SU1081231A1 - Sintered friction material based on iron - Google Patents

Abstract

СПЕЧЕННЫЙ ФРИКЦИОННЫЙ МАТЕРИАЛ НА ОСНОВЕ ЖЕЛЕЗА, содержащий карбид кремни  и графит, о т л и чающийс  тем, что, с целью повышени  физико-механических свойств, предельно допустимых нагрузок и снижени  себестоимости при сохранении фрикционных свойств, он дополнительно содержит порршок вулканического туфа при следующем соотношении кс 1понентов, мас.%: Карбид 2,5-3,0 кремни  2,0-2,5 Графит Порошок вулканического 2,5-3,5 туфа Железо ОстальноеSINTERED IRON-BASED FRICTIONAL MATERIAL containing silicon carbide and graphite, in order to improve physical and mechanical properties, maximum allowable loads and cost reduction while maintaining frictional properties, it additionally contains a volcanic tuff in the following ratio ks 1components, wt%: Carbide 2.5-3.0 silicon 2.0-2.5 Graphite Volcanic powder 2.5-3.5 tuff Iron Else

Description

Изобретение относитс  к поро вой метгшлургии, в частности к спеченным фрикционным материгш на основе железа, используемым в конструкци х фрикционного на чени , работакнцих при сухом тре и трении со смазкой. Известен спеченный фрикцион материал на основе железа С13 с дукицего состава, мас.%: Графит10-25 Карбид кремни  . До 20 Железо60-75 Тверда  смазка Огтальное Недостатком этого материала  вл етс  низка  прочность и раб тоспособность только при сухом трении. Наиболее близким к изобретен по технической сущности и дости гаемому результату  вл етс  спе ный фрикционный материал на осн железа 2 следующего состава, мас.%: Сернокислый никель Графит Ситалл Дисилицид кальци  Карбид кремни  Кремний Дисилицид железа Асбест Остальное Железо Недостатками известного мате  вл ютс  низкие физико-механиЧе свойства, невысокие предельно допустимые нагрузки и высока  себестоимость , составл юща  14901520 руб. за тонну. Целью изобретени   вл етс  повышение физико-механических свойств, предельно допустиквлх нагрузок и снижение себестоимости спеченного фрикциоиного материала при сохранении фрикционных свойств. Поставленна  цель достигаетс  , что спеченный фрикционный материал на основе железа, содержащий карбид кремни  и графит дополнительно содержит пороиок вулканического туфа при следующем соотношении компонентов, мас.%: Карбид кремни 2,5-3,0 Графит2,5-2,5 Порошок вулканического туфа2,5-3,5 Железо Остальное Порошок вулканического туфа  вл етс  отходом производству и не требует дополнительной обработки при его использовании дл  получени  фрикционного материала. Пример. Порошки исходных компонентов смешивали в течение 2,5-3 ч, спрессовали в заготовки при удельном давлении 5-6 т/см и спекали в среде водорода в течение 2 ч при 110-1150 С. В таблице приведены свойства предложенного фрикционного материаа и его себестоимость в сопоставении со свойствами и себестоимостью известного материала.The invention relates to pore metal shlurgii, in particular to sintered iron-based friction materials used in friction structures designed for dry friction and lubricated friction. Known sintered friction material on the basis of iron C13 with Duquia composition, wt.%: Graphite 10-25 Silicon carbide. Up to 20 Iron 60-75 Solid lubricant Ogtal The disadvantage of this material is low strength and working capacity only with dry friction. The closest to the invented technical essence and the achieved result is a fusion material based on iron 2 of the following composition, wt%: Nickel sulphate Graphite Sitall Calcium disilicide Silicon carbide Silicon Iron disilicide Asbestos Else Iron mechanical properties, low maximum permissible loads and high cost, amounting to 14,901,520 rubles. per ton. The aim of the invention is to increase the physicomechanical properties, the maximum tolerances of the loads and the reduction of the cost of the sintered frictional material while maintaining the frictional properties. The goal is achieved that the sintered friction material based on iron, containing silicon carbide and graphite, additionally contains volcanic tuff porosity in the following ratio, wt.%: Silicon carbide 2.5-3.0 Graphite2.5-2.5 Volcanic tuff powder2 , 5-3.5 Iron Else The powder of volcanic tuff is a production waste and does not require additional treatment when used to obtain a friction material. Example. The powders of the initial components were mixed for 2.5–3 h, compressed into blanks at a specific pressure of 5–6 t / cm, and sintered in hydrogen for 2 h at 110–1150 ° C. The table shows the properties of the proposed friction material and its cost price in comparison with the properties and cost of a known material.

Предлагаемый 2,5 Остальное 3,0 ,5 - ИзвестнойProposed 2.5 Rest 3.0, 5 - Known

2525

0,70.7

12,3-13 14 1,0 110 30 15 1,1 100 35 15 1,2 90 3012.3-13 14 1.0 110 30 15 1.1 100 35 15 1.2 90 30

..

0,05 0,3540.05 0.354

0,055 0,44,60.055 0.44.6

0,05 0,450.05 0.45

0,13-0,14 0,38-0,45-8.0.13-0.14 0.38-0.45-8.

тКак следует из приведенных в . . таблице данных предложенный фрикци- 25 онный материал на основе железа имеет себестоимость в 3,3,5 раза ниже, чем себестоимость известного As follows from c. . data table, the proposed iron-based friction material has a cost of 3.3 times less than the cost of a known

Продсшжение таблицыSpreadsheet

70 80 7570 80 75

455 457 460455 457 460

40-50 1490-1520 материала, более высокие физико-механические свойства и предельно допустимые. нагрузки при сохранении фрикционных свойств.40-50 1490-1520 material, higher physico-mechanical properties and maximum permissible. load while maintaining frictional properties.

Claims (1)

СПЕЧЕННЫЙ ФРИКЦИОННЫЙ МАТЕРИАЛ НА ОСНОВЕ ЖЕЛЕЗА, содержащий карбид кремния и графит, о т л ичающийся тем, что, с целью повышения физико-механических свойств, предельно допустимых нагрузок и снижения себестоимости при сохранении фрикционных свойств, он дополнительно содержит порошок вулканического туфа при следующем соотношении компонентов, мас.%:SINTERED FRICTION MATERIAL ON THE BASIS OF IRON, containing silicon carbide and graphite, characterized in that, in order to increase physical and mechanical properties, maximum allowable loads and reduce costs while maintaining frictional properties, it additionally contains volcanic tuff powder in the following ratio of components , wt.%: Карбид кремния 2,5-3,0Silicon Carbide 2.5-3.0 Графит 2,0-2,5Graphite 2.0-2.5 Порошок вулканического туфа Железо * 9 ³ ГVolcanic Tuff Powder Iron * 9 ^3G ОстальноеRest