SE519860C2 - Sätt att tillverka ett skär bestående av en PcBN-kropp och en hårdmetall- eller cermet-substrat - Google Patents

Sätt att tillverka ett skär bestående av en PcBN-kropp och en hårdmetall- eller cermet-substrat

Info

Publication number
SE519860C2
SE519860C2 SE9901221A SE9901221A SE519860C2 SE 519860 C2 SE519860 C2 SE 519860C2 SE 9901221 A SE9901221 A SE 9901221A SE 9901221 A SE9901221 A SE 9901221A SE 519860 C2 SE519860 C2 SE 519860C2
Authority
SE
Sweden
Prior art keywords
pcbn
powder
cemented carbide
making
cermet substrate
Prior art date
Application number
SE9901221A
Other languages
English (en)
Other versions
SE9901221L (sv
SE9901221D0 (sv
Inventor
Ulf Rolander
Gerold Weinl
Original Assignee
Sandvik Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sandvik Ab filed Critical Sandvik Ab
Priority to SE9901221A priority Critical patent/SE519860C2/sv
Publication of SE9901221D0 publication Critical patent/SE9901221D0/sv
Priority to DE60000382T priority patent/DE60000382T2/de
Priority to AT00104912T priority patent/ATE223360T1/de
Priority to EP00104912A priority patent/EP1043291B1/en
Priority to US09/520,878 priority patent/US6287489B1/en
Priority to CN00105817A priority patent/CN1269272A/zh
Priority to JP2000110553A priority patent/JP5456948B2/ja
Publication of SE9901221L publication Critical patent/SE9901221L/sv
Publication of SE519860C2 publication Critical patent/SE519860C2/sv

Description

30 ~-519 860 Z diga spårgeometrin gör automatisk hantering opálitlig. Frånsett påtagliga hälsorisker kan manuell packning leda till ojämn pack- ningsdensitet och till överdriven syreexponering av PCBN-pulvret.
Den ojämna packningsdensiteten gör det nödvändigt att välja en större spårdimension än önskvärt för att säkerställa att den mängd av PCBN som erhålls alltid är tillräcklig. Noggrann kontroll av syreinnehållet i PcBN-pulvret är kritisk för HP/HT-sintringen ef- tersom överskott av syre påverkar konsolideringsprocessen nega- tivt. I princip vill man gärna ha en hög och högt reproducerbar packningsdensitet och reducera syreupptagningen under behandling och lagring.
Enligt uppfinningen, föreligger ett PCBN innehållande pulver med goda flödesegenskaper. Pulvret är speciellt lämpligt att till- verka kroppar av komplicerad form med strama toleranser och högt reproducerbar grönkroppsdensitet.
Enligt metoden enligt uppfinningen föreligger ett pulver lämpligt för att producera materialet beskrivet ovan, omfattande följande steg: l. Blandning av ràmaterialpulver (t ex cBN, hBN, TiC, TiN, Ti(C,N), WC, W, C, Co, Co2Al9, Al, AlN, Al2O3) med en vätska (t ex etanol) och ett pressmedel (t ex polyetylenglykol, PEG) för att bilda en homogen slurry med önskad sammansättning. 2. Formning av sfäriska pulveragglomerat, typiskt 100 pm i diameter, företrädesvis med användning av spraytorkningsteknik. i ett 3. Fyllning av PCBN-pulvret i urtag, fickor, hårdmetall- eller cermetsubstrat. spår etc. 4. Avlägsnande av den organiska tillsatsen från pulvret vid en temperatur och atmosfär lämpliga för det valda pressmedlet (fö- reträdesvis 200-400 OC i strömmande väte för PEG). 5. Sintring av PCBN-pulvret och samtidigt bindning till sub- stratet i en behållare under HP/HT-betingelser för att bilda en kompositkropp t ex ett skär.
Metoden har beskrivits med hänvisning till PCBN men det är uppenbart att det kan användas även med användning av diamant som abrasivt material eller blandningar därav.

Claims (1)

10 U 519 860 Krav
1. Sätt att tillverka ett PcBN-skär bestående av en kropp och ett hårdmetall- eller cermetsubstrat k ä n a t av att PcBN-kroppen framställs genom - blandning av råmaterialpulver d v s cBN och en/ett eller flera av hBN, TiC, TiN, Ti(C,N), WC, W, C, Co, Co2Al9, Al, AlN, Al2O3 med en lämpliga vätska såsom etanol och en organisk tillsats såsom polyetylenglykol, PEG, för att bilda en homogen slurry med önskad sammansättning - bildning av sfäriska pulveragglomerat, typiskt 100 um i diameter, genom spraytorkning - fyllning av PCBN-pulvret i urtag, fickor, spår etc. i ett hårdmetall- eller cermetsubstrat - avlägsnande av den organiska tillsatsen i PcBN-pulvret vid en lämplig temperatur och i en lämplig atmosfär - sintring av PCBN-pulvret och samtidigt bindning till sub- stratet i en behållare under HP/HT-betingelser.
SE9901221A 1999-04-07 1999-04-07 Sätt att tillverka ett skär bestående av en PcBN-kropp och en hårdmetall- eller cermet-substrat SE519860C2 (sv)