SU1271840A1 - Compound for coating high-frequency radioceramics - Google Patents
Compound for coating high-frequency radioceramics Download PDFInfo
- Publication number
- SU1271840A1 SU1271840A1 SU843747785A SU3747785A SU1271840A1 SU 1271840 A1 SU1271840 A1 SU 1271840A1 SU 843747785 A SU843747785 A SU 843747785A SU 3747785 A SU3747785 A SU 3747785A SU 1271840 A1 SU1271840 A1 SU 1271840A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- frit
- coating
- sio
- resistance
- glaze
- Prior art date
Abstract
Изобретение относитс к огнеупорной и керамической промьшленности и позвол ет повысить химстойкость и термостойкость покрыти , а также прочность, диэлектрические свойства к добротность рутиловой и перовскитовой радиокерамики путем введени в состав следующих компонентов, мас.%: фритта 60-67, глазурь 33-40, причем фритта содержит мас.%: SiO. 15,4-20,3; PbO 65,7-77; 3,15 ,5; ZnO 1,9-3,3; 2-,6-5,2, a глазурь содержит мас.%: SiO 60,662 ,9; BjOj 6,8-10,1; 10,113 ,6; 6,2-8; CaO 5,5-7; SrO 4,3-6, причем отношение В20 к SiO равно 1:6-1:9. Кислотостойкость покрыти в НС 0,07-0,09% (по потери веса), щелочеустойчивость в NaOH 0,03-0,05% (по потери веса), термо-. стойкость The invention relates to refractory and ceramic industries and improves the chemical resistance and heat resistance of the coating, as well as the strength, dielectric properties to the quality of rutile and perovskite radio ceramics by introducing the following components, wt.%: Frit 60-67, glaze 33-40, and frit contains wt.%: SiO. 15.4-20.3; PbO 65.7-77; 3.15, 5; ZnO 1.9-3.3; 2-, 6-5,2, a glaze contains wt.%: SiO 60,662, 9; BjOj 6.8-10.1; 10,113, 6; 6.2-8; CaO 5.5-7; SrO 4.3-6, and the ratio of B20 to SiO is 1: 6-1: 9. Acid resistance of coating in NA 0.07-0.09% (by weight loss), alkali resistance in NaOH 0.03-0.05% (by weight loss), thermo. stamina
Description
1 Изобретение относитс : к огнеупорной и керамической промыпшенности и может быть использовано при покрытии изделий из высокочастотной рутиловой и перовскитовой керамики дл работы в установках электротехнической промышленности. Целью изобретени вл етс повышение химстойкости и термостойкости покрыти ,,а также прочности, диэлектрических свойств и добротности рутиловой и перовскитовой радиокерамики . Изобретение по сн етс следукзщи- ми конкретными составами, приведенными табл.1. Исходные тонкоизмельченные компоненты - свинецсодержащую фритту и алюмобороснпикатную глазурь, затвор ют водой до плотности суспензии 1,75-1,78 г/см, смешивают в мешалке в течение 0,5 ч и нанос т на издели высокочастотной керамики рутило вой и перовскитовой с помощью писто лета - распьшител , после чего обжигают в электрической печи по сла ующему режиму: 20 -700С по 50/ч Выдержка при 700-800°С по 50°/ч 700 2 ч1 The invention relates to: refractory and ceramic industry and can be used to coat products from high-frequency rutile and perovskite ceramics for work in installations of the electrical industry. The aim of the invention is to increase the chemical resistance and heat resistance of the coating, as well as the strength, dielectric properties and quality of rutile and perovskite radio ceramics. The invention is explained by the following specific compositions given in Table 1. The initial fine-grained components, lead-containing Frit and alumino-boros pickling glaze, are closed with water to a suspension density of 1.75-1.78 g / cm, mixed in a mixer for 0.5 h, and applied to the high-frequency ceramics products by means of a pisto summers - porschitel, then burned in an electric oven in a slurry mode: 20-700C at 50 / h Exposure at 700-800 ° C at 50 ° / h 700 2 h
800-850 0 по 20°/ч800-850 0 at 20 ° / h
Вьщержка приOverhead
Охлаждение по 850С 1 чCooling at 850С 1 h
Свойства предлагаемых составов представлены в та:бл.2.Properties of the proposed formulations are presented in that: bl.2.
Claims (1)