SU1447539A1 - Method of top casting of steel - Google Patents

Method of top casting of steel Download PDF

Info

Publication number
SU1447539A1
SU1447539A1 SU874213403A SU4213403A SU1447539A1 SU 1447539 A1 SU1447539 A1 SU 1447539A1 SU 874213403 A SU874213403 A SU 874213403A SU 4213403 A SU4213403 A SU 4213403A SU 1447539 A1 SU1447539 A1 SU 1447539A1
Authority
SU
USSR - Soviet Union
Prior art keywords
steel
sheet
molds
casting
metal
Prior art date
Application number
SU874213403A
Other languages
Russian (ru)
Inventor
Валерий Иосифович Вареник
Борис Александрович Бурдонов
Эдуард Брониславович Ланевский
Виктор Михайлович Чабан
Виктор Семенович Щерба
Original Assignee
Карагандинский металлургический комбинат
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Карагандинский металлургический комбинат filed Critical Карагандинский металлургический комбинат
Priority to SU874213403A priority Critical patent/SU1447539A1/en
Application granted granted Critical
Publication of SU1447539A1 publication Critical patent/SU1447539A1/en

Abstract

Изобретение относитс  к черной металлургии, а именно к способам разливки стали сверху, и может быть использовано при разливке стали в крупные листовые изложницы. Цель изобретени  - повышение качества поверхности слитков, снижение расхода листовой стали и трудоемкости изготовлени  защитных приспособлент. Способ включает установку в первые две и последние две по ходу разливки из- |Ложни1да защитных приспособленш1, в качестве которых используют стальные листы площадью, равной площади широких граней, причем последние подвешивают на этих гран х и закрепл ют скобами за верхний торец и осуществл ют последующую заливку изложниц жрщким металлом. 1 з.п. ф-лы, 1 табл. бThe invention relates to ferrous metallurgy, in particular to methods for casting steel from above, and can be used for casting steel into large sheet ingot molds. The purpose of the invention is to improve the surface quality of the ingots, reducing the consumption of sheet steel and the complexity of the manufacture of protective devices. The method includes installation in the first two and last two in the course of casting from a protective locking device, in which steel sheets are used with an area equal to the area of wide faces, the latter being hung on these faces and fixed with brackets for the upper end and carry out the following pouring molds with hard metal. 1 hp f-ly, 1 tab. b

Description

N4 N4

СП СО (UDSP CO (UD

Изобретение относитс  к черной металлургии, а именно к способам раз- пивки стали сверху, и может быть использовано при разливке стали в крупные листовые изложницы.The invention relates to ferrous metallurgy, in particular to methods for smelting steel from above, and can be used for casting steel into large sheet ingot molds.

Цель изобретени  - повышение качества поверхности слитков, снижение расхода листовой стали и трудоемкости изготовлени  защитных приспособ- лений.The purpose of the invention is to improve the surface quality of the ingots, reducing the consumption of sheet steel and the labor intensity of manufacturing protective devices.

Способ осуществл ют следующим образом .The method is carried out as follows.

В листовых изложницах в двух первых и в двух последних по заливке из одного ковша устанавливают защитные приспособлени  в виде стальных лис- . тов площадью, равной площади широких граней, закрепленных на этих гран х скобами за верхний торец, а затем заполн ют изложницы жидким металлом.In sheet molds, in the first two and in the last two in the fill from one bucket, protective devices in the form of steel foxes are installed. This is an area equal to the area of wide faces fixed on these faces with staples at the upper end, and then the molds are filled with liquid metal.

Рекомендуетс  использовать стальные листы толщиной 0,5-1,5 мм.It is recommended to use steel sheets with a thickness of 0.5-1.5 mm.

Установка защитных приспособлений в две первые и две последние по ходу заливки из одного ковша изложницы обусловлена тем, что слитки, полученные именно в этих изложницах, как правило, поражены грубой пленой, котора  не всегда удал етс  при зачистке на МОЗе и приводит к повьш1ен- ной отбраковке металла по плене и порывам при прокатке жести. Защита от разбрызгивани  металла двух первых изложниц обусловлена также тем, что вследствие прожигани  стаканов шиберных затворов кислородом над этими изложницами (двухшиберна  разливка ) происходит заливка неорганизованной .струей металла из-за прохождени  его через еще не прогретые стаканы. Последние же две изложницы заливаютс  через одно шиберное устройство, в котором некачественна  стру  металла обусловлена недостаточно высокой температурой последних порций стали и образующимис  трещинами в стаканах На остальных слитках плены, особенно в верхней части, практически не наблюдаетс  .Installing protective devices in the first two and last two in the course of pouring from one bucket of the mold is due to the fact that the ingots obtained in these molds are usually struck by coarse captivity, which is not always removed when stripping the MOH. rejection of metal on the captivity and gusts when rolling tin. Protection against metal spraying of the first two molds is also due to the fact that, due to the burning of glasses of slide gates with oxygen over these molds (double-slit casting), unorganized metal is poured due to passing it through the still unheated glasses. The last two molds are poured through a single sliding device, in which the poor quality of the metal stream is caused by the insufficiently high temperature of the last portions of steel and the resulting cracks in the cups. The remaining ingots have no trace, especially in the upper part.

Пример. В цехе подготовки составов в две первые и в две посл;ед ние листовые изложницы дл  слитков массой 16,2 т (все 20 изложниц в составе ) на широкие грани устанавливали с помощью устройства дл  подвешива- ни  теплоизол ционных плит стальные листы толщиной 1 мм, шириной, равной ширине грани, и длиной 3000 мм. ОдинExample. In the workshop of preparation of the compositions in the first two and in the last two, single sheet molds for ingots weighing 16.2 tons (all 20 molds in the composition) were installed on wide faces using steel plate 1 mm thick device for suspending heat-insulating plates. width equal to the width of the face, and a length of 3000 mm. One

5 0 50

5 five

5 five

00

5five

00

5five

00

конец листа опускали до упора в поддон , а другой загибали за верхний торец изложниц и креш-ши скобами дл  креплени  теплоизол ционных плит. Раз- лйвку стали марки 08 КП осуществл ли из 320 т ковша через два шиберных затвора.The end of the sheet was lowered all the way into the pallet, and the other was folded over the upper end of the molds and the crash staples for fixing the heat insulating plates. The 08 KP steel grade was divided from a 320 t bucket through two slide gates.

Открьгаание шиберов над первыми двум  изложницами производили с помощью кислорода при высоко подн том ковше, что привело к заливке первых двух изложниц широкой струей. Последние две изложницы заливали через один шибер некачественной струей с подтеком . При осмотре в стрипперном отделении наличи  плены на всех слитках не обнаружено.Opening of the gates above the first two molds was carried out using oxygen with a highly raised ladle, which led to the filling of the first two molds with a wide jet. The last two molds were poured through a single gate with a low-quality jet with a spike. When viewed in the stripper compartment, the presence of captivity on all ingots was not detected.

Технологические и ,технико-экономические показатели плавок предлагаемым и известным способами приведены в таблице.Technological and technical and economic indicators of the bottoms proposed and known methods are shown in the table.

Таким образом, при использовании стальных листов, подвешиваемых на широкие грани на всю высоту двух первых к двух последних изложниц, достигаютс  более высокие технико-экономические показатели, чем при известных способах (см. таблицу),Thus, using steel sheets suspended on wide edges for the entire height of the first two to the last two molds, higher technical and economic indicators are achieved than with the known methods (see table),

Использование предлагаемого способа обеспечивает упрощение процесса изготовлени  защитных приспособлений, экономию в 3-4 раза стального листа, снижение брака и отсортировки металла по плене, снижение количества по- рьгоов металла при прокатке жести.The use of the proposed method simplifies the process of making protective devices, saving 3-4 times the steel sheet, reducing scrap and sorting the metal through the captivity, reducing the number of metal portions during the rolling of tin.

Claims (2)

1. Способ разливки стали сверху преимущественно в крупные листовые изложницы, включшопщй использование защитных приспособлений из листовой стали дл  снижени  пленообразовани  и последющуее заполнение изложницы жидким металлом, отличающий- с   тем, что, с целью повьш1ени  качества поверхности слитков, снижени  расхода листовой стали и трудоемкости изготовлени  защитных приспособлений , защитные приспособлени  устанавливают в двух первых и двух последних по ходу разливки из одного ковша изложницах, при этом в качестЕ:е защитных приспособлений использ утот стальные листы площадью, равной площади широких граней изложниц, причем листы подвешивают на этих гран х и закрепл ют скобами за верхний торец.1. The method of casting steel from above mainly into large sheet molds, including the use of sheet steel protectors to reduce foaming and the subsequent filling of the mold with liquid metal, so as to increase the surface quality of the ingots, reduce the consumption of sheet steel and labor consumption protective devices, protective devices are installed in the first two and the last two in the course of casting from one ladle to the molds, with the following quality: in autonomous ispolz utot steel sheet area equal to the area of the broad faces of the mold, the sheets are suspended at these faces of the clamps and is secured over the upper end. 31447539 31447539 2. Способ по П.1, отличаю- используют толщиной 0,5-1,5 мм.2. The method according to Claim 1, characterized by the use of a thickness of 0.5-1.5 mm. щ и и с   тем, что стальные листыu and with the fact that steel sheets VV ПоказателиIndicators Получено годного металла, т : 5115Received suitable metal, t: 5115 Количество отсортированного металла по плене,% 0,55The amount of sorted metal by captivity,% 0,55 Брак металла поMetal marriage плене, % ,0,23captivity,%, 0.23 Количество порывов полосы при прокатке жести The number of strip breaks when rolling tin в т.ч. по плена, шт/1000 т including on captivity, units / 1000 t Расход листа на защитные приспособлени , кг/тSheet consumption for protective devices, kg / t РазливкаCasting По предлагаемому .способуAccording to the proposed. 31073107 1,20 0,251.20 0.25 5,5 2,75.5 2.7 1,21.2
SU874213403A 1987-01-16 1987-01-16 Method of top casting of steel SU1447539A1 (en)