RU2610741C1 - Enamel - Google Patents
Enamel Download PDFInfo
- Publication number
- RU2610741C1 RU2610741C1 RU2016104211A RU2016104211A RU2610741C1 RU 2610741 C1 RU2610741 C1 RU 2610741C1 RU 2016104211 A RU2016104211 A RU 2016104211A RU 2016104211 A RU2016104211 A RU 2016104211A RU 2610741 C1 RU2610741 C1 RU 2610741C1
- Authority
- RU
- Russia
- Prior art keywords
- enamel
- sio
- zro
- cao
- moo
- Prior art date
Abstract
Description
Изобретение относится к производству эмалей, которые могут быть использованы, преимущественно, для покрытия стальных и чугунных изделий, эксплуатируемых в пищевой, химической отраслях промышленности, сельском хозяйстве.The invention relates to the production of enamels, which can be used mainly for coating steel and cast iron products used in the food, chemical industries, and agriculture.
Известна эмаль, содержащая, мас. %: SiO2 56,2-67,7; Al2O3 0,2-1,0; В2О3 1,0-2,0; ZrO2 10,0-,11,5; СаО 3,0-5,0; Na2O 3,5-4,7; K2O 0,5-0,8; Li2O 3,0-4,0; SrO 4,0-5,0; SnO2 2,0-3,0; Cr2O3 0,8-1,0; Co2O3 0,3-0,8; 3Al2O3⋅2SiO2 4,0-5,0 [1].Known enamel containing, by weight. %: SiO 2 56.2-67.7; Al 2 O 3 0.2-1.0; B 2 O 3 1.0-2.0; ZrO 2 10.0-, 11.5; CaO 3.0-5.0; Na 2 O 3.5-4.7; K 2 O 0.5-0.8; Li 2 O 3.0-4.0; SrO 4.0-5.0; SnO 2 2.0-3.0; Cr 2 O 3 0.8-1.0; Co 2 O 3 0.3-0.8; 3Al 2 O 3 ⋅ 2 SiO 2 4.0-5.0 [1].
Задачей изобретения является повышение термостойкости эмали.The objective of the invention is to increase the heat resistance of enamel.
Технический результат достигается тем, что эмаль, включающая SiO2, B2O3, ZrO2, СаО, Na2O, K2O, Cr2O3, Co2O3, 3Al2O3⋅2SiO2, дополнительно содержит MoO3, при следующем соотношении компонентов, мас. %: SiO2 66,0-67,0; B2O3 5,9-6,4; ZrO2 11,0-12,0; СаО 1,0-1,8; Na2O 2,5-3,2; K2O 1,0-1,8; Cr2O3 0,5-0,8; Со2О3 0,3-0,8; 3Al2O3⋅2SiO2 2,0-3,0; МоО3 6,2-6,7.The technical result is achieved in that the enamel, including SiO2, B2O3ZrO2CaO, Na2O, K2O, Cr2O3, Co2O3, 3Al2O3⋅2SiO2additionally contains MoO3, in the following ratio of components, wt. %: SiO2 66.0-67.0; B2O3 5.9-6.4; Zro2 11.0-12.0; CaO 1.0-1.8; Na2O 2.5-3.2; K2O 1.0-1.8; Cr2O3 0.5-0.8; With2ABOUT3 0.3-0.8; 3Al2O3⋅2SiO2 2.0-3.0; Moo3 6.2-6.7.
В таблице приведены составы эмали.The table shows the composition of the enamel.
Варку фритты эмали осуществляют при температуре 1470-1500°С. Расплав гранулируют в воду. Гранулы размалывают мокрым способом до прохождения через сетку 0056. Полученный шликер с влажностью 44-50% наносят (напыляют) на подготовленную поверхность изделий и закрепляют оплавлением.Enamel frit is cooked at a temperature of 1470-1500 ° С. The melt is granulated into water. The granules are milled wet until passing through a mesh 0056. The resulting slurry with a moisture content of 44-50% is applied (sprayed) to the prepared surface of the products and fixed by reflow.
Источник информацииThe source of information
1. SU 1413063, С03С 8/02, 1987.1. SU 1413063, C03C 8/02, 1987.
Claims (1)