RU2452450C1 - Sorption container - Google Patents
Sorption container Download PDFInfo
- Publication number
- RU2452450C1 RU2452450C1 RU2011112583/15A RU2011112583A RU2452450C1 RU 2452450 C1 RU2452450 C1 RU 2452450C1 RU 2011112583/15 A RU2011112583/15 A RU 2011112583/15A RU 2011112583 A RU2011112583 A RU 2011112583A RU 2452450 C1 RU2452450 C1 RU 2452450C1
- Authority
- RU
- Russia
- Prior art keywords
- sorbent
- zeolite
- sorption
- container
- mixture
- Prior art date
Abstract
Description
Изобретение относится к средствам обработки гнойно-некротических, инфицированных ран, преимущественно за счет физической сорбции микробов, органических и неорганических продуктов их жизнедеятельности, а также продуктов распада тканей, и может быть использовано в хирургической практике при лечении ран, в том числе ожоговых, острых воспалительных заболеваний, гнойных послеоперационных осложнений, перитонитов и т.п.The invention relates to means for treating purulent-necrotic, infected wounds, mainly due to physical sorption of microbes, organic and inorganic products of their vital activity, as well as tissue breakdown products, and can be used in surgical practice in the treatment of wounds, including burns, acute inflammatory diseases, purulent postoperative complications, peritonitis, etc.
Известен сорбционный контейнер, включающий проницаемую эластичную сетчатую оболочку, в полости которой размещен измельченный сорбент (см. RU №2123361, МКИ А61F 13/36, 1998).A sorption container is known, including a permeable elastic mesh shell, in the cavity of which a ground sorbent is placed (see RU No. 2123361, MKI A61F 13/36, 1998).
Степень измельчения используемого сорбента определяется размерами ячей сетчатого материала, а они относительно велики, тем более, если учесть эластичность таких материалов, поэтому, из-за относительно низкой прочности сорбентов (приводящей к их переизмельчению при недостаточно бережном обращении с контейнерами) неизбежно частичное проникновение сорбента за пределы оболочки, что приводит к засорению раны сорбентом и необходимости соответствующей очистки. Кроме того, капроновые и иные ткани прилипают к ране, что излишне ее травмирует при перевязках.The degree of grinding of the used sorbent is determined by the mesh size of the mesh material, and they are relatively large, especially if you take into account the elasticity of such materials, therefore, due to the relatively low strength of the sorbents (leading to their regrinding when the containers are not carefully handled), partial penetration of the sorbent is inevitable the limits of the shell, which leads to clogging of the wound with a sorbent and the need for appropriate cleaning. In addition, kapron and other tissues adhere to the wound, which unnecessarily injures it during dressings.
Известен также сорбционный контейнер, включающий цеолитовый сорбент, размещенный в полости оболочки из гибкого проницаемого неэластичного пористого материала, размеры пор которого меньше размеров частиц сорбента (см. RU №2219887, А61F 13/36, 2002). В качестве сорбента использован клиноптилолитовый туф со степенью измельчения до 0,01 мм, при этом проницаемая оболочка выполнена из пористой целлофановой диализной пленки, медицинской или пищевой), размеры пор которой меньше размеров частиц сорбента.Also known is a sorption container, including a zeolite sorbent, placed in the cavity of the shell from a flexible permeable non-elastic porous material, the pore sizes of which are smaller than the particle sizes of the sorbent (see RU No. 2219887, A61F 13/36, 2002). As a sorbent, clinoptilolite tuff with a degree of grinding up to 0.01 mm was used, while the permeable shell is made of a porous cellophane dialysis film, medical or food), the pore size of which is smaller than the particle size of the sorbent.
Недостаток этого решения - недостаточно высокая скорость сорбции или, при прочих равных условиях, неполнота «использования сорбционной емкости сорбента», что снижает эффективность работы сорбционного контейнера. При этом достижение дисперсности сорбента порядка 100-200 нм сложно достижимо в связи с высокой пластичностью глинистой компоненты, содержание которой в природных цеолитах варьирует в широких пределах, причем пластичный материал существенно перекрывает часть пор, что фактически ведет к потере сорбционной емкости материала. Все это также снижает эффективность работы сорбционного контейнера.The disadvantage of this solution is the insufficiently high sorption rate or, ceteris paribus, the incompleteness of the "use of the sorption capacity of the sorbent", which reduces the efficiency of the sorption container. At the same time, achieving a sorbent dispersion of the order of 100-200 nm is difficult to achieve due to the high plasticity of the clay component, the content of which in natural zeolites varies widely, and the plastic material substantially overlaps part of the pores, which actually leads to a loss in the sorption capacity of the material. All this also reduces the efficiency of the sorption container.
Задача, на решение которой направлено заявленное изобретение, состоит в повышении эффективности работы сорбционного контейнера.The problem to which the claimed invention is directed, is to increase the efficiency of the sorption container.
Технический результат, получаемый при решении названной задачи, выражается в увеличении удельной поверхности сорбента (за счет обеспечения возможности применения существенно более тонкоизмельченных сорбентов), что при прочих равных условиях позволяет уменьшить количество используемых сорбционных контейнеров, кроме того, снижается трудоемкость процесса лечения (за счет уменьшения числа смены контейнеров, исключения необходимости операций очистки ран) и ускорения их заживления.The technical result obtained when solving this problem is expressed in an increase in the specific surface area of the sorbent (due to the possibility of using significantly finer sorbents), which, all other things being equal, can reduce the number of used sorption containers, in addition, the complexity of the treatment process (by reducing the number of container changes, eliminating the need for wound cleansing operations) and accelerating their healing.
Для решения поставленной задачи сорбционный контейнер, включающий цеолитовый сорбент, размещенный в полости оболочки из гибкого неэластичного пористого материала, размеры пор которого меньше размеров частиц сорбента, отличается тем, что оболочка выполнена из диализной пленки, предпочтительно термопластичной, при этом дисперсность сорбента составляет 0,15-10 мкм, кроме того, в качестве сорбента использованы природные цеолиты месторождений вулканогенно-осадочного типа, например, Вангинского, и/или Ванчинского, и/или Водораздельного, и/или Лютогского, и/или Чеховского, и/или Шивертуйского, и/или Хогуруу, предпочтительно, с содержанием глинистого компонента не выше 30% по объему и минералов примесей, например вулканического стекла, и/или полевых шпатов, и/или кварца, не выше 5%, причем названные цеолиты использованы в смеси с цеолитом Люльинского месторождения, доля которого составляет не менее 5% от объема смеси. Кроме того, крупность сорбента, как минимум втрое, превышает размеры пор материала оболочки.To solve the problem, a sorption container comprising a zeolite sorbent placed in the cavity of the shell of a flexible non-elastic porous material, the pore sizes of which are smaller than the particle size of the sorbent, differs in that the shell is made of a dialysis film, preferably thermoplastic, while the dispersion of the sorbent is 0.15 -10 μm, in addition, natural zeolites of volcanic-sedimentary deposits, for example, Vanginsky, and / or Vanchinsky, and / or Dividing, and / or Lutogsky, and / or Chekhovsky, and / or Shivertuysky, and / or Hoguruu, preferably with a clay component content of not more than 30% by volume and minerals of impurities, such as volcanic glass, and / or feldspars, and / or quartz, not higher 5%, and the said zeolites are used in a mixture with the zeolite of the Lulinsky deposit, the proportion of which is at least 5% of the volume of the mixture. In addition, the size of the sorbent, at least three times, exceeds the pore size of the shell material.
Сопоставительный анализ признаков заявленного и известных технических решений свидетельствует о его соответствии критерию "новизна".A comparative analysis of the features of the claimed and known technical solutions indicates its compliance with the criterion of "novelty."
Признаки отличительной части формулы изобретения решают следующие функциональные задачи:The features of the characterizing part of the claims solve the following functional tasks:
Признаки "оболочка выполнена из диализной пленки, предпочтительно термопластичной" обеспечивают возможность применения сорбентов с повышенной степенью измельчения, при наличии тонкопористого материала, обеспечивающего контакт между сорбентом и выделяемым экссудатом, который проникает через поры в диализной пленке, устанавливая тем самым прямой и обратный ток различных (минеральных, органических и биологических) веществ, при этом пленка не прилипает к поверхности раны. Кроме того, упрощается операция герметизации контейнера, которая достаточно легко механизируется.The signs “the shell is made of a dialysis film, preferably thermoplastic” provide the possibility of using sorbents with an increased degree of grinding, in the presence of a finely porous material that provides contact between the sorbent and the exudate that penetrates through the pores in the dialysis film, thereby establishing a direct and reverse current of various ( mineral, organic and biological) substances, while the film does not stick to the surface of the wound. In addition, the operation of sealing the container is simplified, which is quite easily mechanized.
Признак, указывающий, что «дисперсность сорбента составляет 0,15-10 мкм» обеспечивая повышение удельной поверхности сорбента обеспечивает повышение «скорости его работы» и сорбционную емкость, т.е. обеспечивает повышение эффективности работы сорбционного контейнера.A sign indicating that “the dispersion of the sorbent is 0.15-10 μm” by providing an increase in the specific surface of the sorbent provides an increase in “speed of its work” and sorption capacity, i.e. provides an increase in the efficiency of the sorption container.
Признаки, указывающие, что «в качестве сорбента использованы природные цеолиты месторождений вулканогенно-осадочного типа, например Вангинского, и/или Ванчинского, и/или Водораздельного, и/или Лютогского, и/или Чеховского, и/или Шивертуйского, и/или Хогуруу», обеспечивают отсутствие в цеолитовом материале вредных минеральных и химических примесей, характерных для месторождений гидротермального типа, а также обеспечивают присутствие элементов и соединений, ранее присутствовавших в составе живых организмов, а потому структурированных оптимально для воздействия на живые системы. Кроме того, цеолитовый материал месторождений гидротермального типа неоднороден по химическому и минеральному составу (т.е. пробы материала, отбираемые на малом удалении друг от друга резко варьируют по минеральному и химическому составу, кроме того, в нем часто присутствуют повышенные концентрации токсичных элементов (тяжелых металлов, мышьяка и т.п.). При этом обеспечиваются высокая сорбционная емкость предлагаемого сорбционного контейнера и уникальные ионоселективные и ионообменные свойства сорбирующего материала, в том числе способность поставлять в рану содержащиеся в природных цеолитах химические элементы, необходимые для строительства тканей тела, что дополнительно стимулирует процесс заживления ран.Signs indicating that “natural zeolites of deposits of the volcanic-sedimentary type, for example, Vanginsky, and / or Vanchinsky, and / or Lutogorsk, and / or Chekhov, and / or Shivertuysky, and / or Hoguruu, were used as a sorbent ”, Ensure the absence in the zeolite material of harmful mineral and chemical impurities characteristic of hydrothermal deposits, and also ensure the presence of elements and compounds that were previously present in living organisms, and therefore structured about optimal for influencing living systems. In addition, the zeolite material of hydrothermal deposits is heterogeneous in chemical and mineral composition (i.e. material samples taken at a short distance from each other sharply vary in mineral and chemical composition, in addition, it often contains elevated concentrations of toxic elements (heavy metals, arsenic, etc.). This ensures the high sorption capacity of the proposed sorption container and the unique ion-selective and ion-exchange properties of the sorbent material, including bnost supply to the wound contained in natural zeolites the chemical elements needed to build body tissues, which further stimulates the healing process.
Признаки, указывающие, что использованы природные цеолиты «с содержанием глинистого компонента не выше 30% по объему и минералов примесей, например вулканического стекла, и/или полевых шпатов, и/или кварца, не выше 5%», обеспечивают возможность тонкого измельчения цеолитов до заданного диапазона крупности, без потерь сорбционной емкости сорбента.Signs indicating that natural zeolites are used "with a clay component content not exceeding 30% by volume of impurity minerals, such as volcanic glass, and / or feldspars, and / or quartz, not exceeding 5%", provide the possibility of fine grinding of zeolites to a given range of fineness, without loss of sorption capacity of the sorbent.
Признаки, указывающие, что «названные цеолиты используют в смеси с цеолитом Люльинского месторождения» придают сорбенту уникальные биологически активные свойства. Цеолиты Люльинского месторождения являются древнейшими из известных на планете (их возраст оценивается средним палеозоем, в то время как возраст формирования подавляющего большинства других цеолитовых залежей мезозойский и более молодой), при этом названный материал формировался в мелководных морских условиях с характерной фауной губок, остатки которой вошли в состав цеолитового туфа. Кроме того, Люльинские цеолитовые туфы отличаются необычным уникальным набором микроэлементов, что обусловлено наличием примеси в исходных породах стекол андезитобазальтового состава, в то время как другие известные залежи цеолитсодержащих пород формировались почти исключительно по стеклам гранитоидного состава с характерным для них набором микроэлементов. При этом глинистые минералы в Люльинских цеолитовых породах (хлориты, смектит) благодаря более глубокой метаморфизации (по сравнению с остальными цеолитами России и, по видимому, планеты) не гелифицируются даже при длительном контакте с водой, поэтому при «работе» в составе сорбционного контейнера, при поглощении раневых выделений, не происходит кольматирование пор набухающим глинистым материалом, т.е. дольше сохраняется сорбционная способность сорбента.Signs indicating that “the named zeolites are used in a mixture with the zeolite of the Lyulinsky deposit” give the sorbent unique biologically active properties. The zeolites of the Lyulyinsky deposit are the oldest known on the planet (their age is estimated by the Middle Paleozoic, while the age of formation of the vast majority of other zeolite deposits is Mesozoic and younger), while this material was formed in shallow marine conditions with a characteristic fauna of sponges, the remains of which entered in the composition of zeolite tuff. In addition, the Lyulinsky zeolite tuffs are distinguished by an unusual unique set of microelements, which is due to the presence of an impurity in the initial rocks of glasses of andesitobasaltic composition, while other known deposits of zeolite-containing rocks were formed almost exclusively from glasses of granitoid composition with a characteristic set of microelements. At the same time, clay minerals in the Lyulinsky zeolite rocks (chlorites, smectite) due to a deeper metamorphization (compared to other zeolites of Russia and, apparently, planets) are not gelled even after prolonged contact with water, therefore, when “working” as part of a sorption container, when wound secretions are absorbed, pores are not clogged with swelling clay material, i.e. the sorption ability of the sorbent remains longer.
Признаки, указывающие, что доля цеолита Люльинского месторождения «составляет не менее 5% от объема смеси», обеспечивают повышение биологической активности сорбента.Signs indicating that the share of the zeolite of the Lyulinsky deposit "is at least 5% of the volume of the mixture", provide an increase in the biological activity of the sorbent.
Признак второго пункта формулы обеспечивает надежное удержание тонкодисперсного сорбента в полости контейнера.The sign of the second paragraph of the formula provides reliable retention of finely dispersed sorbent in the cavity of the container.
На фиг.1 схематически показан разрез сорбционного контейнера; на фиг.2 показан вид контейнера сверху.Figure 1 schematically shows a section of a sorption container; figure 2 shows a top view of the container.
На чертежах показаны оболочка 1, в полости которой размещена тонкоизмельченная сорбирующая смесь 2, торцовые швы 3 и 4, точечные швы 5.The drawings show the
В качестве сорбента использованы природные цеолиты Дальневосточных и Восточно-Сибирских месторождений вулканогенно-осадочного типа, например Вангинского, и/или Ванчинского, и/или Водораздельного, и/или Лютогского, и/или Чеховского, и/или Шивертуйского, и/или Хогуруу, с содержанием глинистого компонента не выше 30% по объему и минералов примесей (например, таких как вулканическое стекло, полевые шпаты, кварц) не выше 5% по объему. Причем названный цеолитовый материал используют в смеси с цеолитом Люльинского месторождения (Приполярный Урал), доля которого составляет не менее 5% от объема смеси. При этом дисперсность сорбента составляет менее 10 мкм, в диапазоне от 0,15 до 10 мкм.As the sorbent used natural zeolites of the Far East and East Siberian deposits of the volcanic-sedimentary type, for example Vanginsky, and / or Vanchinsky, and / or Watershed, and / or Lyutogsky, and / or Chekhov, and / or Shivertuysky, and / or Hoguruu, with a clay component content not exceeding 30% by volume and impurity minerals (for example, such as volcanic glass, feldspars, quartz) not exceeding 5% by volume. Moreover, the aforementioned zeolite material is used in a mixture with the zeolite of the Lulinsky deposit (Subpolar Urals), the proportion of which is at least 5% of the volume of the mixture. The dispersion of the sorbent is less than 10 microns, in the range from 0.15 to 10 microns.
В качестве оболочки 1 используют диализные медицинскую или пищевую пленки, предпочтительно выполненные на основе целлофана или полиамида с полиэтиленом или полипропилена. Эта пленка имеет тонкие поры и выпускается в виде "труб" (рукавов) разного диаметра (поставляется метражом в виде рулонов или "бухт"). При этом размер пор используемой пленки «привязывают» под крупность сорбента, который как минимум втрое должен превышать размеры пор диализной пленки. Например, если предельная крупность сорбента 0,15 мкм (150 нм), то размер пор не может превышать 50 нм, при использовании сорбента более крупной фракции размер пор не лимитируется и может быть много меньше размера сорбента.As the
В качестве сорбента используют малоглинистый (менее 30% глины) цеолитовый материал (цеолитовые туфы месторождений Вангинское, и/или Ванчинское, и/или Водораздельное, и/или Лютогское, и/или Чеховское, и/или Шивертуйское, и/или Хогуруу) как в их смеси, так и по отдельности. Причем названный цеолитовый материал используют в смеси с цеолитом Люльинского месторождения, доля которого составляет не менее 5% от объема смеси. По нашим данным, чем выше доля цеолита Люльинского месторождения, тем лучше, но поскольку при организации производства сорбционных контейнеров на базе цеолитовых месторождений Дальнего Востока и Восточной Сибири добыча и доставка цеолита из региона полярного Урала ведет к удорожанию этого компонента, его доля ограничена минимальным значением, при котором рост сорбционной эффективности сорбента и улучшение его ионообменных характеристик, по нашим данным, становится заметным.As a sorbent, a small-clay (less than 30% clay) zeolite material (zeolite tuffs of the Vanginskoye and / or Vanchinskoye and / or Watershed and / or Lyutogskoye and / or Chekhovskoye and / or Shivertuyskoye and / or Hoguruu) is used as in their mixture, and separately. Moreover, the aforementioned zeolite material is used in a mixture with the zeolite of the Lulinsky deposit, the proportion of which is at least 5% of the mixture volume. According to our data, the higher the share of zeolite of the Lyulinsky deposit, the better, but since the organization and production of sorption containers based on zeolite deposits in the Far East and Eastern Siberia, the extraction and delivery of zeolite from the region of the polar Urals leads to an increase in the cost of this component, its share is limited to a minimum value, in which, according to our data, an increase in the sorption efficiency of the sorbent and an improvement in its ion-exchange characteristics becomes noticeable.
При изготовлении сорбционного контейнера вначале "трубу" - заготовку оболочки, предварительно подготавливают, для чего ее противоположные стенки 6 точечно скрепляют по всей площади посредством точечных швов 5, формируемых термической сваркой (если контейнер формируется из полиамида с полиэтиленом, то сварку ведут при температуре 130-150°С, если используют целлофан, то температура поднимается до 175-200°С при давлении 4-5 атм). Точечные швы 5 формируют, по меньшей мере, в одной точке на каждые 5 см2 площади сорбционного контейнера. В подготовленной таким образом «трубе» один торец известным образом перекрывают двойным поперечным швом, включающим шов 3 одного (на чертеже - нижележащего) контейнера и шов 4 соседнего с ним (на чертеже - вышележащего) контейнера. Если контейнер формируется из полиамида с полиэтиленом, то сварку ведут при температуре 130-150°С, если используют целлофан, то температура поднимается до 175-200°С при давлении 4-5 атм. Далее, в образовавшийся "кулек" засыпают соответствующую порцию названной сорбирующей смеси (со степенью измельчения менее 10 мкм, в диапазоне от 0,15 до 10 мкм). Объем порции определяется размерами контейнера, его шириной и длиной. После заполнения контейнера сорбирующей смесью 2 формируют второй двойной шов, включающий швы 3 и 4 при соблюдении тех же температурных режимов, как и при формировании предшествующего двойного шва. Далее режущее устройство (на чертежах не показано) отделяет контейнеры друг от друга, разрезая участки 7 между швами 3 и 4, составляющими соответствующие двойные швы. Возможен вариант, когда такой разрез формируют однократно, после нескольких контейнеров (это может быть целесообразно при необходимости работы с ранами большой площади). Такие «сборки», при необходимости, непосредственно перед применением разделяют на отдельные контейнеры, их перерезанием по участку 7 двойного шва (между его одинарными швами 3 и 4).In the manufacture of a sorption container, first a “tube” - a blank of the shell, is preliminarily prepared, for which its
При изготовлении сорбционных контейнеров принимают известные меры для обеспечения их стерильности.In the manufacture of sorption containers, well-known measures are taken to ensure their sterility.
Сорбционный контейнер используют следующим образом.The sorption container is used as follows.
Сорбционные контейнеры прикладывают на раневую поверхность любой из своих плоских сторон или вставляют (укладывают) непосредственно в брюшину (например, при лечении разлитого перитонита или панкреонекроза). При этом точечные швы 5 обеспечивают равномерность распределения сорбента в полости контейнера.Sorption containers are applied to the wound surface of any of their flat sides or inserted (laid) directly into the peritoneum (for example, in the treatment of spilled peritonitis or pancreatic necrosis). In this case, the
Через 16-24 часа, во время перевязки, контейнер меняют на новый. На курс лечения требуется 3-6 перевязок. Установлено выраженное адсорбционное, дезодорирующее, биостимулирующее действие цеолита в контейнерах на ткани. Грануляционная ткань появлялась в среднем на сутки раньше, чем в группе клинического сравнения, что позволяло наложить ранние вторичные швы и добиться лучшего косметического эффекта. Имеется опыт лечения больных с гнойными ранами различной локализации, в сравнении с группой клинического сравнения, сроки лечения в опытной группе достоверно меньше. При этом обеспечивалось надежное удержание сорбента в полости сорбционного контейнера.After 16-24 hours, during ligation, the container is changed to a new one. The course of treatment requires 3-6 dressings. A pronounced adsorption, deodorizing, biostimulating effect of zeolite in containers on tissues has been established. Granulation tissue appeared on average a day earlier than in the clinical comparison group, which made it possible to apply early secondary sutures and achieve a better cosmetic effect. There is experience in the treatment of patients with purulent wounds of different localization, in comparison with the clinical comparison group, the treatment time in the experimental group is significantly less. At the same time, reliable retention of the sorbent in the cavity of the sorption container was ensured.
Проведенные клинические испытания сорбционных контейнеров, оболочки которых изготовлены из диализных медицинских или пищевых пленок, заполненных тонкодисперсными порошками природных цеолитов в смеси с цеолитом Люльинского месторождения, показали высокую эффективность заживления гнойных ран. Диализная пленка не прилипала к тканям, что резко облегчало проведение перевязок.Clinical trials of sorption containers, the shells of which are made of dialysis medical or food films, filled with fine powders of natural zeolites mixed with zeolite from the Lyulinsky deposit, have shown high efficiency in the healing of purulent wounds. The dialysis film did not adhere to the tissues, which greatly facilitated the dressing.
Claims (3)