RU2451656C2 - Method of making porous spherical powder for smooth-bore gun shot cartridges - Google Patents
Method of making porous spherical powder for smooth-bore gun shot cartridges Download PDFInfo
- Publication number
- RU2451656C2 RU2451656C2 RU2010101372/05A RU2010101372A RU2451656C2 RU 2451656 C2 RU2451656 C2 RU 2451656C2 RU 2010101372/05 A RU2010101372/05 A RU 2010101372/05A RU 2010101372 A RU2010101372 A RU 2010101372A RU 2451656 C2 RU2451656 C2 RU 2451656C2
- Authority
- RU
- Russia
- Prior art keywords
- powder
- water
- solvent
- varnish
- porous spherical
- Prior art date
Abstract
Description
Изобретение относится к области получения пористых сферических порохов (СФП) для стрелкового оружия, например гладкоствольного дробового оружия.The invention relates to the field of production of porous spherical powders (TFP) for small arms, for example, smoothbore shotguns.
В патентах [1, 2] предложены способы получения СФП, заключающиеся в раздельном приготовлении нитроцеллюлозного лака в растворителе, водорастворимого эмульгатора и водорастворимой соли (например, сернокислого натрия, хлористого натрия), смешении лака и водного раствора эмульгатора, диспергировании на сферические частицы, отгонке растворителя, промывке и сушке.Patents [1, 2] propose methods for producing TFP, which consist in the separate preparation of nitrocellulose varnish in a solvent, a water-soluble emulsifier and a water-soluble salt (for example, sodium sulfate, sodium chloride), mixing varnish and an aqueous solution of an emulsifier, dispersion on spherical particles, distillation of the solvent washing and drying.
Недостатком этих способов является высокая насыпная плотность полученных порохов и, как следствие, высокое значение массы порохового заряда, при которой не обеспечиваются требуемые баллистические характеристики дробового патрона.The disadvantage of these methods is the high bulk density of the obtained powders and, as a consequence, the high value of the mass of the powder charge, at which the required ballistic characteristics of the shot cartridge are not provided.
Наиболее близким техническим решением (прототип) является способ получения СФП для охотничьего оружия [3], включающий приготовление порохового лака в водной среде при перемешивании нитратов целлюлозы с этилацетатом (ЭА), добавление к лаку костного клея, диспергирование порохового лака на сферические частицы и удаление ЭА при нагревании смеси. В качестве нитроцеллюлозы используют пироксилин №1 или пироксилин №1 с возвратно-технологическими отходами, которые в течение 10…15 минут перемешивают в 4…5 частях воды на 1 мас.ч. пироксилина №1 или пироксилина №1 с возвратно-технологическими отходами совместно с дифениламином (ДФА) в количестве 0,6…1,2% и дополнительно вводимым техническим углеродом в количестве 0,3…1,0%, поступающим в виде водной суспензии с концентрацией 20…30 мас.% и медь (II)-свинец (II) фталат оксидом (ФМС) в количестве 0,5…2,5% от массы пироксилина №1 и с 2,4…2,6 мас.ч. ЭА, а нагревание смеси для удаления ЭА ведут до температуры 92…94°С.The closest technical solution (prototype) is a method for producing TFP for hunting weapons [3], which includes the preparation of powder varnish in an aqueous medium while mixing cellulose nitrates with ethyl acetate (EA), adding bone glue to the varnish, dispersing the powder varnish onto spherical particles and removing EA when heating the mixture. As nitrocellulose, pyroxylin No. 1 or pyroxylin No. 1 with process waste is used, which is mixed for 10 ... 15 minutes in 4 ... 5 parts of water per 1 part by weight pyroxylin No. 1 or pyroxylin No. 1 with process waste together with diphenylamine (DFA) in an amount of 0.6 ... 1.2% and additionally introduced carbon black in an amount of 0.3 ... 1.0%, coming in the form of an aqueous suspension with concentration of 20 ... 30 wt.% and copper (II) -lead (II) phthalate oxide (FMS) in an amount of 0.5 ... 2.5% by weight of pyroxylin No. 1 and with 2.4 ... 2.6 wt.h. EA, and heating the mixture to remove EA lead to a temperature of 92 ... 94 ° C.
Недостатком данного способа является то, что полученный порох не обеспечивает баллистические характеристики в спортивном патроне для охотничьих ружей 12 калибра.The disadvantage of this method is that the resulting powder does not provide ballistic characteristics in a sports cartridge for hunting rifles 12 gauge.
Целью предлагаемого изобретения является получение СФП для спортивного патрона к охотничьим ружьям 12 калибра.The aim of the invention is to obtain TFP for a sports cartridge for hunting rifles 12 gauge.
Поставленная цель достигается тем, что в реактор заливают 2…3 мас.ч. воды, 2…3 мас.ч. ЭА, 2…3 мас.ч. ацетона по отношению к пороховой массе и при перемешивании вводят 1 мас.ч. пороховой массы, состоящей из 60…62 мас.% коллоксилина «Н» с содержанием оксида азота 189…194,5 мл NO/г и 38…40 мас.% нитроглицерина (НГц), затем вводят 1,0…1,6 мас.% мездрового клея по отношению к воде и дополнительно заливают 2…3 мас.ч. воды по отношению к пороховой массе, приготовление, диспергирование порохового лака на сферические частицы и отгонку растворителя из них ведут известным способом.This goal is achieved by the fact that in the reactor pour 2 ... 3 wt.h. water, 2 ... 3 parts by weight EA, 2 ... 3 parts by weight acetone in relation to the powder mass and with stirring, 1 wt.h. a powder mass consisting of 60 ... 62 wt.% colloxylin "N" with a nitric oxide content of 189 ... 194.5 ml NO / g and 38 ... 40 wt.% nitroglycerin (NHz), then 1.0 ... 1.6 wt. .% glue glue in relation to water and optionally pour 2 ... 3 wt.h. water in relation to the powder mass, preparation, dispersion of the powder varnish on spherical particles and distillation of the solvent from them are carried out in a known manner.
Примеры выполнения способа получения СФП к спортивным патронам для ружей 12 калибра в пределах граничных условий (примеры 1…3), а также за их пределами (примеры 4, 5) приведены в таблице.Examples of the method for producing TFP for sports cartridges for 12-gauge rifles within the boundary conditions (examples 1 ... 3), as well as beyond them (examples 4, 5) are shown in the table.
Пример 1. В реактор объемом 1,57 м3 заливается 200 л воды, 200 л ацетона и 200 л ЭА и при перемешивании загружается 100 кг пороховой массы, состоящей из 60 мас.% коллоксилина «Н» с содержанием оксида азота 189…194,5 мл NO/г и 40 мас.% НГц, затем вводится 2,0 кг мездрового клея и заливается дополнительно 300 л воды по отношению к пороховой массе. При температуре 58…64°С ведется приготовление порохового лака в течение 30 минут, а затем при температуре 62…68°С ведется диспергирование порохового лака на сферические частицы в течение 60 минут. После чего ведется отгонка растворителя известным способом. Технологические режимы, физико-химические и баллистические характеристики СФП приведены в таблице.Example 1. In a reactor with a volume of 1.57 m 3 200 l of water, 200 l of acetone and 200 l of EA are poured and with stirring 100 kg of powder mass consisting of 60 wt.% Colloxylin “N” with a content of nitric oxide of 189 ... 194, 5 ml of NO / g and 40 wt.% NHz, then 2.0 kg of glue is added and an additional 300 l of water is poured in relation to the powder mass. At a temperature of 58 ... 64 ° C, the preparation of powder varnish is carried out for 30 minutes, and then at a temperature of 62 ... 68 ° C dispersion of the powder varnish on spherical particles is carried out for 60 minutes. After which the solvent is distilled off in a known manner. Technological modes, physico-chemical and ballistic characteristics of the TFP are shown in the table.
Пример 2. В реактор объемом 1,57 м3 заливается 250 л воды, 250 л ацетона и 250 л ЭА и при перемешивании загружается 100 кг пороховой массы, состоящей из 61 мас.% коллоксилина «Н» с содержанием оксида азота 189…194,5 мл NO/г и 39 мас.% НГц, затем вводится 3,25 кг мездрового клея и заливается дополнительно 250 л воды по отношению к пороховой массе. При температуре 58…64°С ведется приготовление порохового лака в течение 30 минут, а затем при температуре 62…68°С ведется диспергирование порохового лака на сферические частицы в течение 60 минут. После чего ведется отгонка растворителя известным способом. Технологические режимы, физико-химические и баллистические характеристики СФП приведены в таблице.Example 2. In a reactor with a volume of 1.57 m 3, 250 l of water, 250 l of acetone and 250 l of EA are poured and with stirring 100 kg of a powder mass consisting of 61 wt.% Colloxylin “N” with a content of nitric oxide of 189 ... 194, 5 ml of NO / g and 39 wt.% NHz, then 3.25 kg of glue glue is introduced and an additional 250 l of water is poured in relation to the powder mass. At a temperature of 58 ... 64 ° C, the preparation of powder varnish is carried out for 30 minutes, and then at a temperature of 62 ... 68 ° C dispersion of the powder varnish on spherical particles is carried out for 60 minutes. After which the solvent is distilled off in a known manner. Technological modes, physico-chemical and ballistic characteristics of the TFP are shown in the table.
Пример 3. В реактор объемом 1,57 м3 заливается 300 л воды, 300 л ацетона и 300 л ЭА и при перемешивании загружается 100 кг пороховой массы, состоящей из 62 мас.% коллоксилина «Н» с содержанием оксида азота 189…194,5 мл NO/г и 38 мас.% НГц, затем вводится 4,8 кг мездрового клея и заливается дополнительно 200 л воды по отношению к пороховой массе. При температуре 58…64°С ведется приготовление порохового лака в течение 30 минут, а затем при температуре 62…68°С ведется диспергирование порохового лака на сферические частицы в течение 60 минут. После чего ведется отгонка растворителя известным способом. Технологические режимы, физико-химические и баллистические характеристики СФП приведены в таблице.Example 3. In a reactor with a volume of 1.57 m 3, 300 l of water, 300 l of acetone and 300 l of EA are poured and with stirring 100 kg of a powder mass consisting of 62 wt.% Colloxylin “N” with a content of nitric oxide of 189 ... 194, 5 ml of NO / g and 38 wt.% NHz, then 4.8 kg of glue glue is introduced and an additional 200 l of water is poured in relation to the powder mass. At a temperature of 58 ... 64 ° C, the preparation of powder varnish is carried out for 30 minutes, and then at a temperature of 62 ... 68 ° C dispersion of the powder varnish on spherical particles is carried out for 60 minutes. After which the solvent is distilled off in a known manner. Technological modes, physico-chemical and ballistic characteristics of the TFP are shown in the table.
Примечание: По техническим условиям масса порохового заряда - не более 1,45 г, масса дроби - 24 г, средняя скорость полета дроби - не менее 340 м/с, среднее максимальное давление пороховых газов в канале ствола оружия - не более 90 МПа.Note: According to specifications, the mass of the powder charge is not more than 1.45 g, the mass of the fraction is 24 g, the average flight speed of the fraction is not less than 340 m / s, the average maximum pressure of the powder gases in the channel of the barrel of the weapon is not more than 90 MPa.
Из приведенных результатов таблицы видно, что по разработанному авторами способу (примеры 1…3) полученный пористый сферический порох обеспечивает требуемые баллистические характеристики в спортивном патроне к охотничьим ружьям 12 калибра. За пределами граничных условий (примеры 4, 5) баллистические показатели не соответствуют требованиям технических условий на СФП, предназначенный для снаряжения спортивного патрона к охотничьим ружьям 12 калибра.From the results of the table it can be seen that according to the method developed by the authors (examples 1 ... 3), the obtained porous spherical powder provides the required ballistic characteristics in a sports cartridge for 12-gauge hunting rifles. Outside of the boundary conditions (examples 4, 5), the ballistic indicators do not meet the requirements of the technical conditions on the TFP, designed to equip a sports cartridge for 12-gauge hunting rifles.
Технологические режимы, физико-химические и баллистические характеристики изготовленных образцов порохаTable
Technological modes, physico-chemical and ballistic characteristics of the manufactured samples of gunpowder
(Пр. №1)Example
(Project No. 1)
ЛитератураLiterature
1. Патент США №2931800, 1960, Кл. 260-223, МКИ С08В 1/04.1. US patent No. 2931800, 1960, Cl. 260-223, MKI C08B 1/04.
2. Патент ФРГ №1067719, 1960, НКИ 78 С 20, МКИ С06В.2. German patent No. 1067719, 1960, NKI 78 S 20, MKI S06V.
3. Патент РФ №1727375 (С06В 21/00), 1997.3. RF patent No. 1727375 (С06В 21/00), 1997.
Claims (1)