(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,通過分別以所定量含有 含羥基單體、含芳香環單體以及含羧基單體,將該黏接性組合物P架橋所得到的黏接劑,兼具凝集力和應力緩和性,耐久性、耐漏光性以及包含黏接劑層的積層體(例如,觸控面板、液晶面板等)的耐變形性(以下有簡單稱為「耐變形性」的情況。)優異。 In the above-mentioned adhesive composition P, the (meth) acrylate polymer (A) is contained as a monomer unit constituting the polymer by a predetermined amount. a hydroxyl group-containing monomer, an aromatic ring-containing monomer, and a carboxyl group-containing monomer, and the adhesive agent obtained by bridging the adhesive composition P has both cohesive force and stress relaxation property, durability, light leakage resistance, and viscosity-containing The laminate of the adhesive layer (for example, a touch panel, a liquid crystal panel, or the like) is excellent in deformation resistance (hereinafter, simply referred to as "deformation resistance").
另外,如果將上述黏接性組合物P架橋,則矽烷偶聯劑(C)的巰基,與異氰酸酯類架橋劑(B)的異氰酸酯基容易形成硫代氨基甲酸酯鍵,該異氰酸酯類架橋劑(B)的其他異氰酸酯基,與(甲基)丙烯酸酯聚合物(A)的羥基反應,將(甲基)丙烯酸酯聚合物(A)架橋,形成三維網絡結構。而且,據推測矽烷偶聯劑(C)的烷氧基甲矽烷,與(甲基)丙烯酸酯聚合物(A)保持適宜距離,懸掛在(甲基)丙烯酸酯聚合物(A)上。由此,發揮優異的偶聯效果,所得到的黏接劑,即使在高溫條件下以及濕熱條件下,黏接耐久性也優異。 Further, when the above-mentioned adhesive composition P is bridged, the sulfhydryl group of the decane coupling agent (C) and the isocyanate group of the isocyanate-based bridging agent (B) easily form a thiourethane bond, and the isocyanate-based bridging agent The other isocyanate group of (B) reacts with the hydroxyl group of the (meth) acrylate polymer (A) to bridge the (meth) acrylate polymer (A) to form a three-dimensional network structure. Further, it is presumed that the alkoxymethyl decane of the decane coupling agent (C) is suspended from the (meth) acrylate polymer (A) at a suitable distance from the (meth) acrylate polymer (A). Thereby, the excellent coupling effect is exhibited, and the obtained adhesive agent is excellent in adhesive durability even under high temperature conditions and wet heat conditions.
另外,上述黏接性組合物P中,由於(甲基)丙烯酸酯聚合物(A),作為單體單元,含有的含羧基單體的含有量抑制在較低的程度,所得到的黏接劑的貼附對象,可抑制由於酸產生的缺陷,例如,在為透明導電膜或金屬膜等的情況時,也能抑制由於酸產生的這些缺陷。特別是貼附對象為透明導電膜的情況時,可抑制該透明導電膜被腐蝕或該透明導電膜的電阻值發生改變。 Further, in the above-mentioned adhesive composition P, the content of the carboxyl group-containing monomer contained as a monomer unit is suppressed to a low level by the (meth) acrylate polymer (A), and the obtained adhesion is obtained. The object to be attached is capable of suppressing defects due to acid, and for example, in the case of a transparent conductive film or a metal film, these defects due to acid can be suppressed. In particular, when the attached object is a transparent conductive film, the transparent conductive film can be prevented from being corroded or the resistance value of the transparent conductive film can be changed.
(1)(甲基)丙烯酸酯聚合物(A) (1) (meth) acrylate polymer (A)
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,除上述含羥基單體、含芳香環單體以及含羧基單體外,優選 含有烷基的碳原子數為1~20的(甲基)丙烯酸烷基酯,特別是優選作為主成分而含有。另外,根據需要,還可以含有其他的單體。 The (meth) acrylate polymer (A) is preferably a monomer unit constituting the polymer, in addition to the above-mentioned hydroxyl group-containing monomer, aromatic ring-containing monomer, and carboxyl group-containing monomer. The alkyl (meth)acrylate having an alkyl group and having 1 to 20 carbon atoms is particularly preferably contained as a main component. Further, other monomers may be contained as needed.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,通過含有烷基的碳原子數為1~20的(甲基)丙烯酸烷基酯,可以表現優異的黏接性。作為烷基的碳原子數為1~20的(甲基)丙烯酸烷基酯,例如,可以列舉出(甲基)丙烯酸甲基酯、(甲基)丙烯酸乙基酯、(甲基)丙烯酸丙基酯、(甲基)丙烯酸正丁基酯、(甲基)丙烯酸正戊基酯、(甲基)丙烯酸正己基酯、(甲基)丙烯酸2-乙基己基酯、(甲基)丙烯酸異辛基酯、(甲基)丙烯酸正癸基酯、(甲基)丙烯酸正十二烷基酯、(甲基)丙烯酸肉豆蔻基酯、(甲基)丙烯酸十六烷基酯、(甲基)丙烯酸硬脂基酯等。其中,從更加提高黏接性的觀點考慮,優選烷基的碳原子數為1~8的(甲基)丙烯酸酯,特別優選(甲基)丙烯酸甲基酯以及(甲基)丙烯酸正丁基酯。而且,這些可以單獨使用,也可以組合兩種以上使用。 The (meth) acrylate polymer (A) exhibits excellent adhesion as a monomer unit constituting the polymer by an alkyl (meth) acrylate having an alkyl group and having 1 to 20 carbon atoms. Sex. Examples of the (meth)acrylic acid alkyl ester having 1 to 20 carbon atoms in the alkyl group include methyl (meth)acrylate, ethyl (meth)acrylate, and (meth)acrylic acid. Base ester, n-butyl (meth) acrylate, n-pentyl (meth) acrylate, n-hexyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, (meth) acrylate Octyl ester, n-decyl (meth)acrylate, n-dodecyl (meth)acrylate, myristyl (meth)acrylate, cetyl (meth)acrylate, (methyl) ) stearyl acrylate and the like. Among them, from the viewpoint of further improving the adhesion, a (meth) acrylate having an alkyl group having 1 to 8 carbon atoms is preferable, and a methyl (meth) acrylate and a n-butyl (meth) acrylate are particularly preferable. ester. Further, these may be used alone or in combination of two or more.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,優選含有50質量%~93.9質量%的烷基的碳原子數為1~20的(甲基)丙烯酸烷基酯,特別優選含有64.2質量%~93質量%,進一步優選含有80質量%~90質量%。另外,如果含有50質量%以上的(甲基)丙烯酸烷基酯,則(甲基)丙烯酸酯聚合物(A)可被賦予優異的黏接性。另外,通過含有93.9質量%以下的(甲基)丙烯酸烷基酯,可在(甲基)丙烯酸酯聚合物(A)中以優選的量導入其他單體成分。 The (meth) acrylate polymer (A), as a monomer unit constituting the polymer, preferably contains from 50% by mass to 99.9% by mass of an alkyl group having 1 to 20 carbon atoms of (meth)acrylic acid alkyl group. The ester is particularly preferably contained in an amount of from 64.2% by mass to 93% by mass, and more preferably from 80% by mass to 90% by mass. In addition, when 50% by mass or more of the alkyl (meth)acrylate is contained, the (meth) acrylate polymer (A) can be imparted with excellent adhesion. Further, by containing 99.9% by mass or less of the alkyl (meth)acrylate, the other monomer component can be introduced into the (meth)acrylate polymer (A) in a preferred amount.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有含羥基單體。該羥基與異氰酸酯類架橋劑(B)的異氰酸酯基反應性高,通過它們的反應,(甲基)丙烯酸酯聚合物(A)通過異氰酸酯類架橋劑(B)而架橋。通過該架橋結構所得到的黏接劑,耐久性以及耐變形性優異。 The (meth) acrylate polymer (A) contains a hydroxyl group-containing monomer as a monomer unit constituting the polymer. The hydroxyl group has high reactivity with the isocyanate group of the isocyanate-based bridging agent (B), and the (meth)acrylate polymer (A) is bridged by the isocyanate-based bridging agent (B) by the reaction thereof. The adhesive obtained by the bridge structure is excellent in durability and deformation resistance.
作為含羥基單體,例如可以列舉出(甲基)丙烯酸2-羥基乙基酯、(甲基)丙烯酸2-羥基丙基酯、(甲基)丙烯酸3-羥基丙基酯、(甲基)丙烯酸2-羥基丁基酯、(甲基)丙烯酸3-羥基丁基酯、(甲基)丙烯酸4-羥基丁基酯等的(甲基)丙烯酸羥基烷基酯等。其中,從與異氰酸酯類架橋劑(B)的反應性觀點考慮,優選(甲基)丙烯酸2-羥基乙基酯或(甲基)丙烯酸4-羥基丁基酯。這些可以單獨使用,也可以組合兩種以上使用。 Examples of the hydroxyl group-containing monomer include 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, and (methyl). A hydroxyalkyl (meth)acrylate such as 2-hydroxybutyl acrylate, 3-hydroxybutyl (meth)acrylate or 4-hydroxybutyl (meth)acrylate. Among them, 2-hydroxyethyl (meth)acrylate or 4-hydroxybutyl (meth)acrylate is preferred from the viewpoint of reactivity with the isocyanate-based bridging agent (B). These may be used alone or in combination of two or more.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有1質量%~5質量%的含羥基單體,優選含有2質量%~4質量%。含羥基單體的含有量在上述範圍,則形成的架橋結構變得良好,所得到的黏接劑具有優異的耐久性以及耐變形性。含羥基單體的含有量如果小於1質量%,則架橋點過少,凝集力降低,所得到的黏接劑無法發揮優異的耐久性。另一方面,含羥基單體的含有量如果超過5質量%,則架橋點過多,所得到的黏接劑無法變得柔軟,應力緩和性下降,由此,無法應對基材的收縮,耐久性和耐變形性變差。 The (meth) acrylate polymer (A) contains 1% by mass to 5% by mass of the hydroxyl group-containing monomer as the monomer unit constituting the polymer, and preferably contains 2% by mass to 4% by mass. When the content of the hydroxyl group-containing monomer is in the above range, the bridging structure formed is good, and the obtained adhesive has excellent durability and deformation resistance. When the content of the hydroxyl group-containing monomer is less than 1% by mass, the bridging point is too small, the cohesive force is lowered, and the obtained adhesive does not exhibit excellent durability. On the other hand, when the content of the hydroxyl group-containing monomer exceeds 5% by mass, the bridging point is too large, the obtained adhesive cannot be softened, and the stress relaxation property is lowered, whereby the shrinkage of the substrate and the durability cannot be dealt with. And the deformation resistance is deteriorated.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有含芳香環單體。由此,(甲基)丙烯酸酯聚合物(A)具有適宜的硬度,所得到的黏接劑,容易兼具凝集力與應 力緩和性,耐久性以及耐漏光性優異。 The (meth) acrylate polymer (A) contains an aromatic ring-containing monomer as a monomer unit constituting the polymer. Thus, the (meth) acrylate polymer (A) has a suitable hardness, and the obtained adhesive is easy to have both cohesive force and It is excellent in strength, durability, and light leakage resistance.
作為含芳香環單體,例如可以舉出(甲基)丙烯酸苯基酯、(甲基)丙烯酸2-苯基乙基酯、(甲基)丙烯酸苄基酯、(甲基)丙烯酸萘基酯、(甲基)丙烯酸苯氧基乙基酯、(甲基)丙烯酸苯氧基丁基酯、乙氧基化鄰苯基苯酚丙烯酸酯、苯氧基聚乙二醇(甲基)丙烯酸酯、環氧乙烷改性甲酚(甲基)丙烯酸酯、環氧乙烷(EO)改性壬基苯酚(甲基)丙烯酸酯等,其中,從提高凝集力的觀點考慮,優選(甲基)丙烯酸2-苯基乙基酯。這些可以單獨使用,也可以組合兩種以上使用。 Examples of the aromatic ring-containing monomer include phenyl (meth)acrylate, 2-phenylethyl (meth)acrylate, benzyl (meth)acrylate, and naphthyl (meth)acrylate. , phenoxyethyl (meth)acrylate, phenoxybutyl (meth)acrylate, ethoxylated o-phenylphenol acrylate, phenoxy polyethylene glycol (meth) acrylate, Ethylene oxide modified cresol (meth) acrylate, ethylene oxide (EO) modified nonyl phenol (meth) acrylate, etc., among them, (methyl) is preferred from the viewpoint of improving cohesive force. 2-phenylethyl acrylate. These may be used alone or in combination of two or more.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有5質量%~30質量%含芳香環單體,優選為含有10質量%~25質量%,特別優選為含有15質量%~20質量%。含芳香環單體的含有量在上述範圍,則所得到的黏接劑具有優異的應力緩和性、耐久性以及耐漏光性。含芳香環單體的含有量如果小於5質量%,則所得到的黏接劑的耐漏光性變差。另一方面,含芳香環單體的含有量如果超過30質量%,則其他成分的搭配量減少,所得到的黏接劑的耐久性變差。 The (meth) acrylate polymer (A) contains 5% by mass to 30% by mass of the aromatic ring-containing monomer as the monomer unit constituting the polymer, and preferably contains 10% by mass to 25% by mass, particularly preferably Contains 15% by mass to 20% by mass. When the content of the aromatic ring-containing monomer is in the above range, the obtained adhesive has excellent stress relaxation properties, durability, and light leakage resistance. When the content of the aromatic ring-containing monomer is less than 5% by mass, the light leakage resistance of the obtained adhesive is deteriorated. On the other hand, when the content of the aromatic ring-containing monomer exceeds 30% by mass, the amount of the other components is reduced, and the durability of the obtained adhesive is deteriorated.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的單體單元,含有含羧基單體。該羧基可促進(甲基)丙烯酸酯聚合物(A)中的羥基與異氰酸酯類架橋劑(B)的架橋反應,同時,羧基本身也與異氰酸酯類架橋劑(B)發生架橋反應。由此所得到的黏接劑,架橋的程度適當,(甲基)丙烯酸酯聚合物(A)之間的架橋程度均勻,從而耐久性以及耐變形性優異。 The (meth) acrylate polymer (A) contains a carboxyl group-containing monomer as a monomer unit constituting the polymer. The carboxyl group promotes the bridging reaction of the hydroxyl group in the (meth)acrylate polymer (A) with the isocyanate bridging agent (B), and the carboxyl group itself also undergoes a bridging reaction with the isocyanate bridging agent (B). The adhesive thus obtained has an appropriate degree of bridging, and the degree of bridging between the (meth) acrylate polymers (A) is uniform, and the durability and the deformation resistance are excellent.
(甲基)丙烯酸酯聚合物(A),作為構成該聚合物的 單體單元,含有0.1質量%~0.8質量%的含羧基單體,優選為含有0.1質量%~0.5質量%,特別優選為含有0.1質量%~0.3質量%。含羧基單體在上述範圍,則所得到的黏接劑具有優異的耐久性以及耐變形性。含羧基單體的含有量如果小於0.1質量%,則所得到的黏接劑,耐久性及耐變形性變差。另一方面,含羧基單體的含有量如果超過0.8質量%,則所得到的黏接劑,在貼附對象為透明導電膜等的情況時,透明導電膜等被腐蝕,或透明導電膜的電阻值發生大的變化。 (meth) acrylate polymer (A) as a constituent of the polymer The monomer unit contains 0.1% by mass to 0.8% by mass of the carboxyl group-containing monomer, preferably 0.1% by mass to 0.5% by mass, particularly preferably 0.1% by mass to 0.3% by mass. When the carboxyl group-containing monomer is in the above range, the obtained adhesive has excellent durability and deformation resistance. When the content of the carboxyl group-containing monomer is less than 0.1% by mass, the obtained adhesive has poor durability and deformation resistance. On the other hand, when the content of the carboxyl group-containing monomer is more than 0.8% by mass, when the attached adhesive is a transparent conductive film or the like, the transparent conductive film or the like is corroded, or the transparent conductive film is etched. A large change in the resistance value occurs.
作為上述其他的單體,即使是為了不妨礙上述含羥基單體的羥基以及含羧基單體的羧基與異氰酸酯類架橋劑(B)的反應,也優選不包含與異氰酸酯類架橋劑(B)具有反應性的官能基的單體。作為這樣的其他單體,例如可以列舉(甲基)丙烯酸甲氧基乙基、(甲基)丙烯酸乙氧基乙基等的(甲基)丙烯酸烷氧基烷基酯;丙烯醯胺、甲基丙烯醯胺等的非架橋性的丙烯醯胺;(甲基)丙烯酸N,N-二甲基氨基乙基、(甲基)丙烯酸N,N-二甲基氨基丙基等的具有非架橋性的3級氨基的(甲基)丙烯酸酯;乙酸乙烯酯等。這些可以單獨使用,也可以組合兩種以上使用。 The other monomer is preferably not contained in the isocyanate-based bridging agent (B), in order not to hinder the reaction of the hydroxyl group of the hydroxyl group-containing monomer and the carboxyl group of the carboxyl group-containing monomer with the isocyanate bridging agent (B). Reactive functional group monomer. Examples of such other monomers include (meth)acrylic acid alkoxyalkyl esters such as methoxyethyl (meth)acrylate and ethoxyethyl (meth)acrylate; acrylamide, A Non-branching acrylamide such as acrylamide; N,N-dimethylaminoethyl (meth)acrylate, N,N-dimethylaminopropyl (meth)acrylate, etc. A 3-grade amino (meth) acrylate; vinyl acetate, and the like. These may be used alone or in combination of two or more.
(甲基)丙烯酸酯聚合物(A)的聚合方式,可以為無規共聚物,也可以為嵌段共聚物。 The polymerization method of the (meth) acrylate polymer (A) may be a random copolymer or a block copolymer.
(甲基)丙烯酸酯聚合物(A)的重均分子量為140萬~250萬,優選為150萬~220萬,特別優選為180萬~200萬。另外,本說明書中的重均分子量,為根據凝膠滲透色譜法(GPC)法所測定的聚苯乙烯換算的值。 The (meth) acrylate polymer (A) has a weight average molecular weight of from 1.4 to 2.5 million, preferably from 1.5 to 2.2 million, particularly preferably from 1.8 to 2,000,000. The weight average molecular weight in the present specification is a value in terms of polystyrene measured by a gel permeation chromatography (GPC) method.
(甲基)丙烯酸酯聚合物(A)的重均分子量如果小於140萬,則所得到的黏接劑耐久性變差。另外,(甲基)丙烯酸酯聚合物(A)的重均分子量如果超過250萬,則所得到的黏接劑耐變形性降低。 When the weight average molecular weight of the (meth) acrylate polymer (A) is less than 1.4 million, the durability of the obtained adhesive is deteriorated. Further, when the weight average molecular weight of the (meth) acrylate polymer (A) exceeds 2.5 million, the deformation resistance of the obtained adhesive is lowered.
另外,在黏接性組合物P中,(甲基)丙烯酸酯聚合物(A)可以單獨使用一種,也可以組合兩種以上使用。另外,黏接性組合物P還可進一步含有不含有含羥基單體、含芳香環單體或含羧基單體作為構成單體單元的(甲基)丙烯酸酯聚合物。 Further, in the adhesive composition P, the (meth) acrylate polymer (A) may be used alone or in combination of two or more. Further, the adhesive composition P may further contain a (meth) acrylate polymer which does not contain a hydroxyl group-containing monomer, an aromatic ring-containing monomer or a carboxyl group-containing monomer as a constituent monomer unit.
(2)異氰酸酯類架橋劑(B) (2) Isocyanate bridging agent (B)
異氰酸酯類架橋劑(B)具有與(甲基)丙烯酸酯聚合物(A)所具有的羥基的反應性以及與矽烷偶聯劑(C)所具有的巰基的反應性優異的好處。 The isocyanate-based bridging agent (B) has an advantage of being excellent in reactivity with a hydroxyl group of the (meth)acrylate polymer (A) and reactivity with a mercapto group which the decane coupling agent (C) has.
異氰酸酯類架橋劑(B)為至少含有聚異氰酸酯化合物的架橋劑。作為聚異氰酸酯化合物,例如可以舉出甲次苯基二異氰酸酯、二苯甲烷二異氰酸酯、伸二甲苯二異氰酸酯等的芳香族聚異氰酸酯;六亞甲基二異氰酸酯等的脂肪族聚異氰酸酯;異佛爾酮二異氰酸酯、氫化二苯甲烷二異氰酸酯等的脂環式聚異氰酸酯等,以及這些的雙縮脲體、異氰酸酯體,進一步可以列舉乙二醇、丙二醇、新戊二醇、三羥甲基丙烷、蓖麻油等的作為與含有低分子活性氫化合物的反應物的加和物體等。其中在用於偏光板的情況時,從耐久性以及加工性的觀點考慮,優選為三羥甲基丙烷改性芳香族聚異氰酸酯,特別優選為三羥甲基丙烷改性甲次苯基二異氰酸酯。上述異氰酸酯類架橋 劑(B)可以單獨使用一種,或者也可以組合兩種以上使用。 The isocyanate-based bridging agent (B) is a bridging agent containing at least a polyisocyanate compound. Examples of the polyisocyanate compound include aromatic polyisocyanates such as methylphenyl diisocyanate, diphenylmethane diisocyanate, and xylene diisocyanate; aliphatic polyisocyanates such as hexamethylene diisocyanate; and isophorone; Examples of the alicyclic polyisocyanate such as a diisocyanate or a hydrogenated diphenylmethane diisocyanate, and the biuret or isocyanate thereof include ethylene glycol, propylene glycol, neopentyl glycol, trimethylolpropane and hydrazine. An additive such as sesame oil or the like which is a reactant containing a low molecular weight active hydrogen compound. In the case of being used for a polarizing plate, from the viewpoint of durability and workability, trimethylolpropane-modified aromatic polyisocyanate is preferred, and trimethylolpropane-modified methyl phenyl diisocyanate is particularly preferred. . The above isocyanate bridge The agent (B) may be used alone or in combination of two or more.
黏接性組合物P中,異氰酸酯類架橋劑(B)的含有量,相對於(甲基)丙烯酸酯聚合物(A)100質量份,優選為0.01質量份~1質量份,特別優選為0.05質量份~0.5質量份,進一步優選為0.1質量份~0.3質量份。異氰酸酯類架橋劑(B)的含有量在上述範圍,則所得到的黏接劑中,可形成應力緩和性、耐久性以及耐變形性優異的架橋結構。 In the adhesive composition P, the content of the isocyanate-based bridging agent (B) is preferably 0.01 parts by mass to 1 part by mass, particularly preferably 0.05, based on 100 parts by mass of the (meth) acrylate polymer (A). The mass part is -0.5 parts by mass, and more preferably 0.1 parts by mass to 0.3 parts by mass. When the content of the isocyanate-based bridging agent (B) is in the above range, a bridging structure excellent in stress relaxation, durability, and deformation resistance can be formed in the obtained adhesive.
(3)矽烷偶聯劑(C) (3) decane coupling agent (C)
本實施形態中的矽烷偶聯劑(C)具有巰基。該巰基與異氰酸酯類架橋劑(B)的異氰酸酯基容易反應。如前所述,據推測將黏接性組合物P架橋的黏接劑中,矽烷偶聯劑(C)的烷氧基甲矽烷,與(甲基)丙烯酸酯聚合物(A)保持適宜距離,即,異氰酸酯類架橋劑(B)中複數的異氰酸酯基相互間保持距離,懸掛於(甲基)丙烯酸酯聚合物(A)上。像這樣,烷氧基甲矽烷通過與(架橋的)(甲基)丙烯酸酯聚合物(A)保持適宜距離而存在,可發揮優異的偶聯效果,由此所得到的黏接劑,黏接性優異,即使在高溫條件下以及濕熱條件下,黏接耐久性也優異。該效果,在黏接劑的貼附對象為玻璃或金屬等無機材料的情況時,發揮得尤其顯著。 The decane coupling agent (C) in the present embodiment has a mercapto group. The thiol group reacts easily with the isocyanate group of the isocyanate-based bridging agent (B). As described above, it is presumed that the adhesive of the adhesive composition P is bridged, and the alkoxydecane of the decane coupling agent (C) is kept at a suitable distance from the (meth) acrylate polymer (A). That is, the plurality of isocyanate groups in the isocyanate-based bridging agent (B) are kept apart from each other and suspended from the (meth) acrylate polymer (A). In this way, the alkoxycarbane is present at a suitable distance from the (bridged) (meth) acrylate polymer (A), and an excellent coupling effect can be exerted, whereby the obtained adhesive is bonded. It is excellent in adhesion and excellent in adhesion durability even under high temperature conditions and hot and humid conditions. This effect is particularly remarkable when the attachment target of the adhesive is an inorganic material such as glass or metal.
作為矽烷偶聯劑(C),為分子內至少具有一個巰基、至少具有一個烷氧基甲矽烷的有機矽化合物,與黏接劑成分的相溶性良好,且具有光透過性,例如優選實質上為透明者。 The decane coupling agent (C) is an organic ruthenium compound having at least one fluorenyl group in the molecule and having at least one alkoxymethane, and has good compatibility with the binder component and has light permeability. For example, it is preferable to substantially For the transparent.
作為上述矽烷偶聯劑(C),例如,可以列舉出3-巰基丙基三甲氧基矽烷、3-巰基丙基三乙氧基矽烷、3-巰基丙基 甲基二甲氧基矽烷等的含巰基低分子型矽烷偶聯劑;3-巰基丙基三甲氧基矽烷、3-巰基丙基三乙氧基矽烷、3-巰基丙基甲基二甲氧基矽烷等的含巰基矽烷化合物與甲基三乙氧基矽烷、乙基三乙氧基矽烷、甲基三甲氧基矽烷、乙基三甲氧基矽烷等的含烷基矽烷化合物的共縮合物等的含巰基低聚物型矽烷偶聯劑等。其中,從提高耐久性的觀點考慮,優選為含巰基低聚物型矽烷偶聯劑,特別是優選含巰基矽烷化合物與含烷基矽烷化合物的共縮合物,進一步優選為3-巰基丙基三甲氧基矽烷與甲基三乙氧基矽烷的共縮合物。這些可以單獨使用一種,也可以組合兩種以上使用。 Examples of the above decane coupling agent (C) include 3-mercaptopropyltrimethoxydecane, 3-mercaptopropyltriethoxydecane, and 3-mercaptopropylpropyl group. a mercapto group-containing low molecular type decane coupling agent such as methyl dimethoxydecane; 3-mercaptopropyltrimethoxydecane, 3-mercaptopropyltriethoxydecane, 3-mercaptopropylmethyldimethoxy a cocondensate of a decyl-containing decane compound such as a decane or the like, and an alkyl decane-containing compound such as methyltriethoxysilane, ethyltriethoxysilane, methyltrimethoxydecane or ethyltrimethoxydecane. A fluorenyl-containing oligomer-type decane coupling agent or the like. Among them, from the viewpoint of improving durability, a fluorenyl group-containing oligomer-type decane coupling agent is preferable, and a cocondensate containing a decyl decane compound and an alkyl decane-containing compound is particularly preferable, and 3-mercaptopropyl propyl group is further preferable. a cocondensate of oxydecane with methyltriethoxydecane. These may be used alone or in combination of two or more.
黏接性組合物P中矽烷偶聯劑(C)的含有量,相對於(甲基)丙烯酸酯聚合物(A)100質量份,優選為0.01質量份~0.4質量份,特別優選為0.1質量份~0.3質量份。矽烷偶聯劑(C)的含有量如果小於0.01質量份,則有難以得到通過該矽烷偶聯劑(C)產生的效果的情況。另一方面,矽烷偶聯劑(C)的含有量如果超過0.4質量份,則異氰酸酯類架橋劑(B)與(甲基)丙烯酸酯聚合物(A)的反應有受到阻礙的情況。 The content of the decane coupling agent (C) in the adhesive composition P is preferably 0.01 parts by mass to 0.4 parts by mass, particularly preferably 0.1% by mass based on 100 parts by mass of the (meth) acrylate polymer (A). Parts ~ 0.3 parts by mass. When the content of the decane coupling agent (C) is less than 0.01 parts by mass, it may be difficult to obtain an effect by the decane coupling agent (C). On the other hand, when the content of the decane coupling agent (C) exceeds 0.4 parts by mass, the reaction between the isocyanate-based bridging agent (B) and the (meth) acrylate polymer (A) may be inhibited.
(4)各種添加劑 (4) Various additives
黏接性組合物P,根據需要,可以添加在丙烯酸類黏接劑中通常使用的的各種添加劑,例如,帶電防止劑、黏接賦予劑、氧化防止劑、紫外線吸收劑、光穩定劑、阻燃劑、充填劑、折射率調整劑等。 The adhesive composition P may be added with various additives commonly used in acrylic adhesives, for example, a charge preventive agent, an adhesion-imparting agent, an oxidation preventive agent, an ultraviolet absorber, a light stabilizer, and a resist. Fuel, filler, refractive index modifier, etc.
作為帶電防止劑的具體例子,可以列舉N-丁基-4-甲基吡啶鎓六氟磷酸鹽、N-己基-4-甲基吡啶鎓六氟磷酸鹽、 N-丁基-2-己基吡啶高氯酸鹽、雙(氟磺醯亞胺)鉀(KFSI)、雙(三氟甲磺醯亞胺)鉀(KTFSI)、雙(氟磺醯亞胺)鋰(LIFSI)、雙(三氟甲磺醯氯醯亞胺)鋰(LITFSI)、N-丁基-2-己基吡啶鎓雙(三氟甲磺醯基)亞胺等。這些帶電防止劑可以單獨使用一種,也可以組合兩種以上使用。 Specific examples of the antistatic agent include N-butyl-4-methylpyridinium hexafluorophosphate and N-hexyl-4-methylpyridinium hexafluorophosphate. N-butyl-2-hexylpyridine perchlorate, bis(fluorosulfonimide) potassium (KFSI), bis(trifluoromethanesulfonimide) potassium (KTFSI), bis(fluorosulfonimide) Lithium (LIFSI), lithium bis(trifluoromethanesulfonium chloride) (LITFSI), N-butyl-2-hexylpyridinium bis(trifluoromethanesulfonyl)imide, and the like. These charge inhibitors may be used alone or in combination of two or more.
〔黏接性組合物的製造方法〕 [Method for Producing Adhesive Composition]
黏接性組合物P可以通過製造(甲基)丙烯酸酯聚合物(A),將所得到的(甲基)丙烯酸酯聚合物(A)、異氰酸酯類架橋劑(B)和矽烷偶聯劑(C)進行混合,同時,根據需要,加入添加劑來製造。 The adhesive composition P can be obtained by producing a (meth) acrylate polymer (A), the obtained (meth) acrylate polymer (A), an isocyanate bridging agent (B), and a decane coupling agent ( C) Mixing is carried out while adding an additive as needed to manufacture.
(甲基)丙烯酸酯聚合物(A),可以通過用通常的自由基聚合法,聚合構成聚合物的單體單元的混合物來製造。(甲基)丙烯酸酯聚合物(A)的聚合,可根據需要使用聚合引發劑,由溶液聚合法等進行。作為聚合溶劑,例如可以舉出乙酸乙酯、乙酸正丁基酯、乙酸異丁基酯、甲苯、丙酮、己烷、甲基乙基酮等,可以並用兩種以上。 The (meth) acrylate polymer (A) can be produced by polymerizing a mixture of monomer units constituting the polymer by a usual radical polymerization method. The polymerization of the (meth) acrylate polymer (A) can be carried out by a solution polymerization method or the like using a polymerization initiator as needed. Examples of the polymerization solvent include ethyl acetate, n-butyl acetate, isobutyl acetate, toluene, acetone, hexane, methyl ethyl ketone, and the like, and two or more kinds thereof may be used in combination.
作為聚合引發劑,可以列舉偶氮類化合物、有機過氧化物等,可以同時使用兩種以上。作為偶氮類化合物,可以列舉2,2’-偶氮雙異丁腈、2,2’-偶氮雙(2-甲基丁腈)、1,1’-偶氮雙(環己烷1-腈)、2,2’-偶氮雙(2,4-二甲基戊腈)、2,2’-偶氮雙(2,4-二甲基-4-甲氧基戊腈)、二甲基2,2’-偶氮雙(2-甲基丙酸酯)、4,4’-偶氮雙(4-氰基纈草酸)、2,2’-偶氮雙(2-羥基甲基丙腈)、2,2’-偶氮雙〔2-(2-咪坐琳-2-基)丙烷〕等。 Examples of the polymerization initiator include an azo compound and an organic peroxide, and two or more kinds thereof can be used at the same time. Examples of the azo compound include 2,2'-azobisisobutyronitrile, 2,2'-azobis(2-methylbutyronitrile), and 1,1'-azobis(cyclohexane-1). - nitrile), 2,2'-azobis(2,4-dimethylvaleronitrile), 2,2'-azobis(2,4-dimethyl-4-methoxyvaleronitrile), Dimethyl 2,2'-azobis(2-methylpropionate), 4,4'-azobis(4-cyanoshikimate), 2,2'-azobis(2-hydroxyl) Methylpropionitrile), 2,2'-azobis[2-(2-misoline-2-yl)propane], and the like.
作為有機過氧化物,例如,可以列舉出苯甲醯過氧化物、過氧苯甲酸叔丁基酯、異丙苯過氧化氫、二異丙基過氧二碳酸酯、二正丙基過氧二碳酸酯、二(2-乙氧基乙基)過氧二碳酸酯、過氧新葵酸叔丁基酯、過氧特戊酸叔丁基酯、(3,5,5-三甲基己醯基)過氧化物、二丙醯過氧化物、二乙醯過氧化物等。 Examples of the organic peroxide include benzamidine peroxide, t-butyl peroxybenzoate, cumene hydroperoxide, diisopropyl peroxydicarbonate, and di-n-propylperoxy. Dicarbonate, bis(2-ethoxyethyl)peroxydicarbonate, tert-butyl peroxy neopentate, tert-butyl peroxypivalate, (3,5,5-trimethyl Benzyl) peroxide, dipropylene peroxide, diethyl hydrazine peroxide, and the like.
另外,在上述聚合步驟中,通過搭配2-巰基乙醇等的鏈移動劑,可以對得到的聚合物的重均分子量進行調節。 Further, in the above polymerization step, the weight average molecular weight of the obtained polymer can be adjusted by mixing a chain shifting agent such as 2-mercaptoethanol.
得到(甲基)丙烯酸酯聚合物(A)後,在(甲基)丙烯酸酯聚合物(A)的溶液中,添加異氰酸酯類架橋劑(B)、矽烷偶聯劑(C)、稀釋溶劑以及根據需要加入添加劑,進行充分混合,得到在溶劑中稀釋了的黏接性組合物P(塗布溶液)。 After obtaining the (meth) acrylate polymer (A), an isocyanate bridging agent (B), a decane coupling agent (C), a diluent solvent, and the solution of the (meth) acrylate polymer (A) are added. The additive is added as needed, and sufficiently mixed to obtain a tackifying composition P (coating solution) diluted in a solvent.
作為對黏接性組合物P進行稀釋,得到塗布溶液的稀釋溶劑,例如可以使用己烷、庚烷、環己烷等的脂肪族烴;甲苯、二甲苯等的芳香族烴;二氯甲烷、二氯乙烷等的鹵代烴;甲醇、乙醇、丙醇、丁醇、1-甲氧基-2-丙醇等的醇;丙酮、甲基乙基酮、2-戊酮、異佛爾酮、環己酮等的酮類;乙酸乙酯、乙酸丁基酯等的酯;乙基溶纖劑等的溶纖劑類溶劑等。 As a diluent solvent for diluting the adhesive composition P to obtain a coating solution, for example, an aliphatic hydrocarbon such as hexane, heptane or cyclohexane; an aromatic hydrocarbon such as toluene or xylene; methylene chloride; Halogenated hydrocarbon such as dichloroethane; alcohol such as methanol, ethanol, propanol, butanol or 1-methoxy-2-propanol; acetone, methyl ethyl ketone, 2-pentanone, isophor Ketones such as ketone and cyclohexanone; esters such as ethyl acetate and butyl acetate; and cellosolve solvents such as ethyl cellosolve.
作為如此調制的塗布溶液的濃度、黏度,只要為在塗布可能的範圍即可,沒有特別的限制,可以根據情況進行適宜選定。例如,黏接性組合物P的濃度可以稀釋到10質量%~40質量%。另外,得到塗布溶液時,稀釋溶劑等的添加不是必要條件,黏接性組合物P只要是塗布可能的黏度等,稀釋溶劑不添加也可。該情況時黏接性組合物P,將(甲基)丙烯酸 酯聚合物(A)的聚合溶劑直接作為稀釋溶劑的塗布溶液。 The concentration and viscosity of the coating solution to be prepared in this manner are not particularly limited as long as they are within the range of application, and may be appropriately selected depending on the case. For example, the concentration of the adhesive composition P can be diluted to 10% by mass to 40% by mass. In addition, when a coating solution is obtained, the addition of a diluent solvent or the like is not a requirement, and the adhesive composition P may be added without any addition as long as it is a coating viscosity. In this case, the adhesive composition P, (meth)acrylic acid The polymerization solvent of the ester polymer (A) is directly used as a coating solution of a diluent solvent.
〔黏接劑〕 [adhesive]
本實施形態所述黏接劑,是將黏接性組合物P架橋所構成。黏接性組合物P的架橋可通過加熱處理進行。另外,此加熱處理還可兼用作對黏接性組合物P的稀釋溶劑等進行揮發時的乾燥處理。 The adhesive according to the present embodiment is formed by bridging the adhesive composition P. The bridging of the adhesive composition P can be carried out by heat treatment. In addition, this heat treatment can also serve as a drying treatment for volatilizing a dilution solvent or the like of the adhesive composition P.
在進行加熱處理的情況時,加熱溫度優選為50℃~150℃,特別優選為70℃~120℃。另外,加熱時間優選為30秒~10分,特別優選為50秒~2分。加熱處理後,根據需要,也可以在常溫(例如,23℃、50%RH)下放置1~2周左右的熟成期間。需要該熟成期間的情況時,在熟成期間經過後,不需要熟成期間的情況時,在加熱處理結束後,形成黏接劑層。 In the case of heat treatment, the heating temperature is preferably from 50 ° C to 150 ° C, particularly preferably from 70 ° C to 120 ° C. Further, the heating time is preferably from 30 seconds to 10 minutes, and particularly preferably from 50 seconds to 2 minutes. After the heat treatment, if necessary, a ripening period of about 1 to 2 weeks may be left at normal temperature (for example, 23 ° C, 50% RH). When the ripening period is required, when the ripening period is not required after the aging period, the adhesive layer is formed after the heat treatment is completed.
通過上述加熱處理(以及熟成),通過異氰酸酯類架橋劑(B),(甲基)丙烯酸酯聚合物(A)架橋,形成三維網絡結構。另外,矽烷偶聯劑(C)的巰基,與異氰酸酯類架橋劑(B)的異氰酸酯基容易反應,據推測該矽烷偶聯劑(C)的烷氧基甲矽烷,通過該異氰酸酯類架橋劑(B),與(甲基)丙烯酸酯聚合物(A),進一步與上述結構保持適宜距離而存在,發揮優異的偶聯效果。 By the above heat treatment (and aging), a three-dimensional network structure is formed by bridging the isocyanate bridging agent (B) and the (meth) acrylate polymer (A). Further, the fluorenyl group of the decane coupling agent (C) is easily reacted with the isocyanate group of the isocyanate-based bridging agent (B), and it is presumed that the alkoxymethyl decane of the decane coupling agent (C) passes through the isocyanate-based bridging agent ( B), the (meth) acrylate polymer (A) is further provided at a suitable distance from the above structure, and exhibits an excellent coupling effect.
另外,將黏接性組合物P架橋所得到的黏接劑,即使在上述三維網絡結構呈現較為鬆散的狀態時,也通過含有芳香環,而具有適宜的凝集力。由此,不會使凝集力降低,即可提高應力緩和性,因此,黏接劑的耐久性以及耐變形性高。 另外,憑借通過矽烷偶聯劑(C)得到的優異的偶聯效果,對玻璃表面等的黏接性優異,在高溫條件下或濕熱條件下,也可發揮優異的黏接耐久性。例如,在85℃的高溫條件下或60℃、90%RH的濕熱條件下放置250小時的情況時,也能防止和抑制浮起、剝離、氣泡等的發生。另外,將通過上述黏接劑貼合的薄偏光板和薄膜(例如,膜厚度為0.5mm左右)與玻璃板的積層體,在85℃的高溫條件下放置250小時的情況時,也可將該積層體的彎曲抑制得較小。 Further, the adhesive obtained by bridging the adhesive composition P has an appropriate aggregating power by containing an aromatic ring even when the three-dimensional network structure is in a loose state. Thereby, the stress relaxation property can be improved without lowering the cohesive force, and therefore the durability and deformation resistance of the adhesive are high. In addition, the excellent coupling effect by the decane coupling agent (C) is excellent in adhesion to a glass surface or the like, and exhibits excellent adhesion durability under high temperature conditions or under moist heat conditions. For example, when it is left to stand under high temperature conditions of 85 ° C or under hot humid conditions of 60 ° C and 90% RH for 250 hours, occurrence of floating, peeling, bubbles, and the like can be prevented and suppressed. In addition, when a thin polarizing plate and a film (for example, a film thickness of about 0.5 mm) bonded to the above-mentioned adhesive and a laminated body of a glass plate are left at a high temperature of 85 ° C for 250 hours, it is also possible to The bending of the laminate is suppressed to a small extent.
本實施形態所述黏接劑的凝膠分率,優選為55%~80%,特別優選為60%~75%。凝膠分率如果小於55%,則黏接劑的凝集力不足,有耐久性以及再加工性降低的情況。特別是用於COP偏光板的情況時,在高溫下,有得不到充分黏接耐久性的情況。另一方面,凝膠分率如果超過80%,則應力緩和性變得過低,有耐久性或耐變形性降低的情況。 The gel fraction of the adhesive according to the present embodiment is preferably 55% to 80%, particularly preferably 60% to 75%. When the gel fraction is less than 55%, the cohesive force of the adhesive is insufficient, and durability and reworkability may be deteriorated. In particular, in the case of a COP polarizing plate, at the high temperature, sufficient adhesion durability may not be obtained. On the other hand, when the gel fraction exceeds 80%, the stress relaxation property is too low, and durability or deformation resistance may be lowered.
〔黏接片〕 [bonding sheet]
如圖1所示,第1實施形態所述黏接片1A,按照從下往上的順序,由剝離片12、積層於剝離片12的剝離面上的黏接劑層11、以及積層於黏接劑層11上的基材13所構成。 As shown in Fig. 1, in the adhesive sheet 1A of the first embodiment, the release sheet 12, the adhesive layer 11 laminated on the release surface of the release sheet 12, and the adhesive layer are laminated in the order from the bottom to the top. The substrate 13 on the adhesive layer 11 is composed of a substrate 13 .
另外,如圖2所示,第2實施形態所述黏接片1B,由兩片剝離片12a、12b,以及以與這兩片剝離片12a、12b的剝離面相接的方式,被這兩片剝離片12a、12b所夾持的黏接劑層11所構成。另外,本說明書中所謂的剝離片的剝離面,是指剝離片中具有剝離性的面,包括實施了剝離處理的面以及即使未實施剝離處理也顯示出剝離性的面的兩者。 Further, as shown in Fig. 2, the adhesive sheet 1B according to the second embodiment is formed by the two peeling sheets 12a and 12b and the peeling surfaces of the two peeling sheets 12a and 12b. The adhesive layer 11 sandwiched between the release sheets 12a and 12b is formed. In addition, the peeling surface of the peeling sheet in this specification is the surface which has the peeling property in the peeling sheet, and the surface which carried out the peeling process, and the surface which shows the peeling-
在黏接片1A、1B的兩者中,黏接劑層11都是由架橋上述黏接性組合物P所成的黏接劑構成。 In both of the adhesive sheets 1A and 1B, the adhesive layer 11 is composed of an adhesive formed by bridging the above-mentioned adhesive composition P.
黏接劑層11的厚度,根據黏接片1A、1B的使用目的而適宜決定,但通常為5μm~100μm,優選為10μm~60μm的範圍。例如,在作為光學構件,特別是作為偏光板用的黏接劑層使用的情況時,優選為10μm~50μm,特別優選為15μm~30μm。 The thickness of the adhesive layer 11 is appropriately determined depending on the purpose of use of the adhesive sheets 1A and 1B, but is usually in the range of 5 μm to 100 μm, preferably 10 μm to 60 μm. For example, when it is used as an optical member, particularly as an adhesive layer for a polarizing plate, it is preferably 10 μm to 50 μm, and particularly preferably 15 μm to 30 μm.
作為基材13,沒有特別的限制,作為通常的黏接片的基材片所使用的基材都可以使用。例如,除所希望的光學構件之外,還可以列舉出人造絲、丙烯以及聚酯等使用了纖維的織布或者不織布;合成紙;上質紙、玻璃紙、含浸紙、銅板紙等的紙類;鋁、銅等的金屬箔;聚氨酯發泡體、聚乙烯發泡體等的發泡體;聚對苯二甲酸乙二醇酯、聚對苯二甲酸丁二醇酯、聚萘二酸乙二醇酯等的聚酯薄膜;聚氨酯薄膜、聚乙烯薄膜、聚丙烯薄膜、三醋酸纖維素等的纖維素薄膜;聚氯乙烯薄膜、聚偏二氯乙烯薄膜、聚乙烯醇薄膜、乙烯-乙酸乙烯酯共聚物薄膜、聚苯乙烯薄膜、聚碳酸酯薄膜、丙烯酸樹脂薄膜、降冰片烯類樹脂薄膜、環烯烴樹脂薄膜等的塑膠薄膜;這些的兩種以上的積層體等。塑膠薄膜可以為單軸壓延的薄膜或者雙軸壓延的薄膜。 The base material 13 is not particularly limited, and any substrate used as a base material sheet of a usual adhesive sheet can be used. For example, in addition to desired optical members, woven or non-woven fabrics using rayon, acryl, and polyester; synthetic paper; paper of upper quality paper, cellophane, impregnated paper, copper paper, and the like; Metal foil such as aluminum or copper; foam of polyurethane foam, polyethylene foam, etc.; polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate Polyester film such as alcohol ester; cellulose film such as polyurethane film, polyethylene film, polypropylene film, cellulose triacetate; polyvinyl chloride film, polyvinylidene chloride film, polyvinyl alcohol film, ethylene-vinyl acetate A plastic film such as an ester copolymer film, a polystyrene film, a polycarbonate film, an acrylic resin film, a norbornene resin film, or a cycloolefin resin film; or a laminate of two or more of these. The plastic film may be a uniaxially rolled film or a biaxially rolled film.
作為光學構件,例如可以列舉出偏光板(偏光薄膜)、偏光子、相位差板(相位差薄膜)、視野角補償薄膜、提高輝度薄膜、提高對比度薄膜、液晶聚合物薄膜、擴散薄膜、半透過反射薄膜等。其中,偏光板(偏光薄膜)容易收縮,尺寸變化 大,因此從要求耐久性的觀點考慮,適宜作為形成本實施形態的黏接劑(上述黏接劑層11)的基材。另外,特別是聚環烯烴類薄膜或具備該薄膜的偏光板(COP偏光板),容易收縮,尺寸變化大,而且接觸角大,密合性低,因此從要求黏接性、黏接耐久性的觀點考慮,適宜作為形成本實施形態的黏接劑(上述黏接劑層11)的基材。 Examples of the optical member include a polarizing plate (polarizing film), a polarizer, a retardation film (retardation film), a viewing angle compensation film, a brightness enhancement film, a contrast film, a liquid crystal polymer film, a diffusion film, and a semi-transmission. Reflective film, etc. Among them, the polarizing plate (polarizing film) is easy to shrink and the size changes. Since it is large, it is suitable as a base material which forms the adhesive agent (the said adhesive layer 11) of this embodiment from a viewpoint of durability. Further, in particular, a polycycloolefin film or a polarizing plate (COP polarizing plate) including the film is easily shrunk, has a large dimensional change, and has a large contact angle and low adhesion, so that adhesion and adhesion durability are required. From the viewpoint of the viewpoint, it is suitable as a base material for forming the adhesive (the above-mentioned adhesive layer 11) of the present embodiment.
基材13的厚度,根據其種類而有所不同,例如,在光學構件的情況時,通常為10μm~500μm,優選為50μm~300μm,特別優選為80μm~150μm。 The thickness of the base material 13 varies depending on the type thereof. For example, in the case of an optical member, it is usually 10 μm to 500 μm, preferably 50 μm to 300 μm, and particularly preferably 80 μm to 150 μm.
作為剝離片12、12a、12b,可以使用例如聚乙烯薄膜、聚丙烯薄膜、聚丁烯薄膜、聚丁二烯薄膜、聚甲基戊烯薄膜、聚氯乙烯薄膜、氯乙烯共聚物薄膜、聚對苯二甲酸乙二醇酯薄膜、聚萘二酸乙二醇酯薄膜、聚對苯二甲酸丁二醇酯薄膜、聚氨酯薄膜、乙烯乙酸乙烯基薄膜、離聚物樹脂薄膜、乙烯-(甲基)丙烯酸共聚物薄膜、乙烯-(甲基)丙烯酸酯共聚物薄膜、聚苯乙烯薄膜、聚碳酸酯薄膜、聚醯亞胺薄膜、氟樹脂薄膜等。另外,也可使用這些的架橋薄膜。進一步,也可以為這些的積層薄膜。 As the release sheets 12, 12a, 12b, for example, a polyethylene film, a polypropylene film, a polybutene film, a polybutadiene film, a polymethylpentene film, a polyvinyl chloride film, a vinyl chloride copolymer film, or a poly Ethylene terephthalate film, polyethylene naphthalate film, polybutylene terephthalate film, polyurethane film, vinyl acetate film, ionomer resin film, ethylene-(A) Acrylic copolymer film, ethylene-(meth)acrylate copolymer film, polystyrene film, polycarbonate film, polyimide film, fluororesin film, and the like. In addition, bridging films of these can also be used. Further, it is also possible to laminate these films.
上述剝離片的剝離面(特別是與黏接劑層11相接的面),優選為實施有剝離處理。作為剝離處理所使用的剝離劑,例如可以列舉出醇酸類、矽酮類、氟類、不飽和聚酯類、聚烯烴類、蠟類的剝離劑。 It is preferable that the peeling surface of the peeling sheet (particularly the surface in contact with the adhesive layer 11) is subjected to a peeling treatment. Examples of the release agent used for the release treatment include a release agent of an alkyd, an anthrone, a fluorine, an unsaturated polyester, a polyolefin, and a wax.
關於剝離片12、12a、12b的厚度,沒有特別的限制,通常為20μm~150μm左右。 The thickness of the release sheets 12, 12a, and 12b is not particularly limited, but is usually about 20 μm to 150 μm.
在製造上述黏接片1A中,在剝離片12的剝離面上,將含有上述黏接性組合物的溶液(塗布溶液)進行塗布、加熱處理,在形成塗膜後,在其塗膜上將基材13進行積層。另外,上述塗膜,在不需要熟成期間的情況時,直接成為黏接劑層11,在需要熟成期間的情況時,經過熟成期間後成為黏接劑層11。關於加熱處理以及熟成條件如上所述。 In the production of the above-mentioned adhesive sheet 1A, the solution (coating solution) containing the above-mentioned adhesive composition is applied and heat-treated on the release surface of the release sheet 12, and after the coating film is formed, the coating film is formed on the coating film. The substrate 13 is laminated. Further, when the coating film is not required to be matured, the adhesive layer 11 is directly formed, and when it is required to be matured, the adhesive layer 11 is formed after the ripening period. The heat treatment and the ripening conditions are as described above.
另外,在製造上述黏接片1B中,在一個剝離片12a(或者12b)的剝離面上,將含有上述黏接性組合物的塗布溶液進行塗布、加熱處理,在形成塗膜後,在其塗膜上,將另一個剝離片12b(或者12a)的剝離面聚合。上述塗膜,在不需要熟成期間的情況時,直接成為黏接劑層11,在需要熟成期間的情況時,經過熟成期間後成為黏接劑層11。 Further, in the production of the above-mentioned adhesive sheet 1B, the coating solution containing the above-mentioned adhesive composition is applied and heat-treated on the peeling surface of one of the release sheets 12a (or 12b), and after the coating film is formed, On the coating film, the peeling surface of the other release sheet 12b (or 12a) was polymerized. When the coating film is not required to be matured, it directly becomes the adhesive layer 11, and when it is required to be matured, it becomes the adhesive layer 11 after the ripening period.
作為塗布上述塗布溶液的方法,例如可以利用棒塗布法、刮刀塗布法、輥塗布法、板塗布法、模具塗布法、凹板塗布法等。 As a method of applying the above coating solution, for example, a bar coating method, a knife coating method, a roll coating method, a plate coating method, a die coating method, a gravure coating method, or the like can be used.
黏接片1A、1B中的黏接劑層11,霧度值(基於JIS K7136:2000測定的值)優選為1.0%以下,特別優選為0.9%以下,進一步優選為0.8%以下。霧度值如果為1.0%以下,則透明性極高,適宜用作光學用途。 The adhesive layer 11 in the adhesive sheets 1A and 1B has a haze value (value measured based on JIS K7136:2000) of preferably 1.0% or less, particularly preferably 0.9% or less, and further preferably 0.8% or less. When the haze value is 1.0% or less, the transparency is extremely high, and it is suitable for optical use.
在此,例如,在製造由液晶組件和偏光板所構成的液晶顯示裝置中,作為黏接片1A的基材13,使用偏光板,將該黏接片1A的剝離片12剝離,將露出的黏接劑層11和液晶組件進行貼合即可。 Here, for example, in the liquid crystal display device including the liquid crystal module and the polarizing plate, a polarizing plate is used as the substrate 13 of the bonding sheet 1A, and the peeling sheet 12 of the bonding sheet 1A is peeled off to be exposed. The adhesive layer 11 and the liquid crystal module may be attached.
另外,例如,製造在液晶組件和偏光板之間配置 有相位差板的液晶顯示裝置中,作為一例,首先,將黏接片1B的一個剝離片12a(或者12b)剝離,將黏接片1B露出的黏接劑層11和相位差板進行貼合。然後,將作為基材13使用偏光板的黏接片1A的剝離片12剝離,將黏接片1A露出的黏接劑層11和上述相位差板進行貼合。另外,從上述黏接片B的黏接劑層11,將另一個剝離片12b(或者12a)剝離,將黏接片B露出的黏接劑層11和液晶組件進行貼合。 In addition, for example, manufacturing is configured between a liquid crystal module and a polarizing plate In the liquid crystal display device having the retardation plate, as an example, first, one of the release sheets 12a (or 12b) of the adhesive sheet 1B is peeled off, and the adhesive layer 11 and the phase difference plate exposed by the adhesive sheet 1B are bonded together. . Then, the release sheet 12 of the adhesive sheet 1A using the polarizing plate as the base material 13 is peeled off, and the adhesive layer 11 exposed by the adhesive sheet 1A and the phase difference plate are bonded together. Further, the other release sheet 12b (or 12a) is peeled off from the adhesive layer 11 of the above-mentioned adhesive sheet B, and the adhesive layer 11 from which the adhesive sheet B is exposed is bonded to the liquid crystal module.
根據以上的黏接片1A、1B,黏接劑層11的耐久性優異,因此即使在高溫條件下或濕熱條件下,也可防止和抑制基材13與被黏物之間產生浮起、剝離、氣泡等。特別是將COP偏光板作為基材13的情況時,也能將由於COP偏光板的變形而可能產生的應力,在黏接劑層11上吸收、緩和,由此發揮優異的耐久性。另外,根據上述黏接片1A、1B,黏接劑層11耐變形性優異,因此即使在高溫條件下,也可將通過黏接劑層11貼合的薄偏光板和薄膜(例如,膜厚度為0.5mm左右)與玻璃板的積層體的變形抑制得較小。 According to the above-mentioned adhesive sheets 1A and 1B, since the adhesive layer 11 is excellent in durability, it is possible to prevent and suppress floating and peeling between the substrate 13 and the adherend even under high temperature conditions or under moist heat conditions. , bubbles, etc. In particular, when the COP polarizing plate is used as the base material 13, the stress which may be generated by the deformation of the COP polarizing plate can be absorbed and relaxed on the adhesive layer 11, thereby exhibiting excellent durability. Further, according to the above-mentioned adhesive sheets 1A and 1B, the adhesive layer 11 is excellent in deformation resistance, so that a thin polarizing plate and a film (for example, film thickness) which are bonded together by the adhesive layer 11 can be used even under high temperature conditions. The deformation of the laminate of the glass plate of about 0.5 mm is suppressed to be small.
本實施形態所述黏接片1A、1B,也優選將透明導電膜作為被黏物。黏接性組合物P中的(甲基)丙烯酸酯聚合物(A),作為單體單元,所包含的含羧基單體的量如上所述為少量,因此可以抑制由於酸成分對透明導電膜帶來的不良影響。具體而言,為可抑制透明導電膜被腐蝕,或透明導電膜的電阻值發生變化。 In the adhesive sheets 1A and 1B of the present embodiment, it is also preferable to use a transparent conductive film as an adherend. The (meth) acrylate polymer (A) in the adhesive composition P, as a monomer unit, contains a small amount of the carboxyl group-containing monomer as described above, and thus can suppress the transparent conductive film due to the acid component. The negative impact. Specifically, it is possible to suppress the corrosion of the transparent conductive film or the resistance value of the transparent conductive film.
作為上述透明導電膜,例如可以列舉出鉑、金、銀、銅等的金屬;氧化錫、氧化銦、氧化鎘、氧化鋅、二氧化 鋅等的氧化物;錫之氧化銦錫(ITO)、氧化鋅之氧化銦、氟之氧化銦、銻之氧化錫、氟之氧化錫、鋁之氧化鋅等的複合氧化物;硫化物、六硼化鑭、氮化鈦、碳化鈦等的非氧化化合物等所構成的透明導電膜。 Examples of the transparent conductive film include metals such as platinum, gold, silver, and copper; tin oxide, indium oxide, cadmium oxide, zinc oxide, and dioxide. Oxide such as zinc; tin oxide indium tin oxide (ITO), indium oxide of zinc oxide, indium oxide of fluorine, tin oxide of antimony, tin oxide of fluorine, zinc oxide of aluminum, etc.; sulfide, six A transparent conductive film made of a non-oxidizing compound such as lanthanum boride, titanium nitride or titanium carbide.
對上述透明導電膜的電阻值變化進行具體說明,使用本實施形態所述黏接片1A或黏接片1B,將黏接劑層11與透明導電膜貼合,對所得到的積層體,在65℃,95%RH的氣氛下,進行曝露500小時的濕熱促進試驗時,透明導電膜根據以下算式算出的電阻值增加率優選為15%以下,特別優選為10%以下。 Specifically, the change in the resistance value of the transparent conductive film will be specifically described. When the adhesive sheet 1A or the adhesive sheet 1B of the present embodiment is used, the adhesive layer 11 and the transparent conductive film are bonded together, and the obtained laminated body is When the wet heat promotion test for 500 hours of exposure is carried out in an atmosphere of 95° C. and 95% RH, the increase rate of the electric resistance value calculated by the following formula is preferably 15% or less, and particularly preferably 10% or less.
電阻值增加率(%)={(R-R0)/R0}×100(算式中,R0為濕熱促進試驗前的初始電阻值(Ω),R為濕熱促進試驗後的電阻值(Ω)。) Resistance increase rate (%) = {(RR 0 ) / R 0 } × 100 (In the formula, R 0 is the initial resistance value (Ω) before the damp heat promotion test, and R is the resistance value (Ω) after the damp heat promotion test .)
另外,關於透明導電膜電阻值增加率測定方法的詳細情況如後所述。 In addition, the details of the method for measuring the increase rate of the resistance value of the transparent conductive film will be described later.
作為基材13使用了偏光板的黏接片1A(以下有稱為「附有黏接劑層偏光板」的情況。),相對於無堿玻璃的黏接力,優選為0.1N/25mm~20N/25mm,特別優選為0.5N/25mm~10N/25mm,進一步優選為1N/25mm~5N/25mm。黏接力通過在上述範圍內,則在與玻璃板等的被黏物之間,可以防止浮起或剝離等。另外,這裏所說的黏接力,基本上是指通過基於JIS Z0237:2009的180°剝離法所測定的黏接力,但是將測定樣品裁成寬25mm、長100mm,使該測定樣品相對於被黏物,在0.5MPa、50℃,加壓20分貼附之後,以常壓23℃、50%RH 的條件下放置24小時之後,以剝離速度300mm/min進行測定所得到的黏接力。 The adhesive sheet 1A using a polarizing plate as the base material 13 (hereinafter referred to as "the adhesive layer polarizing plate is attached") is preferably 0.1 N/25 mm to 20 N with respect to the adhesive force of the flawless glass. /25 mm is particularly preferably 0.5 N/25 mm to 10 N/25 mm, and further preferably 1 N/25 mm to 5 N/25 mm. When the adhesive force is within the above range, it is possible to prevent floating, peeling, or the like from being adhered to the adherend such as a glass plate. In addition, the adhesive force referred to here basically means the adhesive force measured by the 180° peeling method based on JIS Z0237:2009, but the measurement sample is cut into a width of 25 mm and a length of 100 mm so that the measurement sample is viscous with respect to the adhesion. After being attached at 0.5 MPa, 50 ° C, and pressurized for 20 minutes, at normal pressure of 23 ° C, 50% RH After standing for 24 hours under the conditions, the adhesion obtained by the measurement was performed at a peeling speed of 300 mm/min.
以上說明的實施形態,是為了易於對本發明的理解而記述的,並不是對本發明進行限定而進行的記述。因此,上述實施形態中所公開的各要素,也包括屬於本發明的技術範圍的所有設計變更以及均等物。 The embodiments described above are described in order to facilitate understanding of the present invention, and are not intended to limit the present invention. Therefore, each of the elements disclosed in the above embodiments includes all design changes and equivalents belonging to the technical scope of the present invention.
例如,黏接片1A的剝離片12可以省略,黏接片1B中的剝離片12a、12b中的任意一方也可以省略。 For example, the release sheet 12 of the adhesive sheet 1A can be omitted, and any one of the release sheets 12a and 12b in the adhesive sheet 1B can be omitted.
【實施例】 [Examples]
以下,通過實施例等進一步對本發明進行具體說明,但是本發明的範圍並不受這些實施例等的限定。 The present invention will be specifically described by the following examples, but the scope of the present invention is not limited by the examples and the like.
〔實施例1〕 [Example 1]
1.(甲基)丙烯酸酯聚合物的調制 1. Modulation of (meth) acrylate polymer
將丙烯酸正丁基酯76.9質量份、丙烯酸甲基酯10質量份、丙烯酸2-苯基乙基10質量份、丙烯酸2-羥基乙基酯3質量份以及丙烯酸0.1質量份共聚合,調制(甲基)丙烯酸酯聚合物(A)。將該(甲基)丙烯酸酯聚合物(A)的分子量,用後述方法測定的結果,重均分子量為150萬。 76.9 parts by mass of n-butyl acrylate, 10 parts by mass of methyl acrylate, 10 parts by mass of 2-phenylethyl acrylate, 3 parts by mass of 2-hydroxyethyl acrylate, and 0.1 parts by mass of acrylic acid are copolymerized (A) Acrylate polymer (A). The molecular weight of the (meth) acrylate polymer (A) was measured by the method described later, and the weight average molecular weight was 1.5 million.
2.黏接性組合物的調制 2. Modulation of adhesive composition
在上述步驟(1)中獲得的(甲基)丙烯酸酯聚合物(A)100質量份(固體成分換算值;以下同);作為異氰酸酯類架橋劑(B),將三羥甲基丙烷改性甲次苯基二異氰酸酯(日本聚氨酯工業公司製,商品名「CORONATE L」)0.2質量份;作為具有巰基的矽烷偶聯劑(C),將3-巰基丙基三甲氧基矽烷與甲基三乙氧 基矽烷的共縮合物(信越化學工業公司製,商品名「X-411-1810」,巰基當量:450g/摩爾)0.3質量份進行混合,充分地攪拌,通過用乙酸乙酯進行稀釋,獲得黏接性組合物的塗布溶液。 100 parts by mass of the (meth) acrylate polymer (A) obtained in the above step (1) (converted solid content; the same applies hereinafter); modified trimethylolpropane as an isocyanate bridging agent (B) 0.2 parts by mass of methyl phenyl diisocyanate (manufactured by Nippon Polyurethane Industry Co., Ltd., trade name "CORONATE L"); as a decane coupling agent (C) having a mercapto group, 3-mercaptopropyltrimethoxydecane and methyl three Ethoxygen The co-condensate of decane (manufactured by Shin-Etsu Chemical Co., Ltd., trade name "X-411-1810", thiol equivalent: 450 g/mol) 0.3 parts by mass, mixed well, and diluted with ethyl acetate to obtain a viscosity A coating solution of the conjugate composition.
在此,該黏接性組合物的搭配示於表1。另外,表1所記載的縮寫符號等的詳細情況如下所述。 Here, the matching of the adhesive composition is shown in Table 1. The details of the abbreviations and the like described in Table 1 are as follows.
[(甲基)丙烯酸酯聚合物] [(Meth)acrylate polymer]
BA:丙烯酸正丁基酯 BA: n-butyl acrylate
MA:丙烯酸甲基酯 MA: methyl acrylate
PhEA:丙烯酸2-苯基乙基 PhEA: 2-phenylethyl acrylate
HEA:丙烯酸2-羥基乙基酯 HEA: 2-hydroxyethyl acrylate
AA:丙烯酸 AA: Acrylic
〔矽烷偶聯劑〕 [decane coupling agent]
C1:3-巰基丙基三甲氧基矽烷和甲基三乙氧基矽烷的共縮合物(信越化學工業公司製,商品名「X-411-1810」) C1: a cocondensate of 3-mercaptopropyltrimethoxydecane and methyltriethoxydecane (manufactured by Shin-Etsu Chemical Co., Ltd., trade name "X-411-1810")
C2:3-環氧丙氧基三甲氧基矽烷(信越化學工業公司製,商品名「KBM-403」) C2: 3-glycidoxytrimethoxydecane (manufactured by Shin-Etsu Chemical Co., Ltd., trade name "KBM-403")
3.附有黏接劑層偏光板的製造 3. Manufacture of adhesive layer with polarizer
將所得到的黏接性組合物的塗布溶液,在將聚對苯二甲酸乙二醇酯薄膜的一個面,用矽酮類剝離劑進行了剝離處理的剝離片(琳得科株式公司製,SP-PET3811,厚度:38μm)的剝離處理面上,用刮刀塗布器進行塗布,使乾燥後的厚度為25μm後,用90℃進行1分鐘加熱處理而形成黏接性組合物的塗膜。 The coating solution of the obtained adhesive composition was peeled off by the one side of the polyethylene terephthalate film by the ketone type release agent (The Linde Co., Ltd. product, The peel-treated surface of SP-PET3811, thickness: 38 μm was applied by a knife coater to a thickness of 25 μm after drying, and then heat-treated at 90 ° C for 1 minute to form a coating film of the adhesive composition.
接著,用三醋酸纖維素薄膜,保護聚乙烯醇薄膜所構成的偏光子的一個面,用環烯烴聚合物薄膜保護另一個面 所得的厚度為100μm的COP偏光板,貼合於上述塗膜,使上述塗膜的露出面與環烯烴聚合物薄膜的表面相接觸,之後在23℃、50%RH下放置7天進行熟成,由此得到附有黏接劑層的偏光板。 Next, using a cellulose triacetate film to protect one side of the polarizer composed of the polyvinyl alcohol film, and protecting the other side with the cycloolefin polymer film The obtained COP polarizing plate having a thickness of 100 μm was bonded to the coating film, and the exposed surface of the coating film was brought into contact with the surface of the cycloolefin polymer film, and then allowed to stand at 23° C. and 50% RH for 7 days for aging. Thus, a polarizing plate with an adhesive layer was obtained.
〔實施例2~14,比較例1~6〕 [Examples 2 to 14, Comparative Examples 1 to 6]
除將構成(甲基)丙烯酸酯聚合物(A)的各單體的種類以及比例、(甲基)丙烯酸酯聚合物(A)的重均分子量、異氰酸酯類架橋劑(B)的搭配量、以及矽烷偶聯劑(C)的種類及搭配量,按照表1所示進行變更外,與實施例1同樣地進行操作,製造附有黏接劑層的偏光板。另外,實施例5中,在黏接性組合物的調制時,作為帶電防止劑,搭配了1.8質量份雙(三氟甲磺醯氯醯亞胺)鋰和四乙二醇二甲醚的等摩爾混合品(三光化學工業公司製,商品名「SANKONOL TGR「)。 The type and ratio of each monomer constituting the (meth) acrylate polymer (A), the weight average molecular weight of the (meth) acrylate polymer (A), and the amount of the isocyanate bridging agent (B), The type and amount of the decane coupling agent (C) were changed in the same manner as in Example 1 except that the type and amount of the decane coupling agent (C) were changed, and a polarizing plate with an adhesive layer was produced. Further, in Example 5, when the adhesive composition was prepared, 1.8 parts by mass of lithium bis(trifluoromethanesulfonium chloride) and tetraethylene glycol dimethyl ether were blended as a charge preventing agent. Moore mixed product (manufactured by Sanko Chemical Industry Co., Ltd., trade name "SANKONOL TGR").
在此,上述的重均分子量(MW),為使用凝膠滲透色譜法(GPC)在以下的條件下測定(GPC測定)的聚苯乙烯換算的重均分子量。 Here, the above-mentioned weight average molecular weight (MW) is a polystyrene-equivalent weight average molecular weight measured by gel permeation chromatography (GPC) under the following conditions (GPC measurement).
<測定條件> <Measurement conditions>
‧GPC測定裝置:TOSOH公司製,HLC-8020 ‧GPC measuring device: manufactured by TOSOH, HLC-8020
‧GPC柱(以下的順序通過):TOSOH公司製 ‧GPC column (the following sequence is passed): TOSOH company
TSK guard column HXL-H TSK guard column HXL-H
TSK gel GMHXL(×2) TSK gel GMHXL (×2)
TSK gel G2000HXL TSK gel G2000HXL
‧測定熔劑:四氫呋喃 ‧ Determination of flux: tetrahydrofuran
‧測定溫度:40℃ ‧Measurement temperature: 40 ° C
〔試驗例1〕(凝膠分率的測定) [Test Example 1] (Measurement of gel fraction)
在實施例或比較例中,代替製作附有黏接劑層的偏光板所使用的偏光板,使用將聚對苯二甲酸乙二醇酯薄膜的一個面,用矽酮類剝離劑進行了剝離處理的剝離片(琳得科株式公司製,SP-PET3801,厚度:38μm),進行黏接片的製作。具體而言,在用實施例或比較例的製造過程所得到的剝離片/黏接性組合物的塗膜所構成的構成體的露出的塗膜上,以剝離處理面側相接的方式,將上述剝離片進行積層,在23℃、50%RH的條件下進行7天熟成。由此,來製作由剝離片(SP-PET3801)/黏接劑層(厚度:25μm)/剝離片(SP-PET3811)的構成所形成的黏接片。 In the examples or the comparative examples, instead of using the polarizing plate used for the polarizing plate with the adhesive layer, one side of the polyethylene terephthalate film was peeled off with an anthrone-based release agent. The treated release sheet (SP-PET3801, thickness: 38 μm, manufactured by Linde Co., Ltd.) was used to produce a bonded sheet. Specifically, the exposed coating film of the constituent film composed of the coating film of the release sheet/adhesive composition obtained in the production process of the example or the comparative example is placed so as to be in contact with each other on the side of the release-treated surface. The release sheet was laminated, and aging was carried out for 7 days under conditions of 23 ° C and 50% RH. Thus, an adhesive sheet formed of a release sheet (SP-PET3801)/adhesive layer (thickness: 25 μm)/release sheet (SP-PET3811) was prepared.
將得到的黏接片製成80mm×80mm尺寸的樣品,將其黏接劑層用聚酯制網(網尺寸200)包裹,僅將黏接劑的質量用精密天秤進行稱量。將此時的質量作為M1。 The obtained adhesive sheet was made into a sample of 80 mm × 80 mm size, and the adhesive layer was wrapped with a polyester mesh (mesh size 200), and only the quality of the adhesive was weighed with a precision balance. The mass at this time is taken as M1.
接著,將上述聚酯制網包裹的黏接劑,在室溫(23℃)下,在乙酸乙酯中進行24小時浸漬。之後將黏接劑取出,在溫度23℃、相對濕度50%的環境下,進行24小時風乾,進一步在80℃的烘箱中進行12小時乾燥。僅將乾燥後的黏接劑的質量用精密天秤進行稱量。將此時的質量作為M2。凝膠分率(%)用(M2/M1)×100來表示。將結果示於表2。 Next, the above-mentioned polyester net-wrapped adhesive was immersed in ethyl acetate at room temperature (23 ° C) for 24 hours. Thereafter, the adhesive was taken out, air-dried for 24 hours in an environment of a temperature of 23 ° C and a relative humidity of 50%, and further dried in an oven at 80 ° C for 12 hours. Only the quality of the dried adhesive is weighed with a precision balance. The mass at this time is taken as M2. The gel fraction (%) is represented by (M2/M1) × 100. The results are shown in Table 2.
〔試驗例2〕(霧度值的測定) [Test Example 2] (Measurement of haze value)
作為測定樣品,准備與測定凝膠分率所用的黏接片同樣的黏接片。對於該黏接片的黏接劑層(厚度:25μm),使用霧度測量計(日本電色工業公司製,NDH2000),基於JIS K7136:2000 ,對霧度值(%)進行測定。將結果示於表2。 As the measurement sample, the same adhesive sheet as that used for the measurement of the gel fraction was prepared. For the adhesive layer (thickness: 25 μm) of the adhesive sheet, a haze meter (NDH2000, manufactured by Nippon Denshoku Industries Co., Ltd.) was used, based on JIS K7136:2000. The haze value (%) was measured. The results are shown in Table 2.
〔試驗例3〕(電阻值增加率的測定) [Test Example 3] (Measurement of resistance increase rate)
將在實施例或比較例中得到的附有黏接劑層的偏光板,按照以下的試驗方法,測定ITO膜的電力電阻值,計算電阻值增加率。 The polarizing plate with the adhesive layer obtained in the examples or the comparative examples was measured for the electric resistance value of the ITO film according to the following test method, and the increase rate of the electric resistance value was calculated.
如圖3所示,為電阻值測定樣品S的剖面圖。通過濺射,准備在一個面21a上形成有ITO膜22的聚對苯二甲酸乙二醇酯(PET)薄膜21,用黏接膠帶24(琳得科株式公司製,商品名「TACKLINER TL-70「),將沒有形成PET薄膜21的ITO膜22的面21b與玻璃板23的一個面23a接合。 As shown in FIG. 3, a cross-sectional view of the sample S is measured for the resistance value. A polyethylene terephthalate (PET) film 21 having an ITO film 22 formed on one surface 21a was prepared by sputtering, and an adhesive tape 24 (manufactured by Linda Co., Ltd., trade name "TACKLINER TL-" was prepared. 70"), the surface 21b of the ITO film 22 on which the PET film 21 is not formed is bonded to the one surface 23a of the glass plate 23.
然後,在與ITO膜22的PET薄膜21相接的面的反面(以下稱為「一個面」。)22a上,使含有銀的導電性樹脂材料(藤倉化成公司製,商品名「FA-301CA」,DOTITE觸控面板回路型)呈20mm×5mm的長方形電極形狀,進行塗布後,在溫度80℃下加熱20分鐘乾燥,形成兩個成為電阻值測定點的電極25。此時,調整兩個電極25,25的位置,使其之間的距離略大於20mm。 Then, a conductive resin material containing silver (manufactured by Fujikura Kasei Co., Ltd., trade name "FA-301CA" is formed on the reverse side (hereinafter referred to as "one surface") 22a of the surface of the ITO film 22 which is in contact with the PET film 21. The DOTITE touch panel circuit type has a rectangular electrode shape of 20 mm × 5 mm, and after coating, it is dried by heating at a temperature of 80 ° C for 20 minutes to form two electrodes 25 which are measurement points of resistance values. At this time, the positions of the two electrodes 25, 25 are adjusted so that the distance between them is slightly larger than 20 mm.
另一方面,將實施例或比較例中所得到的附有黏接劑層的偏光板1A’,裁成20mm×250mm尺寸,將剝離片剝離(此時,附有黏接劑層的偏光板1A’,為由偏光板13’和黏接劑層11所構成的積層體)。之後,附有黏接劑的偏光板1A’的黏接劑層11緊貼兩個電極25,25的邊(剛好沒有與之接觸到),在ITO膜22的一個面22a上,貼附附有黏接劑層的偏光板1A’,製作如圖3所示的電阻值測定用樣品S。 On the other hand, the polarizing plate 1A' with the adhesive layer obtained in the example or the comparative example was cut into a size of 20 mm × 250 mm, and the release sheet was peeled off (at this time, the polarizing plate with the adhesive layer was attached) 1A' is a laminate composed of the polarizing plate 13' and the adhesive layer 11. Thereafter, the adhesive layer 11 of the polarizing plate 1A' to which the adhesive is attached is adhered to the sides of the two electrodes 25, 25 (just not in contact therewith), and is attached to one surface 22a of the ITO film 22 A polarizing plate 1A' having an adhesive layer was used to prepare a sample S for measuring a resistance value as shown in FIG.
之後,如圖4所示,利用數字測高儀(HIOKI.E公司製,商品名「3802-50」)30,測定電極25,25之間的初始電阻值R0(Ω)。並且將電阻值測定用樣品S,在60℃、90%RH的環境下放置500小時後,測定濕熱促進後的電阻值R(Ω)。根據所得到的初始電阻值R0以及濕熱促進後的電阻值R,按以下公式算出電阻值測定用樣品S的電阻值增加率。將結果示於表2。 Then, as shown in FIG. 4, the initial resistance value R 0 (Ω) between the electrodes 25 and 25 is measured by a digital altimeter (trade name "3802-50" manufactured by HIOKI.E Co., Ltd.) 30. Further, the sample for measuring the resistance value S was allowed to stand in an environment of 60° C. and 90% RH for 500 hours, and then the resistance value R (Ω) after the moist heat promotion was measured. Based on the obtained initial resistance value R 0 and the resistance value R after the moist heat promotion, the resistance value increase rate of the resistance value measurement sample S was calculated by the following formula. The results are shown in Table 2.
電阻值增加率(%)={(R-R0)/R0}×100 Resistance increase rate (%) = {(RR 0 ) / R 0 } × 100
〔試驗例4〕(黏接力的測定) [Test Example 4] (Measurement of adhesion)
將在實施例或比較例中所得到的附有黏接劑層的偏光板裁斷,製作寬25mm、長100mm的樣品。從該樣品上將剝離片剝離,通過露出的黏接劑層,在無堿玻璃(康寧公司製,鷹XG)上進行該樣品的貼附之後,用栗原製作所公司製的高壓鍋,在0.5MPa、50℃,加壓20分鐘。其後,在常壓23℃、50%RH的條件下,放置24小時後,使用拉伸試驗機(ORIENTEC公司製,TENSILON),基於JIS Z0237:2009,以剝離速度300mm/min、剝離角度180°的條件,測定黏接力(貼附1天後的黏接力;N/25mm)。將結果示於表2。 The polarizing plate with the adhesive layer obtained in the examples or the comparative examples was cut to prepare a sample having a width of 25 mm and a length of 100 mm. The peeling sheet was peeled off from the sample, and the sample was attached to the glass without the enamel glass (manufactured by Corning Co., Ltd., Eagle XG), and the pressure cooker manufactured by Kurihara Co., Ltd. was used at 0.5 MPa. Pressurize at 50 ° C for 20 minutes. Thereafter, the mixture was allowed to stand under normal pressure of 23 ° C and 50% RH for 24 hours, and then a tensile tester (TENSILON, manufactured by ORIENTEC Co., Ltd.) was used, and a peeling speed of 300 mm/min and a peeling angle of 180 were used based on JIS Z0237:2009. The condition of ° was measured for the adhesive force (adhesion force after 1 day of attachment; N/25 mm). The results are shown in Table 2.
〔試驗例5〕(耐久性評價) [Test Example 5] (Durability evaluation)
將在實施例或比較例中所得到的附有黏接劑層的偏光板裁斷,製作200mm×150mm尺寸的樣品。從該樣品上將剝離片剝離,通過露出的黏接劑層,在無堿玻璃(康寧公司製,鷹XG)上進行貼附之後,用栗原製作所公司製的高壓鍋,在0.5MPa、50℃,加壓20分鐘。 The polarizing plate with the adhesive layer obtained in the examples or the comparative examples was cut to prepare a sample having a size of 200 mm × 150 mm. The release sheet was peeled off from the sample, and the exposed adhesive layer was attached to an aluminum-free glass (manufactured by Corning Co., Ltd., Eagle XG), and then a pressure cooker manufactured by Kurihara Co., Ltd. was used at 0.5 MPa and 50 ° C. Pressurize for 20 minutes.
之後,投入到以下耐久條件的環境中,250小時後,利用10倍放大鏡,對浮起或剝離的有無進行確認。評價基準如下。將結果示於表2。 After that, the product was placed in the following environment of durable conditions, and after 250 hours, the presence or absence of floating or peeling was confirmed by a magnifying glass of 10 times. The evaluation criteria are as follows. The results are shown in Table 2.
◎:沒有確認到浮起或者剝離。 ◎: No lifting or peeling was confirmed.
○:確認到0.5mm以下大小的浮起或剝離。 ○: Float or peeling of a size of 0.5 mm or less was confirmed.
△:確認到0.5mm以上1.0mm以下大小的浮起或剝離。 △: Float or peeling of a size of 0.5 mm or more and 1.0 mm or less was confirmed.
×:確認到1.0mm以上大小的浮起或剝離。 ×: Float or peeling of a size of 1.0 mm or more was confirmed.
<耐久條件> <endurance condition>
.85℃ dry . 85°C dry
.60℃,相對濕度90%RH . 60 ° C, relative humidity 90% RH
〔試驗例6〕(面板的耐變形性評價) [Test Example 6] (Evaluation of deformation resistance of panel)
將在實施例以及比較例中所得到的附有黏接劑層的偏光板裁斷,使縱向為200mm、橫向為150mm。從該附有黏接劑層的偏光板上將剝離片剝離,將露出的黏接劑層貼合於縱向250mm、橫向175mm、厚度0.5mm的無堿玻璃(康寧公司製,商品名「鷹-XG」)的中央部分,將其作為樣品。將該樣品在85℃、乾燥的氣氛下放置250小時。之後,在25℃、50%RH的環境下取出,將偏光板側朝上,放置於水準臺上,測定樣品各角(4個)相對於水準台的變形量(角與水準台的距離),合計各角的變形量。根據其結果進行如下評價。將結果示於表2。 The polarizing plate with the adhesive layer obtained in the examples and the comparative examples was cut to have a longitudinal direction of 200 mm and a lateral direction of 150 mm. The release sheet was peeled off from the polarizing plate with the adhesive layer, and the exposed adhesive layer was bonded to a flawless glass having a length of 250 mm, a lateral direction of 175 mm, and a thickness of 0.5 mm (manufactured by Corning Co., Ltd., trade name "Eagle- The central part of XG") is used as a sample. The sample was allowed to stand at 85 ° C in a dry atmosphere for 250 hours. Then, take it out in an environment of 25 ° C and 50% RH, place the polarizing plate side up, place it on the leveling table, and measure the amount of deformation (angle of the angle and the leveling table) of each corner (4) of the sample relative to the leveling table. , the total amount of deformation of each corner. The following evaluation was performed based on the results. The results are shown in Table 2.
◎:變形量的合計為15mm以下 ◎: The total amount of deformation is 15mm or less
○:變形量的合計為15mm以上、20mm以下 ○: The total amount of deformation is 15 mm or more and 20 mm or less.
×:變形量的合計為20mm以上 ×: The total amount of deformation is 20 mm or more
〔試驗例7〕(耐漏光性評價) [Test Example 7] (Evaluation of light leakage resistance)
將在實施例或比較例中所得到的附有黏接劑層的偏光板,用裁斷裝置(荻野製作所公司製,SUPER CUTTER,PN1-600),調整至200mm×150mm大小。將剝離片剝離,通過露出的黏接劑層,在無堿玻璃(康寧公司製,鷹XG)上進行貼附之後,用栗原製作所公司製的高壓鍋,在0.5MPa、50℃,加壓20分鐘。另外,上述貼合是在無堿玻璃內外,將附有黏接劑層的偏光板,在偏光軸成為交叉尼克爾狀態(偏光軸:∠45°,∠135°)的條件下所實施。以該狀態在80℃ dry環境下放置250小時後,在23℃、50%RH的環境下放置2小時,將其作為樣品,按照如下所述的方法對漏光性進行評價。將結果示於表2。 The polarizing plate with the adhesive layer obtained in the example or the comparative example was adjusted to a size of 200 mm × 150 mm by a cutting device (SUPER CUTTER, PN1-600, manufactured by Takino Seisakusho Co., Ltd.). The peeling sheet was peeled off, and the exposed adhesive layer was attached to an aluminum-free glass (manufactured by Corning Co., Ltd., Eagle XG), and then pressed at a pressure of 0.5 MPa and 50 ° C for 20 minutes at 0.5 MPa and 50 ° C. . In addition, the above-mentioned bonding is performed on the inside and outside of the glassless glass, and the polarizing plate with the adhesive layer is applied under the condition that the polarization axis is in the cross-Nikkor state (polarization axis: ∠45°, ∠135°). After leaving it in this state for 80 hours in a dry environment of 80 ° C, it was allowed to stand in an environment of 23 ° C and 50% RH for 2 hours, and this was used as a sample, and the light leakage property was evaluated by the following method. The results are shown in Table 2.
<評價方法> <Evaluation method>
將上述樣品設置於FLAT ILLUMINATOR(DENTSU SANGYO公司製,HF-SL-A312LC,照度:26,000Lux,輝度:10,000cd)上,用二維色彩輝度計(柯尼卡美能達公司製,CA-2000)攝影,通過解析軟件(柯尼卡美能達公司製,CA-S20w)對輝度分布畫像進行變換。將所得到的樣品的輝度分布畫像,根據圖5以及以下所示的評價基準進行評價。 The above sample was placed on a FLAT ILLUMINATOR (manufactured by DENTSU SANGYO Co., Ltd., HF-SL-A312LC, illuminance: 26,000 Lux, luminance: 10,000 cd), and a two-dimensional color luminance meter (manufactured by Konica Minolta, CA-2000) was used. For the photography, the luminance distribution image was converted by an analysis software (CA-S20w, manufactured by Konica Minolta Co., Ltd.). The luminance distribution image of the obtained sample was evaluated based on the evaluation criteria shown in Fig. 5 and below.
◎:輝度分布均勻 ◎: uniform brightness distribution
○:四個角的輝度分布略有變形 ○: The brightness distribution of the four corners is slightly deformed
×:四個角的輝度分布有大的變形 ×: The brightness distribution of the four corners has a large deformation
〔試驗例8〕(黏接劑層的表面電阻值測定) [Test Example 8] (Measurement of surface resistance value of the adhesive layer)
在實施例5中所得到的附有黏接劑層的偏光板,裁斷成50mm×50mm大小,將所得到的樣品在溫度23℃、濕度50%RH下放置24小時。之後,將剝離片剝離,對露出的黏接劑層表面,用電阻 率儀(三菱化學ANALYTECH公司製,HIRESTAUP MCP-HT450型),基於JIS K6911,測定表面電阻值(Ω/Sq)。將結果示於表2。 The polarizing plate with the adhesive layer obtained in Example 5 was cut into a size of 50 mm × 50 mm, and the obtained sample was allowed to stand at a temperature of 23 ° C and a humidity of 50% RH for 24 hours. After that, the release sheet is peeled off, and the surface of the exposed adhesive layer is made of a resistor. The surface resistance value (Ω/Sq) was measured based on JIS K6911 by a rate meter (manufactured by Mitsubishi Chemical Corporation, HIRESTAUP MCP-HT450). The results are shown in Table 2.
另外,表面電阻值優選為3.0×1011Ω/Sq以下,特別優選為1.0×1011Ω/Sq以下,進一步優選為8.0×1010Ω/Sq以下。表面電阻值在上述值以下,則可發揮良好的帶電防止性。 Further, the surface resistance value is preferably 3.0 × 10 11 Ω / Sq or less, particularly preferably 1.0 × 10 11 Ω / Sq or less, and more preferably 8.0 × 10 10 Ω / Sq or less. When the surface resistance value is at most the above value, good charge prevention property can be exhibited.
【表2】
由表2可知,在實施例中所得到的黏接劑層的黏接劑,耐久性、耐變形性以及耐漏光性優異,同時,被黏物透明導電膜的電阻值不易被改變。 As is clear from Table 2, the adhesive of the adhesive layer obtained in the examples was excellent in durability, deformation resistance, and light leakage resistance, and the resistance value of the adherend transparent conductive film was not easily changed.
本發明的黏接劑以及黏接片,適宜於透明導電膜,特別是由氧化銦錫(ITO)所構成的透明導電膜與光學構件,特別是與偏光板的黏接。 The adhesive and the adhesive sheet of the present invention are suitable for a transparent conductive film, in particular, a transparent conductive film made of indium tin oxide (ITO) and an optical member, particularly a polarizing plate.
1A‧‧‧黏接片 1A‧‧‧bonding strip
11‧‧‧黏接劑層 11‧‧‧Adhesive layer
12‧‧‧剝離片 12‧‧‧ peeling film
13‧‧‧基材 13‧‧‧Substrate
Claims (12)