SU994579A2 - Steel - Google Patents

Steel Download PDF

Info

Publication number
SU994579A2
SU994579A2 SU802996968A SU2996968A SU994579A2 SU 994579 A2 SU994579 A2 SU 994579A2 SU 802996968 A SU802996968 A SU 802996968A SU 2996968 A SU2996968 A SU 2996968A SU 994579 A2 SU994579 A2 SU 994579A2
Authority
SU
USSR - Soviet Union
Prior art keywords
steel
fatigue
strength
iron
calcium
Prior art date
Application number
SU802996968A
Other languages
Russian (ru)
Inventor
Владимир Михайлович Семенов
Валентин Иванович Ефимов
Валерий Иванович Сарамутин
Юрий Тимофеевич Добрица
Сергей Семенович Дмитриченко
Михаил Александрович Шаров
Александр Михайлович Поживанов
Аркадий Иванович Третьяков
Петр Сергеевич Климашин
Георгий Петрович Трухман
Юрий Федорович Вяткин
Юрий Викторович Липухин
Виктор Яковлевич Тишков
Валентина Константиновна Рябинкова
Анатолий Алексеевич Чаплыгин
Наталья Алексеевна Еремина
Виталий Михайлович Соколов
Original Assignee
Предприятие П/Я А-1697
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Предприятие П/Я А-1697 filed Critical Предприятие П/Я А-1697
Priority to SU802996968A priority Critical patent/SU994579A2/en
Application granted granted Critical
Publication of SU994579A2 publication Critical patent/SU994579A2/en

Description

(54) СТАЛЬ(54) STEEL

Изобретение относитс  к металл ги  металлов, а именно к стал м, обладающим клсокой прочностью, пл тичностью, усталостной и коррозио усталостной прочностью и ударной костью при пониженных температура и испольэуекых дл  несущих констр ций тракторюв, автомобилей, сельс хоз йственных машин, подвижного с тава железнодорожного транспорта ,и других конструкций в машиностроен По основногй авт.св. 945224 известна сталь l содержаща ,ве Углерод0,04-0,16 Марганец0,9-2,5 Кремний-0,1-0,8 Ванадий0,01-0,3 Алюминий0,01-0,1 Титан0,01-0,3 Бор0,0005-0,002 Компонент из группы, .содержгице 0,01-0,1 Цирконий 0,001-0,01 Кальций Редкоземельные 0,01-0,05 металлы 0,001-0,01 Остальное Железо Однако указанна  цель обладает высокой усталостной прочностью, ч определ ет недостаточную долговеч ть конструкции машин, работающих слови х циклических нагрузок, при ких температурах окружающей среды. Цель изобретени  - повышение устатной прочности при сохранении высопоказателей прочности, пластичтн и в зкости. Дл  достижени  указанной цепи ль, содержаща  углерод, марганец, мний, ванадий, , титан, , компонент из группы, содержащей: коний, кальций, редкоземельные аллы, селен и железо, дополннтельсодержит медь при следующем соотении компонентов, вес.%: 0,04-0,16 Углерод 0,9-2,5 Марганец 0,1-0,8 Кремний 0,01-0,3 Еансщий 0,01-0,10 Ал  чиний 0,01-0,3 0,0005-0,002 0,20-0,80 Компонент из группы, содержащей: 0,01-0,1 1и1рконий 0,001-0,01 Кальций Редкоземельные 0,01-0,05 металлы 0,001-0,01 Остальное Железо Нсспекуег ае стали выплавл ютс  в 100 кг электропечи с основной футеровкой . Химическнй состав стали приведен в табл. 1. Слитки куютс  на сутунки и затем прокатывгиотс  .на прутки 12 и 16 мм дл  испытаний на раст жение, усталестную и корроэионно-усталостную прочность и ударную в зкость. Испытани  на раст жение провод т на машине УМЭ-ЮТМ по ГОСТ 1497-73 От каждой плавки испытывают не менее 5 образцов круглого сечени  с 0 5 мм и п тикратной длиной рабочей части. При этом определ ют предел прочноети ((Те),предел текучести (бу) и относительное уда1инение ((fg J, Ударную в зкость от каждой плавки определ ют не менее чем на б образцах типа 11 квадратного сечени  10х х10 ъ и длиной 55 №4. Испытани  про вод т на ма тниковом копре МК-ЗОА и ГОСТ 9454-78. Предел усталости определ ют на машине МУИ-6000 по ГОСТ 25502-79 на образцах круглого сечени  с диаметром рабочей части, равным 7,5 мм иThe invention relates to metal and metal metals, namely, steels having a high strength, flexibility, fatigue and corrosion, fatigue strength and impact bone at low temperatures and used for bearing structures of tractors, automobiles, agricultural vehicles, vehicles that are mobile. transport, and other structures in the machine-building. According to the main auth. 945224 known steel l containing, Carbon 0.04-0.16 Manganese 0.9-2.5 Silicon-0.1-0.8 Vanadium 0.01-0.3 Aluminum 0.01-0.1 Titanium 0.01-0, 3 Bor.0005-0.002 Component from group, containing 0.01-0.1 Zirconium 0.001-0.01 Calcium Rare-earth 0.01-0.05 metals 0.001-0.01 Iron Rest However, the indicated target has high fatigue strength, It determines the lack of durability of machines operating under the word cyclic loads at ambient temperatures. The purpose of the invention is to increase the static strength while maintaining high indicators of strength, plasticity and viscosity. To achieve the specified chain, containing carbon, manganese, aluminum, vanadium,, titanium, a component from the group containing: horse, calcium, rare earth alla, selenium and iron, in addition contains copper in the following ratio of components, wt.%: 0.04 -0.16 Carbon 0.9-2.5 Manganese 0.1-0.8 Silicon 0.01-0.3 Advanced 0.01-0.10 Al Chine 0.01-0.3 0,0005-0.002 0.20-0.80 Component from the group containing: 0.01-0.1 1i1rconium 0.001-0.01 Calcium Rare-earth 0.01-0.05 metals 0.001-0.01 Remaining Iron Specsteam steel is smelted into 100 kg of electric furnace with the main lining. The chemical composition of the steel is given in table. 1. Ingots are hammered and then rolled to 12 and 16 mm rods for tensile, fatigue and corrosion-fatigue strength and impact strength tests. The tensile tests were carried out on a UME-YUTM machine according to GOST 1497-73. At least 5 samples of circular cross section with 0-5 mm and five times the length of the working section were tested from each heat. In this case, the ultimate strength ((Te), the yield strength (bu) and the relative elimination ((fg J, Impact viscosity from each heat are determined on at least 6 samples of type 11 square section 10x x10 and length 55 No. 4). The tests were carried out on the MK-ZOA tilting machine and GOST 9454-78. The fatigue limit is determined on the MUI-6000 machine according to GOST 25502-79 on circular specimens with a working part diameter of 7.5 mm and

Таблица 1 п тикратным радиусом закруглени .Дл  построени  кривой усталости и определени  предела выносливости испытывают не менее 15 образцов. Условный предел коррозионной усталости определ ли , при непрерывном смачивании рабочей части образцов в водопроводной воде. Вазу испытаний дл  определени  пределов выносливости принимают равной 10-Ю циклов. Результаты испытаний механических, усталостных и усталостно-коррозионных свойств предлагаемой и известной стгшей приведены в табл. 2. Из табл. 2 видно, что предлагаема  сталь по характеристикам прочности, пластичности и в зкости не уступает известной стали, а по усталостной прочности существенно превышает известную сталь. Сталь имеет высокую .коррозионно-усталостную прочность, Введение предлагаемой стали на заводах тракторного и сельскохоз йственного машиностроени  увеличивает срок службы конструкций машин и обеспечивает экономический эффект 880 тыс.руб.Table 1 with a five-fold rounding radius. To build the fatigue curve and determine the fatigue limit, at least 15 samples are tested. The conventional limit of corrosion fatigue was determined by continuously wetting the working part of the samples in tap water. The test vase to determine the fatigue limit is taken as 10 th cycles. The test results of the mechanical, fatigue and fatigue-corrosive properties of the proposed and known starchy are given in table. 2. From table. 2 that the proposed steel in terms of strength, ductility and toughness is not inferior to the known steel, and in terms of fatigue strength significantly exceeds the known steel. Steel has a high corrosion and fatigue strength. The introduction of the proposed steel in the factories of the tractor and agricultural machine building increases the service life of the machine structures and provides an economic effect of 880 thousand rubles.

Claims (1)

Формула изобретения . Сталь по авт.св. № 945224, от личающаяся тем, что, с целью повышения усталостной прочности, она дополнительно содержит медь при следующем соотношении ком понентов, вес.%: Углерод Марганец Кремний Ванадий Алюминий ТитанClaim . Steel for auto No. 945224, characterized in that, in order to increase fatigue strength, it additionally contains copper in the following ratio of components, wt.%: Carbon Manganese Silicon Vanadium Aluminum Titanium 0,04-0,160.04-0.16 0,9-2,5 0,01-0,8 0,01-0,3 0,01-0,10 0,01-0,30.9-2.5 0.01-0.8 0.01-0.3 0.01-0.10 0.01-0.3 Бор 0,0005-0,002Boron 0.0005-0.002 Медь 0,20-0,80Copper 0.20-0.80 Компонент из группы, содержащей: Цирконий 0,01-0,1!A component from the group consisting of: Zirconium 0.01-0.1! Кальций 0,001-0,01Calcium 0.001-0.01 Редкоземельные металлы 0,01-0,05Rare earth metals 0.01-0.05 Селен 0,001-0,01Selenium 0.001-0.01 Железо ОстальноеIron Else
SU802996968A 1980-10-23 1980-10-23 Steel SU994579A2 (en)