SU1114616A1 - Method for surface treatment of titanium dioxide pigment of anathaze modification - Google Patents
Method for surface treatment of titanium dioxide pigment of anathaze modification Download PDFInfo
- Publication number
- SU1114616A1 SU1114616A1 SU803218945A SU3218945A SU1114616A1 SU 1114616 A1 SU1114616 A1 SU 1114616A1 SU 803218945 A SU803218945 A SU 803218945A SU 3218945 A SU3218945 A SU 3218945A SU 1114616 A1 SU1114616 A1 SU 1114616A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- titanium dioxide
- surface treatment
- pigment
- modification
- suspension
- Prior art date
Abstract
СПОСОБ ПОВЕРХНОСТНОЙ ОБРАБОТКИ ПИПЕНТИОи ДВУОКИСИ ТИТАНА АНАТАЗНОЙ МОДИФИ1Ш1ИИ соединени ми алюмини и кремни , В1слючаю1щ{й введе1ше моноэтанол амина, отличаю.щий с тем, что, с целью С1шжени водоемкости пигмента н повышени его дисперги {)уемости в казеине, моноэтанол амин добавл ют до создани рН 7,0-7,2.METHOD OF SURFACE TREATMENT OF PIPENTIA AND TITANIUM DUOXIDE ANTATASIUM MODIFIED STEEL WITH ALUMINUM COMPANIES ALUMINUM SAFETY AMONTANE AMYNTHAL AMINHANIUM DIFFERENTIAL AMONG ADDITIONAL ADDITIONALLY YOU ARE OUT YOURSELVES pH 7.0-7.2.
Description
(Л С(Ls
.4;: О5 11 Изобретение относитс к производ ству пигментной двуокиси титана ана тазной модификаи,ии, примен емой в производстве покрывных казеиновых концентратов, используе№1х дп отде ки кож. Известен способ, по которому поверхностную обработку пигментной дв окиси титана ведут путем последовательного введе1-ш в нагретую до 20-70 С суспензию водорастворимых с лей кремни и алюмини в две стадии с последующей нейтрализацией содой щелочью, фильтрадией,-промывкой, суш кой и измельчением пигмента L11. Недостатком указанного способа вл етс высока водоемкость пигмен та и низкий сухой остаток в покрывном концентрате, пигментированном двуокисью титана. Наиболее близким к изобретению по технической сущности вл етс сп соб получени пигментной двуокиси титана, обработанной моноэтаноламином (МЭА), путем осаждени О,L2 ,0% ША на поверхности частиц анатаза , предварительно обработанных или необработанргых) соединени м алюмини и кремни в количестве МхОз, и SiOt соответственно 0,2-10% и 0,5-5,0%Г21 .Известный способ не позвол ет получить пигмент с низкой водоемкостью и диспергируемостью в казеине- . Цель изобретени - сш жение водо емкости пигмента, улучшение дисперг руемости в казеине. Поставленна цель достигаетс те что согласно способу поверхностной работки пигментной двуокиси титана анатазной модификации соединени ми алюмини и кремни , включающему вве ние моноэтаноламина, последний доба л ют до создани рН 7,0 - 7,2. Осаждение МЭА на поверхности час тиц после нанесени гидроокисей металлов приводит к тому, что молекулы МЭА соедин ютс с поверхностью через ОН-группы, дела ее гидрофиль ной. Введение же МЭА одновременно с сернокислыми сол ми алюмини приводит к обменному взаимодействию аминоспирта и кислой соли с образованием легкоудап емого сульфата аммони и органической молекулы, соедин ющейс с поверхностью частиц и гидрофобИзирующей ее. В результате водоемкость пигмента снижаетс улучшаетс диспергируемость в казёй не. Количество соединений А1 и Si, подаваемое на -обработку двуокиси титана, выбираетс таким образом, чтобы полностью закрыть поверхность частиц, и составл ет от 1 до 4% на один слой, а при двухслойном покрытии 4-8%. Грубодисперсный продукт с малой удельной поверхностью требует меньще модификаторов, мелкодисперсный - больще. Количество МЭА зависит от количества кислого неорганического модификатора, который нужно нейтрализовать до рН 7,0 - 7,2. Пример I. К суспензии двуокиси титана анатазной модификации с концентрацией 100 г/л TiO, имеющей температуру , добавл ют раствор NagSiOj с концентрацией 50 г/л в количестве t% в пересчете на Si02 к ТЮг, суспензию перемешивают 20 мин и добавл ют раствор А12{30и)з с концентрацией 50 г/л , в количестве 0,5% в пересчете на TiOj. Суспензию перемещивают 20 мин и нейтрализуют раствором МЭА концентрацией 100 г/л до рН 7,0. После перемешивани в течение 30 мин проводитс повторна обработка 1% SiOn и 0,5% AljOjK TiO и нейтрализаци суспензии раствором ЮА до рН 7,0. -Количество .МЭА на обе стадии составл ет 1,5%. После перемешивани в течение 30 мин суспензию фильтруют, осадок отмывают, сушат при 120°С и измельчают на лабораторной воздухоструйной мельнице. Водоемкость пигмента 50%. Диспергируемость в бисерной мельнице в казеине за 60 мин 18 мкм. П р и м. е р 2. К суспензии двуокиси титана с концентрацией 100 г/л Добавл ют раствор жидкого стекла с концентрацией 50 г/л SL02B количестве 3% SiOg к TiOj , суспензию перемещивают 20 мин и добавл ют раствор AluCSO) с концентрацией 50 г/л в количестве 1% в пересчете на к TiOg, суспензию перемешивают 20 мин и нейтрализуют раствором ЮА концентрацией 100 г/л до рН 7,0. После перемешивани суспензии в. течение 30 мин проводитс повторна обработка 3% SiOg к TiOj ч 1% AljOj к TiCj. и нейтрализаци суспензии раствором МЭА до рН 7,0. Количество МЭА на нейтрализацию составл ет 7%. После перемешивани в течение 30 мин суспензию фильтруют, oTNfciBaioT, сушат.4 ;: O5 11 The invention relates to the production of pigmented titanium dioxide antase modification, and used in the manufacture of coating casein concentrates, using No. 1x dp leather. There is a method in which the surface treatment of the pigmented titanium oxide dvor is carried out by successively introducing 1-sh into a suspension soluble to 20–70 ° C in water-soluble aluminum and aluminum in two stages, followed by neutralization with soda with alkali, filtrate, rinsing, drying and grinding the pigment L11. The disadvantage of this method is the high water content of the pigment and the low dry residue in the coating concentrate pigmented with titanium dioxide. The closest to the invention to the technical essence is the method of producing titanium dioxide pigment dioxide treated with monoethanolamine (MEA) by deposition of O, L2, 0% PCA on the surface of anatase particles, pretreated or untreated aluminum and silicon compounds in the amount of MhO3, and SiOt, respectively, 0.2-10% and 0.5-5.0% G21. The well-known method does not allow to obtain a pigment with low water capacity and dispersibility in casein-. The purpose of the invention is to reduce the capacity of the pigment, improve dispersibility in casein. This goal is achieved by the fact that, according to the method of surface treatment of titanium dioxide pigment anatase modification with aluminum and silicon compounds, including the introduction of monoethanolamine, the latter is added until a pH of 7.0 - 7.2 is created. The deposition of MEA on the surface of the particles after the application of metal hydroxides leads to the fact that the molecules of MEA are connected to the surface through OH groups, making it hydrophilic. The introduction of MEA simultaneously with aluminum sulphate leads to the exchange interaction of the amino alcohol and acid salt with the formation of readily available ammonium sulfate and an organic molecule that connects to the surface of the particles and hydrophobic it. As a result, the water content of the pigment is reduced, and dispersibility in the case is not improved. The number of compounds A1 and Si supplied to the titanium dioxide processing is chosen in such a way as to completely cover the surface of the particles, and is from 1 to 4% per layer, and with a two-layer coating 4-8%. A coarse product with a low specific surface area requires fewer modifiers, a fine product is more. The amount of MEA depends on the amount of the acidic inorganic modifier, which must be neutralized to a pH of 7.0 - 7.2. Example I. To a suspension of titanium dioxide of anatase modification with a concentration of 100 g / l TiO, having a temperature, is added a solution of NagSiOj with a concentration of 50 g / l in an amount of t% in terms of SiO2 to TiOg, the suspension is stirred for 20 minutes and the solution A12 is added {30i) s with a concentration of 50 g / l, in the amount of 0.5% in terms of TiOj. The suspension is moved for 20 minutes and neutralized with a solution of MEA concentration of 100 g / l to a pH of 7.0. After stirring for 30 minutes, re-treatment with 1% SiOn and 0.5% AljOjKTiO is carried out and the suspension is neutralized with a solution of SA to pH 7.0. The amount of MEA at both stages is 1.5%. After stirring for 30 minutes, the suspension is filtered, the precipitate is washed, dried at 120 ° C and ground in a laboratory air jet mill. Pigment water consumption is 50%. Dispersibility in a bead mill in casein for 60 min 18 microns. Example 2. To a suspension of titanium dioxide with a concentration of 100 g / l. Add a liquid glass solution with a concentration of 50 g / l SL02B amount of 3% SiOg to TiOj, move the suspension for 20 minutes and add AluCSO solution) with a concentration 50 g / l in the amount of 1% in terms of TiOg, the suspension is stirred for 20 minutes and neutralized with a solution of JuA concentration of 100 g / l to a pH of 7.0. After stirring the suspension, c. for 30 min, repeated treatment is carried out with 3% SiOg to TiOj h 1% AljOj to TiCj. and neutralizing the suspension with a MEA solution to pH 7.0. The amount of MEA to neutralize is 7%. After stirring for 30 minutes, the suspension is filtered, oTNfciBaioT, dried
3131
при и измельчают на лаборатор ной воздухоструйной мельнице. Водоемкость пигмента 50%. Диспергируемость в бисерной мельнице в казеине за 60 мин 6 мкм.they are ground and ground in a laboratory air jet mill. Pigment water consumption is 50%. Dispersibility in a bead mill in casein for 60 min 6 microns.
Дл сравнени с предпагае 1м способом воспроизводитс известный способ . Результаты его приведены в примере 3.For comparison with the preparatory method, the known method is reproduced. The results are given in example 3.
Пример 3. В суспензию двуокиси титана, обработанную 2% Alj,0j и 0,7% SiO от веса ИО , добавл ют 0,32% МЭД. Суспензию перемешивают, отфильтровывают. Полученный продукт сушат, измельчают на воздухоструйной мельнице. Водоемкость пигмента 120%. Диспергируемость в казеине в бисерной мельнице за 60 минут 35 мкмExample 3. To a suspension of titanium dioxide, treated with 2% Alj, 0j and 0.7% SiO by weight of the IO, was added 0.32% MED. The suspension is stirred, filtered. The resulting product is dried, ground in an air jet mill. The capacity of the pigment is 120%. Dispersibility in casein in a bead mill for 60 minutes 35 microns
Сравнительные показатели качества по известному и предлагаемому способу представлены в таблице.Comparative quality indicators for the known and proposed method are presented in the table.
Использование предлагаемого способа поверхностной обработки пигментной двуокиси титана обеспечиваетThe use of the proposed method of surface treatment of titanium dioxide pigment provides
164164
по сравнению о известным, снижение водоемкости пигмента на 50%, улучшение диспергируемости в казеинеcompared to the known, reducing the water content of the pigment by 50%, improving the dispersibility of casein
в 2 раза. 2 times.
Результаты испытаний показывают, что полученна двуокись титана соответствует требовани м, предъ вл е « 1М к пигменту в производстве покрывных концентратов.The test results show that the obtained titanium dioxide meets the requirements presented to the pigment in the production of coating concentrates.
Claims (1)