RU2751397C9 - Fire extinguishing plate based on microcapsulated extinguishing agents - Google Patents
Fire extinguishing plate based on microcapsulated extinguishing agents Download PDFInfo
- Publication number
- RU2751397C9 RU2751397C9 RU2020133655A RU2020133655A RU2751397C9 RU 2751397 C9 RU2751397 C9 RU 2751397C9 RU 2020133655 A RU2020133655 A RU 2020133655A RU 2020133655 A RU2020133655 A RU 2020133655A RU 2751397 C9 RU2751397 C9 RU 2751397C9
- Authority
- RU
- Russia
- Prior art keywords
- fire extinguishing
- nitrocellulose
- fire
- microcapsules
- extinguishing agent
- Prior art date
Abstract
Description
Область техникиTechnology area
Изобретение относится к автономным средствам пожаротушения, а именно, к полимерным композиционным материалам, содержащим огнетушащее вещество в форме микрокапсул и предназначенным для создания автономных устройств тушения огня, не требующих применения автоматизации и участия человека.The invention relates to autonomous fire extinguishing means, namely, to polymer composite materials containing a fire extinguishing agent in the form of microcapsules and designed to create autonomous fire extinguishing devices that do not require the use of automation and human participation.
Предшествующий уровень техникиPrior art
Принцип действия микрокапсулированного огнетушащего вещества (ОТВ) основан на импульсном (взрывоподобном и/или ударном) выбросе инкапсулированного в ядре микрокапсулы огнетушащего термоактивируемого вещества в зону активного горения при превышении в защищаемом объеме температуры активации и/или прямом контакте с пламенем.The principle of operation of a microencapsulated fire extinguishing agent (OTV) is based on a pulsed (explosive and / or shock) release of a thermally activated fire extinguishing agent encapsulated in the microcapsule core into the active combustion zone when the activation temperature in the protected volume is exceeded and / or in direct contact with the flame.
Из информационных источников известны автономные установки пожаротушения (АУП) на основе микрокапсулированных огнетушащих веществ (ОТВ) - «пластина», предназначенная для тушения возгорания в замкнутых объемах до 70 л. В широкой продаже находятся автономные установки «Пиростикер 15-60» и «ФОГ 20-50». https://lider01.ru/catalog/ognetushiteli/samosrabatyvayushchie/?yclid=851987157088760098.From information sources known autonomous fire extinguishing installations (AUP) based on microencapsulated fire extinguishing substances (OTV) - "plate", designed to extinguish fire in confined spaces up to 70 liters. Autonomous installations "Pirostiker 15-60" and "FOG 20-50" are widely sold. https://lider01.ru/catalog/ognetushiteli/samosrabatyvayushchie/?yclid=851987157088760098.
Изделия такого рода представляет собой конструкцию в виде пластины толщиной 1-2 мм, состоящую из функционального слоя, выполненного из полимерного композиционного материала, содержащего микрокапсулы с жидким ОТВ, несущей полимерной пленочной основы и фиксирующего клеевого слоя, предназначенного для монтажа АУП на верхней стенке шкафа или непосредственно на защищаемом блоке. В качестве ОТВ в микрокапсулах используют жидкие или газообразные галогенсодержащие углеводороды, например, 2-йодгептафторпропан, 1,1,2,2-тетрафтордибромэтан, перфтор(этил-изопропилкетон), 1,2-дибромгексафторпропан, 1,4-дибромоктафторбутан, 1,1,2,3,3,3-гептафторпропан, октофторциклобутан.Products of this kind represent a structure in the form of a plate with a thickness of 1-2 mm, consisting of a functional layer made of a polymer composite material containing microcapsules with liquid OTB, a supporting polymer film base and a fixing adhesive layer intended for mounting the AUP on the top wall of the cabinet or directly on the protected block. Liquid or gaseous halogenated hydrocarbons are used as OTS in microcapsules, for example, 2-iodoheptafluoropropane, 1,1,2,2-tetrafluorodibromoethane, perfluoro (ethyl-isopropyl ketone), 1,2-dibromohexafluoropropane, 1,4-dibromoctafluorobutane, 1,1 , 2,3,3,3-heptafluoropropane, octofluorocyclobutane.
Размер пластины определяется объемом пространства, подлежащего защите с помощью такой АУП. При возникновении в шкафу возгорания материал АУП нагревается, заключенное в микрокапсулах ОТВ переходит в газообразное состояние. Капсулы, по мере прогрева пластины, взрывообразно раскрываются высвобождая дозированное количества газообразного ОТВ. Подавление возгораний определяется химическим строением ОТВ, которое в очаге возгорания распадается с образованием «тяжелых» свободных радикалов, обрывающих кинетические цепи процесса горения, прекращая его развитие в течение нескольких секунд. Продукты термодеструкции ОТВ, кроме того, обеспечивают изоляцию очага горения от воздуха, создавая газовый «купол» из тяжелых продуктов распада, и препятствуют повторному возгоранию.The size of the plate is determined by the volume of space to be protected by such an AFS. When a fire occurs in the cabinet, the AUP material heats up, the OTV contained in the microcapsules turns into a gaseous state. Capsules, as the plate warms up, explosively open up releasing a metered amount of gaseous OTV. The suppression of fires is determined by the chemical structure of the OTV, which decomposes in the fire site with the formation of "heavy" free radicals, which cut off the kinetic chains of the combustion process, stopping its development within a few seconds. In addition, the products of the thermal destruction of OTB ensure the isolation of the combustion center from the air, creating a gas “dome” of heavy decomposition products, and prevent re-ignition.
Из патента на полезную модель RU 109668, A62D 1/08, опубл. 27.10.2011, Бюл. №30 известно автономное средство пожаротушения, выполненное из материала с огнегасящими свойствами, содержащего микрокапсулы с огнегасящим составом, представляющие собой галогеноуглерод, заключенный в полимерную оболочку из полимочевины и/или полиуретана, и связующее, отличающееся тем, что связующее представляет собой композиционный материал, включающий в себя полимерную составляющую и минеральные волокна и/или частицы, при этом средство пожаротушения является галогеноуглеродом, является 1,1,2,2-тетрафтордибромэтан и/или 1,1,2-трифтортрихлорэтан, и/или 2-йод-1,1,1,2,3,3,3-гептафторпропан, и/или их смесь с другими галогенуглеродами, а средство пожаротушения в виде пластины.From the utility model patent RU 109668,
Известен патент на полезную модель RU 152765 А62С 2/00, 20.06.2015, Автономное средство для пожаротушения с термоактивирующимся микрокапсулированным огнетушащим веществом выполнено в виде многослойной пластины, состоящей из опорной подложки, выполненной из рулонного тканого стеклопластика, пропитанного полимерным латексом, клеевого слоя, нанесенного на одну из сторон опорной подложки, отделяемой защитной пленки, которая временно закрывает клеевой слой, армирующей подложки в виде малярной сетки из стеклоткани, расположенной на противоположной стороне опорной подложки, и нанесенного на армирующую подложку огнегасящего композиционного материала, окрашенного тонкодисперсным красителем, содержащего в качестве полимерного связующего отвержденную пластифицированную дибутилфталатом поливинилацетатную смолу и смесь микрокапсул, содержащих в качестве огнетушащего агента (вещества) галогенсодержащие алифатические насыщенные углеводороды из класса хладонов (фреонов).Known utility model patent RU 152765 A62C 2/00, 06/20/2015, An autonomous fire extinguishing agent with a thermoactivated microencapsulated fire extinguishing agent is made in the form of a multilayer plate consisting of a support substrate made of a roll woven fiberglass impregnated with polymer latex, an adhesive layer applied on one of the sides of the support substrate, a peelable protective film that temporarily covers the adhesive layer, a reinforcing substrate in the form of a painting mesh made of glass cloth located on the opposite side of the support substrate, and a fire-extinguishing composite material applied to the reinforcing substrate, painted with a finely dispersed dye, containing as a polymer binder hardened plasticized with dibutyl phthalate polyvinyl acetate resin and a mixture of microcapsules containing as a fire extinguishing agent (substances) halogenated aliphatic saturated hydrocarbons from the class of freons (freons).
Такие пластины являются пассивно термоактивируемыми, выделение огнегасящего агента из которых происходит не одновременно, а по мере прогрева изделия из такого материала. Недостатком такой пластины является низкая интенсивность выделения ОТВ и, соответственно, значительное время подавления возгорания. Кроме того, применение таких материалов ограничено объемами до 70 л, поскольку в больших объемах скорости поступления огнегасящих веществ и их естественного отвода через технологические отверстия защищаемого оборудования становятся соизмеримыми и не позволяют обеспечить поддержание пожаротушащей концентрации активного вещества.Such plates are passively thermally activated, the release of the extinguishing agent from which does not occur simultaneously, but as the product from such material warms up. The disadvantage of such a plate is the low intensity of the release of OTH and, accordingly, a significant time to suppress the ignition. In addition, the use of such materials is limited to volumes of up to 70 liters, since in large volumes the rates of inflow of extinguishing agents and their natural removal through the technological holes of the protected equipment become comparable and do not allow maintaining the fire extinguishing concentration of the active substance.
В заявке на изобретение RU 2012 142 459, A62D 1/00 для повышения эффективности срабатывания пластин из материала на основе полисилоксановой матрицы и микрокапсулированных огнегасящих агентов предложено окрашивать наружную поверхность пластин в черный цвет с целью увеличения коэффициента поглощения ими лучистой энергии.In the application for invention RU 2012 142 459,
В заявке на изобретение RU 2017138075, A62D 1/00 предложено изделие в виде пластины с фасонным профилем, увеличивающим площадь газовыделения, повышая, таким образом, интенсивность выделения огнетушащего вещества.In the application for invention RU 2017138075,
Все эти приемы несколько уменьшают время тушения возгорания, однако это уменьшение незначительно, а такие АУП так же следует отнести к пассивно активирующимся, в которых выделение ОТВ происходит не одновременно, а по мере прогрева изделия из такого материала.All these techniques somewhat reduce the time for extinguishing the fire, however, this decrease is insignificant, and such AUP should also be classified as passively activated, in which the release of OTF occurs not simultaneously, but as the product from such material warms up.
Наиболее близким аналогом является патент на изобретение RU 2 631 868, C08J 9/34, опубл. 27.09.2017, под названием «Гибкая пластина, содержащая огнегасящий композиционный материал, и способ ее изготовления». Описана гибкая пластина, изготовленная из огнегасящего композиционного материала в котором в полимерной матрице из отвержденного диметилсилоксанового каучука СКТН распределены сыпучие микрокапсулы с ядром из огнегасящего агента, а в качестве добавки увеличивающей теплопроводность, а, следовательно, и скорость выделения ОТВ - алюминиевая пудра. Такие пластины, по представлению автора изобретения имеют в 3 раза большую эффективность огнегашения, но по-прежнему остаются пассивно термоактивируемыми.The closest analogue is the patent for
Раскрытие изобретенияDisclosure of invention
Задачей создания изобретения является разработка пластины для пожаротушения, которая свободна от недостатков прототипа.The task of creating the invention is to develop a plate for fire extinguishing, which is free from the disadvantages of the prototype.
Технический результат изобретения заключается в существенном повышении эффективности пожаротушения предлагаемой пластиной.The technical result of the invention consists in a significant increase in the efficiency of fire extinguishing with the proposed plate.
Поставленная задача была решена путем создания активной термоактивируемой огнетушащей пластины, выполненной в виде многослойной конструкции, включающей функциональный слой, несущий слой, фиксирующий слой. Пластина отличается тем, что функциональный слой представляет собой композиционный материал, состоящий из полимерной матрицы и микрокапсул с ядром из огнетушащего вещества, при этом в качестве термоактивируемой полимерной матрицы используют нитроцеллюлозу-коллоксилин с содержанием азота от 10,7% до 12,2%, при следующем соотношении компонентов, масс. %:The task was solved by creating an active thermally activated fire extinguishing plate made in the form of a multilayer structure, including a functional layer, a supporting layer, a fixing layer. The plate differs in that the functional layer is a composite material consisting of a polymer matrix and microcapsules with a core of a fire extinguishing agent, while nitrocellulose-colloxylin with a nitrogen content of 10.7% to 12.2% is used as a thermally activated polymer matrix, with the following ratio of components, wt. %:
при этом композиционный материал получен с использованием стабилизатора и пластификатора, при следующем соотношении компонентов, в масс. % в пересчете на упомянутую нитроцеллюлозу:while the composite material is obtained using a stabilizer and a plasticizer, with the following ratio of components, in mass. % based on the mentioned nitrocellulose:
Кроме того, в качестве огнетушащего вещества используют жидкие и/или газообразные галогенсодержащие углеводороды, например, 2-йодгептафторпропан, 1,1,2,2-тетрафтордибромэтан, перфтор(этил-изопропилкетон), 1,2-дибромгексафторпропан, 1,4-дибромоктафторбутан, 1,1,2,3,3,3-гептафторпропан, октофторциклобутан.In addition, liquid and / or gaseous halogenated hydrocarbons are used as a fire extinguishing agent, for example, 2-iodoheptafluoropropane, 1,1,2,2-tetrafluorodibromoethane, perfluorine (ethyl isopropyl ketone), 1,2-dibromohexafluoropropane, 1,4-dibromoctafluorobutane , 1,1,2,3,3,3-heptafluoropropane, octofluorocyclobutane.
Кроме того, в качестве стабилизатора используют дифенилметан, централиты.In addition, diphenylmethane and centralites are used as a stabilizer.
Кроме того, в качестве пластификатора используют дибутилфталат. Новый вариант пластины на основе композиционного материала с активной термоактивируемой полимерной матрицей обладает повышенной эффективностью тушения за счет практически единовременного вскрытия микрокапсул с ОТВ с одновременным деструктивным разрушением матрицы и выделения значительного количества нейтральных газов, дополнительно блокирующих очаг возгорания.In addition, dibutyl phthalate is used as a plasticizer. A new version of the plate based on a composite material with an active thermally activated polymer matrix has an increased quenching efficiency due to the almost simultaneous opening of microcapsules with OTF with simultaneous destructive destruction of the matrix and the release of a significant amount of neutral gases, which additionally block the ignition source.
Выбор в качестве вещества матрицы - горючего вещества нитроцеллюлозы-коллоксилин с содержанием азота от 10,7% до 12,2% обусловлен несколькими факторами, а именно: - технической доступностью, промышленно выпускается коллоксилин лаковый по ГОСТ Р 50461-9, - верхний предел по содержанию азота ограничен концентрацией нитрогрупп, при которой НЦ переходит в категорию взрывчатых веществ, - нижний предел ограничен техническими условиями, что не исключает возможности использования нестандартного продукта, если его применение не ограничено растворимостью в применяемых растворителях, обеспечивающих возможность образовывать однородный раствор для диспергирования микрокапсул.The choice of a combustible substance of nitrocellulose-colloxylin with a nitrogen content from 10.7% to 12.2% as a matrix substance is due to several factors, namely: - technical availability, lacquer colloxylin is industrially produced according to GOST R 50461-9, - the nitrogen content is limited by the concentration of nitro groups, at which NC goes into the category of explosives - the lower limit is limited by technical conditions, which does not exclude the possibility of using a non-standard product, if its use is not limited by solubility in the solvents used, which provide the ability to form a homogeneous solution for dispersing microcapsules.
Применение пластин с термоактивируемой полимерной матрицей значительно сокращает огневое воздействие на оборудование в защищаемом объекте, обеспечивая его сохранность.The use of plates with a thermally activated polymer matrix significantly reduces the impact of fire on equipment in the protected object, ensuring its safety.
Осуществление изобретенияImplementation of the invention
В заявляемом изобретении предложен композиционный материал, в котором в качестве термоактивируемой матрицы использован горючий полимерный материал, способный самостоятельно, после кратковременного огневого воздействия, поддерживать горение композита с микрокапсулами ОТВ и обеспечивать, таким образом, залповый выброс всего огнетушащего агента и быстрое подавление очага возгорания в защищаемом объеме.In the claimed invention, a composite material is proposed, in which a combustible polymer material is used as a thermally activated matrix, capable of independently, after a short-term fire exposure, to maintain the combustion of a composite with OTV microcapsules and, thus, to provide a volley release of the entire fire extinguishing agent and rapid suppression of the source of fire in the protected volume.
В качестве матрицы такого материала предложено использовать горючее полимерное вещество - нитроцеллюлозу-коллоксилин с содержанием азота от 10,7% до 12,2% (НЦК).It is proposed to use a combustible polymeric substance - nitrocellulose-colloxylin with a nitrogen content from 10.7% to 12.2% (NCC) - as a matrix for such a material.
Неограниченная растворимость НЦК в таких относительно полярных растворителях, как кетоны, сложные эфиры и совместимость с такими пластификаторами, как дибутилфталат, позволяет получать вязкие растворы, пригодные для наполнения микрокапсулами в широком диапазоне - до 80% вес.(по отношению к композиции с НЦК), при этом нет ограничений по применению других растворителей, пластификаторов, в т.ч. полимерных, и стабилизаторов. Удаление из готовых изделий легко летучих растворителей, содержащихся в относительно небольшом количестве, не вызывает каких-либо технических трудностей.The unlimited solubility of NCC in such relatively polar solvents as ketones, esters and compatibility with plasticizers such as dibutyl phthalate makes it possible to obtain viscous solutions suitable for filling with microcapsules in a wide range - up to 80 wt% (with respect to the composition with NCC), however, there are no restrictions on the use of other solvents, plasticizers, incl. polymer, and stabilizers. The removal of relatively small amounts of readily volatile solvents from finished products does not cause any technical difficulties.
В состав термоактивируемой полимерной матрицы вводят микрокапсулы с ядром из огнетушащего вещества, в качестве которого используют жидкие галогенсодержащие углеводороды, например, 2-йодгептафторпропан, 1,1,2,2-тетрафтордибромэтан, перфтор(этил-изопропилкетон), 1,2-дибромгексафторпропан, 1,4-дибромоктафторбутан, 1,1,2,3,3,3-гептафторпропан, октофторциклобутан.Microcapsules with a core of a fire extinguishing agent are introduced into the composition of a thermally activated polymer matrix, which is used as liquid halogenated hydrocarbons, for example, 2-iodoheptafluoropropane, 1,1,2,2-tetrafluorodibromoethane, perfluoro (ethyl-isopropyl ketone), 1,2-dibromohexafluoropropane, 1,4-dibromoctafluorobutane, 1,1,2,3,3,3-heptafluoropropane, octofluorocyclobutane.
Для обеспечения стабильности композитов с матрицей из НЦК при эксплуатации при повышенных температурах и прямом доступе атмосферной влаги в состав вводят один из известных стабилизаторов, таких как дифенилметан, централиты и др.To ensure the stability of composites with a matrix of NCC during operation at elevated temperatures and direct access to atmospheric moisture, one of the well-known stabilizers, such as diphenylmethane, centralites, etc., is introduced into the composition.
Для регулировки эластичности материала в состав матрицы вводят пластификаторы, например, дибутилфталат.To adjust the elasticity of the material, plasticizers, for example, dibutyl phthalate, are introduced into the matrix.
Композиционный материал имеет следующее соотношение компонентов, масс. %:The composite material has the following ratio of components, mass. %:
при этом композиционный материал получен с использованием стабилизатора и пластификатора при следующем соотношении компонентов в масс. % в пересчете на упомянутую нитроцеллюлозу:while the composite material is obtained using a stabilizer and a plasticizer with the following ratio of components in mass. % based on the mentioned nitrocellulose:
Предлагаемое изобретение поясняется рисунком, на котором показан разрез конструкции огнегасящей пластины для пожаротушения. Пластина представляет собой многослойную конструкцию и состоит из функционального огнегасящего композиционного материала 1 с распределенными в нем микрокапсулами 2, несущей пленочной основы 3, фиксирующего клеевого слоя 4, отделяемой защитной пленки. За счет клеевого слоя пластину фиксируют на верхней стенке защищаемого объема и/или непосредственно на пожароопасных элементах.The invention is illustrated by a drawing, which shows a section of the structure of a fire extinguishing plate for fire extinguishing. The plate is a multilayer structure and consists of a functional fire-extinguishing
При соприкосновении с пламенем происходит возгорание функционального слоя и его беспламенное горение за счет кислорода, входящего в состав самой нитроцеллюлозы. При этом скорость распространения возгорания по поверхности материала на порядок выше ее прогорания внутрь материала. Это приводит к практически одновременному вскрытию микрокапсул с ОТВ по всему материалу. Горение матрицы сопровождается ее полной деструкцией, что обеспечивает беспрепятственный залповый выброс огнетушащего вещества в очаг возгорания, его локализацию и тушение.When in contact with a flame, the functional layer is ignited and its flameless combustion due to oxygen, which is part of the nitrocellulose itself. In this case, the speed of propagation of fire over the surface of the material is an order of magnitude higher than its burning into the interior of the material. This leads to almost simultaneous opening of microcapsules with OTB throughout the material. The combustion of the matrix is accompanied by its complete destruction, which provides an unobstructed salvo discharge of the extinguishing agent into the fire site, its localization and extinguishing.
Дополнительным фактором, обеспечивающим повышенную эффективность предлагаемого композиционного материала, является выделение при сгорании нитроцеллюлозы-коллоксилин значительного количества не поддерживающих горение газообразных продуктов, в среднем 10 л на 10 г нитроцеллюлозы-коллоксилина, основными из которых являются азот (45%), углекислый газ (13,3%), окись углерода (31,6%) и вода, которые дополнительно блокируют доступ кислорода и осуществляют быструю доставку ОТВ к очагу возгорания.An additional factor providing increased efficiency of the proposed composite material is the release of a significant amount of non-combustion gaseous products during combustion of nitrocellulose-colloxylin, on average 10 liters per 10 g of nitrocellulose-colloxylin, the main of which are nitrogen (45%), carbon dioxide (13 , 3%), carbon monoxide (31.6%) and water, which additionally block the access of oxygen and carry out the rapid delivery of the OTS to the fire site.
В таблице приведены результаты сравнительных испытаний известных и заявляемой пожаротушащих пластин. Испытания проводили по методике ГОСТ Р 56459-2015 «Устройства пожаротушения автономные с применением термоактивируемых микрокапсулированных газовыделяющих огнетушащих веществ» в шкафу объемом 50 л на модельном очаге пожара класса В.The table shows the results of comparative tests of the known and claimed fire extinguishing plates. The tests were carried out according to the method of GOST R 56459-2015 "Self-contained fire extinguishing devices with the use of thermally activated microencapsulated gas-emitting fire extinguishing agents" in a 50-liter cabinet on a model class B fire.
Из представленных в таблице данных видно, что время тушения очага возгорания пластиной, изготовленной по рецептуре заявляемого изобретения, существенно меньше, чем у аналогов и прототипа.From the data presented in the table, it can be seen that the time for extinguishing the seat of fire with a plate made according to the recipe of the claimed invention is significantly less than that of analogues and the prototype.
Способ получения огнегасящей пластины для огнетушения содержит следующую последовательность операций.The method of obtaining a fire extinguishing plate for fire extinguishing contains the following sequence of operations.
Для изготовления пластины с заявляемым функциональным слоем готовят 20-60%-ный раствор нитроцеллюлозы-коллоксилин с содержанием азота от 10,7% до 12,2% в ацетоне, или в этилацетате, или в бутилацетате, или в смеси указанных растворителей. В приготовленный раствор вводят стабилизатор 1-2 масс. % в пересчете на НЦК, дибутилфталат 0÷25 масс. % в пересчете на нитроцеллюлозу и микрокапсулы 50÷80 масс. %. в пересчете на композицию с НЦК. Из полученной массы изготавливают пластину путем нанесения через открытый трафарет сплошным слоем или в виде дискретных фрагментов на несущую подложку с последующей сушкой в вытяжном шкафу. Функциональный слой так же можно наносить методом экструзии через фигурные или щелеобразные фильеры с последующим удалением из них растворителя. В качестве подложки используют лавсановую пленку с липким монтажным слоем.For the manufacture of a plate with the claimed functional layer, a 20-60% solution of nitrocellulose-colloxylin is prepared with a nitrogen content of 10.7% to 12.2% in acetone, or in ethyl acetate, or in butyl acetate, or in a mixture of these solvents. In the prepared solution, a stabilizer of 1-2 wt. % in terms of NCC, dibutyl phthalate 0 ÷ 25 wt. % in terms of nitrocellulose and microcapsules 50 ÷ 80 wt. %. in terms of composition with NCC. From the resulting mass, a plate is made by applying through an open stencil in a continuous layer or in the form of discrete fragments on a supporting substrate, followed by drying in a fume hood. The functional layer can also be applied by extrusion through shaped or slit-like dies with subsequent removal of the solvent from them. A lavsan film with a sticky mounting layer is used as a substrate.
Приведенные ниже примеры реализации изобретения не ограничивают иные возможности осуществления изобретения.The following examples of implementation of the invention do not limit other possibilities for carrying out the invention.
Пример 1. 8 г нитроцеллюлозы растворяют в 10 г ацетона при комнатной температуре, добавляют 2 г дибутилфталата. 0,16 г цетролита и смешивают с 15 г микрокапсул с огнегасящим агентом (перфторэтилизопропилкетоном) в оболочке из резорцино-мочевино-формальдегидной смолы. Из полученной композиции изготавливают пластину путем нанесения через открытый трафарет сплошным слоем на подложку из лавсановой пленки с клеевым монтажным слоем с последующей сушкой в вытяжном шкафу для удаления ацетона.Example 1. 8 g of nitrocellulose is dissolved in 10 g of acetone at room temperature, add 2 g of dibutyl phthalate. 0.16 g of citrolite and mixed with 15 g of microcapsules with a fire extinguishing agent (perfluoroethylisopropyl ketone) coated with resorcinol-urea-formaldehyde resin. A plate is made from the obtained composition by applying a continuous layer through an open stencil onto a lavsan film substrate with an adhesive mounting layer, followed by drying in a fume hood to remove acetone.
Пример 2. 10 г нитроцеллюлозы растворяют в 10 г ацетона. Добавляют 0,1 г центролита, 15 г микрокапсул огнегасящим агентом (перфторэтилизопропилкетоном) в оболочке из резорцино-мочевино-формальдегидной смолы и через открытый трафарет наносят на подложку из лавсановой пленки с клеевым монтажным слоем фрагментами диаметр 5 мм образующими регулятную структуру с расстояниями между фрагментами 3 мм.Example 2. 10 g of nitrocellulose is dissolved in 10 g of acetone. 0.1 g of centrolyte, 15 g of microcapsules with a fire extinguishing agent (perfluoroethylisopropyl ketone) in a shell of resorcinol-urea-formaldehyde resin are added and through an open stencil they are applied to a lavsan film substrate with an adhesive mounting layer with fragments 5 mm in diameter forming a regulatory structure with 3 distances between fragments mm.
Пример 3. 10 г нитроцеллюлозы растворяют в 10 г ацетона. Добавляют 0,2 г центролита, 15 г микрокапсул огнегасящим агентом (перфторэтилизопропилкетоном) в оболочке из резорцино-мочевино-формальдегидной смолы и методом экструции через фильеру диаметромЗ мм наносят на подложку из лавсановой пленки с клеевым монтажным слоем полосками, образующими регулярную структуру, с расстояниями между ними 1 мм.Example 3. 10 g of nitrocellulose is dissolved in 10 g of acetone. 0.2 g of centrolite is added, 15 g of microcapsules with a fire extinguishing agent (perfluoroethyl isopropyl ketone) in a shell of resorcinol-urea-formaldehyde resin and by extrusion through a die with a diameter of 3 mm is applied to a substrate made of a lavsan film with an adhesive mounting layer with stripes forming a regular structure, with distances between them 1 mm.
Пример 4. В отличие от примеров 1-2 в качестве, по меньшей мере, одного из микрокапсулированных огнетушащих веществ использовались 2-йодгептафторпропан, 1,1,2,2-тетрафтордибромэтан, перфтор(этил-изопропилкетон), 1,2-дибромгексафторпропан, 1,4-дибромоктафторбутан, 1,1,2,3,3,3-гептафторпропан, октофторциклобутан.Example 4. In contrast to examples 1-2, 2-iodoheptafluoropropane, 1,1,2,2-tetrafluorodibromoethane, perfluoro (ethyl-isopropyl ketone), 1,2-dibromohexafluoropropane were used as at least one of the microencapsulated extinguishing agents, 1,4-dibromoctafluorobutane, 1,1,2,3,3,3-heptafluoropropane, octofluorocyclobutane.
Промышленная применимостьIndustrial applicability
Применение нитроцеллюлозы-коллоксилин с содержанием азота от 10,7% до 12,2% в качестве полимерной матрицы в огнетушащем материале - новая область использования НЦ, при котором используется ее основной недостаток - а именно высокая горючесть. Применение НЦ в таком аспекте позволяет создать высокоэффективные средства тушения огня в ограниченных объемах, срабатывающих в автономном режиме без применения автоматики и участия человека при кратковременном непосредственном огневом воздействии на них.The use of nitrocellulose-colloxylin with a nitrogen content of 10.7% to 12.2% as a polymer matrix in a fire extinguishing material is a new area of NC application, in which its main drawback is used - namely, high flammability. The use of NC in this aspect makes it possible to create highly effective means of extinguishing fire in limited volumes, which are triggered in an autonomous mode without the use of automation and human participation with a short-term direct fire effect on them.
Claims (7)