SU1346610A1 - Method of producing porous articles - Google Patents
Method of producing porous articles Download PDFInfo
- Publication number
- SU1346610A1 SU1346610A1 SU833641928A SU3641928A SU1346610A1 SU 1346610 A1 SU1346610 A1 SU 1346610A1 SU 833641928 A SU833641928 A SU 833641928A SU 3641928 A SU3641928 A SU 3641928A SU 1346610 A1 SU1346610 A1 SU 1346610A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- products
- perhydrol
- aqueous solution
- mixture
- sulfuric acid
- Prior art date
Abstract
Изобретение относитс к производству строительных материалов и может быть использовано дл получени пористьс: изделий с применением отходов переработки слюд ного сырь при извлечении редких металлов. Дл снижени стоимости изделий и упрощени технологии изготовлени в смесь в качестве наполнител ввод т остаточный продукт серно-кислот- ной обработки слоистых алюмосиликатов , а затворение ведут водным раствором пергидрол 0,5-10%-ной концентрации . Получаемые издели характеризуютс плотностью 540-1000 кг /м и теплопроводностью (0,6 - 1,4) х X 10 Дж/см.с-°С. 1 табл. сл оо 4: 05 аThe invention relates to the production of building materials and can be used to obtain porous products using waste mica raw materials in the extraction of rare metals. To reduce the cost of products and simplify the manufacturing technology, the residual product of sulfuric acid treatment of layered aluminosilicates is introduced into the mixture as a filler, and the mixing is carried out with an aqueous solution of perhydrol of 0.5–10% concentration. The resulting products are characterized by a density of 540-1000 kg / m and thermal conductivity (0.6 - 1.4) x X 10 J / cm.S - & C. 1 tab. sl oo 4: 05 and
Description
Изобретение относитс к производству строительных материалов и может быть использовано дл получени пористых -изделий с применением отходов переработки слюд ного сырь при извлечении редких металлов.The invention relates to the production of building materials and can be used to obtain porous products using waste mica raw materials in the extraction of rare metals.
Цель изобретени - снижение стоимости изделий и упрощение технологии изготовлени .The purpose of the invention is to reduce the cost of products and simplify manufacturing technology.
Остаточный продукт серно- кислот- ной обработки слоистых алюмосиликатов образуетс в виде отхода в результате обработки кислотой слюд ного сьфь при извлечении редких металлов.The residual product of sulfuric acid treatment of layered aluminosilicates is formed as a waste as a result of mica treatment with acid when extracting rare metals.
Пример. Дл получени пористых изделий используют остаточный продукт серно-кислотной обработки вермикулита следующего химического состава,%: SiOi 78,76; Fe,0j 0,08; CaO 0,11; MgO 0,20;NaiO U,01 KjO 0,05; 13,56; ,90; COj., COj и AE-jOj не обнаружено. Продукт представлен рентгеноаморфной псевдослюдой состава , содержит активный слоистый кремнезем, имеет насыпную массу до 0,2 г/см и характеризуетс высокой дисперсностью (до 600 м /г) по удельной поверхности . Этот продукт смешивают с природным кварцевым песком и цементом, а затем обрабатывают водным растворомExample. To obtain porous products, the residual product of sulfuric acid vermiculite treatment of the following chemical composition is used,%: SiOi 78.76; Fe, 0j 0.08; CaO 0.11; MgO 0.20; NaiO U, 01 KjO 0.05; 13.56; , 90; COj., COj and AE-jOj not detected. The product is represented by an x-ray amorphous pseudo-mica composition, contains active layered silica, has a bulk density of up to 0.2 g / cm and is characterized by high dispersion (up to 600 m / g) over specific surface. This product is mixed with natural quartz sand and cement, and then treated with an aqueous solution.
Содержание компонентов вContent of components in
смеси, мас.%:mixture, wt.%:
остаточный продукт серно-кислотной обработки вермикулитаresidual product of sulfuric acid vermiculite treatment
природный кварцевый песокnatural quartz sand
цементcement
Обработка смеси водным раствором пергидрол концентрации,%Processing the mixture with an aqueous solution of perhydrol concentration,%
Плотность, кг/мDensity, kg / m
Коэффициент теплопроводности , X 10- Дж/см-с Heat conductivity coefficient, X 10- J / cm-s
пергидрол и формуют изделие по технологии получени чеистого бетона. Состав и свойства изделий представлены в таблице.perhydrol and molded product according to the technology of cellular concrete. The composition and properties of the products are presented in the table.
При сохранении качества получаемых изделий предлагаемый способ по сравнению с известным обеспечивает снижение стоимости и упрощение технологии за счет применени высокодисперсных отходов при исключении операции измельчени кремнеземистого наполнител и снижении концентрации пергидрол из-за повышенной реакционной способности примен емого сырь .While maintaining the quality of the products obtained, the proposed method, in comparison with the known method, reduces the cost and simplifies the technology by using highly dispersed waste while eliminating the grinding operation of the silica filler and reducing the perhydrol concentration due to the increased reactivity of the raw material used.
Claims (1)